Brick Product Data

The properties shown on this data sheet represent typical average results generated using standard ASTM test methods (unless otherwise noted) conducted under controlled condition (using standard rectangular shapes), and should not be considered to be guaranteed specifications. Properties are subject to normal manufacturing statistical standard deviation ranges, and Resco Products, Inc. reserves the right to modify the properties and specifications at any time without prior notice. RESCO PRODUCTS disclaims any express or implied warranties based on this sheet. 2/5/2008 is the date that this data sheet was updated. Check with your RESCO sales representative or RESCO website to determine you have the current sheet

EAGLE 18 H6DM EAGLE 18 H6DM is a resin bonded magnesia-carbon brick containing 18% carbon, a fused magnesite addition plus the addition of antioxidants recommended for the furnaces where extreme operating conditions and for BOF operations in high metal erosion areas. Physical Properties Bulk Density ............................................... 179 /ft3 2.88 g/cm3 Modulus of Rupture.................................... 1600 lb/in2 11.0 Mpa Cold Crushing ........................................... 5500 lb/in2 38.0 Mpa Apparent Porosity ..................................... 4 % Coked Properties Modulus of Rupture...................................... 1200 lb/in2 8.3 Mpa Residual Carbon .......................................... 16 % Apparent Porosity ........................................ 11 % Ignited Properties Apparent Porosity ........................................ 30 % Loss on Ignition............................................ 18 % Hot Modulus of Rupture @ 2000F (1093C) ..................................... 1760 lb/in2 12.1 MPa @ 2550F (1400C) ..................................... 1500 lb/in2 10.3 MPa CHEMICAL ANALYSIS - (loss free) mass %* Magnesia - MgO ............................................................. 96.5 % Lime - CaO .......................................................................2.1% Silica SiO2 .........................................................................0.8% Iron Oxide - Fe2O3 ............................................................0.1% Alumina - Al2O3 .................................................................0.5% *Carbon and antioxident free analysis