FAILURE ANALYSIS OF SAMSUNG NOTE 7 JANUARY 23, 2017
UL and the UL logo are trademarks of UL LLC 2017
Confidential 2
UL & THE SCIENCE OF BATTERY SAFETY
UL HAS DEEP KNOWLEDGE IN THE SCIENCE
OF LITHIUM-ION BATTERY SAFETY
Research staff includes scientists and engineers with backgrounds in material
science, electrochemistry, mechanical and electrical engineering
Research capabilities include failure forensic analysis, internal short circuit
(ISC) simulation, thermal electrochemical modeling, aging simulation and others
Prior research work includes US National Transportation Safety Board (NTSB)
investigation into safety of lithium-ion batteries on airplanes
Published 10+ standards on battery & energy storage technology safety
2
Confidential
All samples provided by Samsung
FIELD EVENT
SAMPLES ANALYSIS
Tear-down examination of 10 damaged Note 7 devices with COMPANY As
batteries to understand the failure mechanism and potential causes of
failure
Study battery failure mechanisms on 110 new COMPANY A batteries
under various abuse conditions to identify potential battery safety issues
PHASE 1
PHASE 2 BATTERY SAFETY
BOUNDARY CHARACTERIZATION
SCOPE OF PROJECT COMPANY A
3
4
Signs of internal short circuit (ISC) at the upper right corner of the cells from 6 damaged devices
Signs of ISC at the upper right corner of 4 swollen cells
MISSING
INSULATION
TAPE
INTERNAL SHORT CIRCUIT
PHASE 1 KEY FINDINGS COMPANY A
5
CT scan of 30 cells and disassembly of 20 cells found only minor anomalies such as small
void/bubble or uneven stress.
Samples show a similar pattern of deformation at upper corners. Upper right corner deformation
appears to be deeper than upper left.
Tear down analysis shows repeating deformation areas on separator at the corner locations.
REPEATED DEFORMATION PATTERNS CAN BE OBSERVED AT THE CORNERS OF THE SEPARATOR
PHASE 2 KEY FINDINGS COMPANY A
Confidential
I. There may be multiple contributing factors relating to battery assembly/manufacturing and
design that when combined led to the failure of the Note 7 in the field
A. Battery assembly/manufacturing:
Deformation at the upper corners
B. Battery design:
Thinner separator could lead to poorer protection and reduced tolerance to manufacturing defects
Higher energy density in general can exacerbate the severity of a battery failure
II. One major failure mechanism is likely:
A combination of deformation at the upper corners + thin separator + repeating mechanical stresses
due to cycling, causing higher possibility of separator damage leading to an ISC between aluminum and
copper foil at the corner
III. Additional investigation is needed to understand the root-cause of the deformations at the upper
corners 6
ASSESSMENT COMPANY A
Confidential
SCOPE OF PROJECT COMPANY B All samples provided by Samsung
FIELD EVENT
SAMPLES ANALYSIS
Tear-down examination of 10 damaged Note 7 devices with COMPANY Bs
batteries to understand the failure mechanism and potential causes of failure
Testing of 40 new Note 7 devices with COMPANY Bs batteries under various
conditions to determine whether the device contributes to battery failure
Study battery failure mechanisms on 354 new COMPANY B batteries under
various abuse conditions to identify potential battery safety issues
SYSTEM LEVEL
COMPATIBILITY CHARACTERIZATION
PHASE 1
PHASE 2
PHASE 3 BATTERY SAFETY BOUNDARY
CHARACTERIZATION
7
8
SIGNS OF
SHORT
CIRCUIT
PHASE 1 KEY FINDINGS COMPANY B
Signs of internal short circuit (ISC) at different locations
of the cells from 5 of the damaged devices
Signs of ISC at the tab locations of swollen cells
Missing insulation tape on the cathode of swollen cells
Sharp-edged protrusions on the tab welding spots
of swollen cells
MISSING
INSULATION
TAPE
CELLS WITH MISSING INSULATION TAPE A65: UNKNOWN
NORMAL CELL WITH
INSULATION TAPES
SHARP-EDGED
PROTRUSIONS
9
Note 7 components do not increase
the battery cell temperature to a level
higher than the specified threshold
Note 7 maximum current drain meets the specifications
provided by Samsung
The maximum charging current, the maximum temperatures
and the maximum cell voltage are within the specifications
with the standard adapter provided by Samsung
PHASE 2 KEY FINDINGS COMPANY B
10
The failure mode (ISC in winding edge) observed in field event
samples can be reproduced by ULs ISC or localized heat pad tests
Flaws were readily found from 3D CT scan of some samples
Tear-down analysis findings include:
Uneven charge status on multiple samples
Signs of internal short circuit
Poor alignment and inconsistent shape and
dimension of tabs and insulation tapes
Sharp edge protrusion of welding joints
PHASE 3 KEY FINDINGS COMPANY B
Confidential
I. No evidence of device-level compatibility issues that may have contributed to the failure of
the Note 7 in the field
II. There may be multiple contributing factors relating to production quality and battery design
that when combined led to the failure of the Note 7 in the field
A. Production quality:
Missing insulation tape on tab could result in higher possibility of ISC
Bigger protrusion of welding points in tab could lead to higher possibility of separator puncture
Misalignment of insulation tape and/or tab could bring more risk of ISC
B. Battery design:
Thinner separator could lead to poorer protection and reduced tolerance
to manufacturing defects
Higher energy density in general can exacerbate the severity of a battery failure
ASSESSMENT (1/2) COMPANY B
11
Confidential
III. One major failure mechanism for field incidents is likely:
The combination of (1) missing insulation tape + (2) sharp edged protrusions on tab + (3) thin
separator, all leading to a high possibility of an ISC between cathode tab and anode, subsequently
resulting in heating and fire
IV. Further analysis is needed to understand the root-cause of the damage to the
edge/corner of the battery which results in ISC at that location
ASSESSMENT (2/2) COMPANY B
12
LEARN MORE ABOUT ULS
BATTERY EXPERTISE AT :
UL.com/batteryscience
13
http://ul.com/batteryscience
Sajeev Jesudas
President, Consumer Business Unit, UL
Sajeev Jesudas leads ULs focus on product quality, performance,
security and safety for UL customers in the consumer, retail and
financial payment services industries globally. He joined UL in
2001 as President for Asia-Pacific operations and since then has
served in many leadership positions with increasing
responsibilities, including the role of Chief Operating Officer and
that of President, International Operations. Jesudas is the current
Chairman of the board of directors of the UL-CCIC joint venture
company in China, and sits on the board of more than 20 UL
affiliate companies globally.
Before joining UL, Jesudas worked in areas of sales and marketing
and general management with a leading global manufacturer of
electrical and electronic products for commercial, industrial, utility,
and telecommunications markets, where he also held senior
positions with Middle East and Asia Pacific regional responsibilities.
Jesudas holds a Bachelor of Science degree in Electrical
Engineering from the University of Kerala, India, and an MBA
degree from the University of Texas, Austin.
SPEAKER BIOGRAPHY
14
UL is a global independent safety science
company with more than a century of
expertise innovating safety solutions.
Dedicated to promoting safe, sustainable and
secure living and working environments, UL
helps safeguard people, products and places,
and builds trust in the the goods, solutions and
innovations of today and tomorrow.
15
THIRD PARTY RIGOR. PROVEN SCIENCE.
WORLD CLASS EXPERTISE.
YEARS 120
OF EXPERTISE
MARKETS 143 AROUND THE WORLD
OUR PEOPLE
North America
4,000+ People Asia Pacific
4,000+ People Africa, Europe,
Latin America,
Middle East
2,000+ People
180+ FACILITIES
12,000+ ASSOCIATES
16
EDUCATION /
TRAINING
INSPECTION
MARKETING CLAIM
VERIFICATION
CERTIFICATION
SOFTWARE
AUDITING /
ANALYTICS
TESTING
ADVISORY
SERVICES
UL EMPOWERS TRUST THROUGH:
17 21
top related