KNOCKOUT
THE COMPETITION
INTRODUCING
DH2FMODIF IED H-13PREHARDENED 37-41 HRC
FEATURES:• Prehardened to 37-41 HRC. No additional heat treating required.
Suited for complex molds and dies susceptible to deformation.• Good machinability• Reduced manufacturing time due to no additional heat treating.• DH2F has better wear resistance than H-13 at like hardness.
Quality Characteristics III cont’d
• An example of tool life offace milling cutter
• An example of tool life ofHSS drill bit
MACHINABILITY
Corporate Office: Lindquist Steels, Inc. 1050 Woodend RoadStratford, CT 06615
800-243-9637 • FAX: 203-386-0132
DH2F is distributed byLindquist Steels, Inc.,
a Daido partner company
200
100
50
30
Tool life T (min)
30 50 70100 200105
VBmax
Cut
ting
spee
d V
(m
/min
)
Cut
ting
spee
d V
(m
/min
) 200
100
30
20
Cutting length L (m/m)
50 70100 300 500 100305
• Cutting parametersTool material Tool shape Cutting fluid Feed Cut
Face milling center M20 NP-100R None 0.075mm/tooth 1.5mm 66-165 80w x 50T x 200l 40 VBmax=0.3mm
Drill bit M2 None 0.1mm/rev 30mm deep hole 20-40 80w x 50T x 200l 40 Tool erosion
Cutting speed Test piece size Hardness Tool life(m/min) (mm) (HRC) and point
10mm dia.tapered-shank drill a = 118”
• DH2F (modified (H13) Prehardened) • H-13 (40 HRC)CHIP SHAPE
www.lindquiststeels.com
Daido Steel Limited and Lindquist Steels, Inc. shall not be held responsible for damage caused by misunderstanding or improper use of the technical information con-tained in this brochure. The contents of this brochure may be subject to change without notice. Please inquire for the latest information. No portion of this brochure may be reproduced without the express permission of Daido Steel Limited and International Mold Steel, Inc.
ParametersTool
CUTTING PARAMETERS:Tool : M2, 10 mm dia., tapered-shank drill a=118˚Feed : 0.10mm/revHole depth : 30 mm
Cutting speed : 25m/minTest piece hardness : 40HRCTest piece size (mm) : 100 x 200 x 300
DAIDO STEEL
APPLICATIONS:• Plastic Molds• Zinc Diecasting Dies• Short Run Aluminum
Die Casting Dies• Plunger Tips, Sprue
Bushings• Die Plate Strippers• Dies for Aluminum
Extrusions• Pattern’s and Core Boxes• Others
Lindquist Steels, Inc. 1950 Old Dunbar Road
West Columbia, SC 29172800-845-7052 • FAX: 803-794-6658
Corporate Office: Lindquist Steels, Inc. 1050 Woodend RoadStratford, CT 06615
800-243-9637 • FAX: 203-386-0132
www.lindquiststeels.com
Lindquist Steels, Inc. 1950 Old Dunbar Road
West Columbia, SC 29172800-845-7052 • FAX: 803-794-6658
www.imsteel.com
DH2Flsi 10/2/06 9:57 AM Page 1
Chemical Composition
Quality Characteristics II
Quality Characteristics III
RT 100 200 300 400 500 600 700
160(1569)
120(1179)
80(785)
40(392)
0
600
400
200
90
70
50
30
10(98)
6(59)
2(19.6)
�
Test temperature (C˚)
Hard
ness
(HV)
T
ensil
e stre
ngth
and
yield
poi
nt k
gf/m
m2 (M
Pa)
Char
py im
pact
ener
gy k
gf •
m/cm
2 (J/
cm 2 )
Elon
gatio
n an
d re
ducti
on o
f are
a (%
)
Hardness
Quality Characteristics I
• Average Coefficient of Thermal Expansion for DH2F
COEFFICIENT OF THERMAL EXPANSION
MECHANICAL PROPERTIES
Spec. 20-100˚C 20-200˚C 20-300˚C 20-400˚C 20-500˚C 20-600˚C 20-700˚C
DH2F 8.9 10.8 11.9 12.6 13.1 13.7 13.9
( x 10-6/˚C )
8
7
6
5
4
3
2
1
0DH2F 37/41
HRCPX5-29/33 HRC High Hard P20
34/38 HRCV44 42/46 HRC
MACHINING CHARACTERISTICS
CHEMICAL COMPOSITION (%)
MATERIAL HARDNESS C S Si MN CR MO V AISI GRADE
DH2F 37-41 HRC .32 – .42 .12 – .15 <1.50 <1.5 4.50 – 5.50 1.00 – 1.50 .40 – 1.20 H-13= =
GENERAL CHEMISTRY
MATERIALS / MOLD LIFE
Fremax-45 4140 HT (28-32 HRC)
P20 (28-32 HRC)
PX5 (29-33 HRC)
DH2F (37-41 HRC)
NAK 55(38-42HRC)
S-7(52-54HRC)
H-13 (48-52 HRC)
DC53 (60-63 HRC)
6
5
4
3
2
1
0Sho
rtLo
ng
Mac
hina
bilit
y
DH2Flsi 10/2/06 9:57 AM Page 3
Chemical Composition
Quality Characteristics II
Quality Characteristics III
RT 100 200 300 400 500 600 700
160(1569)
120(1179)
80(785)
40(392)
0
600
400
200
90
70
50
30
10(98)
6(59)
2(19.6)
�
Test temperature (C˚)
Hard
ness
(HV)
T
ensil
e stre
ngth
and
yield
poi
nt k
gf/m
m2 (M
Pa)
Char
py im
pact
ener
gy k
gf •
m/cm
2 (J/
cm 2 )
Elon
gatio
n an
d re
ducti
on o
f are
a (%
)
Hardness
Quality Characteristics I
• Average Coefficient of Thermal Expansion for DH2F
COEFFICIENT OF THERMAL EXPANSION
MECHANICAL PROPERTIES
Spec. 20-100˚C 20-200˚C 20-300˚C 20-400˚C 20-500˚C 20-600˚C 20-700˚C
DH2F 8.9 10.8 11.9 12.6 13.1 13.7 13.9
( x 10-6/˚C )
8
7
6
5
4
3
2
1
0DH2F 37/41
HRCPX5-29/33 HRC High Hard P20
34/38 HRCV44 42/46 HRC
MACHINING CHARACTERISTICS
CHEMICAL COMPOSITION (%)
MATERIAL HARDNESS C S Si MN CR MO V AISI GRADE
DH2F 37-41 HRC .32 – .42 .12 – .15 <1.50 <1.5 4.50 – 5.50 1.00 – 1.50 .40 – 1.20 H-13= =
GENERAL CHEMISTRY
MATERIALS / MOLD LIFE
Fremax-45 4140 HT (28-32 HRC)
P20 (28-32 HRC)
PX5 (29-33 HRC)
DH2F (37-41 HRC)
NAK 55(38-42HRC)
S-7(52-54HRC)
H-13 (48-52 HRC)
DC53 (60-63 HRC)
6
5
4
3
2
1
0Sho
rtLo
ng
Mac
hina
bilit
y
DH2Flsi 10/2/06 9:57 AM Page 3
KNOCKOUT
THE COMPETITION
INTRODUCING
DH2FMODIF IED H-13PREHARDENED 37-41 HRC
FEATURES:• Prehardened to 37-41 HRC. No additional heat treating required.
Suited for complex molds and dies susceptible to deformation.• Good machinability• Reduced manufacturing time due to no additional heat treating.• DH2F has better wear resistance than H-13 at like hardness.
Quality Characteristics III cont’d
• An example of tool life offace milling cutter
• An example of tool life ofHSS drill bit
MACHINABILITY
Corporate Office: Lindquist Steels, Inc. 1050 Woodend RoadStratford, CT 06615
800-243-9637 • FAX: 203-386-0132
DH2F is distributed byLindquist Steels, Inc.,
a Daido partner company
200
100
50
30
Tool life T (min)
30 50 70100 200105
VBmax
Cut
ting
spee
d V
(m
/min
)
Cut
ting
spee
d V
(m
/min
) 200
100
30
20
Cutting length L (m/m)
50 70100 300 500 100305
• Cutting parametersTool material Tool shape Cutting fluid Feed Cut
Face milling center M20 NP-100R None 0.075mm/tooth 1.5mm 66-165 80w x 50T x 200l 40 VBmax=0.3mm
Drill bit M2 None 0.1mm/rev 30mm deep hole 20-40 80w x 50T x 200l 40 Tool erosion
Cutting speed Test piece size Hardness Tool life(m/min) (mm) (HRC) and point
10mm dia.tapered-shank drill a = 118”
• DH2F (modified (H13) Prehardened) • H-13 (40 HRC)CHIP SHAPE
www.lindquiststeels.com
Daido Steel Limited and Lindquist Steels, Inc. shall not be held responsible for damage caused by misunderstanding or improper use of the technical information con-tained in this brochure. The contents of this brochure may be subject to change without notice. Please inquire for the latest information. No portion of this brochure may be reproduced without the express permission of Daido Steel Limited and International Mold Steel, Inc.
ParametersTool
CUTTING PARAMETERS:Tool : M2, 10 mm dia., tapered-shank drill a=118˚Feed : 0.10mm/revHole depth : 30 mm
Cutting speed : 25m/minTest piece hardness : 40HRCTest piece size (mm) : 100 x 200 x 300
DAIDO STEEL
APPLICATIONS:• Plastic Molds• Zinc Diecasting Dies• Short Run Aluminum
Die Casting Dies• Plunger Tips, Sprue
Bushings• Die Plate Strippers• Dies for Aluminum
Extrusions• Pattern’s and Core Boxes• Others
Lindquist Steels, Inc. 1950 Old Dunbar Road
West Columbia, SC 29172800-845-7052 • FAX: 803-794-6658
Corporate Office: Lindquist Steels, Inc. 1050 Woodend RoadStratford, CT 06615
800-243-9637 • FAX: 203-386-0132
www.lindquiststeels.com
Lindquist Steels, Inc. 1950 Old Dunbar Road
West Columbia, SC 29172800-845-7052 • FAX: 803-794-6658
www.imsteel.com
DH2Flsi 10/2/06 9:57 AM Page 1