A single mode optic fiber with low water peak, with a reduced sensitivity to 

bends for communication systems E3 ﴾G657A1/G652D﴿ ALPHA

Single­mode    optical    fiber    with    low    water    peak  E3  ﴾G657A1/G652D﴿  hybrid  with  advanced 

characteristics  is  a  fiber  with  a  reduced  sensitivity  to  bends.  The  fiber  is  produced  by  vapor  axial 

deposition method  ﴾VAD﴿ with a quartz core alloyed with Germanium.  It  completely complies with  the 

requirements  of  ITU­T  G.652d    and  exceeds  ITU­T  G.657A1  parameters  of  macrobend  loss  and 

attenuation. It is a product manufactured in the Russian Federation. Double acrylic coating provides its 

high  strength  and  a  long  service  life.  The  fiber  works  in  a  full  spectral  range  of  different  access 

networks,  uncluding  FTTH,  and  can  be  applied  in  long  distance  communications.  Fiber  bending 

resistance  and  improved  attenuation  parameters  give  an  advantage  in  the  application  for  residential 

networks.  The  quality  control  system of  the  factory  confirms  plug  compatibility with E3  fiber  ﴾G652d﴿ 

manufactured  by  "Optic  fiber  Systems",  JSC  as well  as with  all  available  on  the market  SMF  fibers. 

Fiber  qulitiy's  compliance  with  Russia  and  international  standarts  is  confirmed  by  the  Certificate  № 

SSAQ 025.1.2.0126 issued by certification agency "Kabelsert" of JSC "VNIIKP" on 08.06.2018.

Dimensional SpecificationsCore­Clad Concentricity, μm

Cladding Diameter, μm

Cladding Non­Circularity, %Coating Diameter, μmFiber Curl, m radius of curvature

Coating­Cladding Concentricity, μm

Length1, km

≤ 0,5

125±0,7

≤ 0,7242±5≥ 4

≤ 12

25,2 / 50,4

1Supplies of other lengths are possible

Macrobend Loss

Winding CondirionsWavelength,

nm 

Induced Attenuation,

(db) 

1 turn around a mandrel with R 10mm

10 turn around a mandrel with R 15mm

1550

15501625

1625

≤ 0,50

≤ 1,50≤ 0,05≤ 0,30

100 turn around a mandrel with R 25mm131015501625

≤ 0,01

Optical SpecificationsMaximum Attenuation*, dB/km at wavelengthsна 1310 nmна 1383 nmна 1550 nm

≤ 0,32≤ 0,32≤ 0,18

на 1625 nm ≤ 0,20

Mechanical Specifications

Environmental Characteristics 

Induced Attenuation 1310 nm, 1550 nm & 1625 nm,

­60ºC ~ +85ºC Temperature+23ºC Water Immersion+85ºC Heat Aging+85ºC/85%Damp Heat

≤ 0,05≤ 0,05≤ 0,05≤ 0,05

2rAttenuation coefficients in a wavelength range do not differ from 

attenuation coefficients at references more than indicated values

3GOST R MEK 60793­1­48 (Method A, fixed analyser) 

4GOST R MEK 60793­1­48 (Method B, jones matrix eigenanalysis) 

ProofTest,                                                  GPa(Other tension force on request)                               % 

Coating Strip Force, NPeak forceTypical average force

≥ 0,69

>1%

1 – 8,91 – 5

Dynamic Stress Corrosion ≥ 20

на 1310 nm/1383 nmEffective Group Index of Refraction

на 1550 nmна 1625 nm

1,4661,4671,470

Performance Specifications

Attenuation vs. wavelength

Point discontinuity, dB

Mode Field Diameter, μm

1285­1330 nm at wavelength 1310 nm1525­1575 nm at wavelength 1550 nm

на 1310 nmна 1550 nm

на 1310 nm

на 1550 nm

≤ 0,03

≤ 0,02

≤ 0,05≤ 0,05

9,2±0,4

10,4±0,5

Cable Cutoff wavelength, (λcc), nm

Dispersion, ps/nm∙km

Zero­dispersion wavelength (λ0), nmZero dispersion slope, ps/nm2∙km 

Polarization Mode Dispersion (PMD), ps/√km

на 1550 нм 

на 1625 nm

Maximum Individual Fiber PMDPMD Link Design Value

≤ 1260

≤ 18

≤ 221300­1324

≤ 0,092

≤ 0,1

≤ 0,06 ≤ 0,04

≤ 0,1FA3 JME4

на 1550  ≤ 18

≤ 22

This Specification offers promotional content. Specific characteristics of optical fiber to be determined in accordance with a contract and TU.