Download - Technical Information - BASF
Technical Information
Soluplus®
August 2019 | Supersedes issue dated September 2015 | Last change DAWF-2019-0893 03_090801e-06/Page 1 of 14
® = Registered trademark of BASF in many countries.
2 of 14 03_90801e-06 Soluplus®
1. Introduction Soluplus® is a polymeric solubilizer with an amphiphilic chemical structure, which was particularly developed for solid solutions.
Due to its bifunctional character, it is able to act as a matrix polymer for solid solutions on the one hand, and, on the other hand, it is capable of solubilizing poorly soluble drugs in aqueous media.
Furthermore, Soluplus® can increase the bioavailability of poorly soluble drugs.
Description Soluplus® is a polyvinyl caprolactam-polyvinyl acetate-polyethylene glycol graft co-poly-
mer. It is a free flowing white to slightly yellowish granule with a faint characteristic odor.
2. Technical properties Structural formula
�
��
��
�
�
�
�
�
�
��
�
PEG 6000 / vinylcaprolactam / vinyl acetate 13 / 57 / 30
Appearance White to yellowish free flowing granules
CAS number 402932-23-4
3 of 14 03_90801e-06 Soluplus®
Molecular weight The average molecular weight determined by gel permeation chromatography is
approximately 118,000 g/mol (nominally in the range of 90 000 – 140 000 g/mol). A representative molecular weight distribution is shown in Figure 1.
[w(lo
g(M
))]
[M/Da]
100
0,0
0,2
0,8
1,0
1,2
1,4
0,4
0,6
1 000 10 000 100 000 10 000 000 100 000 000
MW~118000 g/mol
Figure 1: Gel Permeation Chromatography; Reference: PMMA
Critical Micelle Concentration 7.6 mg/L (surface tension curve shown in Figure 2)
Micelles are typically 70 to 100 nm in diameter (pH 7 buffer)
Sur
face
tens
ion
[mN
/m]
Polymer concentration [mg/l]
0,1
40
45
60
65
50
55
1 10 100 1 000 10 000
CMC Soluplus®
in DI water (23° C)
CMC = 7.6 mg/l
Figure 2
HLB Approximately ~14
Glass Transition Temperature ~70 °C
K-value
31-41 (1% in ethanol)
4 of 14 03_90801e-06 Soluplus®
Solubility
Soluplus® is soluble in water. Furthermore, it is soluble in acetone (up to 50%), methanol (up to 45%), ethanol (up to 25%), dimethylformamide (up to 50%) and in mixtures of (1:1 m/m) methanol/ acetone (up to 50%) and (1:1 m/m) ethanol/acetone (up to 45%). Higher polymer concentration may result in a cloudy or turbid aqueous solution. This is due to formation of colloidal Soluplus® micelles.
Solubility of Soluplus® in common solvents shown in Figure 3.
Con
cent
ratio
n of
Sol
uplu
s® [%
]
aceto
ne0
10
20
30
40
50
60
ethan
ol
MeOH/
aceto
ne
(1:1
m/m) EtO
H/
aceto
ne
(1:1
m/m)
methan
olDMF
Figure 3 This phenomenon is more pronounced at elevated temperature (~40 °C), which is a lower critical solution temperature (LCST). Thus, when the polymer solution is heated at or above its LCST, a clear polymer solution turns cloudy or turbid due to formation of larger micelles. This process is reversible upon cooling the polymer solution.
Soluplus® is not soluble in medium-chain triglyceride Kollisolv® MCT and is not soluble in poloxamer grade Kollisolv® P124.
In Kollisolv® PEG 400 Soluplus® is soluble up to 25% (w/w). The data shown in Figure 4 show the viscosity of a Soluplus®-in-PEG 400 solution and are obtained at 60 °C on a HAAKE Rotovisco with coaxial cylinder DG 43 and a plate-plate PP 60 geometry for a shear rate of 100 1/s.
Viscosity of Soluplus®-in-Kollisolv® PEG 400 solution
Soluplus®-concentration [% (w/w)]
Vis
cosi
ty [m
Pa
· s]
100
0 5 10 15 20 25 301
10
1000
10000
Figure 4: Viscosity of Soluplus®-in-Kollisolv® PEG 400 solution
5 of 14 03_90801e-06 Soluplus®
In Kollisolv® PG (propylene glycol) Soluplus® is soluble up to 2.5% (w/w). The data shown in Figure 5 show the viscosity of a Soluplus®-in-PG solution and are obtained at 60 °C on a HAAKE Rotovisco with coaxial cylinder DG 43 and a plate-plate PP 60 geometry for a shear rate of 100 1/s.
Viscosity of Soluplus®-in-Propylene Glycole solution
Soluplus®-concentration [% (w/w)]
Vis
cosi
ty [m
Pa
· s]
100
0 0.5 1 1.5 2 2.5 31
10
Figure 5: Viscosity of Soluplus®-in-Propylene Glycole solution
Solution Viscosity
Viscosity of Soluplus® is shown in Figure 6 at four distinct temperatures.
Vis
cosi
ty [m
Pa
· s]
Polymer concentration [%]
0
500
1000
1500
2000
2500
0 5 10 15 20 25 30 35
Figure 6: Cone-plate viscosimeter, 100 s-1
6 of 14 03_90801e-06 Soluplus®
Melt Viscosity
The values shown in Figure 7 were obtained on a capillary rheometer.
Shear rate [1/s]
Mel
t Vis
cosi
ty [m
Pa
· s]
100
1000
10000
100000
1 10 100 1000 10000 1000001
10
140 °C160 °C180 °C200 °C220 °C
Figure 7
Specific Heat Capacity
The following graph shows the specific heat capacity and the heat enthalpy for Soluplus® in dependency from temperatur.
Temperature [°C]
cp [J
/g*K
]
Enthalpy [J/g]
dried, 2nd Heating run after quench colling from 150 °C
1.5
2.0
2.5
0 50 100 150
0.5
1.0
300
350
400
0
50
100
150
200
250
Figure 8
Density
The Density of Soluplus® was determined at room temperature using a helium pycno-meter with 1.082 g/cm³.
Angle of Repose
The angle of repose for Soluplus® batch 21819647G0 was determined with the method according to Dr. Pfrengle with 27.5 °.
7 of 14 03_90801e-06 Soluplus®
Particle Size
Soluplus® Granulates are approximately 340 microns in diameter (determined by laser diffraction); images of the granules are shown in Figure 9.
Figure 9
3. Application and processing Solubilization
A potential affinity between Soluplus® and a poorly soluble drug can be pretested by means of various methods. The solubilization capacity of the amphiphilic polymer is tested by determination of the saturation solubility of a poorly soluble drug in a polymer solution. Phosphate buffer as solvent (e. g. pH 7.0) assures comparable conditions when testing ionic solubilizers or drugs. Thus, solubility effects due to pH shifts can be avoided.
Procedure: A 10% polymer solution in phosphate buffer is oversaturated with a discrete drug
and stirred for 72 h at room temperature. The resulting suspension is filtered through 0.45 μm filter and the content of solubilized drug in the filtrate is determined by UV spectroscopy.
Figure 10 shows the results of the solubility enhancement of Soluplus® for various drugs in comparison to the API solubilities in phosphate buffer pH 7.0:
[g/1
00 m
l]
Soluplus®
Pure API
Figure 10: Phosphate buffer pH 7.0; 10% solubilizer solution, saturation solubility detected after 72h stirring
8 of 14 03_90801e-06 Soluplus®
Capacity for Amorphous Solid Solutions Soluplus® was designed for solubilizing high concentrations of poorly water-soluble
APIs in amorphous solid dispersions (ASDs) – these can be produced using a multitude of technologies including, but not limited to: Hot Melt Extrusion, Spray Drying, and Drug-Polymer Layering.
In order to screen for effectiveness, the following procedure is recommended:
Choose an appropriate solvent that dissolves the API and also Soluplus® (e. g. ethanol, methanol, acetone, dimethylformamide). Dissolve both substances with gentle stirring, then cast the solution on a glass plate as a thin film. It is recommended to utilize a scraper that leads to a film of approximately 120 μm. The thin film (thickness of the dry film < 120 μm) enables fast drying and avoids a recrystallization of the poorly soluble drug. Subsequent drying should be performed in a vacuum drying cabinet (50 °C, 10 mbar, 30 min) to ensure a fast and complete drying of the film. Test several concentration ratios of drug to polymer in incremental steps. (e. g. 20, 30, 40 and 50%). Samples should be viewed using polarized light (recommended) or optical microscopy; crystalline API should be visible in ranges beyond the solubility limit. This can be then used as a starting point for designing the formulation. Additional solubilizers (e.g. Kolliphor® RH 40) or plasticizers (e.g. Kollisolv® PEG 1450) can also be incorporated into the solution to test the effect on the solid solution as desired.
Hot Melt Extrusion Soluplus® exhibits a glass transition temperature of approximately 70 °C and is well
extrudable within standard hot melt extrusion devices. As an example, in a standard 16mm twin-screw extruder, temperatures from 120 °C to 220 °C are possible. The polymer shows no chemical degradation even after extrusion at 220 °C. Incorporation of a drug can lead to lower temperatures than 120 °C in dependence on the drug melting point.
The relatively low glass transition temperature for Soluplus® allows for lower temperatures during extrusion processes, resulting in less thermal stress to APIs. A comparison of the Tg against other extrudable polymers is shown in Figure 11.
Tem
pera
ture
[°C
]
Soluplus
®0
20406080
120100
140
180160
200
Kollido
n® VA 64
Kollido
n® 12
PF
Kollido
n® 30
Kollido
n® 90
F
Kollido
n® SR
Kollico
at® MAE
HPMCASHPC
HPMC
70
101
149 156152
114 118 130
186
39
90
Figure 11
9 of 14 03_90801e-06 Soluplus®
The ability to extrude Soluplus® is further shown by observing the melt rheology of the polymer melt, which is shown to be comparatively low vs. well known extrudable polymers such as Kollidon® VA 64. The comparison is shown in Figure 12.
Temperature [°C]
Vis
cosi
ty [P
a · s
]
Soluplus®
Kollidon® VA 64Kollidon® 12 PF
1 000
120 140 160 180 200 220 24010
100
10 000
100 000
Figure 12: Rotary viscosimeter, plate-plate method, angular frequency: 1.6 rad/s
A solid solution of Fenofibrate (melting point ~77 °C) at 20% drug content was prepared as an example at 100 °C. This was prepared using a twin screw co-rotating extruder with a 16 mm diameter at 200 rpm and 1 kg/h. In vitro release from USP II (50 rpm, 700 mL 0.8 M HCl) is shown in Figure 13.
t [min]
Dru
g re
leas
e [%
]
Crystalline fenofibrateSolid solution Soluplus®/fenofibrate
Figure 13
10 of 14 03_90801e-06 Soluplus®
It is important to note that the API does not need to be melted during extrusion in order to produce an amorphous solid dispersion. For example, Itraconazole (melting point ~166 °C) was extruded at 150 °C notably lower than the melting point of the API – in vitro drug release results are shown in Figure 14.
Dru
g re
leas
e [%
]
t [min]
Crystalline itraconazoleSolid solution Soluplus®/itraconazole
Figure 14
Spray Drying Soluplus® has a high solubility in common volatile organic solvents used in spray
drying, while maintaining also a low viscosity that is needed to process (see section 2 for viscosity). Recommended solvents include methanol, ethanol and acetone. Optimal concentrations for spraying range from 5 to 30% w/w depending on solvent, viscosity, API load and other spray dryer conditions. An example formulation of 20% poorly water-soluble drug Ritonavir at 20% w/w in Soluplus® is shown in Figure 15.
Figure 15
11 of 14 03_90801e-06 Soluplus®
Drug Polymer Layering Soluplus® can effectively be layered over beads, spheres, mini-tablets or other fluidized
granules using a conventional fluid bed coater. Similar to spray drying, Soluplus® should first be dissolved together with poorly water-soluble API in a mutually effective solvent (e.g. ethanol, methanol, acetone). Care should be taken to allow coating of the substrate prior to evaporation rather than spray drying of the solution. This is typically controlled with solvent type, solids concentration and temperature profile in the bed. In the following example, poorly water-soluble drug Carbamazepine was spray coated using Soluplus® from an ethanol solution (ratio 1:2 Soluplus®: Ethanol). The mass gain was approximately 10%.
Dru
g re
leas
e [%
]
t [min]
Sugar pellets layered withcarbamazepine/Soluplus®
Figure 16: Dissolution rate of carbamazepine
Capsule formulation Once an amorphous solid dispersion is formed, it can be loaded into a hard gelatin
capsule. It is recommended to mill the ASDs down to an appropriate and desired size, mixed with a disintegrant (e.g. Kollidon® CL) at a concentration of 10-15% w/w and any non-soluble filler may also be used (e.g. microcrystalline cellulose). An example formulation is shown below:
Capsule formulation:
Solid solution 70%
Kollidon® CL 15%
Microcrystalline cellulose 15%
Tablet formulation Using a preformed ASD from hot melt extrusion or spray drying, the formulation may
be compressed into tablets. It is typically recommended to include 5-10% disintegrant (e.g. Kollidon® CL), lubricant, flowability aid and insoluble filler such as microcrystalline cellulose. An example formulation is shown below:
Tablet formulation:
Solid solution 60%
Microcrystalline cellulose (Avicel PH 102) 29%
Kollidon® CL 10%
Magnesium stearate 0.5%
Aerosil 200 0.5%
12 of 14 03_90801e-06 Soluplus®
Case Study – Bioavailability Three poorly water-soluble APIs were used as a case study for Soluplus® bioavailability
enhancement. These drugs were administered to Beagle dogs in a fasted state (n=5). The APIs and dose were as follows: Itraconazole (10 mg/kg bw), Danazol (30 mg/kg bw), and Fenofibrate (10 mg/kg bw).
Formulations were compared in three configurations:
• Crystalline API: 95% API + 5% disintegrant
• Physical Mixture: 15% API + 80% Soluplus® + 5% disintegrant
• Amorphous Solid Dispersion: 95% ASD + 5% disintegrant
All formulations were produced using a 16 mm twin screw co-rotating extruder.
Itraconazole ASDs were produced at 1kg/hr, 200 rpm and 150 °C – the results are shown in Figure 17 where a clear increase in bioavailability is only evident for the ASD.
Time [h]25
Itrac
onaz
ole
bloo
d co
ncen
trat
ion
[ng/
ml]
Physical mixture ItraconazoleCrystalline ItraconazoleSolid solution
0
50
100
150
200
250
300
350
400
450
Figure 17: Blood concentration of itraconazole
Danazol formulations were extruded at 0.9 kg/h, 200 rpm, and 140 °C the results also show a significant increase in bioavailability vs. the crystalline API or the physical mixture (Figure 18):
Time [h]25
Blo
od c
once
ntra
tion
[ng/
ml]
Physical mixture Danazole Crystalline Danazole Solid solution Danazole
0
200
400
600
800
1000
1200
1400
Figure 18: Blood concentration of danazole
13 of 14 03_90801e-06 Soluplus®
Fenofibrate ASDs were extruded at 0.7 kg/h, 200 rpm and 95 °C; in this case both the ASD formulation as well as the physical mixture exhibited large increases in bioavailability – this is due to the ability of Soluplus® to increase drug solubility in aqueous environments. This effect is known for some APIs and may be tested using similar means.
Time [h]25
Blo
od c
once
ntra
tion
[ng/
ml]
Physical mixture FenofibrateCrystalline FenofibrateSolid solution Fenofibrate
0
1000
2000
3000
4000
5000
6000
Figure 19: Blood concentration of fenofibrate
09_130829e-03 November 2017 Page 14 of 14 Pluronic® FT PE 6100
Disclaimer This document, or any answers or information provided herein by BASF, does not constitute a legally binding obligation of BASF. While the descriptions, designs, data and information contained herein are presented in good faith and believed to be accurate, it is provided for your guidance only. Because many factors may affect processing or application/use, we recommend that you make tests to determine the suitability of a product for your particular purpose prior to use. It does not relieve our customers from the obligation to perform a full inspection of the products upon delivery or any other obligation. NO WARRANTIES OF ANY KIND, EITHER EXPRESS OR IMPLIED, INCLUDING WARRANTIES OF MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE, ARE MADE REGARDING PRODUCTS DESCRIBED OR DESIGNS, DATA OR INFORMATION SET FORTH, OR THAT THE PRODUCTS, DESIGNS, DATA OR INFORMATION MAY BE USED WITHOUT INFRINGING THE INTELLECTUAL PROPERTY RIGHTS OF OTHERS. IN NO CASE SHALL THE DESCRIPTIONS, INFORMATION, DATA OR DESIGNS PROVIDED BE CONSIDERED A PART OF OUR TERMS AND CONDITIONS OF SALE.
August 2019
BASF – Nutrition & Health – www.pharma-ingredients.basf.com
14 of 14 03_90801e-05 Soluplus®
4. Handling & Safety Please refer to the individual material safety data sheet (MSDS) for instructions on safe and proper handling and disposal. Material safety data sheets are sent with every consignment. In addition they are available on BASF WorldAccount* or from your local BASF sales representative.
5. Product Specification The current version of the product specification is available on BASF WorldAccount* or from your local BASF sales representative.
6. Regulatory & Quality Please refer to the individual document quality & regulatory product information (QRPI) which is available on BASF WorldAccount* and from your local sales representative. The QRPI covers all relevant information including retest dates, and storage conditions.
7. Toxicology Toxicological studies are available on request. For detailed information and individual reports a secrecy agreement has to be signed in advance. * https://worldaccount.basf.com
8. PRD and Article numbers
PRD-No.* Product name Article numbers Packaging
30446233 Soluplus® 50539897 0.5 kg Plastic bottle
50101050 2.5 kg Plastic jerricans
50477909 12.5 kg Plastic drums
52155222 25 kg Fibreboard boxes
* BASF’s commercial product number.
9. Publications Publications including scientific posters are available on http://pharmaceutical.basf.com/en.html