Download - Welding Inspection CSWIP Gud
Welding Inspector Duties and Responsibilities Section 1
4/23/2007
1 of 691
Main Responsibilities
1.1
Code compliance
Workmanship control Documentation control2 of 691
4/23/2007
Personal Attributes
1.1
Important qualities that good Inspectors are expected to have are:
Honesty
Integrity
Knowledge
Good communicator
Physical fitness
Good eyesight3 of 691
4/23/2007
Standard for Visual Inspection 1.1
Basic RequirementsBS EN 970 - Non-destructive examination of fusion welds - Visual examinationWelding Inspection Personnel should: be familiar with relevant standards, rules and specifications applicable to the fabrication work to be undertaken be informed about the welding procedures to be used have good vision (which should be checked every 12 months)
4/23/2007
4 of 691
Welding Inspection
1.2
Conditions for Visual Inspection (to BS EN 970) Illumination: 350 lux minimum required (recommends 500 lux - normal shop or office lighting)
Vision Access: eye should be within 600mm of the surface viewing angle (line from eye to surface) to be not less than 30600mm
30
4/23/2007
5 of 691
Welding InspectionWhen access is restricted may use: a mirrored boroscope a fibre optic viewing system
1.3
Aids to Visual Inspection (to BS EN 970)
}
Other aids: welding gauges (for checking bevel angles, weld profile, fillet sizing, undercut depth) dedicated weld-gap gauges and linear misalignment (high-low) gauges straight edges and measuring tapes magnifying lens (if magnification lens used it should have magnification between X2 to X5)
usually by agreement
4/23/2007
6 of 691
Welding Inspectors EquipmentMeasuring devices:
1.3
flexible tape, steel rule Temperature indicating crayons Welding gauges Voltmeter Ammeter Magnifying glass Torch / flash light Gas flow-meter
4/23/2007
7 of 691
Welding Inspectors Gauges10mm 10mm1 2
1.3
G.A.L.S.T.D. 16mm
G.A.L.
3 4
L
S.T.D. 16mm
5 6
Fillet Weld Gauges0 IN 1/4 1/2 3/4
TWI Multi-purpose Welding Gauge
Misalignment Gauges Hi-Lo Gauge8 of 691
4/23/2007
HI-LO Single Purpose Welding Gauge
Welding Inspectors Equipment
1.3
Voltmeter
Ammeter
Tong Tester4/23/2007 9 of 691
Welding Inspection 1.3Stages of Visual Inspection (to BS EN 970)Extent of examination and when required should be defined in the application standard or by agreement between the contracting parties For high integrity fabrications inspection required throughout the fabrication process:
Before welding (Before assemble & After assembly) During welding After welding
4/23/2007
10 of 691
Typical Duties of a Welding InspectorBefore WeldingPreparation:
1.5
Familiarisation with relevant documents Application Standard/Code - for visual acceptance requirements
Drawings - item details and positions/tolerances etcQuality Control Procedures - for activities such as material handling, documentation control, storage & issue of welding consumables Quality Plan/Inspection & Test Plan/Inspection Checklist details of inspection requirements, inspection procedures & records required11 of 691
4/23/2007
Typical Duties of a Welding InspectorBefore WeldingWelding Procedures:
1.5
are applicable to joints to be welded & approvedare available to welders & inspectors
Welder Qualifications:
list of available qualified welders related to WPSscertificates are valid and in-date
4/23/2007
12 of 691
Typical Duties of a Welding Inspector 1.5Before WeldingEquipment: all inspection equipment is in good condition & calibrated as necessary all safety requirements are understood & necessary equipment available Materials: can be identified & related to test certificates, traceability ! are of correct dimensions are in suitable condition (no damage/contamination)
4/23/2007
13 of 691
Typical Duties of a Welding Inspector 1.5Before WeldingConsumables: in accordance with WPSs are being controlled in accordance with Procedure Weld Preparations: comply with WPS/drawing
free from defects & contaminationWelding Equipment: in good order & calibrated as required by Procedure
4/23/2007
14 of 691
Typical Duties of a Welding Inspector 1.5Before WeldingFit-up
complies with WPS Number / size of tack welds to Code / good workmanship
Pre-heat if specified
minimum temperature complies with WPS
4/23/2007
15 of 691
Typical Duties of a Welding InspectorDuring WeldingWeather conditions
1.5
suitable if site / field welding
Welding Process(es) in accordance with WPS
Welder is approved to weld the joint
Pre-heat (if required) minimum temperature as specified by WPS maximum interpass temperature as WPS
4/23/2007
16 of 691
Typical Duties of a Welding InspectorDuring WeldingWelding consumables in accordance with WPS in suitable condition controlled issue and handling Welding Parameters current, voltage & travel speed as WPS Root runs if possible, visually inspect root before single-sided welds are filled up
1.6
4/23/2007
17 of 691
Typical Duties of a Welding InspectorDuring WeldingInter-run cleaning in accordance with an approved method (& back gouging) to good workmanship standard Distortion control welding is balanced & over-welding is avoided
1.6
4/23/2007
18 of 691
Typical Duties of a Welding InspectorAfter WeldingWeld Identification identified/numbered as required is marked with welders identity
1.6
Visual Inspection ensure weld is suitable for all NDT visually inspect & sentence to Code requirements
Dimensional Survey ensure dimensions comply with Code/drawing
Other NDT ensure all NDT is completed & reports available19 of 691
4/23/2007
Typical Duties of a Welding InspectorAfter WeldingRepairs
1.6
monitor repairs to ensure compliance with Procedure, ensure NDT after repairs is completed PWHT monitor for compliance with Procedure check chart records confirm Procedure compliance Pressure / Load Test ensure test equipment is suitably calibrated monitor to ensure compliance with Procedure ensure all records are available
4/23/2007
20 of 691
Typical Duties of a Welding InspectorAfter WeldingDocumentation ensure any modifications are on as-built drawings ensure all required documents are available Collate / file documents for manufacturing records Sign all documentation and forward it to QC department.
1.6
4/23/2007
21 of 691
Summary of DutiesIt is the duty of a Welding Inspector to ensure all the welding and associated actions are carried out in accordance with the specification and any applicable procedures.
A Welding Inspector must: Observe To observe all relevant actions related to weld quality throughout production. Record To record, or log all production inspection points relevant to quality, including a final report showing all identified imperfections
Compare To compare all recorded information with the acceptance criteria and any other relevant clauses in the applied application standard
4/23/2007
22 of 691
Welding InspectorTerms & Definitions Section 2
4/23/2007
23 of 691
Welding Terminology & DefinitionsWhat is a Weld?
2.1
A localised coalescence of metals or non-metals produced either by heating the materials to the welding temperature, with or without the application of pressure, or by the application of pressure alone (AWS) A permanent union between materials caused by heat, and or pressure (BS499) An Autogenous weld: A weld made with out the use of a filler material and can only be made by TIG or Oxy-Gas Welding
4/23/2007
24 of 691
Welding Terminology & DefinitionsWhat is a Joint?
2.1
The junction of members or the edges of members that are to be joined or have been joined (AWS) A configuration of members (BS499)
4/23/2007
25 of 691
Joint Terminology 2.2
Edge
Open & Closed Corner
Lap
Cruciform4/23/2007
Tee
Butt26 of 691
Welded Butt Joints 2.2Butt A_________Welded butt joint
Fillet A_________Welded butt joint
Compound A____________Welded butt joint
4/23/2007
27 of 691
Welded Tee Joints 2.2
Fillet A_________Welded T joint
Butt A_________Welded T joint
Compound A____________Welded T joint
4/23/2007
28 of 691
Weld Terminology 2.3
Butt weld
Fillet weld
Spot weld
Edge weld
Plug weld Compound weld
4/23/2007
29 of 691
Butt Preparations Sizes
2.4
Partial Penetration Butt WeldActual Throat Thickness Design Throat Thickness
Full Penetration Butt WeldActual Throat Thickness
Design Throat Thickness
4/23/2007
30 of 691
Weld Zone Terminology 2.5AFace
B
Weld metalHeat Affected Zone Weld Boundary
CRoot
D
A, B, C & D = Weld Toes4/23/2007 31 of 691
Weld Zone Terminology 2.5Weld cap width
Excess Cap height or Weld Reinforcement
Actual Throat Thickness
Design Throat Thickness
Excess Root Penetration4/23/2007 32 of 691
Heat Affected Zone (HAZ) 2.5Maximum Temperature solid weld metal solid-liquid Boundary grain growth zone recrystallised zone partially transformed zone tempered zone unaffected base material
4/23/2007
33 of 691
Joint Preparation Terminology 2.7Included angleAngle of bevel Root Radius
Included angle
Root Face Root Gap Root Gap
Root Face
Single-V Butt4/23/2007
Single-U Butt34 of 691
Joint Preparation TerminologyAngle of bevel
2.8 & 2.9
Angle of bevel
Root Radius
Root Face
Root Gap
Root Gap
Root Face
Land
Single Bevel Butt4/23/2007
Single-J Butt35 of 691
Single Sided Butt Preparations
2.10
Single sided preparations are normally made on thinner materials, or when access form both sides is restricted
Single Bevel
Single Vee
Single-J4/23/2007
Single-U36 of 691
Double Sided Butt Preparations
2.11
Double sided preparations are normally made on thicker materials, or when access form both sides is unrestricted
Double -Bevel
Double -Vee
Double - J4/23/2007
Double - U37 of 691
Weld PreparationTerminology & Typical Dimensions:bevel angle included angle
V-Joints
root face root gap
Typical Dimensions bevel angle root face root gap 30 to 35 ~1.5 to ~2.5mm ~2 to ~4mm
4/23/2007
38 of 691
Butt Weld - Toe Blend6 mm
Most codes quote the weld toes shall blend smoothly
80
Poor Weld Toe Blend Angle3 mm
This statement is not quantitative and therefore open to individual interpretationThe higher the toe blend angle the greater the amount of stress concentration The toe blend angle ideally should be between 20o-30o
20
Improved Weld Toe Blend Angle4/23/2007
39 of 691
Fillet Weld Features
2.13
Excess Weld Metal
Vertical Leg Length
Design Throat
Horizontal leg Length
4/23/2007
40 of 691
Fillet Weld Throat Thickness
2.13
aa = Design Throat Thickness b = Actual Throat Thickness
b
4/23/2007
41 of 691
Deep Penetration Fillet Weld Features 2.13
aa = Design Throat Thickness b = Actual Throat Thickness
b
4/23/2007
42 of 691
Fillet Weld Sizes
2.14
Calculating Throat Thickness from a known Leg Length: Design Throat Thickness = Leg Length x 0.7 Question: The Leg length is 14mm.
What is the Design Throat?Answer: 14mm x 0.7 = 10mm Throat Thickness
4/23/2007
43 of 691
Fillet Weld Sizes
2.14
Calculating Leg Length from a known Design Throat Thickness:
Leg Length = Design Throat Thickness x 1.4Question: The Design Throat is 10mm. What is the Leg length? Answer: 10mm x 1.4 = 14mm Leg Length
4/23/2007
44 of 691
Features to Consider 2
2.14
Importance of Fillet Weld Leg Length Size(a) (b)
4mm 4mm
8mm 2mm
Approximately the same weld volume in both Fillet Welds, but the effective throat thickness has been altered, reducing considerably the strength of weld B4/23/2007 45 of 691
Fillet Weld Sizes(a)Excess
2.14
Importance of Fillet weld leg length Size(b) 6mm (a) 4mm (b) 6mmExcess
4mm
Area = 4 x 4 = 8mm2 2
Area = 6 x 6 = 18mm2 2
The c.s.a. of (b) is over double the area of (a) without the extra excess weld metal being added4/23/2007 46 of 691
Fillet Weld ProfilesFillet welds - Shape
2.15
Mitre Fillet
Convex FilletA concave profile is preferred for joints subjected to fatigue loading
Concave Fillet4/23/2007
47 of 691
Fillet Features to ConsiderEFFECTIVE THROAT THICKNESSa = Nominal throat thickness
2.15
s = Effective throat thickness
a
s
Deep penetration fillet welds from high heat input welding process MAG, FCAW & SAW etc4/23/2007 48 of 691
Welding PositionsPA PB PC PD PE PF PG H-L045 J-L0454/23/2007
2.17
1G / 1F 2F 2G 4F 4G 3G / 5G 3G / 5G 6G 6G
Flat / Downhand Horizontal-Vertical Horizontal Horizontal-Vertical (Overhead) Overhead Vertical-Up Vertical-Down Inclined Pipe (Upwards) Inclined Pipe (Downwards)49 of 691
Welding Positions
2.17
ISO
4/23/2007
50 of 691
Welding position designation 2.17Butt welds in plate (see ISO 6947)
Flat - PA Vertical up - PF
Overhead - PE
Vertical down - PG4/23/2007
Horizontal - PC51 of 691
Welding position designation 2.17Butt welds in pipe (see ISO 6947)
Flat - PAaxis: horizontal pipe: rotated
Vertical up - PF Vertical down - PGaxis: horizontal pipe: fixed axis: horizontal pipe: fixed
H-L0454/23/2007
J-L045
Horizontal - PC52 of 691
axis: inclined at 45 axis: inclined at 45 axis: vertical pipe: fixed pipe: fixed pipe: fixed
Welding position designation 2.17Fillet welds on plate (see ISO 6947)
Flat - PA
Horizontal - PB
Overhead - PD
Vertical up - PF4/23/2007
Vertical down - PG53 of 691
Welding position designation 2.17Fillet welds on pipe (see ISO 6947)
Flat - PAaxis: inclined at 45 pipe: rotated
Horizontal - PBaxis: vertical pipe: fixed
Overhead - PDaxis: vertical pipe: fixed
Horizontal - PB Vertical up - PF Vertical down - PGaxis: horizontal pipe: rotated4/23/2007
axis: horizontal pipe: fixed
axis: horizontal pipe: fixed54 of 691
Plate/Fillet Weld Positions
2.17
PA / 1G
PA / 1F PF / 3G
PB / 2F
PC / 2G
PD / 4F4/23/2007
PE / 4G
PG / 3G55 of 691
Pipe Welding Positions
2.17
PA / 1GWeld: Flat Pipe: rotated Axis: Horizontal
PF / 5GWeld: Vertical upwards Pipe: Fixed Axis: Horizontal 45o
PG / 5GWeld: Vertical Downwards Pipe: Fixed Axis: Horizontal 45o
PC / 2GWeld: Horizontal Pipe: Fixed Axis: Vertical4/23/2007
H-LO 45 / 6GWeld: Upwards Pipe: Fixed Axis: Inclined
J-LO 45 / 6GWeld: Downwards Pipe: Fixed Axis: Inclined56 of 691
Travel Speed Measurement
2.18
Definition: the rate of weld progression measured in case of mechanised and automatic welding processes in case of MMA can be determined using ROL and arc time
4/23/2007
57 of 691
Welding InspectorWelding Imperfections Section 3
4/23/2007
58 of 691
Welding ImperfectionsAll welds have imperfections
3.1
Imperfections are classed as defects when they are of a type, or size, not allowed by the Acceptance Standard
A defect is an unacceptable imperfection A weld imperfection may be allowed by one Acceptance Standard but be classed as a defect by another Standard and require removal/rectification
4/23/2007
59 of 691
Welding ImperfectionsStandards for Welding Imperfections
3.1
BS EN ISO 6520-1(1998) Welding and allied processes Classification of geometric imperfections in metallic materials Part 1: Fusion welding Imperfections are classified into 6 groups, namely: 1 Cracks 2 Cavities 3 Solid inclusions 4 Lack of fusion and penetration 5 Imperfect shape and dimensions 6 Miscellaneous imperfections
4/23/2007
60 of 691
Welding ImperfectionsStandards for Welding Imperfections
3.1
EN ISO 5817 (2003) Welding - Fusion-welded joints in steel, nickel, titanium and their alloys (beam welding excluded) - Quality levels for imperfections This main imperfections given in EN ISO 6520-1 are listed in EN ISO 5817 with acceptance criteria at 3 levels, namely
Level B (highest)Level C (intermediate) Level D (general) This Standard is directly applicable to visual testing of welds ...(weld surfaces & macro examination)
4/23/2007
61 of 691
Welding imperfections classification
3.1
Cracks
4/23/2007
62 of 691
Cracks
3.1
Cracks that may occur in welded materials are caused generally by many factors and may be classified by shape and position.Classified by Shape Longitudinal Transverse Chevron Lamellar Tear Classified by Position HAZ Centerline Crater Fusion zone Parent metal
Note: Cracks are classed as Planar Defects.4/23/2007 63 of 691
Cracks
3.1
Longitudinal parent metal
Transverse weld metal
Longitudinal weld metal Lamellar tearing4/23/2007 64 of 691
Cracks
3.1
Transverse crack4/23/2007
Longitudinal crack65 of 691
Cracks
3.2
Main Crack Types Solidification Cracks Hydrogen Induced Cracks Lamellar Tearing Reheat cracks
4/23/2007
66 of 691
CracksSolidification Cracking
3.2
Occurs during weld solidification process
Steels with high sulphur impurities content (low ductility at elevated temperature) Requires high tensile stress
Occur longitudinally down centre of weld
4/23/2007
67 of 691
Cracks
3.3
Hydrogen Induced Cold Cracking Requires susceptible hard grain structure, stress, low temperature and hydrogen Hydrogen enters weld via welding arc mainly as result of contaminated electrode or preparation
Hydrogen diffuses out into parent metal on cooling Cracking developing most likely in HAZ
4/23/2007
68 of 691
Lamellar Tearing Location: Parent metal
3.5
Steel Type: Any steel type possible Susceptible Microstructure: Poor through thickness ductility
Lamellar tearing has a step like appearance due to the solid inclusions in the parent material (e.g. sulphides and silicates) linking up under the influence of welding stresses Low ductile materials in the short transverse direction containing high levels of impurities are very susceptible to lamellar tearing It forms when the welding stresses act in the short transverse direction of the material (through thickness direction)69 of 691
4/23/2007
Gas CavitiesGas pore Cluster porosity
3.6
Causes: Loss of gas shield Damp electrodes Contamination
Blow hole Herringbone porosity
Arc length too large Damaged electrode flux Moisture on parent material Welding current too low Gas pore 1.6mm
Root piping
4/23/2007
70 of 691
Gas Cavities
3.7
Porosity
Root piping
4/23/2007
71 of 691
Gas Cavities
3.8
Cluster porosity4/23/2007
Herringbone porosity72 of 691
Crater Pipe
3.9
Weld crater
Crater pipe
4/23/2007
73 of 691
Crater Pipe
3.9
Crater pipe is a shrinkage defect and not a gas defect, it has the appearance of a gas pore in the weld crater
Crater cracks (Star cracks)
Causes:
Too fast a cooling rate Deoxidization reactions and liquid to solid volume change Contamination74 of 691
Crater pipe
4/23/2007
Solid Inclusions
3.10
Slag inclusions are defined as a non-metallic inclusion caused by some welding processCauses: Slag originates from welding fluxSlag inclusions Lack of sidewall fusion with associated slag
MAG and TIG welding process produce silica inclusions Slag is caused by inadequate cleaning
Parallel slag lines
Lack of interun fusion + slag
Other inclusions include tungsten and copper inclusions from the TIG and MAG welding process75 of 691
4/23/2007
Solid Inclusions
3.11
Interpass slag inclusions
Elongated slag lines
4/23/2007
76 of 691
Welding ImperfectionsTypical Causes of Lack of Fusion: welding current too low
3.13
bevel angle too steep root face too large (single-sided weld) root gap too small (single-sided weld) incorrect electrode angle linear misalignment welding speed too high welding process related particularly dip-transfer GMAW flooding the joint with too much weld metal (blocking Out)
4/23/2007
77 of 691
Lack of FusionCauses:
3.13
Poor welder skill Incomplete filled groove + Lack of sidewall fusion
Incorrect electrode manipulation Arc blow
1 2 1. Lack of sidewall fusion 2. Lack of inter-run fusion
Incorrect welding current/voltage Incorrect travel speed Incorrect inter-run cleaning
4/23/2007
78 of 691
Lack of Fusion
3.13
Lack of sidewall fusion + incomplete filled groove4/23/2007 79 of 691
Weld Root Imperfections
3.15
Lack of Root Fusion
Lack of Root Penetration80 of 691
4/23/2007
Cap Undercut
3.18
Intermittent Cap Undercut4/23/2007 81 of 691
Undercut
3.18
Root undercut4/23/2007
Cap undercut82 of 691
Surface and Profile
3.19
Incomplete filled groovePoor cap profiles and excessive cap reinforcements may lead to stress concentration points at the weld toes and will also contribute to overall poor toe blend
Poor cap profile
Excessive cap height83 of 691
4/23/2007
Surface and Profile
3.19
Excess cap reinforcement4/23/2007
Incomplete filled groove84 of 691
Weld Root Imperfections
3.20
Excessive root penetration4/23/2007 85 of 691
Overlap
3.21
An imperfection at the toe or root of a weld caused by metal flowing on to the surface of the parent metal without fusing to it
Causes: Contamination Slow travel speed Incorrect welding technique
Current too low
4/23/2007
86 of 691
OverlapToe Overlap
3.21
Toe Overlap
4/23/2007
87 of 691
Set-Up Irregularities
3.22
Linear misalignment is measured from the lowest plate to the highest point. Plate/pipe Linear Misalignment (Hi-Lo) Angular misalignment is measured in degrees
Angular Misalignment
4/23/2007
88 of 691
Set-Up Irregularities
3.22
Linear Misalignment4/23/2007 89 of 691
Set-Up Irregularities
3.22
Linear Misalignment
4/23/2007
90 of 691
Incomplete Groove
3.23
Lack of sidewall fusion + incomplete filled groove4/23/2007 91 of 691
Weld Root ImperfectionsCauses:
3.24
A shallow groove, which may occur in the root of a butt weld
Excessive back purge
pressure during TIG welding
Concave Root
Excessive root bead grinding before the application of the second passwelding current too high for 2nd pass overhead welding root gap too large - excessive weaving
4/23/2007
92 of 691
Weld Root Imperfections
3.24
Concave Root
4/23/2007
93 of 691
Weld Root Imperfections
3.24
Concave root4/23/2007
Excess root penetration94 of 691
Weld Root ImperfectionsA localized collapse of the weld pool due to excessive penetration resulting in a hole in the root run
3.25
Causes:
High Amps/volts Small Root face Large Root Gap Slow Travel Speed
Burn through
4/23/2007
95 of 691
Weld Root Imperfections
3.25
Burn Through
4/23/2007
96 of 691
Oxidized Root (Root Coking)Causes:
Loss or insufficient back purging gas (TIG)
Most commonly occurswhen welding stainless steels
Purging gases include argon, helium and
occasionally nitrogen4/23/2007 97 of 691
Miscellaneous ImperfectionsCauses:
3.26
Accidental striking of the arc onto the parent material Faulty electrode holder
Poor cable insulation Poor return lead clamping
Arc strike4/23/2007 98 of 691
Miscellaneous ImperfectionsCauses:
3.27
Excessive current Damp electrodes Contamination
Incorrect wire feed speed when welding with the MAG welding processArc blow99 of 691
Spatter4/23/2007
Mechanical Damage
3.28
Mechanical damage can be defined as any surface material damage cause during the manufacturing process. Grinding Hammering Chiselling Chipping Breaking off welded attachments (torn surfaces) Using needle guns to compress weld capping runs4/23/2007 100 of 691
Mechanical DamageChipping Marks
3.28
Mechanical Damage/Grinding Mark4/23/2007 101 of 691
Welding InspectorDestructive Testing Section 4
4/23/2007
102 of 691
Qualitative and Quantitative Tests 4.1The following mechanical tests have units and are termed quantitative tests to measure Mechanical Properties Tensile tests (Transverse Welded Joint, All Weld Metal) Toughness testing (Charpy, Izod, CTOD) Hardness tests (Brinell, Rockwell, Vickers)
The following mechanical tests have no units and are termed qualitative tests for assessing joint quality Macro testing Bend testing Fillet weld fracture testing Butt weld nick-break testing4/23/2007 104 of 691
Mechanical Test Samples 4.1Tensile SpecimensCTOD Specimen
Bend Test Specimen Charpy Specimen Fracture Fillet Specimen
4/23/2007
105 of 691
Destructive Testing 4.1WELDING PROCEDURE QUALIFICATION TESTING top of fixed pipe 2 Typical Positions for Test Pieces Specimen Type Macro + Hardness 3 Transverse Tensile Position 5 2, 4
Bend TestsCharpy Impact Tests 4 54/23/2007
2, 43 3
Additional Tests
106 of 691
DefinitionsMechanical Properties of metals are related to the amount of deformation which metals can withstand under different circumstances of force application.
Malleability Ductility Toughness Hardness
Ability of a material to withstand deformation under static compressive loading without rupture
Tensile Strength
4/23/2007
107 of 691
DefinitionsMechanical Properties of metals are related to the amount of deformation which metals can withstand under different circumstances of force application.
Malleability Ductility Toughness Hardness
Tensile Strength
Ability of a material undergo plastic deformation under static tensile loading without rupture. Measurable elongation and reduction in cross section area
4/23/2007
108 of 691
DefinitionsMechanical Properties of metals are related to the amount of deformation which metals can withstand under different circumstances of force application.
Malleability Ductility Toughness Hardness
Ability of a material to withstand bending or the application of shear stresses by impact loading without fracture.
Tensile Strength
4/23/2007
109 of 691
DefinitionsMechanical Properties of metals are related to the amount of deformation which metals can withstand under different circumstances of force application.
Malleability Ductility Toughness Hardness Tensile Strength
Measurement of a materials surface resistance to indentation from another material by static load
4/23/2007
110 of 691
DefinitionsMechanical Properties of metals are related to the amount of deformation which metals can withstand under different circumstances of force application.
Malleability Ductility Toughness Hardness Tensile Strength
Measurement of the maximum force required to fracture a materials bar of unit cross-sectional area in tension
4/23/2007
111 of 691
Transverse Joint Tensile Test
4.2
Weld on plate
Weld on pipe4/23/2007
Multiple cross joint specimens112 of 691
Tensile Test
4.3
All-Weld Metal Tensile Specimen
Transverse Tensile Specimen
4/23/2007
113 of 691
STRA (Short Transverse Reduction Area)For materials that may be subject to Lamellar Tearing
4/23/2007
114 of 691
UTS Tensile test
4.4
4/23/2007
115 of 691
Charpy V-Notch Impact Test 4.5
Objectives: measuring impact strength in different weld joint areas assessing resistance toward brittle fracture Information to be supplied on the test report: Material type Notch type Specimen size Test temperature Notch location Impact Strength Value
4/23/2007
116 of 691
Ductile / Brittle Transition CurveTemperature range
4.6
Ductile fracture 47 Joules
Transition range
Ductile/Brittle transition point 28 Joules Energy absorbed
Brittle fracture - 50 - 40 - 30 - 20 - 10 0 Testing temperature - Degrees Centigrade Three specimens are normally tested at each temperature4/23/2007 117 of 691
Comparison Charpy Impact Test Results 4.6Impact Energy JoulesRoom Temperature 1. 2. 3. 197 Joules 191 Joules 186 Joules -20oC Temperature 1. 2. 3. 49 Joules 53 Joules 51 Joules
Average = 191 Joules
Average = 51 Joules
The test results show the specimens carried out at room temperature absorb more energy than the specimens carried out at -20oC4/23/2007 118 of 691
Charpy V-notch impact test specimen 4.7Specimen dimensions according ASTM E23
ASTM: American Society of Testing Materials4/23/2007 119 of 691
Charpy V-Notch Impact Test 4.8Specime n Pendulu m (striker)
Anvil (support)4/23/2007 120 of 691
Charpy Impact Test22.5o 2 mm 10 mm
4.9
100% BrittleMachined notchFracture surface 100% bright crystalline brittle fracture
8 mm
100% DuctileMachined notch Large reduction in area, shear lips
Randomly torn, dull gray fracture surface4/23/2007 121 of 691
Hardness TestingDefinition
4.10
Measurement of resistance of a material against penetration of an indenter under a constant load There is a direct correlation between UTS and hardness
Hardness tests:Brinell Vickers Rockwell4/23/2007 122 of 691
Hardness TestingObjectives:
4.10
measuring hardness in different areas of a welded joint assessing resistance toward brittle fracture, cold cracking and corrosion sensitivity within a H2S (Hydrogen Sulphide) environment.
Information to be supplied on the test report: material type location of indentation type of hardness test and load applied on the indenter hardness value
4/23/2007
123 of 691
Vickers Hardness TestVickers hardness tests:
4.11
indentation body is a square based diamond pyramid (136 included angle)the average diagonal (d) of the impression is converted to a hardness number from a table it is measured in HV5, HV10 or HV025Diamond indentor Indentation Adjustable shutters
4/23/2007
124 of 691
Vickers Hardness Test Machine
4.11
4/23/2007
125 of 691
Brinell Hardness Test
4.11
Hardened steel ball of given diameter is subjected for
a given time to a given load Load divided by area of indentation gives Brinell hardness in kg/mm2 More suitable for on site hardness testing 30KN
=10mm steel ball4/23/2007 126 of 691
Rockwell Hardness TestRockwell B1KN 1.5KN
Rockwell C
=1.6mm steel ball
120 Diamond Cone
4/23/2007
127 of 691
Hardness Testingusually the hardest region fusion line or fusion boundary
4.12
1.5 to 3mm
HAZ
Hardness Test Methods Vickers Rockwell Brinell
Typical Designations 240 HV10 Rc 22 200 BHN-W
Hardness specimens can also be used for CTOD samples4/23/2007 128 of 691
Crack Tip Opening Displacement testing 4.12 Test is for fracture toughness Square bar machined with a notch placed in the centre. Tested below ambient temperature at a specified temperature. Load is applied at either end of the test specimen in an attempt to open a crack at the bottom of the notch Normally 3 samples4/23/2007 129 of 691
Fatigue Fracture
4.13
Location: Any stress concentration area
Steel Type: All steel typesSusceptible Microstructure: All grain structures Test for Fracture Toughness is CTOD (Crack Tip Opening Displacement)
4/23/2007
130 of 691
Fatigue Fracture
4.13
Fatigue cracks occur under cyclic stress conditions
Fracture normally occurs at a change in section, notch and weld defects i.e stress concentration areaAll materials are susceptible to fatigue cracking
Fatigue cracking starts at a specific point referred to as a initiation pointThe fracture surface is smooth in appearance sometimes displaying beach markings The final mode of failure may be brittle or ductile or a combination of both131 of 691
4/23/2007
Fatigue FracturePrecautions against Fatigue Cracks
Toe grinding, profile grinding.The elimination of poor profiles The elimination of partial penetration welds and weld defects Operating conditions under the materials endurance limits
The elimination of notch effects e.g. mechanical damage cap/root undercutThe selection of the correct material for the service conditions of the component132 of 691
4/23/2007
Fatigue FractureFatigue fracture occurs in structures subject to repeated application of tensile stress. Crack growth is slow (in same cases, crack may grow into an area of low stress and stop without failure).
4/23/2007
133 of 691
Fatigue FractureSecondary mode of failure ductile fracture rough fibrous appearance Fatigue fracture surface smooth in appearance
Initiation points / weld defects4/23/2007 134 of 691
Fatigue FractureFatigue fracture distinguish features: Crack growth is slow
It initiate from stress concentration points load is considerably below the design or yield stress level The surface is smooth The surface is bounded by a curve Bands may sometimes be seen on the smooth surface beachmarks. They show the progress of the crack front from the point of origin The surface is 90 to the load
Final fracture will usually take the form of gross yielding (as the maximum stress in the remaining ligament increase!) Fatigue crack need initiation + propagation periods
4/23/2007
135 of 691
Bend TestsObject of test:
4.15
To determine the soundness of the weld zone. Bend testing can also be used to give an assessment of weld zone ductility. There are three ways to perform a bend test:
Face bend Root bend Side bend
Side bend tests are normally carried out on welds over 12mm in thickness4/23/2007 136 of 691
Bending test
4.16
Types of bend test for welds (acc. BS EN 910):
t up to 12 mm
Root / face bend
Thickness of material - t t over 12 mm
Side bend
4/23/2007
137 of 691
Fillet Weld Fracture TestsObject of test:
4.17
To break open the joint through the weld to permit examination of the fracture surfaces Specimens are cut to the required length A saw cut approximately 2mm in depth is applied along the fillet welds length Fracture is usually made by striking the specimen with a single hammer blow Visual inspection for defects
4/23/2007
138 of 691
Fillet Weld Fracture TestsHammer
4.17
2mm Notch
Fracture should break weld saw cut to root4/23/2007 139 of 691
Fillet Weld Fracture Tests
4.17
This fracture indicates lack of fusion
This fracture has occurred saw cut to root
Lack of Penetration4/23/2007 140 of 691
Nick-Break TestObject of test:
4.18
To permit evaluation of any weld defects across the fracture surface of a butt weld. Specimens are cut transverse to the weld A saw cut approximately 2mm in depth is applied along the welds root and cap Fracture is usually made by striking the specimen with a single hammer blow
Visual inspection for defects
4/23/2007
141 of 691
Nick-Break TestNotch cut by hacksaw
4.18
2 mm 19 mm 2 mm
Approximately 230 mm
Weld reinforcement may or may not be removed
4/23/2007
142 of 691
Nick Break Test
4.18
Alternative nick-break test specimen, notch applied all way around the specimen
Lack of root penetration or fusion
Inclusions on fracture line
4/23/2007
143 of 691
Summary of Mechanical Testing 4.19We test welds to establish minimum levels of mechanical properties, and soundness of the welded joint We divide tests into Qualitative & Quantitative methods:
Quantitative: (Have units/numbers) To measure mechanical properties Hardness (VPN & BHN)
Qualitative: (Have no units/numbers) For assessing joint quality Macro tests
Toughness (Joules & ft.lbs)Strength (N/mm2 & PSI, MPa) Ductility / Elongation (E%)
Bend testsFillet weld fracture tests Butt Nick break tests
4/23/2007
144 of 691
Welding InspectorWPS Welder Qualifications Section 5
4/23/2007
145 of 691
Welding Procedure Qualification 5.1Question: What is the main reason for carrying out a Welding Procedure Qualification Test ? (What is the test trying to show ?) Answer: To show that the welded joint has the properties* that satisfy the design requirements (fit for purpose)
* properties mechanical properties are the main interest - always strength but toughness & hardness may be important for some applications test also demonstrates that the weld can be made without defects
4/23/2007
146 of 691
Welding ProceduresProducing a welding procedure involves: Planning the tasks
5.1
Collecting the data Writing a procedure for use of for trial Making a test welds Evaluating the results Approving the procedure
Preparing the documentation
4/23/2007
147 of 691
Welding Procedures 5.2In most codes reference is made to how the procedure are to be devised and whether approval of these procedures is required. The approach used for procedure approval depends on the code: Example codes: AWS D.1.1: Structural Steel Welding Code BS 2633: Class 1 welding of Steel Pipe Work API 1104: Welding of Pipelines BS 4515: Welding of Pipelines over 7 Bar
Other codes may not specifically deal with the requirement of a procedure but may contain information that may be used in writing a weld procedure 4/23/2007
EN 1011Process of Arc Welding Steels148 of 691
Welding Procedure Qualification 5.3(according to EN ISO 15614)
The welding engineer writes qualified Welding Procedure Specifications (WPS) for production welding
Production welding conditions must remain within the range of qualification allowed by the WPQR
4/23/2007
149 of 691
Welding Procedure Qualification(according to EN Standards)
5.3
welding conditions are called welding variables welding variables are classified by the EN ISO Standard as:
Essential variablesNon-essential variables Additional variablesNote: additional variables = ASME supplementary essential The range of qualification for production welding is based on the limits that the EN ISO Standard specifies for essential variables* (* and when applicable - the additional variables)4/23/2007 150 of 691
Welding Procedure Qualification(according to EN Standards)
5.3
WELDING ESSENTIAL VARIABLESQuestion:
Why are some welding variables classified as essential ?Answer: A variable, that if changed beyond certain limits (specified by the Welding Standard) may have a significant effect on the properties* of the joint * particularly joint strength and ductility
4/23/2007
151 of 691
Welding Procedure Qualification 5.3(according to EN Standards)
SOME TYPICAL ESSENTIAL VARIABLES Welding Process
Post Weld Heat Treatment (PWHT) Material Type Electrode Type, Filler Wire Type (Classification) Material Thickness Polarity (AC, DC+ve / DC-ve) Pre-Heat Temperature Heat Input
Welding Position
4/23/2007
152 of 691
Welding Procedures Type (Grouping) Thickness Diameter (Pipes) Surface condition)
5.3
Components of a welding procedure Parent material
Welding process Type of process (MMA, MAG, TIG, SAW etc) Equipment parameters Amps, Volts, Travel speed
Welding Consumables Type of consumable/diameter of consumable Brand/classification Heat treatments/ storage4/23/2007 153 of 691
Welding ProceduresJoint designEdge preparation Root gap, root face Jigging and tacking Type of baking
5.3
Components of a welding procedure
Welding PositionLocation, shop or site Welding position e.g. 1G, 2G, 3G etc Any weather precaution
Thermal heat treatmentsPreheat, temps Post weld heat treatments e.g. stress relieving4/23/2007 154 of 691
Welding ProceduresObject of a welding procedure test
5.3
To give maximum confidence that the welds mechanical and metallurgical properties meet the requirements of the applicable code/specification. Each welding procedure will show a range to which the procedure is approved (extent of approval) If a customer queries the approval evidence can be supplied to prove its validity
4/23/2007
155 of 691
Welding ProceduresSummary of designations: pWPS: Preliminary Welding Procedure Specification(Before procedure approval)
WPAR (WPQR): Welding Procedure Approval Record(Welding procedure Qualification record)
WPS: Welding Procedure Specification(After procedure approval)
4/23/2007
156 of 691
Example:
WeldingProcedure Specification (WPS)
4/23/2007
157 of 691
Welder Qualification
5.4
Numerous codes and standards deal with welder qualification, e.g. BS EN 287. Once the content of the procedure is approved the next stage is to approve the welders to the approved procedure. A welders test know as a Welders Qualification Test (WQT). Object of a welding qualification test: To give maximum confidence that the welder meets the quality requirements of the approved procedure (WPS). The test weld should be carried out on the same material and same conditions as for the production welds.
4/23/2007
158 of 691
Welder Qualification(according to EN Standards) Question: What is the main reason for qualifying a welder ?
5.4 & 5.5
Answer: To show that he has the skill to be able to make production welds that are free from defects Note: when welding in accordance with a Qualified WPS
4/23/2007
159 of 691
Welder Qualification (according to EN 287 )
5.5
The welder is allowed to make production welds within the range of qualification shown on the Certificate The range of qualification allowed for production welding is based on the limits that the EN Standard specifies for the welder qualification essential variables A Certificate may be withdrawn by the Employer if there is reason to doubt the ability of the welder, for example a high repair rate not working in accordance with a qualified WPS
The qualification shall remain valid for 2 years provided there is certified confirmation of welding to the WPS in that time. A Welders Qualification Certificate automatically expires if the welder has not used the welding process for 6 months or longer.4/23/2007 160 of 691
Welding Procedure Qualification 5.7(according to EN ISO 15614) Welding Engineer writes a preliminary Welding Procedure Specification (pWPS) for each test weld to be made
A welder makes a test weld in accordance with the pWPS A welding inspector records all the welding conditions used for the test weld (referred to as the as-run conditions) An Independent Examiner/ Examining Body/ Third Party inspector may be requested to monitor the qualification process The finished test weld is subjected to NDT in accordance with the methods specified by the EN ISO Standard - Visual, MT or PT & RT or UT4/23/2007 161 of 691
Welding Procedure Qualification 5.7(according to EN ISO 15614) Test weld is subjected to destructive testing (tensile, bend, macro) The Application Standard, or Client, may require additional tests such as impact tests, hardness tests (and for some materials - corrosion tests)
A Welding Procedure Qualification Record (WPQR) is prepared giving details of: The welding conditions used for the test weld Results of the NDT Results of the destructive tests The welding conditions that the test weld allows for production welding The Third Party may be requested to sign the WPQR as a true record4/23/2007 162 of 691
Welder Qualification(according to EN 287 )
5.9
An approved WPS should be available covering the range of qualification required for the welder approval. The welder qualifies in accordance with an approved WPS
A welding inspector monitors the welding to make sure that the welder uses the conditions specified by the WPSEN Welding Standard states that an Independent Examiner, Examining Body or Third Party Inspector may be required to monitor the qualification process
4/23/2007
163 of 691
Welder Qualification(according to EN 287 )
5.9
The finished test weld is subjected to NDT by the methods specified by the EN Standard - Visual, MT or PT & RT or UT The test weld may need to be destructively tested - for certain materials and/or welding processes specified by the EN Standard or the Client Specification A Welders Qualification Certificate is prepared showing the conditions used for the test weld and the range of qualification allowed by the EN Standard for production welding The Qualification Certificate is usually endorsed by a Third Party Inspector as a true record of the test
4/23/2007
164 of 691
Welder Qualification Welders name and identification number Date of test and expiry date of certificate Standard/code e.g. BS EN 287 Test piece details Welding process. Welding parameters, amps, volts Consumables, flux type and filler classification details Sketch of run sequence Welding positions Joint configuration details Material type qualified, pipe diameter etc Test results, remarks Test location and witnessed by Extent (range) of approval4/23/2007
5.10
Information that should be included on a welders test certificate are, which the welder should have or have access to a copy of !
165 of 691
Welding InspectorMaterials Inspection Section 6
4/23/2007
167 of 691
Material InspectionOne of the most important items to consider is Traceability. The materials are of little use if we can not, by use of an effective QA system trace them from specification and purchase order to final documentation package handed over to the Client. All materials arriving on site should be inspected for: Size / dimensions
Condition Type / specification In addition other elements may need to be considered depending on the materials form or shape
4/23/2007
168 of 691
Pipe Inspection(Corrosion, Damage, Wall thickness Ovality, Laminations & Seam)
We inspect the condition
Specification
LP5
Welded seam
Size
Other checks may need to be made such as: distortion tolerance, number of plates and storage.4/23/2007 169 of 691
Plate InspectionWe inspect the condition (Corrosion, Mechanical damage, Laps, Bands & Laminations) Specification5L
Size
Other checks may need to be made such as: distortion tolerance, number of plates and storage.4/23/2007 170 of 691
Parent Material ImperfectionsMechanical damage Lap
Lamination
Segregation line Laminations are caused in the parent plate by the steel making process, originating from ingot casting defects. Segregation bands occur in the centre of the plate and are low melting point impurities such as sulphur and phosphorous. Laps are caused during rolling when overlapping metal does not fuse to the base material.
4/23/2007
171 of 691
Lapping
4/23/2007
172 of 691
Lamination
4/23/2007
173 of 691
Laminations
Plate Lamination4/23/2007 174 of 691
Welding InspectorCodes & Standards Section 7
4/23/2007
175 of 691
Codes & StandardsThe 3 agencies generally identified in a code or standard: The customer, or client The manufacturer, or contractor The 3rd party inspection, or clients representative
Codes often do not contain all relevant data, but may refer to other standards
4/23/2007
176 of 691
Standard/Codes/SpecificationsSTANDARDS
SPECIFICATIONS Examples plate, pipe forgings, castings valves electrodes
CODES Examples pressure vessels bridges pipelines tanks177 of 691
4/23/2007
Welding InspectorWelding Symbols Section 8
4/23/2007
178 of 691
Weld symbols on drawingsAdvantages of symbolic representation: simple and quick plotting on the drawing does not over-burden the drawing no need for additional view gives all necessary indications regarding the specific joint to be obtained
Disadvantages of symbolic representation: used only for usual joints requires training for properly understanding of symbols4/23/2007 179 of 691
Weld symbols on drawingsThe symbolic representation includes: an arrow line a reference line an elementary symbol
The elementary symbol may be completed by: a supplementary symbol a means of showing dimensions some complementary indications4/23/2007 180 of 691
DimensionsConvention of dimensionsIn most standards the cross sectional dimensions are given to the left side of the symbol, and all linear dimensions are give on the right side
BS EN ISO 22553a = Design throat thickness s = Depth of Penetration, Throat thickness z = Leg length (min material thickness)
AWS A2.4In a fillet weld, the size of the weld is the leg length In a butt weld, the size of the weld is based on the depth of the joint preparation
4/23/2007
181 of 691
Weld symbols on drawingsA method of transferring information from the design office to the workshop is:Please weld here
The above information does not tell us much about the wishes of the designer. We obviously need some sort of code which would be understood by everyone. Most countries have their own standards for symbols. Some of them are AWS A2.4 & BS EN 22553 (ISO 2553)
4/23/2007
182 of 691
Weld symbols on drawingsJoints in drawings may be indicated: by detailed sketches, showing every dimension
by symbolic representation
4/23/2007
183 of 691
Elementary Welding Symbols(BS EN ISO 22553 & AWS A2.4)
Convention of the elementary symbols:Various categories of joints are characterised by an elementary symbol. The vertical line in the symbols for a fillet weld, single/double bevel butts and a J-butt welds must always be on the left side.
Weld typeSquare edge butt weldSingle-v butt weld
Sketch
Symbol
4/23/2007
184 of 691
Elementary Welding SymbolsWeld typeSingle-V butt weld with broad root face Single bevel butt weld Single bevel butt weld with broad root face Backing run4/23/2007 185 of 691
Sketch
Symbol
Elementary Welding SymbolsWeld typeSingle-U butt weld Single-J butt weld Surfacing
Sketch
Symbol
Fillet weld4/23/2007 186 of 691
ISO 2553 / BS EN 22553
Plug weld
Square Butt weld
Resistance spot weld
Steep flanked Single-V Butt
Resistance seam weld4/23/2007
Surfacing187 of 691
Arrow Line(BS EN ISO 22553 & AWS A2.4): Convention of the arrow line: Shall touch the joint intersection Shall not be parallel to the drawing Shall point towards a single plate preparation (when only one plate has preparation)
4/23/2007
188 of 691
Reference Line(AWS A2.4) Convention of the reference line:Shall touch the arrow line Shall be parallel to the bottom of the drawing
4/23/2007
189 of 691
Reference Line(BS EN ISO 22553) Convention of the reference line: Shall touch the arrow line Shall be parallel to the bottom of the drawing There shall be a further broken identification line above or beneath the reference line (Not necessary where the weld is symmetrical!)
or
4/23/2007
190 of 691
Double side weld symbols(BS EN ISO 22553 & AWS A2.4) Convention of the double side weld symbols:Representation of welds done from both sides of the joint intersection, touched by the arrow head
Fillet weld
Double bevel
Double J
Double V
Double U
4/23/2007
191 of 691
ISO 2553 / BS EN 22553Reference linesArrow line
Other side
Arrow side
Arrow side
Other side
4/23/2007
192 of 691
ISO 2553 / BS EN 22553MR M
Single-V Butt with permanent backing strip
Single-U Butt with removable backing strip
Single-V Butt flush cap4/23/2007
Single-U Butt with sealing run193 of 691
ISO 2553 / BS EN 22553
Single-bevel butt
Double-bevel butt
Single-bevel butt4/23/2007
Single-J butt194 of 691
ISO 2553 / BS EN 22553s10
10
15
Partial penetration single-V butt S indicates the depth of penetration4/23/2007 195 of 691
ISO 2553 / BS EN 22553a = Design throat thickness s = Depth of Penetration, Throat thickness z = Leg length(min material thickness) a = (0.7 x z)
z
a s
a44mm Design throat
z66mm leg4/23/2007
s66mm Actual throat196 of 691
ISO 2553 / BS EN 22553
Arrow side
Arrow side
4/23/2007
197 of 691
ISO 2553 / BS EN 22553s6
6mm fillet weld
Other side
s6
Other side
4/23/2007
198 of 691
ISO 2553 / BS EN 22553n = number of weld elements l = length of each weld element (e) = distance between each weld element
n x l (e)Welds to be staggered
2 x 40 (50) 3 x 40 (50)
111Process
4/23/2007
199 of 691
ISO 2553 / BS EN 22553All dimensions in mmz5 z65 5
3 x 80 (90)3 x 80 (90)
80
80
80
6 6
90
90
90
4/23/2007
200 of 691
ISO 2553 / BS EN 22553All dimensions in mmz8 3 x 80 (90) 3 x 80 (90)80
z66 6 8 8 90 80 80
90
90
4/23/2007
201 of 691
Supplementary symbols(BS EN ISO 22553 & AWS A2.4)
Convention of supplementary symbolsSupplementary information such as welding process, weld profile, NDT and any special instructions
Site Weld
Toes to be ground smoothly (BS EN only)
Concave or Convex Weld all round
4/23/2007
202 of 691
Supplementary symbols(BS EN ISO 22553 & AWS A2.4) Convention of supplementary symbolsSupplementary information such as welding process, weld profile, NDT and any special instructionsGround flush
MRRemovable backing strip
MPermanent backing strip
111Welding process numerical BS EN
Further supplementary information, such as WPS number, or NDT may be placed in the fish tail4/23/2007 203 of 691
ISO 2553 / BS EN 22553a
b
c4/23/2007
d204 of 691
ISO 2553 / BS EN 22553
Mitre
Convex
Concave
Toes shall be blended205 of 691
4/23/2007
ISO 2553 / BS EN 22553a = Design throat thickness s = Depth of Penetration, Throat thickness z = Leg length(min material thickness) a = (0.7 x z)
z
a s
a44mm Design throat
z66mm leg4/23/2007
s66mm Actual throat206 of 691
ISO 2553 / BS EN 22553 Complimentary Symbols
Field weld (site weld)
Welding to be carried out all round component (peripheral weld)
NDT The component requires NDT inspection
WPS Additional information, the reference document is included in the box207 of 691
4/23/2007
ISO 2553 / BS EN 22553Numerical Values for Welding Processes:111: 121: 131: 135: 136: 141: 311: 72: 15:4/23/2007
MMA welding with covered electrode Sub-arc welding with wire electrode MIG welding with inert gas shield MAG welding with non-inert gas shield Flux core arc welding TIG welding Oxy-acetylene welding Electro-slag welding Plasma arc welding208 of 691
AWS A2.4 Welding Symbols
4/23/2007
209 of 691
AWS Welding Symbols
Depth of Bevel 1(1-1/8) 1/8 60o
Root Opening
Effective Throat
Groove Angle
4/23/2007
210 of 691
AWS Welding SymbolsWelding Process
GSFCAW 1(1-1/8) 1/8 60o
GMAW
GTAWSAW
4/23/2007
211 of 691
AWS Welding SymbolsWelds to be staggered
3 10 3 103SMAW Process
3
104/23/2007 212 of 691
AWS Welding SymbolsSequence of Operations 3rd Operation2nd Operation
1st Operation1(1-1/8) 1/8 60o
FCAW
4/23/2007
213 of 691
AWS Welding SymbolsSequence of Operations RT MT MT1(1-1/8)
FCAW1/8 60o
4/23/2007
214 of 691
AWS Welding SymbolsDimensions- Leg Length
6 leg on member A 6/8
Member A
6 8
Member B4/23/2007 215 of 691
Welding InspectorIntro To Welding Processes Section 9
4/23/2007
221 of 691
Welding ProcessesWelding is regarded as a joining process in which the work pieces are in atomic contact
Pressure welding Forge welding Friction welding
Fusion welding Oxy-acetylene MMA (SMAW)
Resistance Welding
MIG/MAG (GMAW) TIG (GTAW) Sub-arc (SAW) Electro-slag (ESW) Laser Beam (LBW) Electron-Beam (EBW)
4/23/2007
222 of 691
Constant Current Power Source (Drooping Characteristic)100 90 80 70
O.C.V. Striking voltage (typical) for arc initiation Required for: MMA, TIG, Plasma arc and SAW > 1000 AMPS
Voltage
60 50
4030 20
Normal Operating Voltage Range
Large voltage variation, e.g. + 10v (due to changes in arc length)
10 204/23/2007
Small amperage change resulting in virtually constant current e.g. + 5A.40 60 80 100 120 130 140 160 180 200225 of 691
Amperage
Monitoring Heat Input Heat Input: The amount of heat generated in the welding arc per unit length of weld. Expressed in kilo Joules per millimetre length of weld (kJ/mm).
Heat Input (kJ/mm)= Volts x Amps Travel speed(mm/s) x 10004/23/2007 227 of 691
Monitoring Heat Input
Weld and weld pool temperatures
4/23/2007
228 of 691
Monitoring Heat Input
4/23/2007
229 of 691
Monitoring Heat Input Monitoring Heat Input As Required by BS EN ISO 15614-1:2004 In accordance with EN 1011-1:1998When impact requirements and/or hardness requirements are specified, impact test shall be taken from the weld in the highest heat input position and hardness tests shall be taken from the weld in the lowest heat input position in order to qualify for all positions
4/23/2007
230 of 691
Welding InspectorMMA Welding Section 10
4/23/2007
231 of 691
MMA - Principle of operation
4/23/2007
233 of 691
MMA weldingMain features: Shielding provided by decomposition of flux covering Electrode consumable Manual process
Welder controls: Arc length Angle of electrode Speed of travel Amperage settings234 of 691
4/23/2007
Manual Metal Arc Basic Equipment
Control panel (amps, volts) Electrode oven Electrodes Return lead
Power source Holding oven Inverter power source Electrode holder
Welding visor filter glass
Power cables
4/23/2007
235 of 691
MMA Welding PlantTransformer: Changes mains supply voltage to a voltage suitable for welding. Has no moving parts and is often termed static plant. Rectifier: Changes a.c. to d.c., can be mechanically or statically achieved. Generator: Produces welding current. The generator consists of an armature rotating in a magnetic field, the armature must be rotated at a constant speed either by a motor unit or, in the absence of electrical power, by an internal combustion engine. Inverter: An inverter changes d.c. to a.c. at a higher frequency.
4/23/2007
236 of 691
MMA Welding VariablesVoltage The arc voltage in the MMA process is measured as close to the arc as possible. It is variable with a change in arc length O.C.V. The open circuit voltage is the voltage required to initiate, or re-ignite the electrical arc and will change with the type of electrode being used e.g 70-90 volts Current The current used will be determined by the choice of electrode, electrode diameter and material type and thickness. Current has the most effect on penetration. Polarity Polarity is generally determined by operation and electrode type e.g DC +ve, DC ve or AC4/23/2007 237 of 691
Constant Current Power Source (Drooping Characteristic)10090 80 70
O.C.V. Striking voltage (typical) for arc initiation
Voltage
60 50 40 30 20 10 20 40 60 80 100 120 130 140 160 180
Normal Operating Voltage Range
Large voltage variation, e.g. + 10v (due to changes in arc length) Small amperage change resulting in virtually constant current e.g. + 5A.200 239 of 691
Amperage4/23/2007
MMA welding parametersTravel speedToo low wide weld bead contour lack of penetration burn-through Travel speed Too high lack of root fusion incomplete root penetration undercut poor bead profile, difficult slag removal
4/23/2007
240 of 691
MMA welding parametersType of current: voltage drop in welding cables is lower with AC inductive looses can appear with AC if cables are coiled cheaper power source for AC no problems with arc blow with AC DC provides a more stable and easy to strike arc, especially with low current, better positional weld, thin sheet applications welding with a short arc length (low arc voltage) is easier with DC, better mechanical properties DC provides a smoother metal transfer, less spatter
4/23/2007
241 of 691
MMA welding parametersWelding current approx. 35 A/mm of diameter governed by thickness, type of joint and welding
positionToo low poor starting slag inclusions weld bead contour too high lack of fusion/penetration4/23/2007
Welding current
Too high spatter excess penetration undercut burn-through
242 of 691
MMA welding parametersArc length = arc voltageToo low arc can be extinguished stubbing Arc voltage Too high spatter porosity excess penetration undercut burn-through
Polarity: DCEP generally gives deeper penetration4/23/2007 243 of 691
MMA - Troubleshooting
MMA quality (left to right)current, arc length and travel speed normal; current too low; current too high; arc length too short; arc length too long; travel speed too slow; travel speed too high
4/23/2007
244 of 691
MMA electrode holder
Collet or twist type4/23/2007
Tongs type with spring-loaded jaws245 of 691
MMA Welding Consumables MMA Covered ElectrodesThe three main electrode covering types used in MMA welding
Cellulosic - deep penetration/fusion Rutile - general purpose Basic - low hydrogen(Covered in more detail in Section 14)
4/23/2007
246 of 691
MMA welding typical defectsMost welding defects in MMA are caused by a lack of welder skill (not an easily controlled process), the incorrect settings of the equipment, or the incorrect use, and treatment of electrodes Typical Welding Defects: Slag inclusions Arc strikes Porosity Undercut Shape defects (overlap, excessive root penetration, etc.)
4/23/2007
247 of 691
Manual Metal Arc Welding (MMA)Advantages: Field or shop use Range of consumables All positions Portable Simple equipment High welder skill required High levels of fume Hydrogen control (flux) Stop/start problems Comparatively uneconomic when compared with some other processes i.e MAG, SAW and FCAW
Disadvantages:
4/23/2007
248 of 691
Welding InspectorTIG Welding Section 11
4/23/2007
249 of 691
Tungsten Inert Gas WeldingThe TIG welding process was first developed in the USA during the 2nd world war for the welding of aluminum alloys The process uses a non-consumable tungsten electrode The process requires a high level of welder skill The process produces very high quality welds. The TIG process is considered as a slow process compared to other arc welding processes The arc may be initiated by a high frequency to avoid scratch starting, which could cause contamination of the tungsten and weld
4/23/2007
250 of 691
TIG - Principle of operation
4/23/2007
251 of 691
TIG Welding VariablesVoltageThe voltage of the TIG welding process is variable only by the type of gas being used, and changes in the arc length
CurrentThe current is adjusted proportionally to the tungsten electrodes diameter being used. The higher the current the deeper the penetration and fusion
PolarityThe polarity used for steels is always DC ve as most of the heat is concentrated at the +ve pole, this is required to keep the tungsten electrode at the cool end of the arc. When welding aluminium and its alloys AC current is used4/23/2007 254 of 691
Types of currentDC can be DCEN or DCEP DCEN gives deep penetration can be sine or square wave requires a HF current (continuos or periodical) provide cleaning action
AC Type of welding current
4/23/2007
Pulsed requires special power source current low frequency - up to 20 pulses/sec (thermal pulsing) better weld pool control weld pool partially solidifies 256 of 691 between pulses
Choosing the proper electrodeCurrent type influence
+ + + + +
+
+
+ +
-
Current type & polarity Heat balance Penetration Oxide cleaning action Electrode capacity4/23/2007
DCEN 70% at work 30% at electrode Deep, narrow No Excellent (e.g. 3,2 mm/400A)
AC (balanced) 50% at work 50% at electrode Medium Yes - every half cycle Good (e.g. 3,2 mm/225A)
DCEP 35% at work 65% at electrode Shallow, wide Yes Poor (e.g. 6,4 mm/120A)257 of 691
ARC CHARACTERISTICSConstant Current/Amperage CharacteristicLarge change in voltage = Smaller change in amperageOCV
VoltsLarge arc gap Welding Voltage Small arc gap
Amps4/23/2007 258 of 691
TIG - arc initiation methodsArc initiation method Lift arc simple method tungsten electrode is in contact with the workpiece! high initial arc current due to the short circuit impractical to set arc length in advance electrode should tap the workpiece - no scratch! ineffective in case of AC used when a high quality is not essential4/23/2007
HF startneed a HF generator (sparkgap oscillator) that generates a high voltage AC output (radio frequency) costly reliable method required on both DC (for start) and AC (to re-ignite the arc) can be used remotely HF produce interference requires superior insulation259 of 691
Pulsed current usually peak current is 2-10 times Pulse Cycle Peak Background background current time time current current useful on metals sensitive to high heat input reduced distortions in case of dissimilar thicknesses equal penetration can be achievedCurrent (A)
Average current Time
one set of variables can be used in all positions used for bridging gaps in open root joints require special power source4/23/2007 260 of 691
Choosing the proper electrodePolarity Influence cathodic cleaning effect
4/23/2007
261 of 691
Tungsten ElectrodesOld types: (Slightly Radioactive) Thoriated: DC electrode -ve - steels and most metals 1% thoriated + tungsten for higher current values 2% thoriated for lower current values Zirconiated: AC - aluminum alloys and magnesium
New types: (Not Radioactive) Cerium: DC electrode -ve - steels and most metals Lanthanum: AC - Aluminum alloys and magnesium
4/23/2007
262 of 691
TIG torch set-up Electrode extension
StickoutElectrode extension
2-3 times electrode diameter
Low electron emission Unstable arc4/23/2007
Too small
Electrode extension
Too large
Overheating Tungsten inclusions263 of 691
Choosing the correct electrodePolarity Influence cathodic cleaning effect
4/23/2007
264 of 691
Tungsten ElectrodesOld types: (Slightly Radioactive) Thoriated: DC electrode -ve - steels and most metals 1% thoriated + tungsten for higher current values 2% thoriated for lower current values Zirconiated: AC - aluminum alloys and magnesium
New types: (Not Radioactive) Cerium: DC electrode -ve - steels and most metals Lanthanum: AC - Aluminum alloys and magnesium
4/23/2007
265 of 691
Tungsten electrode typesPure tungsten electrodes:colour code - green no alloy additions low current carrying capacity maintains a clean balled end can be used for AC welding of Al and Mg alloys poor arc initiation and arc stability with AC compared with other electrode types used on less critical applications low cost4/23/2007 266 of 691
Tungsten electrode typesThoriated tungsten electrodes:colour code - yellow/red/violet
20% higher current carrying capacity compared to pure tungsten electrodeslonger life - greater resistance to contamination
thermionic - easy arc initiation, more stable arcmaintain a sharpened tip
recommended for DCEN, seldom used on AC (difficult to maintain a balled tip)This slightly radioactive4/23/2007 267 of 691
Tungsten electrode typesCeriated tungsten electrodes:colour code - grey (orange acc. AWS A-5.12)
operate successfully with AC or DCCe not radioactive - replacement for thoriated types
Lanthaniated tungsten electrodes:colour code - black/gold/blue
operating characteristics similar with ceriated electrode
4/23/2007
268 of 691
Tungsten electrode typesZirconiated tungsten electrodes:colour code - brown/white
operating characteristics fall between those of pure and thoriated electrodesretains a balled end during welding - good for AC welding high resistance to contamination preferred for radiographic quality welds
4/23/2007
269 of 691
Electrode tip for DCENPenetration increase2-2,5 times electrode diameter
IncreaseVertex angle
Decrease Bead width increaseElectrode tip prepared for low current welding4/23/2007
Electrode tip prepared for high current welding270 of 691
Electrode tip for ACDC -ve AC
Electrode tip ground4/23/2007
Electrode tip ground and then conditioned271 of 691
TIG Welding VariablesTungsten electrodesThe electrode diameter, type and vertex angle are all critical factors considered as essential variables. The vertex angle is as shown
DC -ve
AC
Vetex angle Note: too fine an angle will promote melting of the electrodes tip4/23/2007
Note: when welding aluminium with AC current, the tungsten end is chamfered and forms a ball end when welding272 of 691
Choosing the proper electrodeFactors to be considered: Electrode tip not properly heated Excessive melting or volatilisation
Too low
Welding current
Too high
Unstable arc
Penetration
Tungsten inclusions
4/23/2007
273 of 691
Shielding gas requirements Preflow and postflowShielding gas flow Welding current
Preflow
Postflow
Flow rate too low
Flow rate too high
4/23/2007
275 of 691
Special shielding methodsPipe root run shielding Back Purging to prevent excessive oxidation during welding, normally argon.
4/23/2007
276 of 691
TIG torch set-upElectrode extension
StickoutElectrode extension
2-3 times electrode diameter
Low electron emission Unstable arc4/23/2007
Too small
Electrode extension
Too large
Overheating Tungsten inclusions277 of 691
TIG Welding ConsumablesWelding consumables for TIG: Filler wires, Shielding gases, tungsten electrodes (nonconsumable). Filler wires of different materials composition and variable diameters available in standard lengths, with applicable code stamped for identification Steel Filler wires of very high quality, with copper coating to resist corrosion. shielding gases mainly Argon and Helium, usually of highest purity (99.9%).
4/23/2007
278 of 691
Tungsten InclusionMay be caused by Thermal Shock of heating to fast and small fragments break off and enter the weld pool, so a slope up device is normally fitted to prevent this could be caused by touch down also.Most TIG sets these days have slopeup devices that brings the current to the set level over a short period of time so the tungsten is heated more slowly and gently
A Tungsten Inclusion always shows up as bright white on a radiograph4/23/2007 279 of 691
TIG typical defectsMost welding defects with TIG are caused by a lack of welder skill, or incorrect setting of the equipment. i.e. current, torch manipulation, welding speed, gas flow rate, etc.
Tungsten inclusions (low skill or wrong vertex angle) Surface porosity (loss of gas shield mainly on site) Crater pipes (bad weld finish technique i.e. slope out)
Oxidation of S/S weld bead, or root by poor gas cover Root concavity (excess purge pressure in pipe) Lack of penetration/fusion (widely on root runs)
4/23/2007
280 of 691
Tungsten Inert Gas WeldingAdvantages High quality
Disadvantages High skill factor required
Good control All positions Lowest H2 process Minimal cleaning Autogenous welding
Low deposition rate Small consumable range High protection required Complex equipment Low productivity
(No filler material) Can be automated4/23/2007
High ozone levels +HF
281 of 691
Welding InspectorMIG/MAG Welding Section 12
4/23/2007
282 of 691
Gas Metal Arc WeldingThe MIG/MAG welding process was initially developed in the USA in the late 1940s for the welding of aluminum alloys. The latest EN Welding Standards now refer the process by the American term GMAW (Gas Metal Arc Welding) The process uses a continuously fed wire electrode The weld pool is protected by a separately supplied shielding gas The process is classified as a semi-automatic welding process but may be fully automated The wire electrode can be either bare/solid wire or flux cored hollow wire
4/23/2007
283 of 691
MIG/MAG - Principle of operation
4/23/2007
284 of 691
MIG/MAG process variables Welding currentIncreasing welding current Increase in depth and width Increase in deposition rate
Polarity
4/23/2007
286 of 691
MIG/MAG process variables Arc voltage
Increasing arc voltage Reduced penetration, increased width Excessive voltage can cause porosity, spatter and undercut
Travel speedIncreasing travel speed Reduced penetration and width, undercut4/23/2007 287 of 691
Gas Metal Arc WeldingTypes of Shielding Gas MIG (Metal Inert Gas) Inert Gas is required for all non-ferrous alloys (Al, Cu, Ni) Most common inert gas is Argon Argon + Helium used to give a hotter arc - better for thicker joints and alloys with higher thermal conductivity
4/23/2007
289 of 691
MIG/MAG shielding gasesType of material Shielding gasCO2 , Ar+(5-20)%CO2
Carbon steel
Stainless steel
Ar+2%O2
Aluminium
Ar
4/23/2007
290 of 691
MIG/MAG shielding gasesAr Ar-He He CO2
Argon (Ar): higher density than air; low thermal conductivity the arc has a high energy inner cone; good wetting at the toes; low ionisation potential Helium (He): lower density than air; high thermal conductivity uniformly distributed arc energy; parabolic profile; high ionisation potential Carbon Dioxide (CO2): cheap; deep penetration profile; cannot support spray transfer; poor wetting; high spatter4/23/2007 291 of 691
MIG/MAG shielding gasesGases for dip transfer: CO2: carbon steels only: deep penetration; fast welding speed; high spatter levels Ar + up to 25% CO2: carbon and low alloy steels: minimum spatter; good wetting and bead contour 90% He + 7.5% Ar + 2.5% CO2:stainless steels: minimises undercut; small HAZ Ar: Al, Mg, Cu, Ni and their alloys on thin sections
Ar + He mixtures: Al, Mg, Cu, Ni and their alloys on thicker sections (over 3 mm)4/23/2007 292 of 691
MIG/MAG shielding gasesGases for spray transfer Ar + (5-18)% CO2: carbon steels: minimum spatter; good wetting and bead contour Ar + 2% O2: low alloy steels: minimise undercut; provides good toughness Ar + 2% O2 or CO2: stainless steels: improved arc stability; provides good fusion Ar: Al, Mg, Cu, Ni, Ti and their alloys Ar + He mixtures: Al, Cu, Ni and their alloys: hotter arc than pure Ar to offset heat dissipation Ar + (25-30)% N2: Cu alloys: greater heat input4/23/2007 293 of 691
Gas Metal Arc WeldingTypes of Shielding Gas MAG (Metal Active Gas) Active gases used are Oxygen and Carbon Dioxide Argon with a small % of active gas is required for all steels (including stainless steels) to ensure a stable arc & good droplet wetting into the weld pool Typical active gases are Ar + 20% CO2 for C-Mn & low alloy steels Ar + 2% O2 100% CO24/23/2007
for stainless steels can be used for C - steels294 of 691
MIG/MAG Gas Metal Arc WeldingElectrode orientation
PenetrationUndercut
Deep
Moderate Shallow
Excess weld metal Maximum Moderate Minimum Severe Moderate Minimum
Electrode extension4/23/2007
Increased extension
295 of 691
MIG / MAG - self-regulating arcStable conditionArc length L = 6,4 mm Arc voltage = 24V Welding current = 250A WFS = 6,4 m/min Melt off rate = 6,4 m/min
Sudden change in gun positionArc length L = 12,7 mm Arc voltage = 29V Welding current = 220A WFS = 6,4 m/min Melt off rate = 5,6 m/min
L
19 mm
L
25 mm
Voltage (V)
Current (A)4/23/2007 296 of 691
MIG/MAG - self-regulating arcSudden change in gun positionArc length L = 12,7 mm Arc voltage = 29V Welding current = 220A WFS = 6,4 m/min Melt off rate = 5,6 m/min
Re-established stable conditionArc length L = 6,4 mm Arc voltage = 24V Welding current = 250A WFS = 6,4 m/min Melt off rate = 6,4 m/min
L
25 mm L
25 mm
Voltage (V)
Current (A)4/23/2007 297 of 691
Terminating the arcCrater fill Burnback time delayed current cut-off to prevent wire freeze in the weld end crater depends on WFS (set as short as possible!)Contact tip3 mm 8 mm 14 mm Insulatin g slag Burnback time 0.05 sec Workpiec e4/23/2007
Current - 250A Voltage - 27V WFS - 7,8 m/min Wire diam. - 1,2 mm Shielding gas Ar+18%CO2298 of 691
0.10 sec
0.15 sec
MIG/MAG - metal transfer modes
Contact tip extension (0-3,2 mm)
Electrode extension 6-13 mm
Contact tip recessed (3-5 mm)
Electrode extension 19-25 mm
Set-up for dip transfer4/23/2007
Set-up for spray transfer299 of 691
MIG/MAG - metal transfer modesVoltageElectrode diameter = 1,2 mm WFS = 8,3 m/min
Current = 295 AVoltage = 28V
Globular transfer
Spray transferElectrode diameter = 1,2 mm WFS = 3,2 m/min Current = 145 A
Dip transfer
Voltage = 18-20V
Current
4/23/2007
Current/voltage conditions
301 of 691
MIG/MAG-methods of metal transferDip transferTransfer occur due to short circuits between wire and weld pool, high level of spatter, need inductance control to limit current raise
Can use pure CO2 or Ar- CO2 mixtures as shielding gasMetal transfer occur when arc is extinguished
Requires low welding current/arc voltage, a low heat input process. Resulting in low residual stress and distortion Used for thin materials and all position welds4/23/2007 303 of 691
MIG/MAG-methods of metal transferSpray transferTransfer occur due to pinch effect NO contact between wire and weld pool! Requires argon-rich shielding gas Metal transfer occur in small droplets, a large volume weld pool Requires high welding current/arc voltage, a high heat input process. Resulting in high residual stress and distortion Used for thick materials and flat/horizontal position welds4/23/2007 306 of 691
MIG/MAG-methods of metal transferPulsed transfer Controlled metal transfer, one droplet per pulse, No transfer between droplet and weld pool! Requires special power sources
Metal transfer occur in small droplets (diameter equal to that of electrode)Requires moderate welding current/arc voltage, a reduced heat input . Resulting in smaller residual stress and distortion compared to spray transfer Pulse frequency controls the volume of weld pool, used for root runs and out of position welds4/23/2007 307 of 691
MIG/MAG - metal transfer modesPulsed transferControlled metal transfer. one droplet per pulse. NO transfer during background current! Requires special power sources Metal transfer occur in small droplets (diameter equal to that of electrode) Requires moderate welding current/arc voltage, reduced heat input smaller residual stress and distortions compared to spray transfer Pulse frequency controls the volume of weld pool, used for root runs and out of position welds4/23/2007 308 of 691
MIG/MAG-methods of metal transferGlobular transferTransfer occur due to gravity or short circuits between drops and weld pool Requires CO2 shielding gas Metal transfer occur in large drops (diameter larger than that of electrode) hence severe spatter Requires high welding current/arc voltage, a high heat input process. Resulting in high residual stress and distortion Non desired mode of transfer!
4/23/2007
310 of 691
Flat or Constant Voltage CharacteristicFlat or Constant Voltage Characteristic Used With MIG/MAG, ESW & SAW < 1000 ampsO.C.V. Arc Voltage Virtually no Change.
33 32 31
Voltage
Small Voltage Change. Large Current Change
100
Amperage
200
300
4/23/2007
315 of 691
MIG/MAG welding gun assemblyContact tip Gas diffuser The Push-Pull gun
Union nut
Gas nozzle
Trigger
Handle4/23/2007
WFS remote control potentiometer
316 of 691
Gas Metal Arc WeldingPROCESS CHARACTERISTICS
Requires a constant voltage power source, gas supply, wire feeder, welding torch/gun and hose package Wire is fed continuously through the conduit and is burnt-off at a rate that maintains a constant arc length/arc voltage Wire feed speed is directly related to burn-off rate Wire burn-off rate is directly related to current When the welder holds the welding gun the process is said to be a semi-automatic process The process can be mechanised and also automated In Europe the process is usually called MIG or MAG4/23/2007 318 of 691
MIG/MAG typical defectsMost welding imperfections in MIG/MAG are caused by lack of welder skill, or incorrect settings of the equipment Worn contact tips will cause poor power pick up, or transfer
Bad power connections will cause a loss of voltage in the arcSilica inclusions (in Fe steels) due to poor inter-run cleaning Lack of fusion (primarily with dip transfer)
Porosity (from loss of gas shield on site etc)Solidification problems (cracking, centerline pipes, crater pipes) especially on deep narrow welds
4/23/2007
322 of 691
WELDING PROCESSFlux Core Arc Welding (Not In The Training Manual)
4/23/2007
323 of 691
Flux cored arc weldingFCAW methods
With gas shielding Outershield
Without gas shielding Innershield
With metal powder Metal core
4/23/2007
324 of 691
Outershield - principle of operation
4/23/2007
325 of 691
Innershield - principle of operation
4/23/2007
326 of 691
ARC CHARACTERISTICSConstant Voltage Characteristic
OCVLarge arc gap Small arc gap
Small change in voltage = large change in amperage
Volts
The self adjusting arc.
Amps4/23/2007 327 of 691
Flux Core Arc Welding (FCAW)Flux core Insulated extension nozzle
Current carrying guild tubeWire joint Flux cored hollow wire
Flux powderArc shield composed of vaporized and slag forming compounds
Flux core wires
4/23/2007
Solidified weld metal and slag
Molten weld pool
Metal droplets covered with thin slag coating328 of 691
Flux cored arc weldingFCAW methods
With gas shielding Outershield
Without gas shielding Innershield (114)
With metal powder Metal core
With active gas shielding (136)4/23/2007
With inert gas shielding (137)329 of 691
FCAW - differences from MIG/MAG usually operates in DCEP but some Innershield wires operates in DCEN power sources need to be more powerful due to the higher currents doesn't work in deep transfer mode require knurled feed rolls Innershield wires use a different type of welding gun4/23/2007 330 of 691
Backhand (drag) techniqueAdvantagespreferred method for flat or horizontal position slower progression of the weld deeper penetration weld stays hot longer, easy to remove dissolved gasses
Disadvantagesproduce a higher weld profile difficult to follow the weld joint can lead to burn-through on thin sheet plates4/23/2007 331 of 691
Forehand (push) techniqueAdvantagespreferred method for vertical up or overhead position arc is directed towards the unwelded joint , preheat effect easy to follow the weld joint and control the penetration
Disadvantagesproduce a low weld profile, with coarser ripples fast weld progression, shallower depth of penetration the amount of spatter can increase
4/23/2007
332 of 691
FCAW advantages less sensitive to lack of fusion requires smaller included angle compared to MMA high productivity all positional smooth bead surface, less danger of undercut basic types produce excellent toughness properties good control of the weld pool in positional welding especially with rutile wires seamless wires have no torsional strain, twist free ease of varying the alloying constituents no need for shielding gas4/23/2007 333 of 691
FCAW disadvantages limited to steels and Ni-base alloys slag covering must be removed FCAW wire is more expensive on a weight basis than solid wires (exception: some high alloy steels) for gas shielded process, the gaseous shield may be affected by winds and drafts more smoke and fumes are generated compared with MIG/MAG in case of Innershield wires, it might be necessary to break the wire for restart (due to the high amount of insulating slag formed at the tip of the wire)
4/23/2007
334 of 691
FCAW advantages/disadvantagesAdvantages: Disadvantages:
1) Field or shop use2) High productivity 3) All positional 4) Slag supports and shapes the weld Bead
1) High skill factor2) Slag inclusions 3) Cored wire is Expensive 4) High level of fume (Inner-shield) 5) Limited to steels and nickel alloys335 of 691
5) No need for shielding gas
4/23/2007
Welding InspectorSubmerged Arc Welding Section 13
4/23/2007
336 of 691
Submerged Arc Welding Introduction Submerged arc welding was developed in the Soviet Union during the 2nd world war for the welding of thick section steel. The process is normally mechanized. The process uses amps in the range of 100 to over 2000, which gives a very high current density in the wire producing deep penetration and high dilution welds. A flux is supplied separately via a flux hopper in the form of either fused or agglomerated. The arc is not visible as it is submerged beneath the flux layer and no eye protection is required.
4/23/2007
337 of 691
SAW Principle of operation
4/23/2007
338 of 691
Principles of operationFactors that determine whether to use SAW chemical composition and mechanical properties required for the weld deposit thickness of base metal to be welded joint accessibility position in which the weld is to be made frequency or volume of welding to be performed
SAW methods
Semiautomatic4/23/2007
Mechanised
Auto