FRANGIBLEAPPROACH MAST
LIGHTS POWER CONTROL ACCESSORIES
LIGHTS
SUPPORT COLUMN
COLUMNS
JUNCTURE PLATE
COUNTER WEIGHT
BINDING BAR
Meticulous works of UBS sta�s end up with the production of frangible approach mast. UBS frangible approach masts are produced and carried out impact tests according to ICAO and FAA. The masts are can be pipe and cage type.
Easy installation, long life and no fade through resistance to UV lights, project design support by UBS, fundamental load calculations and pre-installation instructions make the job easy for the contractor companies.Frangible approach masts can resist static and operational wind loads and jet blasts. According to impact tests which are compliance with ICAO and FAA, frangible approach masts collapse and demount easily on a collision and do not damage any of planes’ windows, body or tails.
Not only resist against wind and jet blast but also frangible during any collision with planes.Extraordinary Power But
Compliance With World Standards!
With production of frangible approach mast UBS is the world’s choice!
Practical solution without need of maintenance.
COMPONENTS OF THE MAST MAST FLOW ANALYSIS
Fran
gibl
e Ap
proa
ch M
ast
Mast Composite Material PropertiesProperty Unit Testing Method Value Testing Method E23 Value
Speci�c Weight g/cm3 ASTM D792 1.8
Fiber Glass Ratio (with respect to mass) % ISO 1162 60
Longitudinal Tensile Strength MPa ASTM D638 450 EN ISO 527-3 > 239
Transversal Tensile Strength MPa ASTM D638 100 EN ISO 527-3 > 50
Longitudinal Modulus of Elasticity GPa ASTM D638 32 EN ISO 527-4 > 23
Transversal Modulus of Elasticity GPa ASTM D638 10 EN ISO 527-4 > 7
Longitudinal Three Point Bending Strength MPa ASTM D790 450 EN ISO 14125 > 240
Transversal Three Point Bending Strength MPa ASTM D790 100 EN ISO 14125 > 100
Bending Modulus of Elasticity GPa (tam eğilme) 30 EN 13706 Ek D > 23
Longitudinal Compressive Strength MPa ASTM D953 170 EN 13706 Ek E > 150
Transversal Compressive Strength MPa ASTM D953 75 EN 13706 Ek E > 70
Shear Strength Between Layers MPa ASTM 2344 26 EN ISO 14130 > 25
Thermal Expansion Coe�cient -1/K ASTM D696 11 E-6
Impact Resistance Kj/m2 ASTM D5942 180
Water Absorption % ISO 62 0,4
Non-Conductivity kV/mm ASTM D149 5
Thermal Conductivity W/mK ASTM C177 0.35
Technical Speci�cations of Frangible Approach Mast Property Pipe type Cage type Notes
Max. light height 12 m 30
Dimension of light connection parts +/- 250mm +/- 250mm Can be changed according to demand
Installation Fixed connection Movable connection
Surface UV resist paint UV resist paint
Material Fiber-glass Fiber-glass Connection parts are aluminum
Weight 18 kg 113 kg
Heydar Aliyev Int. AirportBaku / AzerbaycanT: +99 451 561 99 [email protected]
Uğur Mumcu Sokak No: 21/2Gaziosmanpaşa / AnkaraT: +90 312 447 48 75F: +90 312 447 69 [email protected]
Akova Mah. Sakarya Cad. No: 57Hendek / SakaryaT: +90 264 614 35 36F: +90 264 614 35 [email protected]
Kral Abdülaziz Int. AirportMedina / Suudi ArabiaT: +96 654 388 23 [email protected]
UBS MAIN OFFICE UBS FACTORY UBS BAKU UBS MEDINA