chapter 7 - 1 issues to address... why are dislocations observed primarily in metals and alloys? how...
TRANSCRIPT
![Page 1: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/1.jpg)
Chapter 7 - 1
ISSUES TO ADDRESS...
• Why are dislocations observed primarily in metals and alloys?
• How are strength and dislocation motion related?
• How do we increase strength?
• How can heating change strength and other properties?
Chapter 7: Dislocations & Strengthening
Mechanisms
![Page 2: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/2.jpg)
Chapter 7 - 2
Dislocations & Materials Classes
• Covalent Ceramics (Si, diamond): Motion hard. -directional (angular) bonding
• Ionic Ceramics (NaCl): Motion hard. -need to avoid ++ and - - neighbors.
+ + + +
+++
+ + + +
- - -
----
- - -
• Metals: Disl. motion easier. -non-directional bonding -close-packed directions for slip. electron cloud ion cores
++
++
++++++++ + + + + +
+++++++
![Page 3: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/3.jpg)
Chapter 7 - 3
Dislocation Motion
Dislocations & plastic deformation• Cubic & hexagonal metals - plastic deformation by
plastic shear or slip where one plane of atoms slides over adjacent plane by defect motion (dislocations).
• If dislocations don't move, deformation doesn't occur!
Adapted from Fig. 7.1, Callister 7e.
![Page 4: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/4.jpg)
Chapter 7 - 4
Dislocation Motion
• Dislocation moves along slip plane in slip direction perpendicular to dislocation line
• Slip direction same direction as Burgers vector
Edge dislocation
Screw dislocation
Adapted from Fig. 7.2, Callister 7e.
![Page 5: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/5.jpg)
Chapter 7 - 5
Slip System– Slip plane - plane allowing easiest slippage
• Wide interplanar spacings - highest planar densities
– Slip direction - direction of movement - Highest linear densities
– FCC Slip occurs on {111} planes (close-packed) in <110> directions (close-packed)
=> total of 12 slip systems in FCC– in BCC & HCP other slip systems occur
Deformation Mechanisms
Adapted from Fig. 7.6, Callister 7e.
![Page 6: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/6.jpg)
Chapter 7 - 6
Stress and Dislocation Motion• Crystals slip due to a resolved shear stress, R. • Applied tension can produce such a stress.
slip plane
normal, ns
Resolved shear stress: R =Fs/As
slip
directi
on
AS
R
R
FS
slip
directi
on
Relation between and R
R =FS /AS
Fcos A/cos
F
FS
nS
AS
A
Applied tensile stress: = F/A
slip
directi
on
FA
F
coscosR
![Page 7: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/7.jpg)
Chapter 7 - 7
• Condition for dislocation motion: CRSS R
• Crystal orientation can make it easy or hard to move dislocation
10-4 GPa to 10-2 GPa
typically
coscosR
Critical Resolved Shear Stress
maximum at = = 45º
R = 0
=90°
R = /2=45°=45°
R = 0
=90°
![Page 8: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/8.jpg)
Chapter 7 - 8
Single Crystal Slip
Adapted from Fig. 7.8, Callister 7e.
Adapted from Fig. 7.9, Callister 7e.
![Page 9: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/9.jpg)
Chapter 7 - 9
Ex: Deformation of single crystal
So the applied stress of 6500 psi will not cause the crystal to yield.
cos cos 6500 psi
=35°
=60°
(6500 psi) (cos35)(cos60)
(6500 psi) (0.41)
2662 psi crss 3000 psi
crss = 3000 psi
a) Will the single crystal yield? b) If not, what stress is needed?
= 6500 psi
Adapted from Fig. 7.7, Callister 7e.
![Page 10: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/10.jpg)
Chapter 7 - 10
Ex: Deformation of single crystal
psi 732541.0
psi 3000
coscoscrss
y
What stress is necessary (i.e., what is the yield stress, y)?
)41.0(cos cos psi 3000crss yy
psi 7325 y
So for deformation to occur the applied stress must be greater than or equal to the yield stress
![Page 11: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/11.jpg)
Chapter 7 - 11
• Stronger - grain boundaries pin deformations
• Slip planes & directions (, ) change from one crystal to another.
• R will vary from one crystal to another.
• The crystal with the largest R yields first.
• Other (less favorably oriented) crystals yield later.
Adapted from Fig. 7.10, Callister 7e.(Fig. 7.10 is courtesy of C. Brady, National Bureau of Standards [now the National Institute of Standards and Technology, Gaithersburg, MD].)
Slip Motion in Polycrystals
300 m
![Page 12: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/12.jpg)
Chapter 7 - 12
• Can be induced by rolling a polycrystalline metal
- before rolling
235 m
- isotropic since grains are approx. spherical & randomly oriented.
- after rolling
- anisotropic since rolling affects grain orientation and shape.
rolling direction
Adapted from Fig. 7.11, Callister 7e. (Fig. 7.11 is from W.G. Moffatt, G.W. Pearsall, and J. Wulff, The Structure and Properties of Materials, Vol. I, Structure, p. 140, John Wiley and Sons, New York, 1964.)
Anisotropy in y
![Page 13: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/13.jpg)
Chapter 7 - 13
side view
1. Cylinder of Tantalum machined from a rolled plate:
rolli
ng d
irect
ion
2. Fire cylinder at a target.
• The noncircular end view shows anisotropic deformation of rolled material.
endview
3. Deformed cylinder
platethicknessdirection
Photos courtesyof G.T. Gray III,Los AlamosNational Labs. Used withpermission.
Anisotropy in Deformation
![Page 14: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/14.jpg)
Chapter 7 - 14
4 Strategies for Strengthening: 1: Reduce Grain Size
• Grain boundaries are barriers to slip.• Barrier "strength" increases with Increasing angle of misorientation.• Smaller grain size: more barriers to slip.
• Hall-Petch Equation: 21 /yoyield dk
Adapted from Fig. 7.14, Callister 7e.(Fig. 7.14 is from A Textbook of Materials Technology, by Van Vlack, Pearson Education, Inc., Upper Saddle River, NJ.)
![Page 15: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/15.jpg)
Chapter 7 - 15
• Impurity atoms distort the lattice & generate stress.• Stress can produce a barrier to dislocation motion.
4 Strategies for Strengthening: 2: Solid Solutions
• Smaller substitutional impurity
Impurity generates local stress at A and B that opposes dislocation motion to the right.
A
B
• Larger substitutional impurity
Impurity generates local stress at C and D that opposes dislocation motion to the right.
C
D
![Page 16: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/16.jpg)
Chapter 7 - 16
Stress Concentration at Dislocations
Adapted from Fig. 7.4, Callister 7e.
![Page 17: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/17.jpg)
Chapter 7 - 17
Strengthening by Alloying
• small impurities tend to concentrate at dislocations• reduce mobility of dislocation increase strength
Adapted from Fig. 7.17, Callister 7e.
![Page 18: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/18.jpg)
Chapter 7 - 18
Strengthening by alloying
• large impurities concentrate at dislocations on low density side
Adapted from Fig. 7.18, Callister 7e.
![Page 19: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/19.jpg)
Chapter 7 - 19
Ex: Solid SolutionStrengthening in Copper
• Tensile strength & yield strength increase with wt% Ni.
• Empirical relation:
• Alloying increases y and TS.
21 /y C~
Adapted from Fig. 7.16 (a) and (b), Callister 7e.
Ten
sile
str
engt
h (M
Pa)
wt.% Ni, (Concentration C)
200
300
400
0 10 20 30 40 50 Yie
ld s
tren
gth
(MP
a)wt.%Ni, (Concentration C)
60
120
180
0 10 20 30 40 50
![Page 20: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/20.jpg)
Chapter 7 - 20
• Hard precipitates are difficult to shear. Ex: Ceramics in metals (SiC in Iron or Aluminum).
• Result:S
~y
1
4 Strategies for Strengthening: 3: Precipitation Strengthening
Large shear stress needed to move dislocation toward precipitate and shear it.
Dislocation “advances” but precipitates act as “pinning” sites with
S.spacing
Side View
precipitate
Top View
Slipped part of slip plane
Unslipped part of slip plane
Sspacing
![Page 21: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/21.jpg)
Chapter 7 - 21
• Internal wing structure on Boeing 767
• Aluminum is strengthened with precipitates formed by alloying.
Adapted from Fig. 11.26, Callister 7e. (Fig. 11.26 is courtesy of G.H. Narayanan and A.G. Miller, Boeing Commercial Airplane Company.)
1.5m
Application: Precipitation Strengthening
Adapted from chapter-opening photograph, Chapter 11, Callister 5e. (courtesy of G.H. Narayanan and A.G. Miller, Boeing Commercial Airplane Company.)
![Page 22: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/22.jpg)
Chapter 7 - 22
4 Strategies for Strengthening: 4: Cold Work (%CW)
• Room temperature deformation.• Common forming operations change the cross sectional area:
Adapted from Fig. 11.8, Callister 7e.
-Forging
Ao Ad
force
dieblank
force-Drawing
tensile force
AoAddie
die
-Extrusion
ram billet
container
containerforce
die holder
die
Ao
Adextrusion
100 x %o
do
A
AACW
-Rolling
roll
AoAd
roll
![Page 23: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/23.jpg)
Chapter 7 - 23
• Ti alloy after cold working:
• Dislocations entangle with one another during cold work.• Dislocation motion becomes more difficult.
Adapted from Fig. 4.6, Callister 7e. (Fig. 4.6 is courtesy of M.R. Plichta, Michigan Technological University.)
Dislocations During Cold Work
0.9 m
![Page 24: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/24.jpg)
Chapter 7 - 24
Result of Cold Work
Dislocation density =
– Carefully grown single crystal
ca. 103 mm-2
– Deforming sample increases density
109-1010 mm-2
– Heat treatment reduces density
105-106 mm-2
• Yield stress increases as d increases:
total dislocation lengthunit volume
large hardening
small hardening
y0 y1
![Page 25: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/25.jpg)
Chapter 7 - 25
Effects of Stress at Dislocations
Adapted from Fig. 7.5, Callister 7e.
![Page 26: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/26.jpg)
Chapter 7 - 26
Impact of Cold Work
Adapted from Fig. 7.20, Callister 7e.
• Yield strength (y) increases.• Tensile strength (TS) increases.• Ductility (%EL or %AR) decreases.
As cold work is increased
![Page 27: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/27.jpg)
Chapter 7 - 27
• What is the tensile strength & ductility after cold working?
Adapted from Fig. 7.19, Callister 7e. (Fig. 7.19 is adapted from Metals Handbook: Properties and Selection: Iron and Steels, Vol. 1, 9th ed., B. Bardes (Ed.), American Society for Metals, 1978, p. 226; and Metals Handbook: Properties and Selection: Nonferrous Alloys and Pure Metals, Vol. 2, 9th ed., H. Baker (Managing Ed.), American Society for Metals, 1979, p. 276 and 327.)
%6.35100 x %2
22
o
do
r
rrCW
Cold Work Analysis
% Cold Work
100
300
500
700
Cu
200 40 60
yield strength (MPa)
y = 300MPa
300MPa
% Cold Work
tensile strength (MPa)
200Cu
0
400
600
800
20 40 60
ductility (%EL)
% Cold Work
20
40
60
20 40 6000
Cu
Do =15.2mm
Cold Work
Dd =12.2mm
Copper
340MPa
TS = 340MPa
7%
%EL = 7%
![Page 28: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/28.jpg)
Chapter 7 - 28
• Results for polycrystalline iron:
• y and TS decrease with increasing test temperature.• %EL increases with increasing test temperature.• Why? Vacancies help dislocations move past obstacles.
Adapted from Fig. 6.14, Callister 7e.
- Behavior vs. Temperature
2. vacancies replace atoms on the disl. half plane
3. disl. glides past obstacle
-200C
-100C
25C
800
600
400
200
0
Strain
Str
ess
(M
Pa)
0 0.1 0.2 0.3 0.4 0.5
1. disl. trapped by obstacle
obstacle
![Page 29: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/29.jpg)
Chapter 7 - 29
• 1 hour treatment at Tanneal... decreases TS and increases %EL.• Effects of cold work are reversed!
• 3 Annealing stages to discuss...
Adapted from Fig. 7.22, Callister 7e. (Fig.7.22 is adapted from G. Sachs and K.R. van Horn, Practical Metallurgy, Applied Metallurgy, and the Industrial Processing of Ferrous and Nonferrous Metals and Alloys, American Society for Metals, 1940, p. 139.)
Effect of Heating After %CW te
nsi
le s
tre
ngth
(M
Pa)
duc
tility
(%
EL
)tensile strength
ductility
Recovery
Recrystallization
Grain Growth
600
300
400
500
60
50
40
30
20
annealing temperature (ºC)200100 300 400 500 600 700
![Page 30: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/30.jpg)
Chapter 7 - 30
Annihilation reduces dislocation density.
Recovery
• Scenario 1Results from diffusion
• Scenario 2
4. opposite dislocations
meet and annihilate
Dislocations annihilate and form a perfect atomic plane.
extra half-plane of atoms
extra half-plane of atoms
atoms diffuse to regions of tension
2. grey atoms leave by vacancy diffusion allowing disl. to “climb”
R
1. dislocation blocked; can’t move to the right
Obstacle dislocation
3. “Climbed” disl. can now move on new slip plane
![Page 31: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/31.jpg)
Chapter 7 - 31
• New grains are formed that: -- have a small dislocation density -- are small -- consume cold-worked grains.
Adapted from Fig. 7.21 (a),(b), Callister 7e. (Fig. 7.21 (a),(b) are courtesy of J.E. Burke, General Electric Company.)
33% coldworkedbrass
New crystalsnucleate after3 sec. at 580C.
0.6 mm 0.6 mm
Recrystallization
![Page 32: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/32.jpg)
Chapter 7 - 32
• All cold-worked grains are consumed.
Adapted from Fig. 7.21 (c),(d), Callister 7e. (Fig. 7.21 (c),(d) are courtesy of J.E. Burke, General Electric Company.)
After 4seconds
After 8seconds
0.6 mm0.6 mm
Further Recrystallization
![Page 33: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/33.jpg)
Chapter 7 - 33
• At longer times, larger grains consume smaller ones. • Why? Grain boundary area (and therefore energy) is reduced.
After 8 s,580ºC
After 15 min,580ºC
0.6 mm 0.6 mm
Adapted from Fig. 7.21 (d),(e), Callister 7e. (Fig. 7.21 (d),(e) are courtesy of J.E. Burke, General Electric Company.)
Grain Growth
• Empirical Relation:
Ktdd no
n elapsed time
coefficient dependenton material and T.
grain diam.at time t.
exponent typ. ~ 2
Ostwald Ripening
![Page 34: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/34.jpg)
Chapter 7 - 34
TR
Adapted from Fig. 7.22, Callister 7e.
º
º
TR = recrystallization temperature
![Page 35: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/35.jpg)
Chapter 7 - 35
Recrystallization Temperature, TR
TR = recrystallization temperature = point of highest rate of property change1. Tm => TR 0.3-0.6 Tm (K)
2. Due to diffusion annealing time TR = f(t) shorter annealing time => higher TR
3. Higher %CW => lower TR – strain hardening
4. Pure metals lower TR due to dislocation movements
• Easier to move in pure metals => lower TR
![Page 36: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/36.jpg)
Chapter 7 - 36
Coldwork Calculations
A cylindrical rod of brass originally 0.40 in (10.2 mm) in diameter is to be cold worked by drawing. The circular cross section will be maintained during deformation. A cold-worked tensile strength in excess of 55,000 psi (380 MPa) and a ductility of at least 15 %EL are desired. Further more, the final diameter must be 0.30 in (7.6 mm). Explain how this may be accomplished.
![Page 37: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/37.jpg)
Chapter 7 - 37
Coldwork Calculations Solution
If we directly draw to the final diameter what happens?
%843100 x 400
3001100 x
4
41
100 1100 x %
2
2
2
..
.
D
D
xA
A
A
AACW
o
f
o
f
o
fo
Do = 0.40 in
BrassCold Work
Df = 0.30 in
![Page 38: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/38.jpg)
Chapter 7 - 38
Coldwork Calc Solution: Cont.
• For %CW = 43.8%Adapted from Fig. 7.19, Callister 7e.
540420
y = 420 MPa– TS = 540 MPa > 380 MPa
6
– %EL = 6 < 15• This doesn’t satisfy criteria…… what can we do?
![Page 39: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/39.jpg)
Chapter 7 - 39
Coldwork Calc Solution: Cont.
Adapted from Fig. 7.19, Callister 7e.
380
12
15
27
For %EL < 15
For TS > 380 MPa > 12 %CW
< 27 %CW
our working range is limited to %CW = 12-27
![Page 40: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/40.jpg)
Chapter 7 - 40
Coldwork Calc Soln: RecrystallizationCold draw-anneal-cold draw again• For objective we need a cold work of %CW 12-27
– We’ll use %CW = 20• Diameter after first cold draw (before 2nd cold draw)?
– must be calculated as follows:
100
%1 100 1% 2
02
22
202
22 CW
D
Dx
D
DCW ff
50
02
2
100
%1
.
f CW
D
D
50
202
100%
1.
f
CW
DD
m 335010020
130050
021 ..DD.
f
Intermediate diameter =
![Page 41: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/41.jpg)
Chapter 7 - 41
Coldwork Calculations Solution
Summary:
1. Cold work D01= 0.40 in Df1 = 0.335 m
2. Anneal above D02 = Df1
3. Cold work D02= 0.335 in Df 2 =0.30 m
Therefore, meets all requirements
20100 3350
301%
2
2
x
.
.CW
24%
MPa 400
MPa 340
EL
TSy
%CW1 10.335
0.4
2
x 100 30
Fig 7.19
![Page 42: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/42.jpg)
Chapter 7 - 42
Rate of Recrystallization
• Hot work above TR
• Cold work below TR
• Smaller grains – stronger at low temperature– weaker at high temperature
t/RT
BCt
kT
ERtR
1:note
log
logloglog 0
RT1
log t
start
finish
50%
![Page 43: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/43.jpg)
Chapter 7 - 43
• Dislocations are observed primarily in metals and alloys.
• Strength is increased by making dislocation motion difficult.
• Particular ways to increase strength are to: --decrease grain size --solid solution strengthening --precipitate strengthening --cold work
• Heating (annealing) can reduce dislocation density and increase grain size. This decreases the strength.
Summary
![Page 44: Chapter 7 - 1 ISSUES TO ADDRESS... Why are dislocations observed primarily in metals and alloys? How are strength and dislocation motion related? How do](https://reader037.vdocument.in/reader037/viewer/2022102818/56649e3f5503460f94b308e3/html5/thumbnails/44.jpg)
Chapter 7 - 44
Core Problems:
Self-help Problems:
ANNOUNCEMENTS
Reading: