fatigue failure slides
DESCRIPTION
Fatigue Failure SlidesIntroduction to Fatigue FailureTRANSCRIPT
MM211
Lecture 17introducing FATIGUE FAILUREAtta ul Haq GIK Institute-Fall 20131
1
Just to have an overview where we are nowAtta ul Haq GIK Institute-Fall 20132
Major Issues to be addressed;
1What is FATIGUE
2STRESS CYCLES 4Fatigue Testing 3S-N CURVES
Atta ul Haq GIK Institute-Fall 20133
3
What IS a FATIGUE ?
1Atta ul Haq GIK Institute-Fall 20134
4
Object --> Repeated Motion--> Weakness/tiredness --> Fatigue Example: Your legs/ muscles decrease in output due to constant running
Fatigue in materialsMetals --> Weak/fracture due to repeated loading90% service failure FatigueExamples: materials in continuous loading-unloading applications like bolts/ shafts (Brittle type fracturewhy?)
The PREMATURE failure/lowering of SRENGTH of a material due to repetitive stresses which may be below or above its yield strength Getting Started- Fatigue basicsAtta ul Haq GIK Institute-Fall 20135
5
Requirements for Fatigue FailureThis type of failure occurs in Metals and Polymers, While Ceramics do not undergo this type of failure!!Atta ul Haq GIK Institute-Fall 20136
FATIGUE FAILURE Fracture Surface in a Fatigue failure:
STAGES OF FATIGUE FAILURETwo Main fracture ZONESSmooth Surface Crystalline Surface
CRACK initiationCrack PropagationCatastrophic rupture
Atta ul Haq GIK Institute-Fall 20137
7
StriationHigh magnification SEM Image
Fatigue in Engine CrankshaftAtta ul Haq GIK Institute-Fall 20138Fracture Surface in a Fatigue failure:
Atta ul Haq GIK Institute-Fall 20139Fracture Surface in a Fatigue failure:
Macroscopic ExaminationMicroscopic Examination
Clamshell/beach markingsFiner markings-StriationsIntrusions and ExtrusionsSEM image @ high magnificationSEM image
startprogressEnd
Dislocation motion leads to PERSISTENT SLIP BANDS (PSBs)These SLIP BANDS involve INTRUSIONS and EXTRUSIONS (slip on different set of planes depending on loading cycle) Tiny Steps Stress Raisers Microcrack Initiation (along planes of high shear stress )
Schematic diagram showing Intrusions and Extrusions
CRACK Initiation and Propagation !
Crack formation and propagation is a Micromechanism in fatigueFatigue crack initiation is a surface phenomenon
SLIP BANDS Formation (Persistent Slip Bands)
Crack initiates
Extrusion and Intrusions
CRACKAtta ul Haq GIK Institute-Fall 201310
CRACK Propagation Mechanism !Atta ul Haq GIK Institute-Fall 201311
We will study Crack propagation Stages again once we get familiarize with the loading cycles
2STRESS CYCLES
Atta ul Haq GIK Institute-Fall 201312
12
Atta ul Haq GIK Institute-Fall 201313Types Of Fluctuating Stresses
Reversed Stress cycleRepeated Stress cycleRandom/irregular stress cycles
Stress Cycles in FatigueAtta ul Haq GIK Institute-Fall 201314
Mean Stress:Amplitude Stress:Range:Radius Ratio:
Amplitude Ratio:
14
Atta ul Haq GIK Institute-Fall 201315
CRACK Propagation Mechanism !Atta ul Haq GIK Institute-Fall 201316
Atta ul Haq GIK Institute-Fall 201317In Fatigue:Sub-critical Crack Growth Critical Crack Fracture
Let us consider three samples with same initial crack length subjected to different repeated cycles. Please note that material is also same; Higher Crack Growth rate at higher magnitude of applied stresses and vice versa
Materials life to Fracture is now highly dependent on magnitude of applied stress and final crack length (which is related to materials structural property (resistant to deformation etc..)
Fracture Mechanics for FatigueAtta ul Haq GIK Institute-Fall 201318
Fatigue Life
3S-N CurvesWhler curve/SN curves - A graph showing stress as a function of number of cycles in fatigue.
Atta ul Haq GIK Institute-Fall 201319
19
Presenting Fatigue DataAtta ul Haq GIK Institute-Fall 201320
20
Fatigue Limit/Endurance Limit:The stress below which a material will not fail by fatigue Non-ferrous ferrous Atta ul Haq GIK Institute-Fall 201321
Fatigue Life:The number of cycles permitted at a particular stress before a material fails by fatigue.The stress required to cause failure by fatigue in a given number of cycles.Fatigue Strength:Atta ul Haq GIK Institute-Fall 201322
4Fatigue Testing
Atta ul Haq GIK Institute-Fall 201323
23
Atta ul Haq GIK Institute-Fall 201324
Four Point Bending Set up Cantilever loading
Modified Goodman Relation
a = e (1 m/ u)Soderberg RelationGerber RelationFailure Criteria can also be established by plotting fatigue test dataPredicts safer regions for fatiguea = e (1 m/ u)2a = e (1 m/ y)Atta ul Haq GIK Institute-Fall 201325
Miners Law and Cumulative Damage
Remaining cycles permissible at S2
N1 = lifetime at S1n1 = Number of cycles applied till S1
Fatigue life consumed at S1Atta ul Haq GIK Institute-Fall 201326Fatigue Failure will occur when
Factors Effecting Fatigue Loading and Loading CyclesSurface ConditionsDesign ConsiderationNature of EnvironmentAtta ul Haq GIK Institute-Fall 201327The nature of Surface strongly influence fatigue strength:-Surface Hardness-Surface Roughness-Residual Stresses
--Method 1: shot peening
put surface into compression
shot--Method 2: carburizing
C-rich gas
2. Remove stress concentrators.
badbad
betterbetter
1. Surface Treatments, induce compressive stressess.How to Improve Fatigue Performance
Atta ul Haq GIK Institute-Fall 201328
Atta ul Haq GIK Institute-Fall 201329
Fatigue in PolymersFatigue behaviour and SN curves similar to that of metals except the crack initiation: There is no Concept of Persistent Slip Bands (PSBs) in Polymers , rather crack is initiated with CRAZING phenomenon.
QUIZ-5/6 on Thursday, 8th Week@5:30PM MLH
Atta ul Haq GIK Institute-Fall 201330