POLYBASE R+ S 3 in 1 prefabricated panel Advantageous thermal value* For cold applied or SBS bitumen system Flameless VOC free Quick and easy installation Increases productivity on jobsite value of panel according to specifications Monolithic panel ADVANTAGES ACKNOWLEDGMENT T. 450.477.4423 1.800.363.2307 FRANSYL.COM *The use of a 9’’ wide S/S type tape or self-adhesive underface and sanded surface tape is mandatory. Note: If used with a self-adhesive tape, Lexcor MULTIGRIP Primer is required and the panel must be covered with a cap sheet within the same day. THICKNESS OF POLYBASE R+ S Type HR (Type I) Type THR (Type II) R-11.5 3’’ 2 3/4’’ R-13.5 3 1/2’’ 3 1/4’’’ R-14.5 3 3/4’’ 3 1/2’’ R-15.5 4’’ 3 3/4’’ R-17.5 4 1/2’’ 4 1/4’’ R-19.5 5’’ 4 3/4’’ «R» Insulating Value POLYBASE R+ S 26418 The thermal value of the expanded polystyrene is 100% guaranteed 1 1/2’’ overlapping protection strip * 95 g underlayment membrane of 2.2 mm thick, consisting of a fiberglass reinforcement with a thermofusible underface and a sanded surface OR 180 g underlayment membrane of 2.2 mm thick, consisting of a polyester reinforcement with a thermofusible underface and a sanded surface double-sided 3" self-adhesive overlapping strip 1/2" (12.70 mm) composite panel, factory lamina- ted on both faces of a fireproof fibreglass sheet Fransyl Izolon Insulation Meets Novoclimat requirements

Upload: others

Post on 21-Jul-2020

5 views

Category:

Documents


0 download

TRANSCRIPT

Page 1: POLYBASE R+ S - Fransylv~Polybase_R__S_-_TDS.pdf · POLYBASE R+ S 3 in 1 prefabricated panel Advantageous thermal value* For cold applied or SBS bitumen system Flameless VOC free

POLYBASE R+ S 3 in 1 prefabricated panel

Advantageous thermal value*For cold applied or SBS bitumen systemFlamelessVOC freeQuick and easy installationIncreases productivity on jobsite

value of panel according to specificationsMonolithic panel

ADVANTAGES ACKNOWLEDGMENT

T. 450.477.4423 1.800.363.2307 FRANSYL.COM

*The use of a 9’’ wide S/S type tape or self-adhesiveunderface and sanded surface tape is mandatory.

Note: If used with a self-adhesive tape, Lexcor MULTIGRIP Primeris required and the panel must be covered with a cap sheetwithin the same day.

THICKNESS OF POLYBASE R+ SType HR (Type I) Type THR (Type II)

R-11.5 3’’ 2 3/4’’

R-13.5 3 1/2’’ 3 1/4’’’

R-14.5 3 3/4’’ 3 1/2’’

R-15.5 4’’ 3 3/4’’

R-17.5 4 1/2’’ 4 1/4’’

R-19.5 5’’ 4 3/4’’

«R» Insulating Value

POLYBASE R+ S

26418

The thermal value of the expanded polystyrene is 100% guaranteed

1 1/2’’ overlapping protection strip *

95 g underlayment membrane of 2.2 mm thick,consisting of a fiberglass reinforcement with athermofusible underface and a sanded surface OR180 g underlayment membrane of 2.2 mm thick,consisting of a polyester reinforcement with athermofusible underface and a sanded surface

double-sided 3" self-adhesive overlapping strip

1/2" (12.70 mm) composite panel, factory lamina-ted on both faces of a fireproof fibreglass sheet

Fransyl Izolon Insulation

Meets Novoclimat requirements

Page 2: POLYBASE R+ S - Fransylv~Polybase_R__S_-_TDS.pdf · POLYBASE R+ S 3 in 1 prefabricated panel Advantageous thermal value* For cold applied or SBS bitumen system Flameless VOC free

½" (12.70 MM) COMPOSITE PANEL, FACTORY LAMINATED ON BOTH FACES OF A FIRE RETARDANT FIBREGLASS SHEET

Thermal resistance R-2.5(ASTM C518 C177), (RSI-0.53)

Water vapor permeability < 1.00 perm(ASTM E96) (85 ng/Pa s m2)

Compressive strength(ASTM D 1621) 620 kPa10% deformation (90 lbs / in²)

Tensile strength > 35 kPa(ASTM D 1623) (5.07 lbs / in2)

Water absorption < 1%,(ASTM C 209, ASTM D 2842) < 3,5%

Density 2 lbs / ft3

(ASTME D 1622) (32.04 kg/m3)

Smoke developement 50-170(ASTM E84), evaluation on a 10 min. period

Flame spread 40-60(ASTM E84), evaluation on a 10 min. period

POLYBASE R+ SSPECIFICATIONSDIMENSIONS

ROOFING SYSTEMS

T. 450.477.4423 1.800.363.2307 FRANSYL.COM

Cold bending in lower temperatures (ASTM D6163) Successful, °C (°F)

Longitudinal and transversal tensile strength at breakage (ASTM D6163) Successful, kN/m (lbf/in)

Elongation at breakage Successful, N (lbf)

Longitudinal and transversal elongation at breakage (ASTM D6163) Successful %

Longitudinal and transversal tear strength (ONGC-37.56-M) Successful, N (lbf)

Longitudinal and transversal resistance to lap joint (ONGC-37.56-M), 5J @ 23°C Successful, kN/m (lbf/in)

Width x length: 36’’ x 96’’ (914 mm x 2438 mm)

Thickness of shiplap edge*: 2’’ to 4 1/2’’ (51 mm to 114 mm)

Shiplap: 5/8’’ (16 mm)*1Dimensions may vary ± 2% *2Other dimensions available upon request

95 G MEMBRANE OF 2.2 MM THICK, CONSISTING OFA FIBERGLASS REINFORCEMENT WITH A THERMOFUSIBLEUNDERFACE AND SANDED SURFACE, INCLUDING ADOUBLE-SIDED 3’’ SELF-ADHESIVE OVERLAPPING STRIP

180 G MEMBRANE OF 2.2 MM THICK, CONSISTING OFA POLYESTER REINFORCEMENT WITH A THERMOFUSIBLEUNDERFACE AND SANDED SURFACE, INCLUDING ADOUBLE-SIDED 3’’ SELF-ADHESIVE OVERLAPPING STRIP

OR

Installation:

Option 1: Mechanical fastening

Option 2: Adhesive application(Contact your sales rep. for all details)

for 1/2’’ (12.70 mm) thickness

Polybase R+ S Panel with Cap Sheet :UL Class C Fully Adhered (ref. TGFUC.R16778)CAN/ULC-S107

POLYBASE R+ SHR

(Type I)

Thermal resistance R-3.7(ASTM C518 C177) (RSI-0.65)1’’ (25 mm) thickness

Water vapour permability 5.25 perm(ASTM E96), 1’’ (25 mm) thickness (300 ng/Pa·s·m²)

Compressive strength 80 kPa(ASTM D1621) (11.64 lbs/in²)1 ½ ’’ (38 mm) thickness

Flexural strength 170 kPa(ASTM C 203) (24.78 lbs/in²)1 ½ ’’ (38 mm) thickness

Water absorption (ASTM D 2842) 6%1 ½ ’’ (38 mm) thickness

Density 1 lb/ft³(ASTM D 1621) (16.01 kg/m³)

Limiting Oxygen Index 24%(ULC S-701) % minimum

1.5%Dimensional stability (ASTM D 2126)% maximum linear change

THR(Type II)

R-4(RSI-0.7)

3.5 perm(200 ng/Pa·s·m²)

120 kPa(17.46 lbs/in²)

240 kPa(34.97 lbs/in²)

4%

1.25 lb/ft³(20.01 kg/m³)

24%

1.5%

HD(Type II)

R-4,17(RSI-0.73)

2.25 perm(130 ng/Pa·s·m²)

160 kPa(23.3 lbs/in²)

300 kPa(43.71 lbs/in²)

3%

1.5 lb/ft³(24.02 kg/m³)

24%

1.5%

THD(Type III)

R-4,2(RSI-0.74)

2.25 perm(130 ng/Pa·s·m²)

210 kPa(30.6 lbs/in²)

300 kPa(43.71 lbs/in²)

2%

2 lb/ft³(32.03 kg/m³)

24%

1.5%

Important note: It is possible that blisters are formed in the membrane when the temperature increases; this has no impact on the performance and adhesion of the membrane on the panel. Blisters under the mem-brane will fade upon cooling of the panel.