CH5 SOLID CH5 SOLID GROUND CURINGGROUND CURING

SGC systems were developed by Cubital Ltd. Cubital was found in 1987 as an internal R&D unit at Seitex Corporation Ltd, and first SGC system was installed in 1991

the CSG machine analyzes a CAD file and renders the object as a stack of "slices". The image of the working slice is "printed" on a glass photo-mask using an electro-static process similar to laser printing. That part of the "slice" representing solid material remains transparent.

PROCESSPROCESSStep 1Step 1After using Cubital's Data Front End (DFE) software to After using Cubital's Data Front End (DFE) software to

preprocess and slice the 3D CAD model into individual preprocess and slice the 3D CAD model into individual layers, an image of each layer is produced on an layers, an image of each layer is produced on an electrostatically charged erasable glass plate using electrostatically charged erasable glass plate using Cubital's proprietary ionographic printing techniques. Cubital's proprietary ionographic printing techniques. The image, serving as a photo-mask, is positioned over The image, serving as a photo-mask, is positioned over a thin layer (typically 0.004-0.008 in. thick) of liquid a thin layer (typically 0.004-0.008 in. thick) of liquid photopolymer (resin). The resin is then selectively photopolymer (resin). The resin is then selectively solidified by a powerful UV light through the mask, solidified by a powerful UV light through the mask, creating that layer of the model. creating that layer of the model.

Step 2Step 2After the layer is cured, all unsolidified resin is collected After the layer is cured, all unsolidified resin is collected

for recycling, leaving the hardened areas intact. The for recycling, leaving the hardened areas intact. The cured layer is passed beneath a strong linear UV lamp cured layer is passed beneath a strong linear UV lamp to cure the layer to final strength. to cure the layer to final strength.

PROCESSPROCESS

Step 3Step 3Melted wax is then spread into the newly created cavities. Melted wax is then spread into the newly created cavities.

The wax is cooled and hardened to provide continuous, The wax is cooled and hardened to provide continuous, solid support for the model as it is fabricated. solid support for the model as it is fabricated.

Step 4Step 4The layer is then milled to a smooth, accurate, even The layer is then milled to a smooth, accurate, even

surface. surface. Step 5Step 5A new layer of photopolymer is spread on the milled A new layer of photopolymer is spread on the milled

surface, a new mask is generated on the cleaned glass surface, a new mask is generated on the cleaned glass plate, and the process is repeated until the build is plate, and the process is repeated until the build is complete. After the build is finished, the wax is complete. After the build is finished, the wax is removed, and the parts are ready for use or additional removed, and the parts are ready for use or additional post- processing, if necessary. post- processing, if necessary.

PROCESS PARAMETERSPROCESS PARAMETERS

SGC 4600SGC 4600 SGC 5600SGC 5600

Working volume Working volume mmmm

350 x 350 x 350350 x 350 x 350 500 x 350 x 500500 x 350 x 500

Surface Surface definition mmdefinition mm

0.150.15 0.150.15

X-Y resolution X-Y resolution mmmm

0.0840.084 0.0840.084

Layer thickness Layer thickness mmmm

0.150.15 0.1-0.20.1-0.2

PROCESS PARAMETERSPROCESS PARAMETERS

Min feature size Min feature size mmmm

0.40.4 0.40.4

Net production Net production raterate

164 cm164 cm33/hour/hour 426 cm426 cm33/hour/hour

Layer build Layer build speedspeed

120 s/layer120 s/layer 70 s/layer70 s/layer

Control systemControl system Unix based Unix based workstationworkstation

Unix based Unix based workstationworkstation

PricePrice $ 275,000$ 275,000 $ 470,000$ 470,000

ADVANTAGESADVANTAGES Multiple parts can be positioned within the Multiple parts can be positioned within the

entire working envelop resulting high entire working envelop resulting high throughput throughput

No support structure is required as the wax No support structure is required as the wax support the structure in all directions support the structure in all directions

Each layer is fully cured resulting that the Each layer is fully cured resulting that the dimension is very stable with no shrinkage dimension is very stable with no shrinkage effect after the process and requires no post-effect after the process and requires no post-curing process curing process

Capable to build even the most complicated Capable to build even the most complicated parts without much difficulty parts without much difficulty

Build session can be interrupted and erroneous Build session can be interrupted and erroneous layer can be erased layer can be erased

DISADVANTAGESDISADVANTAGES

The process is rather complicate which The process is rather complicate which required skilled people to look after and required skilled people to look after and unattended operation is not possible unattended operation is not possible

The resin consumption is disregard of the The resin consumption is disregard of the size of the cross section of the parts but size of the cross section of the parts but only depended on the number of layers only depended on the number of layers resulting that it is too expensive for parts resulting that it is too expensive for parts with small cross sectional area with small cross sectional area

High equipment cost (over US$500,000) High equipment cost (over US$500,000) made it not easily to be justified made it not easily to be justified

APPLICATIONSAPPLICATIONS

fabricating wax patterns for fabricating wax patterns for investment casting investment casting

The machines are quite big and can The machines are quite big and can produce large models. produce large models.

CastingCasting ToolingTooling MedicalMedical