CHAPTER SEVENCASTING PROCESSES

Page 2: CHAPTER SEVEN CASTING PROCESSES

INTRODUNCTIONCasting process is one of the earliest metal

shaping techniques known to human being. Casting process consists of pouring molten metal into a refractory mold cavity and allows it to solidify. The mold cavity needs to retain its shape until the metal has solidified and the casting is removed from the mold.

Page 3: CHAPTER SEVEN CASTING PROCESSES

pattern making Patterns are made to produce the proper

sizes and shapes of cavities in the sand molds. Except for some very simple shapes, usually those that are circular, a pattern is necessary if the mold cavity is to have the correct shape and dimensions. Patterns are typically made from wood, plaster, plastics, various metals, and, for lost foam castings, from polystyrene foam. For investment castings, patterns are made from wax or plastics.

Page 4: CHAPTER SEVEN CASTING PROCESSES

PATTERN ALLOWANCESThe dimensions of the pattern are different

from the final dimensions of the casting required. This is required because of various reasons. These are detailed as follows.

ShrinkageDraft

Page 5: CHAPTER SEVEN CASTING PROCESSES

Casting processesOne way of classifying casting is according to

the material used in making mold.Sand casting 3- Continuous CastingDie casting 4- Investment castingCentrifugal casting

Page 6: CHAPTER SEVEN CASTING PROCESSES

Sand castingSilica sand is the principal basic molding

material used by foundry man, whether for iron, steel and for nonferrous castings. Casting produced in silica sand are commonly known as sand castings.

Page 7: CHAPTER SEVEN CASTING PROCESSES

Sand casting

Page 8: CHAPTER SEVEN CASTING PROCESSES

Properties of Moulding Sand 1.Porosity or permeabilityPlasticityAdhesivenessCohesivenessRefractorinessCollapsibility

Page 9: CHAPTER SEVEN CASTING PROCESSES

CORE AND CORE BOXA core may be defined as a preformed

mass of bonded sand that is used to make the internal configuration of a casting.

Page 10: CHAPTER SEVEN CASTING PROCESSES

SAND TESTINGGenerally the following tests are performed to judge the

molding and casting characteristics of foundry sands:1. Moisture content Test 2. Clay content Test3. Chemical composition of sand4. Grain shape and

surface texture of sand.5. Grain size distribution of sand 6. Specific surface

of sand grains7. Water absorption capacity of sand 8. Refractoriness

of sand9. Strength Test10. Permeability Test11. Flowability Test 12. Shatter index Test13. Mould hardness Test.

Page 11: CHAPTER SEVEN CASTING PROCESSES

GATING SYSTEM IN MOLD

Page 12: CHAPTER SEVEN CASTING PROCESSES

FACTORS CONTROLING GATING DESIGNSharp corners and abrupt changes in at any section

or portion in gating system should be avoided for suppressing turbulence and gas entrapment.

(ii) The most important characteristics of gating system besides sprue are the shape, location and dimensions of runners and type of flow. It is also important to determine the position at which the molten metal enters the mould cavity.

(iii) Gating ratio should reveal that the total cross-section of sprue, runner and gate decreases towards the mold cavity which provides a choke effect.

Page 13: CHAPTER SEVEN CASTING PROCESSES

FACTORS CONTROLING GATING DESIGN(iv) Bending of runner if any should be kept

away from mold cavity.(v) Developing the various cross sections of

gating system to nullify the effect of turbulence or momentum of molten metal.

(vi) Streamlining or removing sharp corners at any junctions by providing generous radius, tapering the sprue, providing radius at sprue

Page 14: CHAPTER SEVEN CASTING PROCESSES

FACTORS CONTROLING GATING DESIGN

Page 15: CHAPTER SEVEN CASTING PROCESSES

PERMANENT MOLD OR GRAVITY DIE CASTINGThis process is commonly known as

permanent mold casting in U.S.A and gravity die casting in England. A permanent mold casting makes use of a mold or metallic die which is permanent. A typical permanent mold is shown in Fig. Molten metal is poured into the mold under gravity only and no external pressure is applied to force the liquid metal into the mold cavity.

Page 16: CHAPTER SEVEN CASTING PROCESSES

A typical permanent mold

Page 17: CHAPTER SEVEN CASTING PROCESSES

CENTRIFUGAL CASTINGIn centrifugal casting process, molten

metal is poured into a revolving mold and allowed to solidify molten metal by pressure of centrifugal force.

Page 18: CHAPTER SEVEN CASTING PROCESSES

CONTINNOUS CASTINGIn this process the molten metal is

continuously poured in to a mold cavity around which a facility for quick cooling the molten metal to the point of solidification.

Page 19: CHAPTER SEVEN CASTING PROCESSES

Investment Casting (Lost Wax Process)This process uses a one-piece mold made of

ceramic material, the same material that is used in ceramic casting. The mold is made by surrounding an expendable wax or plastic pattern with the ceramic material in slurry form. When the mold material solidifies it is heated and the wax or plastic replica of the part is melted out, leaving a cavity corresponding to the shape of the desired part. The mold is baked to remove all residues of the pattern and to fuse the ceramic. Molten metal is poured into this cavity. When the metal solidifies, the ceramic mold is broken free and removed from the casting.