• Every day in the history of dentistry ..some one some were is coming up with a newer material.
• There are several inventions..some experiments and some modifications occurring on dental materials …just to get a perfect material
![Page 3: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/3.jpg)
• But…its said that if u want to beat a perfect thing …than not only u have to be perfect…it requires more than that…
![Page 4: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/4.jpg)
COMPOSITE RESIN
Presented by Dr.Rajesh jain
LETS DISCUSS ON
![Page 5: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/5.jpg)
CONTENT
• INTRODUCTION• HISTORY• USES• CLASSIFICATION• COMPOSITION
![Page 6: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/6.jpg)
INTRODUCTION
•They are highly crosslinked polymeric materials reinforced by a dispersion of glass,crystalline or resin filler particles or short fibres bound to the matrix by silane coupling agents.
•It may be defined as a system composed of a mixture of two or more macromolecule which are essentially insoluble in each other and differ in form .
![Page 7: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/7.jpg)
History
• In 1962 Dr. Ray Bowen developed a new type of material known as composite resin. The main innovation was a resin matrix of Bisphenol-A-Glycidyl Methacrylate (Bis-GMA) and a fillers agents. (silica,quartz,glass).
Dr. Ray Bowen
![Page 8: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/8.jpg)
Composite restorative materials
Uses-
Restoration of anterior and posterior teeth
Used as a veneers material.
To bulid up cores
Cementation of orthodontic brackets,maryland bridges,ceramic crowns,inlays ,onlays,laminates
Pit and fissure sealants
Repair of chipped porcelain restorations
![Page 9: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/9.jpg)
classification
1.Based on polymerization method• Self cured.• light cured,UV light cured ,Visible light cured• Dual light cured.
• 2. According to Anusavice (Phillips)Based on size of filler particles-• Conventional 8-12 um• Small particle 1-5 um• Microfilled 0.04-0.4 um• Hybrid 0.6-1.0 um
![Page 10: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/10.jpg)
3.Acco. To Marzoak 6 generations of composites:-
•First generation of composite•Second generation of composite•Third generation of composite•Fourth generation of composite•Fifth generation of composite•Sixth generation of composite
4. Based on matrix composition
Bis-GMAUDMABis-EMATEGDMA
Other resin
![Page 11: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/11.jpg)
5) Based on Radiopacity
•Radiopaque Glasses with barium, strontium, or lithium Ytterbium fluoride (YF3) •Not radiopaque
•2 paste system -base & reactor. Chemically activated•Single paste & liquid -chemically cured.•Single paste system -supplied in syringes. Light activated.•Disposable capsules -compomers
6 ) Based on mode of supply :
![Page 12: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/12.jpg)
7)According to Graham J. Mount; W.R. Hume :
T ype 1 - Macrofilled composite resinT ype 2 - Microfilled composites resinType 3 – hybrid composite resin
8)Based on viscosity Flowable composites. Medium viscosity composites. Packable composites
9).Classification based on area used Anterior composite Posterior composite
![Page 13: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/13.jpg)
10). Classification according to Bayne and Heyman:
•Megafill-1-2µm
•Macrofill-10-100µm
•Midifill-1-10µm
•Minifill-.01-.1µm.
•Microfill -0.04-0.4µm
•Nanofill-.005-.01µm
![Page 14: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/14.jpg)
Midi - filler -
2 um
( beachball)
Mini - filler -
0.1 um
( canteloupe)
Nanofiller -
.02 um (pea)
Microfiller -
.04 um
(marble)
Relative Particle Sizes (not to scale)
![Page 15: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/15.jpg)
Composition
RESIN MATRIX FILLER PARTICLES COUPLING AGENT
THEY ALSO CONTAIN: HYDROQUINONE U.V ABSORBER OPACIFIER COLOUR PIGMENT
![Page 16: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/16.jpg)
Resin matrix
• BIS-GMA resin is the base for composite. Diluents are added to increase flow and handling characteristics or provide cross linking for improved strength. Common examples are:
• RESIN:- BIS-GMA bisphenol glycidylmethacrylate
• DILUENTS:- MMA methylmethacrylateBIS-DMA bisphenol dimethacrylateUDMA urethane dimethacrylate
• CROSS LINK DILUENTSTEGDMA triethylene glycol dimethacrylateEGDMA ethylene glycol dimethacrylate
![Page 17: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/17.jpg)
FILLERS
•Silica particles •Quartz •Glass ( Ba, Sr, Zr)
If the composite is made up of the resin matrix AND fillers, it is called Filled Resin
![Page 18: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/18.jpg)
(1) reinforcement of the matrix resin, resulting in increased hardness, strength, and decreased wear
(2) reduction in polymerization shrinkage
(3) reduction in thermal expansion and contraction
(4) improved workability by increasing viscosity
(5) reduction in water sorption, softening, and staining
(6) increased radiopacity
Benefits of fillers-
![Page 19: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/19.jpg)
• Ground quartz- Makes restoration difficult to polish and cause
abrasion of opposing teeth and restorations
• Colloidal silica— Used in microfilled composites Thicken the resin
• Glasses of ceramic containing heavy metals Radiopacity eg.Barium
Types of fillers used-
![Page 20: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/20.jpg)
Coupling Agent
• Chemical bond– filler particle - resin matrix
• transfers stresses
• Organosilane (bifunctional molecule)– siloxane end bonds to hydroxyl groups on filler– methacrylate end polymerizes with resin
CH3-C-C-O-CH2-CH2-CH2-Si-OH
CH2
O OH
OH
Bonds with filler
Silane
Bis-GMABonds with resin
Phillip’s Science of Dental Materials 2003
![Page 21: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/21.jpg)
Inhibitors
• Prevents spontaneous polymer formation– heat– light
• Extends shelf life• Butylated Hydroxytoluene
Phillip’s Science of Dental Materials 2003
![Page 22: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/22.jpg)
Pigments and UV Absorbers
• Pigments– metal oxides
• provide shading and opacity• titanium and aluminum oxides
• UV absorbers– prevent discoloration– acts like a “sunscreen”
• Benzophenone
Phillip’s Science of Dental Materials 2003
![Page 23: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/23.jpg)
Visible-Light Activation
• Camphorquinone– most common photoinitiator
• absorbs blue light– 400 - 500 nm range
• Initiator reacts with amine activator• Forms free radicals• Initiates addition polymerization
OCH2CHCH2O-C-C=CH2CH2=C-C-O-CH2CH-CH2O -C-
CH3 CH3
CH3
CH3OH OH
O O
Bis-GMA
![Page 24: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/24.jpg)
Polymerization mechanism
1. Chemically activated
2. Light-activated
![Page 25: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/25.jpg)
Two paste system
Base paste – benzoyl peroxide initiator
Catalyst paste– tertiary amine activator (N,N-dimethyl-p-toludine)
1.Chemically activated composite system
![Page 26: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/26.jpg)
• Earliest system---UV light activated system
• Limitations –
Limited penetration of light into resin
Lack of penetration through tooth structure
2.Light activated composite resins—
![Page 27: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/27.jpg)
Visible light activated system---
• Single paste system
• Photoinitiator – Camphoroquinone
• Amine accelerator – diethyl-amino-ethyl-methacrylate
![Page 28: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/28.jpg)
Types of lamps used for curing
LED lamps. Using a solid-state, electronic process, these light sources emit radiation only in the blue part of the visible spectrum between 440 and 480 nm
QTH lamps. QTH lamps have a quartz bulb with a tungsten filament that irradiates both LTV and white light that must be filtered to remove heat and all
wavelengths except those in the violet-blue range (400 to 500 nm).
![Page 29: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/29.jpg)
PAC lamps. PAC lamps use a xenon gas that is ionized to produce a plasma.
The high-intensity white light is filtered to remove heat and to allow blue light (400 to 500 nm) to be emitted.
Argon laser lamps- have the highest intensity and emit at a
single wave length.lamps currently avaialble emit 490 nm
![Page 30: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/30.jpg)
•Consists of 2 light curable pastes
Benzoperioxide and aromatic tertiary amine
•Light curing – promoted by amine/CQ combination •Chemical- amine/BPO interaction
APPLICATION: •Cementation of bulky ceramic inlays
Dual Cure
![Page 31: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/31.jpg)
High intensity curing
• High intensity lamps could provide savings in chair time.
• However high intensity, short exposure times cause accelerated rates of curing, which leads to substantial residual stress build up.
![Page 32: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/32.jpg)
Depth of cure and exposure time
• Light absorption and scattering in resin composites reduces the power density and degree of conversion (DC) with depth of penetration
• Intensity can be reduced by a factor of 10 to 100 in a 2-mm thick layer of composite which reduces monomer conversion to an accceptable level.
• The practical consequence is that curing depth is limited to 2- 3mm
• Light attenuation vary from one type of composite to other depending on opacity,filler size,filler concentration and pigment shade
![Page 33: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/33.jpg)
• Darker shades require long curing time
• When polymerising resin through tooth structure exposure time should be increased by a factor of 2 – 3 to compensate for reduction in light intensity
• For halogen lamps light intensity can decrease depending on quality and age of light source,orientation of light tip,distance between light tip and restoration and presence of contamination,such as composite residue on light tip
• Despite the many advantages of light cured resins,there is still need for chemically cured composites for eg chemicaly cured materials can be used with reliable results as luting agent under metallic restorations.
![Page 34: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/34.jpg)
Polymerization
• Initiation– production of reactive free radicals
• typically with light for restorative materials
• Propagation– hundreds of monomer units– polymer network– 50 – 60% degree of conversion
• Termination
Craig Restorative Dental Materials 2002
![Page 35: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/35.jpg)
C=C
C=C C=C
C=C C=CC=C C=C
C=C C=C
C=C C=C
C=C C=C
C=C C=C
C=C C=C
C=C
C=C
C=CC=
C
C=C
C=C
C=C
C=C C=CC=C C=C
C=C
C=C
polymerization
Ferracane
![Page 36: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/36.jpg)
Degree of conversion
• DC is a measure of percentage of carbon-carbon double bonds that have been converted to single bonds to form polymeric resin
• The higher the DC the better the strength,wear,resistance
• Conversion values of 50%-70% are achieved at room temperature for both types of curing system
![Page 37: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/37.jpg)
Polymerization Shrinkage
Composites exhibit shrinkage while hardening.
More common when the restoration has extended onto root surface results in gap formation.
Most imp regarding the effects of polymerization shrinkage is C-factor.
![Page 38: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/38.jpg)
C--FACTOR
The C-factor is the ratio of bonded (flow-inactive) to unbonded or free (flow-active) surfaces.
The ratio of the restorations bonded to unbonded ( free) surfaces.
C=BONDED WALLS/UNBONDED WALLS
![Page 39: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/39.jpg)
Higher the C-factor , greater is the potential for bond disruption from polymerization effects.
Class IV with C-factor 0.2 is at low risk compared to class I with C-factor 5 is at high risk.
![Page 40: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/40.jpg)
Incremental buildup and cavity configuration
• One technique is the attempt to reduce the so called C-factor(configuration factor) which is related to the cavity preparation geometry
• A layering technique in which restoration is built up in increments , reduces polymerization stress by minimising the Cfactor.
• Incremental technique overcomes both limited depth of cure and residual stress concentration.
![Page 41: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/41.jpg)
![Page 42: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/42.jpg)
Conventional / traditional /macrofilled composite
• Composition-
Ground quartz most commonly used filler
Average size : 8- 12 µm
Filler loading - 70-80 weight % or 50 – 60 vol %
![Page 43: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/43.jpg)
Properties
• Compressive strength- Four to five times greater than that of unfilled resins ( 250-300 Mpa)
• Tensile strength- Double than of unfilled acrylic resins (50 – 65 Mpa)
• Elastic modulus- Four to six times greater (8-15 Gpa)
• Hardness – Considerably greater (55 KHN) than that of unfilled resins
• Coefficient of thermal expansion- High filler –resin ratio reduces the CTE significantly.
![Page 44: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/44.jpg)
• Esthetics – Polishing result in rough surface
Selective wear of softer resin matrix
Tendency to stain
• Radiopacity –
Composites using quartz as filler are radioluscent Radiopacity less than dentin
![Page 45: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/45.jpg)
• Clinical considerations-
Polishing was difficult Poor resistance to occlusal wear
Tendency to discolor Rough surface tends to stain
Inferior for posterior restorations
![Page 46: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/46.jpg)
Microfilled composites
Developed to overcome surface roughness of conventional composites
Composition- Smoother surface is due to the incorporation of microfillers. Colloidal silica is used as the microfiller
200—300 times smaller than the average particle in traditional composites
Filler particles consists of pulverized composite filler particles
![Page 47: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/47.jpg)
Properties
• Inferior physical and mechanical properties to those of traditional composites
• 40 – 80 % of the restorative material is made up of resin
• Increased surface smoothness
• Areas of proximal contact- Tooth drifting
.
![Page 48: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/48.jpg)
Compressive strength- 250- 350 Mpa.Tensile strength- 30- 50 Mpa. Lowest among compositesHardness – 25- 30 KHN.Thermal Expansion Coefficient- highest among composite resins
![Page 49: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/49.jpg)
Clinical considerations
• Choice of restoration for anterior teeth.
• Greater potential for fracture in class 4 and class 2 restorations.
• Chipping occurs at margins.
![Page 50: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/50.jpg)
Small particle composite
• Introduced in an attempt to have good surface smoothness and to improve physical and mechanical properties of conventional composites.
Composition – Smaller size fillers used-
Colloidal silica - present in small amounts ( 5 wt % ) to adjust paste viscosity
Heavy metal glasses . Ground quartz also used
Filler content
65 – 70 vol % or 80 – 90 %
![Page 51: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/51.jpg)
Properties
• Due to higher filler content the best physical and mechanical properties are observed
• Compressive strength- Highest compressive strength (350 – 400 Mpa )
• Tensile strength- Double that of microfilled and 1.5 times greater than that of traditional
composites ( 75- 90 Mpa )
![Page 52: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/52.jpg)
• Hardness – Similar to conventional composites ( 50 – 60 KHN)
• Thermal expansion coefficient- Twice that of tooth structure
• Esthetics – Better surface smoothness than conventional because of small and highly
packed fillers
• Radiopacity – Composites containing heavy metal glasses as fillers are radio-opaque which is
an important property in restoration of posterior teeth
![Page 53: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/53.jpg)
Clinical considerations
• In stress bearing areas such as class 4 and class 2 restorations
• Resin of choice for aesthetic restoration of anterior teeth
• For restoring sub gingival areas
![Page 54: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/54.jpg)
Hybrid composite
• Developed in an effort to obtain even better surface smoothness than that provided by the small particle composite.
• Composition –
2 kinds of fillers- Colloidal silica –present in higher concentrations 10 – 20 wt
%
Heavy metal glasses – Constituting 75 % Average particle size 0.4 – 1.0 µm
![Page 55: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/55.jpg)
Properties
• Range between conventional and small particle• Superior to microfilled composites
• Compressive strength- Slightly less than that of small particle composite(300 – 350 Mpa )
• Tensile strength- Comparable to small particle (70 – 90 Mpa )
• Hardness – Similar to small particle ( 50 – 60 KHN )
![Page 56: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/56.jpg)
• Esthetics – Competitive with microfilled composite for anterior restoration
• Radiopacity – Presence of heavy metal glasses makes the hybrid more radio-opaque than enamel
![Page 57: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/57.jpg)
Clinical considerations
• Used for anterior restorations including class 4 because of its smooth surface and good strength
• Widely employed for stress bearing restorations
![Page 58: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/58.jpg)
Flowable composites
• Modification of SPF and Hybrid composites.
• Reduced filler level
• Clinical considerations-
Class 1 restorations in gingival areas.
Class 2 posterior restorations where acess is difficult.
Fissure sealants.
![Page 59: basic of composite resin](https://reader033.vdocument.in/reader033/viewer/2022051208/544cc6f1b1af9fcd3b8b488d/html5/thumbnails/59.jpg)
Composites for posterior restorations
• Amalgam choice of restoration for posterior teeth
• Mercury toxicity and increased esthetic demand.
• All types of composites except flowable composites
• Conservative cavity preparation
• Meticulous manipulation technique.