This information and all further technical advice is based on our present knowledge and experience. However, it implies no liability or other legal responsibility on our part, including with regard to existing third party intellectual property rights, especially patent rights. In particular, no warranty, whether express or implied, or guarantee of product properties in the legal sense is intended or implied. We reserve the right to make any changes according to technological progress or further developments. The customer is not released from the obligation to conduct careful inspection and testing of incoming goods. Performance of the product described herein should be verified by testing, which should be carried out only by qualified experts in the sole responsibility of a customer. Reference to trade names used by other companies is neither a recommendation, nor does it imply that similar products could not be used.
Product Information
Internet: www.dynasylan.com
E-mail: [email protected]
Evonik Degussa GmbH
Aerosil & Silanes
Weissfrauenstraße 9 D-60287 Frankfurt am Main
Germany
Phone: +49-69-218-5656 Fax: +49-69-218-3967
Evonik Degussa Corporation Aerosil & Silanes
379 Interpace Parkway P.O. Box 677 Parsippany
NJ 07054-0677 USA
Phone:
800-237-6745 (Toll Free) +1-973-541-8513
Fax: +1-973-541-8503
Evonik Degussa (China) Co., Ltd.
Aerosil & Silanes 55, Chundong Road
Xinzhuang Industry Park Shanghai 201108
P.R. China
Phone: +86-21-6119-1052 Fax: +86-21-6119-1075
Page 1 of 5
Dynasylan® SIVO 110
SIVO® SOL Technology for coating systems
Description Dynasylan
® SIVO 110 resembles a multifunctional, basically VOC-free, water-borne sol-gel
system. It is composed of a silica sol, modified with organofunctional silanes. Dynasylan
® SIVO 110 is an opaque to milky, colorless to slightly yellow, low viscous liquid.
Dynasylan® SIVO 110 can be diluted in water and a variety of common organic solvents. Besides
reactive silanol groups it also contains organic functionalities based on Si-bonded epoxy groups. Fig.1 Distribution of functionalized SiO2 sol-particles in Dynasylan
® SIVO 110 (by laser light
scattering) Dynasylan
® SIVO 110 is predominantly suited as a binder for temperature curing sol-gel coatings
and for sol-gel - based hybrid coatings. Featured specific advantages:
• water-borne
• VOC-free
• forms very thin layers (< 2 µm)
• resistant against boiling water
• exceptional hardness
• thermally stable up to approx. 220 °C
This information and all further technical advice is based on our present knowledge and experience. However, it implies no liability or other legal responsibility on our part, including with regard to existing third party intellectual property rights, especially patent rights. In particular, no warranty, whether express or implied, or guarantee of product properties in the legal sense is intended or implied. We reserve the right to make any changes according to technological progress or further developments. The customer is not released from the obligation to conduct careful inspection and testing of incoming goods. Performance of the product described herein should be verified by testing, which should be carried out only by qualified experts in the sole responsibility of a customer. Reference to trade names used by other companies is neither a recommendation, nor does it imply that similar products could not be used.
Product Information
Internet: www.dynasylan.com
E-mail: [email protected]
Evonik Degussa GmbH
Aerosil & Silanes
Weissfrauenstraße 9 D-60287 Frankfurt am Main
Germany
Phone: +49-69-218-5656 Fax: +49-69-218-3967
Evonik Degussa Corporation Aerosil & Silanes
379 Interpace Parkway P.O. Box 677 Parsippany
NJ 07054-0677 USA
Phone:
800-237-6745 (Toll Free) +1-973-541-8513
Fax: +1-973-541-8503
Evonik Degussa (China) Co., Ltd.
Aerosil & Silanes 55, Chundong Road
Xinzhuang Industry Park Shanghai 201108
P.R. China
Phone: +86-21-6119-1052 Fax: +86-21-6119-1075
Page 2 of 5
Technical Data
Properties Value Unit Method
Density (20 °C) approx. 1.14 g/cm³ DIN 51757
Viscosity (20 °C) approx. 7 mPa.s DIN 53015
Flash point >95 °C EN 22719
Boiling point approx. 96 °C ASTM D-1120
pH-value approx. 4.3 DIN 19268
Solid content approx. 35 % 3g / 2h 105 °C
Reactivity Dynasylan
® SIVO 110 resembles a water-borne sol-gel system which does not contain organic
solvents. It does not release alcohols upon hydrolysis contrary to standard functional alkoxysilanes. Dynasylan
® SIVO 110 contains a high concentration of active silanol functions.
Consequently it can chemically bond to surfaces of suited substrates and achieves a high degree of crosslinking by formation of 2- and 3-dimensional siloxane networks. During curing functionalized SiO2 sol-particles align into a densely packed structure and are covalently incorporated into the siloxane network (see fig.2 and 3). This phenomenon serves as an explanation why exceptional hardness and scratch resistance can be achieved with Dynasylan
®
SIVO 110. Additionally a high degree of flexibility is obtained at a considerably low thickness fo the formed layers. Suited substrates: steel, stainless steel, Zn-galvanized steel, aluminum, glass. Dynasylan
® SIVO 110 - based coatings exhibit a state of dryness of 5 (DIN 53150) once dried at
room temperature for 20 min. Complete crosslinking (including reaction of silanol groups) will be reached at temperatures between a minimum of 180 °C and, ideally, 200 – 220 °C. Fig.2 Thermally crosslinked layer of Dynasylan
® SIVO 110 on aluminum substrate (SEM image,
vertically cutted; below: Al-substrate, above: sol-gel coating)
This information and all further technical advice is based on our present knowledge and experience. However, it implies no liability or other legal responsibility on our part, including with regard to existing third party intellectual property rights, especially patent rights. In particular, no warranty, whether express or implied, or guarantee of product properties in the legal sense is intended or implied. We reserve the right to make any changes according to technological progress or further developments. The customer is not released from the obligation to conduct careful inspection and testing of incoming goods. Performance of the product described herein should be verified by testing, which should be carried out only by qualified experts in the sole responsibility of a customer. Reference to trade names used by other companies is neither a recommendation, nor does it imply that similar products could not be used.
Product Information
Internet: www.dynasylan.com
E-mail: [email protected]
Evonik Degussa GmbH
Aerosil & Silanes
Weissfrauenstraße 9 D-60287 Frankfurt am Main
Germany
Phone: +49-69-218-5656 Fax: +49-69-218-3967
Evonik Degussa Corporation Aerosil & Silanes
379 Interpace Parkway P.O. Box 677 Parsippany
NJ 07054-0677 USA
Phone:
800-237-6745 (Toll Free) +1-973-541-8513
Fax: +1-973-541-8503
Evonik Degussa (China) Co., Ltd.
Aerosil & Silanes 55, Chundong Road
Xinzhuang Industry Park Shanghai 201108
P.R. China
Phone: +86-21-6119-1052 Fax: +86-21-6119-1075
Page 3 of 5
Fig. 3 SEM image of the dense, highly ordered packing of SiO2 particles in a thermally crosslinked Dynasylan
® SIVO 110 layer. Visualization achieved by O2-plasma etching
Properties Dynasylan
® SIVO 110 is suited as binder component in temperature crosslinking sol-gel coatings
and sol-gel - based hybrid coatings. Dynasylan® SIVO 110 coatings boast of:
• high hardness (pencil hardness up to 5H, depending on formulation)
• excellent scratch and mar resistance
• superior stability in boiling water (Gt0 upon 2 h treatment in water at 100 °C)
• very good adhesion on various substrates
• very good adhesion towards organic top coats (e.g. epoxies)
• sound flexibility (mandrel bending test according to DIN EN ISO 1519: 2 mm)
• very low thickness of formed layers (recommendation: dry layer of < 2 µm)
• excellent resistance against solvents and other chemicals Recommended areas of application:
• corrosion resistant primer systems
• transparent sol-gel top coats which exhibit a temperature resistance of up to 220 °C
• coatings comprising high hardness, which can be additionally improved by introduction of up to 20 wt.-% silica sol
• transparent easy-to-clean sol-gel - top coats upon adding Dynasylan® SIVO 112
This information and all further technical advice is based on our present knowledge and experience. However, it implies no liability or other legal responsibility on our part, including with regard to existing third party intellectual property rights, especially patent rights. In particular, no warranty, whether express or implied, or guarantee of product properties in the legal sense is intended or implied. We reserve the right to make any changes according to technological progress or further developments. The customer is not released from the obligation to conduct careful inspection and testing of incoming goods. Performance of the product described herein should be verified by testing, which should be carried out only by qualified experts in the sole responsibility of a customer. Reference to trade names used by other companies is neither a recommendation, nor does it imply that similar products could not be used.
Product Information
Internet: www.dynasylan.com
E-mail: [email protected]
Evonik Degussa GmbH
Aerosil & Silanes
Weissfrauenstraße 9 D-60287 Frankfurt am Main
Germany
Phone: +49-69-218-5656 Fax: +49-69-218-3967
Evonik Degussa Corporation Aerosil & Silanes
379 Interpace Parkway P.O. Box 677 Parsippany
NJ 07054-0677 USA
Phone:
800-237-6745 (Toll Free) +1-973-541-8513
Fax: +1-973-541-8503
Evonik Degussa (China) Co., Ltd.
Aerosil & Silanes 55, Chundong Road
Xinzhuang Industry Park Shanghai 201108
P.R. China
Phone: +86-21-6119-1052 Fax: +86-21-6119-1075
Page 4 of 5
Fig. 4 Polyester coil coating upon a 500 h salt spray test; substrate: zinc plated steel; left: treated with a standard primer based on organic solvents (dry layer: 5 µm), right: treated with Dynasylan
® SIVO 110 as a primer (dry layer: < 1 µm).
Processing Dynasylan
® SIVO 110 can be mixed with water at any proportion. Dilution in common organic
solvents such as ethanol, isopropanol, butyl glycol or methoxy propanol is possible. Dynasylan
® SIVO 110 can be formulated with a variety of water-thinnable binders and other
auxiliary agents such as Tego® Wet 280. As of such e.g. a satisfactory compatibility with acrylate-
based polymer dispersions has been achieved. Nevertheless, the final formulation must be checked towards possible incompatibilities such as phase separation or precipitation. Recommended procedures a.o. are storage or stress tests. Upon addition of acids and bases the pH value of Dynasylan
® SIVO 110 can be varied between
4 and 9. These acid or alkaline additives must be selected with care as flocculation or gelation can occur in contact with certain substances. For neutralization Dynasylan
® SIVO 111 is strongly
recommended. For acidification phosphoric acid may be used. For achievement of easy-to-clean properties Dynasylan
® SIVO 112 is highly recommended.
Dynasylan® SIVO 110 must be protected against freezing temperatures!
Application Dynasylan
® SIVO 110 containing formulations can be sprayed, dipped or applied with a doctor
blade. It is recommended to orient towards a 0.2 - 2 µm thickness of the dry layer (approx. 4 µm of a wet layer equals approx. 1µm of the respective dry layer). Hence the total quantity to be applied on smooth substrates will amount to approx. 5g / m². Generally for spray application an aqueous dilution should be used (e.g. 20 wt.-% Dynasylan
® SIVO 110, 0.06 wt.-% processing
agent, 79.94 wt.-% water). Surfaces of treated substrates must be clean and free of grease and dust.
This information and all further technical advice is based on our present knowledge and experience. However, it implies no liability or other legal responsibility on our part, including with regard to existing third party intellectual property rights, especially patent rights. In particular, no warranty, whether express or implied, or guarantee of product properties in the legal sense is intended or implied. We reserve the right to make any changes according to technological progress or further developments. The customer is not released from the obligation to conduct careful inspection and testing of incoming goods. Performance of the product described herein should be verified by testing, which should be carried out only by qualified experts in the sole responsibility of a customer. Reference to trade names used by other companies is neither a recommendation, nor does it imply that similar products could not be used.
Product Information
Internet: www.dynasylan.com
E-mail: [email protected]
Evonik Degussa GmbH
Aerosil & Silanes
Weissfrauenstraße 9 D-60287 Frankfurt am Main
Germany
Phone: +49-69-218-5656 Fax: +49-69-218-3967
Evonik Degussa Corporation Aerosil & Silanes
379 Interpace Parkway P.O. Box 677 Parsippany
NJ 07054-0677 USA
Phone:
800-237-6745 (Toll Free) +1-973-541-8513
Fax: +1-973-541-8503
Evonik Degussa (China) Co., Ltd.
Aerosil & Silanes 55, Chundong Road
Xinzhuang Industry Park Shanghai 201108
P.R. China
Phone: +86-21-6119-1052 Fax: +86-21-6119-1075
Page 5 of 5
Registration
EINECS/ELINCS (EU) Yes
AICS (Australia) No
DSL/NDSL (Canada) No
PICCS (Philippines) No
TSCA (USA) In preparation
IECS (P.R. China) In preparation
ENCS (Japan) Yes
ECL (South Korea) In preparation
Safety and Handling Before considering the use of any chemical read its Material Safety Data Sheet (MSDS) thoroughly for safety and toxicological data as well as for information on proper transportation, storage and use. The Material Safety Data Sheet is available after registration on our website http://www.dynasylan.com or upon request from your local representative.
Packaging and Storage Dynasylan
® SIVO 110 is supplied in 25 kg PE drums and 200 kg PE-inlined steel drums.
Due to its water content Dynasylan
® SIVO 110 must be stored above freezing temperature.
Storage temperatures must not exceed 40 °C.
In sealed containers Dynasylan® SIVO 110 has a shelf life of 12 months.