DESIGNING OF CRADLE-TO-CRADLE LOOPS

FOR ELASTOMER PRODUCTS

Wilma Dierkes, Kuno Dijkhuis, Siti Saiwari, Hans van Hoek,

Louis Reuvekamp, Jacques Noordermeer, Anke Blume

University of Twente

Elastomer Research Testing B.V.

Prince of Songkla University

2

OUTLOOK

INTRODUCTION

EPDM ROOF SHEETING

PROCESS DEVELOPMENT

AND APPLICATION

WHOLE PASSENGER CAR

TIRE RUBBER

LIMITATIONS

SUMMARY ACKNOWLEDGE-

MENTS

1. 2. 3. 4. 5. 6.

2

PROCESS DEVELOPMENT AND APPLICATION

3

IntroductionMaterial from end-of-life tires

http://global.yokohamatire.net/technology/tireknowledge/images/rawmaterials1.jpg

http://www.genan.eu/files/billeder/Tyres/tyre-mountain.gifETRMA: tire production, EU27, 2013

Tires in the EU annually = 4,670,000 tons

Raw materials needed for producing these tires(passenger cars, buses, light trucks):

Rubber: 50% = 2,380,000 tons

Filler (carbon black, silica): 26% = 1,167,500 tons

ZnO: 2% = 100,000 tons

Other ingredients: 4% = 280,200 tons

Steel and wire: 15% = 681,820 tons

Textile cord: 3% = 140,400 tons

3,838,740 tons

4

IntroductionWhat are the trends?

http://www.hankooktire.com/global/tires-services/technology/tire-labeling/overview/_jcr_content/par/image_0.img.jpg/1424738449507.jpg

http://www.tirereview.com/wp-content/uploads/Articles/02_01_2013/109978febcovera_00000060668.jpg

Legislation

R&D: Number of patents on…

Pri

ori

ty d

ate

Pri

ori

ty d

ate

USA Korea

Japan

EU

5

http://wdo.ca/Portals/_default/Skins/wdo/sliderimg/

usedtires.jpg

Cradle to Cradle

Cradle to …

IntroductionRecycling alternatives

http://tyrepyrolysisplants.net/wp-content/uploads/2015/04/usedtirespyrolysis.jpg

FINE GRINDING

6

� Technology Readiness Levels (TRL):- Passenger car tire rubber: TRL5-6 (technology demonstration) - Truck tire rubber: TRL 6-8 (system/subsystem development)

� Concentration of devulcanizate in tire compounds: a multitude of current concentrations (depending on the compound type)

‘Tires back into tires’: The only way to considerably broaden the market for recycled rubber

� Technology Readiness Levels (TRL):- No significant development potential of conventional technologies

(batch, long residence time, high temperatures) - Improvements by after-treatments- New technologies?

� Large-scale application in tires only possible with significant quality improvements

Pyrolysis

Grinding � Technology available, also for very fine powder� No further quality improvements possible� Very limited application in virgin compounds

Devulcanizate

IntroductionStatus of recycling alternatives

7

IntroductionDevulcanization versus reclamation

Crosslink scission �� properties of devulcanisate similar toproperties of original materialDEVULCANIZATION:

REGENERATION: Polymer scission �� shorter polymer chains

�� poor properties

8

Draft research program

Influence of devulcanization conditions:

� Concentration devulcanization aid

(hexadeclyamine)

� Temperature

� Rotor speed

� Time

Influence on

•Mooney viscosity

•Insoluble fraction

•Overall XLD

•Monosulfidic XLD

EPDM roof sheetingOptimization the devulcanization process

Thesis Kuno Dijkhuis,’Recycling of vulcanized EPDM rubber’, University of Twente, 2008

9




(hexadeclyamine)

� Temperature

� Rotor speed

� Time

Influence on

•Mooney viscosity


•Overall XLD

•Monosulfidic XLD



10




(hexadeclyamine)

� Temperature

� Rotor speed

� Time

Influence on

•Mooney viscosity


•Overall XLD

•Monosulfidic XLD



11




(hexadeclyamine)

� Temperature

� Rotor speed

� Time

Influence on

•Mooney viscosity


•Overall XLD

•Monosulfidic XLD



12


Mooney viscosity

Insoluble fraction

Overall

XLD

Mono-sulfidic

XLD

Concentration DA

� � � � �

Temperature � � � � �

Rotor speed � � � O O

Time � � � � �

Feed stockCrosslink density (××××10-4 mol/cm3)

Insoluble fraction(%)Overall Monosulfidic

Di- plus polysulfidic

Conventionally cured

2.39 0.36 (15%) 2.03 (85%) 75.1


13


Mooney viscosity

Insoluble fraction

Overall

XLD

Mono-sulfidic

XLD

Concentration DA

� � � � � � � � �

Temperature � � � � � � � � �

Rotor speed � � � � � O � O O

Time � � � � � � � � �

Feed stockCrosslink density (××××10-4 mol/cm3)

Insoluble fraction(%)Overall Monosulfidic

Di- plus polysulfidic

Conventionally cured

2.39 0.36 (15%) 2.03 (85%) 75.1

Efficiently cured

0.97 0.51 (52%) 0.46 (48%) 71.9

EPDM roof sheetingConventionally versus efficiently cured rubber

14



as

Currently implemented at

several roof sheeting companies

▲▲▲▲ 1% DA, 0.8-2.5 mm

●●●● 1% DA, 20-40mm

■■■■ no DA, 20-40mm

UEAtc: Union Européenne pour l'Agrément

technique dans la construction (1988)

EPDM roof sheetingApplication study

15

DEVULCANIZATION:

REGENERATION:

+sol

gel

sol

M. M. Horikx, J. Polym. Sci. 19, 445 (1956)

Devulcanization versus reclamationAnalytics

16

DEVULCANIZATION:

REGENERATION:

sol

γγγγf, γγγγi: average number of crosslinks per chain in the insoluble network after/ before reclamation

si: soluble fraction of the rubber network before reclaimingsf: soluble fraction of the reclaimed vulcanizatevi : crosslink density of the network prior to treatmentsi : crosslink density of the reclaimed vulcanizateM. M. Horikx, J. Polym. Sci. 19, 445 (1956)

Devulcanization versus reclamationHorikx Model

17

DE-VULCANIZATION OF TIRE RUBBERS

(a) TT: thermal treatment without exclusion of oxygen

S. Saiwari: Post-consumer tires back into new tires; thesis; University Twente, 2013

Passenger car tire rubber: SBRThermo-mechanical treatment

18


(a) TT: thermal treatment without exclusion of oxygen(b) TL: thermal treatment and quenching in liquid nitrogen after treatment



19


(a) TT: thermal treatment without exclusion of oxygen(b) TL: thermal treatment and quenching in liquid nitrogen after treatment

(c) TN: thermal treatment under nitrogen atmosphere; quenching devulcanizate in liquid nitrogen



20


0

5

10

15

20

25

0 100 200 300 400 500 600

Strain (%)

Str

ess

(MP

a)

SBR/D-TT

SBR/D-TL

SBR/D-TN

SBR

0

1

2

3

4

5

SBR SBR/D-TT SBR/D-TL SBR/D-TNM

od

ulu

s a

t 10

0%

str

ain

(M

Pa

)

0

10

20

30

40

50

60

70

80

Hard

nes

s (S

ho

re A

)

Modulus Hardness


TT: thermal treatment without exclusion of oxygenTL: thermal treatment and quenching in liquid nitrogen after treatment

TN: thermal treatment under nitrogen atmosphere; quenching devulcanizate in liquid nitrogen

21


� Decrease in crosslink density without additional sol fraction

indicates less polymer scission

� Stabilizers allow to work at higher temperatures, thus faster processes


SBR devulcanizationEffect of stabilizers

22


Devulcanization aid: DPDS, 15 mmol/100 g

Oil: TDAE, 5%wt

Temperature: 220°°°°C

Time: 6 minutes

Atmosphere: N2 purging

Cooling: Liquid nitrogen

Passenger car tire elastomersDevulcanization mechanisms

23

Ongoing

at

RUG

Factors Conditions

De-vulcanization aid

De-vulcanization oil

De-vulcanization temperature

De-vulcanization atmosphere

Dumping condition

DPDS 30 mmol/100 g compound

TDAE 5% w/w

220°C

With nitrogen gas purging

In liquid nitrogen

Factors Conditions

Swelling time


De-vulcanization time

0, 30 60 minutes

5, 15, 30 and 50 % w/w

6 and 10 minutes

Addition of stabilizer

Factors Conditions

De-vulcanization aids


Swelling time

Swelling temperature

De-vulcanization time

De-vulcanization temperature

De-vulcanization atmosphere

Dumping condition

DPDS 30 mmol/100 g compound

TDAE 5% w/w

30 minutes

65 °C

6 minutes

220 °C

With nitrogen gas purging

Exclusion from air/oxygen


Passenger car tire rubberDevulcanization conditions

24

ACKNOWLEDGEMENTS

Parameter Brabender internal mixer Extruder

DA DPDS, 15 mmol/100g DPDS, 18 mmol/100g

TDAE 5 %wt 6 %wt

Antioxidant TDTBP, 1 %wt TDTBP, 1 %wt

Swelling temperature 65 ͦ C 65 ͦ C

Swelling time 30 minutes 30 minutes

Devulcanization time 6 minutes Min. 6 minutes

Rotor/screw speed 50 rpm 10 rpm

Devulcanization temperature 220 ͦ C 220 ͦ C

Devulcanization atmosphere N2 gas purging N2 gas purging

Screw configuration High shear Low shear with kneading elements in devulcanization zone

Extrudate handling Quenching in LN2 Cooling calender

Passenger car tire rubberInternal mixer versus extruder devulcanization

25

• No adjustment of compound composition

• ‘First shot’ D-GTR; not optimized

• Decrease in tensile strength of

up to 55% for 50/50 blend

• Elongation at break increased for base,

carcass and apex

• Compound adjustment gave an increase in

tensile strength of 60% in a 50/50 blend

• Absolute improvement for apex, slight

decrease for the other compounds

• In a 30/70 blend, the original tensile value will

be reached except for the base compound

Application study in a blendDifferent tire compounds

26

LimitationsSilica compounds

IngredientTESPT TESPD TESPM

(phr)

SSBR 103 103 103

BR 25 25 25

Zeosil 1165 80 80 80

Silane 7.0 6.3 9.0

TDAE 5.0 5.0 5.0

ZnO 2,5 2,5 2,5

Stearic acid 2,5 2,5 2,5

6PPD 2.0 2.0 2.0

TMQ 2.0 2.0 2.0

Sulfur 1,4 2.0 2.2

TBBS 1,7 1,7 1,7

DPG 2.0 2.0 2.0

Untreated PESPM

PESPM 220°°°°C

PESPM 250°°°°C

TESPMTESPM

27

Smoothest surface

96 h swelling,

two passes @ 150 ͦ C & 220 ͦ C

Reference samples

plain white rubber 5% powder 5% compound

TGA

residue

20 %wt

compound: 6 %wt

LimitationsSilica compounds

28


Contaminations

Different polymers

Fillers

Aging during first lifecycle

Fibres Steel Sand Glass …

SBR BR NR IIR

Silica, carbon black become less active

Curing agents and acitvity

Remains of curing agents & reduced curing activity of the polymers

influence new curing process

Challenges

29

EPDM roof sheeting – the easy one

Summary

� Degree of devulcanization strongly depends on network structure

� Amines are the DA’s of choice

� Risk of re-combination at high concentrations and high temperatures

� Rotor speed and devulcanization time have minor influence

� 40% of virgin rubber can be replaced by devulcanizate

� Most critical devulcanization parameter: temperature �� 220 ͦ C

� Screw: low shear design

� Protective atmosphere during and after devulcanization:

absence of oxygen

efficient cooling

� Maximum degree of devulcanization

batch mixer: < 80%

extruder: 80% - 90%

� 90% Limit: bound rubber, stable monosulfidic crosslinks

� Visible particles, even for fine powder

Passenger car tire rubber – the difficult one

30

Acknowledgements

Sponsors of (earlier) work

PhD scholarship for teachers

Sponsor and chemicals supplier

Project partner

Usage of process equipment

Incentive fund from Windesheim – Saxion

Professorship of Polymer Technology