![Page 1: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/1.jpg)
12 Octobre 2017
E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb
a CORIA – UMR 6614 CNRS b GPM – UMR 6634 CNRS
Université et INSA de Rouen
Composites aéronautique soumis au feu :
différents méchanismes de dégradation.
GDR Incendie Balma
![Page 2: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/2.jpg)
Sommaire
Eliot Schuhler, 12 Octobre 2017
Introduction
Set up presentation Apparatus Temperature and thermal flux
Results and discussion
In-situ measurements After exposure observations
Conclusions
2
![Page 3: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/3.jpg)
Introduction Context
Laminar composite
Layer
Non homogenous structure
Anisotropic mechanical and thermal behaviour
Increasing use of composites in the aeronautical field
Inflammation risk due to polymer is a safety issue
5-harness satin weave
3 Eliot Schuhler, 12 Octobre 2017
![Page 4: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/4.jpg)
Introduction
Objectives
2.2 mm thickness PPS resin [±45]7 5-harness satin weave
2 mm thickness Epoxy resin [±45]7 5-harness satin weave
carbon/thermoset and carbon/thermoplastic materials comparison with high thermal flux : 106kW/m²
Virgin Carbon/PPS material Virgin Carbon/Epoxy material
4 Eliot Schuhler, 12 Octobre 2017
![Page 5: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/5.jpg)
Epoxy matrix 𝑇𝑑 = 320°𝐶 𝑇𝑝 = 390°𝐶
PPS matrix 𝑇𝑑 = 480°𝐶 𝑇𝑝 = 550°𝐶
After 600°C in oxidizing atmosphere the carbon fibres start to deteriorate and lose mass.
Introduction Thermal analysis
TGA under oxidizing (Air) and non-oxidizing (N2) atmosphere
Vieille et Al. , Materials & Design, 2015
𝑇𝑑
𝑇𝑝
No fibre degradation in N2 environment.
5
𝑇𝑝
𝑇𝑑
Eliot Schuhler, 12 Octobre 2017
O2
![Page 6: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/6.jpg)
Set up presentation
(1) mirror (2) infrared camera (3) coupon (4) balance (5) flame burner (6) air inlet (7) propane inlet
1
2
1
2
3
4
(1) sample holder (2) insulation sheet (3) 50x5mm² coupon (4) screw
Z
Y
6
Coupon size : 2 x 50 x 50 mm Distance between burner exhaust and coupon surface : 17 mm Window size of the sample holder : 45 mm diam. Flame at the stoichiometry : non-oxidizing flame
Eliot Schuhler, 12 Octobre 2017
![Page 7: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/7.jpg)
Set up presentation
Thermal flux measurement in the center of the flame : goal at 106kW/m²
Thermocouple X position (mm) Temperature in the flame (°C)
TC1 -14 940
TC2 -7 1074
TC3 0 1110
TC4 7 1078
TC5 14 950
Temperature fluctuation in the flame (σ = 4°C)
7
Well-controlled and repeatable heating condition Eliot Schuhler, 12 Octobre 2017
![Page 8: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/8.jpg)
Method : Mass measurement
8 Eliot Schuhler, 12 Octobre 2017
Mass measurement for C/Epoxy samples
Mean residual mass and MLR for C/Epoxy samples
Residual mass and mass loss rate calculation using SawitzkyGolay algorithme for smoothing and first order derivatif calculation. Staggs, J.E.J., Fire Safety Journal, 2005.
![Page 9: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/9.jpg)
Method : Temperature measurement
9 Eliot Schuhler, 12 Octobre 2017
45mm
Temp
erature (°C
)
Thermal image from C/Epoxy sample C/Epoxy sample Temperature
![Page 10: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/10.jpg)
In situ Measurement : Mass loss and temperature
carbon/Epoxy
carbon/PPS
10 Eliot Schuhler, 12 Octobre 2017
![Page 11: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/11.jpg)
After exposure observations
Thickness 9.3 mm (after degradation)
carbon/Epoxy
Thickness 3.5 mm (after degradation)
carbon/PPS
Back face Flame face Side
Back face Flame face Side
Observations after a 300 second exposure to the 106kW/m² flame :
11 Eliot Schuhler, 12 Octobre 2017
![Page 12: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/12.jpg)
After exposure observations
12 Eliot Schuhler, 12 Octobre 2017
30s
Face arrière Face flamme
60s
90s
Température Face arrière (°C)
![Page 13: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/13.jpg)
Conclusion
13 Eliot Schuhler, 12 Octobre 2017
30s
Face arrière Face flamme
60s
90s
Température Face arrière (°C)
After exposure observations
![Page 14: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/14.jpg)
14 Eliot Schuhler, 12 Octobre 2017
Matrice 37 %
Fibre 55%
Porosité 8% Carbone/PPS vierge 68%vol Fibre
Numeric image analysis : C/PPS
![Page 15: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/15.jpg)
After exposure observations : C/PPS
15 Eliot Schuhler, 12 Octobre 2017
30s
60s
90s
30 s 60 s 90 s
Voids% 32 56 77
Matrix% 23 24 7
Fibre% 45 25 16
![Page 16: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/16.jpg)
After exposure observations C/Epoxy
Flame
C/Epoxy
Voids 40 %
Matrix 7 %
Fibre 53 %
16 Eliot Schuhler, 12 Octobre 2017
![Page 17: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/17.jpg)
1. The propane burner used for this study is able : • to provide easily the fire degradation of a small sample under high
thermal flux, up to 200kW/m2. • to provide accurate values of mass and temperature during the fire
degradation of a small sample.
2. The automated image processing allows a quantitative analyse of the sample degradation. • The use of a propane/air flame at stoichiometry highlights the
impact of a non-oxidizing flame on the fibre degradation at high heat flux.
• The image analysis enables the characterisation of different degradation processes inside the Epoxy- and PPS-based samples.
(voids building, major delamination, matrix degradation or melting)
Conclusion
17 Eliot Schuhler, 12 Octobre 2017
![Page 18: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/18.jpg)
Development and Objectives
1. Study of the composites reaction to fire under high flux (200 kW/m²)
2. Study of the simultaneous mechanical and thermal stress on composite samples.
18 Eliot Schuhler, 12 Octobre 2017
![Page 19: GDR Incendie Balma 12 Octobre 2017 - univ-lorraine.frdocs.gdrfeux.univ-lorraine.fr/Balma/CORIA_1.pdf · 12 Octobre 2017 E. Schuhlera, A. Coppallea, B. Vieilleb, J. Yona, Y. Carpierb](https://reader034.vdocument.in/reader034/viewer/2022052013/602a493a9f166b66b8065379/html5/thumbnails/19.jpg)
Merci pour votre attention
Questions ?