PowerLabs Nitrocellulose Synthesis

INTRODUCTION:

Also known as "Cellulose Nitrate", "Collodion Wool", "Soluble Gun Cotton", "Iodion Cotton", "Pyroxylin", "Colloxylin" "Xyloidin","Celloidin" "Parlodion", nitrocellulose is a product that has found many uses on everyday life. It is a white, yellow or transparentplastic, which can be anywhere from brittle to flexible. Nitrocellulose (mainly C6H7N3O11)is used to make anything fromSmokeless Gun Powder (also called Triple Base, due to the addition of nitroglycerine, nitroguanidine flash suppressor and burnrate catalysts), Double Base (DB) solid rocket propellants (with 30 - 50% nitroglycerine added to result in a perfect oxygenbalance), to waterproof fuses in pyrotechnics, inks, adhesives, varnishes, resins, lacquer coatings, embedding sections inmicroscopy, photography, electro techniques, galvanoplasty, and even certain plastics, such as what is used in ping-pong balls.It can have properties ranging from a strong, resistant plastic to an unstable class B (highly flammable, explosive whenconfined) explosive material, all determined by the nitrogen content... Here the procedure for making nitrocellulose are outlined with the sole intent of scientific information. Although it is one of thesafest nitration procedures (there have been no reported cases (at least that I am aware off) of incidents occurring duringmanufacture), and the cellulose nitrate produced here is of a lower nitrogen content (the plastic tetranitrate, as opposed to theexplosive hexanitrate), the products do require expert handling, and even though it does not constitute in a very big explosionhazard, the procedure requires the handling of concentrated Sulphuric and Nitric acids, as well as highly flammable Acetone,which make it very hazardous for anyone unskilled with chemistry to attempt. Once again I discourage anyone to attempt theseprocedures, and if you choose to do so you are doing it at your own risk.

Reactants: Materials:

98% Concentrated Sulphuric Acid (H2So4(l)) Two clean glass beakers

70% Concentrated Nitric Acid (HNO3(aq)) Pipette

Pure Cotton (90% Cellulose, C6H10O5(s)) Stirring Rod

Acetone ((CH3)2CO(l))

Distilled Water (l)

Sodium Bicarbonate (NaHCO3(s))

For trinitrate the formula is as follows: C6H7O(OH)3O + 3 OHNO2 --> C6H7(ONO2)3O + 3H2O

Here all the materials and reactants needed for the synthesis of nitrocellulose can be seen: From the back row to the front,from left to right:

100mL bottle of 98%Conc. H2So4, 100mL bottle of 70% Conc. HNO3, 1L ofDistilled Water, 100mL of Acetone. 10mL Glass pipette 0.5g cotton pad, 2X 150mL Pyrex glass beakers Glass stirring rod.

For this procedure 5ml of 50 - 50% (by vol.) nitrating mixture was prepared, as seen below, and to it the .5g cotton pad was

Nitrocellulose synthesis by POWERLABS! http://www.powerlabs.org/chemlabs/nitrocellulose.htm

1 de 4 23/01/14 20:00

added. The cotton was allowed to nitrate for five minutes at room temperature, while stirring.

The cotton was than washed once in saturated sodium bicarbonate solution and 2 times in distilled water, until the leftoverwater tested neutral. It was than allowed to thoroughly dry and dissolved in acetone.

The acetone was than allowed to vaporize until a concentrated syrup-like nitrocellulose lacquer formed. A small bit ofun-nitrated cotton was than removed, and the rest of the acetone was allowed to dry.

Below a dry cylinder of nitrocellulose can be seen. Notice how it has taken the shape of the beaker and how it formed thinsheets of NC that were smeared on the sides of the beaker: those thin sheets are a material very similar to what is used inguitar and other resistant, high gloss coatings... Next to it is a picture of the cellulose burning. It burns all at once, with a fastbright flame and a characteristic "phomp!" noise as the gas expands. The yellow color is due to carbon in the NC molecule.Notice how it does not produce any smoke. There is, however some residue left, proof that this plastic is the product ofincomplete nitration.

Nitrocellulose synthesis by POWERLABS! http://www.powerlabs.org/chemlabs/nitrocellulose.htm

2 de 4 23/01/14 20:00

CELLULOSE HEXANITRATE:

(For curiosity purposes only, POWERLABS outlines the method used for making rocket-fuel and double base powder gradenitrocellulose.) The procedure is very similar to the one outlined above, except it uses a slightly different nitrating mixture. The proportions arenow 35% / 65% (by volume) for HNO3 / H2SO4, assuming that the acid concentrations used were the same as the ones usedabove. 5 parts of acid are used for every part of dry cellulose (per weight). An alternate nitrating mix is made by adding 1gram offinely powdered Potassium or Sodium Nitrate (KNO3/NaNo3) for every 3.325g (3.819ml) of cold concentrated Sulphuric Acid(H2SO4), and than add cotton to this nitrating mixture when the temperature has stabilized. I don't use this particular procedurebecause it is hazardous (there is a lot of heat involved in the formation of nitric acid by removal of nitrate from the potassiumion) and can cause sputtering as well as releasing toxic fumes. Plus resultant mixture is not only nitric and sulphuric acids, butalso includes potassium or sodium sulphate, which will have a negative effect on the quality of the final product. Complete nitration takes about 10 minutes at room temperature. On a small scale not enough heat is evolved to justify an icebath, which would only slow the process down. The mixture with a greater sulphuric acid content is able to impart more nitrateions to the cellulose, causing it to have a much higher nitrate (nitrogen and oxygen) content. The procedure is still reasonablysafe to perform from a stability point of view (meaning that it is virtually impossible for the nitrocellulose to form upon formation),but now the resultant product (when dry) burns a lot faster, hotter, and releases much more energy than the trinitrate above. Itis, in fact, one of the most energetic deflagrants known, capable of DDT (Deflagration - Detonation Transition) with 123-147%the explosive strength of TNT when detonated at 7300 meters per second (Nitrocellulose (13.35% N) max density 1.2g/cc). NOTE: It is very important to thoroughly neutralize the nitrocellulose by boiling it in NaHCO3 and in distilled water several timesuntil it tests neutral. It is also recommendable to add 0.5-1% of Urea or diphenylamine in fine powder form to neutralize anyremaining nitrogen oxides that could become acidic in moisture and causing accidental ignition of the product. This product can be stored safely under water or dissolved in acetone (NC Lacquer). Now I must say the warning. The nitrocellulose produced by this method is EXPLOSIVE and can deflagrate or even detonateviolently on shock, friction, or spark when dry. These procedures are not to be attempted, and are outlined here only forinformational purposes.

Click on the frame sequence above to watch a short (146KB) .mpg video of a 3cm (1.2") 1gram fluffy nitrocellulose ball beingdeflagrated by flame. The ball was merely sitting on top of a stand, as *ANY* confinement, even it being inside an open jar,would have resulted in an explosion. The heat produced by this burn is so fantastic that it could be felt over a two meters away(you should never look directly at large deflagrations as the light emitted can cause damage to the retina). Despite the fact thatthe camera was positioned 2 meters from the flame, and that all adjustments were made to avoid the light flooding effect, thecamera still couldn't handle the flash that was made. The sound of the flame is a low pitched thump, indicating a large, subsonicair displacement. Of course, due to file size limitations a lot of the original sound and video quality were lost.

Finally, you might have seen (or heard off) a product called "Flash paper" its oftenused in magic tricks: A square piece of normal (white) paper that burns quickly in aflash without making any smoke or leaving any residue. All it is is a piece ofnitrated paper, as per the above method. The picture here shows a piece ofnitrated toilet paper (around the metal stand) burning.

Nitrocellulose synthesis by POWERLABS! http://www.powerlabs.org/chemlabs/nitrocellulose.htm

3 de 4 23/01/14 20:00

Note: Runaway nitration for nitrocellulose occurs at 70oC. Never allow it to go above that temperature while in a nitratingmixture. Never attempt to nitrate large batches at once as the increased heat output will invariably result in runaway.

Comments? Questions? Don't hesitate to e-mail me!

People have visited this page since 27/04/00

Last update 11/02/10

Copyright � 2000-2002 by Sam Barros. All rights reserved. Removing any material from this site for display without consent from its author consists in an infringement of internationalcopyright laws and can result in fines up to $50000 per infringement, plus legal costs. So ASK ME before you removeanything from here.

Nitrocellulose synthesis by POWERLABS! http://www.powerlabs.org/chemlabs/nitrocellulose.htm

4 de 4 23/01/14 20:00