SLIB ITALY slibitaly.com SLIDING BEARINGS DIVISION HYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

Upload: others

Post on 10-Jan-2020

11 views

Category:

Documents


0 download

TRANSCRIPT

Page 1: HYDRAULIC, POWER SUPPLY AND METAL INDUSTRY ITALYdonar.messe.de/exhibitor/hannovermesse/2017/T747177/slib-italy-catalogue-eng-481573.pdfHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

SLIBITALY

slibitaly.com

SLIDING BEARINGS DIVISIONHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

Page 2: HYDRAULIC, POWER SUPPLY AND METAL INDUSTRY ITALYdonar.messe.de/exhibitor/hannovermesse/2017/T747177/slib-italy-catalogue-eng-481573.pdfHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

Slib Italy is specialized in the manufacturing of pressed Sliding Bearings with thin wall-thickness, dry self-lubricating, or with grease or oil lubrication, and produced in accordance to ISO 3547 directive.Slib Italy is also a bushings producer and a producer of sliding bearings for high pressure.

Sliding Bearings can be provided as thrust washer in cylindrical shape, or as strips. Other possible variables can be produced according to specific requests or to customers’ drawings. Dimensions range from a min. of 10 mm to a max. of 1.000 mm, both for standard sizes and for special ones.

These Bearings guarantee superior performances in terms of:

• wear resistance;• load capacity, both static and dynamic;• maximum flexibility of usage in the most different applications;• less space requirement in the application;• resistance to impacts and to vibrations;• possibility of usage both at low and high temperatures;• chemical resistance in contact with various substances.

The aim of FP F.lli Paris with this new production department, together with partners with years of experience in the production of Sliding Bearings, is to become a worldwide reference, focusing its strengths on the achievement, the maintenance and the improvement of the following prerogatives:

• Team work in order to reach the maximum satisfaction of the client.• Flexible manufacturing capability for all the different applications.• Competitive prices and high quality technology.• Guaranty of the agreed lead times.• Attention to the quality of the products.

SLIDING BEARINGS DIVISIONHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

network

Member of:

SLIBITALY

Page 3: HYDRAULIC, POWER SUPPLY AND METAL INDUSTRY ITALYdonar.messe.de/exhibitor/hannovermesse/2017/T747177/slib-italy-catalogue-eng-481573.pdfHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

Fiber + filled PTFE (thickness 400 micron)

BEARING SECTION

Sintering

Carbon steel backing (thickness 0.50 – 3.00 mm)

PS: the values shown in the graph were determined with a test of constant load, and running for 1000 cycles at three different temperatures: -190 °C, +18 °C and +260 °C

GRAPHIC LOAD/SPEEDLOAD

(N/mm2)

SPEED(m/s)

190180170160150140130120110100

0

00.

050.

100.

150.

200.

250.

300.

350.

400.

450.

50

This code identifies a line of bearings that are specially manufactured to allow the bonding of a filled PTFE coated fiber (lead free, in accordance to the European Parliament “ELV” directive 2000/53/EC) on four types of backing metal layers, like carbon steel, bronze, stainless steel and Inconel 625.The Sliding Surface is primarily composed of filled PTFE coated fiber, and other elements to guarantee the high wear resistance. The TX products find their best usage in slow-moving applications, with heavy loads, and

where dry operation is required. Thanks to the thick self-lubricating layer up to 0.40 mm, this product has a high wear resistance, and can work in dirty or abrasive environment.

For this product it is not recommended the use of oil, while the use of special grease, such as silicon or lithium soap, is only possible during the assembly.

TX Type

Page 4: HYDRAULIC, POWER SUPPLY AND METAL INDUSTRY ITALYdonar.messe.de/exhibitor/hannovermesse/2017/T747177/slib-italy-catalogue-eng-481573.pdfHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

TX-C TX-316 TX-625

SUPPORTING SHELL

C 0.17% S 0.045%Mn 1.40% N 0.009%P 0.045%

C 0.03%, Mn 1.80%S 0.025%, Cr 16.70%P 0.03%, Ni 10.00%Si 0.50%, Mo 2.00%

C 0.10%, Co 1.00%Mn 0.05%

Ta + Nb 3.15 ÷ 4.15%Cr 20 ÷ 23%, Ni Rest

Mo 8 ÷ 10%

SLIDING LAYERS Special fiber with filled PTFE, colour black-gray, thickness 400 micron, heavy load capacity and self-lubricating under dry operation.

SINTERING Special adhesive between the fiber and the backing steel, thickness 60 micron.

WORKING TEMPERATURE min - 180°C max + 260 °C min - 180°C max + 260 °C min - 180°C max + 260 °C

COEFFICIENT OF FRICTION 0.03-0.10 0.03-0.10 0.03-0.10

MAX.SPEED 0.50 m/s 0.50 m/s 0.50 m/s

MAX.STATIC LOAD 300 N/mm2 300 N/mm2 400 N/mm2

MAX. DYNAMIC LOAD

(max. speed 0.05 m/s)190 N/mm2 190 N/mm2 190 N/mm2

MAX. DYNAMIC LOAD

(max. speed 0.50 m/s)100 N/mm2 100 N/mm2 100 N/mm2

SHAFT The shaft surface finishing, for optimal performance, shall be between 0.40 and 1.60 micron Ra, depending on different application. Hardness 80 – 160 HB5.

HYDROCARBONS Excellent Excellent Excellent

HYDROCHLORIC ACID

(concentrate to 10%)Excellent Excellent Excellent

SULFURIC ACID(concentrate to 10%) Excellent Excellent Excellent

METHANE Excellent Excellent Excellent

OXYGEN Excellent Excellent Excellent

SODIUM HYDROXIDE Excellent Excellent Excellent

LIQUID NITROGEN Excellent Excellent Excellent

SOLVENTS Good Good Good

CHEM

ICA

L RE

SIST

AN

CEM

ECH

AN

ICA

L PR

OPE

RTIE

S

Carbon Steel S235 JR+ Sintering

+ Fiber + filled PTFE

Aisi 316L+ Sintering

+ Fiber + filled PTFE

Inconel 625+ Sintering

+ Fiber + filled PTFE

Note: The informaton in this data-sheet is to be considered reliable, but conditons and methods of use, which are beyond our control, may modify the results. The informaton and data contained in this data-sheet are the result of a long and detailed research, however F.lli Paris S.r.l. cannot be considered responsible for any incorrect or incomplete data. Owing to the constant development of the products, we reserve the right to make changes to them without prior notice.

Page 5: HYDRAULIC, POWER SUPPLY AND METAL INDUSTRY ITALYdonar.messe.de/exhibitor/hannovermesse/2017/T747177/slib-italy-catalogue-eng-481573.pdfHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

TX-F51 TX-TI1 TX-STEDuplex A182 F51

+ Sintering+ Fiber + filled PTFE

Titanium ASTM B265 Gr.1+ Sintering

+ Fiber + filled PTFE

Stellite 6b+ Sintering

+ Fiber + filled PTFE

SLIBITALY

SLIDING BEARINGS DIVISIONHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

SUPPORTING SHELL

C 0.20%, Cr 22.70%S <0.15%, Ni 5.60%

P 0.025%, Mo 3.20%Si 0.50%, N 0.16%

Mn 1.40%

Ti Rest, O 0.18%N 0.03%, C 0.08%

H 0.015%, Fe 0.20%

Co Rest, Cr 28 ÷ 32%W 3.50 ÷ 5.50%, C 0.90 ÷ 1.40%

Mo 1.50% max, Altro Ni, Fe, Si, Mn

SLIDING LAYERS Special fiber with filled PTFE, colour black-gray, thickness 400 micron, heavy load capacity and self-lubricating under dry operation.

SINTERING Special adhesive between the fiber and the backing steel, thickness 60 micron.

WORKING TEMPERATURE min - 180°C max + 260 °C min - 180 °C - max + 260 °C min - 180°C max + 260 °C

COEFFICIENT OF FRICTION 0.03-0.10 0.03-0.10 0.03-0.10

MAX.SPEED 0.50 m/s 0.50 m/s 0.50 m/s

MAX.STATIC LOAD 400 N/mm2 400 N/mm2 400 N/mm2

MAX. DYNAMIC LOAD

(max. speed 0.05 m/s)190 N/mm2 190 N/mm2 190 N/mm2

MAX. DYNAMIC LOAD

(max. speed 0.50 m/s)100 N/mm2 100 N/mm2 100 N/mm2

SHAFT The shaft surface finishing, for optimal performance, shall be between 0.40 and 1.60 micron Ra, depending on different application. Hardness 80 – 160 HB5.

HYDROCARBONS Excellent Excellent Excellent

HYDROCHLORIC ACID

(concentrate to 10%)Excellent Good Excellent

SULFURIC ACID(concentrate to 10%) Excellent Good Excellent

METHANE Excellent Excellent Excellent

OXYGEN Excellent Good Excellent

SODIUM HYDROXIDE Excellent Good Good

LIQUID NITROGEN Excellent Good Excellent

SOLVENTS Good Good Good

CHEM

ICA

L RE

SIST

AN

CEM

ECH

AN

ICA

L PR

OPE

RTIE

S

Note: The informaton in this data-sheet is to be considered reliable, but conditons and methods of use, which are beyond our control, may modify the results. The informaton and data contained in this data-sheet are the result of a long and detailed research, however F.lli Paris S.r.l. cannot be considered responsible for any incorrect or incomplete data. Owing to the constant development of the products, we reserve the right to make changes to them without prior notice.

Page 6: HYDRAULIC, POWER SUPPLY AND METAL INDUSTRY ITALYdonar.messe.de/exhibitor/hannovermesse/2017/T747177/slib-italy-catalogue-eng-481573.pdfHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

BEARING SECTION

Filled PTFE or filled PTFE modified (thickness 200 – 220 micron)

Sintering

Carbon steel backing(thickness 0.50 – 3.00 mm)

PS: the values shown in the graph were determined with a test of constant load, and running for 1000 cycles at three different temperatures: -190 °C, +18 °C and +260 °C

GRAPHIC LOAD/SPEEDTF-C . TF-316 . TF-625 . TF-F51

140130120110100

90807060

0

00.

100.

200.

300.

400.

500.

600.

700.

800.

901.

00

LOAD(N/mm2)

SPEED(m/s)

The TF type is a composite multilayer material used in the manufacture of dry self-lubricating Sliding Bearings.The main parts composing this product are a filled modified PTFE layer (lead free, in accordance to the European Parliament “ELV” directive 2000/53/EC) for the sliding self-lubricating surface, and a special primer used to allow the sintering of the PTFE layer to four types of baking metal layers, like carbon steel, bronze, stainless steel and Inconel 625.

Thanks to its structure, the TF type provides an excellent match between the mechanical strength of the steel, and the low coefficient of friction due to the modified PTFE sliding layer.This is a product, that can be used in applications with medium loads, and in a clean environment with low levels of abrasive elements such as metal powders. It can also be used with special mineral oils and specific greases such as silicone compounds or lithium soap.

TF Type

GRAPHIC LOAD/SPEEDTF-316S . TF-625S

00.

050.

100.

150.

200.

250.

300.

350.

400.

450.

50

180170160150140130120110100

800

LOAD(N/mm2)

SPEED(m/s)

Page 7: HYDRAULIC, POWER SUPPLY AND METAL INDUSTRY ITALYdonar.messe.de/exhibitor/hannovermesse/2017/T747177/slib-italy-catalogue-eng-481573.pdfHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

Carbon Steel S235 JR

+ Sintering+ Filled PTFE film

Aisi 316L + Sintering

+ Filled PTFE film

Aisi 316L + Sintering*

+ Filled PTFE modified film

Inconel 625 + Sintering

+ Filled PTFE film

Inconel 625 + Sintering*

+ Filled PTFE modified film

Duplex A182 F51 + Sintering

+ Filled PTFE film

TF-C TF-316 TF-316S TF-625 TF-625S TF-F51

CHEM

ICA

L RE

SIST

AN

CEM

ECH

AN

ICA

L PR

OPE

RTIE

S

SLIBITALY

SLIDING BEARINGS DIVISIONHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

SUPPORTING SHELL

C 0.17% max Mn 1.40% max P 0.045% max S 0.045% max N 0.009% max

C 0.03% S 0.025%P 0.03%, Si 0.50%

Mn 1.80%Cr 16.70%Ni 10.00%Mo 2.00%

C 0.03%,S 0.025%, P 0.03%Si 0.50%

Mn 1.80%, Cr 16.70% Ni 10.00%,Mo 2.00%

C 0.10% max Mn 0.05% max

Cr 20 ÷ 23% Mo 8 ÷ 10%

Co 1.00% max Ta + Nb

3.15 ÷ 4.15% Ni Rest.

C 0.10% max Mn 0.05% max

Cr 20 ÷ 23%Mo 8 ÷ 10%

Co 1.00% maxTa + Nb

3.15 ÷ 4.15%Ni Rest.

C 0.20% maxS <0.15%P 0.025%Si 0.50%

Mn 1.40%Cr 22.70%Ni 5.60%

Mo 3.20% N 0.16%

SLIDING LAYERS Filled PTFE film, colour black-gray, thickness 200–220 micron,heavy load capacity and self-lubricating under dry operation, lead free and non-coated.

SINTERINGSintering process made in oven between PTFE and the steel backing at a temperature of +250 ° C, BRONZE FREE

* Special adhesive between the filled PTFE modified film and the backing steel, thickness 60 micron, valid just for TF-316S and TF-625S

WORKING TEMPERATURE

min - 190 °C - max + 260 °C

min - 190 °C - max + 260 °C

min - 190 °C - max + 260 °C

min - 190 °C - max + 260 °C

min - 190 °C - max + 260 °C

min - 190 °C - max + 260 °C

COEFFICIENT OF FRICTION 0.03-0.20 0.03-0.20 0.03-0.20 0.03-0.20 0.03-0.20 0.03-0.20

MAX.SPEED 1.00 m/s 1.00 m/s 0.50 m/s 1.00 m/s 0.50 m/s 1.00 m/s

MAX.STATIC LOAD 250 N/mm2 250 N/mm2 250 N/mm2 250 N/mm2 250 N/mm2 250 N/mm2

MAX. DYNAMIC LOAD

(max. speed)140 N/mm2

(0.10 m/s)140 N/mm2

(0.10 m/s)180 N/mm2

(0.05 m/s)140 N/mm2

(0.10 m/s)180 N/mm2

(0.05 m/s)140 N/mm2

(0.10 m/s)

MAX. DYNAMIC LOAD

(max. speed)60 N/mm2

(1.00 m/s)60 N/mm2

(1.00 m/s)80 N/mm2

(0.50 m/s)60 N/mm2

(1.00 m/s)80 N/mm2

(0.50 m/s)60 N/mm2

(1.00 m/s)

SHAFT For optimal performances, the shaft surface finishing shall be between Ra 0.40 and Ra 1.60 micron, depending on the applications. Hardness 80 - 160 HB5.

HYDROCARBONS Excellent Excellent Excellent Excellent Excellent Excellent

HYDROCHLORIC ACID

(concentrate to 10%)Excellent Excellent Excellent Excellent Excellent Excellent

SULFURIC ACID(concentrate to 10%) Excellent Excellent Excellent Excellent Excellent Excellent

METHANE Excellent Excellent Excellent Excellent Excellent Excellent

OXYGEN Excellent Excellent Excellent Excellent Excellent Excellent

SODIUM HYDROXIDE Excellent Excellent Excellent Excellent Excellent Excellent

LIQUID NITROGEN Excellent Excellent Excellent Excellent Excellent Excellent

SOLVENTS Good Good Good Good Good Good

Note: The informaton in this data-sheet is to be considered reliable, but conditons and methods of use, which are beyond our control, may modify the results. The informaton and data contained in this data-sheet are the result of a long and detailed research, however F.lli Paris S.r.l. cannot be considered responsible for any incorrect or incomplete data. Owing to the constant development of the products, we reserve the right to make changes to them without prior notice.

Page 8: HYDRAULIC, POWER SUPPLY AND METAL INDUSTRY ITALYdonar.messe.de/exhibitor/hannovermesse/2017/T747177/slib-italy-catalogue-eng-481573.pdfHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

This product identifies a new generation of Sliding Bearings for applications in low and high temperature, thanks to a special coating performed with a system similar to the PVD process. This coating confers to the material an excellent resistance to extreme temperatures while maintaining a good coefficient of static friction even with a dynamic heavy load.

The metal backing layers used for this product are the Aisi 316L and the Inconel 625. With this type of product, the shaft should not be heat treated. It is not recommendable to use oil and grease with these bearings.

PMT Type

316

625

Special coating

Special coating

Inconel 625 backing (thickness 0.50 - 3.00 mm)

Aisi 316 backing (thickness 0.50 - 3.00 mm)

BEARING SECTIONGRAPHIC LOAD/SPEEDPMT-625 plusLOAD

(N/mm2)

00.

050.

100.

150.

200.

250.

300.

350.

400.

450.

50

190180170160150140130120110100

0

PS: the values shown in the graph were determined with a test of constant load, and running for 1000 cycles at three different temperatures: -190 °C, +18 °C and +260 °C

GRAPHIC LOAD/SPEEDPMT-316 . PMT-316 plus . PMT-625LOAD

(N/mm2)

SPEED(m/s)

00.

050.

100.

150.

200.

250.

300.

350.

40

150145140135130125120115110100

0

SPEED(m/s)

Page 9: HYDRAULIC, POWER SUPPLY AND METAL INDUSTRY ITALYdonar.messe.de/exhibitor/hannovermesse/2017/T747177/slib-italy-catalogue-eng-481573.pdfHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

SLIBITALY

SLIDING BEARINGS DIVISIONHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

SUPPORTING SHELL

C 0.03%, S 0.025% P 0.03%, Si 0.50%

Mn 1.80%, Cr 16.70% Ni 10.00%, Mo 2.00%

C 0.03%, S 0.025% P 0.03%, Si 0.50%

Mn 1.80%, Cr 16.70% Ni 10.00%, Mo 2.00%

C 0.10%Mn 0.05%

Cr 20 ÷ 23 %Mo 8 ÷ 10 %

Co 1.00%Ta + Nb 3.15 ÷ 4.15 %

Ni Rest.

C 0.10% Mn 0.05%

Cr 20 ÷ 23 %Mo 8 ÷ 10 %

Co 1.00%Ta + Nb 3.15 ÷ 4.15 %

Ni Rest.

SLIDING LAYERS

Physical Vaporization of the special coating.Multilayer deposit of the Surface, minimum hardness 180 HB, and minimum thickness 15 micron.

WORKING TEMPERATURE min - 198°C max + 430 °C min - 100°C max + 500 °C min - 198°C max + 430 °C min - 100°C max + 600 °C

COEFFICIENT OF FRICTION 0.06-0.12 0.08-0.20 0.06-0.12 0.04-0.10

MAX.SPEED 0.40 m/s 0.40 m/s 0.40 m/s 0.50 m/s

MAX.STATIC LOAD 200 N/mm2 200 N/mm2 200 N/mm2 200 N/mm2

MAX. DYNAMIC LOAD

(max. speed 0.10 m/s)150 N/mm2 150 N/mm2 150 N/mm2 190 N/mm2

MAX. DYNAMIC LOAD

(max. speed 0.40 m/s)100 N/mm2 100 N/mm2 100 N/mm2 100 N/mm2

SHAFT The shaft surface finishing, for optimal performance, shall be between 0.40 and 1.60 micron Ra,depending on different application. Hardness 100 – 160 HB5.

HYDROCARBONS Excellent Excellent Excellent Excellent

HYDROCHLORIC ACID

(concentrate to 10%)Excellent Excellent Excellent Excellent

SULFURIC ACID(concentrate to 10%) Excellent Excellent Excellent Excellent

METHANE Excellent Excellent Excellent Excellent

OXYGEN Excellent Excellent Excellent Excellent

SODIUM HYDROXIDE Excellent Excellent Excellent Excellent

LIQUID NITROGEN Excellent Excellent Excellent Excellent

SOLVENTS Excellent Excellent Excellent Excellent

Aisi 316L + Special Coating

Aisi 316L + Special Coating

RESI

STEN

ZA C

HIM

ICA

PRO

PRIE

TÀ M

ECCA

NIC

HE

PMT-316 PMT-316plus

Inconel 625 + Special Coating

PMT-625Inconel 625

+ Special Coating

PMT-625plus

Note: The informaton in this data-sheet is to be considered reliable, but conditons and methods of use, which are beyond our control, may modify the results. The informaton and data contained in this data-sheet are the result of a long and detailed research, however F.lli Paris S.r.l. cannot be considered responsible for any incorrect or incomplete data. Owing to the constant development of the products, we reserve the right to make changes to them without prior notice.

Page 10: HYDRAULIC, POWER SUPPLY AND METAL INDUSTRY ITALYdonar.messe.de/exhibitor/hannovermesse/2017/T747177/slib-italy-catalogue-eng-481573.pdfHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

PS: the values shown in the graph were determined with a test of constant load, and running for 1000 cycles at three different temperatures: -190 °C, +18 °C and +260 °C

GRAPHIC LOAD/SPEED

160150140130120110100

90

00.

100.

200.

300.

400.

500.

600.

700.

800.

901.

00

LOAD(N/mm2)

SPEED(m/s)

BEARING SECTION

smooth spherical indentation grooves

SUPPORTING SHELL Carbon Steel S235 JR or Aisi 304 or Bronze CuSn8 – CuZn25Al5

SLIDING LAYERS Self-lubricating black smooth Surface + Bronze (UNI ISP 4383) Cu (Rest) Sn 9 ÷ 11 % Pb 8 ÷ 11 % Layer Thick-ness max 0.50mm

WORKING TEMPE-RATURE min - 180 °C - max + 350 °C min - 180 °C - max + 350 °C min - 180 °C - max + 350 °C

COEFFICIENT OF FRICTION 0.03-0.10 0.03-0.10 0.03-0.10

MAX. SPEED 1.00 m/s 1.00 m/s 1.00 m/s

MAX. STATIC LOAD 310 N/mm2 310 N/mm2 310 N/mm2

MAX. DYNAMIC LOAD(max speed 0.10 m/s)

160 N/mm2 160 N/mm2 160 N/mm2

MAX. DYNAMIC LOAD(max speed 1.00 m/s)

110 N/mm2 110 N/mm2 110 N/mm2

SHAFT The shaft surface finishing, for optimal performance, shall be between 0.40 and 1.60 micron Ra, depending on different application. Hardness 100 – 160 HB5.

Carbon Steel+ Sintering bronze+ Special treatment

Stainless steel+ Sintering bronze+ Special treatment

Bronze+ Special treatment

MEC

HA

NIC

AL

PRO

PERT

IES

SBM-10 SBM-11 SBM-20

This is a material designed for use where a high wear resistance is needed, even when low or high temperature are present, as much as heavy loads. In comparison to similar materials, this product keeps a relatively low coefficient of friction. The self-lubricating layer is a peculiar mixture of sintered bronze and special solid lubricants.

The backing materials used for this product are carbon steel, stainless steel and bronze. We can produce any dimension for any type of special plain bearings, flanged bearings, thrust washer or sliding plates and shaped tapes according to drawings.Normally, this material does not require any lubrication, but it can be used with hydrodynamic lubrication.

SBM Type

Note: The informaton in this data-sheet is to be considered reliable, but conditons and methods of use, which are beyond our control, may modify the results. The informaton and data contained in this data-sheet are the result of a long and detailed research, however F.lli Paris S.r.l. cannot be considered responsible for any incorrect or incomplete data. Owing to the constant development of the products, we reserve the right to make changes to them without prior notice.

Page 11: HYDRAULIC, POWER SUPPLY AND METAL INDUSTRY ITALYdonar.messe.de/exhibitor/hannovermesse/2017/T747177/slib-italy-catalogue-eng-481573.pdfHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

Please write in the order the FASTRACK type you require.During vacation periods or bank holidays, please contact our office to check our delivery capacity.

INCREASE ON OUR STANDARD PRICE SHIPPING COST WITH EXPRESS CURIER

ITALY 100% 40% 20% up to 5 Kg: 15.00 €up to 10 Kg: 25.00 €

EUROPE 100% 40% 20% up to 5 Kg: 25.00 €up to 10 Kg: 35.00 €

NORTH AMERICA 60% 40% up to 5 Kg: 35.00 €up to 10 Kg: 50.00 €

UARANTEED DELIVERY 3 WORKING DAYS 6 WORKING DAYS 10 WORKING DAYS

LIMIT FOR ORDER ACCEPTANCE

by 12 am of theordering day

by 12 am of theordering day

by 12 am of theordering day

FASTRACK 3 FASTRACK 6 FASTRACK 10

SLIBITALY

SLIDING BEARINGS DIVISIONHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

View all FASTRACK services on our website

For the following products:

TF-C TF-316 TF-625 TF-F51WORKING TEMPERATURE min - 190 °C - max + 260 °C min - 190 °C - max + 260 °C min - 190 °C - max + 260 °C min - 190 °C - max + 260 °C

COEFFICIENT OF FRICTION 0.03-0.20 0.03-0.20 0.03-0.20 0.03-0.20

MAX. SPEED 1.00 m/s 1.00 m/s 1.00 m/s 1.00 m/s

MAX. STATIC LOAD 250 N/mm2 250 N/mm2 250 N/mm2 250 N/mm2

MAX DYNAMIC LOAD(velocità massima 0.10 m/s) 140 N/mm2 140 N/mm2 140 N/mm2 140 N/mm2

MAX DYNAMIC LOAD(velocità massima 1.00 m/s) 60 N/mm2 60 N/mm2 60 N/mm2 60 N/mm2

TX-C TX-316 TX-625 TX-F51WORKING TEMPERATURE min - 180 °C - max + 260 °C min - 180 °C - max + 260 °C min - 180 °C - max + 260 °C min - 180 °C - max + 260 °C

COEFFICIENT OF FRICTION 0.03-0.10 0.03-0.10 0.03-0.10 0.03-0.10

MAX. SPEED 0.50 m/s 0.50 m/s 0.50 m/s 0.50 m/s

MAX. STATIC LOAD 300 N/mm2 300 N/mm2 400 N/mm2 400 N/mm2

MAX DYNAMIC LOAD(velocità massima 0.05 m/s) 190 N/mm2 190 N/mm2 190 N/mm2 190 N/mm2

MAX DYNAMIC LOAD(velocità massima 0.50 m/s) 100 N/mm2 100 N/mm2 100 N/mm2 100 N/mm2

PMT-316 PMT-625WORKING TEMPERATURE min - 198 °C - max + 430 °C min - 198 °C - max + 430 °C

COEFFICIENT OF FRICTION 0.06-0.12 0.06-0.12

MAX. SPEED 0.40 m/s 0.40 m/s

MAX. STATIC LOAD 200 N/mm2 200 N/mm2

MAX DYNAMIC LOAD(velocità massima 0.10 m/s) 150 N/mm2 150 N/mm2

MAX DYNAMIC LOAD(velocità massima 0.40 m/s) 100 N/mm2 100 N/mm2

Page 12: HYDRAULIC, POWER SUPPLY AND METAL INDUSTRY ITALYdonar.messe.de/exhibitor/hannovermesse/2017/T747177/slib-italy-catalogue-eng-481573.pdfHYDRAULIC, POWER SUPPLY AND METAL INDUSTRY

via Marconi 142/144 - 24060, Castelli Calepio (BG) - Italytel +39 035 4425511 - fax +39 035 [email protected]