C05 - 1Virginia Tech
Effect of Resist Thickness
Resists usually do not have uniform thickness on the wafer– Edge bead: The build-up of resist along the
circumference of the wafer- There are edge bead removal systems
– Step coverage
Centrifugal ForceCentrifugal Force
C05 - 2Virginia Tech
Effect of Resist Thickness
The resist can be underexposed where it is thicker and overexposed where it is thinner– This can lead to linewidth variations
Light intensity varies with depth below the surface due to absorption
where is the optical absorption coefficient Thus, the resist near the surface is exposed first
– We have good fortune. There is a process called bleaching in which the exposed material becomes almost transparent
i.e., decreases after exposure to light- Therefore, more light goes to deeper layers
)exp()( 0 xIxI
C05 - 3Virginia Tech
C. A. Mack, “Absorption and exposure in positive photoresist”, Appl. Opt. C. A. Mack, “Absorption and exposure in positive photoresist”, Appl. Opt. 2727(23), Dec. 1, 1988, (23), Dec. 1, 1988, pp. 4913-4919.pp. 4913-4919.
exposedexposed = B and = B and unexposedunexposed = A+B = A+B
C05 - 4Virginia Tech
C05 - 5Virginia Tech
Photoresist Absorption
If the photoresist becomes transparent, and if the underlying surface is reflective, reflected light from the wafer will expose the photoresist in areas we do not want it to.
However, this leads to the possibility of standing waves (due to interference), with resultant waviness of the developed resist
We can solve this by putting an antireflective coating on the surface before spinning the photoresist increases process complexity
C05 - 6Virginia Tech
Standing Waves due to Reflections
C05 - 7Virginia Tech
Standing Waves Due to Reflections
http://www.lithoguru.com/scientist/lithobasics.htmlhttp://www.lithoguru.com/scientist/lithobasics.html
C05 - 8Virginia Tech
(a) (b) (c)
Diffusion during a post-exposure bake (PEB) is often used to reduce standing waves.
Photoresist profile simulations as a function of the PEB diffusion length: (a) 20nm, (b) 40nm, and (c) 60nm.
http://www.lithoguru.com/scientist/lithobasics.htmlhttp://www.lithoguru.com/scientist/lithobasics.html
Removal of Standing Wave Pattern
C05 - 9Virginia Tech
Mask Engineering
There are two ways to improve the quality of the image transferred to the photoresist– Optical Proximity Correction (OPC)– Phase Shift Masks (PSM)
We note that the lenses in projections systems are both finite and circular
Most features on the mask are square We lose the high frequency components of the
pattern We thus lose information about the
“squareness” of the corners
C05 - 10Virginia Tech
Mask Engineering
The effects are quite predictable We can correct them by adjusting feature
dimensions and shapes in the masks
C05 - 11Virginia Tech
Mask Engineering
C05 - 12Virginia Tech
Phase Shift Masks
In a projection system, the amplitudes of the diffracted light at the wafer add– Closely spaced lines interact; the intensity at the
wafer is smeared If we put a material of proper index of refraction on part
of the mask, we can retard some of the light and change its phase by 180 degrees– Properly done, the amplitudes interfere
The thickness of the PS layer is
n is the index of refraction of the phase shift material
12
nd
C05 - 13Virginia Tech
Phase Shift Masks (PSM)
Intensity Intensity pattern is pattern is barely barely sufficient sufficient to resolve to resolve the two the two patterns.patterns.
C05 - 14Virginia Tech
Scanning Projection Aligners
The wafer is simultaneously scanned, thus printing the mask on the wafer
Systems of the type shown on the next page are cost effective, but they must use 1:1 masks– The concept is that it is easier to correct for
aberrations in small regions than a large area– Integration of a focusing laser and vertical positioner
allowed adjustment of imaging plane to maximize resolution
– Technology became obsolete as wafer size increased and linewidths became smaller
C05 - 15Virginia Tech
Scanning Projection Printer
C05 - 16Virginia Tech
Step and Repeat Projection Systems
Steppers expose a limited portion of the wafer at a time– Features on the masks (reticules) are 4-5X
the size of the features exposed on the wafer Steppers also allow better alignment because
they align on the exposure field rather than for the entire wafer– Integration of a focusing laser and vertical
positionerLaser is also used to read information that is scribed on wafer prior to processing
C05 - 17Virginia Tech
Projections Systems
Key features of steppers include– Kohler illumination– Off-axis illumination
Kohler illumination focuses the light at the entrance pupil of a projection lens, rather than on the photoresist
This setup allows the projection lens to capture the diffracted light from any features on the mask
C05 - 18Virginia Tech
Kohler Illumination
C05 - 19Virginia Tech
Off-Axis Illumination
By changing the angle of incidence of the light on the mask, we also change the angle of the diffracted light– Although some of the diffracted light is lost
in this scheme, much of the higher order diffraction is captured
C05 - 20Virginia Tech
Off-Axis Illumination
C05 - 21Virginia Tech
Step and Scan Aligners
https://www.chiphistory.org/product_content/lm_asml_pas5500-400_step&scan_system_1990_intro.htm
C05 - 22Virginia Tech
Step and Scan
C05 - 23Virginia Tech
C05 - 24Virginia Tech
DNQ/Novolac Resist Process
Hexamethyldisilane (HMDS) is often used as an adhesion promoter– As a liquid, drops are deposited on the wafer and then
spread by spinning at 3000 – 6000 rpm for 30 s– Sometime HMDS is applied from the vapor
The surface chemistry is that the silane end of the molecule bonds with the Si while the other end bonds with the resist
Resist is then spun on immediately following HMDS
http://bmrc.berkeley.edu/courseware/ICMfg92/images/gif/spin-on.gif
C05 - 25Virginia Tech
DNQ/Novolac Resist Process
Prebake is usually done on a hot plate at 90—100oC– Infrared or microwave heating can also be used
This step:– Evaporates the last of the solvent
Solvent content in the photoresist film decreases from 25% to 5%
– Adhesion is improved because heat strengthens the bonds between the resist and HMDS
– Stresses in the resist caused by spinning are thermally relieved
The resist flows slightly
C05 - 26Virginia Tech
DNQ/Novolac Resist Process
Exposure times and source intensity are reciprocal—one can reduce exposure times with more intense sources
Exposure time is increase by increasing the bake temperature (due to decomposition of the PAC and thus decreased sensitivity)
The postexposure bake is often done before development because the PAC can diffuse and this will eliminate the standing wave pattern
The developer is a basic solution such as TMAH, NaOH, or KOH and is applied by immersion, or spraying
C05 - 27Virginia Tech
DNQ/Novolac Resist Process
Rinsing in H2O stops the development process The rate for developing depends strongly on
temperature, developer concentration, and the exposure and bake procedures– The chemistry is the dissolution of the carbolic acid
The final step is postbake (typically 10—30 min at 100—140 C)
This hardens the resist and improves etch resistance The resist flows a bit during the process, and all
remaining solvents are driven off
Many of the steps described above are done in a single system called a wafer track system
C05 - 28Virginia Tech
DNQ/Novolac Resist Process
A SITE system ESVG 86 track and coat system
C05 - 29Virginia Tech
Measurement Methods
Measurements are made to determine– Mask Features and defects– Resist Patterns– Etched Features– Alignment Accuracy (x-y-theta)
C05 - 30Virginia Tech
Measurement of Mask Features and Defects
Because almost all production now uses reducing steppers, a defect in a mask will produce a defect in every die– Therefore the mask must be “perfect”
Because of the complexity of the masks, the inspection must be fully automated– manual observation under a microscope is
not possible The process is illustrated in the next slide
C05 - 31Virginia Tech
Mask Inspection System
C05 - 32Virginia Tech
Measurement of Mask Features and Defects
Light is passed through the mask and collected by an image recognition system– Solid state detectors are used to collect the light– The information is compared against the database of
the mask design or with an identical mask The inspection process is more difficult if the mask
contains OPC (optical proximity correction) or is a PSM (phase shift mask)
Often, defects found in this process can be corrected– Lasers can burn off excess Cr– Adding Cr to clear areas is harder
Done using chemical vapor deposition
C05 - 33Virginia Tech
SEM Measurement
C05 - 34Virginia Tech
State-of-the-Art
Capable of exposing down to ~ 10nm – E-beam lithography– X-ray lithography– Extreme UV lithography
E-beam and EUV are performed under vacuum– Throughput is very slow
New resist families are required– Most are very difficult to remove after use
Research needed on mask material for x-ray and EUV– Glass absorbs– Thickness of metal needed to block x-rays is very
thick (20-50m)