Plastics Failure Analysis
Dr. Ahamed ShabeerPolymer Scientist
Bodycote Testing Group- Orange County Materials Testing LaboratoryAnaheim, California
![Page 2: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/2.jpg)
slide number 2
What Does Failure Analysis Require?
ExpertiseWillingness to Not Give UpSystematic ApproachSometimes Luck!
![Page 3: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/3.jpg)
slide number 3
More Like This
![Page 4: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/4.jpg)
slide number 4
ThanLikeThis
![Page 5: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/5.jpg)
slide number 5
Failure Diagnosis is...
Causes
Techniques
![Page 6: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/6.jpg)
slide number 6
Failure Analysis Protocol
Collection of Background and Selection of SamplesReview of Safety ConsiderationsEstablishment of Record KeepingIdentification and Cleaning of SamplesMacroscopic Examination and AnalysisMicroscopic Examination and Analysis
![Page 7: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/7.jpg)
slide number 7
Failure Analysis Protocol (cont.)
Determination of Failure MechanismMechanical TestingChemical AnalysisStress (including Fracture Mechanics) AnalysisTesting Under Simulated Service ConditionsAnalysis of Evidence and Formulations of Conclusions
![Page 8: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/8.jpg)
slide number 8
More Experience
Better Interpretation
Macroscopic and Microscopic Examination
![Page 9: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/9.jpg)
slide number 9
Fractography
Accomplished using Naked EyeMagnifying GlassCommon Light MicroscopyPolarized Light MicroscopyReflected Light MicroscopyScanning Electron Microscope
![Page 10: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/10.jpg)
slide number 10
Modes of Fracture
Ductile FractureBrittle Fracture
![Page 11: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/11.jpg)
slide number 11
DUCTILE FRACTURE
Common in laboratory testing
Standard tensile test of a ductile polymer• no stress concentration• stretched at a constant rate until
rupture• applied stress is essentially uniaxial• material undergoes gross plastic
deformation or yielding (permanently deformed)
Fractures which occur after the applied stress has exceeded the yield stress of the polymer.
![Page 12: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/12.jpg)
slide number 12
DUCTILE FRACTURE
Rare in practice
Ductile fractures rarely are subjects of failure analysis.
Maximum stress should not exceed a small fraction of the yield stress of the material.
Exceptions Intended ductile failures such as:tamper-evident rings found on plastic closures of beverage bottles plastic seals on household fire extinguishers
![Page 13: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/13.jpg)
slide number 13
BRITTLE FRACTURE
• Little or no plastic deformation
• No distortion or shape changes
• Material just “snapped”
• Mating fracture surfaces*
* Attempts to put the mating fracture surfaces together may introduce artifacts which can complicate the interpretation of the fracture
surface
![Page 14: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/14.jpg)
slide number 14
BRITTLE FRACTUREBrittle fractures generally occur:
• at stresses well below the yield stress of the polymer.
• they are favored by high strain rate (e.g. impact)
• they are favored by low temperature, cyclic loading (fatigue), and a stress condition known as plane strain.
Since brittle fractures typically occur in the linear elastic range of the stress-strain curve, elastic stress analysis is justified in many cases.
![Page 15: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/15.jpg)
slide number 15
BRITTLE FRACTURE
NORMALLY BRITTLE MATERIALS
Glass and ceramicsPolystyrene (PS)Styrene-Acrylonitrile Copolymer (SAN)Polymethyl methacrylate (PMMA)Thermosetting Resins
![Page 16: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/16.jpg)
slide number 16
BRITTLE FRACTUREEven though brittle fractures are without gross plastic deformation, localized plasticity is observed on many fracture surfaces.
![Page 17: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/17.jpg)
slide number 17
Failure DiagnosisDoes problem really exist?What is the frequency of failure?Was the onset of the failure sudden or gradual?Did the onset occur after a design change, a change in raw material suppliers, a modification to the production cycle?Does the failure only occur with a specific product?
![Page 18: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/18.jpg)
slide number 18
Determination of Failure Mechanism
Poor DesignFractography
Non-Design FactorsRaw MaterialsCompoundingProcessingEnvironment
![Page 19: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/19.jpg)
slide number 19
Design Factors
Related to Stresses in ApplicationCan be Short-Term or Long-Term Related
![Page 20: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/20.jpg)
slide number 20
Non-Design Factors
Raw MaterialsResinAdditives
CompoundingProcessingEnvironment
![Page 21: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/21.jpg)
slide number 21
Mechanical Testing
Short-term Properties Long-term FatigueLong-term CreepEnvironmental Attack
![Page 22: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/22.jpg)
slide number 22
Short-Term Properties
Checked using Design CriteriaMechanical Property Testing
Tensile StrengthElongation to Yield/BreakImpact StrengthFlexural StrengthAbrasion
Operating Temperature
![Page 23: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/23.jpg)
slide number 23
Long-term Fatigue
Testing must relate to serviceamplitudeHertz
Tested on material or partTested in
FlexuralTensileCompression
![Page 24: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/24.jpg)
slide number 24
Long-term Creep
Requirement must relate to actual serviceTested in
FlexuralTensileCompression
![Page 25: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/25.jpg)
slide number 25
Plastic Compounds
Resin Type Grade
AdditivesStabilizersPlasticizersImpact ModifiersFillers/Reinforcing AgentsFlame RetardantsLubricantsAntiblock AgentsNucleating AgentsProcessing AidsInternal Mold Release AgentsColorantsAntistatic AgentsBlowing Agents
![Page 26: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/26.jpg)
slide number 26
Compounding Variables
Correct CompositionUniform Mixing DegradationLoss of AdditivesContaminants Regrind
![Page 27: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/27.jpg)
slide number 27
Ingredient Analysis
Infrared SpectroscopyEnergy DispersiveGas ChromatographyHigh Performance Liquid Chromatography
![Page 28: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/28.jpg)
slide number 28
Environment
Environmental Stress CrackingLoss of StabilizersLoss of PlasticizersPolymer DegradationThermal AgingWeatheringHydrolysisChemicalsBioProducts
![Page 29: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/29.jpg)
slide number 29
Chemical Analysis
Ingredient AnalysisThermal AnalysisMolecular Weight ChangesMicroscopy
![Page 30: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/30.jpg)
slide number 30
Thermal Analysis
Differential Scanning CalorimetryThermogravimetryThermal Mechanical AnalysisDynamic Mechanical Analysis
![Page 31: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/31.jpg)
slide number 31
Processing Causes of Degradation
Inadequate PredryingProcessing Conditions
TemperatureTimeShear
![Page 32: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/32.jpg)
slide number 32
Molecular Weight Changes
Dilute Solution ViscometryGel Permeation ChromatographyMelt RheologySol/Gel Content
![Page 33: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/33.jpg)
slide number 33
Other Worries
Processing DefectsWeld LinesShrinkageVoids
CrystallinityDegree of CrystallinityMorphologyDistribution
•Residual Stress in Molded Parts
•Degree of Polymer Orientation
•Degree of Crosslinking•Degree of Cure
![Page 34: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/34.jpg)
slide number 34
Stress Analysis
Can be analyzed using FEAMany times needs a different perspective
![Page 35: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/35.jpg)
slide number 35
Case 1 - Infrared SpectroscopyEpoxy Adhesion Failure Problem
A 2-part epoxy had been successfully used to bond transistors in hearing aids built into eye glasses.New problem with epoxy bond failing.Had the correct mix ratio been used?Specification: 70/30 resin/hardener.
![Page 36: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/36.jpg)
slide number 36
Epoxy Adhesion Failure Micro-FTIR Analysis
A small flake of the adhesive was removed under a microscope.Micro-FTIR spectrum recorded.Resin/hardener mixtures of 60/40, 70/30 and 81/19 were made and cured.Recorded FTIR spectra of neat resin, neat hardener and the three mix standards.
![Page 37: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/37.jpg)
slide number 37
Spectrum of Resin and Hardener
917 cm-1
Terminal Epoxy Group at 917 cm-1
![Page 38: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/38.jpg)
slide number 38
Spectrum of Different Ratios
![Page 39: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/39.jpg)
slide number 39
Spectrum of Epoxy from Transistor
917 cm-1
![Page 40: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/40.jpg)
slide number 40
Epoxy Adhesion Failure FTIR Conclusions
Could distinguish mix ratios using relative intensity of resin peaks at 2965 and 2873 cm-1 and hardener peaks at 2922 and 2952 cm-1.Sample from transistor displays correct 70/30 mix ratio and no unreacted epoxy at 917 cm-1.Adhesion failure – likely surface preparation problem.
![Page 41: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/41.jpg)
slide number 41
Case 2 - FTIRPP Regrind Problem
Molder uses outside source for polypropylene regrind.All colors and mixtures of colors are acceptable.Molder was concerned about possible contamination of such mixtures.Molder submitted a bag of regrind for analysis.
![Page 42: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/42.jpg)
slide number 42
PP Regrind FTIR Analysis
Sample consisted of small pieces of 13 different colors and shapes.A typical specimen of each type was isolated and identified by FTIR.Four (4) of the 13 types were not a PP.Contaminants: PE, plasticized PVC, Nylon and Wood Chips.
![Page 43: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/43.jpg)
slide number 43
Case 3 - Infrared SpectroscopyCracking HIPS Door Liners Problem
Refrigerator manufacturer had a warehouse full of refrigerators with cracked HIPS door liners.Cracked liners were submitted for failure analysis.
![Page 44: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/44.jpg)
slide number 44
HIPS Door Liners Microscopy
Cracking appearance was consistent with Environmental Stress Cracking.Panels had residual stresses from thermoforming.Cracking located where panel touched rubber sealing gasket expected to contain extending oils.Cracks contained visible oil.
![Page 45: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/45.jpg)
slide number 45
HIPS Door Liners FTIR Comparison of Oils
Under a microscope, a needle was used to transfer oil from a crack to a salt plate.Extending oils in a gasket were isolated by MEK extraction.FTIR spectra of both oils were recorded.The spectra did not match.Oil from the crack had more peaks.
![Page 46: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/46.jpg)
slide number 46
HIPS Door LinersIdentifying Additional Oil
Spectral subtraction of the gasket oil from the crack oil yields a spectrum for an unsaturated ester such as a vegetable oil.Further checking with plant personnel revealed that they had started to wipe the gasket with corn oil to eliminate sticking.Cracking caused by corn oil application.
![Page 47: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/47.jpg)
slide number 47
Case 4 - Field Returned Instrument Panels PC/ABS
![Page 48: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/48.jpg)
slide number 48
Longitudinal Brittle Cracks PC/ABS Instrument Panels
Failures observed in instrument panels within two years of installation.Exorbitant cost of replacements as failures occurred within the warranty period.
![Page 49: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/49.jpg)
slide number 49
![Page 50: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/50.jpg)
slide number 50
Crack Propagation Mechanism
![Page 51: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/51.jpg)
slide number 51
Microscopic Examination
Crack initiation from the exterior corner edge near ventilation grill Smooth crack origin indicates low level of stressesIncremental crack propagation due to cyclic stresses as suggested from striationsFast crack growth when critical size is reached
![Page 52: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/52.jpg)
slide number 52
Izod Impact Strength
Fractured Panel 0.42 ft-lbs/inch
New Panel 1.24 ft-lbs/inch
• Conditions- Tested in controlled environment laboratory- 2 inch-pound hammer- Tested according to ASTM D256
![Page 53: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/53.jpg)
slide number 53
Melt Flow Index
MFI ASTM D1238Conditions: 250 C
1.2 Kg load
Failed Panel 14.2 g/10 minuteNew Panel 4.3 g/10 minute
Each data point is an average of 3 experiments
![Page 54: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/54.jpg)
slide number 54
FTIR Analysis
![Page 55: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/55.jpg)
slide number 55
Silicone oil - ESC agent
FTIR Analysis
![Page 56: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/56.jpg)
slide number 56
Case 5 - Streaks in Plexiglas
Problem: Microwave door panel of Plexiglas (PMMA) has white streaksPossible Cause: ContaminationTechnique Used: Microscope FTIR
![Page 57: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/57.jpg)
slide number 57
Plexiglas Sheet
Contaminated Streaks
![Page 58: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/58.jpg)
slide number 58
Case 6- Which PP is this?
Problem: Manufacturing Plant has transferred material to unlabeled Gaylord. They only have two types of PP but the materials are different.Technique Used: Thermal Analysis - DSC
![Page 59: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/59.jpg)
slide number 59
Distinguishing Two Similar Polypropylenes
General Purpose
Improved Processability
Melt Flow 12 12 Density 0.903 0.904 Izod 0.70 1.0 Tensile 5050 5400 Elongation 11.0 10.5 Rockwell R 100 103
![Page 60: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/60.jpg)
slide number 60
DSC on Polypropylenes
![Page 61: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/61.jpg)
slide number 61
Case 7 - ABS Knob Crack - ESC
![Page 62: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/62.jpg)
slide number 62
Case 7 - ABS Knob Crack - ESC
Inside surface - oil near the crack
![Page 63: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/63.jpg)
slide number 63
Case 7 - ABS Knob Crack - ESC
FTIR of liquid
residue in cracks -
silicone oil
![Page 64: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/64.jpg)
slide number 64
Case 8 - PE Pipe Failure
Ductile failure of polyethylene gas pipe in service in ArizonaPetrochemical odorLitigants claimed byproducts in natural gas
![Page 65: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/65.jpg)
slide number 65
Case 8 - PE Pipe Failure
SPME sampling and GC-MS analysis detected large number of aromatic and naphthenic compounds, including PAH’s, consistent with diesel fuel exposureFuel plasticized PE, leading to ductile failure
![Page 66: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/66.jpg)
slide number 66
Bodycote Advantages
Multidisciplinary StaffStaff ExpertiseIndustry ExperienceProblem Solving ExperienceExtensive and Diverse LaboratoriesISO 17025Laboratories Accredited by A2LA & ICBO, NADCAP for non metallicsCustomized Reports with Complete DocumentationApproved by Aerospace primes
![Page 67: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/67.jpg)
slide number 67
Failure AnalysisExpert Witness
Polymer AnalysisMaterials Testing
Product DesignMicroscopy
Piping ProductsPolymer Characterization
Composite Characterization Process Troubleshooting
Product Testing/DevelopmentStress Analysis/Design
Major Areas of Expertise
![Page 68: Plastics Failure Analysis - TRFAtrfa.org/erc/docretrieval/uploadedfiles/Technical Papers/2008... · Plastics Failure Analysis Dr. Ahamed Shabeer. ... loading (fatigue), and a stress](https://reader034.vdocument.in/reader034/viewer/2022050903/5aedf4947f8b9aa17b8ba68b/html5/thumbnails/68.jpg)
slide number 68
Thank you for your attention……...