Frosio 17A Inspection work & equipment slide # 1
Use of instruments
![Page 2: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/2.jpg)
Frosio 17A Inspection work & equipment slide # 2
Utstyr utlagt
Inspection Equipment
![Page 3: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/3.jpg)
Frosio 17A Inspection work & equipment slide # 3
Inspection after application
Climatic conditions (Ventilation,
Temperature and humidity) Curing / drying of the film Dry film thickness (DFT) Adhesion Holiday detection (if required)
After application the following must be checked
![Page 4: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/4.jpg)
Frosio 17A Inspection work & equipment slide # 4
Wet paint
Steel
ISO 2808 - 97 Method No.1 Wet film measuring comb
Microns250 225 200 175 150 125 100 75 50 25
![Page 5: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/5.jpg)
Frosio 17A Inspection work & equipment slide # 5
4932-81
0459-21
ISO 2808Wet film thickness gauge
• Measure wet paint film• Here: 25 microns between the teeth
![Page 6: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/6.jpg)
Frosio 17A Inspection work & equipment slide # 6
Using “PIG” Universal on a ship’s hull
• PIG = Paint Inspection Gauge
• Destructive test method
• Possible to verify the number of coats applied
• Possible to measure the thickness of each individual coat
Cd-4932-100
![Page 7: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/7.jpg)
Frosio 17A Inspection work & equipment slide # 7
PIG Paint Inspection GaugeMainly for laboratory use
4932-100
![Page 8: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/8.jpg)
Frosio 17A Inspection work & equipment slide # 8
ISO 2808 - 97 Determination of film thickness
Method No. 6: Magnetic method
• Magnetic induction principle (Method 6 A)
• Permanent magnetic principle (Method 6 B)
• Instruments for magnetic, metallic substrates
• Calibration must be done in accordance with instructions from the manufacturer
• Before testing the paint system must be properly cured.
![Page 9: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/9.jpg)
Frosio 17A Inspection work & equipment slide # 9
ISO 2808 - 97 Determination of film thickness
• High frequency electromagnetic instrument
• For non-magnetic substrates
• Calibration in accordance with the manufacturers instruction
Method No. 7 - Eddy current method
![Page 10: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/10.jpg)
Frosio 17A Inspection work & equipment slide # 10
• Electromagnetic instruments• Calibration on a smooth steel surface min. 1,2 mm
thick• For DFT measurement, not less than 25 and
preferably above 50 microns• Number of readings, as a guide:
– 1 reference area: At least 3 readings evenly
– 2 reference areas for every square meter for flat plates
– 4 reference areas for every length for a web
– 2 reference areas every metre length for a flange
– 2 reference areas every metre length for a pipe
ISO 2808 - 97
Determination of film thicknessMethod No. 10 - On blast cleaned steel substrates
![Page 11: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/11.jpg)
Frosio 17A Inspection work & equipment slide # 11
ISO 2808 - Magnetic and electromagnetic Dry film thickness gauges
• Dry film thickness gauge• Calibrate on smooth
surface to zero and to thickness similar to be measured
• Check with your calibration foil frequently
• Plastic material foils wear easily. Replace frequently.
• No internal memory in gauge
Cd-4932-82
![Page 12: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/12.jpg)
Frosio 17A Inspection work & equipment slide # 12
ISO 2808 - Magnetic and electromagnetic Dry film thickness gauges
• Dry film thickness gauge• Calibrate on smooth
surface to zero and to thickness similar to be measured
• Check with your calibration foil frequently
• Plastic material foils wear easily. Replace frequently.
• No internal memory in gauge
Inspection \ Dryfilmthickness1
![Page 13: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/13.jpg)
Frosio 17A Inspection work & equipment slide # 13
Tørrfilm målere Elektr. Magn.
Magnetic and Electromagnetic Dry Film Thickness Gauges
• ISO 2808• Dry film thickness gauge• Calibrate on smooth
surface to zero and to thickness similar to be measured
• Check with your calibration foil frequently
• Plastic material foils wear easily. Replace frequently.
• Some models have internal memory.
![Page 14: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/14.jpg)
Frosio 17A Inspection work & equipment slide # 14
SSPC - PA 2
Measuring DFT on small areas
1. Area of 10 m2: 5 spot measurements
2. Each spot measurement: The average of 3 individual readings made on one small area
3. The average of 5 spot measurements must be within specified range of film thickness
4. Single spot measurements may be as low as 80% of specified minimum film thickness
5. Individual readings included in the spot measurements may be less than 80% of minimum thickness
Procedure
![Page 15: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/15.jpg)
Frosio 17A Inspection work & equipment slide # 15
SSPC - PA 2 Number of film thickness measurements
1. 10 m2 5 spots (on each spot: 3 measurements)
2. 30 m2 As for case 1 for each 10 m2
3. Up to100 m2 Select 3 areas, each of 10 m2
4. Above 100 m2 The first 100 m2 as for case 3 For each following 100 m2 select randomly one area of 10 m2
Note: If measurements outside the specification for any 10 m2 in case 3 or 4 above are found, then each 10 m2 shall be measured
Case Area Selection of Measurements
![Page 16: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/16.jpg)
Frosio 17A Inspection work & equipment slide # 16
Instruments for measuring surface roughness
• Stylus instruments• Elcometer Mod. 123• Testex Press-O-film• Microscope• Comparator
– Rugotest No. 3– ISO 8503 etc.
![Page 17: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/17.jpg)
Frosio 17A Inspection work & equipment slide # 17
Clemco
Compartor
Surface Roughness acc. to ISO 8503
• Example of a reference comparator: Clemco
• Surface profile comparator comprising four segments.
• Clemco - grit• Clemco shot also available • Check if the profile is
according to specification and the paint manufacturer’s recommendation
![Page 18: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/18.jpg)
Frosio 17A Inspection work & equipment slide # 18
Jan, speil, lykt
Using Inspection Tools: Mirror and Flash light
• Visual inspection• Important tools to be
able to inspect areas difficult to access
![Page 19: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/19.jpg)
Frosio 17A Inspection work & equipment slide # 19
1. Air temperature2. % Relative humidity3. Steel temperature4. Dew point
ISO 8502 – 4 Humidity
Guidance on the estimation of the probability of condensation prior to paint application
Steel temperature min. 3 oC above the dew point
![Page 20: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/20.jpg)
Frosio 17A Inspection work & equipment slide # 20
Steel temperature
Contact Thermometer
• Electronic instrument for measuring the steel temperature
• Steel temperature must be min. 3oC above the dew point
• Other types of thermometers are also available. E.g. magnetic thermometers
![Page 21: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/21.jpg)
Frosio 17A Inspection work & equipment slide # 21
Measuring the Relative Humidity
• ISO 8502 - 4• Photo: Sling hygrometer
for measuring:- Dry temperature- Wet temperature
• Measure the temperature in the vicinity of the work
• Calculate the relative humidity
• Use together with dew point calculator
![Page 22: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/22.jpg)
Frosio 17A Inspection work & equipment slide # 22
Dew Point Calculator
• ISO 8502 - 4• For calculation of dew
point• To be used together with
surface temperature thermometer and sling hygrometer.
• Use this frequently during pre-treatment, application and drying of the paint.
• Recommendation: Every 6 hours and when weather conditions are changing
![Page 23: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/23.jpg)
Frosio 17A Inspection work & equipment slide # 23
Bresle sett
Salt Test Equipment - Bresle Test
• ISO 8502 - 6 (Sampling)
• ISO 8502 - 9 (Conductivity)
• Equipment for sampling and measuring content of water soluble salt on substrate
• Bresle method
![Page 24: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/24.jpg)
Frosio 17A Inspection work & equipment slide # 24
How to measure the salt level on a surface
• Water soluble salts will be removed by water jetting
• Here: The substrate is cleaned at a pressure of 2000 bar
• Salt level is measured by the Bresle method
• Dissolve the salt inside the frame of the patch
• Measure the conductivity of the water sample
Pre-treatment: Wj_saltlevel1
For 15 ml sample size, multiply conductivity measured in μS by a factor of 6 to get mg salt per m2
![Page 25: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/25.jpg)
Frosio 17A Inspection work & equipment slide # 25
Calculating salt level on the substrate
Formula: (L2 – L1) x 6 = mg salt per m2
L2 = μS after cleaning
L1 = μS before cleaning
Water sample, ml: 10 15 20 50
Constant in formula: 4 6 8 20
![Page 26: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/26.jpg)
Frosio 17A Inspection work & equipment slide # 26
Approved
Not approved
Tape Blast cleaned steel
Assessment of Dust on Steel Surfaces Prepared for Painting. ISO 8502-3
![Page 27: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/27.jpg)
Frosio 17A Inspection work & equipment slide # 27
![Page 28: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/28.jpg)
Frosio 17A Inspection work & equipment slide # 28
Glove RagMEK
Rubbing 50 x
No Zinc on the Rag:CuredApproved
ASTM D 4752-87 Curing test of Zinc - ethylsilicate with MEK.
A lot of Zinc on Rag:Not curedFurther curing / Reblasting
![Page 29: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/29.jpg)
Frosio 17A Inspection work & equipment slide # 29
ASTM D 4752-87MEK curing test of zinc ethyl silicate
• Left: One cured and uncured test plate• Right: Uncured zinc over coated. Result: Delamination
A-40807-2
![Page 30: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/30.jpg)
Frosio 17A Inspection work & equipment slide # 30
Glove
Rag
MEK
ASTM D 4752-87 ASTM D 4752-87 Curing test of Zinc – ethyl silicate with MEK. Curing test of Zinc – ethyl silicate with MEK.
Inspection / Zincsilicate_curing1
![Page 31: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/31.jpg)
Frosio 17A Inspection work & equipment slide # 31
ASTM D 3359-87 Adhesion testing by knife and adhesive tape
• There are two test methods• The method to select depends on the DFT
Method A: DFT above 125 micronsMethod B: DFT below 125 microns
(Above 125 if wider cuts are used)
Method A: X - cut. Tape testMethod B: Cross - cut. Tape test
![Page 32: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/32.jpg)
Frosio 17A Inspection work & equipment slide # 32
ASTM 3359-87. Method B
Adhesion testing
• < 50 microns = 1 mm apart (11 cuts)• 50 - 125 microns = 2 mm apart (6 cuts)• > 125 microns = Method A
1. Cuts: 20 mm long2. Brush with a soft brush3. Examine4. Cuts: 20 mm long at 90o on the original cuts5. Brush with...6. Tape 75 mm7. Within 90 + 30 sec. remove tape
![Page 33: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/33.jpg)
Frosio 17A Inspection work & equipment slide # 33
5B The edges of the cuts are completely smooth; none of the lattice is detached
4B Small flakes of the coating is detached at intersections: 5% of the area is affected
3B Small flakes of the coating are detached along edges and at intersections of cuts. The area affected is 5 to 15% of the lattice.
2B The coating has flaked along the edges and on parts of the squares. The area affected is 15 to 35% of the lattice.
1B The coating has flaked along the edges of cuts in large ribbons and whole squares have detached. The area affected is 35 to 65 % of the lattice.
0B Flaking and detachment worse than Grade 1B.
Classification of adhesion test results. Method B. (Example for six parallel cuts).
5B None4B
3B
2B
1B
0B Greater than 65%
![Page 34: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/34.jpg)
Frosio 17A Inspection work & equipment slide # 34
ISO 2409
Cross-cut test Cutting tool
Single bladed knife or
Multi-blade cutting tool with 6 cutting edges spaced 1 mm or 2 mm apart
Spacing of cuts 0 - 60 microns: 1 mm spacing, hard substrates 0 - 60 microns: 2 mm spacing, soft substrates60 - 120 microns: 3 mm spacing, hard/soft substrates121 - 250 microns: 3 mm spacing, hard/soft substrates
![Page 35: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/35.jpg)
Frosio 17A Inspection work & equipment slide # 35
Procedure:• Make 6 parallel cuts with defined space in the
coating.• Repeat operation, crossing original cuts at 90o
so that a grid pattern is formed.• Brush with soft brush.• Apply adhesive tape and pull off.• Classify results in accordance with table 1.
ISO 2409
Cross-cut test
![Page 36: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/36.jpg)
Frosio 17A Inspection work & equipment slide # 36
ISO 2409Cross cut adhesion test
• Cross cut adhesion test
• Cut vertical and horizontal lines to form a grid
• Apply a strong tape• Pull off the tape• Evaluate according to
the standard
Cd-4932-91
![Page 37: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/37.jpg)
Frosio 17A Inspection work & equipment slide # 37
ISO 2409Cross-cut adhesion test
• Left: A good type of cross-cut tool• Right: Evaluation of performed test
0002-001
0002-002
![Page 38: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/38.jpg)
Frosio 17A Inspection work & equipment slide # 38
5B The edges of the cuts are completely smooth; none of the lattice is detached
4B Small flakes of the coating is detached at intersections: 5% of the area is affected
3B Small flakes of the coating are detached along edges and at intersections of cuts. The area affected is 5 to 15% of the lattice.
2B The coating has flaked along the edges and on parts of the squares. The area affected is 15 to 35% of the lattice.
1B The coating has flaked along the edges of cuts in large ribbons and whole squares have detached. The area affected is 35 to 65 % of the lattice.
0B Flaking and detachment worse than Grade 1B.
Classification of Adhesion Test Results. (Example for six parallel cuts).
5B None4B
3B
2B
1B
0B Greater than 65%
![Page 39: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/39.jpg)
Frosio 17A Inspection work & equipment slide # 39
ISO 2409Classification of Cross-cut test
Classi-fication
Description Appearance of surface Six parallel cuts
0 Completely smooth: none of the squares detached
1 Small flakes at the Intersections. Area affected 5 %
2 Flaked along the edges and/or at theIntersections. Area affected: 5-15%
3Flaked along the edges, wholly in large ribbons, and/or partly or wholly on different parts of the squares. Area affected: 15-35%
4Flaked along the edges in large ribbons and/orsome squares have detached partly or wholly. Area affected: 35-65%
5 Any degree of flaking that cannot even be classified by 4.
![Page 40: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/40.jpg)
Frosio 17A Inspection work & equipment slide # 40
ISO 2409Cross cut adhesion test
• Cross cut adhesion test
• Cut vertical and horizontal lines to form a grid
• Apply a strong tape• Pull off the tape• Evaluate according to
the standard
Inspection / Adhesion_crosscut1
![Page 41: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/41.jpg)
Frosio 17A Inspection work & equipment slide # 41
Instruments:• Elcometer Adhesion Tester• Saeberg Adhesion Tester (pneumatic)• Hate Adhesion Tester (hydraulic)• PAT• Other
ISO 4624
Pull-off test for adhesion
Failure:Adhesion failure: Between coats or between or substrate and 1st coatCohesion failure: Inside a coat
![Page 42: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/42.jpg)
Frosio 17A Inspection work & equipment slide # 42
ISO 4624
Pull-off test for adhesion
Procedure:• Test dollies glued onto the coating• Adhesive: Cyano-acrylate or solvent free epoxy• Remove adhesive and coating around the dollies• Pull off test-dollies vertical to the surface• Read adhesion value and report the type of fracture
Fractures:• Adhesion failure - fracture between coats or substrate and 1.
coat• Cohesion failure - fracture within a coat
![Page 43: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/43.jpg)
Frosio 17A Inspection work & equipment slide # 43
ISO 4624Pull-off dollies glued to the structure
• Pull off adhesion test
• Dollies are glued to the structure with a strong glue
• Prior to pull-off: Cut around the dolly, through the paint film and down to the substrate material
Cd-4932-102
![Page 44: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/44.jpg)
Frosio 17A Inspection work & equipment slide # 44
ISO 4624Pull-off testing of paint on a structure
• Pull off adhesion test.• Destructive test method• Here, connecting of the
device for pulling off the dollies
• Read and note the value• Several types of
instruments are available
Cd-4932-101
![Page 45: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/45.jpg)
Frosio 17A Inspection work & equipment slide # 45
ISO 4624Area after pull-off testing
• Pull off adhesion test• The adhesiveadhesive failure -
fracture between coats - or between coating and substrate must be evaluated
• Note adhesion failure, %• The cohesivecohesive failure -
fracture within the coating- must be evaluated.
• Note cohesion failure, %• Also: Note glue failure, %
Cd-4932-103
![Page 46: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/46.jpg)
Frosio 17A Inspection work & equipment slide # 46
ISO 4624Pull-off dollies glued to the structure• Pull off adhesion test• Dollies are glued to the
structure with a strong glue
• Prior to pull-off: Cut around the dolly, through the paint film and down to the substrate material
• Record the pull-off value
• Evaluate the failure
Inspection / Adhesion_pulloff1
![Page 47: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/47.jpg)
Frosio 17A Inspection work & equipment slide # 47
ASTM G 62 - 85 Method A
Pinhole detection. Low voltage.
• Low voltage: < 75 V DC• To detect pinholes, voids or metal particles to
be in the range of 25-250 microns.• Effective for paint films up to a DFT of 500
microns if a wetting agent is used in the water.• This is a non-destructive test.
![Page 48: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/48.jpg)
Frosio 17A Inspection work & equipment slide # 48
ASTM G-62-85, method ALow voltage holiday detector
• Photo: Low voltage pinhole detector
• Detecting pinholes, voids or metal particles in paint film up to 250 microns
• Non destructive test method
• Will only detect defects down to bare metal
• The sponge must be wetted
• Do not use excessive water
Cd-4932-92
![Page 49: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/49.jpg)
Frosio 17A Inspection work & equipment slide # 49
ASTM G-62-85, method ALow voltage pinhole detector
• Photo: Low voltage pinhole detector
• Detecting pinholes, voids or metal particles in paint film up to 250 microns
• Non destructive test method
• Will only detect defects down to bare metal
• The sponge must be wetted
• Do not use excessive water
0002-004
![Page 50: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/50.jpg)
Frosio 17A Inspection work & equipment slide # 50
ASTM G-62-85, method ALow voltage pinhole detector
• Detecting pinholes, voids or metal particles in paint film up to 250 microns
• Non destructive test method
• Will only detect defects down to bare metal
• The sponge must be wetted
• Do not use excessive water
Inspection / Pore_detection1
![Page 51: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/51.jpg)
Frosio 17A Inspection work & equipment slide # 51
ASTM G 62 Method B
Holiday detection. High voltage.
High voltage: 900 - 20.000 V
Used to detect pinholes, voids andareas with thin paint films
This is a destructive test.
![Page 52: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/52.jpg)
Frosio 17A Inspection work & equipment slide # 52
ASTM G-62-85, method B High voltage holiday detector
• Destructive test method for detecting pinholes, voids and thin spots in paint film
• Adjust voltage according to the film thickness or the paint manufacturers recommendation
• Gives a light or signal when pinhole or weak point is detected
Cd-4932-93
![Page 53: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/53.jpg)
Frosio 17A Inspection work & equipment slide # 53
• 0002-005
ASTM G-62-85, method BHigh voltage holiday detector
• Destructive test method for detecting pinholes, voids and thin spots in paint film
• Adjust voltage according to the film thickness or the paint manufacturers recommendation
• Gives a light or signal when pinhole or weak point is detected
![Page 54: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/54.jpg)
Frosio 17A Inspection work & equipment slide # 54
ASTM G 62 Method B
Holiday detection. High voltage.
• High voltage: 900 - 20.000 V
• Used to detect pinholes, voids and
• areas with thin paint films
• This is a destructive test.
Inspection / Holiday_detection1
![Page 55: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/55.jpg)
Frosio 17A Inspection work & equipment slide # 55
ISO 12944 General standard for corrosion protection:
Part 1 General introduction.
Part 2 Classification of environments.
Part 3 Design considerations.
Part 4 Types of surface and surface preparation.
Part 5 Protective paint systems.
Part 6 Laboratory performance test methods.
Part 7 Execution and supervision of paint work.
Part 8 Development of specifications for new work and maintenance.
Paints and varnishes - Corrosion protection of steel structures by protective paints systems.
![Page 56: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/56.jpg)
Frosio 17A Inspection work & equipment slide # 56
ISO 8504 - 1
General principles
Selection of methods
![Page 57: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/57.jpg)
Frosio 17A Inspection work & equipment slide # 57
ISO 8504 Surface preparation methods:
Part 1: General principles. Part 2: Abrasive blast-cleaning.Part 3: Hand- and power-tool
cleaning.
![Page 58: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/58.jpg)
Frosio 17A Inspection work & equipment slide # 58
• Methods• Effectiveness• Fields of
application
ISO 8504 - 2
Abrasive blast-cleaning
![Page 59: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/59.jpg)
Frosio 17A Inspection work & equipment slide # 59
• Methods• Equipment to be used• Procedure to be followed
ISO 8504 - 3
Hand and Power-tool Cleaning
![Page 60: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/60.jpg)
Frosio 17A Inspection work & equipment slide # 60
Steel
Rag soaked
with solvent
No reaction:
Chemically curing
Paint dissolves:
Physically drying
Using solvents to determinegeneric type of paint
2 coat paintLifting/Wrinkling:
Oxidatively curing
![Page 61: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/61.jpg)
Frosio 17A Inspection work & equipment slide # 61
Use a rag soaked
with solvent
No reaction:
Chemically curing
Paint dissolves:
Physically drying
Using solvents to determinegeneric type of paint
Lifting/Wrinkling:
Oxidatively curingInspection / Determine_generic1
![Page 62: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/62.jpg)
Frosio 17A Inspection work & equipment slide # 62
Standards relating to mechanical properties
Property Standard / Test methodAdhesion (Cross cut) ISO 2409, DIN 53251, BS 3900-E6, ASTM 3359Adhesion (Pull-off) ISO 4624, ASTM 4541, BS 3900 - E10
Adhesion (Shear strength)
ASTM D 1002 (Specified for Chartek)
Hardness ISO 2815 (Buchholz - methode)
Hardness ISO 1522 (Kønig - pendel)Hardness BarcholElasticiy ISO 1520 (Cupping test)
Flexibility ISO 6860 ASTM D 522
BS 3900 - E11 (Conical mandrel)
Impact resistance ISO/TR 6272 - 79E ASTM D 2794 - 84
DIN 55669 BS 3900 - E3
![Page 63: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/63.jpg)
Frosio 17A Inspection work & equipment slide # 63
Testing and evaluation.marine atmosphere (1 of 2)
Test method Standards Comments
Physical testingAdhesionAdhesionFlexibilityElasticityHardnessImpact resistanceGlossAbrasion resistance
ISO 2409ISO 4624ISO 1510ISO 1520ISO 2815ISO 6272ISO 2813ASTM D 4060
Before and after exposureBefore and after exposureBefore and after exposureBefore and after exposure
Exposure conditions:SaltsprayProhesion testUV-cabinetCondensation chamberHumidity chamberWeatheringResistance to liquids
ISO 7253 or ASTM B 117
ASTM G 53ISO 6270BS 3900ISO 2810ISO 2812 Oil, petroleum , etc.
![Page 64: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/64.jpg)
Frosio 17A Inspection work & equipment slide # 64
Test method Standards Comments
Evaluation of paint films
BlisteringRustCrackingFlakingChalkingScribe
ISO 4628/2ISO 4628/3ISO 4628/4ISO 4628/5ISO 4628/6ASTM D 1654
Evaluation of the liquid paint
Appearance in tin
Application properties
ISO 2431
ISO 2884
“Flow time”
Viscosity
Testing and evaluation.marine atmosphere (2 of 2)
![Page 65: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/65.jpg)
Frosio 17A Inspection work & equipment slide # 65
Abrasion resistance
• Weigh the painted sample
• Install it in the apparatus and run 1000 cycles
• Measure the weight loss
Testing paints \ Abrasion resistance1
![Page 66: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/66.jpg)
Frosio 17A Inspection work & equipment slide # 66
Flexibility test
• Use a thin test panel• Measure the paint film
thickness• Carry out the impact test
on the rear side of the test panel
• Determine the highest level of impact load before any crack or defect in the paint film occurs
Testing paints \ Flexibility_test1
![Page 67: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/67.jpg)
Frosio 17A Inspection work & equipment slide # 67
Impact test
• Use a thick test panel• Measure the paint film
thickness• Carry out the impact test
on the painted side of the test panel
• Determine the highest level of impact load before any crack or defect in the paint film occurs
Testing paints \ Impact_test1
![Page 68: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/68.jpg)
Frosio 17A Inspection work & equipment slide # 68
Reference area should:
• be representative to the remaining area coated with the same system.
• be available for inspection at any time.• be marked thoroughly to indicate
"ref.area"• not be overcoated
![Page 69: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/69.jpg)
Frosio 17A Inspection work & equipment slide # 69
Controlled application
• Inspection of:» steelwork» cleaning» surface preparation (blastcleaning)» painting» curing» completed system
![Page 70: 45177372 Frosio 17A Inspection Work Equipment](https://reader035.vdocument.in/reader035/viewer/2022062219/5534201a4a79593a568b4b12/html5/thumbnails/70.jpg)
Frosio 17A Inspection work & equipment slide # 70
Number of reference areas
Size of structure(painted area)
m2
Recommended maximumNumber of reference areas
Recommended maximum percentage of reference area relative to total area of structure
Recommended maximum total area of reference areas
m2
< 2000 3 0,6 12
2000 to 5000 5 0,5 25
5000 to 10000 7 0,5 50
10000 to 25000 7 0,3 75
25000 to 50000 9 0,2 100
>50000 9 0,2 200