JS33: 2013
amaican Standard
Specification
for
ot
rolled
s teel bar s for the reinfor cement of conc rete
BURE U OF ST ND RDS J M IC
-
8/10/2019 JS 33 2013
2/14
JS33: 2013
Contents
Page
Foreword
Committee representation
Acknowledgement
Related documents
Spec i f i ca t ion
S ec t io n o n e C o n s t r u c t i o n
1
Scope
1
2
Definitions
1
3
General Requirements
2
4
Chemical Composition
2
5
Requirements for deformations
4
6
Measurements for deformations
4
7
Tensile Properties
5
8
Verification of testing machine
6
9
Bending properties
6
10
Test specimens
7
11 Sampling and testing 8
12
Retests
8
13
Permissible deviatian in mass
9
14
Finish
9
15
Marking and identification
9
16
Manufacturers certificate 9
17 Inspection
10
18
Defects revealed after deliverv 10
Tab les
2
1 Deformed bar designation numbers, nominal dimensions, unit masses and deformation
requirements
limits for manufacturers heat analysis of grade 400 steel
limits for purchasers product analysis of grade 400 steel
Tensile requirements
Bend test requirements
2
3
3
5
7
3
4
5
-
8/10/2019 JS 33 2013
3/14
Foreword
JS33: 2013
This standard is a revision of LS
33: 2005.
In this standard the steel b ars ar e size d a cc ord ing t o t he ir
nom inal diam eter and the sizes are designated by a number in accordance w ith the actual bar diam eter in
millimetres.
C hanges to this standard include: the addition of three bar sizes 28 m m.
30
mm and
35
mm and the
revision ofaverage spacing and average height detailed in table I: the Iabelling m a rk in g o f t he r eb ars as
specified in C lause 16.
The grades are identified by their m inim um yield strengths expressed in M Pa. A m axim um yield strength
lim it h as b een ad op ted.
This standard is intended to be com pulsory.
Com mittee representation
The revision of LS
33: 2005
for the Standards C ouncil, established under the Standards Act 1968, was
carried out under the supervision of the M etallurgy an d B uild in g M aterials C om mittee, which at the tim e
co mp rised th e fo llo win g p erso ns:
M r N orm an H orne. C hairm an
M r T rev or M ck en zie, T ec hn ic al S ec re ta ry
M r Howard Chin
M r A nd rew S tan ig ar
M r Eladio W alker
M r H ora ce W iltsh ire
M r A llain R ob in so n
M r J ose ph P atte rs on
M r Ray D ixon
M r E rro l M cC arth y
M r E ric A nto nio
M r B rian M atth ew s
M r E arl C ro ok s
Ac knowledgment
A re System s Ltd.
A re System s Ltd.
Jam aica Institution of Engineers
S pe ctru m S yste ms
Q ua lity D ea lers
Q ua lity D ea lers
Q u al it y D ea le rs
S te wa rt s H ar dw are
S cie ntific R es ea rc h C ou nc il
E
&
R Hardware Ltd.
T an k-W eld M etals Ltd.
Matthews & C lark e L td.
E stac Industrial Agencies
Ackrowledgrnent
is n a de to t he fo llow in g in sti tu tio ns f o r pe rmi ssion to reprodu ce n aterial fro m th e
f o ll ow ing documen t s:
Ca n ad ia n S ta nda rd s A s so c ia ti on
I n te rna ti onalOrgan iz a ti on f o r S t anda rd i za ti on
S tr uc tu ra l E ngi ne er s A s so c ia ti on o fCa li fo rn ia SEAOC
Re la te d do cument s
T his s ta nd ard m a ke s re fe re nc e t o th e fo llow in g:
A ST M A 70 6/A706M
CSA G30.
2 -M
I SO 6935 -2
Rec om m en ded lateral forc e requirements an d
co nm en tary - 4
th
edition
ASTM E4 Vol. 03.01
AW S DI.4/D I.4M
CSA G30. 18
I SO 6935 -2
S ta nd ard S pe ci f ca tio n for L ow -A llo y S teel D efo rn ed an d P lain B ars fo r Concrete
Reinforcement
S t anda rd P r ac ti ces f or F or ce V eri f ca ti on o fT estin g Machines
S tru ctu ra l W e ld in g C o de - Reinforcing Steel
C ar bo n s te el b ars fo r c on cre te r ein fo re em e nt
S te el fo r th e rein fo ree men t o f c on cre te P art 2 : R ibb ed b a rs
-
8/10/2019 JS 33 2013
4/14
33: 2013
SEAOC Recommended lateral force requirements and commentary - San Francisco:
Seismology Committee, Structural Engineers Association ofCaliforni a, 1996
-
8/10/2019 JS 33 2013
5/14
-
8/10/2019 JS 33 2013
6/14
-
8/10/2019 JS 33 2013
7/14
JS 33: 2013
commonly used include manganese, copper, nickel, chromium, molybdenum, vanadium, silicon,
columbium, titanium and zirconium.
4.2 The carbon equivalent shall be calculated using the chemical composition as shown in the
mill test report by the following formula:
C.E .
% C % Mn/6
% Cu/40
% NiJ20
% Cr/lO - %Mo/50 - % V/LO
i
where:
C.E. is the carbon equivalent
% C is the percentage carbon content
% Mn is the percentage manganese content
%Cu is the percentage copper content
% Ni is the percentage nickel content
% Cr is the percentage chromium content
% Mo is the percentage molybdenum content
% V is the percentage vanadium content.
4.2.1 For Grade 400 steel, in order to ensure adequate weldability, the heat analysis shall be
such as to provide a carbon equivalent not exceeding 0.55%.
The chemical composition as shown by the heat analysis shall be limited to the following
percentages:
Table 2: Limits for manuf
ac urer's heat analysis of grade 400 steel
Element Maximum
Carbon 0.30
Manganese
1.50
Phosph orous
0.035
Sulphur 0.045
Silicon
0.50
An analysis may be made by the purchaser from finished bars representing each heat of steel.
The chemical composition thus determined shall be limited to the following percentages:
Table 3: Limits for purcha
00er's product analvsis of grade 4
steel
Element
Maximum
Carbon
0.33
Manganese
1.56
Phosphorous
0.043
Sulphur
0.053
Silicon
0.55
4.2.2 For Grade 300 steel only, in order to ensure adequate weldability, the heat analysis shall
be such as to provide a carbon equivalent not exceeding 0.40. The carbon equivalent may be
calculated using the chemical composition as shown in the mill test report by the following
formula:
3
Comment [SS2]: Carbon
equiva1ent equation changed to
aligri with National Building Code
and ASTM Standard.
-
8/10/2019 JS 33 2013
8/14
JS33: 2013
C.E.
=
% C % Mn/6
The chemical composition as shown by the heat analysis shall be limited to a maximum of
0.05% phosphorus and 0.05% sulphur.
An analysis may be made by the purchaser from finished bars representing each heat of steel.
The phosphorus and sulphur content thus determined shall not exceed that specified above by
more than 25%.
5. Requirements for deformations
5.1 Deformations shall be spaced along the bar at substantially uniform distances. The
deformations on opposite sides of the bar shall be similar in size and shape.
5.2 The deformations shall be placed with respect to the axis of the bar so that the included angle
is not less than 45. Where the line of deformations forms an included angle with the axis of the
bar from 45 to 70 inclusive, the deformations shall alternately reverse in direction on each side,
or those on one side shall be reversed in direction from those on the opposite side. Where the line
of deformations is over 70, areversal in direction is not required.
5.3 The overall length of deformations shall be such that the gap between the extreme ends of the
deformations on opposite sides of the bar shall not exceed 12.5 of the nominal perimeter of the
bar. Where the ends terminate in a longitudinal rib, the width of the longitudinal rib shall be
considered the gap. Where more than two longitudinal ribs are involved, the total width of all
longitudinal ribs sh all not exceed 25% of the nominal perimeter of the bar. The nominal
perimeter of the bar shall be 3.14 (i.e. r) times the nominal diameter.
5.4 The spacing, height and gap of deformations shall conform to the requirements detailed in
table 1.
6. Measurements of deformations
6.1 The average spacing of deformations shall be determined by dividing a measured length of
the bar specimen by the number of individual deformations and fractional parts of deformations
on any one side of the bar specimen. A measured length of the bar specimen shall be considered
the distance from apoint on a deformation to a corresponding point on any other deformation on
the same side of the bar. Spacing measurements shall not be made over a bar area containing bar
marking symbols involving letters or numbers.
6.2 The average height of deformations shall be determined from measurements made on not less
than two typical deformations. Determinations shall be based on three measurements per
deformation, one at the centre of the overall length and the other two at the quarter points of the
overall length.
4
-
8/10/2019 JS 33 2013
9/14
JS 33: 2013
6.3 Insuffcient height, insuffcient circumferential coverage, or excessive spacing of
deformations shall not constitute cause for rejection unless it has been c1early established by
determinations on each lot tested that typical deformation height, gap, or spacing do not conform
to the requirements detailed in table
.
No rejections shall be made on the basis of measurements
iffewer than ten adjacent deformations on each side of the bar are measured.
7 Tensile properties
7.1 The yield strength and elongation of the two grades ofsteel complying with this standard and
represented by the test specimens shall conform to the requirements detailed in table 2.
The actual yield strength based on mill tests shall not exceed the minimum specified by more
than
25 MPa. Subsequent tests shall not exceed this value by more than an additional 20 MPa.
The tensile strength of any bar shall be at least 25% greater than the actual yield strength
measured in the tensile test.
Table 4. Tensile requirements
Grade 300
Grade 400
Yield strength
300 MPa (min)
400 MPa (min)
Elongation 011 200 mm gauge lengh for
Percent (min) Percent (min)
bar designation numbers.
6,8.9.5. LO.12
9
15. 16, 19.20 12 9
25.28 LO 8
30. 32. 35, 40 LO 7
7.2 Where the steel tested has a sharp-kneed or well defined type of yield point, the yield point
shall be determined at the option of the manufacturer by one of the following methods:
(a) Drop of the beam or halt in the gauge of the testing machine.
Applyan increasing load to the specimen at a uniform rate.
Keep the beam in balance by running out the poise at approximately a steady rate, when alever
and poise machine is used.
When the yield point of the material is reached, the increase of the load will stop, but run the
poise a trifle beyond the balance position, and the beam of the machine will drop for a brief but
appreciable interval of time. When a machine equipped with a load-indicating dial is used, there
is a halt or hesitation of the load indicating pointer corresponding to the drop of the beam.
Note the load at the 'drop of the beam' or the 'halt of the pointer' and record the corresponding
stress as the yield point.
(b) Autographic diagramme method
When a sharp-kneed stress-strain diagramme is obtained by an autographic recording device, the
stress corresponding to the top of the knee or the point at which the curve drops shall be recorded
as the yield point.
5
-
8/10/2019 JS 33 2013
10/14
JS33: 2013
7.3 When testing material for yield point and the test speeimens may not exhibit a well-defined
disproportionate deformation that eharaeterizes a yield point as measured by the drop of the
beam, halt of the pointer, or autographie diagramme method, a value equivalent to the yield point
in its praetieal signifieanee may be determined by one of the following methods and may be
reeorded as yield point:
(a) extension under load using dividers with a 200-mm gauge length.
The extension under load sh all be 1.0 mm and shall be determined by seribing on the speeimen a
200-mm gauge length, pivoting from a priek puneh mark. The yield load shall be reeorded when
the total gauge length under load beeomes 20
mm as measured by the dividers.
(b) extensometer
Attaeh a class C or better extensometer (see NOTE) to the specimen. When the load producing
an extension of 0.005 mm/mm (0.5%) is reached, the stress corresponding to this load shall be
recorded as the yield point.
NOTE. Automatic devices are available that determine the load at the specifed total extension without
plotting a stress-strain curve. Such devices may be used if accuracy for each has been demonstrated.
Multiplying calipers and other such devices are acceptable for use provided that aecuracy has been
demonstrated as equivalent to a class C extensometer.
8 Veritication oftesting machine
8.1 The testing maehine used to deterrnine the properties specified in Clause 8 shall be verified at
least onee per year. The period of time elapsing between such verifications sh all not exceed 12
months.
8.2 The verifieation shall be eonducted bya source approved by the Bureau of Standards.
8.3 Where a testing machine has not been verified in aecordance with 9.1, or where such a
maehine does not meet the aeeuraey and reliability requirements of ASTM E4, the manufacturer
shall not certify any bars as conforming to the requirements of this standard.
9. Bending properties
9.1 Bend test requirements. The requirements for degree of bending and sizes of pins sh all be
as detailed in table 3.
6
-
8/10/2019 JS 33 2013
11/14
JS33: 2013
Table 5. Bend test requirements
Bar designation number Diameter of pin for bend tests
Grade 300 Grade 400
6.8.9.5.10.12.15,16
2d
4d
19.20 5d 5d
25.28 5d 6d
30 . 32. 35,40
5d 8d
where d nominal diarneter of specimen. Specimen is bent through 180.
9.2 Bend test procedures
9.2.
t
General
The bend test specimen shall stand being bent, when at ambient temperature but
in no case less than 16C, around a pin without cracking on the outside of the bent portion.
92 2 Apparatus The ben d shall be made on specimens of sufficient length to ensure free
bending and with apparatus which provide the following:
(a) continuous and uniform application of force throughout the duration of the bending
operation;
(b) unrestricted mavement of the specimen at points of contact with the apparatus and bending
around a pin free to rotate, or bending around a pin on a simple span with end supports free to
rotate;
(c) close wrapping of the specimen around the pin during the bending operation.
9 23 Other methods
Other methods of bend testing may be used, but failures due to such
methods shall not constitute abasis for rejection.
O.Test specimens
tO. Tension test specimens shall be of the full seetion of the bars as-rolled for sizes No. 6 to No.
32.
0.2 As an alternative to testing the full seetion of the bar as-rolled, tension test specimens for
bar sizes over No, 32 may, at the option of the manufacturer, be test ed by the reduced seetion
type of test indicated in
2, I.
10.2.1 Specimens shall be machined from the bar to a diameter of 28,65 mm (650 mrrr' cross-
section) over a length of not less than 225 mm, with fIlets at the ends of the turned-down seetion
having a radius of 13 mm and using a 200-mm gauge length. The reduced seetion may have a
gradual taper from the ends toward the centre, with the ends not more than 1% larger in diameter
than the centre (controlling dimension),
7
-
8/10/2019 JS 33 2013
12/14
JS33: 2013
1 3
The unit stress determinations on full size specimens shall be based on the nominal cross-
sectional areas shown in table 1. For reduced seetion specimens, the yield strength and tensile
strength results shall be corrected by the ratio of as-rolled bar mass to nominal bar mass.
1 4
The bend test specimens shall be the full seetion of the bar as-rolled.
i Sampling and testing
For the purpose of verifcation testing by the Bureau of Standards or other third party, the
delivery shall be sub-divided into test units with a maximum mass of 50 t or a fraction thereof.
Each test unit shall consist of products of the same steel grade and the same nominal diameter
from the same heat or east.
2
One sample of suffcient length shall be taken from each test unit for the following tests:
(a) one tensile test
(b) one bend test
(c) dimensional verifcations
(d) chemical composition tests (product analysis)
13
When a test specimen develops a tlaw due to failure of the testing equipment or improper
specimen preparation, it shall be discarded, and another specimen of the same bar size and grade
and from the same heat or east shall be substituted.
2 Retests
2 Ifany tensile property ofany tension test specimen is less or greater than that specified, and
any part of the fracture is outside the middle third of the gauge length, as indicated by seribe
scratches marked on the specimen before testing, aretest shalI be allowed.
2 2 If the results ofan original tension specimen fail to meet the specifed requirements and are
within 14 MPa of the required tensile strength, within 7 MPa of the required yield point, or
within two percentage units of the required elongation, aretest shall be permitted on two random
specimens for each original tension specimen failure from the lot. If all results of these retest
specimens meet the specifed requirements, the lot shall be accepted.
2 3
If a bend test specimen fails for reasons other than mechanical failure or tlaws in the
specimen as deseribed in 13.4 and 13.5, aretest shall be permitted on two random specimens
from the same lot. The lot shall be accepted only if the results of both retest specimens meet the
specifed requirements. The retest shall be performed on specimens that are at air temperature
but not less than 16C.
12 4
Where a test specimen fails for mechanical reasons such as failure oftesting equipment or
improper specimen preparation, it shall be discarded and another specimen taken.
8
-
8/10/2019 JS 33 2013
13/14
JS33: 2013
12.5 When a test specimen develops a flaw due to failure of the testing equipment or improper
specimen preparation, and is discarded, another specimen of the same bar size and grade and
from the same heat or east shall be substituted.
13. Permissible deviation in mass
Permissible deviation in mass per unit length shall not exceed the limits detailed in table i.
14. Finish
14.1 The bars shall be free from detrimental surface imperfections.
14.2 Rust, seams, surface irregularities, or mill scale shall not be cause for rejection, provided the
mass, dimensions, cross-sectional area and tensile properties of a test specimen cleaned to base
metal by hand wire-brushing or other Ceaning method are not less than the requirements of this
standard.
14.3 Surface imperfections other than those specifed in 15.2 shall be considered detrimental
when specimens containing such imperfections fail to conform to either tensile or bending
requirements.
15. Marking and identification
15.1 Marking of bars. All bars produced to this specifcation, shall be identifed by a
distinguishing set of marks legibly rolled onto the surface of one side of the bar to denote in the
following order, such that each commercial length supplied by the manufacturer shall have at
least one such set of marks:
(a) point of origin - letter or symbol established as the producer's mill designation.
(b) size designation - number corresponding to the bar designation number in table i.
(c) grade ofsteel - number to identify the grade ofany bar. The manufacturer shall
use the following for:
. Grade 300 bars: 300
2. Grade 400 bars: 400
Adequate space should be allowed in-between each of these marks to permit easy differentiation.
If necessary, where the transverse ribs intersect the marks the ribs may be omitted.
15.2 Marking of bundles. Each bundle of bars shall have a durable tag stating the manufacturer,
the number of this Jamaican Standard (lS 33), the grade of steel, the nominal diameter, east or
heat number and country of origin.
16. Manufacturer's certificate
16.1 No bars intended for the reinforcement of concrete shall be dispatched from the
manufacturer's works until tested and certifed to comply with the requirements of this standard.
9
-
8/10/2019 JS 33 2013
14/14
JS33: 2013
16.2 The manufacturer 's certificate relating to each bundIe shall be traceable through the heat
number.
16.3 The manufacturer's certificate shall state the process of manufacture, the chemical
composition, the carbon equivalent and the mechanical properties (as specified in Clause 3,
Clause 4, Clause 8 and Clause
O) applicable to each heat from which the bars purchased is
derived.
16.4 The purchaser shall be provided with a copy of the manufacturer's certificate(s) for each
delivery of bars from the manufacturer's works. When the bars are purchased from a supplier, a
copy of the manufacturer's certificate shall be provided by the supplier on request.
16.5 The manufacturer shall retain records of the unit masses, chemical composition, carbon
equivalent and mechanical properties of the bars made from each heat of steel. These records
shall be capable of being identified with the relevant bundles said.
17. Inspection
An independent inspector approved by the Bureau of Standards shall have free entry to all parts
of the manufacturer's works that concern the manufacture of the material ordered at all times
while work on the contract of the purchaser is being performed. The manufacturer shall afford
the inspector all reasonable facilities to satisfy him that the material is being furrished in
accordance with this standard. All tests (except product analysis) and inspection shall be made at
the place of manufacture prior to shipment, unless otherwise specified, and shall be so conducted
as not to interfere unnecessari Iywith the operation of the works.
18. Defects revealed after delivery
18.1 Should any material after delivery be found not to be in accordance with this standard, such
material shall be deemed not to comply with this standard, notwithstanding any previous
acceptance, provided that it has not been improperly treated.
18.2 Samples tested that represent rejected material shall be preserved for two weeks from the
date the rejection s reported to the manufacturer. In case of dissatisfaction with the results of the
tests, the manufacturer may make claim for a re-hearing within that time.
10