hot explosive pressing of high strength and superhard materials by r. prümmer, germany and k....
DESCRIPTION
Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan. EPNM-2008 May 5-9, 2008. Lisse. Why Hot Expl. Pressing?. HEP Udimet 700 Ni-base Superalloy. Composition of several Nickel based Superalloys. Atomization of Udimet 700 - Powder. - PowerPoint PPT PresentationTRANSCRIPT
![Page 1: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/1.jpg)
Hot Explosive Pressingof High Strength and Superhard Materials
by
R. Prümmer, Germanyand
K. Hokamoto, Japan
EPNM-2008May 5-9, 2008. Lisse
![Page 2: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/2.jpg)
Why Hot Expl. Pressing?HIP
Hot Isost.PressCEP
Cold Expl.PressHEP
Hot Expl. Press.
Pressure limited unlimited unlimited
Duration long shortseveral microsec.
shortseveral microsec.
Diffusion high limited high
Plasticdeformation low medium high
Melting,leadingto welding no locally very high
![Page 3: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/3.jpg)
3
![Page 4: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/4.jpg)
4
HEPUdimet 700
Ni-base Superalloy
![Page 5: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/5.jpg)
5Composition of several Nickel based Superalloys
![Page 6: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/6.jpg)
6Atomization of Udimet 700 - Powder
![Page 7: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/7.jpg)
7
![Page 8: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/8.jpg)
8 Density of Sample after HEP of Udimet 700- Powder
![Page 9: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/9.jpg)
9Hardness of Samples vs. Temperature of HEP
![Page 10: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/10.jpg)
1010
Micrograph of Sample showing surface melting
![Page 11: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/11.jpg)
1113Strength of Sample vs. Temperature of HEP
![Page 12: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/12.jpg)
12
HEPDiamond Powder, 4-8 um grain size
![Page 13: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/13.jpg)
13Principle of Set-up for HEP
![Page 14: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/14.jpg)
14
Set-up for HEP
![Page 15: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/15.jpg)
15
Sample Set -up
High pressure due to mach stem and end plug
![Page 16: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/16.jpg)
16
Sample, longitudinally cut open
![Page 17: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/17.jpg)
17
Micrograph of polished Surface of Diamond Compact
![Page 18: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/18.jpg)
18
Scanning Electron Micrograph of Fracture Surface
![Page 19: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/19.jpg)
19X-ray Diffraction Pattern of Diamond Powder and Compactas delivered: black, after heat treatment: blue; compacted: red
As-received
1100 C
Compact
o
![Page 20: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/20.jpg)
20
0 2 4 6 8
10
8
6
4
2 (a) As-received(b) 1100oC
(c) Compact
cos
/.10
7(m
-1)
sin/.1010 (m-1)
0 2 4 6 8
10
8
6
4
2 (a) As-received(b) 1100oC
(c) Compact
cos
/.10
7(m
-1)
sin/.1010 (m-1)
Hall-Williamson Plot of Diamond Powder and Compact
sin(/) ・ 1010 (m-1)
si
n(/
) ・1
07 (m
-1)
Slope;Lattice strain
![Page 21: Hot Explosive Pressing of High Strength and Superhard Materials by R. Prümmer, Germany and K. Hokamoto, Japan](https://reader036.vdocument.in/reader036/viewer/2022062501/5681682a550346895dddbdf6/html5/thumbnails/21.jpg)
ConclusionsThe effects of the use of hot explosive pressing are demonstrated at the present investigation for Udimet 700 and diamond powders.Surface melting and softening the powders improves the condition of compaction, and the compacts recovered show improved mechanical properties and the crystalline lattice strain.
21