Disclosure to Promote the Right To Information

Whereas the Parliament of India has set out to provide a practical regime of right to information for citizens to secure access to information under the control of public authorities, in order to promote transparency and accountability in the working of every public authority, and whereas the attached publication of the Bureau of Indian Standards is of particular interest to the public, particularly disadvantaged communities and those engaged in the pursuit of education and knowledge, the attached public safety standard is made available to promote the timely dissemination of this information in an accurate manner to the public.

इंटरनेट मानक

“!ान $ एक न' भारत का +नम-ण”Satyanarayan Gangaram Pitroda

“Invent a New India Using Knowledge”

“प0रा1 को छोड न' 5 तरफ”Jawaharlal Nehru

“Step Out From the Old to the New”

“जान1 का अ+धकार, जी1 का अ+धकार”Mazdoor Kisan Shakti Sangathan

“The Right to Information, The Right to Live”

“!ान एक ऐसा खजाना > जो कभी च0राया नहB जा सकता है”Bhartṛhari—Nītiśatakam

“Knowledge is such a treasure which cannot be stolen”

“Invent a New India Using Knowledge”

है”ह”ह

IS 7932 (1982): Boiler Water Treatment Compounds [CHD 13:Water Quality for Industrial Purposes]

IS:79324982 ( Rsaff irmed 1997’)

Indian Standard

SPECIFICATION FOR BOILER WATER TREATMENT COMPOUNDS

( First Revision )

Third Reprint MAY 1998

UDC 621.187.12

0 Copyright 1983

~REAu OP~NDIAN STANDARDS MANAKBHAVAN,9BAHADURSHAHZAFARh4ARG

NEW DELHI 110002

Gr2 February 1983

. -- c v

. .,

.

. *,

__‘. .,

.* ,

IS : 7932 - 1982

Indian Standard SPECIFICATION FOR

BOILER WATER TREATMENT COMPOUNDS

( First Revision )

Boiler Water Sectional Committee, CDC 57

Chairman Representing

SRRI P. C. D. G. SaMUEL Madras Refineries Ltd, Madras

Members

SHRI J. N. BHOWMIK West Bengal State Electricity Board, Calcutta SERI A. K. SANTRA ( Alternate )

SHRI D. CHATTERJEE Delta Enterprises Pvt Ltd, Calcutta DEPUTY DIRECTOR ( CM ),

RDSO, LUCKNOW Railway Board ( Ministry of Railways )

ASSTT CHEMIST & METALLUR- GIST, WR, Bo~B.~Y ( Alternate )

SERI DEV RAJ Power Engineers Training Society, New Delhi DR N. DEVARAJAN Industrial and Agricultural

( Bombay ) Ltd, Bombay Engineering Co

SHRI S. C. DEY Ministry of Industry ( Department of Industrial Develoament ). New Delhi

SRRI SHOMNATH GHOSR Jai Guru Eigineer&g Co ( India ), Calcutta SRRI ANANDAMIY GHOSH ( Alternate )

DR .4. K. GUPTA Hindustan Pertilizer Corporation Ltd, Durgapur Unit, Durgapur

SHRI A. K. SENGUPTA ( Alternate ) SHRI G. T. JADEJA The Tata Hydro-Electric Power Supply Co Ltd,

Bombay SHRI G. M. RAWAL ( Alternate )

SHRIJ. JKA Central Electricity Authority, New Delhi DK V. M. KELKAR Engineers India Ltd, New Delhi

SHRI G. L. RAJANI ( Alternate ) SHRI K. R. KRISRNASWAMY Central Power Research Institute, Bangalore

SHRI P. S. RAJAL ~TCSHMI ( Alternate ) SHRI N. KRITHIVA~AN Central Electrochemical Research Institute ( CSIR ),

Karaikudi SHRI T. M. B.4LASuBRA.ZIANIAN ( Alternate )

SHRI S. M CHA~~EVAN Chemical Consultants, Madras SHRI C. S. RAGHAVAN ( Alternate )

( Continued on page 2 )

@ Copyright 1983

BUREAU GF INDIAN STANDARDS

This publication is protected under the Zndiun Copyright Act ( XIV of 1957 ) and I

leproduction in whole or in part by any means except with written permission of the

- I publisher shall be deemed to be an infringement of copyright under the said Act.

.

‘ ; :,

IS : 7932 - 1982

( Confirmed from page 1 )

hfembers Representing ‘X DR P. K. MATH~R Bhabha Atomic Research Centre, Rombav SRRI R. N~TARAJAN Bharat Heavy EIe( trirals Ltd. Hyderahaci

SHRI T. R. N.~~ARAJAN ( Alternate I ) :

DR A. PRABHAKAR RAO ( Alternate II ) SHRI R. NATARAJAN Hindustan Dorr-Oliver Ltd, Bombay

SRRI SuaA’s~ VERMA ( Alternate ) SHRI RAM GOPAL National Thermal Power Corporation Ltd.

New Delhi SHRI R. K. DWIVEDI ( Alternate 1

SRRIN.RAMACHANDRAN. ion Exchange ( India ) Ltd, Bombay SHRI S. CHANDRASIXH~R ( Alternate )

DR S. K. ROY The Alkali 8r Chemical Corpor&ion of India Ltd. Calcutta

DR V. K. SETH Projects & Development India Ltd, Sindri SKRI S. K. SHO&ZE Development Consultants Pvt Ltd, Calcutta

SHRI R. N. BANERJEE ( Alternate ) SHRI D.’ P. SINCH Delhi Electric Supply Undertaking, New Delhi

S&r K. B. CHHABRA ( Alternate ) SRRI G. P. SINGH Steel Authority of India Ltd, New Delhi

SHRI A. P. SINHA ( Alternate ) SHRIS. K. MATHUR, Director General, ISI ( Ex-o~rio Alember )

Head ( Chemicals )

Secrelary

SHRI A. K. BAHL Assistant Director ( Chemicals ), IS1

AMENDMENT NO. 1 JUNE 2010 TO

IS 7932 : 1982 SPECIFICATION FOR BOILER WATER TREATMENT COMPOUNDS

( First Revision )

(Page 4, clause 2.3.1, line 7) — Substitute ‘IS 1070 : 1992*’ for

‘IS : 1070­1977*’.

(Page 4, clause 2.3.2, lines 1 and 2) — Substitute ‘IS 3025 (Part 21) : 1983†’ for ‘16 of IS : 3025­1964†’.

(Page 4, footnote marked *) — Substitute ‘*Reagent grade water — Specification (third revision)’ for ‘*Specification for water for general laboratory use (second revision)’.

(Page 4, footnote marked †) — Substitute ‘†Methods of sampling and test (physical and chemical) for water and waste water: Part 21 Total hardness (first revision)’ for ‘†Methods of sampling and test (physical and chemical) for water used in industry’.

(Page 5, clause 2.4.1.1, line 2) — Substitute ‘IS 2002 : 1992*’ for ‘IS : 2002­1962*’.

(Page 5, clause 2.4.1.1, line 8) — Substitute ‘IS 715 : 2002†’ for ‘IS : 715­1966†’.

(Page 5, clause 2.4.1.2, line 3) — Substitute ‘IS 1070 : 1992‡’ for ‘IS : 1070­1977‡’.

(Page 5, footnotes) — Substitute the following for the existing footnotes: ‘*Steel plates for pressure vessels for intermediate and high temperature service including boilers — Specification (second revision). †Coated abrasives — Specification (fourth revision). ‡Regent grade water — Specification (third revision).’ (CHD 13)

Reprography Unit, BIS, New Delhi, India

IS : 7932 - 1982

Indian Standard SPECIFICATION FOR

BOILER. WATER TREATMENT COMPOUNDS

( First Revision )

0. FOREWORD

0.1 This Indian Standard ( First Revision ) was adopted by the Indian Standards Institution on 30 November 1982, after the draft finalized by the Boiler Water Sectional Committee had been approved by the Chemical Division Council.

0.2 Boiler water treatment compounds/formulations should be able to reduce the hardness of boiler water with or without formation of a sludge which can be eacily removed by blowdown. They should also afford sufficient protection to the boiler surface against corrosion. These compounds are ~prirnarily intended far pressures up to 2’0 MN/mz. For use at pressures beyond that up to 3 9 MN/m2, care should be exercised.

0.3 This standard was first published in 1976. In the preparation of the

earlier version of the standard considerable assistance was derived from data supplied and investigations carried out by the Research, Designs and Standards Organization of the Ministry of Railways, and M/s Jai Guru Engineering CO ( India ) Ltd, Calcutta, and the same is gratefully acknowledged.

0.3.1 In this revision requirement of solubility has been added, the minimum pH value raised from 8 to 9, hardness reduction test made more precise and the allowable metal loss in the metal loss test lowered from 5 g/m2 to 1 g/m2.

8.4 For the purpose of deciding whether a particular requirement of this

standard is complied with, the final value, observed or calculated expressing the result of a test or analysis, shall be rounded off in accord: ante with IS : 2-19607. The number of significant places retained in the rounded off value should be the same as that of the specified value in this standard.

aRulcs for rounding off numerical values ( revised ).

3

IS : 7932 - 1982

1. SCOPE

1.1 This standard prescribes the rrquiremen’ts and’methods of sampling and test for such water treatment compounds/formulations as do’not hziv,e a specific chemical composition, such a~ compoudds of’ qr.ganic origin. The primary objective of such compo.unds is to reduce hardness of water used in boilers and pressure vessels as well as corrosioh in .the process .of internal treatment. ‘.

2. REQUIREMENTS

2.1 General - The material shall be either liquid or. powder and shall be at -least 99’9 percent soluble in water ( 1 percent solution ) at 60°C.

2.2 pH Value - The compounds shall have a pH value of 9 Min, when determined with the help of @H meter. The @r-I value of liquid compounds shall be determined as such and those of solids shall be determined in a one percent, ( m/v ) aqueoui solution.

2.3 Hardness Reduction - The material shall pass the hardness reduction test prescribed in 2.3.1.

2.3.1 Hardness Reduction Test - Prepare a standard -hard water with temporary hardness of450 and permanent hardness of 200 ( total hard- ness 650 ), both expressed in terms of calcium carbonate in mg/l maintaining ratio of calcium hardness to magnesium hardness as 2:l. Add to this the water treatment compound in a ratio recommended by the manufacturer and boil the mixture under reflux for 4 hours, adding distilled water (sea IS : 1070-1977* ) from time to time to keep the volume constant. The compound shall be considered to be satisfactory if:

98 percent Min of the total hardness is removed by precipitation in 30 minutes of boiling, 100 percent total hardness is removed after 4 hours of boiling, PH of the water is between 10.5 and 11.5 after boiling and no foaming tendency is noticed while boiling.

To-another water sample, add the water treatment compound in a ratio recommended by the manufacturer and allow the mixture to stand for 24 hours at a temperature not exceeding 40°C. The compound shall be considered to be satisfactory if the super- natant liquid has a total hardness of not more than 40 mg/l and a pH value between 9.5 and 10.5.

2.3.2 Total hardness shall be determined as prescribed in 16 of IS : 3025-J964t.

*Specification for water for genrral laboratory use ( second revision ). +Methods of sampling and test ( physical and chemical ) for water used in industry.

4

: s

. . . IS : 7932 - 1982 .

2.4 Metal Loss - “h$ material shall pass the metal loss test prescribed in’ 2.4.1. ,

.* 2.4.1 ifetal Loss i-at .-.

_

’ 2.4.1.1. PreI; are*a 16 cm2 r,ectangular panel of nominal thickness 5’ mm mahe ‘of boiler quality steel ( see IS : 2002-1962* ) or of metal or alloy of whicli.th& liressure vessel. is made, to a fine surface finish by the procedure given below a’nd weigh it:

Rub the panel with Coarse ‘emery and then clean with petroleum hydrocarbon solvent or any other solvent. Remove rust and any

signs of corrosion with flint paper of IS Grit Number 100(2/O) ( ice IS : 7‘15-19661_ ). Then rinse with benzene and wipe dry with a clean rag.

2.4.1.2 Prepare the water treatment compound for application as recommended by the manufacturer in a covered beaker using distilled water conforming to IS :’ 1070-1977$, dip a portion of the metal panel, approximately 3/&h of its area, in the prepared compound and heat at boiling point for a total period of 54 hours involving heating for six hours each day, the solution being made up to its initial volume throughout the test by adding distilled water.

2.4.1.3 At intervals of 18, 30, 42 and 54 hours take out the panel from the beaker, rinse with water, clean with a fine soft brush to remove deposits, then further rinse with acetone, and dry in a desiccator. Weigh the dry panel.

2.4.1.4 The treatment compound shall be considered to be satisfactory if the metal loss is not more than 1 g/m2 at or earlier than 42 hours and if it does not cause any pitting on the body of the panel, particularly at the solution vapour phase line, when examined visually. Report also the results after 54 hours test. Metal loss result after 54 hours test shall be not more than result for 42 hours test.

3. PACKING AND MARKING

3.1 Packing - The material shall be packed in drums or as agreed to between the purchaser and the supplier.

3.2 Marking - The containers shall be securely closed and shall bear legibly and indelibly the following information:

a) Name of the material;

b) Name of the manufacturer and his recognized trade-mark, if any;

*Specification for steel plates for boilers. $Specification for coated abrasives, glue bond ( second revision ). SSpccilication for water for general laboratory use ( secnnd r&ion ).

IS : 7932 - 1982

4 4 e) f 1

32.1

Net mass or volume ( for powder/liquid respectively );

Batch number;

Date of manufacture; and

Shelf life.

The containers may also be marked with the BIS Certification Mark.

32.1.1 The use of the Standard Mark is governed by the provisions of the Bureau of Indian Standards Act, 1986 and the ~Rules and Regulations made. thereunder. The details of conditions under which the licence for the use of Standard Mark may be granted to manufacturers or producers may be obtained from the Bureau of Indian Standards.

4. SAMPLING

4.1 The method of drawing representative samples of the material and criteria for their conformity shall be as prescribed in Appendix A.

APPENDIX A ( Clause 4.1 )

SAMPLING OF BOILER WATER TREATMENT COMPOUNDS

A-l. GENERAL REQUIREMENTS OF SAMPLING

A-1.0 In.drawing, preparing, storing and handling samples, the following precautions and directions shall be observed.

A-l.1 Samples shall not be taken in an exposed place.

A-1.2 The sampling instruments shall be clean and dry.

A-1.3 Precautions shall be taken to protect the samples, the material being sampled, the sampling instruments and the containers for samples from adventitious contamination.

A-1.4 To draw a representative sample, the contents of each container selected for sampling shall be mixed as thoroughly as possible by suitable means.

6

IS : 7932 - 1982 *

A-l.5 The sample shall be placed in clean and airtight glass bottles or other suitable containers on which the material has no action and which have been previously washed several times with the material to be sampled.

A-l.6 The sample containers shall be of such a size that they are filled by the sample leaving an ullage of not more than five .percent.

A-l.7 Each sample container shall be sealed airtight.after filling, and marked with full details of sampling, the date of sampling and the year of manufacture of the material.

A-2. SCALE OF SAMPLING

A-2.1 Lot - All containers in a single consignment of the material drawn from a single batch of manufacture shall constitute a lot. If a consignment is declared or known to consist of different batches of manufacture, the batches shall be marked separately and the groups of containers in each batch shall constitute separate lots.

A-2.2 For ascertaining conformity of the material in a lot to the require- ments of this specification, samples shall be tested for each lot separately. The number of containers to be selected at random from lots of different sizes shall be in accordance with Table 1.

TABLE 1 NUMBER OF CONTAINERS TO BE SELECTED FOR SAMPLXNG

Lm Srzl: SAI~PLE SIZE

.,v n

(1) (2)

Rto 15 3

16 to 40 4

41 to 6.5 5

66 to 110 7

111 and ahovc 10

A-2.2.1 In order to ensure randomness of selection, the following procedure shall be adopted:

‘Arrange all the containers in the lot in a systematic manner and starting from any one, count them as 1, 2, 3 . . . . . . . . . up to Y, where r is the integral part of Jv/tr ( N and n being the lot size and sample size respectively ). Every rth container thus counted shall be withdrawn to oonstitute the test sample.

7

A-3. PREPARATItiN- O# d&i&ES

A-3.1 From each of the containers sel$ti$&cording to A-2.2.1, equal portions of the material shall :be taken out QO: that the total quantity collected from nli the container<& about=8 litres or 6 kg. This shall be the composite sample.

. . . ’ ’ _’

. . A-32 The composite sample sh& be divided into 3 test samples. not less. than 2 litres or 2 kg each. These. tyst samples shall be transferred immediately to thoroughly +shed.bo!?les-ybich are sealed airti,ght with glass stoppers and marked &it% ~l$‘jxi#~i&&ws of ‘sampling as given ih

A-1.7. One test samfile4C4.I be s&t' too&k purchaser and one to the’ ’ supplier. The third test sample* bearing 1be’ seals of the purchaser ahd the supplier shall constitute the referee sampIe, to’ be u&l in ’ case+of dispute. . .

‘\ 1. ‘; . A-3.3 Tests for determination .of all .characteristics given in’ 2 shAl1 be conducted on the composite sample. .

- I

A-4. CRITERIA FOIMONFO@ITY ’ ‘.

t

’ ;

A-l.1 The lot shall be declared as conforming to the require*ments of this specification if all the test results on the composite sample satisfy the corresponding requiremeets givenin 2.

r.

. .