8/12/2019 LG Profile Technical Data

1/2

LG Hausys TECHNICAL DATA

Sr No Description UOM

1 Wind pressure Resistance kgf/cm 259

LG profile spec standard - Korean standard KS F 5602CPE chemical composition (attached report)

Light resistance test ( 4000 hrs on xenon & weather apparatus) KS standard

Air tightness KS F 2292

2 Sound for single glazing Rw dB 29

Sound for double glazing Rw dB 40

3a specification for profile-casements (BF 60 WOA)

Wall thickness (outer wall) mm 2.5

Non-visible surfaces mm 2

Internal Webs mm 1.2

3b Sliding Window System (BF-60ND )

Wall thickness (outer wall) mm 2

Non-visible surfaces mm 2

Internal Webs mm 1

Inter lock mm 1.7

4 Colour

White code

L ( lightness) Value 93.32

a ( H:Red, L: Green) Value -0.45b (H:Yellow, L: Blue) Value 2.91

E 93.32

5 Profile Specification/Test Results

i Limiting Oxygen Index as per ASTM D 2863 % NA

ii Thermal conductivity as per DIN 52612 W/m2k

5mm glass (normal) W/m2k 5.263

22mm glass ( Low-e) W/m2k 1.976

iii Density as per DIN 53495 g/cc 1.5

iv Water absorption as per DIN 53495 % 0

v Flexural modulus of elasticity as per EN ISO 178 Mpa 2500.5

vi Vicat softening temperature as per EN ISO 306 C 92.8

vii Resistence to impact by falling mass at-10 Cat 250g load as per EN 477 kJ/m 13.5

viii Behaviour after heat aging at 150 C for 30+/-3 min as per EN 478 - Pass

ix Heat reversion as per EN 479 % Pass

X Hardness,shore D as per ISO 868 - 99.9

Tensile Strength as per ASTM D 638 Mpa 41.2

xi Elongation at break as per ASTM D 638 % 156.3

Tensile Modulus as per ASTM D 638 Mpa NA

xii

Charpy Impact strenth (At 15j Hammer)afer aging in Xenon Arc Weather -o-

meter as per ASTM D 256

kJ/m

(After 1000

hrs.) 13.4

8/12/2019 LG Profile Technical Data

2/2

xii

Artificial weathering test to standard ISO/CD 4832-2(XENNOTEST-BETA-LM)-

Light Source-NXE2200

Change after

hours NA

xiv

sample exposed in Xenon Arc weather-o-meter for period comparable with

stipulated expose to the sun for 1600,Hrs as per IS:13592-1992 hrs 1000

xv Flammability as per UL-94 NA

xvi Heat reversion test as per IS 4985-00 % 1.76

xvii Stress relief test as per IS 13592-92 NA

xviii

Impact strength at ( -10 degree centigrade for 1 hour at 250 gms load ) IS-

4985-00 Pass

xix RoHS compliance test results:

Cadmium, cd X

Lead, Pb mg/kg 0.8

Mercury, Hg X

Hexavalent Chromium, Cr+6 X

PBDE X

xx Permisible deflection mm 2

6 Hardware

i Hardware Make & Origin Korea

7 Gasket

i Type EPDM

ii Name of Manufacturer LG

iii Country Korea

iv Thickness mm 5

v Thickness of beading mm 1.5

8 Reinforcement details: as per supplier to fabricator

9 Warrentyi On Profile against colour change Year/s 10

ii On Hardware functioning Year/s 1

iv On Gasket Year/s 1