Alkali Silica Reactivity in Concrete
Rick Williams, P.G.
What Is ASR In Concrete?Alkali Silica Reactivity
First discovered in California in the 1930’s
Expansive gels form as alkaline fluids derived from the cement attack certain
reactive siliceous aggregates.
One of the leading causes of premature concrete failure.
2
Recipe For ASR- 3 Ingredients -
1. Alkali Ions
Na2O and K2O found in all cement in varying concentrations.
2. Silica
Reactive SiO2 primarily from amorphous or poorly crystallized siliceous aggregate.
3. Moisture
H2O
All Three Ingredients Must Be Present For Reaction To Initiate
3
Reaction
Equation:
SiO2 + 2NaOH → Na2SiO3 + H2O(Reactive Silica) (Alkali Hydroxide) (Alkali Silica Gel) (Water)
The ASR Process
In the presence of moisture, an alkali hydroxide solution can form.
As the solution migrates, the hydroxides begin attacking the Si-O-Si bonds of reactive siliceous aggregates.
The result is the formation of an expansive alkali-silica gel within the concrete structure.
4
Potentially Reactive Aggregates
Chert
Opal
Flint
Quartzite
Volcanic glass
Strained quartz
Quartz-Arenite
Ordered “Non Reactive” Silica Vs. Disordered “Reactive” Silica
Si
O
OH–
Na+
In the case of non-reactive quartz, the alkali ions cannot penetrate the well-ordered crystal lattice.
5
The Term Alkali-silica Reaction Is Somewhat Misleading
The reaction itself is actually between the OH-ions in the pore solution and certain siliceous components of the aggregates.
The alkalies, specifically sodium and potassium, do not actually attack the reactive silica.
Importance of Alkalis to ASR The importance of the alkalies is that their
presence in high concentrations in the pore solution results in an equally high concentration of OH- ions (to maintain charge equilibrium).
It is this high OH- concentration, and thus high pH, that leads to the initial breakdown of reactive silica components in the aggregates.
The alkalies also ultimately contribute to the expansive ASR gel formation.
6
Why Is ASR So Destructive?
Reaction products (Expansive Gel)resulting from the interaction of Alkali
Hydroxide Ions and Siliceous Aggregate occupy more space than the original Silica Aggregate causing tensile forces to build within the concrete until
cracking occurs.
Worst Case Scenario
High Alkaline Cement >= 0.6% NaOe (NaO Equvialvent)
Reactive Aggregate Chert Chalcedony Opal
Humid Environment Bridge pier submerged in water Dam Site Area that floods; i.e. poor drainage Internal Humidity >= 85%
7
What Does ASR Look Like In The Field?
Map Cracking
8
Map Cracking
Map Cracking In 5 Year Old Bent Cap
9
Backscattered Electron Image
FRACTURE FILLED WITHASR GEL
REACTIVE AGGREGATE
ASR In Thin Section
ASR GEL
10
ASR In Polished Section
ASR In Thin Section
Reactive SiO2
Aggregate
ASR Gel
Cement
11
Test Methods For Predicting ASR Aimed At Aggregates
ASTM Test Methods
ASTM C1260
Mortar bar is immersed in a NaOH solution for 14 days. Expansion of more than .2% after 14 days indicates the aggregate is reactive.
ASTM C1293
Actual concrete specimen tested for 1 year. Expansion of more than .04% after 12 months indicates a reactive aggregate.
Mortar Bar Test
12
ASTM C1260
Pros:
Can be completed in 14 Days
If aggregate passes this test it is virtually assured to be non-reactive.
Cons: Very aggressive – High
NaOH concentration and high temperature.
Performed on Mortar bars –not concrete specimens
It is not uncommon for good aggregate to fail and be classified as reactive.
Many specifying agencies modify this ASTM Standard but use same expansion limits.
ASTM C1293
Pros:
Performed on actual concrete specimens
More representative of field conditions than C1260
Much less aggressive than C1260
Cons:
Takes 1 year to complete
13
Outdoor Exposure Site The University Of Texas At Austin
What Can Be Done To Prevent ASR?
Use low alkaline cement
Use non-reactive aggregate
Use of SCMs and Admixtures
Fly Ash (Class F) – Most widely used; Derived from the combustion of coal, Very Effective
Lithium – Effective before and after ASR has formed
Silica Fume
14
Fly Ash
Generated from the combustion of coal.
Fly ash replacement by mass of cement is an effective way to reduce expansion due to ASR.
The reaction can be slowed down to the point that it will prevent ASR for the design life of the pavement.
Lithium
Lithium forms a gel similar to ASR, however it is not expansive – Lithium Silicate.
Research has proven this to be an effective way to combat ASR before and after the reaction has initiated.
15
Benefits Of Admixtures And SCM’s
Permit the use of local, cost-effective aggregates.
Increase the life span of concrete structures.
If you see cracking like this…
16
……You Can Say:
1. “That’s A Result Of Alkali Silica Reactivity.”
2. “Alkali Silica Reactivity is driven by the attack of alkali hydroxides in the cement on certain reactive siliceous aggregates in the concrete.”
3. “Had the cement, aggregate and exposure condition been properly considered during the design phase, this might have been avoided.”