newuk_p

Technical Data

ALKYDPRIMER

Product descriptionAlkydprimer is an alkyd based primer. This product is part of a complete system which is certified not to spread surface flames.

Recommended useAs a primer for steel structures as part of a suitable alkyd system. Good adhesion to correctly

pretreated aluminium. Dries quickly and is resistant against dry heat up to 120°C.

Film thickness and spreading rateMinimum Maximum Typical

Film thickness, dry (µm) 30 50 40

Film thickness, wet (µm) 60 95 75

Theoretical spreading rate (m²/l)

17,3 10,4 13

Physical propertiesColour Red and Grey

Solids (vol %)* 52 ± 2

Flash point 36ºC ± 2 (Setaflash)

Gloss Flat

Flexibility Good

*Measured according to ISO 3233:1998 (E)

Surface preparation

All surfaces should be clean, dry and free from contamination. The surface should be assessed and treated in accordance with ISO 8504.

Bare steelCleanliness: Blast-cleaning to Sa 2½ (ISO-8501-1:1988). Power tool cleaning to min. St 2 (ISO 8501-1:1988) may be acceptable, subjected to exposure conditions.

Shopprimed steelClean, dry and undamaged approved blast-primer.

Coated surfacesClean, dry and undamaged compatible primer. Please contact your local Jotun office for more information.

Other surfacesThe coating may be used on other substrates. Please contact your local Jotun office for more information.

ALKYDPRIMER

Condition during applicationThe temperature of the substrate should be minimum 3ºC above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to ensure correct drying.

Application methodsSpray Use airless spray or conventional spray

Brush Recommended for stripe coating and small areas, care must be taken to achieve the specified dry film thickness.

Roller May be used but is not recommended for first primer coat, however when using roller application care must be taken to apply sufficient material in order to achieve the specified dry film thickness.

Application dataThinner/Cleaner Jotun Thinner No. 2

Guiding data airless spray

Pressure at nozzle 15 MPa (150 kp/cm² 2100 psi).

Nozzle tip 0.38-0.53 mm (0.015-0.021").

Spray angle 40-80°

Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:

* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate

Substrate temperature 5°C 10°C 23°C 40°C

Surface dry 4 h 3,5 h 2,5 h 1 h

Through dry 28 h 22 h 6 h 4 h

Dry to recoat, minimum 28 h 22 h 16 h 10 h

The given data must be considered as guidelines only. The actual drying time/times before recoating may be shorter or longer, depending on film thickness, ventilation, humidity, underlying paint system, requirement for early handling and mechanical strength etc. A complete system can be described on a system sheet, where all parameters and special conditions could be included.

Typical paint systemAlkyd primerPilot IPilot II

2 x 40 µm1 x 40 µm1 x 40 µm

(Dry Film Thickness)(Dry Film Thickness)(Dry Film Thickness)

Other systems may be specified, depending on area of use

StorageThe product must be stored in accordance with national regulations. Preferred storage conditions are to keep the containers in a dry space provided with adequate ventilation. The containers should be sealed tightly.

ALKYDPRIMER

HandlingHandle with care. Stir well before use.

Packing size5 l , 20 l

Packing may vary from country to country according to local requirements.

Health and safetyPlease observe the precautionary notices displayed on the container. Use under well ventilated conditions. Do not breathe or inhale mist. Avoid skin contact. Spillage on the skin should immediately be removed with suitable cleanser, soap and water. Eyes should be well flushed with water and medical attention sought immediately.

For detailed information on the health and safety hazards and precautions for use of this product, we refer to the Material Safety Data Sheet.

DISCLAIMERThe information in this data sheet is given to the best of our knowledge based on laboratory testing and practical experience. However, as the product is often used under conditions beyond our control, we cannot guarantee anything but the quality of the product itself. We reserve the right to change the given data without notice.

Head Office & NordicJotun PaintsP.O. Box 2021N-3248 SandefjordNorwayPhone +47 33 45 70 00Fax +47 33 46 46 13

EuropeJotun Paints (Europe) Ltd.Stather Road, FlixboroughNorth Lincolnshire DN15 8RRUnited KingdomPhone +44 172 44 00 000Fax +44 172 44 00 100

Middle EastJotun U.A.ERamoul Street, RashidiyahP.O Box 3671Dubai U.A.EPhone +971 4 2 85 15 15Fax +971 4 2 85 90 51

South East AsiaJotun (Singapore) Pte. Ltd.No 11-15, Sixth Lok Yang RoadJurongSingapore 628 111Phone +65 26 54 711Fax +65 26 57 484

Jotun is a World Wide company with factories, sales offices and stocks in more than 50 countries. For your nearest local Jotun address please contact the nearest regional office or visit our website at www.jotun.com

ISSUED 12 FEBRUARY 2002 BY JOTUN PAINTSTHIS DATA SHEET SUPERSEDES THOSE PREVIOUSLY ISSUED

ALKYDPRIMER

Technical DataALUFLEX

Product descriptionAluflex is an aluminium pigmented paint based on a flexible penetrating alkyd oil.

Recommended useFor use in cargo holds and on areas where a thorough pretreatment cannot be carried out. Aluflex penetrates porous surfaces.


Film thickness, dry (µm) 20 50 25Film thickness, wet (µm) 50 120 60Theoretical spreading rate (m²/l)

20 8 16

Physical propertiesColour AluminiumSolids (vol %)* 40 ± 2 Flash point 38ºC ± 2 (Setaflash)Gloss FlatWater resistance FairFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation


Bare steelRemove heavy rust scale.

Coated surfacesIf applied on top of old coating systems (i.e. epoxy or polyurethane), it may be necessary to abrade the surface.



ALUFLEX Page 1

Application methodsSpray Use airless spray or conventional sprayBrush Recommended for stripe coating and small areas, care must be taken to achieve

the specified dry film thickness.Roller May be used however when using roller application care must be taken to apply

sufficient material in order to achieve the specified dry film thickness.

Application data Thinner/Cleaner Jotun Thinner No. 2Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi.).Nozzle tip 0.38 - 0.53 mm (0.015 - 0.021").Spray angle 60 - 80° Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate

Substrate temperature 5°C 10°C 23°C 40°CSurface dry 2 h 2 h 1 h 1 hThrough dry 20 h 10 h 8 h 2 hDry to recoat, minimum 12 h 9 h 6 h 4 h


Typical paint systemAluflexAluflex

1 x 25 µm1 x 35 µm

(Dry Film Thickness)(Dry Film Thickness)

Touch-upFull coat


StorageThe product must be stored in accordance with national regulations. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition.Containers must be kept tightly closed.


Packing size20 l Packing may vary from country to country according to local requirements.

ALUFLEX Page 2










ALUFLEX Page 3

Technical DataALUMINIUM PAINT H.R.

Product descriptionAluminium Paint H.R. is a heat resistant paint, based on an alkyd oil.

Recommended useOn steel items exposed to temperatures up to 250°C, e.g. exhaust pipes, engine parts etc. Can be used as an exterior aluminium finish usually within an alkyd system.



18 12 14,4

Physical propertiesColour AluminiumSolids (vol %)* 36 ± 2 Flash point 36ºC ± 2 (Setaflash)Gloss Aluminium sheenAbrasion resistance FairFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation


Bare steelCleanliness: Blast cleaning to min. Sa 2 ½ (ISO 8501 1:1988), Roughness: use suitable abrasives to achieve Grade Coarse G (85 - 130 µm, Ry5) (ISO 8503-2).



ALUMINIUM PAINT H.R. Page 1


the specified dry film thickness.Roller May be used but is not recommended for first primer coat, however when using

roller application care must be taken to apply sufficient material in order to achieve the specified dry film thickness.

Application data Thinner/Cleaner Jotun Thinner No. 2Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi.).Nozzle tip 0.38 - 0.46 mm (0.015 - 0.018").Spray angle 40 - 60°Filter Check to ensure that filters are clean.




Typical paint systemAluminium Paint HR 2 x 25 µm (Dry Film Thickness)Other systems may be specified, depending on area of use




Packing size5 lPacking may vary from country to country according to local requirements.











Technical DataANODESHIELD ICCP

Product descriptionAnodeshield ICCP is a practically solvent-free, abrasion resistant, two-pack epoxy coating which contains glass flakes.

Recommended useA high build, practically solvent free coating for steel subjected to extreme submerged exposure and mechanical impact. Particularly suitable as anode shield in impressed current cathodic protection systems.



4 1,5 2

Physical propertiesColour Red and GreySolids (vol %)* 98 ± 2 Flash point >55ºC Gloss GlossyGloss retention FairWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Flexibility FairCompatibility withcathodic protection Excellent


Surface preparation




Condition during applicationThe temperature of the substrate should be minimum 10°C and at least 3°C above the dew point

ANODESHIELD ICCP Page 1

of the air, temperature and relative humidity measured in the vicinity of the substrate. The coating should not be exposed to oil, chemicals or mechanical stress until fully cured.

Application methodsSpray Two-comp. heated airless spray Brush Stiff nylon brushOther Putty knife

Application data Mixing ratio (volume) 2 parts Comp. A (base) to be mixed thoroughly with 1 part Comp. B

(curing agent).Pot life (23°C) 30 minutes. In two-comp. spray 40°C - 5 minutes. Thinner/Cleaner Jotun Thinner No. 17/Do not thin when used as anodeshield.Guiding data airless sprayPressure at nozzle 20 MPa (200 kp/cm² 2800 psi).Nozzle tip 0.63-1.09 mm (0.025-0.043").Spray angle 40-80ºFilter Remove all filters.


Substrate temperature 10°C 23°C 40°CSurface dry 10 h 4 h 2 hThrough dry 16 h 7 h 3,5 hCured 14 d 7 d 3 d

Dry to recoat, minimum 16 h 7 h 3,5 h

Dry to recoat, maximum 1 5 d 3 d 2 d

The surface should be free from chalking and contamination prior to application. If the 1.maximum dry to recoat time is exceeded, please contact Jotun Paints for advice.


Typical paint systemBlastcleaning to Sa 2½Anodeshiled ICCPAn approved primer

2 x 400 µm1 x 150 µm


(For overcoating, please contact Jotun Paints for advice.)Other systems may be specified, depending on area of use


Brief application procedure:The steel is to be blast cleaned to at least Sa 2½ (ISO 8501-1:1988). To obtain a good 1.anchor pattern the surface roughness should be minimum 50 microns.The steel temperature should be min. 3°C above the dewpoint of the air close to the steel 2.surface when the paint is applied.Shortly after blast cleaning and before any rust is visible, the first coat is to be applied. 3.The two-pack epoxy is to be applied by stiff nylon brushes or putty-knives. It is important that the coating is thoroughly worked into the steel substrate to secure the best adhesion. Two-component, heated airless spray can also be used. The second coat is to be applied as soon as the first coat is sufficiently cured, and not being 4.too hard. For guidance at least 10 hours at 23°C and at least 20 hours at 10°C between the coats should be allowed for. The maximum curing time before application of the second coat should be 3 days at 23°C.To speed up the curing process at low temperature, the use of warm, dry air is 5.recommended.To secure a better adhesion of the antifouling paint it is advisable to apply one to two coats 6.of primer on top of the shield. The primer should be applied between 3 and 5 days after second coat of epoxy shield.

7.




Packing size2 l or 10 l Comp. A (base) and 1 l or 5 l Comp. B (curing agent).Packing may vary from country to country according to local requirements.











Technical DataANTIFOULING ALUSEA TURBO

Product descriptionA/F Alusea Turbo is a self-polishing antifouling based on specially formulated organotin polymer as binder.

Recommended useAs an antifouling on aluminium vessels operating in global service at speeds above 20 knots.

Film thickness and spreading rateMinimum Maximum

Film thickness, dry (µm) 75 150Film thickness, wet (µm) 155 315Theoretical spreading rate (m²/l)

6,4 3,2

Physical propertiesColour Red, Blue, Black, GreenSolids (vol %)* 48 ± 2 Flash point 26ºC ± 2 (Setaflash)*Measured according to ISO 3233:1998 (E)

Surface preparationCoated surfacesPrior to paint application, all surfaces should be clean, dry and free from contamination. Remove surface contamination by high pressure fresh water cleaning. To be applied on a clean, dry approved primer/undercoat or intact self-polishing antifouling. Remove surface contamination by high pressure fresh water cleaning.



Application methodsSpray Use airless sprayBrush May be used but care must be taken to achieve the specified dry film thickness.Roller May be used however when using roller application care must be taken to apply


ANTIFOULING ALUSEA TURBO Page 1

Application data Thinner/Cleaner Jotun Thinner No. 7Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi).Nozzle tip 0.53 - 0.78 mm (0.021 - 0.031").Spray angle 65 - 80° Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 1 h 1 h 0,5 h 0,5 hThrough dry 1,5 h 1,5 h 1,5 h 1 hDry for launching

1 12-16 h 10-14 h 8-12 h 6-10 h

Dry to recoat, minimum 2 10 h 9 h 6 h 4 h

The interval indicates the time which normally occurs in a drydocking situation where the 1.drying time depends on the total film thickness of primer/antifouling applied. The drying time will increase with increasing film thickness.The surface should be dry and free from any contamination prior to application of the 2.subsequent coat.


Recommended type of primer:Penguard HB, Vinyguard Silvergrey 88





Technical DataANTIFOULING SEACONOMY

Product descriptionSeaconomy is a high build self-polishing antifouling based on specially formulated organotin polymer as binder. This binder dissolves slowly in seawater so that fresh antifouling is continuously exposed.

Recommended useAs an antifouling on vessels operating at medium speed with drydocking intervals up to 36 months. Also useful for upgrading long life vinyl and chlorinated rubber antifouling systems.



6,7 3,3

Physical propertiesColour RedSolids (vol %)* 50 ± 2 Flash point 26ºC ± 2 (Setaflash)*Measured according to ISO 3233:1998 (E)




ANTIFOULING SEACONOMY Page 1




Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 1 h 1 h 0,5 h 0,5 hThrough dry 1,5 h 1,5 h 1,5 h 1,0 hDry for launching

1 12-16 h 10-14 h 8-12 h 6-10 h




Recommended type of primer:Jotamastic 87 with tie coat, Vinyguard Black/Brown, Vinyguard Silvergrey 88, Safeguard, Safeguard Universal.



MSDSMATERIAL SAFETY DATA SHEET

Last changed: 12/03/02 Internal No.: 01 Replaces date: 03/02/00

ANTIFOULING SEAGUARDIAN 1. IDENTIFICATION OF SUBSTANCE AND COMPANY

Approved for use Approved for laboratory use

Approved by Jotun AS

TRADE NAME ANTIFOULING SEAGUARDIANAPPLICATION Antifouling paint FORMULA Xxxx

ART No. PM3051

Producer/importer JOTUN-HENRY CLARK LTD.Address Flixborough, ScunthorpePostal code North Lincolnshire DN15 8RRCountry UKTelephone Å44 1724 40 00 00Fax Å44 1724 40 01 00Contact pers. QA/Environm. dept., JOTUN A/S, NORWAYResponsible QA/Environm. dept., JOTUN A/S, NORWAYEmergency Telephones

Contact the National Poison Center

2. COMPOSITION/INFORMATION ON INGREDIENTS

No Ingredients name CAS No. Conc. (wt%) Classification1 DICOPPER OXIDE 1317-39-1 25-50 Xn, , ; ,22-362 XYLENE, mixed isomers 1330-20-7 10-25 Xn, , ; ,10-20/21-

383 ROSIN 8050-09-7 2,5-10 Xi, , ,434 AROMATIC HYDROCARBONS C9-C12 64742-95-6 2,5-10 Xn, ,N; ,10-37-65-

51/535 TRICHRESYL PHOSPHATE 1330-78-5 1-2,5 Xn, ,N; ,21/22-

51/53

Legend: TÅ=Very toxic, T=Toxic, C=Corrosive, Xn=Harmful, Xi=Irritant, E=Explosive, O=Oxidising, FÅ=Extremely flammable, F=Highly flammable, N=Dangerous for the environment

INGREDIENT COMMENTSSubstances presenting a health hazard within the meaning of the current issue of the CHIP Regulations or assigned occupational exposure limits.

3. HAZARDS IDENTIFICATION

Harmful

FLAMMABLE. HARMFUL BY INHALATION, IN CONTACT WITH SKIN AND IF SWALLOWED. MAY CAUSE SENSITIZATION BY SKIN CONTACT. For potential danger for the environment, see section 12.

4. FIRST AID MEASURES

: 1 / 6 :



ANTIFOULING SEAGUARDIAN GENERALIn all cases of doubt, or when symptoms persist, seek medical attention. Never give anything by mouth to an unconscious person.

INHALATIONKeep the patient warm in a quiet place with fresh air. If breathing has stopped, administer artificial respiration. If unconscious place in the recovery position. Seek medical advice.

SKIN CONTACTRemove contaminated clothing. Wash skin thoroughly with soap and water or use an appropriate skin cleaner. Do NOT use solvents or thinners.

EYE CONTACTRemove any contact lenses. Hold the eyelids apart. Irrigate copiously with clean, fresh water for at least 10 minutes. Seek medical advice if symptoms persist.

INGESTIONDO NOT INDUCE VOMITING. If accidentally swallowed obtain immediate medical attention. Keep at rest. Seek medical advice.

MEDICAL INFORMATION Risk of chemical pneumonia by aspiration. Keep attention: danger of lung damage. General health examination. Professional evaluation of the work station.

5. FIRE-FIGHTING MEASURES

EXTINGUISHING MEDIARecommended: alcohol resistant foam, CO2, powders, water spray. Not to be used: water jet.

FIRE AND EXPLOSION HAZARDSFire will produce dense black smoke containing hazardous products of combustion (see Section 10). Decomposition products may be a hazard to health.

PROTECTIVE EQUIPMENT FOR FIRE FIGHTERSThe personal protective equipment required is provided in section 8. Professional fire-fighters are required to use an air-fed system when dealing with major fires.

OTHER INFORMATIONCool closed containers exposed to fire with water. Do not allow run-off from fire fighting to enter drains or water courses.

6. ACCIDENTAL RELEASE MEASURES

OTHER INFORMATIONExclude sources of ignition and ventilate the area. Avoid breathing vapours. Refer to protective measures listed in sections 7 and 8. Place in container for disposal according to local regulations (see section 13). Contain and collect spillage with non-combustible absorbent materials, e.g. sand, earth, vermiculite and diatomaceous earth. Do not allow to enter drains or watercourses. Clean preferably with a detergent; avoid use of solvents. If the product enters drains or sewers, the local water company should be contacted immediately; in the case of contamination of streams, rivers or lakes, the Environmental Agency.

7. HANDLING AND STORAGE

HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Prevent the creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher than the occupational exposure limits. The product should not be used in vicinity of open flames or other sources of ignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Allways use earth (ground) wire when transferring from one container to another. Personnel should wear anti-static clothing and footwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparks and open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.

: 2 / 6 :



ANTIFOULING SEAGUARDIAN Smoking, eating and drinking are forbidden in the work area.For personal protective equipment see Section 8. Always keep in containers made of the same material as the supply container. Never use pressure to empty the container, it is not a pressure vessel. Electrical equipment should be protected to appropriate standards. The Manual Handling Operations Regulations may apply to the handling of containers of this product.

STORAGEStore in accordance with the regulations for flammable materials. Observe the label precautions. Store in a dry, cold and well ventilated place away from sources of heat, ignition and direct sunlight. Store separately from oxidising agents and strongly alkaline and strongly acidic materials. No smoking. Containers which are opened should be properly resealed and kept upright to prevent leakage.

8. EXPOSURE CONTROL/PERSONAL PROTECTION

Ingredients name CAS no. TLV value TLV yearDICOPPER OXIDE 1317-39-1 1,0 mg/m3;(Cu)XYLENE, mixed isomers 1330-20-7 441,0 mg/m3 ;SkAROMATIC HYDROCARBONS C9-C12 64742-95-6 125,0 mg/m3

EXPOSURE CONTROLProvide adequate ventilation. Where reasonably practicable this should be achieved by the use of local exhaust ventilation and good general extraction. Spray mist contains all substances of the product and must not be inhaled. OELs are taken from the current version of EH40 (by Health & Safety Executive, UK).

RESPIRATORY PROTECTIONWhen use of roller or brush, then charcoal filter is sufficient. Use respiratory protective mask with charcoal and dust filter (A2/P2) when spraying this product.

EYE PROTECTIONEye protection designed to protect against liquid splashes should be worn.

HAND PROTECTIONUse PVA/viton gloves. Barrier creams may help to protect exposed areas of the skin but are not substitutes for full physical protection. Never apply barrier cream to contaminated skin.

PROTECTIVE CLOTHINGWear anti-static clothing made of natural fibre or of heat resistant synthetic fibre.When spraying use suit covering the whole body.

9. PHYSICAL AND CHEMICAL PROPERTIES

Physical State: Liquid. Colour: Light red. Dark red. Odour: Organic solvent. Solubility: Organic solvent. Melting point/range: -

Density: 2,0 - 2,2

Expl. limit LEL-UEL%: 1.10 - 7 Solubility in water:Vapour pressure: Saturation conc.:Decomposition temp.: Rel. dens. sat. air (air=1):pH solution: Boiling point/range: 138 - 144ºC

Flash point: 35ºC pH concentrate: -

Molar weight: Viscosity: 120 - 160 cP

Ignition temp.: 500ºC Odour threshold value:Rel.vap.dens.(air=1): Rel. evap. velocity:Air reactive: Water reactive:

10. STABILITY AND REACTIVITY : 3 / 6 :



ANTIFOULING SEAGUARDIAN STABILITYStable under recommended storage and handling conditions (see section 7).

MATERIALS TO AVOIDKeep away from oxidising agents, strongly alkaline and strongly acidic materials to prevent the exothermic reactions.

HAZARDOUS DECOMPOSITION PRODUCTSIn a fire, hazardous decomposition products such as smoke, carbon monoxide, carbon dioxide and oxides of nitrogen may be produced.

11. TOXICOLOGICAL INFORMATION

GENERALThere are no toxicological data available on the product itself.

INHALATIONExposure to organic solvent vapours may result in adverse health effects such as irritation of the mucous membrane and the respiratory system and adverse effects on the renal and central nervous system. Symptoms and signs include headache; dizziness, fatigue, muscular weakness, drowsiness and in extreme cases, loss of consciousness. Inhalation of smoke (from a fire or from welding on dicopper oxide coated material) may give symptoms like influenza.

SKIN CONTACTRepeated or prolonged exposure may cause skin irritation and dermatitis, due to the product's defatting properties.May cause sensitization by skin contact.

EYE CONTACTSplashes in the eyes may cause irritation and reversible local damage.

INGESTIONAbsorbed by the gastric intestinal system. May cause liver and kidney damage. Accidental ingestion may cause vomiting and abdominal pains. Risk of chemical pneumonia. 12. ECOLOGICAL INFORMATION

DEGRADABILITYAromatic hydrocarbons C9-C12: Not easily degradable.

ACCUMULATIONAromatic hydrocarbons C9-C12: Potential to bioaccumulate.

ECOTOXICITYAromatic hydrocarbons C9-C12: LC50 (fish) = 1-10 mg/l.

OTHER INFORMATIONDo not discharge the product to sewer or drains.The product contains aromatic hydrocarbons C9-C12 labelled "Dangerous for the environment".

13. DISPOSAL CONSIDERATIONS

GENERAL REGULATIONS Wastes, including emptied containers, are controlled wastes and should be disposed of in accordance with regulations made under the Control of Pollution Act and the Environmental Protection Act. Do not allow into drains or water courses. Waste must be disposed of at approved landfill/waste storage or traement facility.

CATEGORY OF WASTE08 00 00 WASTES FROM THE MANUFACTURE, FORMULATION, SUPPLY AND USE (MFSU) OF COATINGS (PAINTS, VARNISHES AND VITREOUS ENAMELS), ADHESIVE, SEALANTS AND PRINTING INKS. 08 01 02 Waste paints and varnish free of halogenated solvents.

14. TRANSPORT INFORMATION

: 4 / 6 :



ANTIFOULING SEAGUARDIAN PROPER SHIPPING NAME PAINT Toll. reg. no:HAZCHEM (Y=black,y=white):

ADR�(Road)UN No. 1263 Dang. goodsClass 3,PG III Label 3 Haz. ID No. 30

Marge No.

RID (Railway)UN No. 1263 Dang. goodsClass 3, PG III Label 3 Haz. ID No. 30

IMDG(Sea)UN No. 1263 Dang. goodsClass 3 Label 3 Pkg Gr III EmS 3 - 05 MFAG Marine Pollutant P Sub Risk Page

IATA(Air)UN No. 1263 Dang. goodsClass 3 Sub RiskLabel Flamm. liq. Pkg Gr III

Transport only in accordance with ADR for road, RID for rail, IMDG for sea transport and IATA for airtransport. ADR / RID: Not restricted, ref. chapter 2.2.3.1.5 (applicable to receptacles of less than 450 litre capacity).

15. REGULATORY INFORMATION

Classif.:

Harmful

COMPOSITION DICOPPER OXIDE (25-50), XYLENE, mixed isomers (10-25), ROSIN (2,5-10)

R-PHRASESR10 Flammable. R20/21/22 - Harmful by inhalation, in contact with skin and if swallowed. R43 May cause sensitization by skin contact.

S-PHRASESS23 Do not breathe vapour/spray. S36/37 Wear suitable protective clothing and gloves. S38 In case of insufficient ventilation, wear suitable respiratory equipment.

REFERENCESThe product is labelled for supply in accordance with the current issue of CHIP Regulations, and latest version of the approved supply list.

16. OTHER INFORMATION

ISSUED: 10/11/00

VENDOR NOTES The information contained in this MSDS is based on the present state of knowledge and current national legislation. As the specific conditions of use of the product are outside the supplier's control, the user is responsible for ensuring : 5 / 6 :



ANTIFOULING SEAGUARDIAN that the requirements of relevant legislation are compiled with. The information in this MSDS provides guidance on health, safety and environmental aspects of the product and should not be construed as any guarantee of technical performance or suitability for particular applications. Further information and relevant advice can be found in: The Environmental Protection (Duty of Care) Regulations 1992 (SI 1992:2839). The Control of Substances Hazardous to Health Regulations 1988 (SI1988:1657). The Highly Flammable Liquids and liquefied Petroleum Gases Regulations 197 (SI 1972:917). The Manual Handling Operations Regulations 1992 (SI 1992:2793). Storage of Flammable Liquids in Containers, HS(G)51. Storage of Packaged Dangerous Substances, HS(G)71. The selection, use and maintenance of respiratory protective equipment: A practical guide HS(G)53.

: 6 / 6 :

Technical DataANTIFOULING SEAGUARDIAN

Product descriptionAntifouling SeaGuardian is a tin free selfpolishing antifouling based on a copolymer binder

Recommended useAs an antifouling on vessels operating in global service, with drydocking intervals up to 36 months.



10 5

Physical propertiesColour Light Red, Dark RedSolids (vol %)* 50 ± 2 Flash point 35ºC ± 2 (Setaflash)*Measured according to ISO 3233:1998 (E)






ANTIFOULING SEAGUARDIAN Page 1


Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 1 h 1 h 0,5 h 0,5 hThrough dry 6 h 5 h 4 h 3 hDry for launching

1 12-16 h 10-14 h 8-12 h 6-10 h




Recommended type of primer:1.coat: Jotamastic 87 Aluminium or Primastic Universal or Jotaguard 85. 2.coat: Safeguard Tar Free or Safeguard.



Packing size20 l.Packing may vary from country to country according to local requirements.


Technical DataANTIFOULING SEAMATE FB 30

Product descriptionSeamate FB 30 is a high build self-polishing antifouling based on specially formulated organotin polymer as binder. This binder dissolves slowly in seawater so that fresh antifouling is continuously exposed

Recommended useAs an antifouling for flatbottom areas on vessels operating at medium speed with drydocking intervals up to 60 months.



6,9 3,5

Physical propertiesColour Light Red/Dard RedSolids (vol %)* 52 ± 2 Flash point 26ºC ± 2 (Setaflash)*Measured according to ISO 3233:1998 (E)






ANTIFOULING SEAMATE FB 30 Page 1



1 12-24 h 10-22 h 8-20 h 6-18 h




Recommended type of primerJotamastic 87 with tie coat, Vinyguard Black/Brown, Vinyguard Silvergrey 88, Safeguard, Safeguard Universal.





Technical DataANTIFOULING SEAMATE HB 22

Product descriptionSeamate HB 22 is a high build self-polishing antifouling based on specially formulated organotin polymer as binder. This binder dissolves slowly in seawater so that fresh antifouling is continuously exposed.

Recommended useAs an antifouling on vessels operating at medium speed with drydocking intervals up to 36 months on sidebottom and up to 60 months on flatbottom. Also useful for upgrading long life vinyl and chlorinated rubber antifouling systems.



6,9 3,5







ANTIFOULING SEAMATE HB 22 Page 1



1 12-24 h 10-22 h 8-20 h 6-18 h




Recommended type of primer:Jotamastic 87 with tie coat, Vinyguard Black/Brown, Vinyguard Silvergrey 88, Safeguard, Safeguard Universal







Recommended useAs an antifouling on vessels operating at medium speed with drydocking intervals up to 60 months.



6,9 3,5










1 12-24 h 10-22 h 8-20 h 6-18 h











Recommended useAs an antifouling on ships/ferries with short distances in service and frequent calls in port, on laid-up ships/storage tankers and on stationary installations.



6,9 3,5










1 12-24 h 10-22 h 8-20 h 6-18 h




Recommended type of primer:Jotamastic 87 with tie coat, Vinyguard Black/Brown, Vinyguard Silvergrey 88, Safeguard, Safeguard Tar Free.





Technical DataANTIFOULING SEAMATE SB 33

Product descriptionSeamate SB 33 is a high build self-polishing antifouling based on specially formulated organotin polymer as binder. This binder dissolves slowly in seawater so that fresh antifouling is continuously exposed.

Recommended useAs an antifouling for side and flatbottom areas on vessels operating at medium speed with drydocking intervals up to 60 months.



6,9 3,5

Physical propertiesColour Light Red /Dark RedSolids (vol %)* 52 ± 2 Flash point 26ºC ± 2 (Setaflash)*Measured according to ISO 3233:1998 (E)






ANTIFOULING SEAMATE SB 33 Page 1



1 12-24 h 10-22 h 8-20 h 6-18 h









Technical DataANTIFOULING SEAPRINCE

Product descriptionAntifouling SeaPrince is a tin free self-polishing antifouling based on a copolymer binder.

Recommended useTo be used on vessels operating in global service, with drydocking intervals up to 30 months on sidebottom and 36 months on flatbottom.



6,7 3,3

Physical propertiesColour Dark Red, Light RedSolids (vol %)* 50 ± 2 Flash point 30ºC ± 2 (Setaflash)*Measured according to ISO 3233:1998 (E)






ANTIFOULING SEAPRINCE Page 1


Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 1 h 1 h 0.5 h 0,5 hThrough dry 1,5 h 1,5 h 1,5 h 1 hDry for launching

1 12-24 h 10-22 h 8-20 h 6-18 h


The interval indicates the time which normally occurs in a drydocking situation where the 1.drying time depends on the total film thickness of primer/antifouling applied. The drying time will increase with increasing film thickness.The substrate should be dry and free from any contamination prior to application of the 2.subsequent coat.


RECOMMENDED TYPE OF PRIMER:1) 1. coat: Jotamastic 87 or Primastic Universal or Jotaguard 85. 2. coat: Safeguard Universal or Safeguad.2) Jotamastic 87, with Vinyguard Silvergrey 88 as tie coat.3) Primastic Universal, with Vinyguard Silvergrey 88 as tie coat.





MATERIAL SAFETY DATA SHEETMSDS

Last changed: 20/09/2001 Internal no.: 01 Replaces date: 22/03/2000

ANTIFOULING SEAQUANTUM CLASSIC

1/7

1. PRODUCT AND COMPANY

Approved for use

Approved for laboratory use


TRADE NAME ANTIFOULING SEAQUANTUM CLASSICAPPLICATION Antifouling paint

ART-NO PM3126

Producer/Importer JOTUN-HENRY CLARK LTD.Address Flixborough, ScunthorpeZipcode & City North Lincolnshire DN15 8RRTelephone +44 1724 40 00 00Fax +44 1724 40 01 00Contactperson QA/Environm. dept., JOTUN A/S, NORWAYResponsible QA/Environm. dept., JOTUN A/S, NORWAYEmergency number Contact the National Poison Center

2. COMPOSITION OF PRODUCT

No Ingredients name CAS-NO Cons.(weight%) Classification

1 DICOPPER OXIDE 1317-39-1 25-50 N Xn,22-362 XYLENE, mixed isomers 1330-20-7 10-25 N Xn,10-20/21-383 AROMATIC HYDROCARBONS C9-C12 64742-95-6 2,5-10 N XnN,10-37-65-51/534 ROSIN 8050-09-7 1-2,5 N Xi,435 COPPER PYRITHIONE 14915-37-8 1-2,5 N T+N,22-26-41-50

Legend T+=Very toxic, T=Toxic, C=Corrosive, Xn=Harmful, Xi=Irritant, IK=No classification required, E=Explosive, O=Oxidising, F+=Extremely flammable, F=Very flammable, N=Dangerous for the environment, Muta=Mutagenic,Carc=Carcinogenic, Repr=Toxic for reproduction

INGREDIENT COMMENTSSubstances presenting a health hazard within the meaning of the current issue of the CHIP Regulations or assignedoccupational exposure limits.

3. HAZARD IDENTIFICATION

Harmful

FLAMMABLE. HARMFUL BY INHALATION, IN CONTACT WITH SKIN AND IF SWALLOWED.IRRITATING TO SKIN. MAY CAUSE SENSITISATION BY SKIN CONTACT.For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL




2/7

In all cases of doubt, or when symptoms persist, seek medical attention. Never give anything by mouth to anunconscious person.

INHALATIONKeep the patient warm in a quiet place with fresh air. If breathing has stopped, administer artificial respiration. Ifunconscious place in the recovery position. Seek medical advice.

SKIN CONTACTRemove contaminated clothing. Wash skin thoroughly with soap and water or use an appropriate skin cleaner. DoNOT use solvents or thinners.

EYE CONTACTRemove any contact lenses. Hold the eyelids apart. Irrigate copiously with clean, fresh water for at least 10 minutes.Seek medical advice if symptoms persist.

INGESTIONDO NOT INDUCE VOMITING. If accidentally swallowed obtain immediate medical attention. Keep at rest. Seekmedical advice.

MEDICAL INFORMATION Risk of chemical pneumonia by aspiration. Keep attention: danger of lung damage. General health examination.Professional evaluation of the work station. Persons with rash are directed to skin expert for examination of allergicdermatitis.

5. FIRE FIGHTING MEASURES

PROPER FIREFIGHTING EQUIPMENTRecommended: alcohol resistant foam, CO2, powders, water spray. Not to be used: water jet.

FIRE AND EXPLOSION HAZARDSFire will produce dense black smoke containing hazardous products of combustion (see Section 10). Decompositionproducts may be a hazard to health.

PERSONAL PROTECTION WHEN FIREFIGHTINGThe personal protective equipment required is provided in section 8. Professional fire-fighters are required to usean air-fed system when dealing with major fires.

OTHER INFORMATIONCool closed containers exposed to fire with water. Do not allow run-off from fire fighting to enter drains or watercourses.


OTHER INFORMATIONExclude sources of ignition and ventilate the area. Avoid breathing vapours. Refer to protective measures listed insections 7 and 8. Place in container for disposal according to local regulations (see section 13). Contain and collectspillage with non-combustible absorbent materials, e.g. sand, earth, vermiculite and diatomaceous earth. Do notallow to enter drains or watercourses. Clean preferably with a detergent; avoid use of solvents. If the product entersdrains or sewers, the local water company should be contacted immediately; in the case of contamination ofstreams, rivers or lakes, the Environmental Agency.


HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Always use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparks




3/7

and open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area.For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty thecontainer, it is not a pressure vessel. Electrical equipment should be protected to appropriate standards. The ManualHandling Operations Regulations may apply to the handling of containers of this product.

STORAGEStore in accordance with the regulations for flammable materials. Observe the label precautions. Store in a dry, coldand well ventilated place away from sources of heat, ignition and direct sunlight. Store separately from oxidisingagents and strongly alkaline and strongly acidic materials. No smoking. Containers which are opened should beproperly resealed and kept upright to prevent leakage.

8. EXPOSURE CONTROL AND PERSONAL PROTECTION

Ingredients name CAS-no OEL value (long-term) OEL value (short-term) OELXYLENE, mixed isomers 1330-20-7 441,0 mg/m3 ;Sk 662,0 mg/m3 ;Sk

AROMATIC HYDROCARBONS C9-C12 64742-95-6 125,0 mg/m3 -

COPPER PYRITHIONE 14915-37-8 0,35 mg/m3 0,45 mg/m3

EXPOSURE CONTROLThe OEL for copper pyrithione has been provided by the manufacturing supplier. Provide adequate ventilation.Where reasonably practicable this should be achieved by the use of local exhaust ventilation and good generalextraction. Spray mist contains all substances of the product and must not be inhaled. OEL's are taken from thecurrent version of EH40 (by Health & Safety Executive, UK). This product may produce hazardous dust duringgenerating working operations. Persons that carries out dust generating operations should wear self-containedbreathing apparatus and suitable preventive working clothes. Appropriate preventive measures should be carried outto prohibit exposure and by-passers.

RESP. PROTECTIONWhen use of roller or brush, then charcoal filter is sufficient. Gas mask with combined filter (dust filter P3/gas filterA2) may be sufficient when spraying. Otherwise wear a self-contained breathing apparatus.


HAND PROTECTIONUse PVA/viton gloves. Barrier creams may help to protect exposed areas of the skin but are not substitutes for fullphysical protection. Never apply barrier cream to contaminated skin.

SKIN PROTECTIONWear anti-static clothing made of natural fibre or of heat resistant synthetic fibre. When spraying use suit coveringthe whole body.




4/7


Form Liquid.Colour Various.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 1,86Expl. limit LEL-UEL., %-%: 1 - 7 Solubility in water

Vapor pressure Saturation conc.

Decomposition temp. Rel. density sat. air (air=1)

pH Solution Boiling point/range 138 - 177ºC

Flash point 25ºC pH concentrate -Molecular weight Viscosity

Ignition temp 500ºC Smelling limits lo-hi

Rel. vapor density (air=1) Rel. evap. velocity

Air reactive Water reactive

10. STABILITY AND REACTIVITY

STABILITYStable under recommended storage and handling conditions (see section 7).

MATERIALS TO AVOIDKeep away from oxidising agents, strongly alkaline and strongly acidic materials to prevent the exothermicreactions.

HAZARDOUS DECOMPOSITION PRODUCTSIn a fire, hazardous decomposition products such as smoke, carbon monoxide, carbon dioxide and oxides ofnitrogen may be produced.


GENERALThe product is classified harmful by inhalation based on tests for acute toxicity by inhalation for similar products.

INHALATIONExposure to organic solvent vapours may result in adverse health effects such as irritation of the mucous membraneand the respiratory system and adverse effects on the renal and central nervous system. Symptoms and signs includeheadache; dizziness, fatigue, muscular weakness, drowsiness and in extreme cases, loss of consciousness. Result oftest for acute toxicity by inhalation of dry paint: LC90=1,17 mg resp. part. /litre air.

SKIN CONTACTRepeated or prolonged contact with the product may lead to removal of natural fats from the skin resulting in non-allergic contact dermatitis and absorption through the skin. Repeated or prolonged contact with skin may causesensitisation.


INGESTIONAbsorbed by the gastric intestinal system. May cause liver and kidney damage. Accidental ingestion may causevomiting and abdominal pains. Risk of chemical pneumonia.

CANCER




5/7

The product contains ethylbenzene. IARC has classified it as a possible human carcinogen (Group 2B) based onsufficient evidence for carcinogenicity in experimental animals, but inadequate evidence for cancer in exposedhumans.

12. ECOLOGICAL INFORMATION

BREAKDOWNCopper pyrithione: Rapid degradation.

ACCUMULATIONAromatic hydrocarbons C9-C12: Potential to bioaccumulate.Copper pyrithione: Does not bioaccumulate.

ECOTOXITYAromatic hydrocarbons C9-C12: LC50 (fish) = 1-10 mg/l.Copper pyrithione:EC50 (fresh water algae) = 0.035 mg/l (120h).LC50 (fish) = 0.0043 mg/l (96h).LC50 (Daphnia) = 0,022 mg/l (48h).

OTHER INFORMATIONThe product should not be allowed to enter drains or water courses or be deposited where it can affect ground orsurface waters. The product contains aromatic hydrocarbons C9-C12 labelled "Dangerous for the environment".The product contains copper pyrithione labelled "Dangerous for the environment".

13. DISPOSAL

Wastes, including emptied containers, are controlled wastes and should be disposed of in accordance withregulations made under the Control of Pollution Act and the Environmental Protection Act. Do not allow into drainsor water courses. Waste must be disposed of at approved landfill/waste storage or treatment facility.

WASTEGROUP08 00 00 WASTES FROM THE MANUFACTURE, FORMULATION, SUPPLY AND USE (MFSU) OFCOATINGS (PAINTS, VARNISHES AND VITREOUS ENAMELS), ADHESIVE, SEALANTS ANDPRINTING INKS. 08 01 02 Waste paints and varnish free of halogenated solvents.




6/7


PROPER SHIPPING NAME PAINTToll. reg. no.

HAZCHEM

ADR (Road)

UN No. 1263 Dang. goods

Class 3, PG III Label 3Haz. id. no 30 Marginno.

RID (Railway)


Class 3, PG III Label 3Haz..id.no 30

IMDG (Sea)


Class 3 Label 3Packaging group III EmS 3-05MFAG Marine Pollutant P

Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk

Label Flamm. liq. Packaging group III

GENERALTransport only in accordance with ADR for road, RID for rail, IMDG for sea transport and IATA for airtransport.


Classification

Harmful

COMPOSITION DICOPPER OXIDE (25-50), XYLENE, mixed isomers (10-25), ROSIN (1-2,5), COPPER PYRITHIONE (1-2,5)

R-PHRASESR10 Flammable. R20/21/22 - Harmful by inhalation, in contact with skin and if swallowed. R38 Irritating to skin.R43 May cause sensitisation by skin contact.

S-PHRASESS23 Do not breathe vapour/spray. S36/37 Wear suitable protective clothing and gloves. S38 In case of insufficientventilation, wear suitable respiratory equipment.

REFERENCESThe product is labelled for supply in accordance with the current issue of CHIP Regulations, and latest version ofthe approved supply list.




7/7


PRINTEDOUT:

20/09/2001

VENDOR NOTESThe use of the preparation is restricted to professional users. The information contained in this MSDS is based onthe present state of knowledge and current national legislation. As the specific conditions of use of the product areoutside the supplier's control, the user is responsible for ensuring that the requirements of relevant legislation arecompiled with. The information in this MSDS provides guidance on health, safety and environmental aspects ofthe product and should not be construed as any guarantee of technical performance or suitability for particularapplications. The Environmental Protection (Duty of Care) Regulations 1992 (SI 1992:2839). Further informationand relevant advice can be found in: The Control of Substances Hazardous to Health Regulations 1988(SI1988:1657). The Highly Flammable Liquids and liquefied Petroleum Gases Regulations 197 (SI 1972:917). TheManual Handling Operations Regulations 1992 (SI 1992:2793). Storage of Flammable Liquids in Containers,HS(G)51. Storage of Packaged Dangerous Substances, HS(G)71. The selection, use and maintenance of respiratoryprotective equipment: A practical guide HS(G)53.

Technical DataANTIFOULING SEAQUANTUM CLASSIC

Product descriptionAntifouling SeaQuantum Classic is a tin-free high performance self-polishing antifouling, based on a hydrolysing organosilyl polymer as binder. This binder dissolves in seawater at a rate permitting the continuous exposure of fresh antifouling.

Recommended useAs an antifouling for newbuildings and major refurbishment, for side and flatbottom areas on vessels operating at medium speed with drydocking intervals up to 60 months.



7 3,5

Physical propertiesColour Light Red /Dark RedSolids (vol %)* 52 ± 2 Flash point 26ºC ± 2 (Setaflash)*Measured according to ISO 3233:1998 (E)

Surface preparationCoated surfacesTo be applied on a clean, dry approved primer/undercoat or intact self-polishing antifouling in accordance with Jotun's requirements. Remove surface contamination by high pressure fresh water cleaning.





ANTIFOULING SEAQUANTUM CLASSIC Page 1


Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 60 min 45 min 30 min 15 minThrough dry 8 h 6 h 4 h 3 hDry for launching

1 12-24 h 10-22 h 8-20 h 8-16 h


Indicate the time which normally occurs in a drydocking situation where the drying time 1.depends on the total film thickness of primer/antifouling applied. The drying time will increase with increasing film thickness.The surface should be dry and free from any contamination prior to application of the 2.subsequent coat.


Recommended type of primer:1) 1. coat: Jotamastic 87 or Primastic Universal or Jotaguard. 2.coat: Safeguard Universal or Safeguard.

2) Jotamastic 87, with Vinyguard Silvergrey 88 as tie coat.

3) Primastic Universal, with Vinyguard Silvergrey 88 as tie coat.

4) Vinyguard Black/Brown/Black.




Technical DataANTIFOULING SEAQUANTUM FB

Product descriptionAntifouling SeaQuantum FB is a tin-free high performance self-polishing antifouling , based on hydrolysing organosilyl polymer as binder. This binder dissolves in seawater at a rate permitting the continuous exposure of fresh antifouling.

Recommended useAs an antifouling for newbuildings and major refurbishment, for flatbottom areas on vessels operating at medium speed with drydocking intervals up to 60 months.



7 3,5

Physical propertiesColour Light Red /Dark RedSolids (vol %)* 52 ± 2 Flash point 26±2 (Setaflash)*Measured according to ISO 3233:1998 (E)






ANTIFOULING SEAQUANTUM FB Page 1



1 12-24 h 10-22 h 8-20 h 8-16 h


1 Indicate the time which normally occurs in a drydocking situation where the drying time depends on the total film thickness of primer/antifouling applied. The drying time will increase with increasing film thickness.

2 The surface should be dry and free from any contamination prior to application of the subsequent coat.


Recommended type of primer:1) 1. coat: Jotamastic 87 or Primastic Universal or Jotaguard 85. 2. coat: Safeguard Universal or Safeguard. 2) Jotamastic 87, with Vinyguard Silvergrey 88 as tie coat.

3) Primastic Universal, with Vinyguard Silvergrey 88 as tie coat.







ANTIFOULING SEAQUANTUM PLUS

1/7


Approved for use



TRADE NAME ANTIFOULING SEAQUANTUM PLUSAPPLICATION Antifouling paint

ART-NO PM3127




1 DICOPPER OXIDE 1317-39-1 25-50 N Xn,22-362 XYLENE, mixed isomers 1330-20-7 10-25 N Xn,10-20/21-383 AROMATIC HYDROCARBONS C9-C12 64742-95-6 1-2,5 N XnN,10-37-65-51/534 ROSIN 8050-09-7 1-2,5 N Xi,435 COPPER PYRITHIONE 14915-37-8 1-2,5 N T+N,22-26-41-50


INGREDIENT COMMENTSThe product is not classified as dangerous by aspiration according to viscosity criterias in the guidelines.Substances presenting a health hazard within the meaning of the current issue of the CHIP Regulations or assignedoccupational exposure limits.


Harmful





2/7

4. FIRST AID

GENERALIn all cases of doubt, or when symptoms persist, seek medical attention. Never give anything by mouth to anunconscious person.









PERSONAL PROTECTION WHEN FIREFIGHTINGThe personal protective equipment required is provided in section 8. Professional fire-fighters are required to use anair-fed system when dealing with major fires.





HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources of




3/7

ignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Always use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area. For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty thecontainer, it is not a pressure vessel. Electrical equipment should be protected to appropriate standards. The ManualHandling Operations Regulations may apply to the handling of containers of this product.







RESP. PROTECTIONWhen use of roller or brush, then charcoal filter is sufficient. Gas mask with combined filter (dust filter P3/gas filterA2) may be sufficient when spraying. Otherwise wear a self-contained breathing apparatus.







4/7




















CANCER




5/7







13. DISPOSAL






6/7



HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk




Classification

Harmful

COMPOSITION DICOPPER OXIDE (25-50), XYLENE, mixed isomers (10-25), ROSIN (1-2,5), COPPER PYRITHIONE (1-2,5)








7/7

PRINTEDOUT:

20/09/2001


Technical DataANTIFOULING SEAQUANTUM PLUS

Product descriptionAntifouling SeaQuantum Plus is a tin-free high performance self-polishing antifouling, based on a hydrolysing organosilyl polymer as binder. This binder dissolves in seawater at a rate permitting the continuous exposure of fresh antifouling.

Recommended useAs an antifouling for newbuildings and major refurbishment, for side and flatbottom areas on vessels operating at medium/high speed with drydocking intervals up to 60 months.



7 3,5







ANTIFOULING SEAQUANTUM PLUS Page 1



1 12-24 h 10-22 h 8-20 h 8-16 h





Recommended type of primer:1) 1 coat: Jotamastic 87 or Primastic Universal or Jotaguard 85. 2 coat: Safeguard Universal or Safeguard.

2) Jotamastic 87, with Vinyguard Silvergrey as tie coat.

3) Primastic Universal, with Vinyguard Silvergrey as tie coat.





Technical DataANTIFOULING SEAQUANTUM ULTRA

Product descriptionAntifouling SeaQuantum Ultra is a tin-free high performance self-polishing antifouling, based on a hydrolysing organosilyl polymer as binder. This binder dissolves in seawater at a rate permitting the continuous exposure of fresh antifouling.

Recommended useAs an antifouling on ships/ferries with short distance in service and frequent calls in port, on laid-up ships/storage tankers and on stationary installations.



7 3,5







ANTIFOULING SEAQUANTUM ULTRA Page 1



1 12-24 h 10-22 h 8-20 h 8-16 h





Recommended type of primer: 1) 1. coat: Jotamastic 87 or Primastic Universal or Jotaguard 85. 2.coat: Safeguard Universal or Safeguard.

2) Jotamastic 87, with Vinyguard Silvergrey 88 as tie coat. 3) Primastic Universal, with Vinyguard Silvergrey 88 as tie coat.







ANTIFOULING SEAQUEEN

1/7


Approved for use



TRADE NAME ANTIFOULING SEAQUEENAPPLICATION Antifouling paint

ART-NO PM3124




1 DICOPPER OXIDE 1317-39-1 25-50 N Xn,22-362 XYLENE, mixed isomers 1330-20-7 10-25 N Xn,10-20/21-383 AROMATIC HYDROCARBONS C9-C12 64742-95-6 2,5-10 N XnN,10-37-65-51/534 ROSIN 8050-09-7 2,5-10 N Xi,435 COPPER PYRITHIONE 14915-37-8 1-2,5 N T+N,22-26-41-50




Harmful


4. FIRST AID

GENERAL




2/7



















3/7








RESP. PROTECTIONWhen use of roller or brush, then charcoal filter is sufficient. Gas mask with combined filter (dust filter P3/gasfilter A2) may be sufficient when spraying. Otherwise wear a self-contained breathing apparatus.







4/7




















CANCER




5/7







13. DISPOSAL






6/7



HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk




Classification

Harmful

COMPOSITION DICOPPER OXIDE (25-50), XYLENE, mixed isomers (10-25), ROSIN (2,5-10), COPPER PYRITHIONE (1-2,5)







7/7


PRINTEDOUT:

07/08/2001


Technical DataANTIFOULING SEAQUEEN

Product descriptionAntifouling SeaQueen is a tin free self-polishing antifouling based on a copolymer binder.

Recommended useTo be used on vessels operating in global service with drydocking intervals up to 36 months on the side and flatbottom. For vessels trading at higher speeds and high operation levels, it can be used for up to 60 months on the flatbottom.



6,7 3,3

Physical propertiesColour Dark Red, Light RedSolids (vol %)* 50 ± 2 Flash point 30ºC ± 2 (Setaflash)*Measured according to ISO 3233:1998 (E)






ANTIFOULING SEAQUEEN Page 1



1 12-24 h 10-22 h 8-20 h 6-18 h


1 The interval indicates the time which normally occurs in a drydocking situation where the drying time depends on the total film thickness of primer/antifouling applied. The drying time will increase with increasing film thickness.

2 The substrate should be dry and free from any contamination prior to application of the subsequent coat.


Recommended type of primer:Recommended type of primer:1) 1. coat: Jotamatic 87 or Primastic Universal or Jotaguard 85. 2. coat: Safeguard Universal or Safeguard.

2) Jotamastic 87, with Vinyguard Silvergrey 88 as tie coat.3) Primastic Universal, with Vinyguard Silvergrey 88 as tie coat.





Technical DataANTIFOULING SUPER TROPIC

Product descriptionA/F Super Tropic is a tin free conventional antifouling.

Recommended useOn vessels operating in global service.



11 7,3

Physical propertiesColour RedSolids (vol %)* 55 ± 2 Flash point 36ºC ± 2 (Setaflash)*Measured according to ISO 3233:1998 (E)

Surface preparationCoated surfacesPrior to paint application, all surfaces should be clean, dry and free from contamination. Remove surface contamination by high pressure fresh water cleaning. To be applied on a clean, dry approved primer/undercoat. Remove surface contamination by high pressure fresh water cleaning.





ANTIFOULING SUPER TROPIC Page 1

Application data Thinner/Cleaner Jotun Thinner No. 2Guiding data airless sprayPressure at nozzle 15 MPa min (150 kp/cm², 2100 psi.).Nozzle tip 0.53 - 0.78 mm (0.021 - 0.031").Spray angle 65 - 80° Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 1,5 h 1 h 0,5 h 0,5 hThrough dry 24 h 20 h 16 h 12 hDry for launching

1 12-24 h 10-22 h 8-20 h 6-18 h


1 The interval indicates the time which normally occurs in a drydocking situation where the drying time depends on the total film thickness of primer/antifouling applied. The drying time will increase with increasing film thickness.



Recommended type of primer:Vinyguard Silvergrey 88, Safeguard.





Technical DataBALLASTIC BLACK

Product descriptionBallastic Black is a bituminous based, high build coating which gives a soft and flexible film. This product is part of a complete system which is certified not to spread surface flames.

Recommended useSteel behind insulation, cofferdams, watertanks (non-potable). Concrete and similar materials as damp-proof coating.



4,2 2,1 4,2

Physical propertiesColour BlackSolids (vol %)* 63 ± 2 Flash point 38ºC ± 2 (Setaflash)Gloss FlatWater resistance GoodFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation






BALLASTIC BLACK Page 1


Application methodsSpray Use airless sprayBrush Recommended for stripe coating and small areas, care must be taken to achieve



Application data Mixing ratio (volume) Single pack.Thinner/Cleaner Jotun Thinner No. 2Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi.).Nozzle tip 0.53 - 0.79 mm (0.021 - 0.031").Spray angle 40 - 80ºFilter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 7 h 7 h 2 h 1 hDry to recoat, minimum 96 h 36 h 24 h 13 h


Typical paint systemBallastic Black Stripe coat

Dry exposure (behind insulation):Ballastic Black 1 x 150 µm (Dry Film Thickness)

Wet exposure (watertanks):Ballastic Black 2 x 150 µm (Dry Film Thickness)Other systems may be specified, depending on area of use


Technical DataBALLASTIC GREY

Product descriptionBallastic Grey is a high build modified acrylic coating.

Recommended useBallastic Grey is intended for use on steel behind insulation and lining in cofferdams and areas with condensation. Overcoat only with itself.



5,2 2,6 3,5

Physical propertiesColour Light grey (Aluminium sheen)Solids (vol %)* 52 ± 2 Flash point 45ºC ± 2 (Setaflash)Gloss FlatWater resistance GoodFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparationThe coating may be used on other substrates. Please contact your local Jotun office for more information.

Condition during applicationThe temperature of the substrate should be min. 3°C above the dew point of the air in the vicinity of the substrate.

Application methods

Mixing ratio (volume) Single pack.Thinner/Cleaner Jotun Thinner No. 2Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi.).Nozzle tip 0.53 - 0.79 mm (0.021 - 0.031").Spray angle 40 - 80ºFilter Check to ensure that filters are clean.

BALLASTIC GREY Page 1


Substrate temperature 5°C 10°C 23°C 40°CSurface dry 4 h 3 h 2 h 1 hThrough dry 26 h 22 h 14 h 5 hDry to recoat, minimum

1 48 h 36 h 20 h 16 h

1 In case of multi-coat application, drying times will be influenced by the number in sequence and by the total thickness of previous coat applied - reference is made to the corresponding system datasheet.


Typical paint systemBallastic GreyBallastic Grey

stripe coat1 x 150-200 µm








Technical DataBALLOXY HB LIGHT

Product descriptionBalloxy HB Light is a two pack modified epoxy coating.

Recommended useBalloxy HB Light is intended for use in water ballast tanks, on steel behind insulation, in cofferdams and areas with condensation and where blast cleaning may not be possible.



5,5 2,7 4,1

Physical propertiesColour Beige /GreenSolids (vol %)* 82 ± 2 Flash point 35ºC ± 2 (Setaflash)Gloss SemiglossWater resistance ExcellentAbrasion resistance Very goodSolvent resistance Good Chemical resistance Good Flexibility Good


Surface preparation


Bare steelCleanliness: Power tool cleaning to min. St 2, mill scale free (ISO 8501-1:1988). Improved surface treatment (blast cleaning to Sa 2½) will improve the performance.


Coated surfacesClean, dry and undamaged compatible primer. Contact your local Jotun office for more information. For maintenance UHPWJ to WJ2 (NACE No.5/SSPC-SP 12) or Power tool cleaning to min. St 2 for rusted areas


BALLOXY HB LIGHT Page 1

Condition during applicationThe temperature of the substrate should be minimum 10°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is required in confined areas to ensure proper drying. The coating should not be exposed to oil, chemicals or mechanical stress until cured.


the specified dry film thickness.Roller May be used for small areas but not recommended for first primer coat, however

when using roller application care must be taken to apply sufficient material in order to achieve the specified dry film thickness.

Application data Mixing ratio (volume) 5 parts Comp. A (Base) to be thoroughly mixed with 1 part Comp. B

(Curing agent).Induction time 10 minutes.Pot life (23°C) 2 hours (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi.).Nozzle tip 0.53 - 0.79 mm (0.021 - 0.031").Spray angle 40 - 80° Filter Check to ensure that filters are cleanNote The temperature of the mixture of base and curing agent is

recommended to be at least 15°C, otherwise solvent may be required to obtain correct viscosity.Too much solvent results in lower sag resistance and slower cure.Thinner should be added after mixing components.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 10°C 23°C 40°CSurface dry 8 h 4 h 2 hThrough dry 24 h 10 h 4 hCured 14 d 7 d 2 d

Dry to recoat, minimum 1 24 h 10 h 4 h

Dry to recoat, maximum 1

1 Provided the surface is free from chalking and other contamination prior to application, there is normally no overcoating time limit. Best intercoat adhesion occurs, however, when the subsequent coat is applied before preceding coat has cured. If the coating has been exposed to direct sunlight for some time, special attention must be paid to surface cleaning and mattening/removal of the surface layer in order to obtain good adhesion.



Typical paint systemBalloxy HB Light 2 x 200 µm (Dry Film Thickness)Other systems may be specified, depending on area of use



Packing size15 l Comp. A, 3 l Comp. B.Packing may vary from country to country according to local requirements.











Technical DataBALLOXY NB LIGHT

Product descriptionBalloxy NB Light is a two pack modified epoxy coating.

Recommended useBalloxy NB Light is inteded on newbuildings for use in water ballast tanks, on steel behind insulation, in cofferdams and areas shopprimed and blasted/grinded as secondary surface preparation.



6,2 3,9 5,2

Physical propertiesColour Beige/GreenSolids (vol %)* 78 ± 2 Flash point 35ºC ± 2 (Setaflash)Gloss SemiglossWater resistance ExcellentAbrasion resistance Very goodSolvent resistance Good Chemical resistance Good


Surface preparation






BALLOXY NB LIGHT Page 1






(Curing agent).Induction time 10 minutes.Pot life (23°C) 2 hours (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100psi.)Nozzle tip 0.53 - 0.79 mm (0.021 - 0.031).Spray angle 40 - 80ºFilter Check to ensure that filters are clean.Note The temperature of the mixture of base and curing agent is

recommended to be at least 15ºC, otherwise solvent may be required to obtain correct viscosity.Too much solvent results in lower sag resistance and slower cure.Thinner should be added after mixing components.







Typical paint systemBalloxy NB Light 2 x 150 µm (Dry Film Thickness)Other systems may be specified, depending on area of use



Packing size15 l Comp. A, 3 l Comp. BPacking may vary from country to country according to local requirements.











Technical DataBALTOFLAKE

Product descriptionBaltoflake is a quick curing, glass flake reinforced polyester coating, high build, that gives long time corrosion protection.

Recommended useSteel structures in general and in particular items subject to extreme mechanical wear. May also be used for protection of aluminium and concrete (special designed systems).



1,6 0,64 1,28

Physical propertiesColour Limited numberSolids (vol %)* 96 ± 2 Flash point 34ºC ± 2 (Setaflash)Gloss SemiflatGloss retention Very goodWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Very good Chemical resistance Very good Flexibility LimitedCompatibility withcathodic protection Very good


Surface preparation


Bare steelBlast cleaning to Sa 2½. (ISO 8501-1:1988). Roughness: using abrasives suitable to achieve a coarse surface of Grade Medium G (50-85µm, Ry5) (ISO 8503-2).

Coated surfacesApproved on top of Baltoflake Holding Primer


BALTOFLAKE Page 1

Condition during applicationThe temperature of the substrate should be minimum 10°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to ensure proper drying. The coating should not be exposed to oil, chemicals or mechanical stress until fully cured.

Application methodsSpray Use normal airless spray or two-comp. airless spray equipmentBrush Recommended for stripe coating and small areas, care must be taken to achieve



Application data Mixing ratio (volume) See separate table.Pot life (23°C) 45 - 55 minutes (Reduced at higher temp.) Thinner If neded max. 5% styrene. Cleaner Acetone or Thinner No. 17 - Guiding data airless sprayPressure at nozzle 15 - 25 MPa (150-250 kp/cm², 2100-4000 psi.). Ratio/Capacity: >45:1, min. 12 l per minute. Slow moving piston.Nozzle tip 0.69 - 1.09 mm (0.027 - 0.043'').Spray angle 40 - 80°Filter To be removedNote For further details please see separate "Working Manual".

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 10°C 23°C 40°CSurface dry 3 h 2 h 2 hThrough dry 5 h 2 h 2 hCured 96 h 48 h 24 h

Dry to recoat, minimum 5 h 2 h 2 h

Dry to recoat, maximum 1 20 h 12 h 12 h

1 The surface should be dry and free from any contamination prior to application. If the maximum dry to recoat time is exceeded, please contact Jotun Paints for advice.


BALTOFLAKE Page 2

Typical paint systemOver Sa 2½:BaltoflakeorBaltoflakeBaltoflake Non Skid

1 x 750-1000 µm

1 x 600-750 µm1 x 400 - 600 µm

(Dry Film Thickness)



Choose curing agent and, if necessary, inhibitor or accelerator according to the table below. Inhibitor or accelerator (if used) must be thoroughly mixed with Baltoflake before adding the required amount of Norpol peroxide. Mechanical agitation for one minute or more.Temperature Addition Notes10-15ºC Norpol accelerator 9802P/S:

2 vol% (320ml to 16l)Norpol peroxide No 1:2 vol% (320ml to 16l)

15-20ºC Norpol peroxide No 1:2 vol% (320ml to 16l)

Temperature applies to the temperature of the steel. Paint temperature: 15-20ºC.

20-25ºC Norpol peroxide No 1:1.25 vol% (200ml to 16l)

Temperature of steel and paint.

25-35ºC Norpol inhibitor 9851:1.25 vol% (200ml to 16l)Norpol peroxide No 1:1.25 vol% (200ml to 16l)

35-40ºC Norpol inhibitor 9851:2,5 vol % (400ml to 16l)Norpol peroxide No 1:1.25 vol% (200ml to 16l)

Temperature applies to the temperature of the paint. Steel temperature above 25ºC.

__________________________________________________________________________

StorageThe product must be stored below 25°C and in accordance with national regulations. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed. SHELF LIFE: 6 months, at 23°C (2 months at 40°C), subject to re-inspection therafter. Shelf life very much depends on tempeature. Lower temperatures (if possible below freezing point) will lengthen the shelf life considerably, while high temperature may lead to gelling in the thin.

HandlingHandle Norpol Peroxide with care. Avoid that it comes in contact with combustible materiales. Accelerator and peroxide must never be mixed directly together.

Packing size16 l (20 kg)Packing may vary from country to country according to local requirements.

BALTOFLAKE Page 3










BALTOFLAKE Page 4

Technical DataBALTOFLAKE ECOLIFE

Product descriptionBaltoflake Ecolife is a styrene free glass flake reinforced polyester coating, high build, that gives long time corrosion protection.




1,63 0,65 0,98

Physical propertiesColour Limited numberSolids (vol %)* 98 ± 1 Flash point 53ºC ± 2 (Setaflash)Gloss SemiflatGloss retention GoodWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Very good Chemical resistance Very good Flexibility LimitedCompatibility withcathodic protection Very good


Surface preparation





BALTOFLAKE ECOLIFE Page 1


Application methodsSpray Preferably 2-comp. airless spray. Application with 1-comp. ordinary airless spray is

also possible, provided that inhibitor is added.Brush Recommended for stripe coating and small areas, care must be taken to achieve

the specified dry film thickness.

Application data Mixing ratio (volume) 2-comp. airless spray:

1,25 vol.% NORPOL peroxide no. 13 at temperatures 10-35° C.2,5% vol.% NORPOL peroxide no. 13 at temperatures 5-10° C.1-comp. ordinary airless spray :Addition of inhibitor and catalyst according to table on page 3.NORPOL peroxide no. 1 can be used instead of no. 13 at temperatures obove 15º C.

Pot life (23°C) 15-20 minutes (Reduced at higher temperatures). After addition of inhibitor for 1-comp. ordinary airless spray: 35 minutes.

Thinner/Cleaner If needed max 5% vinyltoluene. For cleaning: Acetone or Jotun Thinner No 17.

Guiding data airless sprayPressure at nozzle 15 - 25 MPa (150-250 kp/cm², 2100-4000 psi.) Ratio/Capacity: >45:1, min. 12 l per minute. Slow moving piston.Nozzle tip 0,69 - 1.09 mm (0.027 - 0.043'').Spray angle 40-80°, best 60°.Filter To be removed.Note For further details please see separate "Working Manual".

Approved alternatives to Norpol peroxide no 13. can be used. Contact Jotun Paints, Technical Service Department.



Using 2-comp. airless spraySubstrate temperature 5°C 10°C 23°C 40°CSurface dry 2.5 h 2.5 h 0.75 h 0.75 hThrough dry 2.5 h 2.5 h 0.75 h 0.75 hCured 3 d 2 d 1/2 d 1/6 d

Dry to recoat, minimum 2.5 h 2.5 h 0.75 h 0.75 h

Dry to recoat, maximum 1 14 d 14 d 14 d 14 d

Using 1-copm. airless spraySubstrate temperature 10°C 23°C 40°CSurface dry 3 h 2 h 2 hThrough dry 3 h 2 h 2 hCured 3 d 2 d 1 d



1 The surface should be free from chalking and contamination prior to application. If the maximum dry to recoat time is exceeded, please contact Jotun Paints for advice.


Typical paint systemOver Sa 2½:Baltoflake EcolifeorBaltoflake Ecolife

1 x 900-1100 µm

2 x 600-750 µm


(Dry Film Thickness)Other systems may be specified, depending on area of use

MIXING RATIO BY USE OF 1-COMPONENT AIRLESS SPRAY

Temperature of steel and paint should not be lower than 10ºC.

Addition of Norpol Inhibitor No. 9851 Addition of Norpol Peroxide No. 13Steel and paint temp. ºC Volume percent ml. into 16 litres

of Baltoflake Ecolife

Volume percent ml. into 16 litres of Baltoflake

Ecolife10 - 1515 - 2020 - 2525 - 3030 - 35

0.61.251.82.53.1

96200290400500

1.251.251.251.251.25

200200200200200


The temperature of the paint should never be more than 5ºC higher than the steel temperature. The inhibitor should be mixed thoroughly with Baltoflake Ecolife before adding the required amount of Norpol Peroxide No. 13. Mechanical agitation for one minute or more is necessary to secure proper mixing of the catalyst with the main component.

Note: Check temperature of pump during application. Friction in piston may cause increase in temperature. If this should happen, keep pump going to get heated Baltoflake Ecolife out as quickly as possible, and then wash the equipment.

StorageThe product must be stored below 25°C and in accordance with national regulations. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed. SHELF LIFE: 6 months, at 23°C (2 months at 40°C), subject to re-inspection therafter. Shelf life very much depends on tempeature. Lower temperatures (if possible below freezing point) will lengthen the shelf life considerably, while high temperature may lead to gelling in the thin.













Technical DataBALTOFLAKE HOLDING PRIMER

Product descriptionBaltoflake Holding Primer is a two-pack epoxy-based quick-drying primer. Particulary suitable under Baltoflake serie.

Recommended useFor temporary protection of blast-cleaned steel.



16,7 8,3 12,5

Physical propertiesColour YellowSolids (vol %)* 25 ± 2 Flash point -5ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance Very goodSolvent resistance Good Flexibility Good


Surface preparation


Bare steelCleanliness: Blast cleaning to Sa 2½ (ISO 8501-1:1988).Roughness: using abrasives suitable to achieve grade Fine to Medium G (30-85 µm, Ry5) (ISO 8503-2)


BALTOFLAKE HOLDING PRIMER Page 1




Application data Mixing ratio (volume) 17 parts of Comp. A (base) thoroughly mixed with 0,5 parts Comp.

B (curing agent).Induction time 10 minutes.Pot life (23°C) 24 - 36 hours (Reduced at higher temp.). Thinner/Cleaner Jotun Thinner No. 3/17

(No. 3 - Fast evaporation) - (No. 17 - Slow evaporation).Guiding data airless sprayPressure at nozzle 10-15 MPa (100 kp/cm² 1500 psi).Nozzle tip 0.38-0.53 mm (0.015-0.021").Spray angle 40-95°Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 10°C 23°C 40°CSurface dry 10 min 3 min 1 minThrough dry 15 min 4 min 2 minCured 14 d 7 d 3 d

Dry to recoat, minimum 1,2 2 d 1 d 1/2 d

Dry to recoat, maximum 1,2

1 Recommended data given for recoating with Baltoflake products.2 The surface should be free from any contamination prior to application of the subsequent coat



Typical paint systemBaltoflake Holding Primer 1 x 20 µm (Dry Film Thickness)

Normally overcoated with one of the products in the Baltoflake serieOther systems may be specified, depending on area of use



Packing size17 l Comp. A and 0,5 l Comp. B.Packing may vary from country to country according to local requirements.











Technical DataBALTOFLAKE MULTI

Product descriptionBaltoflake Multi is a glass flake reinforced polyester coating with a wide film thickness range that gives long term corrosion protection. It can be applied both with ratio 1:1 two-component airless spray and ordinary one-component airless equipment.




3,2 1,6 2

CommentsSolid volume rate may decrease at lower film thicknesses.

Physical propertiesColour Limited range of coloursSolids (vol %)* 95 ± 1 Flash point 34ºC ± 2 (Setaflash)Gloss SemiflatGloss retention GoodWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Very good Chemical resistance Very good Flexibility LimitedCompatibility withcathodic protection Very good


BALTOFLAKE MULTI Page 1

Surface preparation





Condition during applicationThe temperature of the substrate should be minimum 5°C (10º when using 1-comp. spray) and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to ensure proper drying. The coating should not be exposed to oil, chemicals or mechanical stress until fully cured.

Application methodsSpray Preferably 1:1 two-comp. airless spray. Other types of two-component equipment

can be used. Application with 1-comp. ordinary airless spray is also possible. Brush Recommended for stripe coating and small areas, care must be taken to achieve


Application data Mixing ratio (volume) 1:1 two-component airless spray:

Norpol accelerator 9802P/S (1% Co) is added to one paint container and Norpol MEK peroxide No. 1 to the other. 1-component airless spray: Both Norpol accelerator 9802P/S (1% Co) and Norpol MEK peroxide No. 1 is added to the same container.For correct addition, see tables below. Warning:Accelerator and peroxide must never be mixed directly together.

Pot life (23°C) 10-55 minutes (Reduced at higher temperatures). Thinner/Cleaner If needed max 5% styrene. For cleaning: Acetone or Jotun Thinner

No 17.Guiding data airless sprayPressure at nozzle 15 - 25 MPa (150-250 kp/cm², 2100-4000 psi.) Ratio/Capacity: >45:1, min. 12 l per minute. Slow moving piston.Nozzle tip 0,69 - 1.09 mm (0.027 - 0.043'').Spray angle 40-80°, best 60°.Filter To be removed.Note For further details please see separate "Working Manual".

Approved alternatives to Norpol catalyst No 1. can be used. Contact Jotun Paints, Technical Service Department.



Using 2-comp. airless spraySubstrate temperature 5°C 10°C 23°C 40°CSurface dry 3 h 2,5 h 1 h 1 hThrough dry 3 h 2,5 h 1 h 1 hCured 72 h 48 h 12 h 4 h

Dry to recoat, minimum 3 h 2,5 h 1 h 1 h

Dry to recoat, maximum 1 12 h 12 h 12 h 12 h

Using 1-comp. airless spraySubstrate temperature 10°C 23°C 40°CSurface dry 3 h 2 h 2 hThrough dry 3 h 2 h 2 hCured 72 h 48 h 24 h


Dry to recoat, maximum 12 h 12 h 12 h



Typical paint systemOver Sa 2½:Baltoflake Multi

Imersed areas:Baltoflake Multi

1 x 500 µm

2 x 600 µm



Number of coats and dry film thickness will vary, depending on corrosion class and lifetime request. Please contact Jotun Paints, Technical Service Dept. at nearest Jotun office for advice.



MIXING TABELS:When using 2-component spray, the temperature of the paint should not be lower than 15°C. Mechanical agitation for 1 min. is necessary to secure proper mixing of the added components into the paint:

1:1-2-component airless spray. Mark one paint container A and the other B.

Addition to container ANorpol accelerator 9802P/S

Addition to container B Norpol peroxide No. 1Steel

temperature Volume % ml. to 16 ltr. Volum % ml to 16 ltr.

5-15°C 4,6 735 4,2 67015-30°C 2,3 370 4,2 67030-35°C 2,3 370 2,1 335After addition of Norpol Peroxide No 1, the content of container B should be used within 8 hours.

2-component airless spray wich is equipped with peroxide injection pump:Addition of Norpol accelerator 9802P/S

Addition of Norpol peroxide No 1

Steel temperature

Volume % ml. to 16 ltr. Volum %5-15°C 2,3 370 2,115-30°C 1,15 185 2,130-35°C 1,15 185 1,0

1-component airless spray:Addition of Norpol accelerator 9802P/S

Addition of Norpol peroxide No 1Steel temperature

Volume % ml. to 16 ltr. Volum % ml to 16 ltr.10-15°C 2,3 370 2,1 33515-20°C 1,15 185 2,1 33520-25°C 1,15 185 1,0 16025-30°C 0,6 95 1,0 16030-35°C 0,6 95 0,8 130The temperature of the paint should never be more than 5°C higher than the steel temperature. The accelerator should be mixed properly into the paint before Norpol Peroxide No 1 is added.

___________________________________________________________________________

StorageThe product must be stored below 25°C and in accordance with national regulations. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed. SHELF LIFE: 6 months, subject to re-inspection therafter. Shelf life very much depends on tempeature. Lower temperatures (if possible below freezing point) will lengthen the shelf life considerably, while high temperature may lead to gelling in the thin.


Packing size16 litres (20 kg)Packing may vary from country to country according to local requirements.


Technical DataBALTOFLAKE MULTI E

Product descriptionBaltoflake Multi E is a styrene free glass flake reinforced polyester coating with wide film thickness range that gives long term corrosion protection. It can be applied both with ratio 1:1 two-component airless spray and ordinary one-component airless equipment.




3,3 1,63 2

Physical propertiesColour Limited range of coloursSolids (vol %)* 98 ± 1 Flash point 53ºC ± 2 (Setaflash)Gloss SemiflatGloss retention GoodWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Very good Chemical resistance Very good Flexibility LimitedCompatibility withcathodic protection Very good


Surface preparation





BALTOFLAKE MULTI E Page 1

Condition during applicationThe temperature of the substrate should be minimum 5°C (10º when using 1-comp. spray) and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to ensure proper drying. The coating should not be exposed to oil, chemicals or mechanical stress until fully cured.

Application methodsSpray Preferably 1:1 2-comp. airless spray. Other types of 2-component equipment can

be used. Application with 1-comp. ordinary airless spray is also possible. Brush Recommended for stripe coating and small areas, care must be taken to achieve


Application data Mixing ratio (volume) 1:1-2-component airless spray:

Norpol accelerator 9802P/S (1% Co) is added to one paint container and Norpol peroxide No. 1 to the other. 1-component airless spray: Both Norpol accelerator 9802P/S (1% Co) and Norpol peroxide No. 1 is added to the same container.For correct addition, see tables below. Warning: Accelerator and peroxide must never be mixed directly together.

Pot life (23°C) 10-55 minutes (Reduced at higher temperatures). Thinner/Cleaner If needed max 5% vinyl toluene. For cleaning: Acetone or Jotun

Thinner No 17.Guiding data airless sprayPressure at nozzle 15 - 25 MPa (150-250 kp/cm², 2100-4000 psi.) Ratio/Capacity: >45:1, min. 12 l per minute. Slow moving piston.Nozzle tip 0.69 - 1.09 mm (0.027 - 0.043'').Spray angle 40-80°, best 60°.Filter To be removed.Note For further details please see separate "Working Manual".

Approved alternatives to Norpol catalyst No 1 can be used. Contact Jotun Paints, Technical Service Department.



Using 2-comp. airless spray Substrate temperature 5°C 10°C 23°C 40°CSurface dry 3 h 2.5 h 1 h 1 hThrough dry 3 h 2.5 h 1 h 1 hCured 3 d 2 d 1/2 d 1/6 d

Dry to recoat, minimum 3 h 2.5 h 1 h 1 h


Using 1-comp. airless spraySubstrate temperature 10°C 23°C 40°CSurface dry 3 h 2 h 2 hThrough dry 3 h 2 h 2 hCured 3 d 2 d 1 d





Typical paint systemBaltoflake Multi E

For immersed areas:Baltoflake Multi E

1 x 500 µm

2 x 600 µm


(Dry Film Thickness)Number of coats and dry film thickness will vary, depending on corrosion class and lifetime request. Please contact Jotun Technical Support at nearest Jotun office for advice. Other systems may be specified, depending on area of use

MIXING TABELS:

When using 2-component spray, the temperature of the paint should not be lower than 15°C. Mechanical agitation for for 1 min. is necessary to secure proper mixing of the added components into the paint:

1:1-2-component airless spray. Mark one paint container A and the other B.

Addition to container ANorpol accelerator 9802P/S

Addition to container B Norpol peroxide No. 1Steel

temperature Volume % ml. to 16 ltr. Volum % ml to 16 ltr.

5-10°C 4,6 735 4,2 67010-35°C 4,6 735 2,1 335After addition of Norpol Peroxide No 1, the content of container B should be used within 8 hours.


2-component airless spray wich is equipped with peroxide injection pump:Addition of Norpol accelerator 9802P/S


Volume % ml. to 16 ltr. Volum %5-10°C 2,3 370 2,110-35°C 2,3 370 1,0

1-component airless spray:Addition of Norpol accelerator 9802P/S


Volume % ml. to 16 ltr. Volum % ml to 16 ltr.10-15°C 2,3 370 1,0 16015-20°C 1,15 185 1,0 16020-25°C 0,8 130 1,0 16025-35°C 0,6 95 1,0 160

The temperature of the paint should never be more than 5°C higher than the steel temperature. The accelerator should be mixed properly into the paint before Norpol Peroxide No 1 is added.

______________________________________________________________________________

StorageThe product must be stored below 25°C and in accordance with national regulations. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed. SHELF LIFE: 6 months, subject to re-inspection therafter. Shelf life very much depends on tempeature. Lower temperatures (if possible below freezing point) will lengthen the shelf life considerably, while high temperature may lead to gelling in the thin.


Packing size16 litres (20 kg)Packing may vary from country to country according to local requirements.




Technical DataBARRIER

Product descriptionBarrier is a two-pack zinc rich epoxy primer with a high content of zinc.

Recommended useAs a primer on blast cleaned steel. Barrier is used in combination with advanced coating systems to further improve protection against corrosion.



21,2 5 13,3

CommentsIn a systems of DFT of max. 90 µm, the drying time will increase.

Physical propertiesColour GreySolids (vol %)* 53 ± 2 Flash point 27ºC ± 2 (Setaflash)Gloss FlatWater resistance ExcellentAbrasion resistance Very goodSolvent resistance Very good Flexibility GoodCompatibility withcathodic protection Good


Surface preparation


Bare steelCleanliness: Blast cleaning to min. Sa 2 ½ (ISO 8501-1:1988) or for maintenance UHPWJ to WJ2 (NACE No.5/SSPC-SP 12). Roughness: using abrasives suitable to achieve grade Fine to Medium G (30-85 µm, Ry5) (ISO 8503-2)


Condition during application

BARRIER Page 1

The temperature of the substrate should be minimum 5°C and at least 3ºC above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is required in confined areas to ensure correct drying.



Application data Mixing ratio (volume) 3 part Comp. A (base) to 1 part Comp. B (curing agent)

Mixing: ½ hour prior to use.Pot life (23°C) 24 hours. (Reduced at higher temp.). Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa min (150 kp/cm², 2100 psi.).Nozzle tip 0.38 - 0.53 mm (0.015 - 0.021").Spray angle 40 - 80°Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 50 min 20 min 10 min 4 minThrough dry 3 h 2 h 1,5 h 0,7 hCured 10 d 7 d 5 d 2 d

Dry to recoat, minimum 1 3 h 2 h 1,5 h 0,7 h


1 Recommended data given for recoating with coatings normally specified on top of zinc epoxy coatings.



Typical paint systemBarrier 1 x 25-90 µm (Dry Film Thickness)

Subsequent coating(s) by choice e.g.: epoxy, acrylic or vinyl.Other systems may be specified, depending on area of use

Storage

BARRIER Page 2

The product must be stored in accordance with national regulations. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition.Containers must be kept tightly closed.

HandlingHandle with care. Stir well before use.Continuous stirring during application will prevent the heavy zinc pigment from settling.

Packing size3 l Comp. A (base) and 1 l Comp. B (curing agent).6.75 l Comp. A (base) and 2.25 l Comp. B (curing agent).Packing may vary from country to country according to local requirements.






Middle EastJotun U.A.E Ltd. LLC.Al Quoz Industrial AreaP.O Box 3671Dubai U.A.EPhone +971 4 3 39 50 00Fax +971 4 3 38 06 66

South East AsiaJotun (Singapore) Pte. Ltd.No 11-15, Sixth Lok Yang RoadJurongSingapore 628 111Phone +65 6265 4711Fax +65 6265 7484


ISSUED 22 APRIL 2002 BY JOTUN PAINTSTHIS DATA SHEET SUPERSEDES THOSE PREVIOUSLY ISSUED

BARRIER Page 3

Technical DataBARRIER 77

Product descriptionBarrier 77 is a two-pack zinc rich epoxy primer.

Recommended useAs a primer on blast cleaned steel. Barrier 77 is used in combination with advanced coating systems to further improve protection against corrosion.



21,2 7,1 10,6

Physical propertiesColour GreySolids (vol %)* 53 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss FlatWater resistance ExcellentAbrasion resistance Very goodSolvent resistance Very good Flexibility Good


Surface preparation




Condition during applicationThe temperature of the substrate should be minimum 5°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to ensure proper drying.

BARRIER 77 Page 1



Application data Mixing ratio (volume) 3 part Comp. A (base) to 1 part Comp. B (curing agent)

Mixing: ½ hour prior to use.Pot life (23°C) 24 hours (Reduced at higher temp.). Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa min (150 kp/cm², 2100 psi.).Nozzle tip 0.38 - 0.53 mm (0.015 - 0.021").Spray angle 40 - 80°Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 50 min 20 min 10 min 4 minThrough dry 3 h 2 h 1,5 h 0,7 hCured 10 d 7 d 5 d 2 d

Dry to recoat, minimum 1 3 h 2 h 1,5 h 0,7 h


1 Recommended data given for recoating with coatings normally specified on top of zinc epoxy coatings.



Typical paint systemBarrier 77 1 x 25 - 75 µm (Dry Film Thickness)Subsequent coating(s) by choice e.g.: Epoxy, Acrylic or Vinyl.


BARRIER 77 Page 2



Packing size13.5 l Comp. A (base) and 4.5 l Comp. B (curing agent).











BARRIER 77 Page 3

Technical DataCHEMCLEAR

Product descriptionChemclear is a preaccelerated clear vinyl ester coating.

Recommended useAs sealer (size) on concrete surfaces or in combination with glassfibre as a laminating resin.



6,4 3,2 4,8

CommentsPractical consumption on concrete: 0.15 - 0.3 l/m²

Physical propertiesColour Clear (Yellowish shade)Solids (vol %)* 96 ± 2 Flash point 34ºC ± 2 (Setaflash)Gloss GlossyWater resistance ExcellentSolvent resistance Very good Chemical resistance Very good Flexibility Good


Surface preparation

All concrete damaged by exposure to chemicals, contaminated by any substance or unsound in any way, shall be removed to expose sound concrete.

Other surfacesConcrete surface preparation by using dust free captive blasting units, grinding equipment, sand blasting or high pressure water jetting is critical to achieving the right surface profile prior to paint application. Contact your local Jotun office for more information.

The coating may be used on other substrates. Please contact your local Jotun office for more information.

Condition during applicationThe temperature of the substrate should be minimum 15°C and at least 3°C above the dew point of the air. The temperature and the relative humidity should be measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to ensure proper drying. The coating should not be exposed to oil, chemicals or mechanical stress until fully cured.

CHEMCLEAR Page 1

Application methodsSpray Use airless sprayBrush Recommended Roller Recommended

Application data Mixing ratio (volume) MIXING OF COMPONENTS:

Add the various ingredients while stirring in the following proportions and order, based on 16 liters of CHEMCLEAR:

Mixing when used as sealer:

1: Add maximum 3.5 litres of styrene.2: Add 400 ml of Norpol Catalyst no. 11.

Mixing when used as laminating resin:

1: Add maximum 50 ml of Norpol Inhibitor 9853. Mix well.2: Add 400 ml of Norpol Catalyst no. 11.

Mechanical stirring in min. 1 minute is necessary. The temperature in CHEMCLEAR should not exceed 25 °C. If exceeded, the pot life will be drastically reduced.

Pot life (23°C) 20 - 30 minutes ; at 15°C: 40 - 50 minutes Thinner Thin with 15-20 vol% styrene prior to use as sealer. No thinning

necessary when used as liminating resin.Cleaner Acetone or Jotun Thinner No 17 or No 23Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi.)Nozzle tip 0.33 - 0.46 mm (0.013 - 0.018").Spray angle 40 - 80°Filter Check to ensure that filters are clean.






CHEMCLEAR Page 2

Typical paint system1) Chemclear2) Chemflakeor Baltoflake

2 x 750 µm1 x 1000 µm



StorageThe product must be stored below 25°C and in accordance with national regulations. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed.

HandlingSHELF LIFE: 4 months, subject to re-inspection thereafter. Shelf life very much depends on temperature. Lower temperatures (if possible below freezing point) will prolong the shelf life considerably, while high temperature may lead to gelling in the tin.

Packing size16 l (16 kg) clearPacking may vary from country to country according to local requirements.










CHEMCLEAR Page 3

Technical DataCHEMFLAKE CV

Product descriptionChemflake CV (Conductive Version) is a glass flake reinforced high build vinyl ester coating with high conductivity.

Recommended useSteel in aggressive environments. For gasoline or bulk crude tanks where anti-static coating is required.



1,92 1,37 1,6

Physical propertiesColour BlackSolids (vol %)* 96 ± 2 Flash point 34ºC ± 2 (Setaflash)Gloss SemiflatWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Flexibility Limited


Surface preparation





CHEMFLAKE CV Page 1



Application data Mixing ratio (volume) Ratios and order of addition:

Add the various ingredients while stirring in the following properties and order, based on 16 liters of CHEMFLAKE CV base component.

1: 2 vol% (320 ml) Norpol Accelerator 9802 (Cobalt octoate in styrene, 1% Co)

2: 0.6 vol% (100 ml) Norpol DMA 9826 (10% dimethylanilin in styrene)

1. and 2. must be properly mixed in before adding:

3: 2.5 vol% (400 ml) Norpol Cat. No. 1 or 11 (MEK-peroxide)

Mechanical stirring in min. 1 minute is necessary.

The temperature in CHEMFLAKE CV should preferably not exceed 25° C, as pot life may be drastically reduced if exceeded.

In the temperature range 25 - 30° C, one may overcome the problem by first adding Norpol Inhibitor No. 9853 (max 0.4 vol% - 60 ml per 16 l CHEMFLAKE CV), stir well and then continue with 1, 2 and 3 as described above.

Approved alternatives to Norpol Catalysts can be used.Please contact Jotun Paints, Technical Service Department.

WARNING!........................................Norpol Accelerator 9802 and Norpol Cat. No. 1(MEK-peroxide) must never be mixed directly with each other. Be sure that steel temperature is equal or higher than paint temperature.

Pot life (23°C) 35 minutes (reduced at higher temp.) Cleaner Acetone or Jotun Thinner No. 17/23.Guiding data airless sprayPressure at nozzle 15 - 25 MPa min (150 - 280 kp/cm², 2100 - 4000 psi.)Nozzle tip 0.86 - 1.14 mm (0.034 - 0.045")Spray angle 40 - 80°Filter To be removed.

CHEMFLAKE CV Page 2






Typical paint systemChemflake CV 2 x 750 µm (Dry Film Thickness) Other systems may be specified, depending on area of use






CHEMFLAKE CV Page 3








CHEMFLAKE CV Page 4

Technical DataCHEMFLAKE SPECIAL

Product descriptionChemflake Special is a high build glass flake reinforced vinyl ester coating, specially designed for high temperature service.

Recommended useSteel in aggressive environments. For maximum corrosion and chemical protection also in high temperature environment. May also be used for protection of aluminium and concrete (special designed systems).



1,6 0,96 1,28

Physical propertiesColour Red, WhiteSolids (vol %)* 96 ± 2 Flash point 34ºC ± 2 (Setaflash)Gloss SemiflatWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Flexibility Limited


Surface preparation




CHEMFLAKE SPECIAL Page 1


Application methodsSpray Use normal airless spray or two-comp. airless spray equipmentBrush Recommended for stripe coating and small areas, care must be taken to achieve


Application data Mixing ratio (volume) Choose quantity of curing agent, accelerator and inhibitor according

to the table below. Inhibitor or accelerator must be thoroughly mixed with Chemflake Classic before adding the required amount of MEK-peroxide. Mechanical agitation for one minute or more.

Note:Check temperature of pump during application. Friction in piston may cause increase in temperature. If this should happen, get the Chemflake Classic out as quickly as possible.If the temperature is ranging near the max. temperature in a zone, it is recommended to reduce the content of peroxide/accelerator respectively, or to increase the content of inhibitor.

Approved alternatives to Norpol Catalysts can be used.Please contact Jotun Paints, Technical Service Department.

Warning:Accelerator 9802 and MEK-peroxide must never be mixed directly together.Be sure that steel temperature is equal or higher than paint temperature.

Steel and paint temperature: 40º C --------------------------------------------------------- 0.2 vol% ( 30 ml)NORPOL Inhibitor 9853 1.4 vol% (225 ml) NORPOL Accelerator 9802 0.6 vol% (100 ml) NORPOL Accelerator 9826 2.2 vol% (350 ml) NORPOL Catalyst no. 1 or 1135º C ---------------------------------------------------------- 1.40 vol% (225 ml) NORPOL Accelerator 9802 0.6 vol% (100 ml) NORPOL Accelerator 9826 2.2 vol% (350 ml) NORPOL Catalyst no. 1 or 11 30º C ---------------------------------------------------------- 1.75 vol% (280 ml) NORPOL Accelerator 9802 0.6 vol% (100 ml) NORPOL Accelerator 9826 2.2 vol% (350 ml) NORPOL Catalyst no. 1 or 11 25º C ---------------------------------------------------------- 2.0 vol% (320 ml) NORPOL Accelerator 9802 0.6 vol% (100 ml) NORPOL Accelerator 9826 2.5 vol% (400 ml) NORPOL Catalyst no. 1 or 11 20º C ----------------------------------------------------------- 2.25 vol% (360 ml) NORPOL Accelerator 9802 0.6 vol% (100 ml) NORPOL Accelerator 9826 2.5 vol% (400 ml) NORPOL Catalyst no. 1 or 11 15º C -----------------------------------------------------------

Pot life (23°C) 25 - 50 minutes (reduced at higher temp.)


Cleaner Acetone or Jotun Thinner No. 17/23.Guiding data airless sprayPressure at nozzle 15 - 25 MPa (150-280 kp/cm², 2100-4000 psi.). Ratio/Capacity: > 45:1. Min. 12 l per minute. Slow moving piston.Nozzle tip 0.86 - 1.14 mm (0.034 - 0.045”).Spray angle 40 - 80°Filter To be removed.Note For further details please see separate "Working Manual".




1 The surface should be dry and free from any contamination prior to application. If the maximum dry to recoat time is exceeded, please contact Jotun Paints for advice


Typical paint systemOn steel:Chemflake Special 2 x 750 µm (Dry Film Thickness)

Holiday detector after 1st coat:NACE RPO 188-88. (400 volt per 100 µm)Other systems may be specified, depending on area of use





Technical DataCHEMFLAKE TOUCH-UP SET

Product descriptionChemflake Touch-Up Set is a Vinyl ester thickening paste intended for mixing with Chemflake (all types).

Recommended useAfter mixing the paste with Chemflake (all types), a paint is obtained suitable for touching-up articles with a brush.

Physical propertiesColour ColourlessSolids (vol %)* 96 ± 2 Flash point 34ºC ± 2 (Setaflash)*Measured according to ISO 3233:1998 (E)

Application methodsBrush Recommended for stripe coating and small areas, care must be taken to achieve


Application data Mixing ratio (volume) Add the ingredients to 2.5 litres of paste and CHEMFLAKE (all

types).

Inhibitor:Max. 0.4 vol% (10 ml.) Norpol Inhibitor 9853 if potlife is too short.

Accelerators:1. 2 vol% (50 ml) Norpol Accelerator 9802.2. 0.6 vol% (15 ml) Norpol Accelerator 9826.

1 and 2 must be properly mixed before adding catalyst

Catalyst:3. 2.5 vol% (65 ml) Norpol Cat. No. 1.

WARNING! ..........................................Norpol Accelerator 9802 and Norpol Cat. No. 1 (MEK-peroxide) must never be mixed directly together.

Instead of mixing small amounts of inhibitor, alt. accelerators as described above, a premixed Chemflake (all types) can be added to the paste. Catalyst must be added separately.

MixingThe tin (3 litres) contains 0.5 kg paste which is mixed with 2.5 kg (2.0 litres) of Chemflake (all types). Use a mechanical mixer to ensure good mixing.

Pot life (23°C) 45 minutes (reduced at higher temp.) Thinner/Cleaner No thinning. For cleaning: Acetone or Jotun Thinner No. 17.

CHEMFLAKE TOUCH-UP SET Page 1



Packing size0.5 kg in 3 litres tin.Packing may vary from country to country according to local requirements.










CHEMFLAKE TOUCH-UP SET Page 2

Technical DataCHEMLINE EP

Product descriptionChemline EP is a solvent-free two-pack epoxy glassfibre lining system.

Recommended useFor use as lining in storage tanks where the condition of the steel, the content or other reasons require the use of a lining in combination with glass fibre mat.



1 0,33 0,6

Physical propertiesColour ClearSolids (vol %)* 100 ± Flash point Non-flammableGloss GlossyWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Flexibility Fair


Surface preparation


Bare steelCleanliness: Blast cleaning to min. Sa 2 ½ (ISO 8501 1:1988). Roughness: using abrasives suitable to achieve Grade Medium G (50 - 85 µm, Ry5) (ISO 8503-2).

Coated surfacesApproved on top of thin coat (50 µm) of Tankguard HB


CHEMLINE EP Page 1

Condition during applicationThe temperature of the substrate should be minimum 10°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. The coating should not be exposed to oil, chemicals or mechanical stress until fully cured.

Application methodsRoller See application procedure.

Application data Mixing ratio (volume) Mixing ratio by weight: 5 parts Comp. A (base) to be mixed

thoroughly with 3 parts Comp. B (curing agent).Pot life (23°C) 1-2 hours. (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17/or stronger, No. 23

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 23°C 40°CSurface dry 10-20 h 4-6 hThrough dry 16-30 h 6-8 hCured 5-12 d 4-7 d

Dry to recoat, minimum 12 h 6 h

Dry to recoat, maximum 1 3 d 2 d

1 The surface should be free from contamination prior to application.


Typical paint systemBlastcleaning to Sa 2½.Tankguard HB 40-50 µm (Dry Film Thickness).All pittings to be filled with Chemline EP Putty.Chemline EP: One layer system:Chemline EP A+B plus 450 g/m² glass mat 1500-1800 microns.Two layer system:Chemline EP A+B plus 300 g/m² glass mat 2500-3000 microns.Other systems may be specified, depending on area of use

CHEMLINE EP Page 2



Packing size12 kg Comp. A, 7.2 kg Comp. B.Packing may vary from country to country according to local requirements.










CHEMLINE EP Page 3

Technical DataCHEMLINE EP PUTTY

Product descriptionChemline EP Putty is a solvent-free epoxy putty. To be mixed on site.

Recommended useFor use as putty/caulking of interiors of storage tanks.

Physical propertiesColour YellowSolids (vol %)* 100 ± Flash point Non-flammableGloss GlossyWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Flexibility Fair


Surface preparation






Application methodsOther Trowel, see application procedure.

Application dataMixing ratio (volume) Mixing ratio by weight: 5 parts Comp. A (base) to be mixed

CHEMLINE EP PUTTY Page 1

thoroughly with 3 parts Comp. B (curing agent) then add adequate quantity of Aerosil 300 to A+B mixture to reach the required past viscosity.

Pot life (23°C) ½-1 hour. (Reduced at higher temp.) Cleaner Jotun Thinner No. 17 or stronger, No. 23

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 23°C 40°CSurface dry 10-20 h 4-6 hThrough dry 16-30 h 6-8 hCured 5-12 d 4-7 d



1 The surface should be free from contamination prior to application.


Typical paint systemEither direct on blast cleaned surface or on Tankguard HB. Fill curb angles, overlap welds and holes with diameter less than 1 cm² with Chemline EP Putty.Other systems may be specified, depending on area of use



Packing size3.1 kg Comp. A, 1.9 kg Comp. B.Packing may vary from country to country according to local requirements.



Last changed: 05/10/2000 Internal no.: 06 Replaces date:

CHEMTECH EPOXY PRIMER - COMP. A

1/6


Approved for use



TRADE NAME CHEMTECH EPOXY PRIMER - COMP. AAPPLICATION Two-pack high molecular epoxy primer.

ART-NO PM3336




1 XYLENE, mixed isomers 1330-20-7 10-25 N Xn,10-20/21-383 PROPAN-2-OL 67-63-0 2,5-10 N F,114 N-BUTANOL 71-36-3 2,5-10 N Xn,10-22-37/38-41-67




Harmful Highly flammable

HIGHLY FLAMMABLE. HARMFUL BY INHALATION AND IN CONTACT WITH SKIN. IRRITATING TOEYES AND SKIN.For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL




2/6






MEDICAL INFORMATION Risk of chemical pneumonia by aspiration. Keep attention: danger of lung damage. General health examination.Professional evaluation of the work station. Regulary medical control. Person developing a skin rash are to bedirected to a dermatologist for examination.



FIRE AND EXPLOSION HAZARDSFire will produce dense black smoke containing hazardous products of combustion (see Section 10). Decompositionproducts may be a hazard to health. Appropirate self-contained breathing apparatus may be required.






HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Always keep incontainers made of the same material as the supply container. Always use earth (ground) wire when transferringfrom one container to another. Personnel should wear anti-static clothing and footwear. Floors should be




3/6

electrically conductive. Keep container tightly closed. Exclude sources of heat, sparks and open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist. For personal protectiveequipment see Section 8. Never use pressure to empty the container, it is not a pressure vessel. Electrical equipmentshould be protected to appropriate standards. The Manual Handling Operations Regulations may apply to thehandling of containers of this product. Smoking, eating and drinking are forbidden in the work area.




PROPAN-2-OL 67-63-0 999,0 mg/m3, Sk 1250,0 mg/m3, Sk

N-BUTANOL 71-36-3 - 154,0 mg/m3;Sk

EXPOSURE CONTROLPersons with allergic reactions to epoxy should not work with epoxy containing products. Provide adequateventilation. Where reasonably practicable this should be achieved by the use of local exhaust ventilation and goodgeneral extraction. Spray mist contains all substances of the product and must not be inhaled. OEL's are taken fromthe current version of EH40 (by Health & Safety Executive, UK).

RESP. PROTECTIONWhen use of roller or brush, then charcoal filter is sufficient. Use respiratory protective mask with charcoal anddust filter (A2/P2) when spraying this product.


HAND PROTECTIONUse PVA gloves.Barrier creams may help to protect exposed areas of the skin but are not substitutes for fullphysical protection. Never apply barrier cream to contaminated skin.

SKIN PROTECTIONWear anti-static clothing made of natural fibre or of heat resistant synthetic fibre.When spraying use suit coveringthe whole body.




4/6


Form Liquid.Colour Various.Odour Organic solvent.Solubility Organic solvent.Melting point/range Density 1,39

Expl. limit LEL-UEL., %-%: 1,1-12,0 Solubility in water



pH Solution Boiling point/range 82-144°C

Flash point 17°c pH concentrate

Molecular weight Viscosity

Ignition temp 287°C Smelling limits lo-hi








GENERALThere are no toxicological data available on the product itself. The epoxy compound in this product showed nosensitization in animal experiments. Whether this compound gives allergy to humans is not known. Neverthelessthe possibility of allergy in hypersesitive persons, can not be excluded. Skin contact with the preparation andexposure to spray mist and vapour should be avoided.

INHALATIONExposure to organic solvent vapours may result in adverse health effects such as irritation of the mucous membraneand the respiratory system and adverse effects on the renal and central nervous system. Symptoms and signs includeheadache; dizziness, fatigue, muscular weakness, drowsiness and in extreme cases, loss of consciousness.



INGESTIONAccidental ingestion may cause vomiting and abdominal pains. Risk of chemical pneumonia.Absorbed by the




5/6

gastrointestinal tract. May cause liver and kidney damage.


OTHER INFORMATIONThe product should not be allowed to enter drains or water courses or be deposited where it can affect ground orsurface waters.

13. DISPOSAL


WASTEGROUP08 00 00 WASTES FROM THE MANUFACTURE, FORMULATION, SUPPLY AND USE (MFSU) OFCOATINGS (PAINTS, VARNISHES AND VITREOUS ENAMELS), ADHESIVE, SEALANTS ANDPRINTING INKS. 08 01 03 waste from water-based paints and varnishes.



HAZCHEM

ADR (Road)


Class 3,5 (b) Label 3Haz. id. no 33 Marginno.

RID (Railway)


Class 3,5 (b) Label 3Haz..id.no 33

IMDG (Sea)


Class 3.2 Label 3Packaging group II EmS 3-05MFAG 310 Marine Pollutant

Sub. risk Page 3268

IATA (Airplane)


Class 3 Sub. risk

Label 3 Packaging group II

GENERALTransport only in accordance with ADR for road, RID for rail, IMDG for sea transport and IATA for airtransport.The product is not classified as dangerous goods for carriage.





6/6

Classification

Harmful Highly flammable

COMPOSITION XYLENE, mixed isomers (10-25)

R-PHRASESR11 - Highly flammable. R20/21 Harmful by inhalation and in contact with skin. R36/38 - Irritating to eyes andskin.

S-PHRASESS16-Keep away from sources of ignition - No smoking. S23 Do not breathe vapour/spray. S36/37 Wear suitableprotective clothing and gloves. S38 In case of insufficient ventilation, wear suitable respiratory equipment.



PRINTEDOUT:

10/05/2000

VENDOR NOTES Persons with epoxy allergic reactions, should not work with this kind of products. The information contained inthis MSDS is based on the present state of knowledge and current national legislation. As the specific conditions ofuse of the product are outside the supplier's control, the user is responsible for ensuring that the requirements ofrelevant legislation are compiled with. The information in this MSDS provides guidance on health, safety andenvironmental aspects of the product and should not be construed as any guarantee of technical performance orsuitability for particular applications. The Environmental Protection (Duty of Care) Regulations 1992 (SI1992:2839). Further information and relevant advice can be found in: The Control of Substances Hazardous toHealth Regulations 1988 (SI1988:1657). The Highly Flammable Liquids and liquefied Petroleum GasesRegulations 197 (SI 1972:917). The Manual Handling Operations Regulations 1992 (SI 1992:2793). Storage ofFlammable Liquids in Containers, HS(G)51. Storage of Packaged Dangerous Substances, HS(G)71. The selection,use and maintenance of respiratory protective equipment: A practical guide HS(G)53.



CHEMTECH EPOXY PRIMER - COMP. B

1/6


Approved for use



TRADE NAME CHEMTECH EPOXY PRIMER - COMP. BAPPLICATION Two-pack high molecular epoxy primer.

ART-NO PM3337




1 XYLENE, mixed isomers 1330-20-7 25-50 N Xn,10-20/21-382 N-BUTANOL 71-36-3 10-25 N Xn,10-22-37/38-41-673 1-METHOXY-2-PROPANOL 107-98-2 10-25 N 10


INGREDIENT COMMENTS Substances presenting a health hazard within the meaning of the current issue of the CHIP Regulations or assignedoccupational exposure limits.


Harmful

FLAMMABLE. HARMFUL BY INHALATION AND IN CONTACT WITH SKIN. IRRITATING TO SKIN.RISK OF SERIOUS DAMAGE TO EYES .For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL




2/6






MEDICAL INFORMATION Risk of chemical pneumonia by aspiration. Keep attention: danger of lung damage. General health examination.Professional evaluation of the work station.









HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Always use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.




3/6

Smoking, eating and drinking are forbidden in the work area.For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty thecontainer, it is not a pressure vessel. Electrical equipment should be protected to appropriate standards. The ManualHandling Operations Regulations may apply to the handling of containers of this product.




1-METHOXY-2-PROPANOL 107-98-2 375,0 mg/m3;Sk 1120,0 mg/m3;Sk

N-BUTANOL 71-36-3 - 154,0 mg/m3;Sk

EXPOSURE CONTROLProvide adequate ventilation. Where reasonably practicable this should be achieved by the use of local exhaustventilation and good general extraction. Use respiratory protection when the concentration of solvents/compoundsexceeds the Occupational Exposure Limit. Spray mist contains all substances of the product and must not beinhaled. OEL's are taken from the current version of EH40 (by Health & Safety Executive, UK).








4/6


Form Liquid.Colour Brownish.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 0,88Expl. limit LEL-UEL., %-%: 1,1-11,3 Solubility in water



pH Solution Boiling point/range 118-144ºC












SKIN CONTACTRepeated or prolonged contact with the product may lead to removal of natural fats from the skin resulting in non-allergic contact dermatitis and absorption through the skin.


INGESTIONAccidental ingestion may cause vomiting and abdominal pains. Risk of chemical pneumonia.Absorbed by thegastric intestinal system. May cause liver and kidney damage.


OTHER INFORMATION




5/6

The product should not be allowed to enter drains or water courses or be deposited where it can affect ground orsurface waters.

13. DISPOSAL





HAZCHEM

ADR (Road)


Class 3,31 (c) Label 3Haz. id. no 30 Marginno.

RID (Railway)


Class 3,31 (c) Label 3Haz..id.no 30

IMDG (Sea)


Class 3.3 Label 3Packaging group III EmS 3 - 05MFAG 310 Marine Pollutant

Sub. risk Page 3372

IATA (Airplane)


Class 3 Sub. risk

Label 3 Packaging group III



Classification

Harmful

COMPOSITION XYLENE, mixed isomers (25-50), N-BUTANOL (10-25)

R-PHRASES




6/6

R10 Flammable. R20/21 Harmful by inhalation and in contact with skin. R38 Irritating to skin. R41 Risk of seriousdamage to eyes.

S-PHRASESS23 Do not breathe vapour/spray. S26 In case of contact with eyes, rinse immediately with plenty of water and seekmedical advice.S36/37 Wear suitable protective clothing and gloves. S38 In case of insufficient ventilation, wearsuitable respiratory equipment. S39 Wear eye/face protection.



PRINTEDOUT:

06/10/2000

VENDOR NOTES The information contained in this MSDS is based on the present state of knowledge and current nationallegislation. As the specific conditions of use of the product are outside the supplier's control, the user is responsiblefor ensuring that the requirements of relevant legislation are compiled with. The information in this MSDSprovides guidance on health, safety and environmental aspects of the product and should not be construed as anyguarantee of technical performance or suitability for particular applications. The Environmental Protection (Dutyof Care) Regulations 1992 (SI 1992:2839). Further information and relevant advice can be found in: The Control ofSubstances Hazardous to Health Regulations 1988 (SI1988:1657). The Highly Flammable Liquids and liquefiedPetroleum Gases Regulations 197 (SI 1972:917). The Manual Handling Operations Regulations 1992 (SI1992:2793). Storage of Flammable Liquids in Containers, HS(G)51. Storage of Packaged Dangerous Substances,HS(G)71. The selection, use and maintenance of respiratory protective equipment: A practical guide HS(G)53.



CONSEAL PRIMER

1/6


Approved for use



TRADE NAME CONSEAL PRIMERAPPLICATION Alkyd based primer

ART-NO M3145




1 XYLENE, mixed isomers 1330-20-7 25-50 N Xn,10-20/21-38




Harmful

FLAMMABLE. HARMFUL BY INHALATION AND IN CONTACT WITH SKIN. IRRITATING TO SKIN.For potential danger for the environment, see section 12.

4. FIRST AID


INHALATION



CONSEAL PRIMER

2/6

Keep the patient warm in a quiet place with fresh air. If breathing has stopped, administer artificial respiration. Ifunconscious place in the recovery position. Seek medical advice.













HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Always use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area.For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty the



CONSEAL PRIMER

3/6

container, it is not a pressure vessel. Electrical equipment should be protected to appropriate standards. The ManualHandling Operations Regulations may apply to the handling of containers of this product.




EXPOSURE CONTROLProvide adequate ventilation. Where reasonably practicable this should be achieved by the use of local exhaustventilation and good general extraction. Spray mist contains all substances of the product and must not be inhaled.OEL's are taken from the current version of EH40 (by Health & Safety Executive, UK).






Form Liquid.Colour Various.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 1,2-1,4Expl. limit LEL-UEL., %-%: 1.10 - 7 Solubility in water











CONSEAL PRIMER

4/6







SKIN CONTACTRepeated or prolonged exposure may cause skin irritation and dermatitis, due to the product's defatting properties.


INGESTIONAbsorbed by the gastric intestinal system. May cause liver and kidney damage. Accidental ingestion may causevomiting and abdominal pains. Risk of chemical pneumonia. Product contains small amounts of lead-components,that are toxic. Repeated and/or prolonged exposures may result in: adverse respiratory effects (such as cough,tightness of chest or shortness of breath).

CANCERThe product contains ethylbenzene. IARC has classified it as a possible human carcinogen (Group 2B) based onsufficient evidence for carcinogenicity in experimental animals, but inadequate evidence for cancer in exposedhumans.


OTHER INFORMATIONDo not discharge the product to sewer or drains.

13. DISPOSAL

Wastes, including emptied containers, are controlled wastes and should be disposed of in accordance withregulations made under the Control of Pollution Act and the Environmental Protection Act. Do not allow into drainsor water courses.




CONSEAL PRIMER

5/6



HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)


Class 3 Label 3Packaging group III EmS 3 - 05MFAG Marine Pollutant

Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk


GENERALTransport only in accordance with ADR for road, RID for rail, IMDG for sea transport and IATA for airtransport.ADR / RID: Not restricted, ref. chapter 2.2.3.1.5 (applicable to receptacles of < 450 litre capacity).IMDG: Notrestricted, ref. chapter. 2.3.2.5, (applicable to receptacles of < 450 litre).


Classification

Harmful


R-PHRASESR10 Flammable. R20/21 Harmful by inhalation and in contact with skin. R38 Irritating to skin.






CONSEAL PRIMER

6/6

PRINTEDOUT:

03/02/2000

VENDOR NOTES The information contained in this MSDS is based on the present state of knowledge and current nationallegislation. As the specific conditions of use of the product are outside the supplier's control, the user is responsiblefor ensuring that the requirements of relevant legislation are compiled with. The information in this MSDSprovides guidance on health, safety and environmental aspects of the product and should not be construed as anyguarantee of technical performance or suitability for particular applications. Further information and relevantadvice can be found in: The Environmental Protection (Duty of Care) Regulations 1992 (SI 1992:2839). TheControl of Substances Hazardous to Health Regulations 1988 (SI1988:1657). The Highly Flammable Liquids andliquefied Petroleum Gases Regulations 197 (SI 1972:917). The Manual Handling Operations Regulations 1992 (SI1992:2793). Storage of Flammable Liquids in Containers, HS(G)51. Storage of Packaged Dangerous Substances,HS(G)71. The selection, use and maintenance of respiratory protective equipment: A practical guide HS(G)53.

Technical DataCONSEAL PRIMER

Product descriptionFast drying, alkyd based primer with active corrosion preventing pigments.

Recommended useSpecially designed for containers or other items of steel or aluminium where a fast-drying primer is required. Does not contain chromates and is resistant against dry heat up to 120°C.



11 7,3 8,8

Physical propertiesColour Grey, Red, Yellow, WhiteSolids (vol %)* 44 ± 2 Flash point 26ºC ± 2 (Setaflash)Gloss FlatWater resistance GoodFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparationBare steelCleanliness: Blast-cleaning to Sa 2½ (ISO-8501-1:1988). Power tool cleaning to min. St 2 (ISO 8501-1:1988) may be acceptable for minor toch-up work, subjected to exposure conditions.


Other surfacesFor aluminium substrates, thorough washing and sweeping with a nonmetallic blast medium is required.


CONSEAL PRIMER Page 1

Condition during applicationThe temperature of the substrate should be minimum 3°C above the dew point of the air in the vicinity of the substrate.

Application methodsSpray Use airless spray or conventional sprayBrush Recommended Roller Recommended

Application data Thinner/Cleaner Jotun Thinner No. 7Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi).Nozzle tip 0.38-0.53 mm (0.015-0.021").Spray angle 40-80°Filter Check to ensure that filters are clean.


Substrate temperature 5°C 10°C 23°C 40°CSurface dry 30 min 20 min 15 min 10 minThrough dry 2,5 h 2 h 1,5 h 1 hDry to recoat, minimum 2,5 h 2 h 1,5 h 1 h


* Dry to recoat: Conseal Primer can be recoated with coatings containing xylene or stronger solvents within 24 hours or after 5 days after application.

1 The surface should be free from chalking and contamination prior to application of the subsequent coat.*


Typical paint systemConseal Primer 1 x 50 µm (Dry Film Thickness). Conseal Touch-Up 1 x 70 µm (Dry Film Thickness).Other systems may be specified, depending on area of use




Packing size200 l drums, 20 l tins.Packing may vary from country to country according to local requirements.











Technical DataCONSEAL TOPCOAT

Product descriptionConseal Topcoat is a semi glossy quick drying acrylic-based topcoat, with good chemical resistance and corrosion protection in combination with a suitable primer system. Conseal Topcoat is sprayable even at low temperatures.

Recommended useA highly water-resistant topcoat for containers and other steel constructions.



6,7 4 5

Physical propertiesColour According to colour card and Multicolor tinting system (MCI)Solids (vol %)* 40 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss SemiglossGloss retention ExcellentWater resistance Very goodAbrasion resistance GoodSolvent resistance Limited Chemical resistance Good Flexibility Good


Surface preparation


Coated surfacesClean, dry and undamaged compatible primer. Contact your local Jotun office for more information.


CONSEAL TOPCOAT Page 1




Application data Mixing ratio (volume) Single pack.Thinner/Cleaner Jotun Thinner 7Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi.).Nozzle tip 0.45-0.66 mm (0.018-0.026").Spray angle 40 - 65°Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 40 min 30 min 20 min 15 minThrough dry 17 h 15 h 10 h 5 hDry to recoat, minimum 3 h 2,5 h 2 h 1,5 h


Typical paint systemBarrierConseal Topcoat

1 x 40 µm1 x 80 µm





Technical DataCONSEAL TOUCH-UP

Product descriptionConseal Touch-up is a quick drying high build acrylic primer/topcoat.

Recommended useSpecially formulated, high build coating for touch-up of containers etc. May be applied directly on steel.



6,5 4,1 4,1

Physical propertiesColour According to colour card and Multicolor tinting system (MCI)Solids (vol %)* 49 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss SemiglossGloss retention GoodAbrasion resistance GoodSolvent resistance Good Chemical resistance Good Flexibility Good


Surface preparation





CONSEAL TOUCH-UP Page 1


Application methodsSpray Use airless spray (thin 5-10 %) Brush Recommended for stripe coating and small areas, care must be taken to achieve



Application data Thinner/Cleaner Jotun Thinner No. 7

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 40 min 30 min 20 min 15 minThrough dry 17 h 11 h 10 h 6 hDry to recoat, minimum 3 2,5 2 1,5


Typical paint system1) Conseal Touch-up2) Barrier 77Conseal Touch-up

1 x 120 µm1 x 40 µm1 x 75 µm






Packing size5 l, 20 lPacking may vary from country to country according to local requirements.











Technical DataCORREX

Product descriptionCorrex is a semi-glossy silicon alkyd based topcoat with excellent colour and gloss retention

Recommended useFor use as maintenance paint on façade plates and as topcoat in a traditional alkyd system on steel structures.



16 12 12

Physical propertiesColour According to colour cardSolids (vol %)* 48 ± 2 Flash point 35ºC ± 2 (Setaflash)Gloss SemiglossGloss retention ExcellentFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation





CORREX Page 1




Application data Thinner/Cleaner Jotun Thinner No. 2Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi).Nozzle tip 0.38 - 0.46 mm (0.015 - 0.018"). Spray angle 65 - 80° Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 5°C 10°C 23°C 40°CSurface dry 4 h 4 h 3 h 1 hThrough dry 17 h 7 h 4 h 2 hDry to recoat, minimum 24 h 18 h 14 h 10 h




Typical paint systemCromoprimerCorrex

2 x 40 µm1 x 40 µm





CORREX Page 2











CORREX Page 3


Last changed: 03.05.2002 Internal No.: 06 Replaces date:

CORROGUARD SPECIAL - COMP. A

: 1/6

1. IDENTIFICATION OF SUBSTANCE AND COMPANY

Approved for use



TRADE NAME CORROGUARD SPECIAL - COMP. AAPPLICATION Two-pack high molecular epoxy paint.FORMULA .

ART No. PM3443

Producer/importer JOTUN PAINTS (EUROPE) LTD.Address Flixborough, ScunthorpePostal code North Lincolnshire DN15 8RRCountry UKTelephone +44 1724 40 00 00Fax +44 1724 40 01 00Contact pers. SHE-dept., JOTUN A/S, NORWAYResponsible SHE-dept., JOTUN A/S, NORWAYEmergencyTelephones



No Ingredients name CAS No. Conc. (wt%) Classification

1 XYLENE, mixed isomers 1330-20-7 10-25 Xn 10-20/21-38

2 N-BUTANOL 71-36-3 2,5-10 Xn 10-22-37/38-41-67

Legend: T+=Very toxic, T=Toxic, C=Corrosive, Xn=Harmful, Xi=Irritant, E=Explosive, O=Oxidising, F+=Extremely flammable, F=Highlyflammable, N=Dangerous for the environment



Harmful

FLAMMABLE. HARMFUL BY INHALATION AND IN CONTACT WITH SKIN. IRRITATING TO EYESAND SKIN.For potential danger for the environment, see section 12.



INHALATION




: 2/6









PROTECTIVE EQUIPMENT FOR FIRE FIGHTERSThe personal protective equipment required is provided in section 8. Professional fire-fighters are required to usean air-fed system when dealing with major fires.





HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Allways use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area.For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty thecontainer, it is not a pressure vessel. Electrical equipment should be protected to appropriate standards. The ManualHandling Operations Regulations may apply to the handling of containers of this product. Smoking, eating anddrinking are forbidden in the work area.




: 3/6



Ingredients name CAS no. TLV value(long term)

OEL value(short term)

TLVyear

XYLENE, mixed isomers 1330-20-7 441,0 mg/m3 ;Sk 662,0 mg/m³, Sk

N-BUTANOL 71-36-3 154,0 mg/m3;Sk

EXPOSURE CONTROLPersons with allergic reactions to epoxy should not work with epoxy containg products. Provide adequateventilation. Where reasonably practicable this should be achieved by the use of local exhaust ventilation and goodgeneral extraction. Spray mist contains all substances of the product and must not be inhaled. OELs are taken fromthe current version of EH40 (by Health & Safety Executive, UK).

RESPIRATORY PROTECTIONWhen use of roller or brush, then charcoal filter is sufficient. Use respiratory protective mask with charcoal anddust filter (A2/P2) when spraying this product.


HAND PROTECTIONUse Viton gloves.Barrier creams may help to protect exposed areas of the skin but are not substitutes for fullphysical protection. Never apply barrier cream to contaminated skin.

PROTECTIVE CLOTHINGWear anti-static clothing made of natural fibre or of heat resistant synthetic fibre.When spraying use suit coveringthe whole body.


Physical State: Liquid.Colour: Various.Odour: Organic solvent.Solubility: Organic solvent.Melting point/range: - Density: 1,55Expl. limit LEL-UEL%: 1,1 - 11.3 Solubility in water:

Vapour pressure: Saturation conc.:

Decomposition temp.: Rel. dens. sat. air (air=1):

pH solution: Boiling point/range: 118 - 144ºC

Flash point: 25ºC pH concentrate: -Molar weight: Viscosity:

Ignition temp.: 287ºC Odour threshold value:

Rel.vap.dens.(air=1): Rel. evap. velocity:

Air reactive: Water reactive:






: 4/6


HAZARDOUS DECOMPOSITION PRODUCTSIn a fire, hazardous decomposition products such as smoke, carbon monoxide, carbon dioxide and oxides ofnitrogen may be produced.Produktet kan avspalte sm† mengder formaldehyd under herdeprosessen.




SKIN CONTACTRepeated or prolonged contact with the product may lead to removal of natural fats from the skin resulting in non-allergic contact dermatitis and absorption through the skin. Repeated or prolonged contact with skin may causesensitation.



CARCINOGENICITYThe product contains ethylbenzene. IARC has classified it as a possible human carcinogen (Group 2B) based onsufficient evidence for carcinogenicity in experimental animals, but inadequate evidence for cancer in exposedhumans.




GENERAL REGULATIONSWastes, including emptied containers, are controlled wastes and should be disposed of in accordance withregulations made under the Control of Pollution Act and the Environmental Protection Act. Do not allow into drainsor water courses. Waste must be disposed of at approved landfill/waste storage or traement facility.

CATEGORY OF WASTE08 01 02 Waste paints and varnish free of halogenated solvents. 08 00 00 WASTES FROM THEMANUFACTURE, FORMULATION, SUPPLY AND USE (MFSU) OF COATINGS (PAINTS, VARNISHESAND VITREOUS ENAMELS), ADHESIVE, SEALANTS AND PRINTING INKS.




: 5/6


PROPER SHIPPING NAME PAINTToll. reg. no:

HAZCHEM(Y=black,y=white):

ADR(Road)


Class 3, PGIII Label 3Haz. ID No. 30 Marge No.

RID (Railway)


Class 3, PGIII Label 3Haz. ID No. 30

IMDG(Sea)


Class 3 Label 3Pkg Gr III EmSMFAG Marine Pollutant

Sub Risk Page

IATA(Air)


Class 3 Sub Risk

Label flamm. liq. Pkg Gr III

Transport only in accordance with ADR for road, RID for rail, IMDG for sea transport and IATA for airtransport.ADR/RID: Not restricted, ref. chapter 2.2.3.1.5 (applicable to receptacles of <450 litre capacity). IMDG: Notrestricted, ref. chapter 2.3.2.5 (applicable to receptacles of <450 litre).


Classif.:

Harmful


R-PHRASESR10 Flammable. R20/21 Harmful by inhalation and in contact with skin. R36/38 - Irritating to eyes and skin.




ISSUED: 03.05.2002




: 6/6

VENDOR NOTESPersons with epoxy allergic reactions, should not work with this kind of products. The information contained inthis MSDS is based on the present state of knowledge and current national legislation. As the specific conditions ofuse of the product are outside the supplier's control, the user is responsible for ensuring that the requirements ofrelevant legislation are compiled with. The information in this MSDS provides guidance on health, safety andenvironmental aspects of the product and should not be construed as any guarantee of technical performance orsuitability for particular applications. The Environmental Protection (Duty of Care) Regulations 1992 (SI1992:2839). Further information and relevant advice can be found in: The Control of Substances Hazardous toHealth Regulations 1988 (SI1988:1657). The Highly Flammable Liquids and liquefied Petroleum GasesRegulations 197 (SI 1972:917). The Manual Handling Operations Regulations 1992 (SI 1992:2793). Storage ofFlammable Liquids in Containers, HS(G)51. Storage of Packaged Dangerous Substances, HS(G)71. The selection,use and maintenance of respiratory protective equipment: A practical guide HS(G)53.



CORROGUARD STAYER - COMP. A

: 1/6


Approved for use



TRADE NAME CORROGUARD STAYER - COMP. AAPPLICATION Two-pack high molecular epoxy paint.FORMULA .

ART No. PM3442






2 N-BUTANOL 71-36-3 2,5-10 Xn 10-22-37/38-41-67




Harmful




INHALATION




: 2/6














HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Allways use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area.For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty thecontainer, it is not a pressure vessel. Electrical equipment should be protected to appropriate standards. The ManualHandling Operations Regulations may apply to the handling of containers of this product. Smoking, eating anddrinking are forbidden in the work area.




: 3/6




OEL value(short term)

TLVyear


N-BUTANOL 71-36-3 154,0 mg/m3;Sk -

EXPOSURE CONTROLPersons with allergic reactions to epoxy should not work with epoxy containg products. Provide adequateventilation. Where reasonably practicable this should be achieved by the use of local exhaust ventilation and goodgeneral extraction. Spray mist contains all substances of the product and must not be inhaled. OELs are taken fromthe current version of EH40 (by Health & Safety Executive, UK).



HAND PROTECTIONUse Viton gloves.Barrier creams may help to protect exposed areas of the skin but are not substitutes for fullphysical protection. Never apply barrier cream to contaminated skin.



Physical State: Liquid.Colour: Various.Odour: Organic solvent.Solubility: Organic solvent.Melting point/range: - Density: 1,54Expl. limit LEL-UEL%: 1,1 - 11.3 Solubility in water:




Flash point: 25ºC pH concentrate: -Molar weight: Viscosity:

Ignition temp.: 287ºC Odour threshold value:








: 4/6


HAZARDOUS DECOMPOSITION PRODUCTSIn a fire, hazardous decomposition products such as smoke, carbon monoxide, carbon dioxide and oxides ofnitrogen may be produced.Produktet kan avspalte sm† mengder formaldehyd under herdeprosessen.












CATEGORY OF WASTE08 01 02 Waste paints and varnish free of halogenated solvents. 08 00 00 WASTES FROM THEMANUFACTURE, FORMULATION, SUPPLY AND USE (MFSU) OF COATINGS (PAINTS, VARNISHESAND VITREOUS ENAMELS), ADHESIVE, SEALANTS AND PRINTING INKS.




: 5/6




ADR(Road)



RID (Railway)



IMDG(Sea)



Sub Risk Page

IATA(Air)


Class 3 Sub Risk




Classif.:

Harmful






ISSUED: 03.05.2002




: 6/6




CORROGUARD - COMP. B

1/5


Approved for use



TRADE NAME CORROGUARD - COMP. BAPPLICATION Two-pack high molecular epoxy paint.FORMULA

ART No. PM3444









Harmful








2/5













HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Allways use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area.For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty thecontainer, it is not a pressure vessel. Electrical equipment should be protected to appropriate standards. The ManualHandling Operations Regulations may apply to the handling of containers of this product.

STORAGEStore in accordance with the regulations for flammable materials. Observe the label precautions. Store in a dry, coldand well ventilated place away from sources of heat, ignition and direct sunlight. Store separately from oxidisingagents and strongly alkaline and strongly acidic materials. No smoking. Containers which are opened should be




3/5

properly resealed and kept upright to prevent leakage.



OEL VALUE(short term)

TLV year


EXPOSURE CONTROLProvide adequate ventilation. Where reasonably practicable this should be achieved by the use of local exhaustventilation and good general extraction. Resperatory protection are to be used when the concentation ofsolvents/compounds exceeds the Occupational Exposure LimitSpray mist contains all substances of the product andmust not be inhaled. OELs are taken from the current version of EH40 (by Health & Safety Executive, UK).






Physical State: Liquid.Colour: Brownish.Odour: Organic solvent.Solubility: Organic solvent.Melting point/range: - Density: 0.95Expl. limit LEL-UEL%: 1,1 - 7,0 Solubility in water:




Flash point: 25ºC pH concentrate: -Molar weight:9 Viscosity:

Ignition temp.: 525°C Odour threshold value:






HAZARDOUS DECOMPOSITION PRODUCTSIn a fire, hazardous decomposition products such as smoke, carbon monoxide, carbon dioxide and oxides of




4/5

nitrogen may be produced.












CATEGORY OF WASTE08 00 00 WASTES FROM THE MANUFACTURE, FORMULATION, SUPPLY AND USE (MFSU) OFCOATINGS (PAINTS, VARNISHES AND VITREOUS ENAMELS), ADHESIVE, SEALANTS ANDPRINTING INKS. 08 01 02 Waste paints and varnish free of halogenated solvents.




ADR(Road)






5/5

RID (Railway)



IMDG(Sea)



Sub Risk Page

IATA(Air)


Class 3 Sub Risk




Classif.:

Harmful






ISSUED: 03.05.2002




CORROGUARD HB - COMP. A

1/6


Approved for use



TRADE NAME CORROGUARD HB - COMP. AAPPLICATION Two-pack high molecular epoxy paint.FORMULA .

ART-NO PM3363




1 XYLENE, mixed isomers 1330-20-7 10-25 N Xn,10-20/21-382 N-BUTANOL 71-36-3 2,5-10 N Xn,10-22-37/38-41-67




Harmful


4. FIRST AID

GENERAL




2/6



















3/6

and open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area.For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty thecontainer, it is not a pressure vessel. Electrical equipment should be protected to appropriate standards. The ManualHandling Operations Regulations may apply to the handling of containers of this product. Smoking, eating anddrinking are forbidden in the work area.



Ingredients name CAS-no OEL value (long-term) OEL value (short-term) OELXYLENE, mixed isomers 1330-20-7 441,0 mg/m3,Sk 662,0 mg/m3,Sk

N-BUTANOL 71-36-3 154,0 mg/m3;Sk -




HAND PROTECTIONUse Viton gloves. Barrier creams may help to protect exposed areas of the skin but are not substitutes for fullphysical protection. Never apply barrier cream to contaminated skin.





4/6


Form Liquid.Colour Various.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 1,53Expl. limit LEL-UEL., %-%: 1,1 - 11.3 Solubility in water











HAZARDOUS DECOMPOSITION PRODUCTSIn a fire, hazardous decomposition products such as smoke, carbon monoxide, carbon dioxide and oxides ofnitrogen may be produced.Produktet kan avspalte små mengder formaldehyd under herdeprosessen.






INGESTIONAccidental ingestion may cause vomiting and abdominal pains. Risk of chemical pneumonia. Absorbed by thegastric intestinal system. May cause liver and kidney damage.




5/6




13. DISPOSAL


WASTEGROUP08 01 02 Waste paints and varnish free of halogenated solvents. 08 00 00 WASTES FROM THEMANUFACTURE, FORMULATION, SUPPLY AND USE (MFSU) OF COATINGS (PAINTS, VARNISHESAND VITREOUS ENAMELS), ADHESIVE, SEALANTS AND PRINTING INKS.



HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk


GENERALTransport only in accordance with ADR for road, RID for rail, IMDG for sea transport and IATA for airtransport.Not ADR-restricted ref. NOTE under E of marginal 2301, and according to IMDG, ref. chapter 2.3.2.5. (applicableto receptacles of less than 450 litres capacity).





6/6

Classification

Harmful






PRINTEDOUT:

05/09/2001




CORROGUARD HB - COMP. B

1/6


Approved for use



TRADE NAME CORROGUARD HB - COMP. BAPPLICATION Two-pack high molecular epoxy paint.

ART-NO PM3364




1 XYLENE, mixed isomers 1330-20-7 25-50 N Xn,10-20/21-38




Harmful


4. FIRST AID


INHALATION




2/6














HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Always use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area. For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty the




3/6








HAND PROTECTIONUse Viton gloves. Barrier creams may help to protect exposed areas of the skin but are not substitutes for fullphysical protection. Never apply barrier cream to contaminated skin.



Form Liquid.Colour Brownish.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 0.95Expl. limit LEL-UEL., %-%: 1,1 - 7,0 Solubility in water












4/6









INGESTIONAccidental ingestion may cause vomiting and abdominal pains. Risk of chemical pneumonia. Absorbed by thegastric intestinal system. May cause liver and kidney damage.




13. DISPOSAL






5/6



HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk

Label flamm. liq. Packaging group III



Classification

Harmful









6/6

PRINTEDOUT:

05/09/2001


Technical DataCROMOPRIMER

Product descriptionCromoprimer is an alkyd based primer. It does not contain chromates. This product is part of a complete system which is certified not to spread surface flames.

Recommended useAs a primer for steel structures as part of a suitable alkyd system. Good adhesion to correctly pretreated aluminium. Dries quickly and is resistant against dry heat up to 120°C.



17,3 10,4 13

Physical propertiesColour YellowSolids (vol %)* 52 ± 2 Flash point 36ºC ± 2 (Setaflash)Gloss FlatFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation






Condition during applicationThe temperature of the substrate should be minimum 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate.

CROMOPRIMER Page 1




Application data Thinner/Cleaner Jotun Thinner No. 2Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi).Nozzle tip 0.38-0.53 mm (0.015-0.021")Spray angle 40-80°Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 4 h 3,5 h 2,5 h 1 hThrough dry 28 h 22 h 6 h 4 hDry to recoat, minimum 28 h 22 h 16 h 10 h




Typical paint systemCromoprimerPilot IPilot II

2 x 40 µm1 x 40 µm1 x 40 µm





CROMOPRIMER Page 2

Packing size5 l , 20 l Packing may vary from country to country according to local requirements.










CROMOPRIMER Page 3

Technical DataEPOXY HOLDING PRIMER

Product descriptionEpoxy Holding Primer is a two-pack epoxy-based quick-drying primer.

Recommended useFor temporary protection of blast-cleaned steel.



16,7 8,3 12,5

Physical propertiesColour RedSolids (vol %)* 25 ± 2 Flash point -5ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance Very goodSolvent resistance Good Flexibility Good


Surface preparation




EPOXY HOLDING PRIMER Page 1




Application data Mixing ratio (volume) 18 parts of Comp. A (base) thoroughly mixed with 0,5 parts Comp.

B (curing agent).Pot life (23°C) 24 - 36 hours (Reduced at higher temp.). Thinner/Cleaner Jotun Thinner No. 3/17

(No. 3 - Fast evaporation) - (No. 17 - Slow evaporation).Guiding data airless sprayPressure at nozzle 10-15 MPa (100 kp/cm² 1500 psi).Nozzle tip 0.38-0.53 mm (0.015-0.021").Spray angle 40-95°Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 15 min 10 min 1-3 min 0,3-0,6 minThrough dry 20 min 15 min 4 min 1-2 minCured 21 d 14 d 7 d 3 d



1 The surface should be free from any contamination prior to application of the subsequent coat


Typical paint systemEpoxy Holding Primer 1 x 20 µm (Dry Film Thickness)

Normally overcoated with systems based on chlorinated polymers,vinyl or epoxy.Other systems may be specified, depending on area of use




Packing size18 l Comp. A and 0,5 l Comp. B.Packing may vary from country to country according to local requirements.











Technical DataFUTURA AS

Product descriptionFutura AS is a two-pack polyurethane topcoat with excellent gloss and colour retention. No maximum overcoating interval.

Recommended useAs topcoat over an epoxy/epoxy mastic system where a glossy finish is required. Cures at low temperatures.



15,7 9,4 11,8

Physical propertiesColour Available in white and colours tinted from Multicolour Industry

tinting system (MCI) base 1-2-3 as well as a limited number of std. marine colours.

Solids (vol %)* 47 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss GlossyGloss retention Very goodWater resistance Very goodAbrasion resistance Very goodSolvent resistance Good Chemical resistance Good Flexibility Very good


Surface preparation




FUTURA AS Page 1




Application data Mixing ratio (volume) 9 parts of Comp. A (base) to 1 part Comp. B (curing agent)Pot life (23°C) 4 hours (Reduced at higher temperature). Thinner/Cleaner Jotun Thinner No. 10 For hot climate and need of slower

evaporation, use Jotun Thinner No. 25.Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi).Nozzle tip 0.33 - 0.46 mm (0.013 - 0.018"). Spray angle 40 - 80°Filter Check to ensure that filters are clean.Note Depending on working condition, temperature, application

equipment etc., it may be necessary to adjust the viscosity by adding from 0 up to 10% Jotun Thinner No. 10. For hot climate and need of slower evaporation, use Jotun Thinner No. 25.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 0°C 5°C 10°C 23°C 40°CSurface dry 4 h 2 h 1 h 0,5 h 0,5 hThrough dry 20 h 10 h 6 h 3 h 1,5 hCured 20 d 15 d 10 d 5 d 2 d

Dry to recoat, minimum 12 h 10 h 6 h 3 h 1,5 h


1 The surface must be free from any chalking or any other contamination and if necessary, sufficiently roughened prior to application.


Typical paint systemJotamastic 87Futura AS

1 x 250 µm1 x 40 µm



FUTURA AS Page 2



Packing size18 ltr Comp A, 2 ltr Comp B4,5 ltr Comp A, 0.5 ltr Comp BPacking may vary from country to country according to local requirements.










FUTURA AS Page 3

Technical DataHARDTOP AS

Product descriptionHardtop AS is a two-pack polyurethane topcoat with excellent gloss and colour retention.

Recommended useAs topcoat over an epoxy/epoxy mastic system where a durable, high gloss finish is required in aggressive atmospheric exposure. Cures at low temperatures.



16,7 10 12,5

Physical propertiesColour According to colour card and Multicolour tinting system (MCI)Solids (vol %)* 50 ± 2 Flash point 26ºC ± 2 (Setaflash)Gloss GlossyGloss retention ExcellentWater resistance Very goodAbrasion resistance Very goodSolvent resistance Very good Chemical resistance Very good Flexibility Very good


Surface preparation




HARDTOP AS Page 1




Application data Mixing ratio (volume) 4 parts of Comp. A (base) to 1 part Comp. B (curing agent).Pot life (23°C) 4 hours (Reduced at higher temp.). Thinner/Cleaner Jotun Thinner No. 10Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi).Nozzle tip 0.33-0.46 mm (0.013-0.018").Spray angle 40-80° Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 0°C 5°C 10°C 23°C 40°CSurface dry 8 h 4 h 2 h 1 h 0,5 hThrough dry 40 h 30 h 16 h 8 h 4 hCured 20 d 15 d 10 d 5 d 2 d

Dry to recoat, minimum 24 h 18 h 10 h 5 h 2,5 h




Typical paint systemJotamastic 87Hardtop AS

2 x 150 µm1 x 50 µm



HARDTOP AS Page 2



Packing size16 l Comp. A and 4 l Comp. B. 4 l Comp. A and 1 l Comp. B.Packing may vary from country to country according to local requirements.










HARDTOP AS Page 3

Technical DataHARDTOP HB

Product descriptionHardtop HB is a two-pack semigloss polyurethane topcoat with excellent colour retention.

Recommended useAs topcoat over an epoxy/epoxy mastic system where a durable, high grade finish is required in aggressive atmospheric exposure. Cures at low temperatures.



8,3 5 6,3

Physical propertiesColour Available in white and colours tinted from Multicolour tinting

system (MCI)Solids (vol %)* 50 ± 2 Flash point 26ºC ± 2 (Setaflash)Gloss SemiglossGloss retention ExcellentWater resistance Very goodAbrasion resistance Very goodSolvent resistance Very good Chemical resistance Very good Flexibility Very good


Surface preparation




HARDTOP HB Page 1




Application data Mixing ratio (volume) 4 parts of Comp. A (base) to 1 part Comp. B (curing agent).Pot life (23°C) 4 hours (Reduced at higher temp.). Thinner/Cleaner Jotun Thinner No. 10Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi).Nozzle tip 0.46-0.58 mm (0.018-0.023").Spray angle 40-80° C Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 0°C 5°C 10°C 23°C 40°CSurface dry 16 h 8 h 4 h 2 h 1 hThrough dry 50 h 35 h 20 h 10 h 5 hCured 20 d 15 d 10 d 5 d 2 d

Dry to recoat, minimum 30 h 21 h 12 h 6 h 3 h




Typical paint systemJotamastic 87Hardtop HB

1 x 250 µm1 x 80 µm



HARDTOP HB Page 2



Packing size16 l Comp. A and 4 l Comp. B Packing may vary from country to country according to local requirements.










HARDTOP HB Page 3

Technical DataHARDTOP AS ME

Product descriptionHardtop AS ME is a two-pack polyurethane topcoat with excellent gloss and colour retention.

Recommended useAs topcoat over an epoxy/epoxy mastic system where a durable, high gloss finish is required in aggressiveatmospheric exposure. Cures at low temperatures.



16,7 6,3 10



Surface preparation




HARDTOP AS ME Page 1





Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 4 h 2 h 1 h 0,5 hThrough dry 30 h 16 h 8 h 4 hCured 15 d 10 d 5 d 2 d

Dry to recoat, minimum 18 h 10 h 5 h 2,5 h





Typical paint systemJotamastic 87Hardtop AS ME

2 x 150 µm1 x 50 µm






Packing size16 Ltr. Comp. A and 4 Ltr. Comp. B. 4 Ltr. Comp. A and 1 Ltr. Comp. B.Packing may vary from country to country according to local requirements.













JOTAARMOUR AS - COMP. A

1/6


Approved for use



TRADE NAME JOTAARMOUR AS - COMP. AAPPLICATION Two-pack. modified epoxy based paint

ART-NO PM3419




1 EPOXY RESIN, LOW MOL. (MW<700) 25068-38-6 10-25 N XiN,36/38-43-51/532 XYLENE, mixed isomers 1330-20-7 10-25 N Xn,10-20/21-383 BENZYL ALCOHOL 100-51-6 1-2,5 N Xn,20/224 ISOBUTANOL 78-83-1 2,5-10 N Xn,10-37/38-41-67




Harmful

FLAMMABLE. HARMFUL BY INHALATION. IRRITATING TO EYES AND SKIN. MAY CAUSESENSITISATION BY SKIN CONTACT.For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL




2/6















HANDLING ADVICEAvoid any skin contact with products containing epoxy; they may cause allergic reactions. Vapours are heavier thanair and may spread along floors. Vapours may form explosive mixtures with air. Prevent the creation of flammableor explosive concentrations of vapour in air and avoid vapour concentration higher than the occupational exposurelimits. The product should not be used in vicinity of open flames or other sources of ignition. Use explosion-proofelectrical equipment. The product may charge electrostatically. Always use earth (ground) wire when transferringfrom one container to another. Personnel should wear anti-static clothing and footwear. Floors should be




3/6

electrically conductive. Keep container tightly closed. Exclude sources of heat, sparks and open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist. Smoking, eating anddrinking are forbidden in the work area.For personal protective equipment see Section 8. Always keep in containersmade of the same material as the supply container. Never use pressure to empty the container, it is not a pressurevessel. Electrical equipment should be protected to appropriate standards. The Manual Handling OperationsRegulations may apply to the handling of containers of this product. Smoking, eating and drinking are forbidden inthe work area.




ISOBUTANOL 78-83-1 154,0 mg/m3 231,0 mg/m3

EXPOSURE CONTROLPersons with allergic reactions to epoxy should not work with epoxy containing products. Provide adequateventilation. Where reasonably practicable this should be achieved by the use of local exhaust ventilation and goodgeneral extraction. Use respiratory protection when the concentration of solvents/compounds exceeds theOccupational Exposure Limit. Spray mist contains all substances of the product and must not be inhaled. OEL's aretaken from the current version of EH40 (by Health & Safety Executive, UK).



HAND PROTECTIONUse PVA/EVAL gloves. Barrier creams may help to protect exposed areas of the skin but are not substitutes for fullphysical protection. Never apply barrier cream to contaminated skin.





4/6


Form Liquid.Colour Various.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 1.48Expl. limit LEL-UEL., %-%: 1.1 - 10.9 Solubility in water













GENERALThere are no toxicological data available on the product itself. Based on the properties of the epoxyconstituents andconsidering toxicological data on similar preparations, this preparation may be a skin sensitizer and an irritant. Itcontains low molecular epoxy constituents which are irritating to eyes, mucous membrane and skin. Repeated skincontact may lead to irritation and to sensitisation, possibly with cross-sensitisation to other epoxies. Skin contactwith the preparation and exposure to spray mist and vapour should be avoided.


SKIN CONTACTRepeated or prolonged contact with the product may lead to removal of natural fats from the skin resulting in non-allergic contact dermatitis and absorption through the skin. Repeated or prolonged contact with skin may causesensitisation. Repeated skin contact may lead to irritation and sensitisation, possible with cross-sensitisation to otherepoxies. Allergic reactions may occur after short time exposure.


INGESTION




5/6

Absorbed by the gastric intestinal system. May cause liver and kidney damage. Accidental ingestion may causevomiting and abdominal pains. Risk of chemical pneumonia.



BREAKDOWNEpoxy resin, low mol. (MW<700): 12% (OECD 301B (mod.Sturm))

ECOTOXITYEpoxy resin, low mol. (MW<700):LC50 (Rainbow trout) = 1,5 mg/l (OECD 203)EC50 (Daphnia) = 3,6 mg/l (OECD 202)IC50 ( Resp. inhibition activated mud) > 100 mg/l (EEC(1998))

OTHER INFORMATIONThe product should not be allowed to enter drains or water courses or be deposited where it can affect ground orsurface waters. The product contains epoxy compounds labelled "Dangerous for the environment".

13. DISPOSAL





HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)




6/6


Class 3 Sub. risk

Label Flamm liq. Packaging group



Classification

Harmful

COMPOSITION EPOXY RESIN, LOW MOL. (MW<700) (10-25)

R-PHRASESR10 Flammable. R20 Harmful by inhalation. R36/38 - Irritating to eyes and skin. R43 May cause sensitization byskin contact.

S-PHRASESS23 Do not breathe vapour/spray. S24 Avoid contact with skin. S37-Wear suitable gloves. S38 In case ofinsufficient ventilation, wear suitable respiratory equipment. P92 Contains epoxy constituents - See informationsupplied by the manufacturer This information is supplied in the present MSDS.



PRINTEDOUT:

05/09/2001




JOTAARMOUR AS - COMP. B


Approved for use



TRADE NAME JOTAARMOUR AS - COMP. BAPPLICATION Two-pack. modified epoxy based paint

ART-NO PM3420




1 3-AMINOMETHYL-3,5,5-TRIMETHYLCYCLOHEXYLAMINE 2855-13-2 10-25 N C,21/22-34-43-52/532 BENZYL ALCOHOL 100-51-6 10-25 N Xn,20/223 2,2,4 TRIMETHYL HEXAMETHYLENE DIAMINE 25620-58-0 2,5-10 N C;A,22-34-43-52/53

Legend T+=Very toxic, T=Toxic, C=Corrosive, Xn=Harmful, Xi=Irritant, IK=No classification required, E=Explosive, O=Oxidising, F+=Extremely flammable, F=Very flammable, N=Dangerous for the environment, Muta=Mutagenic, Carc=Carcinogenic, Repr=Toxic for reproduction



Corrosive

HARMFUL IF SWALLOWED. CAUSES BURNS. MAY CAUSE SENSITISATION BY SKIN CONTACT. For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL

1 / 6



JOTAARMOUR AS - COMP. B In all cases of doubt, or when symptoms persist, seek medical attention. Obtain advice via telephone; before the patient is transported to a doctor or hospital. Never give anything by mouth to an unconscious person.


SKIN CONTACTRemove contaminated clothing. Wash skin thoroughly with soap and water or use an appropriate skin cleaner. Do NOT use solvents or thinners. Flush the skin with plenty of water.

EYE CONTACTRemove any contact lenses. Hold the eyelids apart. Rinse with lukewarm water for 1 hour. Seek immediately medical advice.

INGESTIONDO NOT INDUCE VOMITING. Drink water or milk/cream immediately. If accidentally swallowed obtain immediate medical attention. Keep at rest. Seek medical advice.

MEDICAL INFORMATION Regulary medical control. Person developing a skin rash are to be directed to a dermatologist for examination.Obtain miedical surveillance concerning burn injuries in mouth and throat. Aspiration hazard by vomiting. All poisoned persons should be transported in recovery position. An authorised person should acompany under the transport. Stomach-rinsing may bee considered, for instance with an antioxydant. Eye injuries should be treated with chloramphenicol or antiseptic eye treatment. Local anesthetica may be given to relieve pain.




PERSONAL PROTECTION WHEN FIREFIGHTINGThe personal protective equipment required is provided in section 8. Professional fire-fighters are required to use an air-fed system when dealing with major fires.



OTHER INFORMATIONAvoid breathing vapours. Refer to protective measures listed in sections 7 and 8. Contain and collect spillage with non-combustible absorbent materials, e.g. sand, earth, vermiculite and diatomaceous earth. Place in container for disposal according to local regulations (see section 13). Do not allow to enter drains or watercourses. Clean preferably with a detergent; avoid use of solvents. If the product enters drains or sewers, the local water company should be contacted immediately; in the case of contamination of streams, rivers or lakes, the Environmental Agency.


HANDLING ADVICEAvoid skin and eye contact. Avoid inhalation of vapour and spray mist. For personal protective equipment see Section 8. Never use pressure to empty the container, it is not a pressure vessel. Always keep in containers made of

2 / 6



JOTAARMOUR AS - COMP. B the same material as the supply container. The Manual Handling Operations Regulations may apply to the handling of containers of this product.

STORAGEKeep out of frost. Store in a dry, cold and well ventilated place away from sources of heat, ignition and direct sunlight. Observe the label precautions. Keep away from oxidizing materials, strongly alkaline materials and strong acids. No smoking. Containers which are opened should be properly resealed and kept upright to prevent leakage.


EXPOSURE CONTROLProvide adequate ventilation. Where reasonably practicable this should be achieved by the use of local exhaust ventilation and good general extraction. OEL's are taken from the current version of EH40 (by Health & Safety Executive, UK). Spray mist contains all substances of the product and must not be inhaled.

RESP. PROTECTIONWhen workers are facing concentrations above the occupational exposure limit they must use appropriate certified respirators.Use respiratory protective mask with charcoal and dust filter (A2/P2) when spraying this product. When spraying, use also K-filter.


HAND PROTECTIONUse butyl rubber/ viton gloves.Barrier creams may help to protect exposed areas of the skin but are not substitutes for full physical protection. Never apply barrier cream to contaminated skin.

SKIN PROTECTIONCotton or cotton/synthetic overalls or coveralls are normally suitable. Grossly contaminated clothing should be removed and the skin washed with soap and water or a proprietary skin cleaner. When spraying use suit covering the whole body.


Form Liquid. Colour Yellowish. Odour Organic solvent. Solubility Organic solvent. Melting point/range - Density 1,30Expl. limit LEL-UEL., %-%: 1,3 - 13,0 Solubility in water



pH Solution Boiling point/range 205ºCFlash point >100ºC pH concentrate -Molecular weight Viscosity








3 / 6






INHALATIONVapour may cause irritation of the respiratory organ and the lungs.

SKIN CONTACTProlonged contact may cause burn damage. Products containing amines irritate the skin and may lead to allegic ecema. The allergic response may occur after a short periode of contact.

EYE CONTACTCauses burns.Splashes in the eyes may cause irritation and possible risk of irreversible damage if the eyes are not flushed with plenty of water.

INGESTIONAccidental ingestion may cause vomiting and abdominal pains. May cause burn damage to mucous membrane, esophagus and stomach.


BREAKDOWN3-aminomethyl-3,5,5-trimethylcyclohexylamine:BOD (28d) = 8 %2,2,4-trimethylhexamethylendiamine: Not readily biodegradable.

ACCUMULATION3-aminomethyl-3,5,5-trimethylcyclohexylamine:

log Pow = 0,79Bioaccumulation: low

ECOTOXITY3-aminomethyl-3,5,5-trimethylcyclohexylamine:

Fish: LC50 (96 h) = 110 mg/l. LC0 (96 h) = 70 mg/l.Daphnia: EC50 (24 h) = 42 mg/l. NOEC (21 d) = 3 mg/l. EC10 (21d) = 10 mg/l.Algea: IC50 (72 h) = 37 mg/l. IC0 (72 h) = 1,5 mg/l.

3-aminomethyl-3,5,5-trimethylcyclohexylamine:Bacteria: Pseudomonas putida, incipient inhibition of cellbreeding at (18 h) = 1120 mg/l.

2,2,4-trimethylhexametylendiamine:Fish: LC50 (96 h) = 1000 mg/lDaphnia: EC50 (24 h) = 31,5 mg/lAlgea: EC50 (72 h) = 29,5 mg/lBacteria: IC50 (3 h) = 100 mg/l

OTHER INFORMATIONThe product should not be allowed to enter drains or water courses or be deposited where it can affect ground or surface waters. The product contains components which are harmful to aquatic organisms, see point 2.

13. DISPOSAL

Wastes, including emptied containers, are controlled wastes and should be disposed of in accordance with regulations made under the Control of Pollution Act and the Environmental Protection Act. Do not allow into drains or water courses. Waste must be disposed of at approved landfill/waste storage or treatment facility.

WASTEGROUP08 00 00 WASTES FROM THE MANUFACTURE, FORMULATION, SUPPLY AND USE (MFSU) OF COATINGS (PAINTS, VARNISHES AND VITREOUS ENAMELS), ADHESIVE, SEALANTS AND PRINTING INKS. 08 01 02 Waste paints and varnish free of halogenated solvents.

4 / 6





PROPER SHIPPING NAME AMINES, LIQUID, CORROSIVE, N.O.S.(isophorone diamine,2,2,4-trimethyl hexamethylene diamine.)

Toll. reg. no.HAZCHEM

ADR (Road)UN No. 2735 Dang. goods


RID (Railway)UN No. 2735 Dang. goods


IMDG (Sea)UN No. 2735 Dang. goods


Sub. risk Page

IATA (Airplane)UN No. 2735 Dang. goods

Class 8 Sub. risk




Classification

Corrosive

COMPOSITION 3-AMINOMETHYL-3,5,5-TRIMETHYLCYCLOHEXYLAMINE (10-25), 2,2,4 TRIMETHYL HEXAMETHYLENE DIAMINE (2,5-10)

R-PHRASESR22 Harmful if swallowed. R34 - Causes burns. R43 May cause sensitization by skin contact.

S-PHRASESS23 Do not breathe vapour/spray. S26 In case of contact with eyes, rinse immediately with plenty of water and seek medical advice.S36/37/39 Wear suitable protection clothing, gloves and eyes/face protection. S38 In case of insufficient ventilation, wear suitable respiratory equipment. S45 In case of accident or if you feel unwell, seek medical advice immediately (show the label where possible).



5 / 6



JOTAARMOUR AS - COMP. B PRINTED OUT:

05/09/2001

VENDOR NOTES The information contained in this MSDS is based on the present state of knowledge and current national legislation. As the specific conditions of use of the product are outside the supplier's control, the user is responsible for ensuring that the requirements of relevant legislation are compiled with. The information in this MSDS provides guidance on health, safety and environmental aspects of the product and should not be construed as any guarantee of technical performance or suitability for particular applications. The Environmental Protection (Duty of Care) Regulations 1992 (SI 1992:2839). Further information and relevant advice can be found in: The Control of Substances Hazardous to Health Regulations 1988 (SI1988:1657). The Highly Flammable Liquids and liquefied Petroleum Gases Regulations 197 (SI 1972:917). The Manual Handling Operations Regulations 1992 (SI 1992:2793). Storage of Flammable Liquids in Containers, HS(G)51. Storage of Packaged Dangerous Substances, HS(G)71. The selection, use and maintenance of respiratory protective equipment: A practical guide HS(G)53.

6 / 6


Last changed: 05/09/2001 Internal no.: Replaces date:

JOTAARMOUR AS - COMP. C


Approved for use



TRADE NAME JOTAARMOUR AS - COMP. CAPPLICATION

ART-NO PM3421






There are no riskphrases given for this product according to EU-legislation. For potential danger for the environment, see section 12.

4. FIRST AID

GENERALIn all cases of doubt, or when symptoms persist, seek medical attention.

INHALATIONKeep the patient warm in a quiet place with fresh air. Seek medical attention if significant amounts have been inhaled or if the patient is feeling any discomfort.

SKIN CONTACTIf clothing comes in contact with the product, they should be laundered before re-use. Wash with soap and water.

EYE CONTACTRemove any contact lenses. Hold the eyelids apart. Rinse immediately with plenty of water. Seek medical advice if symptoms persist.

INGESTIONSymptomatic treatment.Get medical advice if any discomfort develops.

1 / 4





PROPER FIREFIGHTING EQUIPMENTUse extinguishing media appropriate for surrounding fire.



SAFETY MEASUREMENTS TO PROTECT PERSONSRefer to protective measures listed in sections 7 and 8.

SAFETY MEASUREMENTS TO PROTECT ENVIRONMENTIf the product contaminates sea, lakes or drains, inform appropriate authorities in accordance with local regulations.

PROPER METHODS FOR DAMAGE LIMITATION AND CLEANUPCollect carefully in tightly closed containers. Avoid dust generation.

OTHER INFORMATIONCollect spill. See section 13.


HANDLING ADVICEAvoid the inhalation of dusts. Use personal protective equipment as specified in section 8.

STORAGEObserve the label precautions. Keep container dry. Keep container tightly closed.


EXPOSURE CONTROLProvide adequate ventilation.

RESP. PROTECTIONUse dust mast with dust filter P1.

EYE PROTECTIONWear dust-proof goggles if dust formation is possible.

HAND PROTECTIONUse resistant gloves.

SKIN PROTECTIONProtective clothing when necessary.

2 / 4





Form Powder. Colour Various. Odour None or uncharacteristic. Solubility Insoluble in: Water. Melting point/range Density 3,7-4,5Expl. limit LEL-UEL., %-%: - Solubility in water



pH Solution Boiling point/range

Flash point - pH concentrate -Molecular weight Viscosity -Ignition temp Smelling limits lo-hi





HAZARDOUS DECOMPOSITION PRODUCTSNot known.


INHALATIONDust may irritate respiratory tract and lungs.

SKIN CONTACTRepeated or prolonged contact causes drying of the skin.

EYE CONTACTDust in the eyes will cause mainly mechanical irritation.


MOBILITYIndissoluble in water.

ECOTOXITYNot known.

OTHER INFORMATIONNor expected to be harmful for the environment.

13. DISPOSAL

Do not allow into drains or water courses. Waste must be disposed of at approved receiving station.

3 / 4





PROPER SHIPPING NAMEToll. reg. no.HAZCHEM

ADR (Road)UN No. Dang. goods

Class Label

Haz. id. no Marginno.

RID (Railway)UN No. Dang. goods

Class Label

Haz..id.no

IMDG (Sea)UN No. Dang. goods

Class Label

Packaging group EmS

MFAG Marine Pollutant

Sub. risk Page

IATA (Airplane)UN No. Dang. goods

Class Sub. risk

Label Packaging group

GENERALTransport only in accordance with ADR for road, RID for rail, IMDG for sea transport and IATA for airtransport. The product is not classified as dangerous goods for carriage.


Classification

S-PHRASESS22 Do not breathe dust.


PRINTED OUT:

05/09/2001

VENDOR NOTES The information contained in this MSDS is based on the present state of knowledge and current national legislation. As the specific conditions of use of the product are outside the supplier's control, the user is responsible for ensuring that the requirements of relevant legislation are compiled with. The information in this MSDS provides guidance on health, safety and environmental aspects of the product and should not be construed as any guarantee of technical performance or suitability for particular applications.

4 / 4

Technical DataJOTAARMOUR AS

Product descriptionJotaArmour AS is a three-pack, abrasion-resistant, high solids epoxy-based coating formulated to be applied in high film thickness for durability, wear resistant and anti-slip properties under dry, wet and oily conditions. JotaArmour AS comprises a two-component surface tolerant, abrasion-resistant, high solids epoxy-based coating, incorporating selected particle sized blends of abrasion-resistant, fused, aluminium oxides as the third component.

Recommended useFor severe dry, wet and oily conditions requiring durability, wear resistance, anti-slip properties, such as flight decks, military applications, extreme environments. Approved to U.K. Defence Standard 80-134 for the Royal Navy. One-coat, high build application over surface tolerant anti-corrosive primer.



1,3 0,3 1

Comments* anti-slip roughness profile of coating limits accuracy on film thickness measurements.

Physical propertiesColour Limited range including Grey BS 640, Grey 38, BlackSolids (vol %)* 92 ± 2 Flash point 35ºC ± 2 (Setaflash)Gloss SemiglossGloss retention FairWater resistance Very goodAbrasion resistance ExcellentSolvent resistance Good Chemical resistance Very good Flexibility Good


Surface preparationCoated surfacesClean, dry and undamaged compatible primer. Contact your local Jotun office for more information.



Application methodsSpray Gravity Feed Hopper Gun or other suitable equipment. Consult Jotun for additional

information, as required.

Application data Mixing ratio (volume) 6 parts Comp. A to 1 part Comp. B to 10.5 parts Comp. C.Mixing 10 min. prior to useInduction time 10 minutes.Pot life (23°C) 2 hours (reduced at higher temperatures) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle Air pressure supply 4.0-4.5 bar VOC 200 gms./ltr. - ASTM D3960 - US

180 gms./ltr. - PG66/23 (97) - UK

Nozzle tip 8 mmSpray angle 45°Filter Remove filters.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 10°C 23°C 40°CSurface dry 8 h 4 h 2 hThrough dry 24 h 10 h 4 hCured 14 d 7 d 2 d



Provided the surface is free from chalking and other contamination prior to application, there 1.is normally no overcoating time limit. Best intercoat adhesion occurs, however, when the subsequent coat is applied before preceding coat has cured. If the coating has been exposed to direct sunlight for some time, special attention must be paid to surface cleaning and mattening/removal of the surface layer in order to obtain good adhesion.


Typical paint systemJotamastic 87 Alu Red Toned 1-2 x 150 µm (Dry Film Thickness)JotaArmour AS 1 x 1000 µm (Dry Film Thickness)


JOTAARMOUR AS Page 2



Packing size4.1 l Comp. A and 0.7 l Comp. B and 7 l Comp. C kit packed in 20 l mixing pail.Packing may vary from country to country according to local requirements.










JOTAARMOUR AS Page 3

Technical DataJOTABRIGHT ANTISTAIN

Product descriptionJotabright Antistain is a bright, non-yellowing acrylic topcoat, designed to control rust staining, and formulated for quick drying at low temperatures.

Recommended useExterior finishing coat for steel structures. Offering minimum maintenance costs. Corrosion control benefits maximised when used in combination with Jotamastic 87 or Pioner Primer.



11 5,5 11

Physical propertiesColour White and selected coloursSolids (vol %)* 44 ± 2 Flash point 37ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance GoodSolvent resistance Limited Chemical resistance Good Flexibility Good


Surface preparation





JOTABRIGHT ANTISTAIN Page 1

Application methodsSpray Use airless spray (thin 5%)Brush Recommended for stripe coating and small areas, care must be taken to achieve



Application data Thinner/Cleaner Jotun Thinner No. 7Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.46-0.66 mm (0.018-0.026")Spray angle 40-80°Filter Check to ensure that filters are clean.


Substrate temperature 5°C 10°C 23°C 40°CSurface dry 60 min 45 min 30 min 15 minThrough dry 10 h 9 h 7 h 4 hDry to recoat, minimum

1 5 h 4 h 2 h 1,5 h


1 In case of multi-coat application, drying times will be influenced by the number in sequence and by the total thickness of previous coat applied - reference is made to the corresponding system datasheet.



Typical paint system1) Jotamastic 87*Jotabright Antistain2) Pioner Primer*Jotabright Antistain

1 x 250 µm1-2 x 40 µm2 x 75 µm1-2 x 40 µm

(Dry Film Thickness)(Dry Film Thickness)(Dry Film Thickness)(Dry Film Thickness)

*) Single coat Jotabright Antistain requires appropriate primer shade.Other systems may be specified, depending on area of use




Packing size20 l and 5 l.Packing may vary from country to country according to local requirements.













JOTABUILD HB - COMP. A

1/6


Approved for use



TRADE NAME JOTABUILD HB - COMP. AAPPLICATION Two-pack. epoxyprimer

ART-NO PM3360




1 EPOXY RESIN, LOW MOL. (MW<700) 25068-38-6 10-25 N XiN,36/38-43-51/532 BENZYL ALCOHOL 100-51-6 2,5-10 N Xn,20/223 XYLENE, mixed isomers 1330-20-7 2,5-10 Xn,10-20/21-38

4 1-METHOXY-2-PROPANOL 107-98-2 2,5-10 N 105 ISOBUTANOL 78-83-1 1-2,5 N Xn,10-37/38-41-67




Irritating

FLAMMABLE. IRRITATING TO EYES AND SKIN. MAY CAUSE SENSITISATION BY SKIN CONTACT.For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL




2/6



















3/6

electrically conductive. Keep container tightly closed. Exclude sources of heat, sparks and open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist. Smoking, eating anddrinking are forbidden in the work area.For personal protective equipment see Section 8. Always keep in containersmade of the same material as the supply container. Never use pressure to empty the container, it is not a pressurevessel. Electrical equipment should be protected to appropriate standards. The Manual Handling OperationsRegulations may apply to the handling of containers of this product.














4/6
















INHALATIONExposure to organic solvent vapours may result in adverse health effects such as irritation of the mucous membraneand the respiratory system and adverse effects on the renal and central nervous system. Symptoms and signs includeheadache; dizziness, fatigue, muscular weakness, drowsiness and in extreme cases, loss of consciousness.Inhalation of vapours from organic solvents may lead to nausea, vomiting and headache.






5/6

INGESTIONAbsorbed by the gastric intestinal system. May cause liver and kidney damage. Accidental ingestion may causevomiting and abdominal pains. Risk of chemical pneumonia. The swallowing of large quantities not expected dueto shape of the product.






13. DISPOSAL





HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)






6/6

Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk




Classification

Irritating


R-PHRASESR10 Flammable. R36/38 - Irritating to eyes and skin. R43 May cause sensitisation by skin contact.

S-PHRASESS23 Do not breathe vapour/spray. S24 Avoid contact with skin. S37-Wear suitable gloves. S38 In case ofinsufficient ventilation, wear suitable respiratory equipment. P92 Contains epoxy constituents - See informationsupplied by the manufacturer. This information is supplied in the present MSDS.



PRINTEDOUT:

21/08/2001




JOTABUILD HB - COMP. B

1/6


Approved for use



TRADE NAME JOTABUILD HB - COMP. BAPPLICATION Two-pack. epoxyprimer

ART-NO PM3361




1 XYLENE, mixed isomers 1330-20-7 10-25 Xn,10-20/21-38

2 ISOBUTANOL 78-83-1 2,5-10 N Xn,10-37/38-41-673 2,4,6-TRIS(DIMETHYLAMINOMETHYL)PHENOL 90-72-2 2,5-10 N Xn,22-36/384 3,6-DIAZAOCTANETHYLENEDIAMIN 112-24-3 2,5-10 N C,21-34-43-52/53




Harmful

FLAMMABLE. HARMFUL BY INHALATION AND IN CONTACT WITH SKIN. IRRITATING TO EYESAND SKIN. MAY CAUSE SENSITISATION BY SKIN CONTACT.For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL




2/6






MEDICAL INFORMATION Risk of chemical pneumonia by aspiration. Keep attention: danger of lung damage. General health examination.Professional evaluation of the work station. Person developing a skin rash are to be directed to a dermatologist forexamination.













3/6














4/6


Form Liquid.Colour Yellowish.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 0,95Expl. limit LEL-UEL., %-%: 1,1 -9,3 Solubility in water















SKIN CONTACTRepeated or prolonged contact with the product may lead to removal of natural fats from the skin resulting in non-allergic contact dermatitis and absorption through the skin. Repeated or prolonged contact with skin may causesensitisation. Products containing amines irritates the skin and may lead to allergic eczema.The allergic responsemay occur after a short periode of contact.



CANCER




5/6



OTHER INFORMATIONThe product should not be allowed to enter drains or water courses or be deposited where it can affect ground orsurface waters. The product contains components which are harmful to aquatic organisms, see point 2.

13. DISPOSAL





HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk

Label Flamm liq. Packaging group III






6/6

Classification

Harmful

COMPOSITION ISOBUTANOL (2,5-10), 3,6-DIAZAOCTANETHYLENEDIAMIN (2,5-10)

R-PHRASESR10 Flammable. R20/21 Harmful by inhalation and in contact with skin. R36/38 - Irritating to eyes and skin. R43May cause sensitisation by skin contact.




PRINTEDOUT:

21/08/2001


Technical DataJOTABUILD HB

Product descriptionJotabuild HB is a high solid, high build, two-pack polyamide cured epoxy coating.

Recommended useAnticorrosive epoxy primer/intermediate coat for steel structures. It can be applied on to bare steel or a suitable primer/shopprimer



7,6 3,8 5,1

Physical propertiesColour Grey, Red, WhiteSolids (vol %)* 76 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss FlatGloss retention FairWater resistance GoodAbrasion resistance Very goodSolvent resistance Very good Chemical resistance Very good Flexibility Good


Surface preparation





Other surfaces

JOTABUILD HB Page 1


Condition during applicationThe temperature of the substrate should be minimum 20ºC and minimum 3ºC above the dew point of the air. The temperature and the relative humidity should be measured in the vicinity of the substrate. Jotabuild HB should not be exposed to water, chemicals or mechanical stress before the paint is fully cured.

Application methods

Mixing ratio (volume) 3 parts Comp. A (base) to be mixed thoroughly with 1 part Comp. B (curing agent)

Pot life (23°C) 3½ hours. (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 25 MPa (250 kp/cm² 4000 psi)Nozzle tip 0.46 - 0.69mm (0.018-0.027")Spray angle 40 - 80°Filter Check to ensure that filters are clean.


Substrate temperature 25°C 40°CSurface dry 3,5 h 1.5 hThrough dry 12 h 4 hCured 7 d 3 d



1 Recommended data given for recoating with the same generic type of paint.2 Provided the surface is free from chalking and other contamination prior to application, there

is normally no overcoating time limit. Best intercoat adhesion occurs, however, when the subsequent coat is applied before preceding coat has cured. If the coating has been exposed to direct sunlight for some time, special attention must be paid to surface cleaning and mattening/removal of the surface layer in order to obtain good adhesion


Typical paint system

On bare steel or shopprimer.Jotabuild HB 2 x 150 µm (Dry Film Thickness)Polyurethane or epoxy topcoat 1 x 50 µm (Dry Film Thickness)Other systems may be specified, depending on area of use

JOTABUILD HB Page 2


Packing size12 Ltr. Comp. A (base) and 4 Ltr. Comp. B (curing agent) Packing may vary from country to country according to local requirements.









ISSUED 24 MAY 2002 BY JOTUN PAINTSTHIS DATA SHEET SUPERSEDES THOSE PREVIOUSLY ISSUED

JOTABUILD HB Page 3

Technical DataJOTACOTE 412

Product descriptionA high build, solvent free, two pack cycloaliphatic amine adduct cured epoxy coating.

Recommended useProtection of steel, concrete and masonry surfaces in hygienic locations such as food

processing plants,potable water storage tanks and storage of edible products suitable for use as a tank

lining for a wide range of petroleum products - contact Jotun for specific recommendations.



5 2 4

Physical propertiesColour Black, Red oxide, White and greenSolids (vol %)* 100 ± Flash point >100ºC (Setaflash)Gloss GlossyWater resistance ExcellentAbrasion resistance Very goodSolvent resistance Very good Chemical resistance Very good Flexibility Good


Surface preparationBare steelCleanliness: Blast cleaning to min. Sa 2 ½ (ISO 8501-1:1988) or for maintenance UHPWJ to WJ2 (NACE No.5/SSPC-SP 12). Roughness: using abrasives suitable to achieve grade Fine to Medium G (30-85 µm, Ry5) (ISO 8503-2)


Condition during applicationFor steel substrate: The temperature of the substrate should be minimum 10°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. For Concrete: The moisture content in the concrete should not exceed 4 % (by weight). The coating should not be exposed to oil, chemicals or mechanical stress until fully

JOTACOTE 412 Page 1

cured.

Application methodsSpray Use airless sprayBrush Recommended Roller Recommended

Application data Mixing ratio (volume) 2 parts Comp. A (base) to be mixed throughly withh 1 part Comp. B

(curing agent). Pot life (23°C) 1 hour (reduced at higher temperature). Thinner/Cleaner Jotun Thinner No. 4 / Jotun Thinner No. 17 Guiding data airless sprayPressure at nozzle Pressure at nozzle: 25 - 35 MPa (3600 - 5000 p.s.i.)Nozzle tip 0.53 mm - 0.65 mm (0.021” - 0.026”)Spray angle 40° - 80°Filter Min. 60 mesh recommended, check to ensure filter is clean.


Substrate temperature 10°C 23°C 40°CSurface dry 15 h 6 h 1.5 hThrough dry 30 h 12 h 4 hCured 15 d 7 d 4 d


Dry to recoat, maximum 96 h 48 h 18 h


Typical paint systemJotacote 412 2 x 250 microns (Dry Film Thickness)Other systems may be specified, depending on area of use

StorageThe product must be stored in accordance with national regulations. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed.


JOTACOTE 412 Page 2

Packing size

13.3 Ltr. component A, 6.7 Ltr.. component B2.67 Ltr. component A, 1.33 Ltr. component B.











JOTACOTE 412 Page 3

Technical DataJOTACOTE 5

Product descriptionJotacote 5 is a two-pack, water borne inorganic zinc rich silicate primer. Can be applied in high film thickness.

Recommended useAs protection on blast cleaned steel. Can be used alone and also overcoated with water borne coatings, as well as with suitable solvent borne coatings, such as epoxy and others. Not to be overcoated with alkyds. Jotacote 5 can also be used as a one coat system for interior tanks. A separate resistance list is available.

Film thickness and spreading rateMinimum Maximum Typical Typical for

immersion services:

Film thickness, dry (µm) 50 200 75 125Film thickness, wet (µm) 75 300 110 190Theoretical spreading rate (m²/l)

13,4 3,4 8,9 5,4

CommentsVOC: 0 g/l (Actual).There is a risk of mud cracking if the dry film thickness exceeds 250 µm

Physical propertiesColour GreySolids (vol %)* 67 ± 2 Flash point Non flammableGloss FlatWater resistance Very goodAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent within pH range of 6-10Flexibility Limited


Surface preparation




JOTACOTE 5 Page 1

Condition during applicationThe temperature of the substrate should be minimum 5°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to ensure proper drying. Use mistcoat technique for subsequent coat to avoid popping (pinholes). If possible avoid application at relative humidity below (30%) due to risk of dry spraying.

Application methodsSpray Conventional spray. (for example, Wiwa high pressure pump R/F/W-G-34020).Brush Recommended for stripe coating and small areas, care must be taken to achieve


Application data Mixing ratio (volume) 25 kg Comp. B (Zinc powder) to be sifted slowly into 7 kg Comp. A

(Silicate solution) and mixed thoroughly. It is recommended to pass the mixture through a 60 mesh sieve before use.

Pot life (23°C) 5 hours. Thinner/Cleaner Fresh water.Guiding data airless sprayNozzle tip 1.8 - 2.2 mm (0.71” - 0.87”)Note With Jotacote 5 it is recommended to flush the system with Jotun

thinner No. 4 and then circulate water through the spraying equipment for some minutes before application. After the paintwork is finished, flush the system with water. During painting it is necessary to continuously stir the paint with a mechanical stirrer.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate* Relative humidity < = 70%

Substrate temperature 10°C 23°C 40°CSurface dry 20 min 15 min 10 minThrough dry 40 min 30 min 20 minCured 20 d 10 d 5 d



JOTACOTE 5 Page 2


Jotacote 5WaterFine SpecialWaterFine SpecialWaterFine Topcoat

1 x 75 µm1 x 60 µm1 x 60 µm1 x 50 µm


FOR INTERIOR OF TANKS OR SINGLE COAT SYSTEM: Jotacote 5 1 x 125 µm (Dry Film Thickness)


Complete curing:When the Jotacote 5 is used as a one coat system for the interior of tanks the paint must be completely cured before the tank is put into service. In order to achieve this the following procedures can be used:

Apply 125 µm Jotacote 5.l

Let the paint dry/cure with good ventilation and low humidity until minimum recoating time is l

reached.Spray water (seawater is preferred) on the coating and leave the tank closed. Repeat the l

waterspraying 3 - 4 times during a 48 hours period.Remove the water and let the tank dry. l

Procedure for preparation and cleaning of application equipment

To avoid solvent contamination of the water borne paint the spraying equipment has to be conditioned before use. All equipment containing solvents in the pump, hoses and gun have to be thoroughly cleaned according to the following instructions.

If the application equipment is made in stainless steel, designed for and only used for application of water borne coatings this preparation and cleaning procedure is not needed.

Before spraying:Circulate Jotun Thinner No. 17 through the equipment and hoses. Then Jotun Thinner No. 4 before fresh clean water.

After spraying:Clean the equipment and hoses with water and detergent (Kraftvask), then circulate Jotun Thinner No. 4 and finally Jotun Thinner No. 17.

StorageThe component A must be stored above 0°C and in accordance with national regulations, subject to re-inspection thereafter. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. The product component B is zinc dust and has no strict limitation's for storage. Containers must be kept tightly closed.

JOTACOTE 5 Page 3

HandlingHandle with care. Stir well before use.Continuous stirring during application will prevent the heavy zinc pigment from settling. SHELF LIFE: 9 months at 23°C for Comp. A, 4 years for comp. B Higher temperatures during storage may reduce the shelf life and may lead to gelling in the tin.

Packing size7 kg Comp. A , 25 kg Comp. B (Together 9.7 l paint)Packing may vary from country to country according to local requirements.










JOTACOTE 5 Page 4



JOTACOTE OXR - COMP. A

1/7


Approved for use



TRADE NAME JOTACOTE OXR - COMP. AAPPLICATION Two-pack topcoat based on reinforced epoxyester

ART-NO PM3424




1 EPOXY RESIN, LOW MOL. (MW<700) 25068-38-6 10-25 N XiN,36/38-43-51/532 N-BUTYL ACETATE 123-86-4 2,5-10 N 10-66-673 AROMATIC HYDROCARBONS C9-C12 64742-95-6 1-2,5 N XnN,10-37-65-51/53




Irritating

FLAMMABLE. MAY CAUSE SENSITISATION BY SKIN CONTACT.For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL




2/7















HANDLING ADVICEAvoid any skin contact with products containing epoxy; they may cause allergic reactions. Vapours are heavier thanair and may spread along floors. Vapours may form explosive mixtures with air. Prevent the creation of flammableor explosive concentrations of vapour in air and avoid vapour concentration higher than the occupational exposurelimits. The product should not be used in vicinity of open flames or other sources of ignition. Use explosion-proofelectrical equipment. The product may charge electrostatically. Allways use earth (ground) wire when transferringfrom one container to another. Personnel should wear anti-static clothing and footwear. Floors should be




3/7

electrically conductive. Keep container tightly closed. Exclude sources of heat, sparks and open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist. Smoking, eating anddrinking are forbidden in the work area. For personal protective equipment see Section 8. Always keep incontainers made of the same material as the supply container. Never use pressure to empty the container, it is not apressure vessel. Electrical equipment should be protected to appropriate standards. The Manual HandlingOperations Regulations may apply to the handling of containers of this product.



Ingredients name CAS-no OEL value (long-term) OEL value (short-term) OELN-BUTYL ACETATE 123-86-4 724,0 mg/m3 966,0 mg/m3










4/7
















INHALATIONExposure to organic solvent vapours may result in adverse health effects such as irritation of the mucous membraneand the respiratory system and adverse effects on the renal and central nervous system. Symptoms and signs includeheadache; dizziness, fatigue, muscular weakness, drowsiness and in extreme cases, loss of consciousness.Inhalation of vapours from organic solvents may lead to nausea, vomiting and headache.






5/7

INGESTIONAccidental ingestion may cause vomiting and abdominal pains. Risk of chemical pneumonia.


BREAKDOWNEpoxy resin, low mol. (MW<700): 12% (OECD 301B (mod.Sturm))Aromatic hydrocarbons C9-C12: Not easily degradable.


ECOTOXITYEpoxy resin, low mol. (MW<700):LC50 (Rainbow trout) = 1,5 mg/l (OECD 203)EC50 (Daphnia) = 3,6 mg/l (OECD 202)IC50 ( Resp. inhibition activated mud) > 100 mg/l (EEC(1998))Aromatic hydrocarbons C9-C12: LC50 (fish) = 1-10 mg/l.

OTHER INFORMATIONThe product should not be allowed to enter drains or water courses or be deposited where it can affect ground orsurface waters. The product contains epoxy compounds labelled "Dangerous for the environment". The productcontains aromatic hydrocarbons C9-C12 labelled "Dangerous for the environment".

13. DISPOSAL

Wastes, including emptied containers, are controlled wastes and should be disposed of in accordance withregulations made under the Control of Pollution Act and the Environmental Protection Act. Do not allow into drainsor water courses. Waste must be disposed of at approved landfill/waste storage or traement facility.





6/7



HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)


Class 3.3 Label 3Packaging group III EmS 3 - 05MFAG Marine Pollutant

Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk






7/7


Classification

Irritating


R-PHRASESR10 Flammable. R43 May cause sensitisation by skin contact.

S-PHRASESS23 Do not breathe vapour/spray. S24 Avoid contact with skin. S37-Wear suitable gloves. S38 In case ofinsufficient ventilation, wear suitable respiratory equipment. P92 Contains epoxy constituents - See informationsupplied by the manufacturer. This information is supplied in the present MSDS.



PRINTEDOUT:

06/08/2001




JOTACOTE OXR - COMP. B

1/6


Approved for use



TRADE NAME JOTACOTE OXR - COMP. BAPPLICATION Two-pack topcoat based on reinforced epoxyester

ART-NO PM3425




1 N-BUTYL ACETATE 123-86-4 10-25 N 10-66-672 XYLENE, mixture of isomers 1330-20-7 2,5-10 Xn,10-20/21-38




FLAMMABLE. VAPOURS MAY CAUSE DROWSINESS AND DIZZINESS.For potential danger for the environment, see section 12.

4. FIRST AID



SKIN CONTACT




2/6

Remove contaminated clothing. Wash skin thoroughly with soap and water or use an appropriate skin cleaner. DoNOT use solvents or thinners.












HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Allways use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area.For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty the




3/6





XYLENE, mixture of isomers 1330-20-7 441,0 mg/m3 H 662,0 mg/m3 H

EXPOSURE CONTROLProvide adequate ventilation. Where reasonably practicable this should be achieved by the use of local exhaustventilation and good general extraction. Resperatory protection are to be used when the concentration ofsolvents/compounds exceeds the Occupational Exposure Limit. Spray mist contains all substances of the productand must not be inhaled. OEL's are taken from the current version of EH40 (by Health & Safety Executive, UK).



HAND PROTECTIONUse PVA/EVOH gloves.Barrier creams may help to protect exposed areas of the skin but are not substitutes for fullphysical protection. Never apply barrier cream to contaminated skin.



Form Liquid.Colour Transparent.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 1,30Expl. limit LEL-UEL., %-%: 0,6 - 7,5 Solubility in water











4/6














13. DISPOSAL






5/6



HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)


Class 3.3 Label 3Packaging group III EmS 3 - 05MFAG Marine Pollutant

Sub. risk Page

IATA (Airplane)


Class Sub. risk

Label Flamm liq. Packaging group III



Classification

COMPOSITION N-BUTYL ACETATE (10-25)

R-PHRASESR10 Flammable. R67 Vapours may cause drowsiness and dizziness.

S-PHRASESS23 Do not breathe vapour/spray. S38 In case of insufficient ventilation, wear suitable respiratory equipment.



PRINTEDOUT:

06/08/2001

VENDOR NOTES The information contained in this MSDS is based on the present state of knowledge and current national




6/6

legislation. As the specific conditions of use of the product are outside the supplier's control, the user is responsiblefor ensuring that the requirements of relevant legislation are compiled with. The information in this MSDSprovides guidance on health, safety and environmental aspects of the product and should not be construed as anyguarantee of technical performance or suitability for particular applications. The Environmental Protection (Dutyof Care) Regulations 1992 (SI 1992:2839). Further information and relevant advice can be found in: The Control ofSubstances Hazardous to Health Regulations 1988 (SI1988:1657). The Highly Flammable Liquids and liquefiedPetroleum Gases Regulations 197 (SI 1972:917). The Manual Handling Operations Regulations 1992 (SI1992:2793). Storage of Flammable Liquids in Containers, HS(G)51. Storage of Packaged Dangerous Substances,HS(G)71. The selection, use and maintenance of respiratory protective equipment: A practical guide HS(G)53.

Technical DataJOTACOTE OXR

Product descriptionJotacote OXR is a two-pack reinforced epoxyester topcoat with excellent gloss and colour retention.

Recommended useAs topcoat over an epoxy/epoxy mastic system where a durable, high gloss finish is required in aggressive atmospheric exposure.



11,8 5,7 9,5



Surface preparation




JOTACOTE OXR Page 1


Application methodsSpray Use airless sprayBrush Recommended for strip coating and small areas, care must be taken to achieve the

specified dry film thickness.



Substrate temperature 5°C 10°C 23°C 40°CSurface dry 12 h 8 h 4 h 2 hThrough dry 14 h 9 h 5 h 3 hCured 15 d 10 d 5 d 2 d





Typical paint systemPenguard HBJotacote OXR

2 x 150 µm1 x 75 µm



JOTACOTE OXR Page 2



Packing size 14 l Comp. A and 6 l Comp.B. 3,5 l Comp. A and 1,5 l Comp. B.Packing may vary from country to country according to local requirements.










JOTACOTE OXR Page 3



JOTACOTE PSO - COMP. A

1/6


Approved for use



TRADE NAME JOTACOTE PSO - COMP. AAPPLICATION Two-pack topcoat based on a polysiloxan binder.

ART-NO PM3357




1 N-BUTYL ACETATE 123-86-4 25-50 N 10-66-672 AROMATIC HYDROCARBONS C9-C12 64742-95-6 1-2,5 N XnN,10-37-65-51/53




FLAMMABLE.For potential danger for the environment, see section 12.

4. FIRST AID



SKIN CONTACT




2/6













HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Allways use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area.For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty the




3/6






EXPOSURE CONTROLProvide adequate ventilation. Where reasonably practicable this should be achieved by the use of local exhaustventilation and good general extraction. Respiratory protection are to be used when the concentration ofsolvents/compounds exceeds the Occupational Exposure Limit. Spray mist contains all substances of the productand must not be inhaled. OEL's are taken from the current version of EH40 (by Health & Safety Executive, UK).



HAND PROTECTIONUse PVA/EVOH gloves. Barrier creams may help to protect exposed areas of the skin but are not substitutes for fullphysical protection. Never apply barrier cream to contaminated skin.



Form Liquid.Colour White.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 1,00Expl. limit LEL-UEL., %-%: 1,2 - 7,5 Solubility in water



pH Solution Boiling point/range 127ºC









4/6











BREAKDOWNAromatic hydrocarbons C9-C12: Not easily degradable.


ECOTOXITYAromatic hydrocarbons C9-C12: LC50 (fish) = 1-10 mg/l.

OTHER INFORMATIONThe product should not be allowed to enter drains or water courses or be deposited where it can affect ground orsurface waters. The product contains aromatic hydrocarbons C9-C12 labelled "Dangerous for the environment".

13. DISPOSAL






5/6



HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk




Classification

R-PHRASESR10 Flammable.




PRINTEDOUT:

16/07/2001

VENDOR NOTES The information contained in this MSDS is based on the present state of knowledge and current nationallegislation. As the specific conditions of use of the product are outside the supplier's control, the user is responsiblefor ensuring that the requirements of relevant legislation are compiled with. The information in this MSDSprovides guidance on health, safety and environmental aspects of the product and should not be construed as anyguarantee of technical performance or suitability for particular applications. The Environmental Protection (Dutyof Care) Regulations 1992 (SI 1992:2839). Further information and relevant advice can be found in: The Control ofSubstances Hazardous to Health Regulations 1988 (SI1988:1657). The Highly Flammable Liquids and liquefied




6/6

Petroleum Gases Regulations 197 (SI 1972:917). The Manual Handling Operations Regulations 1992 (SI1992:2793). Storage of Flammable Liquids in Containers, HS(G)51. Storage of Packaged Dangerous Substances,HS(G)71. The selection, use and maintenance of respiratory protective equipment: A practical guide HS(G)53.



JOTACOTE PSO - COMP. B

1/6


Approved for use



TRADE NAME JOTACOTE PSO - COMP. BAPPLICATION Two-pack topcoat based on a polysiloxan binder.

ART-NO PM3358




1 N-BUTYL ACETATE 123-86-4 25-50 N 10-66-672 3-AMINOPROPYLTRIETHOXYSILANE 919-30-2 10-25 N C,22-34




Corrosive

FLAMMABLE. CAUSES BURNS. VAPOURS MAY CAUSE DROWSINESS AND DIZZINESS.For potential danger for the environment, see section 12.

4. FIRST AID

GENERALIn all cases of doubt, or when symptoms persist, seek medical attention. Obtain advice via telephone; before thepatient is transported to a doctor or hospital. Never give anything by mouth to an unconscious person.

INHALATION




2/6


SKIN CONTACTRemove contaminated clothing. Wash skin thoroughly with soap and water or use an appropriate skin cleaner.Flush the skin with plenty of water. Do NOT use solvents or thinners.

EYE CONTACTRemove any contact lenses. Hold the eyelids apart. Seek medical advice. Rinse with lukewarm water for 1 hour.

INGESTIONDO NOT INDUCE VOMITING. If accidentally swallowed obtain immediate medical attention. Keep at rest. Drinkwater or milk/cream immediately. Rinse the mouth with large amounts of water if the patient is conscious. Seekmedical advice.

MEDICAL INFORMATION Risk of chemical pneumonia by aspiration. Keep attention: danger of lung damage. General health examination.Professional evaluation of the work station. Obtain miedical surveillance concerning burn injuries in mouth andthroat. Aspiration hazard by vomiting. All poisoned persons should be transported in recovery position. Anauthorised person should acompany under the transport. Stomach-rinsing may bee considered, for instance with anantioxydant. Eye injuries should be treated with chloramphenicol or antiseptic eye treatment. Local anesthetica maybe given to relieve pain. Eye specialist should be consulted as soon as possible.









HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Allways use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area. For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty thecontainer, it is not a pressure vessel. Electrical equipment should be protected to appropriate standards. The Manual




3/6

Handling Operations Regulations may apply to the handling of containers of this product.




EXPOSURE CONTROLProvide adequate ventilation. Where reasonably practicable this should be achieved by the use of local exhaustventilation and good general extraction. Resperatory protection are to be used when the concentration ofsolvents/compounds exceeds the Occupational Exposure Limit. Spray mist contains all substances of the productand must not be inhaled. OEL’s are taken from the current version of EH40 (by Health & Safety Executive, UK).








4/6


Form Liquid.Colour Colourless.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 1,0Expl. limit LEL-UEL., %-%: 1,2 - 7,5 Solubility in water











HAZARDOUS DECOMPOSITION PRODUCTSIn a fire, hazardous decomposition products such as smoke, carbon monoxide, carbon dioxide and oxides ofnitrogen may be produced. May split off ethanol in case of hydrolysis.




SKIN CONTACTCauses burns. Repeated or prolonged contact with the product may lead to removal of natural fats from the skinresulting in non-allergic contact dermatitis and absorption through the skin. Repeated or prolonged contact withskin may cause sensitisation.

EYE CONTACTSplashes in the eyes may cause irritation and possible risk of irreversible damage if the eyes are not flushed withplenty of water.

INGESTIONMay cause burn damage to mucous membrane, esophagus and stomach. Accidental ingestion may cause vomitingand abdominal pains. Risk of chemical pneumonia.


OTHER INFORMATIONThe product should not be allowed to enter drains or water courses or be deposited where it can affect ground or




5/6

surface waters.

13. DISPOSAL




PROPER SHIPPING NAME FLAMMABLE LIQUID, CORROSIVE, N.O.S. (3-aminopropyltrietoksysilan, .)Toll. reg. no.

HAZCHEM

ADR (Road)


Class 3,33 (c) Label 3+8Haz. id. no 30 Marginno.

RID (Railway)


Class 3,33 (c) Label 3+8Haz..id.no 30

IMDG (Sea)


Class 3 Label 3 + 8Packaging group III EmS 3 - 02MFAG Marine Pollutant

Sub. risk 8 Page

IATA (Airplane)


Class 3 Sub. risk 8Label 3+8 Packaging group III



Classification

Corrosive

COMPOSITION N-BUTYL ACETATE (25-50), 3-AMINOPROPYLTRIETHOXYSILANE (10-25)

R-PHRASESR10 Flammable. R34 - Causes burns. R67 Vapours may cause drowsiness and dizziness.

S-PHRASESS23 Do not breathe vapour/spray. S26 In case of contact with eyes, rinse immediately with plenty of water and seekmedical advice.S36/37/39 Wear suitable protection clothing, gloves and eyes/face protection. S38 In case of




6/6

insufficient ventilation, wear suitable respiratory equipment. S45 In case of accident or if you feel unwell, seekmedical advice immediately (show the label where possible).



PRINTEDOUT:

16/07/2001


Technical DataJOTACOTE PSO

Product descriptionJotacote PSO is a two-pack polysiloxane topcoat with excellent gloss and colour retention.

Recommended useAs topcoat over an epoxy/epoxy mastic system where a durable, high gloss finish is required in aggressive atmospheric exposure.



11,8 5,7 9,5



Surface preparation





JOTACOTE PSO Page 1



Application data Mixing ratio (volume) 1,5 parts of Comp. A (base) to 1 part Comp. B (curing agent).Pot life (23°C) 6 hours (Reduced at higher temp.). Thinner/Cleaner Jotun Thinner No. 26Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi).Nozzle tip 0.33-0.46 mm (0.013-0.018").Spray angle 40-80° Filter Check to ensure that filters are clean.


Substrate temperature 5°C 10°C 23°C 40°CSurface dry 6 h 5 h 3,5 h 2 hThrough dry 8 h 7 h 4 h 3 hCured 15 d 10 d 5 d 3 d





Typical paint systemPenguard HBJotacote PSO

2 x 150 µm1 x 75 µm





JOTACOTE PSO Page 2

Packing size12,8 l Comp. A and 7,2 l Comp. B. 3,2 l Comp. A and 1,8 l Comp. B.Packing may vary from country to country according to local requirements.










JOTACOTE PSO Page 3

Technical DataJOTAFLOOR COATING

Product descriptionJotafloor Coating is a high performance, self smoothing, solvent free, seamless epoxy coating capable of being applied at varying thicknesses to suit the final use of the floor. Jotafloor Coating offers excellent chemical, abrasion and impact resistance.

Recommended useJotafloor Coating has a wide range of application uses ranging from light industrial areas to floors requiring long lasting protection from abrasion and heavy loads. Typical areas include:

Warehousesl

Garagesl

Dairiesl

Factoriesl

Laboratoriesl

Aircraft hangersl

Plant roomsl

Food manufacuring plantsl



5 2 3,3

Physical propertiesColour Cream 908, Light grey 967, Papyrus 980, Yellow 414 and Red

2230Solids (vol %)* 98 ± 2 Flash point >100ºC (Setaflash)Gloss GlossyWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Check chemical resistance values in Jotafloor chemical

resistance chart.


Surface preparation





Condition during applicationThe temperature of the substrate should be minimum 10°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. The moisture content in the concrete should not exceed 4 % (by weight). The coating should not be exposed to oil, chemicals or mechanical stress until fully cured.

Application methodsBrush Stiff nylon brushRoller Recommended Other It is very important to pierce the coating with a spiked roller, after achieving the

desired thickness, to avoid air bubbles.


(curing agent). NO PART MIXINGMixing Use a slow speed drill and mixing paddle. Pour the full contents of

the mixed material onto the floor immediately after mixing is completed.

Pot life (23°C) Jotafloor Coating Comp. B (20) 10 min. (30 min. after poured on to the floor).Jotafloor Coating Comp. B (40) 20 min. (45 min. after poured on to the floor).

Thinner/Cleaner Jotun Thinner No. 17Note This product should be applied by a trained specialist. Jotun can

offer a list of Licensed Applicators on request to your local Jotun office.

JOTAFLOOR COATING Page 2

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateCuring agent Comp. B (20):

Substrate temperature 15°C 23°C 40°CSurface dry 6 h 3 h 2 hThrough dry 24 h 15 h 6 hCured 10 d 7 d 3 d



Curing agent Comp. B (40):Substrate temperature 15°C 23°C 40°CSurface dry 8 h 5 h 2 hThrough dry 32 h 20 h 8 hCured 12 d 9 d 3 d





Typical paint systemJotafloor SealerJotafloor CoatingorJotafloor Solvent Free PrimerJotafloor Coating

1 x 50 µm1 x 300 µm

1-2 x 100 µm1 x 300-500 µm



Note: Thickness of the finished system will vary depending on use of the finished floor. Consult your local Jotun Office for advice.Other systems may be specified, depending on area of use




Packing size13 l. Comp. A (base) and 6.5 l. Comp. B (curing agent).2.6 l. Comp. A (base) and 1.3 l. Comp. B. (curing agent).Packing may vary from country to country according to local requirements.













JOTAFLOOR DAMP BOND - COMP. A

1/6


Approved for use



TRADE NAME JOTAFLOOR DAMP BOND - COMP. AAPPLICATION Two-pack. epoxyprimer

ART-NO PM3430

Producer/Importer JOTUN PAINTS (EUROPE) LTD.Address Flixborough, ScunthorpeZipcode & City North Lincolnshire DN15 8RRTelephone +44 1724 40 00 00Fax +44 1724 40 01 00Contactperson SHE-dept., JOTUN A/S, NORWAYResponsible SHE-dept., JOTUN A/S, NORWAYEmergency number Contact the National Poison Center



1 EPOXY RESIN, LOW MOL. (MW<700) 25068-38-6 50-100 N XiN,36/38-43-51/532 FURFURYLALCOHOL 98-00-0 25-50 Xn,20/21/22




Harmful

HARMFUL BY INHALATION, IN CONTACT WITH SKIN AND IF SWALLOWED. IRRITATING TO EYESAND SKIN. MAY CAUSE SENSITISATION BY SKIN CONTACT.For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL




2/6




EYE CONTACTRemove any contact lenses. Hold the eyelids apart. Irrigate copiously with clean, fresh water for at least 10 minutes.


MEDICAL INFORMATION Risk of chemical pneumonia by aspiration. Keep attention: danger of lung damage. General health examination.Professional evaluation of the work station. Person developing a skin rash are to be directed to a dermatologist forexamination.









HANDLING ADVICEAvoid any skin contact with products containing epoxy; they may cause allergic reactions. Keep container tightlyclosed. Exclude sources of heat, sparks and open flame. Use non-sparking tools. Avoid skin and eye contact. Avoidinhalation of vapour and spray mist. Smoking, eating and drinking are forbidden in the work area.For personalprotective equipment see Section 8. Always keep in containers made of the same material as the supply container.




3/6

Never use pressure to empty the container, it is not a pressure vessel. The Manual Handling Operations Regulationsmay apply to the handling of containers of this product.

STORAGEStore in accordance with the regulations for flammable materials. Observe the label precautions. Store in a dry, coldand well ventilated place away from sources of heat, ignition and direct sunlight.


Ingredients name CAS-no OEL value (long- term) OEL value (short- term) OELFURFURYLALCOHOL 98-00-0 20,0 mg/m3, Sk 61,0 mg/m3, Sk




HAND PROTECTIONUse 4H gloves or PVA.Barrier creams may help to protect exposed areas of the skin but are not substitutes for fullphysical protection. Never apply barrier cream to contaminated skin.



Form Liquid.Colour Clear.Odour Organic solvent.Solubility Organic solvents (most).Melting point/range Density 1,13

Expl. limit LEL-UEL., %-%: 0,8-16,3 Solubility in water



pH Solution Boiling point/range 171°C

Flash point 77°C pH concentrate







MATERIALS TO AVOID




4/6

Keep away from oxidising agents, strongly alkaline and strongly acidic materials to prevent the exothermicreactions.





SKIN CONTACTRepeated or prolonged contact with the product may lead to removal of natural fats from the skin resulting in non-allergic contact dermatitis and absorption through the skin. Repeated or prolonged contact with skin may causesensitisation. Repeated skin contact may lead to irritation and sensitization, possible with cross-sensitisation toother epoxies. Allergic reactions may occur after short time exposure.







13. DISPOSAL






5/6


PROPER SHIPPING NAME ENVIRONMENTALLY HAZARDOUS SUBSTANCE, LIQUID N.O.S.(Epoxyresin, low mol. MW <700, )

Toll. reg. no.

HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)


Class 9 Label 9Packaging group III EmS -MFAG - Marine Pollutant

Sub. risk Page

IATA (Airplane)


Class 9 Sub. risk




Classification

Harmful

COMPOSITION EPOXY RESIN, LOW MOL. (MW<700) (50-100), FURFURYLALCOHOL (25-50)

R-PHRASESR20/21/22 - Harmful by inhalation, in contact with skin and if swallowed. R36/38 - Irritating to eyes and skin. R43May cause sensitization by skin contact.

S-PHRASESS23 Do not breathe vapour/spray. S36/37 Wear suitable protective clothing and gloves. S38 In case of insufficientventilation, wear suitable respiratory equipment. P92 Contains epoxy constituents - See information supplied by themanufacturer This information is supplied in the present MSDS.



PRINTEDOUT:

21/11/2001




6/6




JOTAFLOOR DAMP BOND - COMP. B

1/6


Approved for use



TRADE NAME JOTAFLOOR DAMP BOND - COMP. BAPPLICATION Two-pack. epoxyprimer

ART-NO PM3431




1 3,6-DIAZAOCTANETHYLENEDIAMIN 112-24-3 2,5-10 N C,21-34-43-52/532 BENZYL ALCOHOL 100-51-6 25-50 N Xn,20/223 FURFURYLALCOHOL 98-00-0 10-25 Xn,20/21/22




Harmful

HARMFUL BY INHALATION, IN CONTACT WITH SKIN AND IF SWALLOWED. MAY CAUSESENSITISATION BY SKIN CONTACT.For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL




2/6






MEDICAL INFORMATIONRisk of chemical pneumonia by aspiration. Keep attention: danger of lung damage. General health examination.Professional evaluation of the work station. Person developing a skin rash are to be directed to a dermatologist forexamination.









HANDLING ADVICEKeep container tightly closed. Exclude sources of heat, sparks and open flame. Use non-sparking tools. Avoid skinand eye contact. Avoid inhalation of vapour and spray mist. Smoking, eating and drinking are forbidden in the workarea.For personal protective equipment see Section 8. Always keep in containers made of the same material as the




3/6

supply container. Never use pressure to empty the container, it is not a pressure vessel. The Manual HandlingOperations Regulations may apply to the handling of containers of this product.

STORAGEStore in accordance with the regulations for flammable materials. Observe the label precautions. Store in a dry, coldand well ventilated place away from sources of heat, ignition and direct sunlight.


Ingredients name CAS-no OEL value (long- term) OEL value (short-term)

OEL

FURFURYLALCOHOL 98-00-0 20,0 mg/m3, Sk 61,0 mg/m3, Sk




HAND PROTECTIONUse gloves of viton or 4H gloves.Barrier creams may help to protect exposed areas of the skin but are notsubstitutes for full physical protection. Never apply barrier cream to contaminated skin.



Form Liquid.Colour Clear.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 0.97Expl. limit LEL-UEL., %-%: 1.3-16.3 Solubility in water










MATERIALS TO AVOID




4/6

Keep away from oxidising agents, strongly alkaline and strongly acidic materials to prevent the exothermicreactions.





SKIN CONTACTRepeated or prolonged contact with the product may lead to removal of natural fats from the skin resulting in non-allergic contact dermatitis and absorption through the skin. Repeated or prolonged contact with skin may causesensitisation. Products containing amines irritate the skin and may lead to allegic ecema. The allergic response mayoccur after a short periode of contact.




ECOTOXITY


13. DISPOSAL






5/6


PROPER SHIPPING NAME

Toll. reg. no.

HAZCHEM

ADR (Road)

UN No. Dang. goods

Class Label


RID (Railway)

UN No. Dang. goods

Class Label

Haz..id.no

IMDG (Sea)

UN No. Dang. goods

Class Label

Packaging group EmS

MFAG Marine Pollutant

Sub. risk Page

IATA (Airplane)

UN No. Dang. goods

Class Sub. risk


GENERALTransport only in accordance with ADR for road, RID for rail, IMDG for sea transport and IATA for airtransport.The product is not classified as dangerous goods for carriage.


Classification

Harmful

COMPOSITION 3,6-DIAZAOCTANETHYLENEDIAMIN (2,5-10), BENZYL ALCOHOL (25-50), FURFURYLALCOHOL (10-25)

R-PHRASESR20/21/22 - Harmful by inhalation, in contact with skin and if swallowed. R43 May cause sensitization by skincontact.







6/6

PRINTEDOUT:

20/11/2001


Technical DataJOTAFLOOR DAMP BOND

Product descriptionJotafloor Damp Bond is a specially formulated two component, epoxy resin based primer used to promote adhesion between Jotafloor products and the parent concrete substrate. Can also be applied directly onto damp green concrete thereby aiding the curing process.

Recommended useFor use primarily as a primer for Jotafloor systems in many situations such as

Kitchensl

Factoriesl

Car parksl

Traffic Decksl

Warehousesl

Basementsl

Manufacturing facilitiesl

Industrial Unitesl

Provides a cost effective method of curing and priming using one product thereby minimising labour costs and down time. It is important to seek technical advice from your local Jotun office on choice of primer and application technique.

Physical propertiesColour Limited numberSolids (vol %)* 80 ± 2 Flash point 80ºC ± 2 (Setaflash)Water resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Flexibility Good


JOTAFLOOR DAMP BOND Page 1

Surface preparation




Other surfacesConcrete surface preparation by using dust free captive blasting units, grinding equipment, sand blasting or high pressure water jetting is critical to achieving the right surface profile prior to paint application. Please contact your local Jotun office for more information.Application on green concrete can take place as soon as it is practical to walk on the surface. Damp green concrete can be brushed or subject to light grinding prior to application of the primer.


Condition during applicationThe temperature of the substrate should be minimum 15°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. The moisture content in the concrete should not exceed 5 % (by weight).

Application methodsSpray Use airless spray or rollerBrush Recommended for stripe coating and small areas, care must be taken to achieve

the specified dry film thickness.Other For use on new concrete, apply as soon as practically possible to the freshly placed

concrete. One coat applied at 100 microns D.F.T. is sufficient to effectively cured normal concrete. Two coats applied at right angles can be considered if the subsequent floor coating is to be applied within the normal curing period. Old concrete will require a regime of surface preparation as detailed below.

Application data Mixing ratio (volume) 2 parts Comp. A ( base) to 1 part Comp. B (curing agent). We

strongly recommended no part mixing.Mixing Mix and use immediatelyPot life (23°C) 30 mins. (reduced at higher temperatures) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi)Nozzle tip 0.63 - 1.09 mm (0.025-0.043")Spray angle 65 - 80°Filter Filters to be removed prior to spraying.






Recommended data given for product prior to application of Jotafloor Non Slip Aggregate and 1.subsequent over coating with Jotafloor PU Topcoat



Jotafloor Damp BondJotafloor Coating

Jotafloor Damp BondJotafloor Glass FlakeJotafloor Non Slip AggregateJotafloor PU Topcoat

Jotafloor Damp BondJotafloor Topcoat

1 x 100 µm1 x 300 µm

1 x 100 µm1 x 300 µm

2 x 70 µm

1 x 100 µm2 x 50 µm



(Dry FilmThickness)


Note: Jotafloor Damp Bond can be used in many different situations but has limitations relative to negative water pressure. We recommend consulting your local Jotun Technical Department for advice on choice of system.Other systems may be specified, depending on area of use




Packing size20 l Comp. A (base) and 4 l Comp. B (curing agent)Packing may vary from country to country according to local requirements.













JOTAFLOOR GLASS FLAKE - COMP. A

1/6


Approved for use



TRADE NAME JOTAFLOOR GLASS FLAKE - COMP. AAPPLICATION Two-pack glassflacearmed epoxypaint.

ART-NO PM3432

Producer/Importer JOTUN PAINTS (EUROPE) LTD.Address Flixborough, ScunthorpeZipcode & City North Lincolnshire DN15 8RRTelephone +44 1724 40 00 00Fax +44 1724 40 01 00Contactperson SHE-dept., Jotun A/S, NorwayResponsible SHE-dept., Jotun A/S, Norway



1 EPOXY RESIN, LOW MOL. (MW<700) 25068-38-6 25-50 N XiN,36/38-43-51/532 XYLENE, mixed isomers 1330-20-7 2,5-10 N Xn,10-20/21-383 N-BUTANOL 71-36-3 2,5-10 N Xn,10-22-37/38-41-67




Harmful

FLAMMABLE. IRRITATING TO EYES AND SKIN. MAY CAUSE SENSITISATION BY SKIN CONTACT.For potential danger for the environment, see section 12.

4. FIRST AID


INHALATION




2/6














HANDLING ADVICEAvoid any skin contact with products containing epoxy; they may cause allergic reactions. Vapours are heavier thanair and may spread along floors. Vapours may form explosive mixtures with air. Prevent the creation of flammableor explosive concentrations of vapour in air and avoid vapour concentration higher than the occupational exposurelimits. The product should not be used in vicinity of open flames or other sources of ignition. Use explosion-proofelectrical equipment. The product may charge electrostatically. Always use earth (ground) wire when transferringfrom one container to another. Personnel should wear anti-static clothing and footwear. Floors should beelectrically conductive. Keep container tightly closed. Exclude sources of heat, sparks and open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist. Smoking, eating anddrinking are forbidden in the work area.For personal protective equipment see Section 8. Always keep in containersmade of the same material as the supply container. Never use pressure to empty the container, it is not a pressurevessel. Electrical equipment should be protected to appropriate standards. The Manual Handling OperationsRegulations may apply to the handling of containers of this product. Smoking, eating and drinking are forbidden inthe work area.




3/6



Ingredients name CAS-no OEL value (long term) OEL value (short time) OELXYLENE, mixed isomers 1330-20-7 441,0 mg/m3 ;Sk 662,0 mg/m3 ;Sk

N-BUTANOL 71-36-3 154,0 mg/m3;Sk 154,0 mg/m3;Sk




HAND PROTECTIONUse 4H gloves or PVA.Barrier creams may help to protect exposed areas of the skin but are not substitutes for fullphysical protection. Never apply barrier cream to contaminated skin.





4/6


Form Liquid.Colour Various.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 1,28-1,32Expl. limit LEL-UEL., %-%: 1,1 - 11,3 Solubility in water

















INGESTIONAbsorbed by the gastric intestinal system. May cause liver and kidney damage. Accidental ingestion may cause




5/6

vomiting and abdominal pains. Risk of chemical pneumonia.






13. DISPOSAL





HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk





6/6



Classification

Harmful


R-PHRASESR10 Flammable. R36/38 - Irritating to eyes and skin. R43 May cause sensitization by skin contact.

S-PHRASESS23 Do not breathe vapour/spray. S24 Avoid contact with skin. S37-Wear suitable gloves. S38 In case ofinsufficient ventilation, wear suitable respiratory equipment. P92 Contains epoxy constituents - See informationsupplied by the manufacturer This information is supplied in the present MSDS.



PRINTEDOUT:

19/11/2001




JOTAFLOOR GLASS FLAKE - COMP. B

1/6


Approved for use



TRADE NAME JOTAFLOOR GLASS FLAKE - COMP. BAPPLICATION Two-pack glassflacearmed epoxypaint.

ART-NO PM3433




1 3-AMINOMETHYL-3,5,5-TRIMETHYLCYCLOHEXYLAMINE 2855-13-2 10-25 N C,21/22-34-43-52/532 BENZYL ALCOHOL 100-51-6 10-25 N Xn,20/223 2,2,4 TRIMETHYL HEXAMETHYLENE DIAMINE 25620-58-0 2,5-10 N C,22-34-43-52/534 XYLENE, mixed isomers 1330-20-7 10-25 N Xn,10-20/21-385 N-BUTANOL 71-36-3 2,5-10 N Xn,10-22-37/38-41-67




Corrosive

FLAMMABLE. HARMFUL BY INHALATION, IN CONTACT WITH SKIN AND IF SWALLOWED.CAUSES BURNS. MAY CAUSE SENSITISATION BY SKIN CONTACT.For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL




2/6

In all cases of doubt, or when symptoms persist, seek medical attention. Obtain advice via telephone; before thepatient is transported to a doctor or hospital. Never give anything by mouth to an unconscious person.


SKIN CONTACTRemove contaminated clothing. Wash skin thoroughly with soap and water or use an appropriate skin cleaner.Flush the skin with plenty of water. Do NOT use solvents or thinners.


INGESTIONDO NOT INDUCE VOMITING. If accidentally swallowed obtain immediate medical attention. Keep at rest. Drinkwater or milk/cream immediately. Rinse the mouth with large amounts of water if the patient is conscious. Seekmedical advice.

MEDICAL INFORMATION Risk of chemical pneumonia by aspiration. Keep attention: danger of lung damage. General health examination.Professional evaluation of the work station. Obtain miedical surveillance concerning burn injuries in mouth andthroat. Aspiration hazard by vomiting. All poisoned persons should be transported in recovery position. Anauthorised person should acompany under the transport. Stomach-rinsing may bee considered, for instance with anantioxydant. Eye injuries should be treated with chloramphenicol or antiseptic eye treatment. Local anesthetica maybe given to relieve pain. Eye specialist should be consulted as soon as possible.













3/6












Form Liquid.Colour Colourless.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 0,97Expl. limit LEL-UEL., %-%: 1,1-13,0 Solubility in water











4/6








SKIN CONTACTCorrosive. Repeated or prolonged contact with the product may lead to removal of natural fats from the skinresulting in non-allergic contact dermatitis and absorption through the skin. Repeated or prolonged contact withskin may cause sensitisation. Products containing amines irritate the skin and may lead to allegic ecema. Theallergic response may occur after a short periode of contact.

EYE CONTACTSplashes in the eyes may cause irritation and possible risk of irreversible damage if the eyes are not flushed withplenty of water.

INGESTIONMay cause burn damage to mucous membrane, esophagus and stomach. Accidental ingestion may cause vomitingand abdominal pains. Risk of chemical pneumonia.Absorbed by the gastric intestinal system. May cause liver andkidney damage.








3-aminomethyl-3,5,5-trimethylcyclohexylamine:Bacteria: Pseudomonas putida, incipient inhibition of cellbreeding




5/6

at (18 h) = 1120 mg/l.2,2,4-trimethylhexametylendiamine:

Fish: LC50 (96 h) = 1000 mg/lDaphnia: EC50 (24 h) = 31,5 mg/lAlgea: EC50 (72 h) = 29,5 mg/lBacteria: IC50 (3 h) = 100 mg/l


13. DISPOSAL




PROPER SHIPPING NAME AMINES, LIQUID, CORROSIVE, FLAMMABLE, N.O.S. (xylenes,isophoronediamine,)

Toll. reg. no.

HAZCHEM

ADR (Road)


Class 8, PG II Label 8+3Haz. id. no 83 Marginno.

RID (Railway)


Class 8, PG II Label 8+3Haz..id.no 83

IMDG (Sea)


Class 8 Label 8+3Packaging group II EmS 8-04MFAG Marine Pollutant

Sub. risk 3 Page

IATA (Airplane)


Class 8 Sub. risk 3Label 8+3 Packaging group II





6/6


Classification

Corrosive

COMPOSITION 3-AMINOMETHYL-3,5,5-TRIMETHYLCYCLOHEXYLAMINE (10-25), 2,2,4 TRIMETHYL HEXAMETHYLENEDIAMINE (2,5-10), XYLENE, mixed isomers (10-25)

R-PHRASESR10 Flammable. R20/21/22 - Harmful by inhalation, in contact with skin and if swallowed. R34 - Causes burns.R43 May cause sensitization by skin contact.

S-PHRASESS23 Do not breathe vapour/spray. S26 In case of contact with eyes, rinse immediately with plenty of water and seekmedical advice.S38 In case of insufficient ventilation, wear suitable respiratory equipment. S36/37/39 Wearsuitable protection clothing, gloves and eyes/face protection. S45 In case of accident or if you feel unwell, seekmedical advice immediately (show the label where possible).



PRINTEDOUT:

19/11/2001


Technical DataJOTAFLOOR GLASS FLAKE

Product descriptionA two pack, high solids epoxy reinforced with glass flakes that constitutes the protective layer of the Jotafloor Traffic Deck System. Offers all round protection against substances likely to assist in steel corrosion within a concrete substrate and provides excellent resistance to impact and abrasion and the stresses found in car parks/traffic decks subject to heavy vehicular traffic.

Recommended useFor use in conjunction with Jotafloor products comprising the Jotafloor Traffic Deck System. Can be spray, brush or roller applied in two or three coats depending on the volume of traffic expected. This product can also be used independently of the Jotafloor Traffic Deck System. A wide range of colours are available. Typical areas include:

Underground car parksl

Rampsl

External traffic deckl

Concrete balconiesl

Parking baysl

Pedestrian walkwaysl



2,66 1,6 2,66

Physical propertiesColour Limited numberSolids (vol %)* 80 ± 2 Flash point 30ºC ± 2 (Setaflash)Water resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Flexibility Good


JOTAFLOOR GLASS FLAKE Page 1

Surface preparation




Other surfacesConcrete surface preparation by using dust free captive blasting units, grinding equipment, sand blasting or high pressure water jetting is critical to achieving the right surface profile prior to paint application. Please contact your local Jotun office for more information.



Application methodsSpray Use airless spray or rollerBrush Recommended for stripe coating and small areas, care must be taken to achieve


Application data Mixing ratio (volume) 3 parts Comp. A ( base) to 1 part Comp. B (curing agent). We

strongly recommended no part mixing.Pot life (23°C) 1 hour (reduced at higher temperatures) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi)Nozzle tip 0.63 - 1.09 mm (0.025-0.043")Spray angle 65 - 80°Filter Filters to be removed prior to spraying.Note This product should be applied by a trained specialist. Jotun can




Substrate temperature 10°C 23°C 40°CSurface dry 14 h 5,5 h 2,5 hThrough dry 48 h 12 h 5 hCured 14 d 7 d 3 d



Recommended data given for product prior to application of Jotafloor Non Slip Aggregate and 1.subsequent over coating with Jotafloor Polyurethane Finish.



Jotafloor SealerJotafloor Glass FlakeJotafloor Non Slip AggregateJotafloor PU Topcoat

Jotafloor Damp BondJotafloor Glass FlakeJotafloor Non Slip AggregateJotafloor PU Topcoat

Jotafloor Solvent Free PrimerJotafloor Glass FlakeJotafloor Non Slip AggregateJotafloor PU Topcoat

1 x 40 µm1 x 300 µm

2 x 70 µm

1 x 100 µm1 x 300 µm

2 x 70 µm

1 x 150 µm1 x 400 µm

3 x 70 µm

(Dry Film Thickness)(Dry Film Thickness)(Available in various sizes)(Dry FilmThickness)


(Dry Film Thickness)(Dry Film Thickness)(Available in various sizes)(Dry Film Thickness)





Technical DataJOTAFLOOR NON SLIP AGGREGATE TYPE - FINE / MEDIUM / COARSE

Product descriptionJotafloor Non Slip Aggregate is pre-bagged graded, hard wearing aggregate designed to be applied in combination with Jotafloor products to give a non slip floor finish. Aggregate is cast on to wet material and the excess swept off when dry. Coverage depends on quantity initially used and desired profile.

Recommended useUsed where non slip areas are required in locations such as:

Rampsl

Warehouse aislesl

Food Production Plantsl

Dairiesl

Production wet areasl

Industrial slippery areasl

Car parksl

Traffic Deck Systemsl

CommentsGrades: Fine, Medium or Coarse (depending on texture required)Coverage: 2 – 6 kg/m2 gross - 1.5 – 4 kg/m2 nett

Physical propertiesFlash point Non-flammable*Measured according to ISO 3233:1998 (E)

Condition during applicationAccording to specifications for the chosen topcoat.

Application methodsOther If required Jotafloor Non Slip Aggregate can be used with Jotafloor Topcoat,

Jotafloor Coating and Jotafloor SL Universal if required. (Advice should be sought from your local Jotun office regarding application techniques as these vary slightly from product to product).

Jotafloor Non Slip Aggregate is cast on to the wet first coat of the Jotafloor material until the whole surface is covered. Aggregate should not be thrown onto the wet coating as this may damage the first coat. Distribute the aggregate from a container eg. distribution sieve, that will allow the aggregate to fall directly onto the wet coating.

Once the first coat has dried, remove the excess aggregate from the surface by vacuum or sweeping brush for reuse if clean.

Apply the final coat of Jotafloor material to the desired thickness.



Packing sizeJotafloor Non Slip Aggregate Fine, Medium and Coarse supplied in 25 kg bags.Packing may vary from country to country according to local requirements.










JOTAFLOOR NON SLIP AGGREGATE TYPE - FINE / MEDIUM / COARSE Page 2



JOTAFLOOR PU TOPCOAT - COMP. A

1/6


Approved for use



TRADE NAME JOTAFLOOR PU TOPCOAT - COMP. AAPPLICATION Two-pack, polyurethane topcoat.

ART-NO PM3434




1 N-BUTYL ACETATE 123-86-4 2,5-10 N 10-66-672 XYLENE, mixed isomers 1330-20-7 2,5-10 N Xn,10-20/21-383 ETYL-3-ETHOXYPROPIONAT 763-69-9 10-25 N 10




FLAMMABLE.For potential danger for the environment, see section 12.

4. FIRST AID



SKIN CONTACT




2/6

















3/6





XYLENE, mixed isomers 1330-20-7 441,0 mg/m3 ;Sk 662,0 mg/m3 ;Sk

ETYL-3-ETHOXYPROPIONAT 763-69-9 50,0 ppm 100,0 ppm


RESP. PROTECTIONFresh air mask have to be used when spraying, even if there is good ventilation.With other handlig methods thanspraying: When good ventilation fresh air mask could be replaced with protection mask and combination cartridgeA2/P3.


HAND PROTECTIONUse (e.g. 4H) gloves or PVA.Barrier creams may help to protect exposed areas of the skin but are not substitutes forfull physical protection. Never apply barrier cream to contaminated skin.















4/6








EYE CONTACTSplashes in the eyes may cause irritation and reversible local damage. Splashes in the eyes may cause irritation andreversible damage.





13. DISPOSAL






5/6



HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk




Classification

R-PHRASESR10 Flammable.




PRINTEDOUT:

19/11/2001

VENDOR NOTES The information contained in this MSDS is based on the present state of knowledge and current nationallegislation. As the specific conditions of use of the product are outside the supplier's control, the user is responsiblefor ensuring that the requirements of relevant legislation are compiled with. The information in this MSDSprovides guidance on health, safety and environmental aspects of the product and should not be construed as anyguarantee of technical performance or suitability for particular applications. The Environmental Protection (Dutyof Care) Regulations 1992 (SI 1992:2839). Further information and relevant advice can be found in: The Control ofSubstances Hazardous to Health Regulations 1988 (SI1988:1657). The Highly Flammable Liquids and liquefied




6/6

Petroleum Gases Regulations 197 (SI 1972:917). The Manual Handling Operations Regulations 1992 (SI1992:2793). Storage of Flammable Liquids in Containers, HS(G)51. Storage of Packaged Dangerous Substances,HS(G)71. The selection, use and maintenance of respiratory protective equipment: A practical guide HS(G)53.



JOTAFLOOR PU TOPCOAT - COMP. B

1/6


Approved for use



TRADE NAME JOTAFLOOR PU TOPCOAT - COMP. BAPPLICATION Two-pack, polyurethane topcoat.

ART-NO PM3435




1 N-BUTYL ACETATE 123-86-4 2,5-10 N 10-66-672 HEXAMETHYLENE-DI-ISOCYANATE 822-06-0 <0.5 N T,23-36/37/38-42/434 ALIPHATIC POLYISOCYANATE 28182-81-2 50-100 N Xn,42/435 AROMATIC HYDROCARBONS C9-C12 64742-95-6 2,5-10 N XnN,10-37-65-66-67-

51/53




Harmful

FLAMMABLE. HARMFUL BY INHALATION. MAY CAUSE SENSITIZATION BY INHALATION ANDSKIN CONTACT.For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL




2/6




EYE CONTACTRemove any contact lenses. Hold the eyelids apart. Irrigate copiously with clean, fresh water for at least 10 minutes.Seek medical advice.


MEDICAL INFORMATION Risk of chemical pneumonia by aspiration. Keep attention: danger of lung damage. General health examination.Professional evaluation of the work station. Persons handling isocyanates in their work should be examined by aphysician once a year.



FIRE AND EXPLOSION HAZARDSFire will produce dense black smoke containing hazardous products of combustion (see Section 10). Burning maygive decomposition of toxic vapours.

PERSONAL PROTECTION WHEN FIREFIGHTINGWear



OTHER INFORMATIONExclude sources of ignition and ventilate the area. Avoid breathing vapours. Refer to protective measures listed insections 7 and 8. Place in container for disposal according to local regulations (see section 13). Contain and collectspillage with non-combustible absorbent materials, e.g. sand, earth, vermiculite and diatomaceous earth. Do notallow to enter drains or watercourses. Contaminated area should be cleaned immediately with a agent fordestruction.A possible (inflammable) destruction agent is: 45 vol% water, 50 vol% ethanol or isopropanol, 5 vol%ammonia solution.Et annet mulig (ikke brannfarlig) destruksjonsmiddel er: 5 vol% natriumkarbonat og 95 vol%vann. Add the same decontaminant to the remnants and let stand for several days until no further reaction in nonsealed container. Close the container and follow the instructions in point 13 about handling of waste.If the productenters drains or sewers, the local water company should be contacted immediately; in the case of contamination ofstreams, rivers or lakes, the Environmental Agency.


HANDLING ADVICEPersons with a history of asthma, allergies, chronic or recurrent respiratory disease should not be employed in anyprocess that keeps isocyanates.The Manual Handling Operations Regulations may apply to the handling ofcontainers of this product. Order.nr 536: "Production and use of polyuretanproducts (isocyanates)", and order.nr313 Regulations of diisocyanates.Vapours are heavier than air and may spread along floors. Vapours may formexplosive mixtures with air. Prevent the creation of flammable or explosive concentrations of vapour in air andavoid vapour concentration higher than the occupational exposure limits. The product should not be used in vicinity




3/6

of open flames or other sources of ignition. Use explosion-proof electrical equipment. The product may chargeelectrostatically. Always use earth (ground) wire when transferring from one container to another. Personnel shouldwear anti-static clothing and footwear. Floors should be electrically conductive. Keep container tightly closed.Exclude sources of heat, sparks and open flame. Use non-sparking tools. Avoid skin and eye contact. Avoidinhalation of vapour and spray mist. Smoking, eating and drinking are forbidden in the work area.For personalprotective equipment see Section 8. Always keep in containers made of the same material as the supply container.Never use pressure to empty the container, it is not a pressure vessel. Electrical equipment should be protected toappropriate standards. Special caution should be payed to minimize contact with humidity from air or water: CO2will be produced in closed containers that can form overpressure.Halfful containers should be carefully handled.

STORAGEStore in accordance with the regulations for flammable materials. Observe the label precautions. Store in a dry, coldand well ventilated place away from sources of heat, ignition and direct sunlight. Store separately from oxidisingagents and strongly alkaline and strongly acidic materials. No smoking. Containers which are opened should beproperly resealed and kept upright to prevent leakage. Prevent unauthorised access. Always use the same packagingas originally used.



HEXAMETHYLENE-DI-ISOCYANATE 822-06-0 0,02 mg/m3;Sens

AROMATIC HYDROCARBONS C9-C12 64742-95-6 566,0 mg/m3 850,0 mg/m3

EXPOSURE CONTROLProvide adequate ventilation. Where reasonably practicable this should be achieved by the use of local exhaustventilation and good general extraction. Use respiratory protection when the concentration of solvents/compoundsexceeds the Occupational Exposure Limit. Spray mist contains all substances of the product and must not beinhaled. OEL's are taken from the current version of EH40 (by Health & Safety Executive, UK). Wash hands at theend of workday and before eating, smoking and toiletvisit.Take immediately off contaminated clothing. Clothesshould be kept apart and washed before used.

RESP. PROTECTIONFresh air mask have to be used when spraying, even if there is good ventilation.With other handlig methods thanspraying: When good ventilation fresh air mask could be replaced with protectionmask and combination cartridgeA3.


HAND PROTECTIONUse PVA or viton gloves.Barrier creams may help to protect exposed areas of the skin but are not substitutes forfull physical protection. Never apply barrier cream to contaminated skin.





4/6












MATERIALS TO AVOIDHold the product away from oxidizer agent, strong acid and strong basic materials.Exothermic reactions can existwith amines and alcohol .The product reacts slowly with water and will form CO2. Explosion can occure in closedcontainers.

HAZARDOUS DECOMPOSITION PRODUCTSIn a fire , hazardous decomposition products such as free isocyanates, amines, nitriles, cyanides, nitrous gases andcarbon monoxide.


GENERALProducts containing isocyanates may cause acute irritation and sensitisation of respiratory system, reduced tidalvolume tightness of chest, and asthmatic reactions.Sensitized persones can as followed by this show asmaticsymptoms by exposure of atmosfæric consentrasions under administrative norm.Repeated exposure can makepermanent damage on respiratorisystem.

INHALATIONExposure to organic solvent vapours may result in adverse health effects such as irritation of the mucous membraneand the respiratory system and adverse effects on the renal and central nervous system. Symptoms and signs includeheadache; dizziness, fatigue, muscular weakness, drowsiness and in extreme cases, loss of consciousness. Maycause sensitizing by inhalation. By heating, inhalation of isocyanate vapours may affect the lungs and give rise toasthma. Aerosols containing isocyanate may give allergic reactions in the respiratory organs.

SKIN CONTACTRepeated or prolonged contact with the product may lead to removal of natural fats from the skin resulting in non-allergic contact dermatitis and absorption through the skin. Repeated or prolonged contact with skin may causesensitisation. Organic svents may defat the skinMay cause sensitizing by skin contact.

EYE CONTACTSplashes in the eyes may cause irritation and reversible local damage. Splashes in the eyes may cause irritation andreversible damage.





5/6






13. DISPOSAL

Wastes, including emptied containers, are controlled wastes and should be disposed of in accordance withregulations made under the Control of Pollution Act and the Environmental Protection Act. Do not allow into drainsor water courses. Remnants in used packaging should be neutralized as described in chapter 6.

WASTEGROUP08 00 00 WASTES FROM THE MANUFACTURE, FORMULATION, SUPPLY AND USE (MFSU) OFCOATINGS (PAINTS, VARNISHES AND VITREOUS ENAMELS), ADHESIVE, SEALANTS ANDPRINTING INKS. 08 05 00 AVFALL SOM INNEHOLDER ISOCYANATER



HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk







6/6

Classification

Harmful

COMPOSITION HEXAMETHYLENE-DI-ISOCYANATE (<0.5), ALIPHATIC POLYISOCYANATE (50-100)

R-PHRASESR10 Flammable. R20 Harmful by inhalation. R42/43 May cause sensitization by inhalation or by skin contact.

S-PHRASESS23 Do not breathe vapour/spray. S24 Avoid contact with skin. S37-Wear suitable gloves. S38 In case ofinsufficient ventilation, wear suitable respiratory equipment. P91 Contains isocyanates - See information suppliedby the manufacturer: The information is supplied in the present MSDS.



PRINTEDOUT:

19/11/2001

VENDOR NOTES The information contained in this MSDS is based on the present state of knowledge and current nationallegislation. As the specific conditions of use of the product are outside the supplier's control, the user is responsiblefor ensuring that the requirements of relevant legislation are compiled with. The information in this MSDSprovides guidance on health, safety and environmental aspects of the product and should not be construed as anyguarantee of technical performance or suitability for particular applications. The Environmental Protection (Dutyof Care) Regulations 1992 (SI 1992:2839). Further information and relevant advice can be found in: The Control ofSubstances Hazardous to Health Regulations 1988 (SI1988:1657). The Highly Flammable Liquids and liquefiedPetroleum Gases Regulations 197 (SI 1972:917). The Manual Handling Operations Regulations 1992 (SI1992:2793). Storage of Flammable Liquids in Containers, HS(G)51. Storage of Packaged Dangerous Substances,HS(G)71. Ready-to-use paints containing isocyanates may have an irritant effect on mucous membranes -especially on breathing organs - and cause hypersensitivity reactions. The selection, use and maintenance ofrespiratory protective equipment: A practical guide HS(G)53.

Technical DataJOTAFLOOR PU TOPCOAT

Product descriptionA two-pack, high solids polyurethane constituting the finishing layer of the Jotafloor Traffic Deck System. Offers excellent gloss and colour retention and resistance to contaminants normally found in a car park/traffic deck situation. VOC compliant (350-380 g/l dependant on colour) - 1990 EPA - PG6/23(95).

Recommended useFor use in conjunction with Jotafloor products comprising the Jotafloor Traffic Deck System. Can be spray, brush or roller applied in two or three coats depending on the volume of traffic expected. This product can also be used independently of the Jotafloor Traffic Deck System. A wide range of colours are available. Typical areas include:

Underground car parksl

Rampsl

External traffic deckl

Concrete balconiesl

Parking baysl

Pedestrian walkwaysl



12,6 7,9 10,5

Physical propertiesColour According to colour card and Multicolor tinting system (MCI)Solids (vol %)* 63 ± 2 Flash point 34ºC ± 2 (Setaflash)Gloss GlossyGloss retention ExcellentWater resistance Very goodAbrasion resistance Very goodSolvent resistance Very good Chemical resistance Very good Flexibility Very good


Surface preparation



Other surfacesConcrete surface preparation by using dust free captive blasting units, grinding equipment, sand blasting or high pressure water jetting is critical to achieving the right surface profile prior to paint application. Please contact your local Jotun office for more information.






Application data Mixing ratio (volume) 5 parts Comp. A (Base) to 1 part Comp. B (Curing agent).Pot life (23°C) 2½ hours Thinner/Cleaner Jotun Thinner No. 10Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi)Nozzle tip 0.35-0.55 mm (0.015-0.021")Spray angle 40-80ºFilter Check to ensure that filters are clean.Note Detailed mixing and application instructions can be found on the

relevant Product Information Sheet.

JOTAFLOOR PU TOPCOAT Page 2


Substrate temperature 0°C 5°C 10°C 23°C 40°CSurface dry 24 h 16 h 10 h 5 h 3 hThrough dry 48 h 24 h 16 h 7 h 3 hCured 24 d 21 d 14 d 7 d 4 d



The surface should be dry and free from any contamination or chalking prior to application of 1.the subsequent coat.


Typical paint systemJotafloor SealerJotafloor Glass FlakeJotafloor Non Slip AggregateJotafloor PU Topcoat

Jotafloor Damp BondJotafloor Glass FlakeJotafloor Non Slipp AggregateJotafloor PU Topcoat

Jotafloor Solvent Free PrimerJotafloor Glass FlakeJotafloor Non Slipp AggregateJotafloor PU Topcoat

Jotafloor Solvent Free Primer Jotafloor Non Slipp AggregateJotafloor PU Topcoat

1 x 40 µm1 x 300 µm

2 x 70 µm

1 x 100 µm1 x 300 µm

2 x 70 µm

1 x 150 µm1 x 400 µm

2 x 70 µm

1 x 40 µm

2 x 70 µm



(Dry Film Thickness)(Dry Film Thickness)(Available in various sizes)(Dry Film Thickness)

(Dry Film Thickness)(Available in various sizes)(Dry Film Thickness)





Packing size15 ltr. Comp. A and 3 ltr. Comp. B4 l ltr. Comp. A and 0.8 ltr. Comp. BPacking may vary from country to country according to local requirements.











Technical DataJOTAFLOOR RAPID DRY

Product descriptionJotafloor Rapid Dry is a single component, fast drying, glossy alkyd topcoat, offering durability not normally associated with alkyd floor products.

Recommended useIdeal for floors requiring a fast, easy to use, light duty floor coating where drying time is at premium:

Exhibition hallsl

In-house eventsl

Concerts/Sports venues/Open Days etc.l

Also as a general purpose floor coating offering protection from mild spillages and light pedestrian traffic.

Factoryl

Warehousel

Domestic Applicationsl

Garage show roomsl



16,8 8,4 12

Physical propertiesColour Limited numberSolids (vol %)* 42 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss GlossyGloss retention GoodWater resistance LimitedAbrasion resistance GoodFlexibility Good*Measured according to ISO 3233:1998 (E)

JOTAFLOOR RAPID DRY Page 1

Surface preparation



Other surfacesThe surface must be sound, clean and dry. Surface contamination to be removed by detergent and fresh water cleaning.






Application data Mixing ratio (volume) Single packThinner/Cleaner Jotun Thinner No. 7Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.43-0.48 mm (0.017-0.019")Spray angle 40-80°Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateMaximum dry to recoat: Within 8 hours or after 1 week

Substrate temperature 5°C 10°C 23°C 40°CSurface dry 60 min 30 min 20 min 15 minThrough dry 4 h 1 h 1 h 1 hDry to recoat, minimum

1 3 h 2,5 h 2 h 1 h



Jotafloor Rapid Dry can be recoated with coatings containing xylene or stronger solvents 1.within 8 hours or after 7 days after application.The surface should be dry and free from any contamination prior to application of the 2.subsequent coat.


Typical paint systemJotafloor Rapid Dry 2-3 x 35 µm (Dry Film Thickness)















Technical DataJOTAFLOOR SCREED

Product descriptionJotafloor Screed is a high performance, trowel applied, three component, solvent free epoxy floor coating offering exceptional strength characteristics, resistance to a range of chemicals, and superior abrasion/wear properties. Generally applied at 5 mm thickness and above. (Seek advice from Jotun Technical Dept.)

Recommended useThe high strength impervious finish makes Jotafloor Screed ideal for heavy industrial areas such as:

Steelworksl

Engineering plantsl

Chemical production areasl

Oil refineriesl

Dairiesl

Also ideally suited where heavy traffic is expected or a durable non-slip finish is required. Jotafloor Screed may be overcoated with Jotafloor Topcoat or Jotafloor Coating if different colours are required. Jotafloor Screed exhibits very high bond strength and adhesion characteristics making it an ideal repair material for concrete and floor joint edges.



0,25 0,17 0,2

CommentsJotafloor Screed can be applied at higher thicknesses to suit specific requirements. Request further information from Jotun Technical Department.

Physical propertiesColour Colour of the graded aggragateSolids (vol %)* 98 ± Flash point >100ºC (Setaflash)Water resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Check chemical resistance values on Jotafloor chemical

resistance chart.


Surface preparation




Condition during applicationThe temperature of the substrate should be minimum 12°C (preferably 15°C)and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. The moisture in the concrete should not exceed 4 % (by weight). The coating should not be exposed to oil, chemicals or mechanical stress until fully cured.

Application methodsOther

Nylon or steel trowel.

Mixing ratio (volume) 1.7 l Comp. A (base) to be mixed thoroughly with 1 l Comp. B (curing agent) before adding 24 kg graded aggregates. NO PART MIXING

Mixing Mix the resin and curing agent well before adding the aggregate. A forced action drill and appropriate mixing paddle should be used. The three components are supplied in a 20 ltr. can that can be used as the mixing vessel.

Pot life (23°C) 25 min. (Comp. A + Comp. B only), 40 min. (mix. with aggregate). Cleaner Jotun Thinner No. 17 or fresh water.Note It is essential to apply Jotafloor Screed onto Jotafloor Screed Primer

whilst the primer is still "tacky". See separate Technical Data Sheet.

This product should be applied by a trained specialist. Jotun can offer a list of Licensed Applicators on request to your local Jotun office.






The given data must be considered as guidelines only. The actual drying time/times before

JOTAFLOOR SCREED Page 2

recoating may be shorter or longer, depending on film thickness, ventilation, humidity, underlying paint system, requirement for early handling and mechanical strength etc. A complete system can be described on a system sheet, where all parameters and special conditions could be included.

Typical paint systemJotafloor Screed PrimerJotafloor Screedand eventuallyJotafloor Topcoat

1 x 150 µm1 x 5000 µm

1-2 x 50 µm





Packing size1.7 l Comp. A (base) and 1 l Comp. B (curing agent). 24 kg graded aggregate.Packing may vary from country to country according to local requirements.










JOTAFLOOR SCREED Page 3

Technical DataJOTAFLOOR SCREED PRIMER

Product descriptionJotafloor Screed Primer is a two pack solvent free, epoxy resin primer exhibiting excellent penetration properties in cementitious substrates and promotes good adhesion for Jotafloor Screed.

Recommended useAs a primer/sealer for Jotafloor Screed.


Film thickness, dry (µm) 150Film thickness, wet (µm) 150Theoretical spreading rate (m²/l)

6,66

Physical propertiesColour TransparentSolids (vol %)* 98 ± Flash point >100ºC (Setaflash)Water resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Check chemical resistance values on Jofloor chemical

resistance chart.


Surface preparation





Application methodsBrush Recommended Roller Recommended

Application data Mixing ratio (volume) 2 parts Comp. A (base) to be mixed thoroughly with 1.2 parts

Comp. B (curing agent). NO PART MIXINGPot life (23°C) 25 min. Cleaner Jotun Thinner No. 17 or fresh water. (No thinning is allowed).Note It is essential to apply Jotafloor Screed onto Jotafloor Screed Primer

whilst the primer is still "tacky".

Jotafloor Screed PrimerJotafloor Screedand eventuallyJotafloor Topcoat

1 x 150 µm1 x 5000 µm

1-2 x 50 µm





Packing size2.5 l Comp. A (base) and 1.5 l Comp. B (curing agent).Packing may vary from country to country according to local requirements.



JOTAFLOOR SCREED PRIMER Page 2








JOTAFLOOR SCREED PRIMER Page 3

Technical DataJOTAFLOOR SEALER

Product descriptionJotafloor Sealer is a transparent two-pack epoxy sealer/primer exhibiting excellent penetration properties to ensure good adhesion between Jotafloor products and most masonry surfaces.

Recommended useAs a sealer/primer for subsequent Jotafloor products or for use independently as a dustbinder for concrete floors.



12,5 7,7 10

CommentsSubstrate porosity and profile will affect practical coverage rates.

Physical propertiesColour TransparentSolids (vol %)* 40 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss GlossyWater resistance Very goodSolvent resistance Excellent Chemical resistance Excellent Check chemical resistance values in Jotafloor chemical

resistance chart.Flexibility Good


Surface preparation





JOTAFLOOR SEALER Page 1

Condition during applicationThe temperature of the substrate should be minimum 10°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to ensure proper drying. The moisture content in the concrete should not exceed 4 % (by weight). The coating should not be exposed to oil, chemicals or mechanical stress until fully cured.





(curing agent).NO PART MIXING

Mixing ½ hour prior to use.Pot life (23°C) 8 hours (reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.46 - 0.58 mm (0.018-0.023")Spray angle 40-80°Filter Check to ensure that filters are clean


Substrate temperature 10°C 23°C 40°CSurface dry 2 h 1 h 0.5 hThrough dry 14 h 6,5 h 3 hCured 14 d 7 d 2 d


1 The surface should be free from chalking and contamination prior to application. Best intercoat adhesion occurs when the subsequent coat is applied before the preceding coat has cured.



Typical paint systemAs dust binder:Jotafloor Sealer Nominal

For coloured finish:Jotafloor SealerJotafloor TopcoatorJotafloor SealerJotafloor CoatingorJotafloor SealerJotafloor SL Universal

1 x 40 µm2 x 50 µm

1-2 x 40 µm1 x 300 µm

1-2 x 40 µm1 x 2000-4000 µm




Note: Thickness of the finished system will vary depending on use of the finished floor. Consult your local Jotun Office for advice.




Packing size16 l Comp. A (base) and 4 l Comp. B (curing agent) 4 l Comp. A (base) and 1 l Comp. B (curing agent)Packing may vary from country to country according to local requirements.




Technical DataJOTAFLOOR SL UNIVERSAL

Product descriptionJotafloor SL Universal is a high performance, self smoothing, solvent free, three component, seamless epoxy coating capable of being applied at varying thicknesses to suit the final use of the floor. Jotafloor SL Universal offers excellent chemical, abrasion and impact resistance.

Recommended useJotafloor SL Universal has a wide range of application uses ranging from light industrial areas to floors requiring long lasting protection from abrasion and heavy loads. Typical areas include:

Warehousesl

Garagesl

Dairiesl

Factoriesl

Laboratoriesl

Aircraft hangersl

Plant roomsl

Food manufacturing plantsl

The product is designed to be applied at thicknesses between 2mm and 5mm. Greater depths can be achieved but advice should be sought from your local Jotun Technical Department.



0,65 0,2 0,5

Physical propertiesColour Cream 908, Light Grey 967, Papyrus 980, Yellow 414 and Red

2230Solids (vol %)* 98 ± 2 Flash point > 100ºC (Setaflash)Gloss GlossyWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Check chemical resistance values in Jotafloor chemical

resistance chart.


Surface preparation






Application methodsOther Steel trowel or height adjustable steel spreader. Once the desired film thickness is

achieved, it is very important to pierce the coating with a spiked roller, this will help to avoid air bubbles.

Mixing ratio (volume) 8.6 l Comp. A (base) to be mixed thoroughly with 4.3 l Comp. B (curing agent) and then add 14.2 kg graded aggregates. NO PART MIXING

Mixing Mix the resin and curing agent well before adding the aggregate. Use a slow speed drill and mixing paddle. Mix the three components in the container supplied. Pour the full contents of the mixed material on to the floor immediately after mixing is completed.

Pot life (23°C) Jotafloor SL Universal Comp. B (20) 10 min. (30 min. after poured on to the floor).Jotafloor SL Universal Comp. B (40) 20 min. (45 min. after poured on to the floor).

Cleaner Jotun Thinner No. 17Note This product should be applied by a trained specialist. Jotun can


JOTAFLOOR SL UNIVERSAL Page 2

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateCuring agent comp. B (20):




Curing agent comp. B (40):Substrate temperature 15°C 23°C 40°CSurface dry 8 h 5 h 2 hThrough dry 32 h 20 h 8 hCured 12 d 9 d 3 d


Dry to recoat, maximum 96 d 3 d 36 d



Typical paint systemJotafloor SealerJotafloor SL UniversalorJotafloor Solvent Free PrimerJotafloor SL Universal

1-2 x 40 µm1 x 2000 µm

1-2 x 100 µm1 x 5000 µm








Packing size8.6 l. Comp. A (base) and 4.3 l. Comp. B (curing agent). 14.2 kg graded aggregate.Packing may vary from country to country according to local requirements.











Technical DataJOTAFLOOR SOLVENT FREE PRIMER

Product descriptionJotafloor Solvent Free Primer is a transparent two-pack epoxy primer exhibiting excellent penetration properties to ensure good adhesion between Jotafloor products and host masonry surfaces.

Recommended usePrimer/sealer on concrete masonry, normally under Jotafloor Topcoat, Jotafloor SL Universal and Jotafloor Coating.



20 5 10

Physical propertiesColour TransparentSolids (vol %)* 98 ± Flash point > 100ºC (Setaflash)Gloss GlossyWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Check chemical resistance values in Jotafloor chemical

resistance chart.


Surface preparation





Application methodsBrush Recommended Roller Recommended


(curing agent). NO PART MIXINGPot life (23°C) Jotafloor Solvent Free Primer Comp. B (20) 10 min. (30 min. after

poured on to the floor).Jotafloor Solvent Free Primer Comp. B (40) 20 min. (45 min. after poured on to the floor).

Thinner/Cleaner Jotun Thinner No. 17

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateCuring agent comp. B (20):




Curing agent comp. B (40):Substrate temperature 15°C 23°C 40°CSurface dry 12 h 10 h 6 hThrough dry 42 h 30 h 18 hCured 12 d 9 d 3 d





JOTAFLOOR SOLVENT FREE PRIMER Page 2

Typical paint systemJotafloor Solvent Free PrimerJotafloor SL UniversalorJotafloor Solvent Free PrimerJotafloor Topcoat

1-2 x 100 µm1 x 2000 µm

1-2 x 100 µm1-2 x 50 µm







Packing size2.6 l Comp. A (base) and 1.3 l Comp. B (curing agent). Packing may vary from country to country according to local requirements.










JOTAFLOOR SOLVENT FREE PRIMER Page 3

Technical DataJOTAFLOOR TOPCOAT

Product descriptionJotafloor Topcoat is a two-pack epoxy floor coating offering good chemical resistance, durability and available in a variety of colours. May also be used as a final coating on Jotafloor Screed.

Recommended useAreas requiring a dust free, hard wearing and aesthetically pleasing floor coating such as:

Warehousesl

Garagesl

Workshopsl

Production areasl

Excellent adhesion to primed concrete, mortar, screed and a limited number of other surfaces make Jotafloor Topcoat ideal for many uses in light to medium industrial areas.



12,5 8,3 10

Physical propertiesColour White, Grey 38, Black, Yellow 2, Red 49, Green 137 and available

in Multicolor IndustrySolids (vol %)* 50 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss GlossyGloss retention FairWater resistance Very goodAbrasion resistance Very goodSolvent resistance Excellent Chemical resistance Excellent Check chemical resistance values on Jotun chemical

resistance chart.Flexibility Good


JOTAFLOOR TOPCOAT Page 1

Surface preparation










(curing agent)Mixing ½ hour prior to use.Pot life (23°C) 8 hours. (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.46 - 0.58 mm (0.018-0.023")Spray angle 40 - 80ºFilter Check to ensure that filters are clean.


Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 10°C 23°C 40°CSurface dry 2,5 h 1,5 h 0,5 hThrough dry 14 h 6,5 h 3 hCured 14 d 7 d 3 d


The surface should be free from chalking and contamination prior to application. Best 1.intercoat adhesion occurs when the subsequent coat is applied before the preceding coat has cured. If this is exceeded it may be necessary to roughen the surface.


Typical paint systemJotafloor SealerJotafloor Topcoat

1 x 40 µm1-2 x 50 µm





Packing size16 l Comp. A (base) and 4 l Comp. B (curing agent)4 l Comp. A (base) and 1 l Comp. B (curing agent)Packing may vary from country to country according to local requirements.




Technical DataJOTAGUARD 85

Product descriptionJotaguard 85 is a two-pack epoxy coal-tar coating.

Recommended useSteel structures permanently or frequently submerged in water, inside crude oil tanks, sewage treatment plants, buried concrete structures etc. Excellent in combination with cathodic protection.



8,7 3,3 6,5

Physical propertiesColour Black, BrownSolids (vol %)* 65 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss SemiflatWater resistance ExcellentAbrasion resistance GoodChemical resistance Good (Discolouration may occur)Flexibility GoodCompatibility withcathodic protection Very good*Measured according to ISO 3233:1998 (E)

Surface preparation






JOTAGUARD 85 Page 1

Condition during applicationThe temperature of the substrate should be minimum 5°C and at least 3ºC above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is required in confined areas to ensure correct drying.



Application data Mixing ratio (volume) 4 parts Comp. A (base) to be thoroughly mixed to 1 part Comp. B

(curing agent)Pot life (23°C) 8 hours. (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.53 - 0.79 mm (0.021-0.031")Spray angle 65 - 80°Filter Check to ensure that filters are clean.




Dry to recoat, maximum 1,2 7 d 7 d 7 d 4 d

The surface should be free from chalking and contamination prior to application. At interior 1.exposure note that best intercoat adhesion occurs when the subsequent coat is applied before the preceding coat is cured. At exterior exposure, the chalking effect especially from the sunlight limits the maximum dry to recoat time.Maximum figures refer to exterior surfaces. For interior surfaces, there are no limit.2.


JOTAGUARD 85 Page 2

Typical paint systemJotaguard 85 3 x 100 µm (Dry Film Thickness)Other systems may be specified, depending on area of use













JOTAGUARD 85 Page 3

Technical DataJOTAGUARD SPECIAL 70

Product descriptionJotaguard Special 70 is a two-pack epoxy coal-tar coating.

Recommended useSteel structures permanently or frequently submerged in water, inside crude oil tanks, sewage treatment plants, buried concrete structures etc. Excellent in combination with cathodic protection.



7 3,5 4,7

Physical propertiesColour Black, BrownSolids (vol %)* 70 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss SemiflatWater resistance ExcellentAbrasion resistance GoodChemical resistance Good (Discolouration may occur)Flexibility GoodCompatibility withcathodic protection Very good*Measured according to ISO 3233:1998 (E)

Surface preparation






JOTAGUARD SPECIAL 70 Page 1




Application data Mixing ratio (volume) 2 parts Comp. A (base) to be thoroughly mixed to 1 part Comp. B

(curing agent)Pot life (23°C) 4 hours. (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.53 - 0.79 mm (0.021-0.031")Spray angle 65 - 80°Filter Check to ensure that filters are clean.



Dry to recoat, minimum 1,3 72 h 36 h 12 h 8 h

Dry to recoat, maximum 7 d 7 d 7 d 5 d

Best intercoat adhesion occurs, when the subsequent coat is applied before preceding coat 1.has cured. If the coating has been exposed to direct sunlight for some time, special attention must be paid to removal of chalking, surface cleaning and mattening/removal of the surface layer in order to obtain good adhesion.



Typical paint systemJotaguard Special 70 2 x 150 µm (Dry Film Thickness)Other systems may be specified, depending on area of use














Technical DataJOTAGUARD SPECIAL 90

Product descriptionJotaguard Special 90 is a high solid, two-pack epoxy coal-tar coating.

Recommended useSubmerged steel structures, buried concrete or steel structures. Excellent protection against corrosion. Excellent in combination with cathodic protection.



4,5 1,8 3

Physical propertiesColour Black , BrownSolids (vol %)* 90 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss SemiflatWater resistance ExcellentAbrasion resistance GoodSolvent resistance Good (discoloration)Chemical resistance Good Flexibility GoodCompatibility withcathodic protection Excellent



Surface preparation









Application data Mixing ratio (volume) 7 parts Comp. A (base) to be mixed thoroughly with (by volume)

3 part Comp. B (curing agent)Pot life (23°C) 1 hour (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 20 MPa (200 kp/cm² 2800 psi)Nozzle tip 0.53 - 0.79mm (0.021-0.031")Spray angle 40 - 80°Filter Check to ensure that filters are clean.





Dry to recoat, maximum 1,2 7 d 7 d 5 d

Best intercoat adhesion occurs, when the subsequent coat is applied before preceding coat 1.has cured. If the coating has been exposed to direct sunlight for some time, special attention must be paid to removal of chalking, surface cleaning and mattening/removal of the surface layer in order to obtain good adhesion.


Typical paint systemJotaguard Special 90 2 x 300 m (Dry Film Thickness)Other systems may be specified, depending on area of use









JOTAMASTIC 87 COLD CLIMATE - COMP. B

1/6


Approved for use



TRADE NAME JOTAMASTIC 87 COLD CLIMATE - COMP. BAPPLICATION Two-pack surface tolerant epoxy primer for cooler temperatures (-5°C)

ART-NO PM3937




1 XYLENE, mixed isomers 1330-20-7 10-25 N Xn,10-20/21-382 N-BUTANOL 71-36-3 25-50 N Xn,10-22-37/38-41-67




Harmful

FLAMMABLE. HARMFUL IF SWALLOWED. IRRITATING TO RESPIRATORY SYSTEM AND SKIN.RISK OF SERIOUS DAMAGE TO EYES . VAPOURS MAY CAUSE DROWSINESS AND DIZZINESS.For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL




2/6



















3/6





N-BUTANOL 71-36-3 154,0 mg/m3;Sk -




HAND PROTECTIONUse butyl rubber/ viton gloves.Barrier creams may help to protect exposed areas of the skin but are not substitutesfor full physical protection. Never apply barrier cream to contaminated skin.





4/6


Form Liquid.Colour Yellowish.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 1.01Expl. limit LEL-UEL., %-%: 1.10 - 11.30 Solubility in water


















CANCERThe product contains ethylbenzene. IARC has classified it as a possible human carcinogen (Group 2B) based on




5/6

sufficient evidence for carcinogenicity in experimental animals, but inadequate evidence for cancer in exposedhumans.



13. DISPOSAL





HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk







6/6

Classification

Harmful

COMPOSITION N-BUTANOL (25-50)

R-PHRASESR10 Flammable. R22 Harmful if swallowed. R37/38 - Irritating to respiratory system and skin. R41 Risk of seriousdamage to eyes. R67 Vapours may cause drowsiness and dizziness.

S-PHRASESS23 Do not breathe vapour/spray. S26 In case of contact with eyes, rinse immediately with plenty of water and seekmedical advice.S38 In case of insufficient ventilation, wear suitable respiratory equipment. S39 Wear eye/faceprotection.



PRINTEDOUT:

31/08/2001




JOTAMASTIC 87 STANDARD - COMP. B 1. PRODUCT AND COMPANY



TRADE NAME JOTAMASTIC 87 STANDARD - COMP. BAPPLICATION Two-pack. modified epoxy based paint

ART-NO PM3224




1 3-AMINOMETHYL-3,5,5-TRIMETHYLCYCLOHEXYLAMINE 2855-13-2 10-25 N C,21/22-34-43-52/532 BENZYL ALCOHOL 100-51-6 10-25 N Xn,20/223 2,2,4 TRIMETHYL HEXAMETHYLENE DIAMINE 25620-58-0 2,5-10 N C,22-34-43-52/53




Corrosive

HARMFUL BY INHALATION, IN CONTACT WITH SKIN AND IF SWALLOWED. CAUSES BURNS. MAY CAUSE SENSITISATION BY SKIN CONTACT. For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL

1 / 6



JOTAMASTIC 87 STANDARD - COMP. B In all cases of doubt, or when symptoms persist, seek medical attention. Obtain advice via telephone; before the patient is transported to a doctor or hospital. Never give anything by mouth to an unconscious person.



EYE CONTACTRemove any contact lenses. Hold the eyelids apart. Rinse with lukewarm water for 1 hour. Seek immediately medical advice.Seek medical advice if symptoms persist.


MEDICAL INFORMATION Obtain miedical surveillance concerning burn injuries in mouth and throat. Aspiration hazard by vomiting. All poisoned persons should be transported in recovery position. An authorised person should acompany under the transport. Stomach-rinsing may bee considered, for instance with an antioxydant. Eye injuries should be treated with chloramphenicol or antiseptic eye treatment. Local anesthetica may be given to relieve pain. Regulary medical control. Person developing a skin rash are to be directed to a dermatologist for examination.










2 / 6



JOTAMASTIC 87 STANDARD - COMP. B the same material as the supply container. The Manual Handling Operations Regulations may apply to the handling of containers of this product.




RESP. PROTECTIONWhen workers are facing concentrations above the occupational exposure limit they must use appropriate certified respirators.Use respiratory protective mask with charcoal and dust filter (A2/P2) when spraying this product.


HAND PROTECTIONUse gloves of viton or 4H gloves.Barrier creams may help to protect exposed areas of the skin but are not substitutes for full physical protection. Never apply barrier cream to contaminated skin.



Form Liquid. Colour Yellowish. Odour Organic solvent. Solubility Organic solvent. Melting point/range - Density 1,30Expl. limit LEL-UEL., %-%: 1,3 - 13,0 Solubility in waterVapor pressure Saturation conc.Decomposition temp. Rel. density sat. air (air=1)pH Solution Boiling point/range 205ºCFlash point >100ºC pH concentrate -Molecular weight ViscosityIgnition temp 435ºC Smelling limits lo-hiRel. vapor density (air=1) Rel. evap. velocityAir reactive Water reactive





3 / 6



JOTAMASTIC 87 STANDARD - COMP. B 11. TOXICOLOGICAL INFORMATION


INHALATIONExposure to vapours may result in adverse health effects such as irritation of the mucous membrane and the respiratory system.

SKIN CONTACTProlonged contact may cause burn damage. Products containing amines irritates the skin and may lead to allergic eczema.The allergic response may occur after a short periode of contact.


INGESTIONAccidental ingestion may cause vomiting and abdominal pains. May cause burn damage to mucous membrane, esophagus and stomach. 12. ECOLOGICAL INFORMATION







2,2,4-trimethylhexametylendiamine:Fish: LC50 (96 h) = 1000 mg/lDaphnia: EC50 (24 h) = 31,5 mg/lAlgea: EC50 (72 h) = 29,5 mg/lBacteria: IC50 (3 h) = 100 mg/l

OTHER INFORMATIONDo not discharge the product to sewer or drains.The product contains components which are harmful to aquatic organisms, see point 2.

13. DISPOSAL

Wastes, including emptied containers, are controlled wastes and should be disposed of in accordance with regulations made under the Control of Pollution Act and the Environmental Protection Act. Do not allow into drains or water courses.


4 / 6



JOTAMASTIC 87 STANDARD - COMP. B 14. TRANSPORT INFORMATION

PROPER SHIPPING NAME AMINES, LIQUID, CORROSIVE N.O.S. (isophorone diamine,2,2,4-trimethyl hexamethylene diamine.)


ADR (Road)UN No. 2735 Dang. goodsClass 8, PG III Label 8Haz. id. no 80 Marginno.

RID (Railway)UN No. 2735 Dang. goodsClass 8, PG III Label 8Haz..id.no 80

IMDG (Sea)UN No. 2735 Dang. goodsClass 8 Label 8Packaging group III EmS 8 - 05MFAG Marine PollutantSub. risk Page

IATA (Airplane)UN No. 2735 Dang. goodsClass 8 Sub. riskLabel Corrosive Packaging group III



Classification

Corrosive


R-PHRASESR20/21/22 - Harmful by inhalation, in contact with skin and if swallowed. R34 - Causes burns. R43 May cause sensitization by skin contact.




5 / 6



JOTAMASTIC 87 STANDARD - COMP. B PRINTED OUT:

19/11/2001

VENDOR NOTES The information contained in this MSDS is based on the present state of knowledge and current national legislation. As the specific conditions of use of the product are outside the supplier's control, the user is responsible for ensuring that the requirements of relevant legislation are compiled with. The information in this MSDS provides guidance on health, safety and environmental aspects of the product and should not be construed as any guarantee of technical performance or suitability for particular applications. Further information and relevant advice can be found in: The Environmental Protection (Duty of Care) Regulations 1992 (SI 1992:2839). The Control of Substances Hazardous to Health Regulations 1988 (SI1988:1657). The Highly Flammable Liquids and liquefied Petroleum Gases Regulations 197 (SI 1972:917). The Manual Handling Operations Regulations 1992 (SI 1992:2793). Storage of Flammable Liquids in Containers, HS(G)51. Storage of Packaged Dangerous Substances, HS(G)71. The selection, use and maintenance of respiratory protective equipment: A practical guide HS(G)53.

6 / 6

Technical DataJOTAMASTIC 87

Product descriptionJotamastic 87 is a two-pack surface-tolerant, abrasion resistant, high solids epoxy-based primer/topcoat which may be applied in high film thickness. Two hardeners (comp.B) are available, according to temperature conditions. Cures down to -5ºC by using cold climate comp. B. This product is a part of a complete system which is certified not to spread surface flames.

Recommended useSteel where blast cleaning may not be possible, and where gloss retention is of minor importance. Can be used alone or in combination with various systems of primers and topcoats. Gives excellent corrosion protection both in salt and fresh water. If exposed to sunlight chalking may occur.

Film thickness and spreading rateStandard comp. B Minimum Maximum TypicalFilm thickness, dry (µm) 150 300 200Film thickness, wet (µm) 180 365 245Theoretical spreading rate (m²/l)

5,5 2,7 4,1

Cold climate comp. B Minimum Maximum TypicalFilm thickness, dry (µm) 150 250 200Film thickness, wet (µm) 200 340 270Theoretical spreading rate (m²/l)

4,9 3 3,7

Physical propertiesColour Limited numberSolids (vol %)* 82 ± 2 Standard comp. B

74 ± 2 Cold climate comp. BFlash point 35ºC ± 2 Standard comp. B (Setaflash)

31ºC ± 2 Cold climate comp. B (Setaflash) Gloss SemiglossGloss retention FairWater resistance Very goodAbrasion resistance Very goodSolvent resistance Good Chemical resistance Very good Flexibility Good


JOTAMASTIC 87 Page 1

Surface preparation






Condition during applicationThe temperature of the substrate should be minimum +10°C (Std) (-5°C in CC) and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is required in confined areas to ensure proper drying.




Application data Mixing ratio (volume) 6 parts Comp. A to 1 part Standard Comp. B

4 parts Comp. A to 1 part Cold Climate Comp. B.Induction time 10 minutes.Pot life (23°C) 2 hours (standard Comp. B),

1 hour (cold climate hardner) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.58-0.79 mm (0.023-0.031")Spray angle 40-80°Filter Check to ensure that filters are clean.


Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateStandard comp. BSubstrate temperature 10°C 23°C 40°CSurface dry 8 h 4 h 2 hThrough dry 24 h 10 h 4 hCured 14 d 7 d 2 d



Cold climate comp. BSubstrate temperature -5°C 0°C 5°C 10°C 23°CSurface dry 24 h 18 h 12 h 6 h 2.5 hThrough dry 48 h 26 h 18 h 12 h 5 hCured 21 d 14 d 7 d 3 d 2 d


Dry to recoat, maximum 1 - - - - -



Typical paint systemJotamastic 87Hardtop AS

2 x 200 µm1 x 50 µm





Packing size16 l Comp. A and 2.7 l Standard Comp. B (16 l Comp. A and 4 l Cold Climate Comp. B)Packing may vary from country to country according to local requirements.


Technical DataJOTAMASTIC 87 ALUMINIUM

Product descriptionJotamastic 87 Aluminium is a two-pack surface-tolerant, abrasion resistant, high solids epoxy-based coating, for use in cases where optimum pretreatment is not feasible. It may be applied in high film thickness. Two hardeners (comp.B) are available, according to temperature conditions. Cures down to -5ºC by using cold climate comp. B. This product is a part of a complete system which is certified not to spread surface flames.

Recommended useSteel where blast cleaning may not be possible, and where gloss retention is of minor importance. Can be used alone or in combination with various systems of primers and topcoats. Gives excellent corrosion protection both in salt and fresh water. If exposed to sunlight chalking may occur.


5,8 2,9 4,4


4,7 2,8 3,5

Physical propertiesColour Aluminium and Aluminium redtonedSolids (vol %)* 87 ± 2 Standard comp. B

70 ± 2 Cold climate comp. BFlash point 40ºC ± 2 Standard comp. B (Setaflash)

31ºC ± 2 Cold climate comp. B (Setaflash Gloss SemiglossGloss retention FairWater resistance ExcellentAbrasion resistance Very goodSolvent resistance Good Chemical resistance Good Flexibility Good


JOTAMASTIC 87 ALUMINIUM Page 1

Surface preparation







Application methodsSpray Use airless spray (thin 10%)Brush May be used but care must be taken to achieve the specified dry film thickness.Roller May be used for small areas but not recommended for first primer coat, however


Application data Mixing ratio (volume) 5.5 parts Comp. A ( base) to 1 part Standard comp. B (hardener)

3.7 parts Comp. A (base) to 1 part Cold climate comp. B (hardener)Induction time 10 minutes.Pot life (23°C) 1½ hour (Standard comp. B) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.53 - 0.79 mm (0.021-0.031")Spray angle 65-80°Filter Check to ensure that filters are clean.


Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateStandard comp. BSubstrate temperature 10°C 23°C 40°CSurface dry 8 h 4 h 2 hThrough dry 24 h 10 h 4 hCured 14 d 7 d 2 d



Cold climate comp. BSubstrate temperature -5°C 0°C 5°C 10°C 23°CSurface dry 24 h 18 h 12 h 6 h 2,5 hThrough dry 48 h 26 h 18 h 12 h 5 hCured 21 d 14 d 7 d 3 d 2 d





Typical paint systemJotamastic 87 AluminiumJotamastic 87Hardtop AS

1 x 200 µm1 x 200 µm1 x 50 µm





Packing size14,7 l Comp. A and 2.7 l Standard Comp. B(14,7 l Comp. A and 4 l Cold Climate Comp. B) Packing may vary from country to country according to local requirements.


Technical DataJOTAMASTIC 87 GF

Product descriptionJotamastic 87 GF is a two-pack surface-tolerant, abrasion resistant, high solids epoxy-based primer/topcoat reinforced with glass flakes, which may be applied in high film thickness. Two hardeners (comp.B) are available, according to temperature conditions. Cures down to -5ºC by using cold climate comp. B. This product is a part of a complete system which is certified not to spread surface flames.

Recommended useAnticorrosive primer with improved abrasion resistance for steel structures, cures down to -5ºC by using cold climate comp. B. Useful on steel where blast cleaning may not be possible, and where gloss retention is of minor importance

Film thickness and spreading rateStandard climate hardener Minimum Maximum TypicalFilm thickness, dry (µm) 200 350 250Film thickness, wet (µm) 250 440 315Theoretical spreading rate (m²/l)

4 2,3 3,2

Cold climate hardener Minimum Maximum TypicalFilm thickness, dry (µm) 200 300 250Film thickness, wet (µm) 285 430 360Theoretical spreading rate (m²/l)

3,5 2,3 2,8

Physical propertiesColour White, Grey , Red Solids (vol %)* 80 ± 2 Standard climate hardener

70 ± 2 Cold climate hardenerFlash point 35ºC ± 2 Standard Comp. B (Setaflash)

31ºC ± 2 Cold Climate Comp. B (Setaflash) Gloss SemiglossGloss retention FairWater resistance Very goodAbrasion resistance ExcellentSolvent resistance Good Chemical resistance Very good Flexibility Good


JOTAMASTIC 87 GF Page 1

Surface preparation










Application data Mixing ratio (volume) 6 parts Comp. A to 1 part Standard Comp. B

4 parts Comp. A to 1 part Cold Climate Comp. B.Induction time 10 minutes.Pot life (23°C)

2 hours (standard Comp. B)

1 hour (cold climate hardner) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi)Nozzle tip 0.48 - 0.89 mm (0.019 - 0.035")Spray angle 40 - 80°Filter Filters to be removed prior to spraying.


Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateStandard hardenerSubstrate temperature 10°C 23°C 40°CSurface dry 8 h 4 h 2 hThrough dry 24 h 10 h 4 hCured 14 d 7 d 2 d



Cold climate hardenerSubstrate temperature -5°C 0°C 5°C 10°C 23°CSurface dry 24 h 18 h 12 h 6 h 2,5 hThrough dry 48 h 26 h 18 h 12 h 5 hCured 21 d 14 d 7 d 3 d 2 d





Typical paint systemJotamastic 87 GFHardtop AS

2 x 250 µm1 x 50 µm





Packing size16 l Comp. A and 2.7 l Standard Comp. B (16 l Comp. A and 4 l Cold Climate Comp. B)Packing may vary from country to country according to local requirements.




JOTAPROOF TOPCOAT - COMP. A

1/6


Approved for use



TRADE NAME JOTAPROOF TOPCOAT - COMP. AAPPLICATION Two-pack acrylic topcoat based on acrylic binder.

ART-NO PM3422




1 N-BUTYL ACETATE 123-86-4 10-25 N 10-66-672 AROMATIC HYDROCARBONS C9-C12 64742-95-6 2,5-10 N XnN,10-37-65-51/53





4. FIRST AID



SKIN CONTACT




2/6













HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Allways use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area. For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty the




3/6












Form Liquid.Colour Various.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 1,52Expl. limit LEL-UEL., %-%: 1,0 - 7,5 Solubility in water











4/6
















13. DISPOSAL






5/6



HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk




Classification






PRINTEDOUT:

07/08/2001





6/6




JOTAPROOF TOPCOAT - COMP. B

1/6


Approved for use



TRADE NAME JOTAPROOF TOPCOAT - COMP. BAPPLICATION Two-pack acrylic topcoat based on acrylic binder.

ART-NO PM3423




1 N-BUTYL ACETATE 123-86-4 25-50 N 10-66-67





4. FIRST AID



SKIN CONTACT




2/6




MEDICAL INFORMATIONRisk of chemical pneumonia by aspiration. Keep attention: danger of lung damage. General health examination.Professional evaluation of the work station.









HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Allways use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area. For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty the




3/6























4/6












13. DISPOSAL






5/6



HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk




Classification






PRINTEDOUT:

07/08/2001





6/6


Technical DataJOTAPROOF TOPCOAT

Product descriptionJotaproof Topcoat is a two-pack acrylic topcoat with excellent gloss and colour retention.

Recommended useAs topcoat over an epoxy/epoxy mastic system where a durable, high gloss finish is required in aggressive atmospheric exposure. Cures at low temperatures.



10,5 5 8,4



Surface preparation





JOTAPROOF TOPCOAT Page 1



Application data Mixing ratio (volume) 3,5 parts of Comp. A (base) to 1 part Comp. B (curing agent).Pot life (23°C) 3 hours (Reduced at higher temp.). Thinner/Cleaner Jotun Thinner No. 26Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi).Nozzle tip 0.33-0.46 mm (0.013-0.018").Spray angle 40-80° Filter Check to ensure that filters are clean.


Substrate temperature 5°C 10°C 23°C 40°CSurface dry 6 h 5 h 3,5 h 2 hThrough dry 8 h 7 h 4 h 2 hCured 15 d 10 d 5 d 3 d



The surface must be free from any chalking or any other contamination and if necessary, 1.sufficiently roughened prior to application.


Typical paint systemBarrier 50 µm (Dry Film Thickness)Jotamastic PlusJotaproof Topcoat

250 µm 75 µm






Packing size16 l Comp. A and 4 l Comp. B 4 l Comp. A and 1 l Comp. B.Packing may vary from country to country according to local requirements.









ISSUED 4 MARCH 2002 BY JOTUN PAINTSTHIS DATA SHEET SUPERSEDES THOSE PREVIOUSLY ISSUED




JOTASPEED - COMP. B

1/6


Approved for use



TRADE NAME JOTASPEED - COMP. BAPPLICATION Two-pack epoxy paint.

ART-NO PM3292






INGREDIENT COMMENTS Substances presenting a health hazard within the meaning of the current issue of the CHIP Regulations orassigned occupational exposure limits.


Harmful


4. FIRST AID





JOTASPEED - COMP. B

2/6




MEDICAL INFORMATIONRisk of chemical pneumonia by aspiration. Keep attention: danger of lung damage. General health examination.Professional evaluation of the work station.





OTHER INFORMATIONDo not allow run-off from fire fighting to enter drains or water courses.




HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Always use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area.For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty thecontainer, it is not a pressure vessel. Electrical equipment should be protected to appropriate standards. The ManualHandling Operations Regulations may apply to the handling of containers of this product.




JOTASPEED - COMP. B

3/6










Form Liquid.Colour Brown.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 0,99Expl. limit LEL-UEL., %-%: 1,1-11,3 Solubility in water















JOTASPEED - COMP. B

4/6










13. DISPOSAL





JOTASPEED - COMP. B

5/6


PROPER SHIPPING NAME RESIN SOLUTIONToll. reg. no.

HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)


Class 3 Label 3Packaging group III EmS 3-05MFAG Marine Pollutant

Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk




Classification

Harmful






PRINTEDOUT:

21/11/2001

VENDOR NOTES The information contained in this MSDS is based on the present state of knowledge and current nationallegislation. As the specific conditions of use of the product are outside the supplier's control, the user is responsible



JOTASPEED - COMP. B

6/6

for ensuring that the requirements of relevant legislation are compiled with. The information in this MSDSprovides guidance on health, safety and environmental aspects of the product and should not be construed as anyguarantee of technical performance or suitability for particular applications. Further information and relevantadvice can be found in: The Environmental Protection (Duty of Care) Regulations 1992 (SI 1992:2839). TheControl of Substances Hazardous to Health Regulations 1988 (SI1988:1657). The Highly Flammable Liquids andliquefied Petroleum Gases Regulations 197 (SI 1972:917). The Manual Handling Operations Regulations 1992 (SI1992:2793). Storage of Flammable Liquids in Containers, HS(G)51. Storage of Packaged Dangerous Substances,HS(G)71. The selection, use and maintenance of respiratory protective equipment: A practical guide HS(G)53.

Technical DataJOTASPEED AL

Product descriptionJotaspeed AL is an anti-corrosive 2-pack epoxy coating, which has the capability of being overcoated in a short time.

Recommended useHigh build epoxy coating in a system for above water use, which under suitable condition may be completed in one day.



5,2 2,6 4,3

Physical propertiesColour Aluminium and aluminium red tonedSolids (vol %)* 65 ± 2 Flash point 29ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance Very goodSolvent resistance Excellent


Surface preparation






JOTASPEED AL Page 1





Application data Mixing ratio (volume) 4 parts A (base) + 1 part B (curing agent).

Mechanically stir well part A, add part B and mix thoroughly.Pot life (23°C) 2 hours (reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 225 kp/cm² 3300 psiNozzle tip 0.021” - 0.027” (0.53 - 0.69 mm)Spray angle 40-80ºFilter Check to secure that filters are clean


Substrate temperature 5°C 10°C 23°C 40°CSurface dry 2 h 1,5 h 0,75 h 0,5 hThrough dry 7 h 4 h 2,5 h 1,5 hCured 14 d 10 d 7 d 2 d

Dry to recoat, minimum 7 h 4 h 2,5 h 1,5 h




JOTASPEED AL Page 2

Typical paint systemJotaspeed ALJotaspeed MIOHardtop AS

1 x 150 µm1 x 150 µm1 x 40 µm





Packing size16 ltr. Comp. A (base) 4 ltr. Comp. B (curing agent)Packing may vary from country to country according to local requirements.










JOTASPEED AL Page 3

Technical DataJOTASPEED MIO

Product descriptionJotaspeed MIO is an anti-corrosive 2-pack epoxy coating, which has the capability of being overcoated in a short time.




5,2 2,6 4,3

Physical propertiesColour Grey and RedSolids (vol %)* 65 ± 2 Flash point 29ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance Very goodSolvent resistance Excellent


Surface preparation


Bare steelCleanliness: Blast-cleaning to Sa 2½ (ISO-8501-1:1988).




JOTASPEED MIO Page 1






Mechanically stir well part A, add part B and mix thoroughly.Pot life (23°C) 2 hours (reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 225 kp/cm² 3300 psiNozzle tip 0.021” - 0.027” (0.53 - 0.69 mm)Spray angle 40-80ºFilter Check to secure that filters are clean


Substrate temperature 5°C 10°C 23°C 40°CSurface dry 2 h 1,5 h 0,75 h 0,5 hThrough dry 7 h 4 h 2,5 h 1,5 hCured 14 d 10 d 7 d 2 d






Typical paint systemBarrier 1 x 40 µm or Jotabar ZEPJotaspeed MIOHardtop ASorJotaspeed ALJotaspeed MIOHardtop AS

1 x 60 µm1 x 200 µm1 x 40 µm

1 x 150 µm1 x 150 µm1 x 40 µm

















Technical DataJOTASPEED ZP

Product descriptionJotaspeed ZP is an anti corrosive 2-pack epoxy coating, which has the capability of being overcoated in a short time.




5,2 2,6 4,3

Physical propertiesColour Light red and greySolids (vol %)* 65 ± 2 Flash point 29ºC ± 2 Gloss FlatWater resistance Very goodAbrasion resistance Very goodSolvent resistance Excellent


Surface preparation






JOTASPEED ZP Page 1






Mechanically stir well part A, add part B and mix thoroughly.Pot life (23°C) 2 hours (reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 225 kp/cm² 3300 psiNozzle tip 0.018” - 0.023” (0.46 - 0.58 mm)Spray angle 40 - 80ºFilter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 5°C 10°C 23°C 40°CSurface dry 2 h 1,5 h 0,75 h 0,5 hThrough dry 7 h 4 h 2,5 h 1,5 hCured 14 d 10 d 7 d 2 d





JOTASPEED ZP Page 2

Typical paint systemBarrier 1 x 40 µm or Jotabar ZEPJotaspeed ZPHardtop ASorJotaspeed ZP Jotaspeed MIOHardtop AS

1 x 60 µm1 x 200 µm1 x 40 µm

1 x 150 µm1 x 150 µm1 x 40 µm
















JOTASPEED ZP Page 3

Technical DataJOTATHANE

Product descriptionA two-pack high solid, VOC compliant (350-380 g/l dependant on colour) - 1990 EPA - PG6/23(95), aliphatic polyurethane topcoat with excellent gloss and colour retention.

Recommended useAs a glossy topcoat over most epoxy systems where a durable, weather-resistant finish is required in a wide range of aggressive atmospheres.



12,6 7,9 10,5

Physical propertiesColour According to colour card and Multicolor tinting system (MCI)Solids (vol %)* 63 ± 2 Flash point 34ºC ± 2 (Setaflash)Gloss GlossyGloss retention ExcellentWater resistance Very goodAbrasion resistance Very goodSolvent resistance Very good Chemical resistance Very good Flexibility Very good


Surface preparation








Application data Mixing ratio (volume) 5 parts Comp. A (Base) to 1 part Comp. B (Curing agent).Pot life (23°C) 2½ hours Thinner/Cleaner Jotun Thinner No. 10Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi)Nozzle tip 0.35-0.55 mm (0.015-0.021")Spray angle 40-80ºFilter Check to ensure that filters are clean.


Substrate temperature 0°C 5°C 10°C 23°C 40°CSurface dry 24 h 16 h 10 h 5 h 2 hThrough dry 48 h 24 h 16 h 7 h 3 hCured 24 d 21 d 14 d 7 d 3 d



The surface should be dry and free from any contamination or chalking prior to application of 1.the subsequent coat.


Typical paint systemJotamastic 87Jotathane

2 x 200 µm1 x 60 µm



JOTATHANE Page 2



Packing size15 l Comp. A and 3 l Comp. B3,75 l Comp. A and 0,75 l Comp. BPacking may vary from country to country according to local requirements.










JOTATHANE Page 3

Technical DataJOTUN ANTI-SKID

Product descriptionJotun Anti-Skid is an aluminium oxide, intended to be spread into the last coat in a non-skid system.

Recommended useFor use on decks, floors, gangways and other areas where additional friction properties are required. The spreading is to take place in the wet film during application.Recommended quantity:For Deckpaint and Penguard Topcoat (volume solids about 50%), 1,5 - 2,0 kg./10 litre paint is recommended. For Pioner Topcoat (volume solids about 30-40%), 1,0 - 1,5 kg./10 litre paint is recommended.If a more rough surface is required, the quantity may be increased.Particle size : 180 - 250 µm

Physical propertiesColour DarkSolids (vol %)* 100 ± Flash point N.A.*Measured according to ISO 3233:1998 (E)

Surface preparationCoated surfacesAccording to specifications for the chosen topcoat.



HandlingHandle with care.

Packing size3 kgPacking may vary from country to country according to local requirements.

JOTUN ANTI-SKID Page 1










JOTUN ANTI-SKID Page 2



JOTUN MULTICOLOR INDUSTRI TINTING COLOR 1. PRODUCT AND COMPANY

Approved for use

Approved for laboratory use Approved by Jotun AS

TRADE NAME JOTUN MULTICOLOR INDUSTRI TINTING COLORAPPLICATION Tinting colour

ART-NO PM3920




1 AROMATIC HYDROCARBONS C9-C12 64742-95-6 25-50 N XnN,10-37-65-66-67-51/53

2 POLYAMINE FATTY ACID CONDENSATION POLYMER - 1-2,5 Xi,R-36/38-43


INGREDIENT COMMENTS Substances presenting a health hazard within the meaning of the current issue of the CHIP Regulations or assigned occupational exposure limits.The product is not classified as dangerous by aspiration according to viscosity criterias in the guidelines.


Irritating

FLAMMABLE. IRRITATING TO RESPIRATORY SYSTEM. MAY CAUSE SENSITISATION BY SKIN CONTACT. For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL

1 / 6



JOTUN MULTICOLOR INDUSTRI TINTING COLOR In all cases of doubt, or when symptoms persist, seek medical attention. Never give anything by mouth to an unconscious person.


SKIN CONTACTRemove contaminated clothing. Wash skin thoroughly with soap and water or use an appropriate skin cleaner. Do NOT use solvents or thinners.

EYE CONTACTRemove any contact lenses. Hold the eyelids apart. Irrigate copiously with clean, fresh water for at least 10 minutes. Seek medical advice if symptoms persist.

INGESTIONDO NOT INDUCE VOMITING. If accidentally swallowed obtain immediate medical attention. Keep at rest. Seek medical advice.

MEDICAL INFORMATION Risk of chemical pneumonia by aspiration. Keep attention: danger of lung damage. General health examination. Professional evaluation of the work station.







OTHER INFORMATIONExclude sources of ignition and ventilate the area. Avoid breathing vapours. Refer to protective measures listed in sections 7 and 8. Place in container for disposal according to local regulations (see section 13). Contain and collect spillage with non-combustible absorbent materials, e.g. sand, earth, vermiculite and diatomaceous earth. Do not allow to enter drains or watercourses. Clean preferably with a detergent; avoid use of solvents. If the product enters drains or sewers, the local water company should be contacted immediately; in the case of contamination of streams, rivers or lakes, the Environmental Agency.

2 / 6



JOTUN MULTICOLOR INDUSTRI TINTING COLOR 7. HANDLING AND STORAGE

HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Prevent the creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher than the occupational exposure limits. The product should not be used in vicinity of open flames or other sources of ignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Always use earth (ground) wire when transferring from one container to another. Personnel should wear anti-static clothing and footwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparks and open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist. Smoking, eating and drinking are forbidden in the work area.For personal protective equipment see Section 8. Always keep in containers made of the same material as the supply container. Never use pressure to empty the container, it is not a pressure vessel. Electrical equipment should be protected to appropriate standards. The Manual Handling Operations Regulations may apply to the handling of containers of this product.

STORAGEStore in accordance with the regulations for flammable materials. Observe the label precautions. Store in a dry, cold and well ventilated place away from sources of heat, ignition and direct sunlight. Store separately from oxidising agents and strongly alkaline and strongly acidic materials. No smoking. Containers which are opened should be properly resealed and kept upright to prevent leakage.


Ingredients name CAS-no OEL value OELAROMATIC HYDROCARBONS C9-C12 64742-95-6 125,0 mg/m3

EXPOSURE CONTROLProvide adequate ventilation. Where reasonably practicable this should be achieved by the use of local exhaust ventilation and good general extraction. OEL's are taken from the current version of EH40 (by Health & Safety Executive, UK).

RESP. PROTECTIONWhen use of roller or brush, then charcoal filter is sufficient. Use respiratory protective mask with charcoal and dust filter (A2/P2) when spraying this product.


HAND PROTECTIONUse PVA gloves.Barrier creams may help to protect exposed areas of the skin but are not substitutes for full physical protection. Never apply barrier cream to contaminated skin.

SKIN PROTECTIONWear anti-static clothing made of natural fibre or of heat resistant synthetic fibre.When spraying use suit covering the whole body.

3 / 6



JOTUN MULTICOLOR INDUSTRI TINTING COLOR 9. PHYSICAL AND CHEMICAL PROPERTIES

Form Liquid. Colour Various. Odour Organic solvent. Solubility Organic solvent. Melting point/range - Density 1.13Expl. limit LEL-UEL., %-%: 1 - 6 Solubility in waterVapor pressure Saturation conc.Decomposition temp. Rel. density sat. air (air=1)pH Solution Boiling point/range 162-177°CFlash point 48ºC pH concentrate -Molecular weight ViscosityIgnition temp 500ºC Smelling limits lo-hiRel. vapor density (air=1) Rel. evap. velocityAir reactive Water reactive







INHALATIONExposure to organic solvent vapours may result in adverse health effects such as irritation of the mucous membrane and the respiratory system and adverse effects on the renal and central nervous system. Symptoms and signs include headache; dizziness, fatigue, muscular weakness, drowsiness and in extreme cases, loss of consciousness.

SKIN CONTACTRepeated or prolonged exposure may cause skin irritation and dermatitis, due to the product's defatting properties.Repeated or prolonged contact with skin may cause sensitisation.


INGESTIONAccidental ingestion may cause vomiting and abdominal pains. Risk of chemical pneumonia. 12. ECOLOGICAL INFORMATION




4 / 6



JOTUN MULTICOLOR INDUSTRI TINTING COLOR OTHER INFORMATIONDo not discharge the product to sewer or drains.The product contains aromatic hydrocarbons C9-C12 labelled "Dangerous for the environment".

13. DISPOSAL

Wastes, including emptied containers, are controlled wastes and should be disposed of in accordance with regulations made under the Control of Pollution Act and the Environmental Protection Act. Do not allow into drains or water courses. Waste must be disposed of at approved landfill/waste storage or treatment facility.



PROPER SHIPPING NAME PAINT Toll. reg. no.HAZCHEM

ADR (Road)UN No. Dang. goodsClass LabelHaz. id. no Marginno.

RID (Railway)UN No. Dang. goodsClass LabelHaz..id.no

IMDG (Sea)UN No. 1263 Dang. goodsClass 3.3 LabelPackaging group EmS 3 - 05MFAG 310 Marine PollutantSub. risk Page 3372

IATA (Airplane)UN No. Dang. goodsClass Sub. riskLabel Packaging group

GENERALTransport only in accordance with ADR for road, RID for rail, IMDG for sea transport and IATA for airtransport. Not ADR-restricted ref. NOTE under E of marginal 2301, and according to IMDG, ref. chapter 2.3.2.5. (applicable to receptacles of less than 450 litres capacity).


Classification

Irritating

COMPOSITION POLYAMINE FATTY ACID CONDENSATION POLYMER (1-2,5)

5 / 6



JOTUN MULTICOLOR INDUSTRI TINTING COLOR R-PHRASESR10 Flammable. R37 Irritating to respiratory system. R43 May cause sensitization by skin contact.

S-PHRASESS23 Do not breathe vapour/spray. S24 Avoid contact with skin. S37-Wear suitable gloves. S38 In case of insufficient ventilation, wear suitable respiratory equipment.



PRINTED OUT:

07/11/2000


6 / 6

Technical DataJOTUN THINNER NO. 2

Product descriptionSolvent thinner.

Recommended useGeneral purpose thinner for most conventional alkyd or oil based paints. Consult the technical data sheet for the actual Jotun product.

Consult the technical data sheet for the actual Jotun product.

Physical propertiesColour ClearSolids (vol %)* 0 ± 0 Flash point 43ºC ± 2 (Setaflash)*Measured according to ISO 3233:1998 (E)



Packing size10 ltrs.Packing may vary from country to country according to local requirements.










JOTUN THINNER NO. 2 Page 2



Recommended useA fast evaporating thinner for Shopprimer Iron Oxide Epoxy Two Pack and Epoxy Holding Primer.



StorageThe product must be stored in accordance with national regulations. Preferred storage conditions are to keep the container in a dry space provided with adequate ventilation at room temperature (15-25ºC). The containers should be sealed tightly.Note: Low flash point.


Packing size10 ltrsPacking may vary from country to country according to local requirements.





Recommended useThinner for zinc ethyl silicate paints.Cleaner for equipment that has been used with waterborne products.










Recommended useGeneral purpose thinner for acrylic and chlorinated rubber paints and antifouling compositions.










Recommended useThinner for polyurethane or similar paint products e.g. Hardtop as as well as vinyl coal tar e.g. Vinyguard Black/Brown.NOTE: Not for use with zinc silicates.


Physical propertiesColour clearSolids (vol %)* 0 ± Flash point 25ºC ± 2 (Setaflash)*Measured according to ISO 3233:1998 (E)








Recommended useThinner for Shopprimer Iron Oxide PVB One Pack and Shopprimer Iron Oxide PVB Two Pack.


Physical propertiesFlash point 10ºC ± 2 (Setaflash)*Measured according to ISO 3233:1998 (E)








Recommended useThinner for epoxies and similar paint products.

NOTE: Not for use with Tankguard products.










Recommended useThinner for Tankguard products and other epoxies.General cleaner for all epoxy products.Consult the technical data sheet for the actual Jotun product.









Recommended useThinner for Zinc ethyl silicate paints.








Technical DataMAMMUT PRIMER

Product descriptionMammut Primer is a high build urethane alkyd based primer. This product is part of a complete system which is certified not to spread surface flames.

Recommended useSteel structures for general industrial purpose in combination with an alkyd system.



8,3 5 6,3

Physical propertiesColour Grey, WhiteSolids (vol %)* 50 ± 2 Flash point 36ºC ± 2 (Setaflash)Gloss FlatWater resistance FairFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation






MAMMUT PRIMER Page 1







Substrate temperature 5°C 10°C 23°C 40°CSurface dry 4 h 3 h 2 h 0,5 hThrough dry 26 h 22 h 6 h 3 hDry to recoat, minimum 16 h 12 h 8 h 5 h


The surface should be dry and free from any contamination prior to application of the 1.subsequent coat.


Typical paint systemMammut PrimerMammut TopcoatorMammut Primer Pilot IPilot II

1 x 80 µm1 x 80 µm

1 x 80 µm1 x 40 µm1 x 40 µm

(Dry Film Thickness)(Dry Film Thickness)(Dry Film Thickness)(Dry Film Thickness)(Dry Film Thickness)(Dry Film Thickness)



Technical DataMAMMUT TOPCOAT

Product descriptionMammut Topcoat is a high build urethane alkyd based topcoat. This product is part of a complete system which is certified not to spread surface flames.

Recommended useAs topcoat over Mammut Primer or other alkyd based primers on steel structures for general marine and industrial purposes, exterior and interior.



10 5 6,3

Physical propertiesColour White, White BT, Grey 38Solids (vol %)* 50 ± 2 Flash point 36ºC ± 2 (Setaflash)Gloss GlossyGloss retention GoodWater resistance FairAbrasion resistance GoodFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparationCoated surfacesClean, dry and undamaged compatible primer. Please contact your local Jotun office for more information.



MAMMUT TOPCOAT Page 1




Application data Thinner/Cleaner Jotun Thinner No. 2Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.46 - 0.69 mm (0.018 - 0.027")Spray angle 65-80°Filter Check to ensure that filters are clean.






Typical paint systemMammut PrimerMammut Topcoat

1 x 80 µm1 x 80 µm






Technical DataMARATHON

Product descriptionMarathon is a high solids, two-pack epoxy coating reinforced with glass flakes.

Recommended useSteel and concrete structures subject to aggressive exposure, both atmospheric and mechanical. Offers extremely good protection against corrosion and has outstanding abrasion resistance. Proved records for use in high pressure vessels.



4 2 3,2

Physical propertiesColour Limited numberSolids (vol %)* 80 ± 2 Flash point 30ºC ± 2 (Setaflash)Gloss GlossyGloss retention FairWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Flexibility GoodCompatibility withcathodic protection Very good


Surface preparation





MARATHON Page 1




Application data Mixing ratio (volume) 3 parts Comp. A ( base) to 1 part Comp. B (curing agent)Pot life (23°C) 1 hour (reduced at higher temperatures) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi)Nozzle tip 0.63 - 1.09 mm (0.025-0.043")Spray angle 65 - 80°Filter Filters to be removed prior to spraying.


Substrate temperature 10°C 23°C 40°CSurface dry 14 h 5,5 h 3 hThrough dry 32 h 12 h 6 hCured 14 d 7 d 3 d





MARATHON Page 2

Typical paint systemOn Sa 2½ :Marathon 300 µm + 200 µm (Dry Film Thickness)For extended corrosion protection, on Sa 2½ :BarrierMarathon

1 x 25 µm*300 µm + 200 µm


For aggressive chemical exposure, on Sa 2½ :Tankguard HBMarathon

1 x 50 µm300 µm + 200 µm


* It is important that Barrier is applied with DFT 25 µm, and therefore Barrier must be thinned 25-40 %.Other systems may be specified, depending on area of use






MARATHON Page 3








MARATHON Page 4

Technical DataMARATHON IQ GF

Product descriptionMarathon IQ GF is a practically solvent free, abrasion resistant, two-pack epoxy coating which contains glass flakes.

Recommended useA high build coating for steel subject to extreme atmospheric or mechanical exposure. For maximum mechanical strenght, i.e. hulls of ice-going vessels, 1-coat system shall be used.

Film thickness and spreading rateMinimum Maximum Typical For ice

resistanceFilm thickness, dry (µm) 250 650 300 500Film thickness, wet (µm) 250 650 300 500Theoretical spreading rate (m²/l)

3,9 1,5 3,3 2,0

Physical propertiesColour Limited numberSolids (vol %)* 98 ± 2 Flash point 55ºC Gloss GlossyGloss retention FairWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Flexibility FairCompatibility withcathodic protection Excellent


MARATHON IQ GF Page 1

Surface preparation






Application methodsSpray Two-comp. heated airless spray. If permitted, thin 10%, to use normal airless spray

(However, the abrasion resistance may be reduced. No thinning accepted when used for ice resistance)


Application data Mixing ratio (volume) 2 parts Comp. A (base) to be mixed thoroughly with

1 part Comp. B (curing agent)Pot life (23°C) 30 minutes (Reduced at higher temperatures). Thinner/Cleaner Jotun Thinner No. 17, max 10%.Guiding data airless sprayPressure at nozzle 20 MPa (200 kp/cm2 2800 psi)Nozzle tip 0.63-1.09 mm (0.025-0.045")Spray angle 40-80°Filter Remove all filters.Note Thinning will prolong the drying and curing times. Best application

viscocity is obtained at around 20ºC.






Recoating with it self if there is no mechanical stress of surface during the paint workSubstrate temperature 10°C 23°CSurface dry 6 h 3 hThrough dry 20 h 10 hCured 14 d 7 d


Dry to recoat, maximum 5 d 3 d

The surface should be free from chalking and contamination prior to application. If the 1.maximum dry to recoat time is exceeded, please contact Jotun Paints for advice


Typical paint systemOn Sa 2½ or intact dry, clean shopprimer: Marathon IQ GF 1-2 x 300 µm (Dry Film Thickness)For maximum ice resistance, on Sa 2½: Marathon IQ GF 1 x 500 µm (Dry Film Thickness)If overcoated with antifouling, a tie-coat is required.Other systems may be specified, depending on area of use







MUKI - Z NO. 2001 FW - COMP. A

1/6


Approved for use



TRADE NAME MUKI - Z NO. 2001 FW - COMP. AAPPLICATION Two-pack modified zincethylsilicate shop primer.

ART-NO PM3108




1 PROPAN-2-OL 67-63-0 25-50 N Xi,F,11-36-672 ETHANOL 64-17-5 25-50 N F,113 TETRAETHYL ORTHOSILICATE 78-10-4 2,5-10 N Xn,10-20-36/37




Irritating Highly flammable

HIGHLY FLAMMABLE. IRRITATING TO EYES. VAPOURS MAY CAUSE DROWSINESS ANDDIZZINESS.For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL




2/6















HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Allways use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.




3/6




Ingredients name CAS-no OEL value (long-term) OEL value (short-term) OELPROPAN-2-OL 67-63-0 999,0 mg/m3;Sk 1250,0 mg/m3;Sk

ETHANOL 64-17-5 1920,0 mg/m3 -

TETRAETHYL ORTHOSILICATE 78-10-4 87,0 mg/m3 260,0 mg/m3




HAND PROTECTIONUse PVA gloves. Barrier creams may help to protect exposed areas of the skin but are not substitutes for fullphysical protection. Never apply barrier cream to contaminated skin.





4/6


Form Liquid.Colour Green. Red.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 0.9Expl. limit LEL-UEL., %-%: 2 - 19 Solubility in water























5/6

13. DISPOSAL





HAZCHEM

ADR (Road)


Class 3,5(b) Label 3Haz. id. no Marginno.

RID (Railway)


Class 3,5(b) Label 3Haz..id.no

IMDG (Sea)



Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk

Label 3 Packaging group



Classification

Irritating Highly flammable

COMPOSITION PROPAN-2-OL (25-50)

R-PHRASESR11 - Highly flammable. R36 - Irritating to eyes. R67 - Vapours may cause drowsiness and dizziness.

S-PHRASES




6/6

S16 - Keep away from sources of ignition - No smoking. S23 - Do not breathe vapour/spray. S38 - In case ofinsufficient ventilation, wear suitable respiratory equipment.



PRINTEDOUT:

17/08/2001


Technical DataMUKI - Z No. 2001 FW

Product descriptionMuki-Z No. 2001 FW is a two-pack, modified low zinc ethyl silicate shopprimer designed to utilize extra high productivity in connection with advanced welding technology (MIG/ MAG/G-FCAW). Other pronounced features with Muki-Z No. 2001 FW are the reduced health risk during welding and cutting and the reduction in weld defects.

Recommended useTo be used as a preconstruction primer on blast-cleaned steel surfaces in automatic shop-priming plants to protect steel during transport, storage and production.



18,7 14

CommentsDry film thickness measured on a smooth test panel.

Physical propertiesColour Green, Grey, RedSolids (vol %)* 28 ± 2 Flash point 14ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent within pH range 6-10.Flexibility Limited


MUKI - Z No. 2001 FW Page 1

Surface preparation




Condition during applicationThe temperature of the substrate should be minimum at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Recommended steel temperature: 30-40°C.

Application methodsSpray Use airless spray or conventional sprayBrush Recommended for touch-up purposes.

Application data Mixing ratio (volume) 10 parts by volume Comp. A (Silicate solution) to be thoroughly

mixed with 6,75 parts by volume Comp. B (Zinc paste).Pot life (23°C) 24 hours. (Reduced at higher temperatures). Thinner/Cleaner Jotun Thinner No. 4/25

(No. 4 - Fast Evaporation) - (No. 25 - Slow evaporation).Guiding data airless sprayPressure at nozzle 5 - 7 MPa (50 - 70 kp/cm², 700 - 900 psi).Nozzle tip 0.38 - 0.58 mm (0.015 - 0.023").Spray angle 40 - 95ºNote * Proper routines for cleaning and maintenance of the priming unit

are necessary to achieve high productivity and uniform quality. Before start of work and after finishing with Muki-Z No. 2001 FW it is recommended to circulate Jotun Thinner No. 4 or No. 25 through the entire spraying equipment for some minutes. During application it is necessary to use a mechanical stirrer.

* The Comp. B (Zinc paste) must be stirred continuously while the Comp. A (Silicate solution) is added.


Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate* Relative humidity at 80 %

Substrate temperature 23°C 40°CSurface dry 1-3 min 20-40 sec Through dry 3-5 minCured

1 1 d 1 d

Dry to recoat, minimum 2 1 d 1 d


Curing time to be verified by MEK-test (ASTM D 4752-87). 1.Recommended data given for recoating with coatings normally specified on top of 2.shopprimers.The substrate should be free from any zinc salts and other contamination prior to application 3.of the subsequent coat.


Typical paint systemMuki-Z No. 2001 FW 1 x 15 - 20 µm (Dry Film Thickness measured on a smooth test panel).

Undamaged shopprimer can be overcoated with a choice of systems based on epoxy, vinyl or chlorinated rubber resins.Other systems may be specified, depending on area of use


HandlingSHELF LIFE: 6 months at room temperature for Comp. A. Handle with care. Stir well before Use. Continuous stirring during application will prevent the heavy zinc pigment from settling.

Packing size10 l Comp. A , 6,75 l Comp. BPacking may vary from country to country according to local requirements.


Technical DataMUKI - Z No. 3000

Product descriptionMuki-Z No. 3000 is a two-pack, modified medium zinc ethyl silicate shopprimer designed to utilize high productivity in connection with advanced welding technology (MIG/ MAG/ G-FCAW). Another pronounced feature with Muki-Z No. 3000 is the reduced health risk during welding and cutting.

Recommended useTo be used as a preconstruction primer on blast cleaned steel surfaces in automatic shop-priming plants to protect steel during transport, storage and production.



18,7 14

CommentsDry film thickness meaured on a smooth test panel.

Physical propertiesColour Grey, Green, RedSolids (vol %)* 28 ± 2 Flash point 14ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent within pH range 6-10Flexibility Limited


MUKI - Z No. 3000 Page 1

Surface preparation






Application data Mixing ratio (volume) 10 parts by volume Comp. A (Silicate solution) to be thoroughly

mixed with 6 parts by volume Comp. B (Zinc paste).Pot life (23°C) 24 hours. (Reduced at higher temperatures). Thinner/Cleaner Jotun Thinner No. 4/25

(No. 4 - Fast Evaporation) - (No. 25 - Slow evaporation).Guiding data airless sprayPressure at nozzle 5-7 MPa (50 - 70 kp/cm², 700 - 900 psi.).Nozzle tip 0.38 - 0.58 mm (0.015 - 0.023").Spray angle 40 - 95°Note

* Proper routines for cleaning and maintenance of the priming unit are necessary to achieve high productivity and uniform quality. Before start of work and after finishing with Muki-Z No. 3000 it is recommended to circulate Jotun Thinner No. 4 or No. 25 through the entire spraying equipment for some minutes. During application it is necessary to use a mechanical stirrer.

* The Comp. B (Zinc paste) must be stirred continuously while the Comp. A (Silicate solution) is added.


Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate* Relative humidity at 80 %

Substrate temperature 23°C 40°CSurface dry 1-3 min 20-40 sec Through dry 3-5 min 1-2 minCured

1 2 d 1 d

Dry to recoat, minimum 2 2 d 1 d


Curing time to be verified by MEK-test (ASTM D 4752-87).1.Recommended data given for recoating with coatings normally specified on top of 2.shop-primers.The substrate should be free from zinc salts and other contamination prior to application of 3.the subsequent coat.


Typical paint systemMuki-Z No. 3000 1 x 15 - 20 µm (Dry Film Thickness measured on a smooth test panel).

Undamaged shopprimer can be overcoated with a choice of systems based on epoxy, vinyl or chlorinated rubber resins.Other systems may be specified, depending on area of use


HandlingSHELF LIFE: 6 months at room temperature for Comp. A. Handle with care. Stir well before Use. Continuous stirring during application will prevent the heavy zinc pigment from settling.

Packing size10 l Comp. A , 6 l Comp. B.Packing may vary from country to country according to local requirements.


Technical DataNAVIGUARD

Product descriptionNaviguard is a solvent free, two-pack epoxy coating.

If used in tanks for potable water, the paint shall not be thinned and washing procedure must be adhered to.Recommended useA mechanically very strong, high build, high solids coating for steel below and above water. It has also very good chemical resistance and is suitable as anode shield in impressed current systems.



5 2 3,3

Physical propertiesColour White, RedSolids (vol %)* 100 ± Flash point >100ºC (Setaflash)Gloss GlossyGloss retention FairWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Flexibility FairCompatibility withcathodic protection Excellent


Surface preparation





NAVIGUARD Page 1


Application methodsSpray Two-comp. heated airless spray. If permitted, thin 10%, to use normal airless sprayBrush Recommended for stripe coating and small areas, care must be taken to achieve



1 part Comp. B (curing agent)Pot life (23°C) In two-comp. spray at 60°C - 5 minutes. If thinned 10%, 30

minutes at 23°C.

Thinner/Cleaner Jotun Thinner No. 17 Guiding data airless sprayPressure at nozzle 20 MPa (200 kp/cm² 2800 psi)Nozzle tip 0.53-0.79 mm (0.021-0.031")Spray angle 40-80°Filter Check to ensure that filters are clean.


Substrate temperature 10°C 23°C 40°CSurface dry 8 h 4 h 3,5 hThrough dry 20 h 10 h 4 hCured 14 d 7 d 3 d





NAVIGUARD Page 2

Typical paint systemOn Sa 2½ or intact dry, clean shopprimer:Naviguard 1-2 x 300 µm (Dry Film Thickness)When used as impressed current anode shield coating on Sa 2 ½:Naviguard 2 x 500 µm (Dry Film Thickness)Other systems may be specified, depending on area of use

SPECIAL WASHING PROCEDURE WHEN THIS PRODUCT IS USED IN TANKS FOR POTABLE WATERAfter the paint is cured (see drying/curing time above) under good ventilation, the tank shall be thoroughly washed with fresh 50 - 80°C water. The wash water must be renewed (replaced) during this prosess. Then the tank is filled with water. Repeat the prosedure (washing/filling water) three times.






NAVIGUARD Page 3








NAVIGUARD Page 4

Technical DataNAVITAR AS

Product descriptionNavitar AS is a solventless, two-pack epoxy coal-tar coating which may be applied by ordinary airless spray in a high film thickness.

Recommended useSubmerged steel structures, buried concrete or steel structures. Excellent protection against corrosion. Excellent in combination with cathodic protection.



4,5 2,3 3

Physical propertiesColour Dark Brown/BlackSolids (vol %)* 90 ± 2 Flash point 75ºC ± 2 SetaflashGloss SemiflatWater resistance ExcellentAbrasion resistance GoodSolvent resistance Good (discoloration)Chemical resistance Good Flexibility GoodCompatibility withcathodic protection Excellent


NAVITAR AS Page 1

Surface preparation









Application data Mixing ratio (volume) 2 parts Comp. A (base) to be mixed thoroughly with (by volume)

1 part Comp. B (curing agent)Pot life (23°C) 1 hour (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 20 MPa (200 kp/cm² 2800 psi)Nozzle tip 0.53 - 0.79mm (0.021-0.031")Spray angle 40 - 80°Filter Check to ensure that filters are clean.

NAVITAR AS Page 2


Substrate temperature 10°C 23°C 40°CSurface dry 24 h 12 h 3,5 hThrough dry 48 h 24 h 5 hCured 14 d 7 d 3 d


Dry to recoat, maximum 1,2 7 d 7 d 4 d

The surface should be free from chalking and contamination prior to application. At interior 1.exposure note that best intercoat adhesion occurs when the subsequent coat is applied before the preceding coat is cured. At exterior exposure the chalking effect especially from the sunlight limits the maximum dry to recoat time.Maximum figures refer to exterior surfaces. For interior surfaces, there are no limit.2.


Typical paint systemNavitar AS (diluted 25%)Navitar AS

stripe coat1 x 300 µm (Dry Film Thickness)




Packing size13 l Comp. A (base) and 6.5 l Comp. B (curing agent)Packing may vary from country to country according to local requirements.



NAVITAR AS Page 3








NAVITAR AS Page 4

Technical DataPENGUARD CLEAR VARNISH

Product descriptionPenguard Clear Varnish is a two-pack transparent epoxy varnish.

Recommended useSealer on concrete masonry, normally under Penguard Topcoat or as a dust-binder on concrete.



16,7 10 12,5

Physical propertiesColour TransparentSolids (vol %)* 50 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss GlossyWater resistance Very goodSolvent resistance Excellent Chemical resistance Excellent Flexibility Good


Surface preparation





PENGUARD CLEAR VARNISH Page 1





1 part Comp. B (curing agent)Mixing ½ hour prior to use.Pot life (23°C) 8 hours (reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.33 - 0.46 mm (0.013-0.018")Spray angle 40-80°Filter Check to ensure that filters are clean


Substrate temperature 10°C 23°C 40°CSurface dry 2 h 1 h 0,5 hThrough dry 14 h 6,5 h 3 hCured 14 d 7 d 3 d



The surface should be free from chalking and contamination prior to application. Best 1.intercoat adhesion occurs when the subsequent coat is applied before the preceding coat has cured.


Typical paint systemAs dust binder:Penguard Clear Varnish NominalFor transparent finish:Penguard Clear Varnish 1-2 x 40 µm (Dry Film Thickness)For coloured finish:Penguard Clear VarnishPenguard Topcoat

1 x 40 µm1-2 x 50 µm




Technical DataPENGUARD HB

Product descriptionPenguard HB is a high build, two-pack epoxy coating based on epoxy resin with high molecular weight. This product is a part of a complete system which is certified not to spread surface flames.

Recommended useAs part of a system for steel and concrete structures above and below water. May be used in tanks for potable water.



6,8 3,6 5,4

If used in tanks for potable water, washing procedure must be adhered to.Physical propertiesColour Grey, Red, White, AluminiumSolids (vol %)* 54 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss FlatGloss retention FairWater resistance Very goodAbrasion resistance Very goodSolvent resistance Excellent Chemical resistance Excellent Flexibility Good


PENGUARD HB Page 1

Surface preparation






Condition during applicationThe temperature of the substrate should be minimum 10°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to ensure proper drying. The coating should not be exposed to oil, chemicals or mechanical stress until cured. If necessary, Penguard Stayer, Penguard Primer, Penguard HB, Penguard Special may be used down to 2ºC, provided a special accelerator is added.

Application methodsSpray Airless sprayBrush Recommended for stripe coating and small areas, care must be taken to achieve



1 part Comp. B (curing agent)Mixing ½ hour prior to use.Pot life (23°C) 8 hours. (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.46 - 0.69mm (0.018-0.027")Spray angle 40 - 80°Filter Check to ensure that filters are clean.

PENGUARD HB Page 2


Substrate temperature 10°C 23°C 40°CSurface dry 5 h 2,5 h 1 hThrough dry 16 h 8 h 3,5 hCured 14 d 7 d 3 d



1 Provided the surface is free from chalking and other contamination prior to application, there is normally no overcoating time limit. If the coating has been exposed to direct sunlight for some time, special attention must be paid to surface cleaning and mattening/removal of the surface layer in order to obtain good adhesion.


Typical paint system1) On bare steel or shopprimer:Penguard HBPenguard Topcoat2) Penguard PrimerPenguard HBPenguard Topcoat

2 x 100 µm1 x 50 µm1 x 50 µm1 x 100 µm1 x 50 µm

(Dry Film Thickness)(Dry Film Thickness)(Dry Film Thickness)(Dry Film Thickness)(Dry Film Thickness)


SPECIAL WASHING PROCEDURE WHEN THIS PRODUCT IS USED IN TANKS FOR POTABLE WATEREitherAfter the paint is cured (see drying/curing time above), the tank is filled with warm water (above 60 - 80°C), which shall remain in the tank for 24 hours. Then the tank is thoroughly washed, using water of min. 80°C together with brushes or washed with steamorAfter the paint is cured (see drying/curing time above), the tank shall be ventilated with warm air, min 23°C for 7 days. Then the tank is filled three times with warm water (min. 50°C), each filling shall remain in the tank for 24 hours. Finally, the tank is washed, using water of min. 50°C together with brushes or washed with steam



PENGUARD HB Page 3











PENGUARD HB Page 4

Technical DataPENGUARD PRIMER

Product descriptionPenguard Primer is a two-pack epoxy primer based on a high molecular weight epoxy resin. This product is part of a complete system which is certified not to spread surface flames.

Recommended useAnticorrosive primer in a complete Penguard system. Can be used on steel, galvanised steel or aluminium. May be overcoated with epoxy, chlorinated rubber, vinyl or polyurethane coatings. May be used in tanks for potable water.



12,8 8,5 10,2

Physical propertiesColour RedSolids (vol %)* 51 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance Very goodSolvent resistance Excellent Chemical resistance Excellent Flexibility Good


Surface preparation




PENGUARD PRIMER Page 1





1 part Comp. B (curing agent).Mixing ½ hour prior to use.Pot life (23°C) 8 hours. (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.46 - 0.58mm (0.018-0.023")Spray angle 40 - 80°Filter Check to ensure that filters are clean.


Substrate temperature 10°C 23°C 40°CSurface dry 2 h 1 h 0,5 hThrough dry 14 h 6,5 h 3 hCured 14 d 7 d 3 d






Typical paint systemPenguard PrimerPenguard HBPenguard Topcoat

1 x 50 µm1 x 100 µm1 x 50 µm



SPECIAL WASHING PROCEDURE WHEN THIS PRODUCT IS USED IN TANKS FOR POTABLE WATEREitherAfter the paint is cured (see drying/curing time above), the tank is filled with warm water (above 60 - 80°C), which shall remain in the tank for 24 hours. Then the tank is thoroughly washed, using water of min. 80°C together with brushes or washed with steamorAfter the paint is cured (see drying/curing time above), the tank shall be ventilated with warm air, min 23°C for 7 days. Then the tank is filled three times with warm water (min. 50°C), each filling shall remain in the tank for 24 hours. Finally, the tank is washed, using water of min. 50°C together with brushes or washed with steam







Technical DataPENGUARD SPECIAL

Product descriptionPenguard Special is a two-pack zinc phosphate pigmented epoxy coating based on an epoxy resin with high molecular weight.

Recommended useSteel work in general, galvanized steel or aluminium. Usually used in combination with an epoxy or polyurethane system.



6,3 3,3 5

Physical propertiesColour Red, Grey, off whiteSolids (vol %)* 50 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance Very goodSolvent resistance Excellent Chemical resistance Excellent Flexibility Good


Surface preparation




Other surfacesFor aluminium, galvanized and stainless steel, the surface must be clean and dray. Consult your local Jotun office for further details


PENGUARD SPECIAL Page 1





(curing agent).Mixing ½ hour prior to use.Pot life (23°C) 8 hours. (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.46-0.69 mm (0.018-0.027")Spray angle 40-80°Filter Check to ensure that filters are clean.






Typical paint systemPenguard Special 1-2 x 100 µm (Dry Film Thickness)Normally topcoated with Epoxy or Polyurethane.Other systems may be specified, depending on area of use


Technical DataPENGUARD STAYER

Product descriptionPenguard Stayer is a two-pack high build epoxy coating with micaceous iron oxide. This product is a part of a complete system which is certified not to spread surface flames.

Recommended useAs primer or intermediate coat in an epoxy system on steel structures. Penguard Stayer is designed to give good adhesion at long recoating intervals.



6,3 3,2 5

Physical propertiesColour Grey, RedSolids (vol %)* 50 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance Very goodSolvent resistance Excellent Chemical resistance Excellent Flexibility Good


Surface preparation





PENGUARD STAYER Page 1





(curing agent).Mixing ½ hour prior to use.Pot life (23°C) 8 hours. (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.53 - 0.69 mm (0.021 - 0.027")Spray angle 40-80°Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 10°C 23°C 40°CSurface dry 2 h 1 h 0,5 hThrough dry 14 h 7 h 3,5 hCured 14 d 7 d 3 d





Typical paint systemPenguard StayerPenguard Topcoat

2 x 100 µm1 x 50 µm




Technical DataPENGUARD TOPCOAT

Product descriptionPenguard Topcoat is a two-pack epoxy topcoat based on a polyamide cured epoxy resin. This product is a part of a complete system which is certified not to spread surface flames.

Recommended useAs finishing coat in epoxy systems. Also on concrete where epoxy paints are specified. May be used in tanks for potable water



12,5 8,3 10

Physical propertiesColour According to colour card and MCISolids (vol %)* 50 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss GlossyGloss retention FairWater resistance Very goodAbrasion resistance Very goodSolvent resistance Excellent Chemical resistance Excellent Flexibility Good


Surface preparation




PENGUARD TOPCOAT Page 1






(curing agent)Mixing ½ hour prior to use.Pot life (23°C) 8 hours. (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.46 - 0.58 mm (0.018-0.023")Spray angle 40 - 80ºFilter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 10°C 23°C 40°CSurface dry 2,5 h 1,5 h 0,5 hThrough dry 14 h 6,5 h 3 hCured 14 d 7 d 3 d



The surface should be free from chalking and contamination prior to application. Best 1.intercoat adhesion occurs when the subsequent coat is applied before the preceding coat is cured. If this is exceeded it may be necessary to roughen the surface.



Typical paint systemPenguard PrimerPenguard HBPenguard Topcoat

1 x 50 µm1 x 100 µm1 x 50 µm



Special washing procedure when this product is used in tanks for potable waterEitherAfter the paint is cured (see drying/curing time above), the tank is filled with warm water (above 60 - 80°C), which shall remain in the tank for 24 hours. Then the tank is thoroughly washed, using water of min. 80°C together with brushes or washed with steamorAfter the paint is cured (see drying/curing time above), the tank shall be ventilated with warm air, min 23°C for 7 days. Then the tank is filled three times with warm water (min. 50°C), each filling shall remain in the tank for 24 hours. Finally, the tank is washed, using water of min. 50°C together with brushes or washed with steam .







Technical DataPENGUARD HB MIO

Product descriptionPenguard HB MIO is a two pack high build epoxy coating pigmented with micaceous iron oxide, providing a tough chemical and abrasion resistant coating

Recommended useAs an intermediate coat in an epoxy system for onshore and offshore structural steelwork, installations, pipework, tank externals and bridges.



5,6 3,7 4,5

Physical propertiesColour Grey, Light grey and Red.Solids (vol %)* 56 ± 2 Flash point 23ºC ± 2 (Setaflash)Gloss FlatGloss retention FairWater resistance Very goodAbrasion resistance Very goodSolvent resistance Excellent Chemical resistance Excellent Flexibility Good


Surface preparation






PENGUARD HB MIO Page 1





1 part Comp. B (curing agent)Mixing 1/2 hour prior to use.Pot life (23°C) 8 hours. (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.53 mm - 0.69mm (0.021" - 0.027")Spray angle 40° - 80°Filter To be removed.


Substrate temperature 10°C 23°C 40°CSurface dry 5 h 2.5 h 1 hThrough dry 16 h 8 h 3,5 hCured 14 d 7 d 3 d






Penguard PrimerPenguard HB MIOHardtop AS

1 x 50 microns1 x 125 microns1 x 50 microns

(Dry Film Thickness)(Dry film thickness)(Dry Film Thickness)





Packing size16 Ltr. Comp. A (Base) and 4 Ltr. Comp. B (Curing agent.) Packing may vary from country to country according to local requirements.











Technical DataPENGUARD LOW TEMP. ADDITIVE

Product descriptionPenguard Low Temp. Additive is a chemical that will assist drying and curing of Penguard paints at low temperatures (down to 2ºC).

Recommended useAdd 2 % (400 ml to 20 l) to mixed Penguard Primer, Penguard HB, Penguard Special and Penguard Stayer. For all data except drying/curing time, follow the recommendation given in each individual technical data sheet.


Penguard Primer:Substrate temperature 2°C 5°C 10°C 23°CSurface dry 10 h 5 h 2 h 1 hThrough dry 24 h 16 h 8 h 4 hCured - d 16 d 8 d 4 d



Penguard HB and Penguard Special:Substrate temperature

2°C 5°C 10°C 23°C

Surface dry 12 h 6 h 3 h 2 hThrough dry 30 h 20 h 10 h 5 hCured - d 16 d 8 d 4 dDry to recoat, minimum

1 30 h 20 h 10 h 5 h


Penguard Stayer: Substrate temperature 2°C 5°C 10°C 23°CSurface dry 10 h 5 h 2 h 1 hThrough dry 24 h 16 h 8 h 4 hCured - d 16 d 8 d 4 dDry to recoat, minimum

1 24 h 16 h 8 h 4 h


1 If any of these products are used on top of high build zinc silicate, following points should be observed: a) The zinc silicate must be completely cured (MEK-test). b) Mist coat application techniques may be necessary. c) The minimum dry to recoat time should be doubled.





Packing size0,4 l Penguard Low Temp. AdditivePacking may vary from country to country according to local requirements.










PENGUARD LOW TEMP. ADDITIVE Page 2

Technical DataPENGUARD TIE COAT 100

Product descriptionPenguard Tie Coat 100 is a two-pack corrosion preventing polyamide cured epoxy tie coat.

Recommended useOn steel structures for use as tie coat/sealer on top of inorganic zinc silicate.



14 8,4 12

Physical propertiesColour RedSolids (vol %)* 42 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss SemiglossWater resistance Very goodAbrasion resistance Very goodSolvent resistance Excellent Chemical resistance Excellent Flexibility Good


Surface preparation


Coated surfacesCured and clean inorganic zinc silicate primer (tested with MEK).


Condition during applicationThe temperature of the substrate should be minimum 5°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to ensure proper drying. The coating should not be exposed to oil, chemicals or mechanical stress until cured.

Application methodsSpray Airless spray or conventional spray.Brush Recommended for stripe coating and small areas, care must be taken to achieve

PENGUARD TIE COAT 100 Page 1



(curing agent)Induction time 30 minutes.Pot life (23°C) 4 hours. (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.018" (0.46 mm)Spray angle 40-80ºFilter Check to ensure that filters are clean.Note Thinner should be added after mixing components. Extra thinner

(up to 30%) may be added to avoid popping on difficult substrates.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 10°C 23°C 40°CSurface dry 2 h 1 h 0,5 hThrough dry 14 h 6,5 h 3 hCured 14 d 7 d 3 d



1 The surface should be free from chalking and contamination prior to application of the subsequent coat.


Typical paint systemResist 78 or 86Penguard Tie Coat 100Jotamastic 87Hardtop AS

1 x 60 µm1 x 35 µm1 x 200 µm1 x 40 µm



StorageThe product must be stored in accordance with national regulations. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed.

Handling


Handle with care. Stir well before use.










ISSUED 31 JANUARY 2002 BY JOTUN PAINTSTHIS DATA SHEET SUPERSEDES THOSE PREVIOUSLY ISSUED


Technical DataPILOT I

Product descriptionPilot I is an alkyd based paint with good adhesion to the substrate. This product is part of a complete system which is certified not to spread surface flames.

Recommended useIntermediate coat on steel where an alkyd system is required. May also be used as flat topcoat.



17,7 10,6 13,3

Physical propertiesColour White, Grey, BlackSolids (vol %)* 53 ± 2 Flash point 35ºC ± 2 Gloss FlatWater resistance LimitedFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation







PILOT I Page 1

Roller May be used however when using roller application care must be taken to apply sufficient material in order to achieve the specified dry film thickness.

Application data Thinner/Cleaner Jotun Thinner No. 2Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi)Nozzle tip 0.38 - 0.53 mm (0.015 - 0.021") Spray angle 65 - 80°Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 5°C 10°C 23°C 40°CSurface dry 3 h 2 h 1,5 h 0,5 hThrough dry 24 h 8 h 4 h 2 hDry to recoat, minimum 20 h 18 h 12 h 8 h



Typical paint system1)CromoprimerPilot IPilot II

2 x 40 µm1 x 40 µm1 x 40 µm


1)Mammut PrimerPilot IPilot II

1 x 80 µm1 x 40 µm1 x 40 µm





Packing size20 l and 5 lPacking may vary from country to country according to local requirements.

PILOT I Page 2










PILOT I Page 3

Technical DataPILOT II

Product descriptionPilot II is an alkyd based topcoat for both exterior and interior use.This product is part of a complete system which is certified not to spread surface flames.

Recommended useTopcoat in a traditional alkyd system suitable for steel and woodwork. Good weather and colour stability. Good hiding power.



16 9,6 12

Physical propertiesColour According to colour card and Multicolour tinting system (MCI)Solids (vol %)* 48 ± 2 Flash point 36ºC ± 2 (Setaflash)Gloss GlossyGloss retention GoodWater resistance LimitedAbrasion resistance FairFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation





PILOT II Page 1




Application data Thinner/Cleaner Jotun Thinner No. 2Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi)Nozzle tip 0.38 - 0.53 mm (0.015 - 0.021") Spray angle 40 - 80°Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 5°C 10°C 23°C 40°CSurface dry 5 h 4 h 3 h 1 hThrough dry 25 h 14 h 7 h 3 hDry to recoat, minimum 36 h 18 h 16 h 12 h



Typical paint system1)CromoprimerPilot IPilot II

2 x 40 µm1 x 40 µm1 x 40 µm


2)Mammut PrimerPilot IPilot II

1 x 80 µm1 x 40 µm1 x 40 µm





PILOT II Page 2

Packing size20 l and 5 lPacking may vary from country to country according to local requirements.










PILOT II Page 3

Technical DataPIONER PRIMER

Product descriptionPioner Primer is a rust preventing primer based on a chlorinated polymer.This product is part of a complete system which is certified not to spread surface flames.

Recommended useSteel and concrete structures exposed to moderate environments. Quick drying and may be used at low temperatures.



8,6 4,3 5,7

Physical propertiesColour Grey, Red, WhiteSolids (vol %)* 43 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss FlatWater resistance GoodAbrasion resistance GoodSolvent resistance Limited Chemical resistance Good Flexibility Good


Surface preparation






PIONER PRIMER Page 1


Application methodsSpray Use airless sprayBrush Recommended for touch-up purposes.Roller May be used but is not recommended for first primer coat, however when using


Application data Thinner/Cleaner Jotun Thinner No. 7Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.46-0.69 mm (0.018-0.027")Spray angle 40-80°Filter Check to ensure that filters are clean


Substrate temperature 5°C 10°C 23°C 40°CSurface dry 40 min 30 min 20 min 15 minThrough dry 10 h 8 h 5 h 3 hDry to recoat, minimum 4,5 h 3,5 h 2 h 1,5 h


Typical paint systemPioner Primer greyPioner Primer whitePioner Topcoat

1 x 75 µm1 x 75 µm1 x 50 µm





Technical DataPIONER TOPCOAT

Product descriptionPioner Topcoat is an acrylic resin based topcoat.

Recommended useFinishing coat systems for protection of steel and concrete in a variety of climatic conditions, exterior and interior. Water resistant and unsaponifiable. Quick drying and may be used at low temperatures.



8,5 5,7 6,8

Physical propertiesColour According to colour card and Multicolor tinting system (MCI)Solids (vol %)* 34 ± 2 Flash point 37ºC ± 2 (Setaflash)Gloss GlossyGloss retention GoodWater resistance Very goodAbrasion resistance GoodSolvent resistance Limited Chemical resistance Good Flexibility Good


Surface preparation




PIONER TOPCOAT Page 1







Substrate temperature 5°C 10°C 23°C 40°CSurface dry 60 min 45 min 30 min 15 minThrough dry 10 h 9 h 7 h 4 hDry to recoat, minimum 5 h 4 h 2 h 1,5 h



Pioner PrimerPioner TopcoatorVinyguard Silvergrey 88Pioner Topcoat

2 x 75 µm1 x 50 µm

2 x 80 µm1 x 50 µm





Technical DataPOLYMASTIC 2000

Product descriptionPolymastic 2000 is a two-pack, surface tolerant modified solvent free epoxy mastic coating.

Recommended useAnticorrosive coating for steel structures, also where blast cleaning may not be possible. Can be used alone or overcoated with a variety of topcoats, except alkyds. For above and below water (e.g. water ballast, slop tanks, steel constructions etc.).



4,8 1,9 3,2

Physical propertiesColour Red, Light Grey, Off White, AluminiumSolids (vol %)* 96 ± 2 Flash point Non-flammableGloss SemiglossGloss retention FairWater resistance Very goodAbrasion resistance GoodSolvent resistance Good Chemical resistance Good Flexibility Good


POLYMASTIC 2000 Page 1

Surface preparation







Application methodsSpray Use airless spray with high pressure ratio (min. 60:1).Brush Recommended for stripe coating and small areas, care must be taken to achieve



Application data Mixing ratio (volume) 2 parts Comp. A (base) to be mixed thoroughly with 1 part Comp.

B (curing agent).Pot life (23°C) 60 min. (Reduced at higher temp.). Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 20 MPa (200 kp/cm² 2800 psi).Nozzle tip 0.021-0.031" (0.53-0.79 mm).Spray angle 40-80ºFilter Check to ensure that filters are clean.Note * It is of vital importance that the nozzle and other parts of the

spraying equipment are cleaned properly directly after the work is done due to the short pot life. If a pail is used under the spray pump and new paint poured into it, this pail must be changed every one hour.* The hoses should be of good quality and not longer than necessary.* The temperature of base and curing agent is recommended to be 18ºC or higher when the paint is mixed.


Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 5°C 10°C 23°C 40°CSurface dry 50 h 28 h 7 h 3 hThrough dry 60 h 32 h 9 h 4 hCured 21 d 14 d 7 d 3 d




Typical paint systemPolymastic 2000orPolymastic 2000

2 x 200 µm

1 x 300 µm











PRIMASTIC COLD CLIMATE - COMP. B

1/6


Approved for use



TRADE NAME PRIMASTIC COLD CLIMATE - COMP. BAPPLICATION Two-pack surface tolerant epoxy primer for cooler temperatures (-5°C)

ART-NO PM3365




1 XYLENE, mixed isomers 1330-20-7 10-25 N Xn,10-20/21-382 N-BUTANOL 71-36-3 25-50 N Xn,10-22-37/38-41-67




Harmful


4. FIRST AID

GENERAL




2/6



















3/6





N-BUTANOL 71-36-3 154,0 mg/m3;Sk -









4/6
























5/6




13. DISPOSAL





HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk







6/6

Classification

Harmful






PRINTEDOUT:

31/08/2001




PRIMASTIC STANDARD - COMP. B 1. PRODUCT AND COMPANY



TRADE NAME PRIMASTIC STANDARD - COMP. BAPPLICATION Two pack modified epoxy primer/topcoat

ART-NO PM3101




1 3-AMINOMETHYL-3,5,5-TRIMETHYLCYCLOHEXYLAMINE 2855-13-2 10-25 N C,21/22-34-43-52/532 BENZYL ALCOHOL 100-51-6 25-50 N Xn,20/223 2-METYL-1,5-PENTAMETYLENDIAMIN - 10-25 N C,20/22-34




Corrosive

HARMFUL BY INHALATION AND IF SWALLOWED. CAUSES BURNS. MAY CAUSE SENSITISATION BY SKIN CONTACT. For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL

1 / 6



PRIMASTIC STANDARD - COMP. B In all cases of doubt, or when symptoms persist, seek medical attention. Obtain advice via telephone; before the patient is transported to a doctor or hospital. Never give anything by mouth to an unconscious person.



EYE CONTACTRemove any contact lenses. Hold the eyelids apart. Rinse with lukewarm water for 1 hour. Seek medical advice.


MEDICAL INFORMATION Regulary medical control. Person developing a skin rash are to be directed to a dermatologist for examination.Obtain miedical surveillance concerning burn injuries in mouth and throat. Aspiration hazard by vomiting. All poisoned persons should be transported in recovery position. An authorised person should acompany under the transport. Stomach-rinsing may bee considered, for instance with an antioxydant. Eye injuries should be treated with chloramphenicol or antiseptic eye treatment. Local anesthetica may be given to relieve pain. Eye specialist should be consulted as soon as possible.








HANDLING ADVICEAvoid skin and eye contact. Avoid inhalation of vapour and spray mist. For personal protective equipment see Section 8. Never use pressure to empty the container, it is not a pressure vessel. Always keep in containers made of the same material as the supply container. The Manual Handling Operations Regulations may apply to the handling of containers of this product.


2 / 6



PRIMASTIC STANDARD - COMP. B 8. EXPOSURE CONTROL AND PERSONAL PROTECTION


RESP. PROTECTIONWhen workers are facing concentrations above the occupational exposure limit they must use appropriate certified respirators.Use respiratory protective mask with charcoal and dust filter (A2/P2) when spraying this product.


HAND PROTECTIONUse gloves of viton or 4H gloves.Barrier creams may help to protect exposed areas of the skin but are not substitutes for full physical protection. Never apply barrier cream to contaminated skin.



Form Liquid. Colour Yellowish. Odour Characteristic. Solubility Organic solvent. Melting point/range - Density 0,98Expl. limit LEL-UEL., %-%: 1,3-13,0 Solubility in waterVapor pressure Saturation conc.Decomposition temp. Rel. density sat. air (air=1)pH Solution Boiling point/range 205°CFlash point >100ºC pH concentrate -Molecular weight ViscosityIgnition temp 435°C Smelling limits lo-hiRel. vapor density (air=1) Rel. evap. velocityAir reactive Water reactive







INHALATION

3 / 6



PRIMASTIC STANDARD - COMP. B Exposure to vapours may result in adverse health effects such as irritation of the mucous membrane and the respiratory system.

SKIN CONTACTCauses burns.Products containing amines irritates the skin and may lead to allergic eczema.The allergic response may occur after a short periode of contact.

EYE CONTACTCorrosive. Severe eye irritationMay cause irreversible eye damage.

INGESTIONAccidental ingestion may cause vomiting and abdominal pains. May cause burn damage to mucous membrane, esophagus and stomach. 12. ECOLOGICAL INFORMATION

BREAKDOWN3-aminomethyl-3,5,5-trimethylcyclohexylamine:BOD (28d) = 8 %






OTHER INFORMATIONDo not discharge the product to sewer or drains.The product contains components which are harmful to aquatic organisms.

13. DISPOSAL

Wastes, including emptied containers, are controlled wastes and should be disposed of in accordance with regulations made under the Control of Pollution Act and the Environmental Protection Act. Do not allow into drains or water courses.


4 / 6



PRIMASTIC STANDARD - COMP. B 14. TRANSPORT INFORMATION

PROPER SHIPPING NAME AMINES, LIQUID, CORROSIVE N.O.S. (isophorone diamine,2-methyl-1,5-pentamethylene diamine )


ADR (Road)UN No. 2735 Dang. goodsClass 8, PG III Label 8Haz. id. no 80 Marginno.

RID (Railway)UN No. 2735 Dang. goodsClass 8, PG III Label 8Haz..id.no 80

IMDG (Sea)UN No. 2735 Dang. goodsClass 8 Label 8Packaging group III EmS 8 - 05MFAG Marine PollutantSub. risk Page

IATA (Airplane)UN No. 2735 Dang. goodsClass 8 Sub. riskLabel Corrosive Packaging group III



Classification

Corrosive

COMPOSITION 3-AMINOMETHYL-3,5,5-TRIMETHYLCYCLOHEXYLAMINE (10-25), 2-METYL-1,5-PENTAMETYLENDIAMIN (10-25)

R-PHRASESR20/22 Harmful by inhalation and if swallowed. R34 - Causes burns. R43 May cause sensitization by skin contact.

S-PHRASESS23 Do not breathe vapour/spray. S26 In case of contact with eyes, rinse immediately with plenty of water and seek medical advice.S36/37/39 Wear suitable protection clothing, gloves and eyes/face protection. S45 In case of accident or if you feel unwell, seek medical advice immediately (show the label where possible).



5 / 6



PRIMASTIC STANDARD - COMP. B PRINTED OUT:

21/11/2001


6 / 6

Technical DataPRIMASTIC

Product descriptionPrimastic is a two-pack, high solids modified epoxy coating. Available with two different hardeners for varying substrate temperatures, Standard (Std) and Cold Climate (CC).

Recommended useAnticorrosive primer for steel and concrete structures above water, also on steel where blastcleaning may not be possible.


7,8 3,1 6,2


7,2 2,9 5,7

Physical propertiesColour Limited numberSolids (vol %)* 78 ± 2 Standard climate hardener

72 ± 2 Cold climate hardenerFlash point 35ºC ± 2 Standard Comp. B (Setaflash)

31ºC ± 2 Cold Climate Comp. B (Setaflash) Gloss SemiglossGloss retention FairWater resistance GoodAbrasion resistance Very goodSolvent resistance Good Chemical resistance Good Flexibility Good


PRIMASTIC Page 1

Surface preparation










PRIMASTIC Page 2

Application data Mixing ratio (volume)

7 parts by volume Comp. A (Base) to 1 part Standard Comp.B (hardener)

4 parts by volume Comp.A (Base) to 1 part Cold Climate Comp. B hardener)

Induction time 10 minutes.Pot life (23°C)

2 hours (standard Comp. B)

1 hour (cold climate Comp. B) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi.)Nozzle tip 0.58 - 0.79 mm (0.023 - 0.031")Spray angle 40 - 80°Filter Check to ensure that the filters are cleanNote * The temperature of the mixture of base and curing agent is

recommended to be at least 15°C, otherwise extra solvent may be required to obtain correct viscosity.* Too much solvent results in lower sag resistance and slower cure.* If extra solvent is necessary, this should be added after mixing of the two components.




Cold temperature hardenerSubstrate temperature -5°C 0°C 5°C 10°C 23°CSurface dry 24 h 18 h 12 h 6 h 2,5 hThrough dry 48 h 26 h 18 h 12 h 5 hCured 21 d 14 d 7 d 3 d 2 d


Dry to recoat, maximum - - - - -


PRIMASTIC Page 3

Typical paint systemPrimasticHardtop AS

2 x 125 µm1 x 50 µm





Packing size16 Comp. A and 2,3 l Standard Comp. B or 4 l Cold Climate Comp B.Packing may vary from country to country according to local requirements.










PRIMASTIC Page 4



PRIMASTIC UNIVERSAL COLD CLIMATE - COMP. B

1/6


Approved for use



TRADE NAME PRIMASTIC UNIVERSAL COLD CLIMATE - COMP. BAPPLICATION Two-pack surface tolerant epoxy primer for cooler temperatures (-5°C)

ART-NO PM3366




1 XYLENE, mixed isomers 1330-20-7 2,5-10 N Xn,10-20/21-382 N-BUTANOL 71-36-3 25-50 N Xn,10-22-37/38-41-67




Harmful


4. FIRST AID

GENERAL




2/6



















3/6





N-BUTANOL 71-36-3 154,0 mg/m3;Sk -









4/6
























5/6




13. DISPOSAL





HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk







6/6

Classification

Harmful






PRINTEDOUT:

30/08/2001




PRIMASTIC UNIVERSAL STANDARD - COMP. B

1/6


Approved for use



TRADE NAME PRIMASTIC UNIVERSAL STANDARD - COMP. BAPPLICATION Two-pack. modified epoxy based paint

ART-NO PM3341




1 3-AMINOMETHYL-3,5,5-TRIMETHYLCYCLOHEXYLAMINE 2855-13-2 10-25 N C,21/22-34-43-52/532 BENZYL ALCOHOL 100-51-6 10-25 N Xn,20/223 2,2,4 TRIMETHYL HEXAMETHYLENE DIAMINE 25620-58-0 2,5-10 N C,22-34-43-52/534 XYLENE, mixed isomers 1330-20-7 25-50 N Xn,10-20/21-38




Corrosive

FLAMMABLE. HARMFUL BY INHALATION, IN CONTACT WITH SKIN AND IF SWALLOWED.CAUSES BURNS. MAY CAUSE SENSITISATION BY SKIN CONTACT.For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL




2/6

In all cases of doubt, or when symptoms persist, seek medical attention. Obtain advice via telephone; before thepatient is transported to a doctor or hospital. Never give anything by mouth to an unconscious person.


SKIN CONTACTRemove contaminated clothing. Wash skin thoroughly with soap and water or use an appropriate skin cleaner. DoNOT use solvents or thinners. Flush the skin with plenty of water.


INGESTIONDO NOT INDUCE VOMITING. Drink water or milk/cream immediately. Rinse the mouth with large amounts ofwater if the patient is conscious. If accidentally swallowed obtain immediate medical attention. Keep at rest. Seekmedical advice.

MEDICAL INFORMATION Risk of chemical pneumonia by aspiration. Keep attention: danger of lung damage. General health examination.Professional evaluation of the work station. Obtain miedical surveillance concerning burn injuries in mouth andthroat. Aspiration hazard by vomiting. All poisoned persons should be transported in recovery position. Anauthorised person should acompany under the transport. Eye injuries should be treated with chloramphenicol orantiseptic eye treatment. Stomach-rinsing may bee considered, for instance with an antioxydant. Local anestheticamay be given to relieve pain. Eye specialist should be consulted as soon as possible.Person developing a skin rashare to be directed to a dermatologist for exampnation.









HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Always use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing and




3/6

footwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area.For personal protective equipment see Section 8.Always keep in containers made of the same material as the supply container. Never use pressure to empty thecontainer, it is not a pressure vessel. Electrical equipment should be protected to appropriate standards. The ManualHandling Operations Regulations may apply to the handling of containers of this product.






















4/6






INHALATIONExposure to organic solvent vapours may result in adverse health effects such as irritation of the mucous membraneand the respiratory system and adverse effects on the renal and central nervous system. Symptoms and signs includeheadache; dizziness, fatigue, muscular weakness, drowsiness and in extreme cases, loss of consciousness. Vapourmay cause irritation of the respiratory organ and the lungs.

SKIN CONTACTCauses burns.Repeated or prolonged exposure may cause skin irritation and dermatitis, due to the product's defattingproperties.Products containing amines irritates the skin and may lead to allergic eczema.The allergic response mayoccur after a short periode of contact.

EYE CONTACTCauses burns.Severe eye irritationMay cause irreversible eye damage.

INGESTIONAccidental ingestion may cause vomiting and abdominal pains. Risk of chemical pneumonia.Absorbed by thegastric intestinal system. May cause liver and kidney damage. May cause burn damage to mucous membrane,esophagus and stomach.









2,2,4-trimethylhexametylendiamine:Fish: LC50 (96 h) = 1000 mg/lDaphnia: EC50 (24 h) = 31,5 mg/lAlgea: EC50 (72 h) = 29,5 mg/l




5/6

Bacteria: IC50 (3 h) = 100 mg/l

OTHER INFORMATIONDo not discharge the product to sewer or drains.The product contains components which are harmful to aquaticorganisms.

13. DISPOSAL




PROPER SHIPPING NAME AMINES, LIQUID, CORROSIVE, FLAMMABLE, N.O.S. (xylenes,isophoronediamine,)

Toll. reg. no.

HAZCHEM

ADR (Road)


Class 8, PG II Label 8+3Haz. id. no 83 Marginno.

RID (Railway)


Class 8, PG II Label 8+3Haz..id.no 83

IMDG (Sea)


Class 8 Label 8+3Packaging group II EmS 3 - 04MFAG Marine Pollutant

Sub. risk 3 Page

IATA (Airplane)


Class 8 Sub. risk 3Label 8+3 Packaging group II



Classification

Corrosive

COMPOSITION 3-AMINOMETHYL-3,5,5-TRIMETHYLCYCLOHEXYLAMINE (10-25), 2,2,4 TRIMETHYL HEXAMETHYLENEDIAMINE (2,5-10), XYLENE, mixed isomers (25-50)




6/6

R-PHRASESR10 Flammable. R20/21/22 - Harmful by inhalation, in contact with skin and if swallowed. R34 - Causes burns.R43 May cause sensitization by skin contact.

S-PHRASESS23 Do not breathe vapour/spray. S26 In case of contact with eyes, rinse immediately with plenty of water and seekmedical advice.S38 In case of insufficient ventilation, wear suitable respiratory equipment. S36/37/39 Wearsuitable protection clothing, gloves and eyes/face protection. S45 In case of accident or if you feel unwell, seekmedical advice immediately (show the label where possible).



PRINTEDOUT:

21/11/2001


Technical DataPRIMASTIC UNIVERSAL

Product descriptionPrimastic Universal is a two-pack, surface-tolerant, high solids modified epoxy coating. Available with two different hardeners for varying substrate temperatures, Standard (Std) and Cold Climate (CC).

Recommended useAnticorrosive primer for steel structures above and below water, also on steel where blastcleaning may not be possible.

Film thickness and spreading rateStandard Comp. B Minimum Maximum TypicalFilm thickness, dry (µm) 100 250 125Film thickness, wet (µm) 135 330 165Theoretical spreading rate (m²/l)

7,5 3 6

Cold climate Comp. B Minimum Maximum TypicalFilm thickness, dry (µm) 100 250 125Film thickness, wet (µm) 145 360 180Theoretical spreading rate (m²/l)

7 2,8 5,6

Physical propertiesColour Aluminium and Aluminium redtonedSolids (vol %)* 75 ± 2 Standard climate hardener

70 ± 2 Cold climate hardenerFlash point

35ºC ± 2 Standard Comp. B (Setaflash)

31ºC ± 2 Cold Climate Comp. B (Setaflash)

Gloss SemiglossGloss retention FairWater resistance Very goodAbrasion resistance Very goodSolvent resistance Good Chemical resistance Good Flexibility Good


PRIMASTIC UNIVERSAL Page 1

Surface preparation






Condition during applicationThe temperature of the substrate should be minimum +10°C (Std) (-5°C in CC) and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is required in confined areas to ensure proper drying. The coating should not be exposed to oil, chemicals or mechanical stress until cured.




Application data Mixing ratio (volume) 5 parts Comp. A (Base) to 1 part Standard Comp.B.

4 parts Comp. A to 1 part cold Climate Comp. B.Induction time 10 minutes.Pot life (23°C) 2 hours (Standard Comp. B)

1 hours (Cold Climate comp. B) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi.)Nozzle tip 0.58 - 0.79 mm (0.023 - 0.031")Spray angle 40-80°Filter Check to ensure that the filters are clean.


Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateStandard Comp. BSubstrate temperature 10°C 23°C 40°CSurface dry 8 h 4 h 2 hThrough dry 24 h 10 h 4 hCured 14 d 7 d 2 d



Cold climate Comp. BSubstrate temperature -5°C 0°C 5°C 10°C 23°CSurface dry 24 h 18 h 12 h 6 h 2,5 hThrough dry 48 h 26 h 18 h 12 h 5 hCured 21 d 14 d 7 d 3 d 2 d


Dry to recoat, maximum - - - - -


Typical paint systemAbove water:Primastic UniversalHardtop AS

2 x 125 µm1 x 40 µm


Under water:Primastic UniversalAntifouling system as specified

2 x 200 µm (Dry Film Thickness)




Packing size

16 Ltr. Comp. A, 3.2 Ltr. Standard Comp. B.16 Ltr. Comp. A, 4 l Cold Climate Comp. B



Technical DataQUICKSTEP

Product descriptionQuickstep is a quick drying glossy alkyd based topcoat.

Recommended useAs topcoat on exterior and interior floors and normally used over a physically drying primer.



8,4 16,8 12

Physical propertiesColour Limited numberSolids (vol %)* 42 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss GlossyGloss retention GoodWater resistance LimitedAbrasion resistance GoodFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation





QUICKSTEP Page 1





Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 5°C 10°C 23°C 40°CSurface dry 60 min 30 min 20 min 15 minThrough dry 4 h 1 h 1 h 1 hDry to recoat, minimum

1 3 h 2,5 h 2 h 1 h

Quickstep can be recoated with coatings containing xylene or stronger solvents within 8 hours 1.or after 7 days after application.


Typical paint systemVinyguard Silvergrey 88Quickstep

2 x 80 µm1 x 35 µm





QUICKSTEP Page 2











QUICKSTEP Page 3

Technical DataRESIST 78

Product descriptionResist 78 is a two-pack, moisture curing, ethyl silicate based zinc-rich coating. Resist 78 meets Aramco specifications 09-AMSS-071 tested according to SSPC 20.

Recommended useProtection of blast-cleaned steel. Normally used in combination with an epoxy for optimum protection against corrosion. May withstand temperatures up to 400°C.



14 7,8 9,3

CommentsThere is a risk of mud-cracking if the thickness exceeds 120 µm.

Physical propertiesColour GreySolids (vol %)* 70 ± 2 Flash point 14ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent within pH-range 6-10Flexibility Limited


Surface preparation




RESIST 78 Page 1

Condition during applicationThe temperature of the substrate should be min. 5°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Zinc silicate paints in general requires moisture for curing. At low humidity the curing will be improved by gently sprinkling fresh water over the paint film, and/or by artificial humidification of the surrounding atmosphere. The paint must be completely cured before topcoating, otherwise the adhesion of the subsequent coat will be unsatisfactory. Use Methyl ethyl ketone (MEK) test according to ASTM D 4752-87 to verify the curing time before topcoating. Unweathered zinc silicate films are porous and the porosity may vary according to the weather condition during application and the application technique. When overcoating, the air in the pores will escape through the new coat of paint and may cause blisters or pinholes ("popping") in the coat just after application. To avoid this a mist coat/full coat technique is recommended: First apply a thin coat to fill the pores in the zinc silicate film and a few minutes later apply to full specified film thickness. In difficult cases it may be necessary to thin the next coat, or use Penguard Tie Coat 100 as first overcoat.


the specified dry film thickness. In order to avoid settling of heavy zinc, continuous mechanical stirring during application is recommended.

Application data Mixing ratio (volume) Comp. A is a liquid and Comp. B is dry zinc powder. Consists of 10 l

A plus 18.5 kg Comp. B (together 12.6 l paint). Pour the zinc powder slowly into the liquid during mechanical mixing. The Comp. A must be well shaken before use. Stir until lump free and pass through a 60 mesh sieve.

Pot life (23°C) 8 hours. (Reduced at higher temp.) Thinner/Cleaner Adjusting spray pattern and drying may sometimes become

necessary. Use max 5% *, Jotun Thinner No. 4 (fast evaporation) when temperature is low and Jotun Thinner No. 25 (slow evaporation) when temperature is high.

Guiding data airless sprayPressure at nozzle 10 MPa (100 kp/cm², 1400 psi)Nozzle tip 0.46-0.58 mm (0.018-0.023")Spray angle 30-80°Filter Check to ensure that filters are clean.Note * Thinner should be added after mixing components.

RESIST 78 Page 2

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate* Relative humidity at 70%

Substrate temperature 5°C 10°C 23°C 40°CSurface dry 60 min 30 min 15 min 13 minThrough dry 90 min 45 min 30 min 25 minCured

1 18 h 13 h 4 h 1,5 h

Dry to recoat, minimum 2 18 h 13 h 4 h 1,5 h


Curing time to be verified by MEK test (ASTM D 4752-87)1.Recommended data given for recoating with coatings normally specified on top of zinc ethyl 2.silicate coatings.The surface should be free of zinc salts and other contamination prior to application.3.


Typical paint systemResist 78 1 x 75 µm (Dry Film Thickness) Overcoat with an epoxy system.Other systems may be specified, depending on area of use

StorageThe component A must be stored below 25°C and in accordance with national regulations, subject to re-inspection thereafter. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. The product component B is zinc dust and has no strict limitation's for storage. Containers must be kept tightly closed.

HandlingSHELF LIFE: 6 months at 23°C for Comp. A. , 4 years for comp. B. Higher temperatures during storage may reduce the shelf life and may lead to gelling in the tin. Handle with care. Stir well before use.Continuous stirring during application will prevent the heavy zinc pigment from settling.

Packing size10 l Comp. A, 18.5 kg Comp. B. (Together 12.6 l paint).


RESIST 78 Page 3










RESIST 78 Page 4

Technical DataRESIST 86

Product descriptionResist 86 is a two-pack, quick curing zinc rich ethyl silicate coating. The curing rate is dependant on air humidity and temperature.

Recommended useProtection of blast-cleaned steel. Normally used in combination with an epoxy system for optimum protection against corrosion. Withstands temperatures up to 400ºC.



12 6,7 8

CommentsThere is a risk of mud-cracking if the film thickness exceeds 120µm.

Physical propertiesColour Greenish greySolids (vol %)* 60 ± 2 Flash point 14ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent within pH-range 6-10Flexibility Limited


Surface preparation






the specified dry film thickness. In order to avoid settling of heavy zinc, continuous mechanical stirring during application is recommended.

Application data Mixing ratio (volume)

Comp. A is a liquid and Comp. B is dry zinc powder.Consists of 8 l A plus 18,5 kg B (this makes 11,3 ltrs. paint). Pour the zinc powder slowly into the liquid during mechanical mixing. The Comp. A must be well shaken before use. Stir until lump free and pass through a 60 mesh sieve.

Pot life (23°C) 8-12 hours. (Reduced at higher temp.) Thinner/Cleaner Adjusting spray pattern and drying may sometimes become

necessary*. Use max 5% Jotun Thinner No. 4 (fast evaporation) when temperature is low and Jotun Thinner No. 25 (slow evaporation) when temperature is high. Thinner should be added after mixing of components

Guiding data airless sprayPressure at nozzle 10 MPa (100 kg/cm², 1400 psi)Nozzle tip 0.46-0.58 mm (0.018-0.023")Spray angle 30-80ºFilter Check to ensure that filters are clean.Note *Thinner should be added after mixing components.

RESIST 86 Page 2

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate* Relativ humidity of 70%

Substrate temperature 5°C 10°C 23°C 40°CSurface dry 60 min 30 min 15 min 13 minThrough dry 90 min 45 min 30 min 25 minCured

1 18 h 13 h 4 h 1,5 h

Dry to recoat, minimum 2 18 h 13 h 4 h 1,5 h


Curing time to be verified by MEK test (ASTM D 4752-87).1.Recommended data given for recoating with coatings normally specified on top of zinc ethyl 2.silicate coatings.The surface should be free of zinc salts and other contamination prior to application.3.


Typical paint systemResist 86 1 x 75 µm (Dry Film Thickness)Topcoat: Normally with an epoxy system.Other systems may be specified, depending on area of use



Packing size8 ltrs. Comp. A, 18,5 kg Comp. B (This makes 11.3 ltrs. paint).


RESIST 86 Page 3










RESIST 86 Page 4

Technical DataRESIST GTI

Product descriptionResist GTI is a two-pack, moisture curing, ethyl silicate based zinc-rich coating.

Recommended useProtection of blast-cleaned steel. Normally used in combination with an epoxy or a vinyl system for optimum protection against corrosion. Resist GTI can also be used alone for protection of chemical tanks. A separate resistance list is available. May withstand temperatures up to 400°C.



12 6 8

CommentsThere is a risk of mud-cracking if the film thickness exceeds 120 µm.

Physical propertiesColour Greenish greySolids (vol %)* 60 ± 2 Flash point 16ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent within pH-range 6-10Flexibility Limited


RESIST GTI Page 1

Surface preparation







Application data Mixing ratio (volume) 28.5 kg Comp. B (zinc powder) to be poured slowly into 10 l Comp.

A (Base) during mechanical mixing. Stir until lump free and pass through a 60 mesh sieve.

Pot life (23°C) 8-12 hours. (Reduced at higher temp.) Thinner/Cleaner JotunThinner No. 4/25Guiding data airless sprayPressure at nozzle 10 MPa (100 kp/cm² 1400 psi)Nozzle tip 0.46-0.58 mm (0.018-0.023")Spray angle 30-80°Filter Check to ensure that filters are clean.Note Adjusting spray pattern and drying may sometimes become

necessary. Use max 5% Jotun Thinner No. 4 (fast evaporation) when temperature is low and Jotun Thinner No. 25 (slow evaporation) when temperature is high.

REMARKS: Thinner should be added after mixing components.

RESIST GTI Page 2

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate* Relative humidity at 80%Normal hardenerSubstrate temperature 5°C 10°C 23°C 40°CSurface dry 60 min 30 min 15 min 13 minThrough dry 90 min 45 min 30 min 25 minCured

1 36 h 24 h 12 h 7 h


Curing time to be verified by MEK test (ASTM D 4752-87)1.Recommended data given for recoating with coatings normally specified on top of zinc ethyl 2.silicate coatings.


Typical paint systemWhen overcoated:Resist GTI 1 x 75 µm (Dry Film Thickness)Topcoat with an epoxy or a vinyl system.

For interior of tanks:Resist GTI 1 x 100 µm (Dry Film Thickness)


COMPLETE CURING :When Resist GTI is used as a one coat system for the interior of tanks the paint must be completely cured. In order to achieve this the following procedures can be used. - Apply 100 µm Resist GTI - Let the paint dry/cure with good ventilation and low humidity for 4 hours- Then let the paint cure at high humidity and preferably at high temperature. Curing is to be verified by MEK-test (ASTM D 4752-87) - Spray water (seawater is preferred) on the coating and leave the tank closed. Repeat the waterspraying 3-4 times during a 48 hours period - Remove the water and let the tank dry - Check the curing by scraping the coating with a coin. The coin shall produce a shiny mark without any loosened zinc


RESIST GTI Page 3


Packing size10 l Comp. A, 28.5 kg Comp. B (Together 14.5 l paint)Packing may vary from country to country according to local requirements.










RESIST GTI Page 4

Technical DataROYAL WHITE

Product descriptionRoyal White is a high build urethane alkyd based topcoat. It gives a practically non-yellowing colour stable paint film with excellent gloss.

Recommended useAs topcoat over Mammut Primer or other alkyd based primers on steel structure where excellent gloss is required.



6,3 4,9 5,5

Physical propertiesColour WhiteSolids (vol %)* 44 ± 2 Flash point 36ºC ± 2 (Setaflash)Gloss GlossyGloss retention Very goodWater resistance FairAbrasion resistance GoodChemical resistance Good Flexibility Fair*Measured according to ISO 3233:1998 (E)

Surface preparation





ROYAL WHITE Page 1









Typical paint systemMammut PrimerRoyal White

1 x 80 µm1 x 80 µm





Packing size5 l, 20 lPacking may vary from country to country according to local requirements.

ROYAL WHITE Page 2










ROYAL WHITE Page 3

Technical DataSAFEGUARD

Product descriptionSafeguard is a two-pack corrosion preventing coal tar epoxy coating

Recommended useFor use as long term protection of submerged steel and water tanks. Safeguard offers very good adhesion to self-polishing antifoulings when applied under correct conditions



12,8 3,2 4,3

CommentsApplication range, dry, 50** When used as a sealer coat, additional thinner may be necesary (5-10%)

Physical propertiesColour Dark Brown/BrownSolids (vol %)* 64 ± 2 Flash point 27ºC ± 2 (Setaflash)Gloss SemiglossWater resistance ExcellentAbrasion resistance GoodSolvent resistance Good Chemical resistance Good Flexibility Good


SAFEGUARD Page 1

Surface preparation






Condition during applicationThe temperature of the substrate should be minimum 5°C and at least 3ºC above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is required in confined areas to ensure correct drying.




(curing agent)Pot life (23°C) 8 hours (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.53-0.78 mm (0.021-0.031")Spray angle 65-80°Filter Check to ensure that filters are clean.

SAFEGUARD Page 2


Substrate temperature 5°C 10°C 23°C 40°CSurface dry 5 h 2 h 1,5 h 5/6 hThrough dry 48 h 24 h 10 h 4 hCured 21 d 14 d 7 d 3 d



The surface should be free from chalking and contamination prior to application. For interior 1.exposure, note that best intercoat adhesion occurs when the subsequent coat is applied before the preceding coat is cured. For exterior exposure the chalking effect - especially from the sunlight - limits the maximum "dry to recoat" time.


Typical paint systemJotaguard 85Safeguard

1 x 150 µm1 x 150 µm


Antifouling as requiredOther systems may be specified, depending on area of use



Packing size17.15 l Comp. A and 2.85 l Comp. BPacking may vary from country to country according to local requirements.



SAFEGUARD Page 3








SAFEGUARD Page 4



SAFEGUARD UNIVERSAL - COMP. A

1/6


Approved for use



TRADE NAME SAFEGUARD UNIVERSAL - COMP. AAPPLICATION Two-pack. modified epoxy based paint

ART-NO PM3367




1 EPOXY RESIN, LOW MOL. (MW<700) 25068-38-6 10-25 N XiN,36/38-43-51/532 XYLENE, mixed isomers 1330-20-7 10-25 N Xn,10-20/21-383 BENZYL ALCOHOL 100-51-6 1-2,5 N Xn,20/224 ISOBUTANOL 78-83-1 2,5-10 N Xn,10-37/38-41-67




Harmful

FLAMMABLE. HARMFUL BY INHALATION AND IN CONTACT WITH SKIN. IRRITATING TO EYESAND SKIN. MAY CAUSE SENSITISATION BY SKIN CONTACT.For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL




2/6



















3/6

electrically conductive. Keep container tightly closed. Exclude sources of heat, sparks and open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist. Smoking, eating anddrinking are forbidden in the work area.For personal protective equipment see Section 8. Always keep in containersmade of the same material as the supply container. Never use pressure to empty the container, it is not a pressurevessel. Electrical equipment should be protected to appropriate standards. The Manual Handling OperationsRegulations may apply to the handling of containers of this product. Smoking, eating and drinking are forbidden inthe work area.




ISOBUTANOL 78-83-1 - 154,0 mg/m3




HAND PROTECTIONUse (e.g. 4H) gloves or PVA.Barrier creams may help to protect exposed areas of the skin but are not substitutes forfull physical protection. Never apply barrier cream to contaminated skin.





4/6



















INGESTION




5/6

Absorbed by the gastric intestinal system. May cause liver and kidney damage. Accidental ingestion may causevomiting and abdominal pains. Risk of chemical pneumonia.






13. DISPOSAL





HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)



Sub. risk Page

IATA (Airplane)




6/6


Class 3 Sub. risk




Classification

Harmful

COMPOSITION EPOXY RESIN, LOW MOL. (MW<700) (10-25), XYLENE, mixed isomers (10-25)

R-PHRASESR10 Flammable. R20/21 Harmful by inhalation and in contact with skin. R36/38 - Irritating to eyes and skin. R43May cause sensitization by skin contact.

S-PHRASESS23 Do not breathe vapour/spray. S36/37 Wear suitable protective clothing and gloves. S38 In case of insufficientventilation, wear suitable respiratory equipment. P92 Contains epoxy constituents - See information supplied by themanufacturer This information is supplied in the present MSDS.



PRINTEDOUT:

22/10/2001




SAFEGUARD UNIVERSAL - COMP. B


Approved for use



TRADE NAME SAFEGUARD UNIVERSAL - COMP. BAPPLICATION Two-pack. modified epoxy based paint

ART-NO PM3368




1 3-AMINOMETHYL-3,5,5-TRIMETHYLCYCLOHEXYLAMINE 2855-13-2 10-25 N C,21/22-34-43-52/532 BENZYL ALCOHOL 100-51-6 10-25 N Xn,20/223 2,2,4 TRIMETHYL HEXAMETHYLENE DIAMINE 25620-58-0 2,5-10 N C;A,22-34-43-52/53




Corrosive

HARMFUL IF SWALLOWED. CAUSES BURNS. MAY CAUSE SENSITISATION BY SKIN CONTACT. For potential danger for the environment, see section 12.

4. FIRST AID

GENERAL

1 / 6



SAFEGUARD UNIVERSAL - COMP. B In all cases of doubt, or when symptoms persist, seek medical attention. Obtain advice via telephone; before the patient is transported to a doctor or hospital. Never give anything by mouth to an unconscious person.



EYE CONTACTRemove any contact lenses. Hold the eyelids apart. Rinse with lukewarm water for 1 hour. Seek medical advice.


MEDICAL INFORMATION Regulary medical control. Person developing a skin rash are to be directed to a dermatologist for examination.Obtain miedical surveillance concerning burn injuries in mouth and throat. Aspiration hazard by vomiting. All poisoned persons should be transported in recovery position. An authorised person should acompany under the transport. Stomach-rinsing may bee considered, for instance with an antioxydant. Eye injuries should be treated with chloramphenicol or antiseptic eye treatment. Local anesthetica may be given to relieve pain.










2 / 6



SAFEGUARD UNIVERSAL - COMP. B the same material as the supply container. The Manual Handling Operations Regulations may apply to the handling of containers of this product.




RESP. PROTECTIONWhen workers are facing concentrations above the occupational exposure limit they must use appropriate certified respirators.Use respiratory protective mask with charcoal and dust filter (A2/P2) when spraying this product. When spraying, use also K-filter.


HAND PROTECTIONUse (e.g. 4H) gloves or PVA.Barrier creams may help to protect exposed areas of the skin but are not substitutes for full physical protection. Never apply barrier cream to contaminated skin.



Form Liquid. Colour Yellowish. Odour Organic solvent. Solubility Organic solvent. Melting point/range - Density 1,03Expl. limit LEL-UEL., %-%: 1,3 - 13,0 Solubility in water



pH Solution Boiling point/range 205ºCFlash point >100ºC pH concentrate -Molecular weight Viscosity








3 / 6






INHALATIONExposure to vapours may result in adverse health effects such as irritation of the mucous membrane and the respiratory system.

SKIN CONTACTProlonged contact may cause burn damage. Products containing amines irritate the skin and may lead to allegic ecema. The allergic response may occur after a short periode of contact.


INGESTIONAccidental ingestion may cause vomiting and abdominal pains. May cause burn damage to mucous membrane, esophagus and stomach.








OTHER INFORMATIONThe product should not be allowed to enter drains or water courses or be deposited where it can affect ground or surface waters. The product contains components which are harmful to aquatic organisms, see point 2.

13. DISPOSAL

Wastes, including emptied containers, are controlled wastes and should be disposed of in accordance with regulations made under the Control of Pollution Act and the Environmental Protection Act.


4 / 6





PROPER SHIPPING NAME AMINES, LIQUID, CORROSIVE, N.O.S.(isophorone diamine,2,2,4-trimethyl hexamethylene diamine.)


ADR (Road)UN No. 2735 Dang. goods


RID (Railway)UN No. 2735 Dang. goods


IMDG (Sea)UN No. 2735 Dang. goods


Sub. risk Page

IATA (Airplane)UN No. 2735 Dang. goods

Class 8 Sub. risk

Label Corrosive Packaging group III



Classification

Corrosive


R-PHRASESR22 Harmful if swallowed. R34 - Causes burns. R43 May cause sensitization by skin contact.




5 / 6



SAFEGUARD UNIVERSAL - COMP. B PRINTED OUT:

05/10/2001

VENDOR NOTES The information contained in this MSDS is based on the present state of knowledge and current national legislation. As the specific conditions of use of the product are outside the supplier's control, the user is responsible for ensuring that the requirements of relevant legislation are compiled with. The information in this MSDS provides guidance on health, safety and environmental aspects of the product and should not be construed as any guarantee of technical performance or suitability for particular applications. The Environmental Protection (Duty of Care) Regulations 1992 (SI 1992:2839). Further information and relevant advice can be found in: The Control of Substances Hazardous to Health Regulations 1988 (SI1988:1657). The Highly Flammable Liquids and liquefied Petroleum Gases Regulations 197 (SI 1972:917). The Manual Handling Operations Regulations 1992 (SI 1992:2793). Storage of Flammable Liquids in Containers, HS(G)51. Storage of Packaged Dangerous Substances, HS(G)71. The selection, use and maintenance of respiratory protective equipment: A practical guide HS(G)53.

6 / 6



SAFEGUARD UNIVERSAL COLD CLIMATE -COMP. B

1/6


Approved for use



TRADE NAME SAFEGUARD UNIVERSAL COLD CLIMATE - COMP. BAPPLICATION Two-pack epoxy paint.

ART-NO PM3369






INGREDIENT COMMENTS Substances presenting a health hazard within the meaning of the current issue of the CHIP Regulations orassigned occupational exposure limits.


Harmful


4. FIRST AID

GENERAL




2/6















HANDLING ADVICEVapours are heavier than air and may spread along floors. Vapours may form explosive mixtures with air. Preventthe creation of flammable or explosive concentrations of vapour in air and avoid vapour concentration higher thanthe occupational exposure limits. The product should not be used in vicinity of open flames or other sources ofignition. Use explosion-proof electrical equipment. The product may charge electrostatically. Always use earth(ground) wire when transferring from one container to another. Personnel should wear anti-static clothing andfootwear. Floors should be electrically conductive. Keep container tightly closed. Exclude sources of heat, sparksand open flame. Use non-sparking tools. Avoid skin and eye contact. Avoid inhalation of vapour and spray mist.Smoking, eating and drinking are forbidden in the work area.For personal protective equipment see Section 8.




3/6

Always keep in containers made of the same material as the supply container. Never use pressure to empty thecontainer, it is not a pressure vessel. Electrical equipment should be protected to appropriate standards. The ManualHandling Operations Regulations may apply to the handling of containers of this product.











Form Liquid.Colour Brown.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 1,0Expl. limit LEL-UEL., %-%: 1,1-11,3 Solubility in water







Rel. vapor density (air=1) Rel. evap. velocity -





4/6














13. DISPOSAL






5/6


PROPER SHIPPING NAME RESIN SOLUTIONToll. reg. no.

HAZCHEM

ADR (Road)



RID (Railway)



IMDG (Sea)


Class 3 Label 3Packaging group III EmS 3-05MFAG Marine Pollutant

Sub. risk Page

IATA (Airplane)


Class 3 Sub. risk




Classification

Harmful





6/6





PRINTEDOUT:

21/11/2001


Technical DataSAFEGUARD UNIVERSAL

Product descriptionSafeguard Universal is a two-pack corrosion preventing epoxy vinyl-based coating. Available with two different hardeners for varying substrate temperatures, Standard (Std) and Cold Climate (CC).

Recommended useSafeguard Universal is normally used as undercoat in combination with epoxy and polyurethane systems. It gives a very good adhesion for various topcoats (not alkyds) as well as self-polishing antifoulings.



13 3,2 4,3

CommentsAs a sealer coat, (dry film thickness 50 µm) additional thinner may be necessary (5-10%)Spreading rates shown for standard version only.

Physical propertiesColour Red, GreySolids (vol %)* 65 ± 2 Standard climate hardener

62 ± 2 Cold climate hardenerFlash point 27ºC ± 2 (Setaflash)

lbs/gal (330 gms./ltr.) USA-EPA Method 24263 gms./ltr.UK-PG6/23(92).Appendix 3

Gloss SemiglossWater resistance ExcellentAbrasion resistance GoodSolvent resistance Good Chemical resistance Good Flexibility Good


SAFEGUARD UNIVERSAL Page 1

Surface preparation





Condition during applicationThe temperature of the substrate should be minimum +10°C (Std) (-5°C in CC) and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is required in confined areas to ensure proper drying. The coating should not be exposed to oil, chemicals or mechanical stress until cured.



Application data Mixing ratio (volume) 8,5 parts Comp. A (base) to 1 part Standard Comp. B (curing agent)

5,7 parts Comp. A (base) to 1 part Cold Climate Comp. B (curing agent)

Pot life (23°C) 2 hours (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.53-0.78 mm (0.021-0.031")Spray angle 65-80° Filter Check to ensure that filters are clean.Note * The temperature of the mixture of base and curing agent is

recommended to be at least 15°C, otherwise extra solvent may be required to obtain correct viscosity.* Too much solvent results in lower sag resistance and slower cure.* Thinner should be added after mixing components.


Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateSafeguard Universal Standard:Substrate temperature 10°C 23°C 40°CSurface dry 6 h 3 h 1,5 hThrough dry 20 h 8 h 3,5 hCured 14 d 7 d 3 d



Safeguard Universal Cold Climate:Substrate temperature 0°C 5°C 10°C 23°CSurface dry 15 h 10 h 5 h 2 hThrough dry 24 h 18 h 12 h 5 hCured 14 d 7 d 3 d 2 d


Dry to recoat, maximum - - - -

The surface should be free from chalking and contamination prior to application. For interior 1.exposure, note that best intercoat adhesion occurs when the subsequent coat is applied before the preceding coat is cured.


Typical paint systemJotamastic 87 AluminiumSafeguard Universal

1 x 200 µm1 x 150 µm


Antifouling as requiredOther systems may be specified, depending on area of use



Packing size17 l Comp. A and 2 l Standard Comp. B or 3 l Cold Climate Comp. B.



Technical DataSE-LETT

Product descriptionSe-Lett is a light reflecting paint transforming and reflecting light in a very visible bright colour.

Recommended useSe-Lett is used for warning signs and signal color on airplanes and airports, transport material, quay structures, liferafts, beacons and buoys, signposts etc.



19 11,2 14

Physical propertiesColour Signal orangeSolids (vol %)* 56 ± 2 Flash point 40ºC ± 2 (Setaflash)Gloss FlatFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation





Application methodsSpray Use conventional sprayBrush Recommended for stripe coating and small areas, care must be taken to achieve


SE-LETT Page 1

Application data Thinner/Cleaner Jotun Thinner No. 2Filter Check to ensure that filters are clean.




The surface should be free from any contamination prior to application of the subsequent 1.coat.


Typical paint systemA conventional corrosion protection system to be overcoated with:Pilot I whiteSe-LettSe-Lett Clear Varnish

2 x 40 µm2 x 40 µm1 x 30 µm






SE-LETT Page 2










SE-LETT Page 3

Technical DataSE LETT CLEAR VARNISH

Product descriptionSe Lett Clear Varnish is an acrylic based varnish containing UV- and light stabilizing additives that prolong the durability of the system.

Recommended useSe Lett Clear Varnish is used on top of Se Lett.



11 13,2 11

Physical propertiesColour ClearSolids (vol %)* 33 ± 2 Flash point 62ºC ± 2 (Setaflash)Gloss SemiglossFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation





Application methodsSpray Use conventional sprayBrush May be used but care must be taken to achieve the specified dry film thickness.Roller May be used however when using roller application care must be taken to apply


Application data Thinner/Cleaner Jotun Thinner No. 2Filter Check to ensure that filters are clean.


Substrate temperature 5°C 10°C 23°C 40°CSurface dry 4 h 3 h 2 h 1h hThrough dry 9 h 4 h 3 h 1,5 hDry to recoat, minimum 9 h 4 h 3 h 1,5 h




Typical paint systemA conventional corrosion protection system:Pilot I whiteSe-LettSe-Lett Clear Varnish

2 x 40 µm2 x 40 µm1 x 30 µm





Packing size1 ltr.Packing may vary from country to country according to local requirements.

SE LETT CLEAR VARNISH Page 2










SE LETT CLEAR VARNISH Page 3

Technical DataSHOPPRIMER EPS

Product descriptionShopprimer EPS is an epoxy based quick drying primer.

Recommended useTo be used as a preconsturction primer on blast cleaned steel surfaces in automatic shoppriming plants to protect steel during transport, storage and production.



12,5 8,3


Physical propertiesColour Grey and RedSolids (vol %)* 25 ± 2 Flash point -5ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance Very goodSolvent resistance Very good Flexibility Good


Surface preparationThe coating may be used on other substrates. Please contact your local Jotun office for more information.

Condition during applicationThe temperature of the substrate should be min. 3°C above the dew point of the air in the vicinity of the substrate. Recommended steel temperature 30-40°C.


Substrate temperature 23°C 40°CSurface dry 1-3 min 20-40 sec Through dry 4 min 1-2 minCured 7 d 3 d





Typical paint systemShopprimer EPS 1 x 20-30 µm (Dry Film Thickness measured on a smooth test panel).Normally overcoated with a choice of systems based on chlorinated polymers, vinyl or epoxy resins.Other systems may be specified, depending on area of use


HandlingStir well before use.

Packing size18.0 l Comp. A and 0.5 l Comp. B. Packing may vary from country to country according to local requirements.



SHOPPRIMER EPS Page 2








SHOPPRIMER EPS Page 3

Technical DataSHOPPRIMER IRON OXIDE EPOXY TWO-PACK

Product descriptionShopprimer Iron Oxide Epoxy Two Pack is an epoxy based quick drying primer.




12,5 8,3

CommentsDry film thickness measured on a smooth test panel

Physical propertiesColour RedSolids (vol %)* 25 ± 2 Flash point -5ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance Very goodSolvent resistance Very good Flexibility Good


Surface preparation




SHOPPRIMER IRON OXIDE EPOXY TWO-PACK Page 1




0.5 parts Comp. B (curing agent).Pot life (23°C) 24-36 hours (Reduced at higher temp.). Thinner/Cleaner Jotun Thinner No. 3/17

( No. 3 - Fast evaporation) - (No. 17 - Slow evaporation)Guiding data airless sprayPressure at nozzle 10-15 MPa (100-150 kp/cm² 1500-2100 psi).Nozzle tip 0.38-0.53 mm (0.015-0.021").Spray angle 40-95ºCFilter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 23°C 40°CSurface dry 1-3 min 20-40 sec Through dry 4 min 1-2 minCured 7 d 2,5 d

Dry to recoat, minimum 7 h 2,5 h


Typical paint systemShopprimer Iron Oxide Epoxy Two-Pack 1 x 20-30 µm (Dry Film Thickness measured on a smooth test panel).

Normally overcoated with a choice of systems based on chlorinated polymers, vinyl or epoxy resins.Other systems may be specified, depending on area of use




Packing size17.0 l Comp. A and 0.5 l Comp. B. Packing may vary from country to country according to local requirements.











Technical DataSHOPPRIMER IRON OXIDE PVB FD ONE-PACK

Product descriptionShopprimer Iron Oxide PVB FD One-Pack is a vinyl phenolic resin modified quick drying primer with very low content of free phenol.




6,5 4,3


Physical propertiesColour Red and GreySolids (vol %)* 13 ± 2 Flash point -5ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance GoodSolvent resistance Limited Flexibility Good


Surface preparation




SHOPPRIMER IRON OXIDE PVB FD ONE-PACK Page 1



Application data Thinner/Cleaner Jotun Thinner No. 4/11

(No. 4. - Fast evaporation) - (No. 11 - Slow evaporation).Cleaner Guiding data airless sprayPressure at nozzle 5-8 MPa (50-80 kp/cm², 700-1120 psi).Nozzle tip 0.38-0.58 mm (0.015-0.023").Spray angle 40-95ºCFilter Check to ensure that filters are clean.


Substrate temperature 23°C 40°CSurface dry 1-2 min 15-30 sec Through dry 3 min 1-2 minDry to recoat, minimum 4 h 4 h


Typical paint systemShopprimer Iron Oxide PVB FD One-Pack 1 x 20 - 30 µm (Dry Film Thickness measured on a smooth test panel).

Normally overcoated with a choice of systems based on alkyds, chlorinated polymers, vinyl or epoxy resins.Other systems may be specified, depending on area of use



HandlingSHELF LIFE: 3 months at room temperature. Handle with care. Stir well before use.

Packing size20 l Shopprimer Iron Oxide PVB FD One-Pack.200 l Shopprimer Iron Oxide PVB FD One-Pack.1000 l Shopprimer Iron Oxide PVB FD One-Pack.Packing may vary from country to country according to local requirements.











Technical DataSHOPPRIMER IRON OXIDE PVB ONE-PACK

Product descriptionShopprimer Iron Oxide PVB One-Pack is a vinyl phenolic resin modified quick drying primer with very low content of free phenol.




6,5 4,3


Physical propertiesColour RedSolids (vol %)* 13 ± 2 Flash point -5ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance GoodSolvent resistance Limited Flexibility Good


Surface preparation




SHOPPRIMER IRON OXIDE PVB ONE-PACK Page 1



Application data Thinner/Cleaner Jotun Thinner No. 4/11

(No. 4. - Fast evaporation) - (No. 11 - Slow evaporation).Cleaner Guiding data airless sprayPressure at nozzle 5-8 MPa (50-80 kp/cm² 700-1120 psi).Nozzle tip 0.38-0.58 mm (0.015-0.023").Spray angle 40-95ºCFilter Check to ensure that filters are clean.




Typical paint systemShopprimer Iron Oxide PVB One-Pack 1 x 20 - 30 µm (Dry Film Thickness measured on a smooth test panel).

Normally overcoated with a choice of systems based on alkyds chlorinated polymers, vinyl or epoxy resins.Other systems may be specified, depending on area of use



HandlingSHELF LIFE: 3 months at room temperature. Handle with care. Stir well before use.

Packing size20 l Shopprimer Iron Oxide PVB One-Pack.200 l Shopprimer Iron Oxide PVB One-Pack.1000 l Shopprimer Iron Oxide PVB One-Pack.Packing may vary from country to country according to local requirements.











Technical DataSHOPPRIMER IRON OXIDE PVB TWO-PACK

Product descriptionShopprimer Iron Oxide PVB is a two-pack, vinyl phenolic resin modified quick drying primer with a very low content of free phenol.

Recommended useTo be used as a preconstruction primer on blast cleaned steel surfaces in automatic shoppriming plants to protect steel during transport, storage and production.



6,5 4,3


Physical propertiesColour Red and GreySolids (vol %)* 13 ± 2 Flash point -5ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance GoodSolvent resistance Limited Flexibility Good


Surface preparation




SHOPPRIMER IRON OXIDE PVB TWO-PACK Page 1



Application data Mixing ratio (volume) 19.5 parts Comp. A to be mixed thoroughly with 0,5 parts Comp. B.Pot life (23°C) 2-3 weeks Thinner/Cleaner Jotun Thinner No. 4/11

(No. 4 - Fast evaporation) - (No. 11 - Slow evaporation)Guiding data airless sprayPressure at nozzle 5-8 Mpa (50-80 kp/cm² 700-1120 psi).Nozzle tip 0.38-0.58 mm (0.015-0.023).Spray angle 40-95ºFilter Check to ensure that filters are clean.




Typical paint systemShopprimer Iron Oxide PVB Two-Pack 1 x 20-30µm (Dry Film Thickness measured on a smooth test panel.)

Normally overcoated with a choice of systems based on alkyds chlorinated polymers, vinyl or epoxy resins.Other systems may be specified, depending on area of use




Packing size19.5 l Comp. A. 0.5 l Comp. B.195 l Comp. A. 5 l Comp. B.975 l Comp. A. 25 l Comp. B.Packing may vary from country to country according to local requirements.











Technical DataSPONTAN VARNISH

Product descriptionSpontan Varnish is a clear varnish based on urethane alkyd

Recommended useProtection of interior and exterior wood work.



16,4 8,2 11,7

Physical propertiesColour TransparentSolids (vol %)* 41 ± 2 Flash point 36ºC ± 2 (Setaflash)Gloss GlossyGloss retention Very goodWater resistance GoodAbrasion resistance GoodFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation

Clean and dry surface. Surface contamination is to be removed by detergents and fresh water cleaning.





SPONTAN VARNISH Page 1

Application data Thinner/Cleaner Jotun Thinner No. 2






Typical paint systemSpontan Varnish 1 - 3 x 35 µm (Dry Film Thickness)

New wood-work should first be prepared with one coat Spontan Varnish thinned 10% with Jotun Thinner No. 2. Other systems may be specified, depending on area of use



Packing size3.0 l Packing may vary from country to country according to local requirements.


Technical DataSOLVALITT

Product descriptionSølvalitt is a heat resisting paint based on silicone acrylic binder.

Recommended useTo be used as a topcoat on items exposed to high temperatures (up to 600ºC) in combination with Zinc Silicate coatings, maximum 400ºC.

Film thickness and spreading rateAluminium Minimum Maximum TypicalFilm thickness, dry (µm) 20 30 20Film thickness, wet (µm) 60 85 60Theoretical spreading rate (m²/l)

17,5 11,7 17,5

Colours Minimum Maximum TypicalFilm thickness, dry (µm) 20 30 20Film thickness, wet (µm) 50 70 50Theoretical spreading rate (m²/l)

21 14 21

Physical propertiesColour Aluminium and limited colour rangeSolids (vol %)* 35 ± 2 Aluminium

42 ± 2 ColoursFlash point 26°C (Setaflash)Gloss Aluminium sheen/FlatFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation





SOLVALITT Page 1






Substrate temperature 5°C 10°C 23°C 40°CSurface dry 60 min 45 min 30 min 15 minThrough dry 4 h 3 h 2 h 1 hDry to recoat, minimum 6 h 3 h 2 h 1 h




Typical paint systemResist GTI or 78 or 86SølvalittorSølvalitt

1 x 75 µm1-2 x 20 µm

2-3 x 20 µm



SOLVALITT Page 2


HandlingSHELF LIFE: 6 months at 23°C. Higher temperatures during storage may reduce the shelf life and may lead to gelling in the tin. Handle with care. Stir well before use.











SOLVALITT Page 3

Technical DataSOLVALITT 230

Product descriptionSølvalitt 230 is a heat resistent paint based on a silicone acrylic binder.

Recommended useApplied over inorganic zinc silicate primers such as Resist GTI or Resist 86 for protection of steel work under elevated temperatures up to 230ºC dry temperature service ( for intermittant periods up to 250ºC).



14 7 9,3

Physical propertiesColour AluminiumSolids (vol %)* 28 ± 2 Flash point 33ºC (Setaflash)Gloss GlossyGloss retention GoodWater resistance Very goodAbrasion resistance GoodSolvent resistance Limited Chemical resistance Good Flexibility Good


Surface preparation



Coated surfacesCured and clean zinc silicate primer.





Application data Thinner/Cleaner Jotun Thinner No. 7Guiding data airless sprayPressure at nozzle 15 Mpa (150 kp/cm² 2100 psi)Nozzle tip 0.38-0.46 mm (0.018-0.026")Spray angle 40-80ºFilter Check to ensure that filters are clean.


Substrate temperature 5°C 10°C 23°C 40°CSurface dry 60 min 45 min 30 min 15 minThrough dry 4 h 3 h 2 h 1,5 hDry to recoat, minimum

1 4-8 h 3-6 h 2-4 h 1,5-3 h



Typical paint systemResist 86/78 or Resist GTISølvalitt 230orSølvalitt 230

1 x 75 µm1-2 x 30 µm

2-3 x 20 µm




SOLVALITT 230 Page 2

HandlingSHELF LIFE: 6 months at 23°C. Higher temperatures during storage may reduce the shelf life and may lead to gelling in the tin. Handle with care. Stir well before use.











SOLVALITT 230 Page 3

Technical DataTANKGUARD AQUA

Product descriptionTankguard Aqua is a solvent-free, two-pack epoxy coating for potable water tanks. This product has a BS 6920 (1996) certificate for the carriage and storage of potable water

Recommended useA mechanically very strong, high build, solvent free coating.



4,44 2 3,3

CertificatesThis product has a BS (6920 (1996) certificate for the carriage and storage of potable water.(These certificates are just a few examples of available certificates. Please contact Jotun for details)

Physical propertiesColour White, Light RedSolids (vol %)* 100 ± Flash point >100ºC ± (Setaflash)Gloss GlossyGloss retention FairWater resistance ExcellentAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent Flexibility Fair


Surface preparation


Bare steelBlast cleaning to Sa 2½. (ISO 8501-1:1988). Should this product be applied over any zinc rich primer or zinc shopprimer the use of an epoxy tie coat is needed please consult your local Jotun office.



Application methodsSpray 2 comp. plural airless spray equipment or airless spray equipment with high pressure

ratio (min. 65:1). When being sprayed through airless spray equipment the product temp should be maintained between 22-30 ºC , with recommended temp. of 25-30 ºC, this provides the best optimum working potlife. If an extended length of spray hose is used it may be advisable to use heated paint lines to maintain the product temperature.



(curing agent). Mixing ratio (weight): 10 kg Comp. A and 3,3 kg Comp. B.

Pot life (23°C) 30 minutes at 23ºC. Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle Using a 65:1 airless pump and 80 psi entry pressure providing >35.3

MPa (>353kp/cm² >5200 psi). The best spray pattern is achieved using a 70 degree 0.021" thou tip size with a hose diameter min. 3/8", max length 20m.

Nozzle tip 0.58 or 0.63 mm (0.021" or 0.023")Spray angle 70ºFilter Remove filter at nozzle.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 5°C 10°C 23°C 40°CSurface dry 24 h 16 h 4 h 3 hThrough dry 48 h 24 h 10 h 5 hCured 21 d 14 d 7 d 3 d





TANKGUARD AQUA Page 2

Typical paint systemOn Sa 2½Tankguard Aqua 2 x 300µm (Dry Film Thickness)

Note: Tankguard Aqua should not be used on top of of any zink rich primer/shopprimer.




Packing size12 l Comp. A (base) and 6 l Comp. B (curing agent).Packing may vary from country to country according to local requirements.










TANKGUARD AQUA Page 3

Technical DataTANKGUARD HB

Product descriptionTankguard HB is a high-build epoxy coating with high resistance to a wide range of chemicals and solvents.

Recommended useInteriors of tanks and gas pipes. A separate resistance list is available.



6,3 3,3 5

Physical propertiesColour Light grey, Light green and red.Solids (vol %)* 50 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance Very goodSolvent resistance Excellent Chemical resistance Excellent


Surface preparation





TANKGUARD HB Page 1




(curing agent)Mixing ½ hour prior to usePot life (23°C) 8 hours (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 23Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.46-0.69 mm (0.018-0.027")Spray angle 40-80ºCFilter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 10°C 23°C 40°CSurface dry 7 h 3,5 h 1,5 hThrough dry 24 h 6 h 4 hCured 14 d 7 d 3 d





Typical paint systemTankguard HB 3 x 100 µm (Dry Film Thickness) Other systems may be specified, depending on area of use



TANKGUARD HB Page 2











TANKGUARD HB Page 3

Technical DataTANKGUARD SPECIAL PRIMER AND MID-COAT

Product descriptionTankguard Special Primer and Mid-Coat is a two-component phenolic epoxy coating with high resistance to a wide range of chemicals and solvents.

Recommended useInterior of tanks. Tankguard Special Primer and Tankguard Special Mid-Coat are the first and second coat in the Tankguard Special coating system. A separate resistance list is available.



7,9 4,2 6,3

Physical propertiesColour Light red (primer), Yellow (mid-coat)Solids (vol %)* 63 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodSolvent resistance Excellent Chemical resistance Excellent Flexibility Fair


Surface preparation





TANKGUARD SPECIAL PRIMER AND MID-COAT Page 1





(curing agent)Induction time 20 minutes.Pot life (23°C) 3 hours (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 23Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.46-0.69 mm (0.018-0.027")Spray angle 40-80°Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 15°C 23°C 40°CSurface dry 10 h 5,5 h 2 hThrough dry 16 h 8,5 h 4 hCured 14 d 7 d 3 d



The surface should be free from chalking and contamination prior to application. If the 1.maximum dry to recoat time is exceeded, please contact Jotun Protective Coatings for advice.


Typical paint systemTankguard Special PrimerTankguard Special Mid-CoatTankguard Special Topcoat

100 µm100 µm100 µm




Technical DataTANKGUARD SPECIAL TOPCOAT

Product descriptionTankguard Special Topcoat is a two-component phenolic epoxy coating with high resistance to a wide range of chemicals and solvents.

Recommended useInterior of tanks. Tankguard Special Topcoat is the final coat in the Tankguard Special coating system. A separate resistance list is available.



7,9 4,2 6,3

Physical propertiesColour GreySolids (vol %)* 63 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss SemiglossWater resistance Very goodSolvent resistance Excellent Chemical resistance Excellent Flexibility Fair


Surface preparation

Clean and dry surface. Surface contamination is to be removed by detergents and fresh water cleaning.



TANKGUARD SPECIAL TOPCOAT Page 1



Application data Mixing ratio (volume) 3,7 parts Comp. A (base) to be mixed thoroughly with

1 part Comp. B (curing agent)Induction time 20 minutes.Pot life (23°C) 3 hours (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 23Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.46-0.69 mm (0.018-0.027")Spray angle 40-80°Filter Check to ensure that filters are clean.


Substrate temperature 23°C 40°CSurface dry 5,5 h 2 hThrough dry 8,5 h 4 hCured 7 d 3 d





Typical paint systemTankguard Special PrimerTankguard Special Mid-CoatTankguard Special Topcoat

100 µm100 µm100 µm






Packing size14,7 l Comp. A and 4 l Comp. B Packing may vary from country to country according to local requirements.











Technical DataTANKGUARD STORAGE

Product descriptionTankguard Storage is a two-component, high solid phenolic epoxy coating with high resistance to a wide range of chemicals and solvents.

Recommended useCorrosion protection for the internal lining of steel storage tanks being resistant to a wide range of chemicals including, but not limited to, crude oil and aromatic and aliphatic solvents and others.



6,3 3,2 5

Physical propertiesColour Light red and redSolids (vol %)* 63 ± 2 Flash point 28ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodSolvent resistance Excellent Chemical resistance Excellent Flexibility Fair


Surface preparation





TANKGUARD STORAGE Page 1




Application data Mixing ratio (volume) 6,5 parts Comp. A (base) to be mixed thoroughly with 1 part Comp.

B (curing agent)Induction time 20 minutes.Pot life (23°C) 4 hours (Reduced at higher temp.) Thinner/Cleaner Jotun Thinner No. 23Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.46-0.69 mm (0.018-0.027")Spray angle 40-80°Filter Check to ensure that filters are clean.






Typical paint systemTankguard Storage 2 x 125 µm (Dry Film Thickness)Other systems may be specified, depending on area of use




Packing size16,3 l Comp. A and 2,5 l Comp. B Packing may vary from country to country according to local requirements.













ULTRA TOPCOAT

1/6


Approved for use



TRADE NAME ULTRA TOPCOATAPPLICATION Alkydbased based topcoat.

ART-NO PM3096




1 XYLENE, mixed isomers 1330-20-7 25-50 N Xn,10-20/21-382 1-METHOXY-2-PROPANOL 107-98-2 1-2,5 N 103 AROMATIC HYDROCARBONS C9-C12 64742-95-6 2,5-10 N XnN,10-37-65-51/53




Harmful


4. FIRST AID

GENERAL



ULTRA TOPCOAT

2/6

















ULTRA TOPCOAT

3/6













Form Liquid.Colour Various.Odour Organic solvent.Solubility Organic solvent.Melting point/range - Density 1,21Expl. limit LEL-UEL., %-%: 0,1 - 7,0 Solubility in water










ULTRA TOPCOAT

4/6









INGESTIONAbsorbed by the gastric intestinal system. May cause liver and kidney damage. Accidental ingestion may causevomiting and abdominal pains. Risk of chemical pneumonia. Product contains small amounts of lead-components,that are toxic.






OTHER INFORMATIONDo not discharge the product to sewer or drains. The product contains aromatic hydrocarbons C9-C12 labelled"Dangerous for the environment".

13. DISPOSAL

Wastes, including emptied containers, are controlled wastes and should be disposed of in accordance withregulations made under the Control of Pollution Act and the Environmental Protection Act.




ULTRA TOPCOAT

5/6



HAZCHEM

ADR (Road)

UN No. Dang. goods

Class Label


RID (Railway)

UN No. Dang. goods

Class Label

Haz..id.no

IMDG (Sea)


Class 3.3 Label 3Packaging group III EmS 3 - 05MFAG 310 Marine Pollutant

Sub. risk Page 3372

IATA (Airplane)

UN No. Dang. goods

Class Sub. risk




Classification

Harmful







ULTRA TOPCOAT

6/6


PRINTEDOUT:

16/10/2001


Technical DataULTRA TOPCOAT

Product descriptionUltra Topcoat is a quick drying and glossy acrylic modified alkyd topcoat that contains aromatic solvents.

Recommended useTo be used as topcoat on steel and other metal constructions with high gloss and colour retention demands.



15 11,3 12,8

Physical propertiesColour According to Multicolor tinting system(MCI)Solids (vol %)* 46 ± 2

37 ± 2 BlackFlash point 25ºC ± 2 (Setaflash)Gloss GlossyWater resistance LimitedAbrasion resistance LimitedFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation





ULTRA TOPCOAT Page 1




Application data Thinner/Cleaner Jotun Thinner No. 7Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi.)Nozzle tip 0.38 - 0.53 mm (0.015 - 0.021")Spray angle 40 - 80ºFilter Check to ensure that the filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 60 min 30 min 20 min 15 minThrough dry 5 h 3 h 3 h 2 hCured

1



Ultra Topcoat can be recoated with coatings containing xylene or stronger solvents within 30 1.hours or after 7 days after application.The surface should be dry and free from any contamination prior to application of the 2.subsequent coat.


Typical paint systemConseal PrimerUltra Topcoat

2 x 40 µm1 x 35 µm






Technical DataUNIVERSAL PRIMER

Product descriptionUniversal Primer is a two-pack, abrasion resistant, high solids epoxy-based primer/topcoat which may be applied in high film thickness.

Recommended useOn steel. Can be used alone or in combination with various systems of primers and topcoats. Gives excellent corrosion protection both in salt and fresh water.



4,8 2,4 4,8

Physical propertiesColour Aluminium, limited numberSolids (vol %)* 72 ± 2 Flash point 35ºC ± 2 (Setaflash)VOC 240 gms./ltr.UK-PG6/23(92).Appendix 3Gloss SemiglossGloss retention FairWater resistance Very goodAbrasion resistance Very goodSolvent resistance Good Chemical resistance Very good Flexibility Good


UNIVERSAL PRIMER Page 1

Surface preparation


Bare steelSand sweeped steel to min. Sa 2 ½ or intact shopprimer. Improved surface treatment will improve the performance.




Condition during applicationThe temperature of the substrate should be minimum -5°C and minimum 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is required in confined areas to ensure proper drying. Do not use heated air until the solvents have evaporated from the paint film to avoid surface drying and solvent entrapment. The coating should not be exposed to stain until cured.

Application methodsSpray Use airless sprayBrush Recommended for stripe coating and small areas, care must be taken to achieve the

specified dry film thickness.Roller May be used for small areas but not recommended for first primer coat, however


Application data Mixing ratio (volume) 3 parts Comp. A to 1 part Comp. BMixing 10 min prior to useInduction time 10 minutes.Pot life (23°C) 2 hours (reduced at higher temperatures) Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.53-0.79 mm (0.021-0.031")Spray angle 40-80°Filter Check to ensure that filters are clean.


Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature -5°C 0°C 5°C 10°C 23°CSurface dry 24 h 15 h 8 h 5 h 2,5 hThrough dry 60 h 30 h 20 h 10 h 5 hCured 21 d 14 d 7 d 3 d 2 d

Dry to recoat, minimum 1 60 h 30 h 20 h 10 h 5 h


Substrate temperature 40°CSurface dry 1 hThrough dry 2 hCured 1 d

Dry to recoat, minimum 1 2 h

Dry to recoat, maximum 2 -

1 Recommended data given for recoating with the same generic type of paint.2 Provided the surface is free from chalking and other contamination prior to application, there is

normally no overcoating time limit. Best intercoat adhesion occurs, however, when the subsequent coat is applied before preceding coat has cured. If the coating has been exposed to direct sunlight for some time, special attention must be paid to surface cleaning and mattening/removal of the surface layer in order to obtain good adhesion.



Universal Primer 2 x 150 µm (Dry Film Thickness)Hardtop AS 1 x 50 µm (Dry Film Thickness)




Packing size13.5 l Comp. A and 4.5 l Comp. B Packing may vary from country to country according to local requirements.


Technical DataVINYGUARD BLACK/BROWN

Product descriptionVinyguard Black/Brown is a vinyl-coal tar coating.

Recommended useOn buried or submerged structures offering high water and chemical resistance. Easily applied even at low temperatures. Excellent in combination with cathodic protection.



6 3,6 4,5

Physical propertiesColour Black, BrownSolids (vol %)* 36 ± 2 Flash point 30ºC ± 2 (Setaflash)Gloss FlatWater resistance ExcellentAbrasion resistance Very goodSolvent resistance Limited Chemical resistance Good Flexibility Good


Surface preparation






Condition during applicationThe temperature of the substrate should be minimum 3ºC above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is required in confined areas to ensure correct drying.





Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 40 min 30 min 20 min 15 minThrough dry 3 h 2,5 h 2 h 1,5 hDry to recoat, minimum 2,5-8 h 2-6 h 1,5-4,5 h 1,5 h


Typical paint systemBarrierorShopprimer Iron OxideVinyguard Black/Brown/Black

1 x 25-50 µm

1 x 25 µm3 x 80 µm




VINYGUARD BLACK/BROWN Page 2













VINYGUARD BLACK/BROWN Page 3

Technical DataVINYGUARD SILVERGREY 88

Product descriptionVinyguard Silvergrey 88 is a quick drying, non tar modified vinyl primer.

Recommended useAs a touch-up primer. Contains no tar and can be used as a primer under vinyl, chlorinated rubber and alkyd coatings for steel structures, both above and below the waterline.



10,9 3,8 4,8

CommentsWhen used as a sealer coat in 35µm dry film thickness, 5-10% additional thinning may be necessary.

Physical propertiesColour Aluminium and aluminium red tonedSolids (vol %)* 38 ± 2 Flash point 28ºC ± 2 (Setaflash)Gloss FlatWater resistance Very goodAbrasion resistance GoodSolvent resistance Limited Chemical resistance Good Flexibility Good


Surface preparation





Other surfaces

VINYGUARD SILVERGREY 88 Page 1







Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrateNormal hardenerSubstrate temperature 5°C 10°C 23°C 40°CSurface dry 30 min 20 min 15 min 10 minThrough dry 4 h 3 h 2 h 1.5 hDry to recoat, minimum

1 4 h 3 h 2 h 2 h




Typical paint systemBelow water:Vinyguard Silvergrey 88 3 x 80 µm (Dry Film Thickness)Above water:Vinyguard Silvergrey 88Pioner Topcoatalt.Pilot II

2 x 80 µm1 x 50 µm

1 x 40 µm





Packing size20 Ltr. Packing may vary from country to country according to local requirements.











Technical DataWASHPRIMER

Product descriptionWashprimer is a two-pack, vinyl based primer containing phosphoric acid.

Recommended useGalvanized steel and aluminium surfaces. Improves performance of subsequent coats. Washprimer must not be used under two-pack epoxy paints.



22 11 11

Physical propertiesColour Green/Yelllow (transparent)Solids (vol %)* 11 ± 2 Flash point 13ºC ± 2 (Setaflash)Gloss FlatFlexibility Excellent*Measured according to ISO 3233:1998 (E)

Surface preparation





the specified dry film thickness.Roller Recommended

WASHPRIMER Page 1

Application data Mixing ratio (volume) 4 parts of Comp. A (base) to 1 part Comp. B (curing agent).Pot life (23°C) 8 hours. Thinner/Cleaner Jotun Thinner No. 4Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.33-0.46 mm (0.013-0.018")Spray angle 40-80ºFilter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate Substrate temperature 5°C 10°C 23°C 40°CSurface dry 60 min 45 min 30 min 13 minThrough dry 120 min 90 min 60 min 25 minDry to recoat, minimum

1 120 min 90 min 60 min 25 min


Typical paint systemWashprimerCromoprimer/AlkydprimerPilot II

1 x 10 µm1 x 30 µm1 x 40 µm





Packing size4 l Comp. A, 1 l Comp. B0.8 l Comp. A, 0.2 l Comp. B Packing may vary from country to country according to local requirements.

WASHPRIMER Page 2










WASHPRIMER Page 3

Technical DataWATERFINE ACRYLIC PRIMER

Product descriptionWaterFine Acrylic Primer is a one-pack anticorrosive primer based on an acrylic emulsion.

Recommended useAs primer on steel, galvanized steel and aluminium above waterline. The product is quick dring and give good corrosion protection in mildly to moderate corrosive environments. May be overcoated with water borne acrylics, solvent borne acrylics, alkyds, epoxies and polyurethane paints.



5,7 3,8 5,7

CommentsVOC: 66 g/l (Actual).

Physical propertiesColour Grey, RedSolids (vol %)* 46 ± 2 Gloss FlatWater resistance Good*Measured according to ISO 3233:1998 (E)

Surface preparation





Other surfacesFor aluminium and galvanized surface; degreasing, light abrading or sand sweeping.


Condition during applicationThe temperature of the substrate should be minimum 5°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to ensure proper drying. Risk of dry spraying when applying at low relative humitity (below 30 %).

Application methodsSpray Use airless spray or conventional spray (thin 5-10 % with fresh clean water)Brush Recommended for stripe coating and small areas, care must be taken to achieve



Application data Thinner/Cleaner Fresh clean water.Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.38 - 0.53 mm (0.015 - 0.023") Spray angle 40-80°Filter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate* Relative Humidity 70%.

Substrate temperature 5°C 10°C 23°C 40°CSurface dry 60 min 40 min 30 min 15 minThrough dry 3 h 1,5 h 1 h 0,5 hDry to recoat, minimum 3 h 2,5 h 1 h 1 h


Typical paint systemCorrosivity category C2 (ISO 12944)WaterFine Acrylic PrimerWaterFine Topcoat

1 x 80 µm1 x 50 µm


Corrosivity category C3 (ISO 12944)WaterFine Acrylic PrimerWaterFine Topcoat

2 x 120 µm1 x 40 µm



WATERFINE ACRYLIC PRIMER Page 2

Procedure for preparation and cleaning of application equipmentTo avoid solvent contamination of the water borne paint the spraying equipment has to be conditioned before use. All equipment containing solvents in the pump, hoses and gun have to be thoroughly cleaned according to the following instructions.




StorageThe product must be stored above 0°C and in accordance with national regulations, subject to re-inspection thereafter. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed. WaterFine Acrylic Primer should be protected from temperatures higher than 40ºC.






Technical DataWATERFINE BARRIER

Product descriptionWaterFine Barrier is a three-pack, water borne organic zinc rich epoxy primer. Complies with SSPC 20:1982.

Recommended useAs primer on steel in a complete water borne corrosion resistant paint system. Can also be used in systems together with suitable solvent borne coatings, such as epoxy, acrylics etc. Not to be overcoated with alkyds.



11,2 6,2 9,3

CommentsVOC: 92,5 g/l (Actual).

Physical propertiesColour Red (toned)Solids (vol %)* 56 ± 2 Flash point Non-flammable Gloss FlatWater resistance Very goodAbrasion resistance GoodSolvent resistance Very good Flexibility Fair


Surface preparation








Application data Mixing ratio (volume) 6.3 l Comp. A (Epoxy base) to be mixed thoroughly with 1.4 l

Comp. B (Curing agent), then 16.9 kg Comp. C (Zinc powder) to be sifted slowly into Comp. A + B and mixed thoroughly. This gives 10.0 l paint. It is recommended to pass the mixture through a 50 mesh sieve before use.

Mixing ½ hour prior to use.Pot life (23°C) 6 hours Thinner/Cleaner Fresh clean waterCleaner Fresh clean water and Jotun Thinner No. 4Guiding data airless sprayPressure at nozzle 15 Mpa (150 kp/cm2 2100 psi)Nozzle tip 0.38-0.53 mm (0.017-0.023”).Spray angle 40-80°Filter Make certain that the filters are perfectly clean.Note With WaterFine Barrier it is recommended to flush system with

Jotun Thinner No. 4 and then circulate water through the spraying equipment for some minutes before application. After paintwork is finished, first flush the system with water and then Jotun Thinner No. 4.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate* Relative Humidity 50%.

Substrate temperature 10°C 23°C 40°CSurface dry 35 min 15 min 15 minThrough dry 40 h 4 h 3 hCured 14 d 7 d 5 d



WATERFINE BARRIER Page 2

Typical paint systemCorrosivity category C5-I (ISO 12944), (System 1, NORSOK M-501)WaterFine BarrierWaterFine PrimerWaterFine Topcoat

1 x 50 µm1 x 120 µm1 x 80 µm


For transport containers:WaterFine BarrierWaterFine Topcoat Semigloss

1 x 60 µm1 x 80 µm








StorageThe product must be stored above 0°C and in accordance with national regulations, subject to re-inspection thereafter. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. Containers must be kept tightly closed.


Packing size6.3 l Comp. A, 1.4 l Comp. B and 16.9 kg Comp. C. (Together 10 l paint)Packing may vary from country to country according to local requirements.










ISSUED 11 MARCH 2002 BY JOTUN PAINTSTHIS DATA SHEET SUPERSEDES THOSE PREVIOUSLY ISSUED


Technical DataWATERFINE PRIMER

Product descriptionWaterFine Primer is a two-pack, anticorrosive, quick drying, water borne epoxy primer / intermediate paint which cures down to 5°C. Contains active corrosion protective pigments and flashrusting inhibitors.

Recommended useAs a primer/intermediate paint on steel, aluminium, galvanized steel and thermally sprayed zinc surfaces above the waterline. May be overcoated with water borne acrylics, water borne epoxy and suitable solvent borne coatings.



9,2 3,7 7,6


Physical propertiesColour Grey, RedSolids (vol %)* 46 ± 2 Flash point non flammable Gloss GlossyWater resistance Very goodFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation





WATERFINE PRIMER Page 1





Application data Mixing ratio (volume) 1 part of Comp. A to be thoroughly mixed with 1.2 part of Comp. B.

To secure a proper mix. a mechanical stirrer should be used to stir up both the components separately before mixture and during the mixing of the two components thoroughly down to the bottom of the vessel (mix for at least 5 minutes).

Induction time 30 minutes.Pot life (23°C) 3 hours. NOTE: THE PAINT MUST NOT BE USED AFTER EXCEEDED

POT LIFE TIME. USE E.G. AN ALARM CLOCK TO TELL WHEN THE POT LIFE HAS EXCEEDED.

Thinner Fresh clean water.Cleaner Jotun Thinner No. 17 and Jotun Thinner No. 4Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.38-0.53 mm (0.017-0.023")Spray angle 40-80°Filter Make certain that the filters are perfectly clean.Note In order to secure a proper mixing, it is recommended that the

temperature of the two components is approx. 20ºC when mixing.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate* Relative humidity 70%.

Substrate temperature 5°C 10°C 23°C 40°CSurface dry 60 min 60 min 45 min 45 minThrough dry 5 d 2 d 1 d 1 dCured 20 d 14 d 7 d 5 d


Dry to handle : 5ºC = 6 hours, 10ºC = 2 hours, 23ºC = 2 hours, 35ºC = 1 hour.



Typical paint systemCorrosivity category C4 (ISO 12944)WaterFine PrimerWaterFine Topcoat

2 x 60 µm1 x 50 µm


Corrosivity category C5-I (ISO 12944), (System 1, NORSOK M-501)WaterFine Barrier WaterFine PrimerWaterFine Topcoat

1 x 50 µm1 x 120 µm1 x 80 µm










Packing size9 l Comp. A, 11 l Comp. B. Packing may vary from country to country according to local requirements.




Technical DataWATERFINE SPECIAL

Product descriptionWaterFine Special is a two-pack water borne epoxy intermediate paint which cures down to 5°C.

Recommended useAs an intermediate paint for both water borne and hybrid systems in aggressive environments above the waterline and to be used as a tie coat between some solvent borne and water borne paints.



8 3,8 6

CommentsVOC: 72,5 g/l (Actual).

Physical propertiesColour White, GreySolids (vol %)* 48 ± 2 Flash point Non flammable Gloss FlatWater resistance GoodFlexibility Good*Measured according to ISO 3233:1998 (E)

Surface preparation





WATERFINE SPECIAL Page 1




Application data Mixing ratio (volume) 12.8 l of Comp. A to be throughly mixed with 7.2 l of Comp. B.

To secure a proper mix. a mechanical stirrer should be used during the mixing of the two components.

Induction time 30 minutes.Pot life (23°C) 3 hours Cleaner Fresh clean water, Jotun Thinner No. 4 or No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.38-0.53 mm (0.015-0.021")Spray angle 40-80ºFilter Make certain that the filters are perfectly clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate* Relative humidity 70%

Substrate temperature 5°C 10°C 23°C 40°CSurface dry 7 h 2 h 1,5 h 1 hThrough dry 7 d 3 d 0,5 d 0,3 dCured 20 d 14 d 7 d 5 d




Typical paint systemCorrosivity category C5-I (ISO 12944)

Water borne system:WaterFine Zn-PrimerWaterFine SpecialWaterFine SpecialWaterFine Topcoat

1 x 40 µm1 x 90 µm1 x 70 µm1 x 50 µm


Hybrid system:*Jotamastic 87WaterFine SpecialWaterFine Topcoat

1 x 200 µm 1 x 40-80 µm1 x 50 µm


* WaterFine Special used as tie-coat between solvent-borne and water borne-coating.


Procedure for preparation and cleaning of application equipment To avoid solvent contamination of the water borne paint the spraying equipment has to be conditioned before use. All equipment containing solvents in the pump, hoses and gun have to be thoroughly cleaned according to the following instructions.






Packing size12.8 l Comp. A, 7.2 l Comp. B.Packing may vary from country to country according to local requirements.


Technical DataWATERFINE TOPCOAT

Product descriptionWaterFine Topcoat is an one-pack hard and glossy topcoat based on an acrylic emulsion.

Recommended useAs topcoat on water borne primer or intermediate coat in a complete water borne corrosion resistant paint system. High gloss and very good weather properties. Can also be used in combination with suitable solvent borne/solvent free primer/undercoat, and as maintenance coating on a wide range of topcoats.



9 4,5 6


Physical propertiesColour White and selection of coloursSolids (vol %)* 36 ± 2 Gloss GlossyGloss retention ExcellentWater resistance GoodFlexibility Very good*Measured according to ISO 3233:1998 (E)

Surface preparation




WATERFINE TOPCOAT Page 1

Condition during applicationThe temperature of the substrate should be minimum 5°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to ensure proper drying. Risk of dry spraying when applying at low relative humitity (below 30 %).


the specified dry film thickness.Roller May be used but care must be taken to achieve the specified dry film thickness.

Roller quality available.

Application data Thinner/Cleaner Fresh clean waterGuiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm² 2100 psi)Nozzle tip 0.38-0.53 mm (0.015 - 0.021")Spray angle 40-80ºFilter Check to ensure that filters are clean.

Drying timeDrying times are generally related to air circulation, temperature, film thickness and number of coats, and will be affected correspondingly. The figures given in the table are typical with:* Good ventilation (Outdoor exposure or free circulation of air)* Typical film thickness* One coat on top of inert substrate* Relative humidity 70%

Substrate temperature 5°C 10°C 23°C 40°CSurface dry 90 min 30 min 25 min 20 minThrough dry 6 h 1,5 h 1 h 1 hDry to recoat, minimum 8 h 2,5 h 1,5 h 1 h


Typical paint systemCorrosivity category C4 (ISO 12944)WaterFine PrimerWaterFine Topcoat

2 x 100 µm1 x 50 µm


Corrosivity category C5-I (ISO 12944)WaterFine BarrierWaterFine PrimerWaterFine Topcoat

1 x 50 µm2 x 120 µm1 x 80 µm




Procedure for preparation and cleaning of application equipmentTo avoid solvent contamination of the water borne paint the spraying equipment has to be conditioned before use. All equipment containing solvents in the pump, hoses and gun have to be thoroughly cleaned according to the following instructions.






Packing size20 ltr. Packing may vary from country to country according to local requirements.




Technical DataWATERFINE ZN PRIMER

Product descriptionWaterFine Zn Primer is a two-pack, water borne inorganic zinc rich silicate primer.

Recommended useAs primer on blast cleaned steel in a complete water borne corrosion resistant paint system. Can also be used in systems together with suitable solvent borne coatings, such as epoxy, acrylics etc. Not to be overcoated with alkyds.



38 11,4 14,3


Physical propertiesColour GreySolids (vol %)* 57 ± 2 Flash point Non-flammableGloss FlatWater resistance Very goodAbrasion resistance ExcellentSolvent resistance Excellent Chemical resistance Excellent within pH range of 6-10Flexibility Limited


Surface preparation




WATERFINE ZN PRIMER Page 1

Condition during applicationThe temperature of the substrate should be minimum 5°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is usually required in confined areas to ensure proper drying. Use mistcoat technique for subsequent coat to avoid popping (pinholes). If possible avoid application at relative humidity below (30%) due to risk of dry spraying.

Application methodsSpray Conventional spray. (for example, Wiwa high pressure pump R/F/W-G-34020).Brush Recommended for stripe coating and small areas, care must be taken to achieve


Application data Mixing ratio (volume) 27,6 kg Comp. B (Zinc powder) to be sifted slowly into 10 l. Comp.

A. (Silicate solution) and mixed thoroughly. This gives 14.1 l paint. It is recommended to pass the mixture through a 60 mesh sieve before use.

Pot life (23°C) 5 hours Thinner/Cleaner Fresh waterNote With WaterFine Zn Primer it is recommended to flush system with

Jotun Thinner No. 4 and then circulate water through the spraying equipment for some minutes before appliction. After paintwork is finished, flush the system with water. During painting it is necessary to continuously stir the paint with a mechanical stirrer.


Substrate temperature 5°C 10°C 23°C 40°CSurface dry 25 min 15 min 10 min 10 minThrough dry 60 min 25 min 20 min 15 minCured 20 d 14 d 7 d 5 d



Typical paint systemWaterFine Zn PrimerWaterFine SpecialWaterFine SpecialWaterFine Topcoat

1 x 40 µm1 x 90 µm1 x 70 µm1 x 50 µm









StorageThe component A must be stored above 0°C and in accordance with national regulations, subject to re-inspection thereafter. Storage conditions are to keep the containers in a dry, cool, well ventilated space and away from source of heat and ignition. The product component B is zinc dust and has no strict limitation's for storage. Containers must be kept tightly closed.

HandlingHandle with care. Stir well before use.Continuous stirring during application will prevent the heavy zinc pigment from settling. SHELF LIFE: 9 months at 23°C for Comp. A, 4 years for comp. B Higher temperatures during storage may reduce the shelf life and may lead to gelling in the tin.

Packing size10 l Comp. A, 27.6 kg Comp. B. (Together 14,1 l paint)Packing may vary from country to country according to local requirements.




Technical DataWINTERGRADE BALLOXY HB LIGHT

Product descriptionWintergrade Balloxy HB Light is a two pack modified epoxy coating intended for use at temperatures between -5°C and 10°C.

Recommended useWintergrade Balloxy HB Light is intended for use in water ballast tanks, on steel behind insulation, in cofferdams and areas with condensation and where blastcleaning may not be possible.



4,7 2,4 3,6

Physical propertiesColour Beige/GreenSolids (vol %)* 71 ± 2 Flash point 35ºC ± 2 SetaflashGloss FlatWater resistance ExcellentAbrasion resistance Very goodSolvent resistance Good Chemical resistance Good Flexibility Good


WINTERGRADE BALLOXY HB LIGHT Page 1

Surface preparation






Condition during applicationThe temperature of the substrate should be minimum -5°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is required in confined areas to ensure proper drying. The coating should not be exposed to oil, chemicals or mechanical stress until cured.





(Curing agent).Induction time 10 minutes.Pot life (23°C) 1½ hours. Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi.)Nozzle tip 0.53 - 0.79 mm (0.021 - 0.031")Spray angle 40 - 80°Filter Check to ensure that the filters are clean.Note REMARKS:

* The temperature of the mixture of base and curing agent is recommended to be at least 15°C, otherwise extra solvent may be required to obtain correct viscosity.* Too much solvent results in lower sag resistance and slower cure.* Thinner should be added after mixing components.



Substrate temperature

Cold temperature hardenerSubstrate temperature -5°C 0°C 5°C 10°C 23°CSurface dry 24 h 18 h 12 h 6 h 2,5 hThrough dry 48 h 26 h 18 h 12 h 5 hCured 21 h 14 h 7 h 3 h 2 h



The surface should be free from chalking and contamination prior to application. Best 1.intercoat adhesion occurs when the subsequent coat is applied before the preceding coat has cured. If this is exceeded it may be necessary to roughen the surface.


Typical paint systemWintergrade Balloxy HB Light 2 x 200 µm (Dry Film Thickness)Other systems may be specified, depending on area of use



Packing size15 l Comp. A, 5 l Comp. BPacking may vary from country to country according to local requirements.


Technical DataWINTERGRADE PENGUARD HB

Product descriptionWintergrade Penguard HB is a high build, two-pack amine adduct cured epoxy coating.

Recommended useAs part of a system for steel and concrete structures above and below water. It is possible to use Wintergrade Penguard HB down to -5ºC.



5,6 3 4,5

Physical propertiesColour Grey, Red, WhiteSolids (vol %)* 45 ± 2 Flash point 25ºC ± 2 (Setaflash)Gloss FlatGloss retention FairWater resistance Very goodAbrasion resistance Very goodSolvent resistance Excellent Chemical resistance Excellent


WINTERGRADE PENGUARD HB Page 1

Surface preparation





Condition during applicationThe temperature of the substrate should be minimum -5°C and at least 3°C above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. Good ventilation is required in confined areas to ensure proper drying. The coating should not be exposed to oil, chemicals or mechanical stress until cured.




Application data Mixing ratio (volume) 10 parts Comp. A (Base) to be thoroughly mixed with 1 part Comp.

B (Curing agent). Induction time 30 minutes.Pot life (23°C) 4 hour Thinner/Cleaner Jotun Thinner No. 17Guiding data airless sprayPressure at nozzle 15 MPa (150 kp/cm², 2100 psi)Nozzle tip 0.58 - 0.79 mm (0.023 - 0.031")Spray angle 40 - 80°Filter Check to ensure that filters are clean.Note * The temperature of the mixture of base and curing agent is

recommended to be at least 15ºC, otherwise extra solvent may be required to obtain correct viscosity.* Too much solvent results in lower sag resistance and slower cure.* Thinner should be added after mixing components.



Substrate temperature

Substrate temperature -5°C 0°C 5°C 10°C 23°CSurface dry 10 h 6 h 3 h 2 h 1 hThrough dry 36 h 24 h 12 h 8 h 4 hCured - d 14 d 7 d 5 d 3 d



Provided the surface is free from chalking and other contamination prior to application, there 1.is normally no overcoating time limit. If the coating has been exposed to direct sunlight for some time, special attention must be paid to surface cleaning and mattening/removal of the surface layer in order to obtain good adhesion.


Typical paint systemWintergrade Penguard HBHardtop AS

2 x 100 µm1 x 40 µm





Packing size16 l Comp. A (base) and 1.6 l Comp.B (curing agent)4 l Comp. A (base) and 0.4 l Comp. B (curing agent)Packing may vary from country to country according to local requirements.


newuk_p

Documents

specified dry film thickness

typical film thickness

csurface dry

hthrough dry

dry heat

primer coat

complete system

system sheet