metal forming, production engineering ii
DESCRIPTION
Production EngineeringTRANSCRIPT
![Page 1: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/1.jpg)
Lecturer:-Zeradam Y.
March, 2014
Ambo University Institute of Technology
Department of Mechanical Engineering
Production Engineering II (MEng 3162)
![Page 2: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/2.jpg)
Outline
• Sheet metal forming operation
• Applications of sheet metal
• Cutting operationShearingBlankingPunching
• Engineering analysis of sheet metal cutting
![Page 3: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/3.jpg)
Part ISheet metal forming
Sheet metal working includes cutting and forming operations performed on relatively thin sheets of metal.
Shearing Blanking Punching
Bending Drawing Spinning Stretching
Cutting Forming
![Page 4: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/4.jpg)
Con..
Typical sheet metal thicknesses are below 6mm (1/4in). When the thickness exceeds about 6mm,the stock is
usually referred to as plate rather than sheet. The sheet or plate stock used in sheet metalworking is
produced by rolling.
![Page 5: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/5.jpg)
Applications
Construction equipments
Automobile and truck bodies
Ship building furniture Railway Cars
Airplane
![Page 6: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/6.jpg)
Con..
space industries;
Chemical industry;Drink & food industry.
Nuclear
![Page 7: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/7.jpg)
Con..
Shower cabinets and others Washing machines
Cookers Refrigerator bodies
Domestic use
![Page 8: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/8.jpg)
Five basic sheet metal operations
Cutting Shearing Blanking Punching
![Page 9: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/9.jpg)
Con..
Forming Bending, Spinning, Stretching, Drawing
![Page 10: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/10.jpg)
Cutting operation
• Cutting of sheet metal is accomplished by a shearing action between two sharp cutting edges.
• The upper cutting edge (the punch) sweeps down past a stationary lower cutting edge(the die).
![Page 11: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/11.jpg)
Con..
c
(1)
Just before the punch contact the work
![Page 12: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/12.jpg)
Con..
• c
(2)
Punch begins to push into the work, causing plastic deformation
![Page 13: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/13.jpg)
Con..
• c
(3)
Punch compresses and penetrates into the work and causing a smooth cut surface
![Page 14: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/14.jpg)
Con..
• c(4)
Fracture is initiated at the opposing cutting edges that separate the sheet.
Symbols V and F represents motion and applied force , respectively, t = stock thickness , c = clearance.
![Page 15: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/15.jpg)
Shearing
• Is a sheet metal cutting operation along a straight line between two cutting edges.
• Shearing is typically used to cut large sheets into smaller sections for subsequent press working operations.
![Page 16: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/16.jpg)
Con..
• It is performed on a machine called a power shear, or squaring shear.
• The upper blade of the power shears is often inclined (to reduce
cutting force).
• The shearing operation constitutes the first stage of any forming
process by producing either
The starting material (cutting out of a sheet) OR
Preparing an existing work piece e.g by punching a hole or a
series of holes before forming.
![Page 17: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/17.jpg)
Blanking
• Involves cutting of sheet metal along a closed outline in a single step to separate the piece from the surrounding stock, as shown in figure a the part that is cut out is the desired product in the operation and is called the blank.
![Page 18: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/18.jpg)
Punching
• Is similar to blanking except that the separated piece is scrap, called the slug. the remaining stock is desired part. the distinction is illustrated in figure b.
![Page 19: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/19.jpg)
Engineering analysis of sheetmetal cutting
• One of the important parameters in sheet metal cutting is clearance between the punch and die
• The clearance c in a shearing operation is the distance between the punch and die.
• Typical clearance in conventional press working range between 4% and 8% of the sheet metal thickness t.
![Page 20: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/20.jpg)
Con..
• Measured perpendicular to the direction of the blade movement.
• It affects the finish of the cut(burr) and machine’s power consumption.
![Page 21: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/21.jpg)
Con..
• If the clearance is too small, then the fracture line tend to pass each other ,causing a double burnishing and large cutting force.
![Page 22: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/22.jpg)
con..
• If the clearance is too large ,the metal becomes pinched between the cutting edges and an excessive burr results.
![Page 23: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/23.jpg)
Con..
• The correct clearance depends on sheetmetal type and thickness.
• The recommended clearance can be calculated by the following formula:
C = Act
Where:
C=Clearance , mm;
Ac = Clearance allowance (percentage of the material thickness)
t=Stock thickness, mm.
![Page 24: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/24.jpg)
Con..
• The clearance allowance is determined according to the type of metal 4.5%, 6% or 7.5% of the material thickness.
• For convenience, metals are classified into three groups with an associated allowance value for each group.
Clearance allowance for three sheet metal groups
![Page 25: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/25.jpg)
Con..
• The calculated clearance values can be applied to conventional blanking and hole-punching operations to determine the proper punch and die sizes.
• The die opening must always be larger than the punch size(obviously).
• Because of the geometry of the sheared edge, the outer dimension of the part cut out of sheet will be larger than the hole size.
![Page 26: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/26.jpg)
Con..
• Punch and die sizes for a round blank of diameter Db are determined as;
Blanking punch diameter =Db-2c
Blanking die diameter =Db
• Punch and die sizes for a round hole of diameter Dh are determined as:
Hole punch diameter = Dh
Hole die diameter = Dh+2c
![Page 27: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/27.jpg)
Con..
Angular Clearance Purpose: allows slug
or blank to drop through die
Typical values: 0.25 to 1.5 on each side
![Page 28: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/28.jpg)
Cutting force
• Estimates of cutting force are important because this force determines the size (tonnage) of the press needed. Cutting force F in sheetmetal working can be determined by
Where S= Shear strength of the metal, Mpa
t = Sthock thickness, mm
L= length of the cut edge,mm
• In blanking ,punching ,slotting ,and similar operations , L is the perimeter length of the blank or hole being cut.
•
![Page 29: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/29.jpg)
Con..
Example
A round disk of 150mm diameter is to be blanked from a
strip of 3.2mm cold rolled steel whose shear
strength=310MPa. Determine (a) the appropriate punch
and die diameters, and (b) blanking force.
![Page 30: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/30.jpg)
Con..
Other sheet-metal cutting operations
![Page 31: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/31.jpg)
Cutoff
Is a shearing operation in which blanks are separated from a sheet-metal strip by cutting the opposite sides of the part in sequence.
![Page 32: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/32.jpg)
Con..
With each cut, anew part is produced.
Distinguish it from a conventional shearing operation.
• The cut edges are not necessarily straight
![Page 33: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/33.jpg)
Parting
Involves cutting a sheet-metal strip by a punch with two cutting edges that match the opposite sides of the bank.
![Page 34: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/34.jpg)
Con..
This might be required because the part outline has an irregular shape.
Parting is less efficient than cutoff in the sense that it results in some wasted materials.
![Page 35: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/35.jpg)
Slotting
Is the term sometimes used for a punching operzation that cuts out an elongated or rectangular hole.
![Page 36: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/36.jpg)
Perforating
Involves the simultaneous punching of a pattern of holes in sheet metal.
The hole pattern is usually for decorative purposes, or allow passage of light, gas, of fluid.
![Page 37: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/37.jpg)
Notching and Seminotching
• Notching involves cutting out a portion of metal From the side of the sheet or strip.
• Seminotching removes a portion of metal from the interior of the sheet.
![Page 38: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/38.jpg)
Con..
Seminotching might seem the same as punching and slotting operation.
The difference is that the metal removed by seminotching creats part of the blank outline, while punching and slotting creates holes in the blank.
![Page 39: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/39.jpg)
Shaving
![Page 40: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/40.jpg)
Fine blanking
Is a shearing operation used to blank sheet metal parts with close tolerances and smooth, straight edges in one step, as illustrated in figure (b).
![Page 41: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/41.jpg)
Con..
Pressure pad applies holding force(Fh) in order to prevent distortion.
The punch then descends with slower than the normal velocity and smaller clearance to provide the desired dimension and cut edge.
The process in usually for small stock thicknesses.
![Page 42: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/42.jpg)
Questions ?
![Page 43: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/43.jpg)
Part II
![Page 44: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/44.jpg)
Bending operation
Bending in sheet metal work is defined as the straining of the metal around a straight axis (figure a).
During bending the metal on the inside of the neutral plane is compressed ,while the metal on the outside of the neutral plane is stretched (figure b).
![Page 45: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/45.jpg)
Con..
• The metal is plastically deformed so the bend takes a permanent set upon removal of stresses that caused it.
• Bending produces little or no change in the thickness of the sheet metal.
![Page 46: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/46.jpg)
V-Bending and Edge bending
Bending operations are performed by using punch and die tooling .
The common bending methods are
1. V-Bending ,performed with a V-die.
![Page 47: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/47.jpg)
Con..
2. Edge bending , performed with wiping die.
![Page 48: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/48.jpg)
Con..
![Page 49: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/49.jpg)
Engineering analysis of bending
The metal of thickness t is bend through an angle called the bend angle α.
This results in a sheet metal part with an included angle α’, where α + α’= 180°
![Page 50: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/50.jpg)
Con.. R=Inside Bend radius
W= The bend is made over the width of the work piece W.
Kba= k factor ( the location of the neutral axis in the material.
• Calculated as the ratio of the neutral axis (measured from the inside
bend surface to the material thickness)
• Since neutral axis is the theoretical location at which the material is
neither compressed nor stretched .we use the following
recommended values of K.
![Page 51: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/51.jpg)
Con..
Recommended value of Kba
R<2t,Kba=0.33
R ≥2t,Kba=0.50 t=stock thickness
![Page 52: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/52.jpg)
Bend allowance
The bend allowance (Ab) is the length of the neutral axis between the bend lines, or the arc length of the bend.
![Page 53: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/53.jpg)
Spring back When the bending pressure removed at the end of deformation ,elastic
energy remains in the bent part ,causing it to recover particularly to its original shape. This elastic recovery is called springback.
Figure: (1) during the operation ,the work is forced to take the radius Rt and included angle α’t determined by the bending tool (punch in v-bending) (2) after the punch is removed ,the work springs back to radius R and included angle α’. Symbol: F=applied bending force.
![Page 54: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/54.jpg)
Con..
• Spring back in bending show itself as a decrease in bend angle and an increase in bend radius.
Sb= spring backα’= Included angle of the sheet metal (after spring
back)α’t =Included angle of the bending tool
![Page 55: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/55.jpg)
Compensation for springback
Can accomplished by several methods one of these methods is over bending. Due to this elastic recovery, it is necessary to over-bend the sheet a precise amount to achieve the desired bend radius and bend angle . This is called over bending.
![Page 56: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/56.jpg)
Bending force
![Page 57: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/57.jpg)
Con..
F = Bending force
TS = Tensile strength of the sheet metal
W = Width of part in the direction of the bend axis.
t= stock thickness
D=die opening dimension
Kbf= Is a constant for differences encountered in actual bending process. Its value depends on type of bending: For V-bending, Kbf=1.33; and for edge bending, Kbf=0.33
![Page 58: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/58.jpg)
Con..
Example: A sheet metal blank is to be bent as shown in figure below. The metal has a modulus of elasticity=205(103) MPa, yield strength=275MPa, and tensile strength=450MPa. Determine (a) the starting blank size and (b) the bending force if a V-die is used with a die opening dimension = 25mm.
![Page 59: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/59.jpg)
Other bending operations
Flanging
![Page 60: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/60.jpg)
Con..
![Page 61: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/61.jpg)
Con..
![Page 62: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/62.jpg)
Miscellaneous bending operations
• Figure: miscellaneous bending operations: (a) channel bending (b) U-bending
(c) air bending
(d) offset bending
(e) corrugating
symbol : F=applied force.
Bending
![Page 63: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/63.jpg)
Part III
![Page 64: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/64.jpg)
Drawing
Drawing is a sheet metal forming operation used to make cup shaped ,box-shaped ,or other complex curved, hollow shaped parts.
It is performed by placing a piece of sheet metal over a die cavity and pushing the metal into the opening with a punch.
The blank must be held down flat against the die by blank holder.
![Page 65: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/65.jpg)
Con..
( a ) Drawing of cup shaped part :
(1) start of operation before punch contacts work, and
(2) near end of stroke
![Page 66: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/66.jpg)
Con..
(b) Workpart:
(1) starting blank, and
(2) drawn part .
Symbols: C=clearance, Db=blank diameter, Dp= punch diameter, Rp=punch corner radius, F=drawing force,Fh=holding force.
![Page 67: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/67.jpg)
Parts produced
Ammunition shellsBeverage
SinksAutomobile and
Other parts
![Page 68: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/68.jpg)
Mechanics of drawing
A blank diameter Db is drawn into a die by means of a punch of diameter Dp.
The punch and die must have a corner radii, given by Rp and Rd .
![Page 69: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/69.jpg)
Con..
If the punch and die were to have sharp corners (Rp and Rd=0) a hole punching process wood be accomplished rather than drawing operation.
The sides of the punch and die are separated by a clearance c.
The clearance in drawing is about 10% grater than the stock thickness.
C= 0.1t
![Page 70: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/70.jpg)
Con..
![Page 71: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/71.jpg)
Stages in deformation of the work
1) Punch makes initial contact with work
![Page 72: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/72.jpg)
Con..
2) bending
![Page 73: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/73.jpg)
Con..
3) straightening
![Page 74: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/74.jpg)
Con..
4) Friction and compression
![Page 75: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/75.jpg)
Con..
5) Final cup shape
![Page 76: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/76.jpg)
Engineering analysis of drawing
Checking for feasibility of the operation
First Drawing ration: The ratio of blank diameter Db to
punch diameter Dp.
Un upper limit on the drawing ration is a value of 2.0 (DR≤2.0)
![Page 77: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/77.jpg)
Con..
Second Reduction r
The value of reduction r should be less than 0.50
![Page 78: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/78.jpg)
Con..
Third Thickness to diameter ration
It is desirable the ratio to be greater than 1%.
![Page 79: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/79.jpg)
Con..
Example 1
![Page 80: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/80.jpg)
Drawing force
F = drawing force, Nt = original blank thicknessTS= tensile strengthDb and Dp = starting blank and punch diameter.
Constant 0.7 is correction factor to account for friction.
![Page 81: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/81.jpg)
Con..
Where Fh=holding force in drawing ,NY=yield strength of the sheet metalt =starting stock thickness,mmRd=die corner radius, mm
The holding force (Fh) required can be calculated by using the following formula.
![Page 82: Metal Forming, Production Engineering II](https://reader035.vdocument.in/reader035/viewer/2022081508/557d472bd8b42ae3298b4727/html5/thumbnails/82.jpg)
Con..
1
Example 2