s.pioneertestinglaboratory.com/certificate_file/facilties available... · is-4985:2000 page 6 of 30...

S.

NO

.

Name of

Material

Tests to be Conducted Test Method Quantity

of Sample

Required

No. of days

required

for testing

8) Aggregate Impact Value IS 2386(Pt-IV) 9) Aggregate Crushing Value IS 2386(Pt-IV) 10) Los Angeles Aggregate Abrasion Value IS 2386(Pt-IV) 11) 10 % Fine Value IS 2386(Pt-IV) 12) Organic Impurities IS 2386(Pt-II)

13) Petrography examination IS-2386(Pt-8) 5 kg 5-7

Chemical test 5-7

1) Alkali Aggregate Reactivity IS 2386(Pt-VII) 50gm

2) Chloride Content BS 812(Pt-117) 50gm

3) Sulphate Content BS 812(Pt-118) 50gm

(b) Fine Aggregate /

Sand 6 parameters 15 kg 10

Physical tests

1)Sieve Analysis IS 2386(Pt-I)

2) Soundness IS 2386(Pt-V)

3) Deleterious Material IS 2386(Pt-I&II)

4) Specific Gravity IS 2386(Pt-III)

5) Water Absorption IS 2386(Pt-III)

6) Bulk Density IS 2386(Pt-III)

7) Silt Content (By Volume) CPWD Spec.

8) Silt Content (By Wt.) IS-2386(Pt-11)

9) Bulking of Sand IS 2386(Pt-III)

10) Moisture Content IS 2386(Pt-III)

11) Organic Impurities IS 2386(Pt-II)

12) Sand Equivalent IS 2720(Pt-37) 1 kg 10

Chemical test

1) Chloride Content BS 812(Pt-117) 50gm

2) Sulphate Content BS 812(Pt-118) 50gm

4. Aluminium

Section Chemical + Physical Test Full section 5-7

(A) Chemical Composition:

1. Aluminium, % IS-733:1983

2. Copper, % IS- 504(Pt-3)

3. Magnesium, % IS- 504(Pt-6)

4. Silicon, % IS- 504(Pt-1)

5. Iron, % IS- 504(Pt-2)

6. Manganese, % IS- 504(Pt-5)

7. Zinc, % IS- 504(Pt-4)

8. Titanium IS- 504(Pt-3)

9. Chromium, % IS- 504(Pt-8)

10. Thickness of Powder Coating,

micron

IS 101(Pt-3/ Sec.-

2)

11. Dimension, mm IS 3965:1981

(B) Mechanical Composition: 1 mtr 5-7

1. Yield/0.2% Proof Stress IS 1608:2005

2. Tensile Strength, N/mm2 IS 1608:2005

3. Elongation, % IS 1608:2005

of 30

S.

NO.

Name of

Material


of Sample

Required

No. of days

required

for testing

5. APP Membrane

(As Per ASTM)

Complete test As per ASTM 1 mtr x 2

pcs.

10-12

Membrane Thickness ASTM D-751

Reinforcement --

Softening Point ASTM D-36

Penetration ASTM D-5

Tensile Strength ASTM D-146 Elongation at Break ASTM D-146

Tear Resistance ASTM D-4073

Lap Joint Strength ASTM D-3164M

Water Vapor Permeability ASTM E-96

Water Absorption

Short term

Long term

ASTM D-570

Creeping of Membrane UE ATC

Flexibility at Low Temp ASTM D-5147

Impermeability of the

Membrane to Water

UE ATC

Resistance to Thermal ageing UE ATC

Resistance to UV Ageing ASTM G-154

6. Alumnium Alloys Salt Spray Test ASTM B-117-

2011

2 Specimen

7. Brick (Clay Brick/

Fly ash Lime

brick/ Fly ash

brick)

Complete 20pcs. 15 days

1) Dimension IS-1077:1992

2)Compressive Strength IS-3495:1992

3)Efflorescence IS-3495:1992

4)Water Absorption test IS-3495:1992

8. Block Board

Complete IS-1659:2004 Full width 8-10

Dimensions IS 1659:2004

Dimensional Changes Caused by Humidity

A) At 40 ± 5% Relative Humidity

B) At 90 % ± 5% Relative Humidity

IS 1659:2004

Resistance to Water IS 1659:2004

Adhesion of Plies IS 1659:2004

Mycological Test IS 1659:2004

Modulus of Rupture & Modulus of Elasticity

IS 1659:2004

Spot Test IS 1659:2004

9. Bitumen Complete 2 kg 5-7

1. Penetration at 25˚c IS-1203:1978

2. Softening Point IS-1205:1978

3. Flash Point IS-1209:1978

4. Solubility in Trichloroethylene IS-1216:1978

5. Absolute viscosity at 60˚C Poises IS- 1206:1978

6. Ductility at 25˚C IS- 1208:1978

7. Kinematic Viscosity IS- 1206:1978

of 30

S.

NO.

Name of

Material


of Sample

Required

No. of days

required

for testing

10. Bitumen

Emulsion Complete 2 ltr 5-7

1. Residue on 600µ Sieve, % IS- 8887:2004

2. Coagulation of Emulsion

at low temperature

IS- 8887:2004

3. Viscosity by Saybolt Furol

viscometer

IS- 3117

4. Miscibility with Water IS- 8887:2004

5. Storage Stability after 24 hrs, % IS- 8887:2004

6. Tests on Residue

a) Residue by Evaporation, %

b) Penetration at 25ºC/100 gm

c) Ductility, 27ºC/cm

d) Solubility in trichlora- ethylene %

by mass

IS- 8887:2004

IS- 1203:1978

IS- 1208:1978

IS- 1216:1978

11. Bentonite Complete 5 kg 5-7

Liquid limit IS-2720:1985

pH Value IS-2720:1987

Marsh Cone Viscosity IS-6186:1986

Sand Content IS-6186:1986

Swelling Index IS-2720:1977

Density --

Moisture Content IS-6186:1986

Gel formation Index IS-6186:1986

12. Bitumen

CRMB/ PMB

Complete 5 kg 5-7

1. Penetration at 25˚c IS-1203:1978

2. Softening Point IS-1205:1978

3. Flash Point IS-1209:1978

4. Elastic Recovery of half thread in

Ductilometer at 150C

IS-15462:2004

5. Viscosity at 1500 poise IS-1206:1978

Thin film oven test

1. Loss in Mass, % IS-9382:1979

2. Increase in Softening Point, 0C IS-1205:1978

3. Reduction in Penetration

Of residue at 250C, %

IS-1203:1978

4. Elastic Recovery of Half thread in

ductilometer at 250C, %

IS-15462:2004

of 30

S.

NO.

Name of Material Tests to be Conducted Test Method Quantity

of Sample

Required

No. of days

required

for testing

13. Barbed Wire Complete Test 5 mtrs. 5-7 days

(A) Mechanical Test

Dia of line wire, mm IS-278:2009

Diameter of point wire, mm IS-278:2009

Mass, g/m IS-278:2009

Distance between Two Barbs, mm IS-278:2009

No. of lays between two consecutive

barbs

IS-278:2009

Tensile Strength of line wire IS-1608:2005

Breaking load of completed wire IS-278:2009

Freedom from Defect IS-278:2009

Wrapping Test IS-1755:1983

(B) Chemical Test

Carbon, % IS-228(Pt-1) :1987

Manganese, % IS-228(Pt-2) :1987

Phosphorus, % IS-228(Pt-3) :1987

Sulphur, % IS-228(Pt-9) :1989

Mass of Zinc Coating(Line wire),

g/m2

IS-6745:1972

Mass of Zinc Coating (point wire),

g/m2

IS-6745:1972

Chromate Conversion Coating IS-1340:1977

14. Curing Compound Complete 1 ltr 7-8

Type ASTM C-309-03

Colour Visual

Specific gravity (by Hydrometer) --

Drying time ASTM C-309-03

Water retention properties Loss

of water (72 hours)

ASTM C-156

Curing Efficiency BS-75

15. Cement Mortar Ratio test IS-1199:1959 5 kg 5-7

16. Concrete Beam Flexural Strength IS-516:1959 3 nos 7-10

17. Concrete Cylinder Split Tensile Strength IS-5816:1999 3 nos 7-10

18. Concrete Cylinder RCPT Test ACTM C-1202 3 nos 7-10

19. Concrete Cube Drying Shrinkage BS-1881:1970 3 nos 35-38

20. Concrete Cube Moisture Movement BS-1881:1970 3 nos 35-38

21. Concrete Cylinder Water Permeability test DIN-1048:1991 3 nos 7-10

22. Concrete Cube &

Micro Con. Cube

Comp. Strength IS- 516:1959 3 nos 5-7

23. Concrete Cube Comp. strength by ACT Method IS-9013 3 nos 5-7

24. Chloropyriphos Chloropyriphos, % IS 8963:2006 500gm 5-7

25. C.C. Pavement

Slab

Water Absorption 3 nos. 7-10

Compressive strength 3 nos

26. Copper Brass

(IS-3685)

Purity test IS-191:2007 100 gm 5-7

1. Copper + Silver, %

2. Bismuth, %

3. Lead, %

4. Total Impurities, %

5. Resistivity Test, (Ω, m)

6. Conductivity Test

of 30

S.

NO.

Name of Material Tests to be Conducted Test Method Quantity of

Sample

Required

No. of days

required

for testing

27. Cement

(OPC/PPC/ 43 Gr/ 53

Gr)

Chemical 500 gm 5-7

1) Ratio of % Age of lime to

% Age of SiO2, Al2O3 &

Fe2O3

IS-4032:1985

2) Ratio of % Age of Alumina

to that of Iron Oxide

IS-4032:1985

3) Insoluble Residue, % by

mass

IS-4032:1985

4) Magnesia (as Mgo), % by

mass

IS-4032:1985

5) Total Sulphur Content IS-4032:1985

6) Loss on Ignition IS-4032:1985

7) Total Chloride IS-4032:1985

8) Alkalies Content

a) Alkali Content (asNa2O)

b) Alkali Content (as K2O)

IS-4032:1985

Physical 15 kg 8-9 (except

28 days

compressiv

e

strength

test)

28-30 (incl.

28 days

comp.

strength

test)

1) Fineness IS-4031:1999

2) Soundness

a) Le-Chatellier Expansion

b) Autoclave Expansion

IS-4031:1988

3) Setting Time

(a) Initial

(b) Final

IS-4031:1988

4) Compressive Strength

(a) 72±1 hour

(b) 168±2 hour

(c)672±4 hour

IS-4031:1988

5) Consistency IS-4031:1988

Chemical + Physical Test 15 kg 28-30

28 CPVC Pipe

As per IS 15778

Complete 1 mtr.x 6pc. 15

1. Dimensions of Pipe, mm IS-12235

2. Pipe Ends IS-15778

3. Visual Appearance IS-15778

4. Opacity, % IS-12235

5. Reversion Test, % IS-12235

6. Vicat Softening Tem. IS-12235

7. Density, kg/m3 IS-12235

8. Mechanical Properties

a) Resistance to External

b) Flattening Test

c) Tensile Strength

d) Resistance to external

blows at 0°C

IS-15778

IS-12235

--

IS-4985:2000

of 30

S.

NO.

Name of Material Tests to be Conducted Test Method Quantity of

Sample

Required

No. of days

required

for testing

29. Cast Iron Pipe

As per IS 210

(A) Chemical Test 1 Pc. 5-7

1. Carbon, % IS-12308

2. Manganese, % IS-12308

3. Phosphorus, % IS-12308

4. Silicon, % IS-12308

5. Sulphur, % IS-12308

(B) Mechanical Test Full length 5-7

1. External Diameter, mm IS-8329:2000

2. Wall Thickness, mm IS-8329:2000

3. Tensile Strength,

N/mm2

IS-1608:2005

4. Elongation, % IS-1608:2005

Chemical + Physical

Test

Full length 5-7

30. Concrete mix (Design mix) Complete Test As per IS 10262

& 456

Coarse

Aggregate

20mm &

10mm- 50 kg

(each)

Fine

Aggregate- 50

kg

Cement- 1 Bag

Admixture- 1

Liter

Water – 1 Liter

28-30

31. Coal Moisture Content IS-1350 1 kg 7-10

Volatile matter

Ash Content

Fixed Carbon

Sulphur content

32. Concrete Structure Rebound Hammer

IS-13311(Pt-2)

- 5-7

33. Core (Bituminous) Core Cutting 1 Core 4-5

34. Core Cutting + Testing

(Concrete)

Core Cutting + Testing 1 Core 4-5

35. Coupler Slip test IS-16172:2014 2 Pcs. 5-7

Tensile strength IS-1608:2005

Chemical composition IS-228

36. Concrete Slab Rebar Location -- - 5-7

of 30

S.

NO.


of Sample

Required

No. of days

required

for testing

37. CRC /HRC sheet

As per IS 513/ IS 1079

Complete Test 400mm x

400mm x1

Pc.

5-7

Dimension

Tensile Strength IS-1608:2005

Yield Stress IS-1608:2005

Elongation IS-1608:2005

Hardness IS 1586

Bend test IS 1599

Plastic Strain Ratio _r_ IS 11999

Tensile Strain hardening_n IS 15756

Freedom from defects IS 513

Surface roughness IS 513

Cupping Test IS 10175(Pt-1)

38. Conduit Pipe

(IS-9537(Pt-1):1980 IS-9537(Pt-3):1983)

Marking -- 1 mtr. x 6

Pcs.

7-10

Dimensions

(a) Max. Outside diameter

(b) Min. Outside diameter

(c) Min. Inside diameter

(d) Length of Conduit, m

(e) Uniformity of Wall Thickness

(f) Dimension of socket end

IS 9537(Pt-3):1983

Construction Visually

Mechanical Properties

(a) Bending Test

(b) (b) Compression Test

IS 9537(Pt-3):1983

&

IS 9537(Pt-1):1980

Resistance to Heat IS 9537(Pt-3):1983

Resistance to Burning IS 9537(Pt-1):1980

Electrical Characteristics IS 9537(Pt-1):1980

39. Casing Pipe

(IS-12818:2010)

Colour -- 6 mtrs. 12-15

Visual Appearance --

Dimension

a) Screen Pipes

b) Ribs

c) Length of Pipe

d) Slots Dimension

IS 12818-2010 &

IS 12235(Pt-1)2004

Threading of Pipes --

EPDM Sealing Ring --

Internal Diameter IS 12818:2010

Density IS 12235(Pt-

14):2004

Resistance to External Blows at

00C

IS 12235(Pt-9):2004

Tensile Strength IS 12235(Pt-

13):2004

Vicat softening temperature IS 12235(Pt-2):204

Effect on water

IS 12235(Pt-4 &

10):2004 & IS

4985:2000

of 30

S.

NO.


of Sample

Required

No. of days

required

for testing

40. Ceramic Glazed

Wall & Floor Tile

(IS-15622:2006)

(A) Physical Properties

Water Absorption,

IS 13630 (P-2): 2006 20 nos. 8-10

Modulus of rupture IS 13630 (P-6): 2006

Scratch hardness of Surface IS 13630 (P-13): 2006

Thermal shock resistance IS 13630 (P-5): 2006

Crazing Resistance IS 13630 (P-9): 2006

Dimension

(a) Length

(b) Width

IS 13630 (P-1): 2006

Surface Quality IS 13630 (P-1): 2006

Straightness of sides IS 13630 (P-1): 2006

Rectangularity IS 13630 (P-1): 2006

(B) Chemical Properties

Resistance to staining

IS 13630 (P-8): 2006

Resistance to household IS 13630 (P-8): 2006

41. DBC/ DBM/ BC/

SDBC/ BM Complete 20 kg 7-10

1. Gradation, % IS-2386:1963

2. Bitumen/ Binder Content, % CPWD Spec.

3. Stripping Value, %

(Retained coating)

IS-6241:1971

4. Density, gm/cc MORTH Spec.

5. Combined Flakiness &

Elongation, %

IS-2386:1963

6. Loss Angles Abrasion Value,

%

IS-2386:1963

7. Impact Value, % IS-2386:1963

8. Water Absorption, % IS-2386:1963

9. Deleterious Material MORTH Spec.

42. Decorative

Laminates Sheet

(as per IS

2046:1995)

1. Thickness, mm IS-2046:1995 1mtr. x 1

mtr. x 2

pcs.

10-12

2. Resistance to Surface Wear IS-2046:1995

3. Resistance to immersion IS-2046:1995

4. Resistance to Dry Heat at 1800C IS-2046:1995

5. Dimensional Stability

At deviated temp

(i) Longitudinal direction

(ii) Cross-Longitudinal direction

IS-2046:1995

6. Resistance to Impact IS-2046:1995 7. Resistance to Cracking IS-2046:1995 8. Resistance to Scratching, N IS-2046:1995 9. Resistance to Staining IS-2046:1995 10. Resistance to Steam IS-2046:1995

11. Resistance to Cigarette Burns IS-2046:1995

of 30

S.

NO.


of Sample

Required

No. of days

required

for testing

43. Diesel Complete 2 ltr. 7-10

Kinematic viscosity IS-1448:1976

Flash point IS-1448:1998

Sediment

Bacteria, Fungi, Mold

Sulphur IS-1448:1979

Distillation

Cold filter plug point Karl

Fischer

Visual Appearance

44. Decorative Plywood

(IS-1328:1996)

Type-1 (Cl. 7.1)

Open Splits, Checks or

Open joints (Cl. 7.1.1)

Visually Full width 8-10

Type-2 (Cl. 7.2)

Open Splits, Checks or

Open joints, tight knots

And Patches and Pin knots

Visually

Dimension, mm

(Cl. 8.0)

Length

Width

Thickness

Squareness

Edge Straightness

IS 1328:1996

Finish Visually

Moisture Content IS 1734(Pt-1):1983

Resistance to water IS 1328:1996

Mycological test IS 1734(Pt-7):1983 21-22

Static Bending Strength IS 1734(Pt-11):1983

45. Expended

Polystyrene

(IS-4671)

Complete (Water vapour per

meance) 2 mtr. 8-10

Bulk Density, kg/m3 IS-5688:1982

Dimension, mm IS-4671:1984

Compressive Strength (at 10%

deformation), kg/cm2

IS-4671:1984

Cross Breaking Strength, Kg/cm2 IS-4671:1984

Water Vapour Per Meance, gm/m2 IS-4671:1984

Thermal Stability, % IS-4671:1984

Moisture Absorption, % IS-4671:1984

Flammability IS-4671:1984

46. Elastomeric

Bearing

Identification of polymer 1 Pc. (200

gm)

7-10

Polymer Content

Ash content

Hardness test

of 30

S.

NO.

Name of Material Tests to be

Conducted

Quantity

of Sample

Required

No. of days

required

for testing

47. Electric Wire/Cable, PVC insulated (Single Core)

(Complete test except FRLS test)

As Per IS-694:2010 / IS 1554 / IS 7098

Annealing Test 15 mtr. 20-25

Tensile Test for

Aluminium

Wrapping Test for

Aluminium

Conductor Resistance

Test

Test for over all

Dimension and

thickness

Tensile strength Elongation test

Ageing in Air oven

After Ageing Tensile

Strength

Elongation test

Shrinkage test

Hot Deformation test

Loss of Mass in Air Oven

Heat Shock test

Insulation Resistance

test

Water Immersion AC

test

Water Immersion DC

test

AC High Voltage at

room temp.

Flammability test

Cold Bend test

Cold Impact test

Insulation Resistance

test

Thermal Stability test

FRLS tests (Per core) Oxygen Index test 10 mtr. 10 days

Flame Retardance test

Temperature Index

Smoke density test

Halogen acid test

For additional each core 25% extra

of 30

S. NO.

Name of Material Tests to be Conducted Test Method Quantity of Sample Required

No. of days required for testing

48. Flush Door Shutters (as per IS 2202)

1. Construction IS-2202:1999 Full shutter 3 pcs. 20 to 25

2. Workmanship and Finish Visual days

3. No. of Defect for Type of Face Panel IS-303:1989

4. Dimension and Squareness Test IS-4020:1998

5. General Flatness Test IS-4020:1998

6. Local Plane ness Test IS-4020:1998

7. Impact Indentation Test IS-4020:1998

8. Flexure Test IS-4020:1998

9. Edge Loading Test IS-4020:1998

10. Shock Resistance IS-4020:1998

11. Buckling Test IS-4020:1998

12. Slamming Test IS-4020:1998

13. Misuse Test IS-4020:1998

14. Varying Humidity Test IS-4020:1998

15. Screw Withdrawal Resistance Test IS-4020:1998

15. End Immersion Test IS-4020:1998

16. Knife Test IS-4020:1998

17. Glue Adhesion Test IS-4020:1998

Acceptance test 1. End Immersion Test IS-4020:1998 1 Pc 20-25

2. Knife Test IS-4020:1998

3. Glue Adhesion Test IS-4020:1998

49. FRP/ GRP Door Shutter

1. Dimension and Squareness Test IS-4020:1998 Full 1 pc.Laminated sheet ½ mtr.

20-25

2. General Flatness Test IS-4020:1998

3. Local Planeness Test IS-4020:1998

4. Impact Indentation Test IS-4020:1998

5. Edge Loading Test IS-4020:1998

6. Shock Resistance IS-4020:1998

7. Buckling Test IS-4020:1998

8. Slamming Test IS-4020:1998

9. Misuse Test IS-4020:1998

10. Fiber Glass Content IS-14856:2000

11. Tensile Strength, N/mm2 IS-14856:2000

12. Bending Strength, N/mm2 IS-14856:2000

13. Water Absorption, % IS-14856:2000

14. Fire Retardancy IS-14856:2000

50. Fiber Glass wool 1. Density, kg/m3 IS-3144:1992 1 mtr. x 1mtr. x 2

pcs. 10-12

2. Thickness, mm IS-3144:1992

3. Recovery after, Compression, % IS-3144:1992

4. Shot Content, % loss in wt.% a) 500 micron b) 250 micron

IS-3144:1992

5. Moisture Content, % IS-3144:1992

6. Moisture Absorption, % IS-3144:1992

7. Alkalinity (PH) IS-3144:1992

8. Heat Resistance test/Internal self heating

--

9. Sulphur, % IS-3144:1992

10. Chloride, % IS-3144:1992

of 30

S. NO.



51. Fly Ash 1. Silicon Dioxide Plus Aluminum Oxide Plus Iron Oxide, %

IS-1727:1967

2 kg 7 to 10

2. Silicon Oxide (as SiO2), % IS-1727:1967

3. Reactive Silica, % IS-3812:2013

4. Magnesium Oxide (as MgO) IS-1727:1967

5. Total Sulphur Content IS-1727:1967

6. Available Alkalis (as Na2O), % IS-3812:2013

7. Total Chloride, % IS-4032:1985

8. Loss on Ignition, % IS-1727:1967

Physical 4kg 28 to 35

1) Sieve Analysis IS-1727:1967

2)Fineness IS-1727:1967

3) Lime Reactivity IS-1727:1967

4) Compressive Strength IS-1727:1967

5) Soundness IS-1727:1967

S. NO.

Name of Material

Tests to be Conducted Test Method Quantity of Sample Required


52. G.I. Pipe Complete (Mechanical) 1mtr.X 2pcs. 5-7

1. Dimension (a) Outside dia (b) Wall Thickness

IS-1239:2004

2. Mass, kg/mtr (Plain end) --

3. Tensile Strength IS-1608:2005


5. Flattening Test IS-2328:2005

6. Bend Test IS-2329:2005

(B) Chemical Composition 1. Carbon, % 2. Manganese, % 3. Phosphorous, % 4. Sulphur %

IS-228

1 Pc. 5-7

5. Mass of Zinc Coating IS-6745:1972

6. Uniformity of Zinc Coating IS-233

7. Adhesion Test IS-2629

54. Glass beads Sieve BS-6088:1981 1 kg 5-7

Free Flow Test MORTH Spec.

Roundness BS-6088:1981

55. Granite Stone Complete 1foot/1foot x 6pcs. (thickness 50mm)

7-10

Comp. Strength (Kg/cm2) IS-1121:1974

Water Absorption (%) IS-1124:1974

Specific Gravity IS-1124:1974

Hardness (Mohs’ Scale) IS-13630(Pt-13)

Dry Density, (M/v) IS-13030:1991

Porosity IS-1124:1974

Tensile Strength IS-1121:1974

Shear Strength IS-1121:1974

Ultrasonic Pulse Velocity IS-13311:1992

Resistance to wear IS-1706:1972

Acceptance test Comp. Strength IS-1121:1974 7-10

Specific Gravity IS-1124:1974

Hardness (Mohs’ Scale) IS-13630(Pt-13)

56. Gunmetal Chemical Test 1 Pc. 5 to 7

1. Tin, IS-4027:1987

2. Zinc, IS-4027:1987

3. Lead, % IS-4027:1987

4. Nickel, % IS-4027:1987

5. Aluminium, % IS-4027:1991

6. Silicon IS-4027:2000

7. Antimony, IS-4027:1990

8. Iron, IS-4027:1991

9. Total Impurities, % IS-318:1981

10. Copper, % IS-4027:1987

Mechanical Test 1 mtr. x 2 Pcs. 5 to 7

1) Yield Stress IS-1608:2005

2) Tensile Strength IS-1608:2005

3) Elongation IS-1608:2005

of 30

S. NO.



57. Granite Stone (IS-14223(Pt-I)

:1995)

Comp. Strength IS 1121(Pt.-

I):1974

Water Absorption IS 1124:1974 Specific Gravity IS 1122:1974 Hardness IS 13630(Pt.-

13):2006

Dry Density IS 13030:1991 Porosity IS 1124:1974 Tensile Strength IS 1121(Pt-3):1974 Shear Strength IS 1121(Pt-4):1974 Ultrasonic Pulse Velocity IS 13311(Pt-

1):1992

Resistance to wear IS 1706:1972

58. GSB (MORTH Spec.)

Gradation IS 2386(Pt-1):1963 California Bearing Ratio (CBR) IS 2720(P-16):1987 Water Absorption IS 2386(P-3):1963 Maximum Dry Density (MDD) IS 2720(P-8):1983 Optimum Moisture Content (OMC) IS 2720(P-8):1983 Atterberg Limit a) Liquid Limit b) Plastic Limit c) Plasticity Index

IS 2720(Pt-5):1985

10% Fine Value BS 812(Pt-3) Deleterious Constituents MORTH Spec.

59. Gypsum Powder (Plaster of Paris)

(A) Chemical Analysis Loss on Ignition (as LOI) IS-2547:1978

Free Lime (as Ca (OH)2) IS-2547:1978

Sulphur Trioxide (as SO3) IS-1288:1982

Calcium Oxide (as CaO) IS-1288:1982

Soluble Magnisium Salts (as MgO) IS-2547:1978

Soluble Sodium Salts (as Na2O) IS-2547:1978

(B) Physical Analysis Setting Time

a) Neat Plaster

IS-2547:1978

Transverse Strength IS-2547:1978

Soundness IS-2547:1978 Residue on 150micron Sieve IS-2547:1978 Consistency IS-2547:1978

Complete Test 1 bag 7-10

60. HDPE Sheathing Duct Pipe (as per IRC 18:2000)

Density IS-7328:1992 1.2 mtr x 3pcs.

10

Tensile strength ASTM D-638

Carbon black content IS-2530:1963

Workability test IRC-18:2000

Transverse load test IRC-18:2000

Tension load test IRC-18:2000

Water loss test IRC-18:2000

Wall thickness --

61. Hardening Compound

Compressive strength 30 days

Resistance to wear

of 30

S. NO.



62. HDPE Film (as per IS 2508)

Complete 3 mtr. x 1 Pc. 7-10

1. Appearance Visual

2. Odour --

3. Thickness IS-2508:1984

4. Density IS-2508:1984

5. Melt Flow Index IS-2530:1963

6. Carbon Black Content IS-2530:1963

7. Carbon Black Dispersion IS-2530:1963

8. Tensile Strength at break (a) Length Wise Direction (b) Cross Wise Direction

IS-2508:1984

9. Elongation at break, % (a) Length Wise Direction (b) Cross Wise Direction

IS-2508:1984

63 H. T. Strand (as per IS 14268)

Complete

IS-14268:1995

1.2 mtr. x 2 Pcs. 5-7

1. Dia, mm 2. Area, mm

2

IS-14268:1995

3. Mass, kg/km IS-14268:1995


5. Breaking Load, KN IS-1608:2005 6. 0.2 % Proof Load, KN IS-1608:2005

7. Workmanship and Finish IS-14268:1995

8. Length of Lay IS-14268:1995

9. Modulus of Elasticity, IS-14268:1995

10. Difference in dia of Central Course and Surrounding Wire

IS-14268:1995

(B) Chemical Test 1. Phosphorus, % 2. Sulphur, %

IS-228

1 Pc.

64. HDPE Pipe (upto 315mm outer dia) (as per IS 4984)

Complete 1 mtr. x 5 pcs. 15-16

1) Colour --

2) Visual Appearance IS-4984:1995


4) Hydraulic Characteristics (Acceptance Test)

IS-4984:1995

Type Test IS-4984:1995

5) Reversion Test IS-4984:1995

6) Density IS-7328:1992

7) Melt Flow rate IS-2530:1963

8) Carbon Black Content IS-2530:1963

9) Carbon Black Dispersion IS-2530:1963

of 30

S. NO.



65. HDPE Pipe (IS-14333:1996)

Colour 1 Mtr X 6 Pcs

10 Days

Visual Appearance IS 14333:1996

Dimension a) Outer diameter b) Ovality c) Wall thickness

IS 14333:1996

Hydraulic Characteristics Internal Pressure creep Rupture test at 80

0C (Cl. 8.0)

(a) Type Test (for 165 Hours) (b) Acceptance Test (for 48 Hours)

IS 14333:1996

Reversion Test IS 14333:1996

Density IS 7328:1992

Melt Flow rate IS 2530:1963

Carbon Black Content IS 2530:1963

Carbon Black Dispersion IS 2530:1963

66. HDPE Sheet (IS-10889:2004)

Appearance Visual 1 Mtr

3-4 Days

Film form Visual

Odour --

Density 230C IS 13360(Pt-3/Sec.1)

:1995

Melt Flow Rate IS 13360(Pt-4/Sec.1) :1995

Carbon Black Content IS 2530:1963

Carbon black dispersion Test IS 2530:1963

Thickness IS 10889:2004 Annex-A

Tensile Strength at break (a) Machine Direction (b) Transverse Direction

IS 13360(Pt-5/Sec.1) & IS 13360(Pt-5/Sec.3)

Elongation at break (a) Machine Direction (b) Transverse Direction

IS 13360(Pt-5/Sec.1) :1996 & IS 13360 (Pt-5/Sec.3):1999

67. Inhibitor Solution pH By pH Meter 500 gm 5-7

Specific Gravity test

Chloride content BS-1881:1988

Appearance

68. Job Mix Formula (Bituminous)

Complete Test As Per MORTH C.A 2Bag/ F.A1bag Bitumen 15 Kg Lime, Filler etc.

69. Job Mix Formula (Non Bituminous)

Complete Test As per MORTH/ CPWD

C.A 2Bag F.A1bag,dust etc.

of 30

S. NO.



70 Junction Box Complete Visual Examination -- Dimension, mm

Outside Diameter

Inside Diameter

Thickness

--

Resistance to Heat, mm IS 3419:1988 Resistance to Burning, Sec. IS 3419:1988 Moisture Absorption Test, % IS 3419:1988 Resistance to Chemical action

Alkaline Solution

IS 3419:1988

Copper Test At 120±2C for 7 hrs.

IS 3419:1988

Resistance to Oil, % At 60±1C for 48 hrs.

a) Change in External Dimension, % i) Outside Diameter, B, %

ii) Length, D, %

b) Visual Examination

IS 3419:1988

Resistance to Impact IS 3419:1988 Electrical Characteristics

a) Electric Strength,

b) Insulation Resistance, M

--

71. Kerb Stone Water Absorption IS-2185:2005 3 Pcs. 5-7

Compressive strength IS-516:1959

72. Kota Stone Complete Test 1 ft. x 1 ft. x 4 pcs. (50mm thickness)

7-8

1) Specific gravity IS-1122:1974

2) Water absorption IS-1124:1974

3) Hardness IS-13630:2016

4) Transverse Strength IS-1121:2013

5) Compressive Strength IS-1121:2013

6) Resistance to Wear IS-1706:1972

7) Dimension a) Length b) Width c) Thickness

IS-1130:1969

73. Lime Powder (Hydrated)

(A) Chemical Composition 5 kg 7-10

1. Calcium and Magnesium Oxide IS-6932:1973

2. Magnesium Oxide IS-6932:1973

3. Silica, Alumina and Ferric Oxide IS-6932:1973

4. Insoluble Residue in Dilute Acid and Alkali, %

IS-6932:1973

5. Carbon Dioxide, % IS-6932:1973

6. Available Lime (as CaO), % IS-1514:1959

(B) Physical Composition 1. Fineness a) Residue on 2.36mm b) Residue on 300µ c) Residue on 212µ

IS-6932:1973 5 kg

2. Workability, bumps IS-6932:1973

3. Popping & Pitting IS-6932:1973

of 30

S. NO.



74. Marble Stone

(IS-1130:1969)

Water Absorption IS 1124:1974 Specific Gravity IS 1122:1974 Scratch Hardness IS 13630(Pt-13):2006 Thickness IS 1130:1969

75. MDF Board (IS-12406:2003)

Dimension, mm a) Length b) Width c) Thickness d) Edge Straightness e) Squareness

IS 2380(Pt-2):1977

Density IS 2380(Pt-3):1977 Variation from Mean Density IS 2380(Pt-3):1977 Moisture Content IS 2380(Pt-3):1977 Water Absorption IS 2380(Pt-16):1977 Linear Expansion IS 2380(Pt-17):1977 Modulus of Rupture IS 2380(Pt-4):1977 Modulus of Elasticity IS 2380(Pt-4):1977 Internal Bond IS 2380(Pt-5):1977 Screw Withdrawl Strength IS 2380(Pt-14):1977

76. M.S. Channel/ Beam / Angle (As per IS 2062:2011)

Tensile strength Elongation Yield stress

IS-1608:2005

1/2 mtr. x 2 Pcs.

5-7

Bend test IS-1599:1985

Izod Impact (room temp) IS-1757 1 pc. thick

Izod Impact test (0°Temp.

Chemical Composition 1 PC. 5-7

Carbon IS 228(P-I):1987

Manganese IS 228(P-2):1987

Phosphorus IS 228(P-3):1987

Silicon IS 228(P-8):1989

Sulphur IS 228(P-9):1989

Nitrogen IS 228(Pt-19):1998

Carbon Equivalent IS-2062:2011

77. M.S. Pipe (as per 1161)

Complete Test 2 mtr. x 3 pcs.

7 days

Physical Test

1) Dimension

2) Mass --

3) Yield Stress 4) Tensile Strength 5) Elongation

IS-1608:2005

6) Bend Test IS-2329:2005

7) Flattening Test IS-2328:2005

Chemical Test

1) Carbon IS 228(P-I):1987

2) Manganese IS 228(P-2):1987

3) Phosphorous IS 228(P-3):1987

4) Sulphur IS 228(P-9):1989

of 30

S. NO.



78. M.S. Conduit Pipe Complete Test 1 Pc. 5-7 Dimension IS-9537:1981 Bending test IS-9537:1981 Compression test (load applied 750N)

IS-9537:1980

Length of screw thread IS-9537:1981

79. M.S. Bolt Tensile test IS-1608:2005 2 Pcs. 7-10 Rockwell Hardness IS-1586:2000

Vicker Hardness IS-1501:2002

Chemical Test

1) Carbon IS 228(P-I):1987 2) Manganese IS 228(P-2):1987 3) Phosphorous IS 228(P-3):1987 4) Sulphur IS 228(P-9):1989 5) Boron IS 228 6) Mass of Zinc Coating IS-6745:1972 7) Uniformity of Zinc Coating IS-2633:1986

80. M.S. Hollow Section Pipe (as per IS 4923:1997)

Complete 1 mtr. x 2 Pcs

7-10

(A) Physical Characteristics)

1. Outside dimension of side IS-4923:1997

2. Wall Thickness, mm IS-4923:1997

3. Straightness, mm IS-4923:1997

4. Twist, mm IS-4923:1997

5. Squareness of corner IS-4923:1997

6. Radius of corner, mm IS-4923:1997

7. Concavity/Convexity, mm IS-4923:1997

8. Yield Stress, N/mm2

9. Tensile Strength, N/mm2

10. Elongation, %

IS-1608:2005

11. Mass, kg/mtr. IS-4923:1997

12. Oiling and Painting IS-4923:1997

13. Height of internal IS-4923:1997

(B) Chemical Composition 1 Pc. 5-7 1. Carbon, % IS 228(P-I):1987 2. Manganese, % IS 228(P-2):1987 3. Silicon, % IS 228(P-3):1989 4. Sulphur, % IS 228(P-9):1989 5. Phosphorous, % IS 228(P-3):1987

81. Micro Silica (as per IS 15388)

Complete 3 kg 7-10 A) Physical Composition 1. Oversize % Retained on 45 µ IS Sieve

IS-1727:1967

2. Compressive Strength at 7 days

IS-1727:1967

(B)Chemical Composition 1. Silica (SiO2), % IS-1727:1967 2. Moisture Content, % IS-1727:1967 3. Loss on Ignition, % IS-1727:1967 4. Alkalies as Na2O, % Is-4032:1985

of 30

S. NO.



82. Marine Plywood (as per IS 710)

Complete Full length 25-30

1. Dimension IS-710:2010

2. Workmanship and Finish Visually 3. Moisture Content IS-1734:1983 4. Glue Adhesion in Dry State a) Glue Shear Strength, N b) Adhesion of Plies

IS-1734(Pt-4) 1983

5. Water Resistance Test (Boiling for 72 Hrs.) a) Glue Shear Strength, N b) Adhesion of Plies

IS-1734:1983


a) Parallel to Grain Direction b) Perpendicular to the Grain Direction c) Sum of the tensile Strength

IS-1734:1983

7. Mycological Test a) Visual b) Glue Shear Strength, N c) Adhesion of Plies

IS-1734:1983

8. Static Bending Strength a) Modulus of Elasticity, N/mm

2

b) Modulus of Rupture, N/mm2

IS-1734:1983

9. Wet Bending Strength a) Modulus of Elasticity, N/mm

2

b) Modulus of Rupture, N/mm2

IS-1734:1983

10. Retention of Preservative Chemicals IS-1734:1983

83. MDF / MDP Board (as per IS 3087)

Complete 1mtr. length (Full width)

10-12

1. Finish Visually

2. Dimension, mm IS-3087:2005

3. a) Density, kg/m3

b) Density Variation, % IS-23801

4. a) Moisture Content, % b) Moisture Variation, %

IS-23801

5. Water Absorption, % a) 2 hrs. Soaking b) 24 hrs. Soaking

IS-23801

6. Swelling in Water, %

7. Swelling Due to Surface Absorption, %

8. Workability

9. a) Modulus of Rupture, b) Modulus of Elasticity,

10. Tensile Strength Perpendicular To Surface, N/mm

2

11. Tensile Strength Perpendicular To Surface, N/mm

2

12. Screw Withdrawal Strength, N

13. Formaldehyde Content

IS-13745:1993

of 30

S. NO.



84. Nut/Bolt/Fastners Rockwell Hardness IS-1586:2000 1 Pc.

5-7

Brinell Hardness

Chemical Composition 1. Carbon, % 2. Manganese, % 3. Silicon, % 4. Sulphur, % 5. Phosphorous, %

IS 228(P-I):1987 IS 228(P-2):1987 IS 228(P-3):1989 IS 228(P-9):1989 IS 228(P-3):1987

Mass of zinc coating IS-6745:1972

85. Pre Laminated Particle Board (IS 12823)

Complete Full width (1 mtr.length)

10 days

1. Thickness, mm IS-12823:2015

2. Density kg/m3 IS-2380:1977

3. Density Variation, % IS-2380:1977


5. Water Absorption, % (a) 2 Hours (b) 24 Hours

IS-2380:1977

6. Thickness swelling, % IS-2380:1977

7. Modulus of rupture, N/mm2 IS-2380:1977

8. Modulus of elasticity, N/mm2 IS-2380:1977


Perpendicular to surface IS-2380:1977

10. Screw withdrawal strength N IS-2380:1977

11. Resistance to steam IS-12823:2015

12. Test for crack resistance IS-12823:2015

13. Resistance to Cigarette Burn IS-12823:2015

14. Resistance to stain IS-12823:2015

15. Abrasion Resistance IS-12823:2015

86. Paver Block (as per IS 15658:2006)

Complete 12 Pcs. 7-10

Dimension IS-15658:2006

Water Absorption IS-15658:2006

Compressive Strength IS-15658:2006

Abrasion Resistance

IS-15658:2006

87. PVC Water Stop (as per IS 15058)

Complete 1 mtr. length with ½ mtr. slab (2mm thick)

30 days

1) Dimension -

2) Tensile Strength 3) Elongation at break

IS-13360:1996

4) Hardness IS-13360:1996

5) Water Absorption IS-15058:2002

6) Accelerated Extraction IS-15058:2002

7) Stability on effect of Alkali test IS-15058:2002

8) Cold Bend Temp. IS-9766:1992

88. Plastic Piece Identification 100 gm 3-5

Glass Content

of 30

S. NO.



89. Plywood (as per IS 303) (MR & BWR)

Complete 1 mtr. x 2 pc. 20 to 25

1) Type of Surface of Plywood --

2) Visual observation --


4) Workmanship and finish --

5) Glue Adhesion Test (a) Resistance to water (b) Mycological test

IS-1734:1983

(6) Moisture Content IS-1734:1983

(7) Static bending strength IS-1734:1983

90. PVC Pipe (as per IS 4985:2000)

Complete 1 mtr. x 6 Pcs 15-16

1. Visual Appearance --


3. Opacity, % IS-12235:2004

4. Reversion Test, % IS-12235:2004

5. Vicat Softening Temp. 0C IS-12235:2004

6. Density, g/cc IS-12235:2004

7. Sulphated Ash Content, % IS-4985:2000

8. Mechanical Properties a) Hydrostatic Characteristic Acceptance Test b) Resistance to external, blows

IS-4985:2000 & IS-12235

91. PVC Conduit Pipe (as per IS 9537 Part-3)

Complete 1 mtr. x 6 Pcs 7-10

Marking


Mechanical Properties (a) Bending Test (b) Compression Test

IS-9537:1983

Resistance to Heat IS-9537:1983

Resistance to Burning IS-9537:1983

Electrical Characteristics IS-9537:1983

92. Plain Round Bar (as per IS 432 Part-2)

Complete test 1 mtr. x2 pcs. 7-10

Mechanical Test

Diameter IS-1566:1982

Tensile Strength Yield Stress Elongation

IS-1608:2005

Reverse Bend Test IS-1716:1985

Chemical test

Phosphorus IS-228(Pt-3)

Sulphur IS-228(Pt-9)

93. PPR Pipe (as per IS 15801:2008)

Complete 1 mtr. x 6 Pcs. 10-12

Dimension

Visual appearance

Hydraulic characteristics Acceptance (1 hour) Acceptance (22 hours) Acceptance (165 hours)

Reversion test

Density

Melt Flow rate

Opacity

of 30

S. NO.



94. PE-AL-PE Pipe (as per IS 15450)

Complete IS-15450:2004 1 mtr. x 6 Pcs.

10-12

Visual Appearance

Dimension --

Density IS- 73:1992

Melt Flow Rate IS-2530:1963

Carbon Black Content IS-2530:1963

Carbon Black Dispersion IS-2530:1963

Adhesion Test IS-15450:2004

Apparent Tensile Strength IS-15450:2004

Bursting Pressure Test IS-15450:2004

Hydraulic Characteristics IS-15450:2004

95 Paint (Enamel paint/ Distemper/ Plastic emulsion)

Complete 2 ltr. 8-10

Consistency

Drying time

Surface Day Hard Dry Touch Dry

Finish

Scratch hardness

Gloss

Water repellency

96. Pre-Laminated Fiber Board (IS-14587:1998)

Complete 2 ltr. 8-10

Density IS:2380 (P-3):1977

Moisture Content IS:2380 (P-3):1977

Water Absorption IS:2380 (P-3):1977

Thickness swelling IS:2380 (P-16):1977

Modulus of rupture IS:2380 (P-17):1977

Modulus of Elasticity IS:2380 (P-4):1977

Tensile Strength IS:2380 (P-4):1977

Screw withdrawl strength IS:2380 (P-5):1977

Abrasion Resistance IS:2380 (P-14):1977

Resistance to Steam IS 14587:1998

Resistance to Crack growth IS 14587:1998

Resistance to Cigarette Burn IS 14587:1998

Resistance to stain IS 14587:1998

97. Plywood for concrete shuttering work (IS-4990:2011)

Complete

Dimension & Tolerance a) Length b) Width c) Thickness d) Squareness, % e) Edge Straightness, %

IS 4990:2011

Workmanship and Finish Visually

Moisture Content IS 1734(Pt-1):1983

Glue Adhesion in Dry State IS 1734(Pt-4):1983

Resistance to Water Test IS 1734(Pt-4&5) :1983

Mycological Test IS 1734(Pt-7):1983

Tensile Strength IS 1734(Pt-9):1983

Static Bending Strength IS 1734(Pt-11):1983

Wet Bending Strength IS 1734(Pt-11):1983

Retention of Preservative IS 2753(Pt-1):1991

of 30

S. NO.



98. Paper Grammage IS 1060(Pt-1):1966 10 sheets 7-10 Moisture IS 1060(Pt-1):1966 pH IS 1060(Pt-1):1966 Opacity IS 1060(Pt-1):1966 Tensile Index

a) Machine Direction b) Cross Direction

IS 1060(Pt-1):1966

Thickness IS 1060(Pt-1):1966 Ash TAPPI T-211 Brightness IS 1060(Pt-II):1966

99. Soil Complete Test 10 kg 7-10

Plasticity Index Liquid Limit Plastic Limit

IS-2720(Pt-5)

Specific Gravity IS-2720(Pt-2)

Particle Size Distribution IS-2720(Pt-4)

(a)By Sieve analysis

Proctor Compaction Test (MDD / OMC) IS-2720(Pt-8)

Deleterious Substances

Direct shear (c & fy value) IS-2720(Pt-13)

CBR IS-2720(Pt-16)

Moisture Content IS-2720(Pt-29)

Free Swelling Index IS-2720(Pt-40)

100 S.S Kitchen Sink Complete Test 1 pc 7-10 days

Chemical Test

1. Carbon, % IS 228(Pt-1):1987

2. Manganese, % IS 228(Pt-2):1987

3. Phosphorus, % IS 228(Pt-3):1987

4. Silicon, % IS 228(Pt-8):1989

5. Sulphur, % IS 228(Pt-9):1989

6. Nickel, % IS 228(Pt-5):1987

7. Chromium, % IS 228(Pt-6):1987

Mechanical Test

1. Yield Stress, N/mm2 IS-1608:2005

2. Tensile strength, N/mm2 IS-1608:2005


4. Rockwell Hardness, HRB IS-1586:2000

5. Thickness after Forming, mm IS-13983:1994

6. Dimension, mm (a) Length (b) Depth (c) Width

IS-13983:1994

of 30

S. NO.



101. Shuttering Plywood (as per IS 4990)

Complete Full width x 1 mtr. length

7-10

Dimension & Tolerance IS-4990:2011 Workmanship and Finish Visually Moisture Content IS-1734(Pt-1) Glue Adhesion in Dry State IS-1734(Pt-4 &5) Resistance to Water Test IS-1734 Mycological Test IS-1734 Tensile Strength IS-1734 Static Bending Strength (i) Along the Face Grain Direction (ii) Across the Face Grain Direction

IS-1734

Wet Bending Strength (i) Along the Face Grain Direction (ii) Across the Face Grain Direction

IS-1734

Retention of Preservative IS-2753

102. Soil & Rain Water System (IS-13592:2013)

Complete Dimension, mm (a) Mean outside diameter (b) Outside diameter at any point (c) Wall thickness, s (d) Inside diameter of socket, D1 (e) Inside diameter of beading, D2 (f) Length of Beading & Neck, (g) Neck of socket, B (h) Length beyond beading, C

IS 13592:2013

Visual appearance Reversion Test, % IS 12235(Pt-5): 2004 Stress Relief Test IS 12235(Pt-6): 2004 Vicat Softening Temp.°C IS 12235(Pt-2): 2004 Resistance to Sulphuric Acid IS 12235(Pt-7): 2004 Impact Strength at 0°C IS 12235(Pt-9): 2004 Tensile Strength, MPa IS 12235(Pt-13) :2004 Axial Shrinkage, % (for type B pipes only)

IS 13592:2013

Water Tightness of joint At 0.05 MPa for 15 minute

IS 13592:2013

103. Stainless Steel (as per IS 6911)

(A) Chemical Test 1 Pc 5-7 1. Carbon, % IS 228(Pt-1):1987 2. Manganese, % IS 228(Pt-2):1987 3. Phosphorus, % IS 228(Pt-3):1987 4. Nickel, % IS 228(Pt-5):1987 5. Chromium, % IS 228(Pt-6):1987 6. Silicon, % IS 228(Pt-8):1989 7. Sulphur, % IS 228(Pt-9):1989

(B) Mechanical Test 1 mtr. x 2 Pcs.

5-7

1. Tensile strength 2. Elongation, 3. Yield Stress

IS-1608:2005

4. Rockwell Hardness IS-1586:2000

of 30

S. NO.



104. SFRC Manhole Cover

Load test -- 1 Pc. 5-7

105 SFRC Mainhole Cover

Breaking Load IS-12592:2002 2 pc 3-4 days

106 TMT Steel Chemical Test 1 mtr. x 1pcs. 3 days

1) Carbon IS 228(Pt-1):1987

2) Sulphur IS 228(Pt-9):1989

3) Phosphorus IS 228(Pt-3):1987

4) Sulphur + Phosphorus IS-1786:2008

5) Carbon Equivalent IS-1786:2008

Physical Test 1 mtr. x 2pcs. 4 days

1) Yield Stress 2) Tensile Strength 3) TS/YS Ratio 4) Elongation

IS-1608:2005

5) Bend Test IS-1599:2012

6) Rebend Test IS-1786:2008

7) Nominal mass IS-1786:2008

Pull Out Test 1 mtr. X 3 pc Plain bar & 1 mtr. X 3 pc tmt steel

30 days

107. Toughened Glass (as per IS 2835:1987)

Complete 1 Pc. 7-8

1. Dimension (a) Thickness

IS-2835:1987

2. Scratches Rubs & Crush (a) Central (b) Outer

IS-2835:1987

3. Bow, % (a) Central (b) Outer

IS-2835:1987

4. Sulphur Stains (a) Central (b) Outer

IS-2835:1987

5. Corner Breakage and chips IS-2835:1987

of 30

S. NO.



108. Thermoplastic Paint (white)

Complete 5 kg 7-10

1. Binder Content, % ASTM D4797-88 BS:3262(P1):1989

2. Glass Beads Content, % ASTM D4797-88 BS:3262(P1):1989

3. Softening Point, ◦C ASTM D-36-1995

4. Low Temp. Cracking Resistance test

BS 3262(P1):1989

5. Drying Time, Minutes IS:101(P3):1986

6. Titanium Dioxide (Tio2) ASTM D-4797-88(2007) BS:3262(P1):1989

7. Calcium Carbonate as Inert Filler BS:3262(P1):1989

109 Thermoplastic Paint (Yellow)

Complete Test ASTM D4797-88 BS:3262(P1):1989

2 kg 5-7

1. Binder Content, % ASTM D4797-88 BS:3262(P1):1989

2. Softening Point, ◦C ASTM D-36-1995

3. Low Temp. Cracking Resistance test

BS 3262(P1):1989

4. Drying Time, Minutes IS:101(P3/Sec1):1986

110. Teak wood (as per IS 1708)

Moisture IS 1708(Pt-1):1986 1 Pc. 5-7

Density IS 1708(Pt-2):1986

111. Ultrasonic Pulse Velocity test

Complete Test IS 13311 Part-1 - 5-7

112. U PVC Pipe (as per IS 12818:1992)

Complete 1 mtr. x 5 pcs.

10-12

Colour Visually

Visual Appearance Visually


Height, mm IS-12818:2010

Internal Diameter IS-12818:2010

Density, g/cc IS-12235:2004

Resistance to External Blows at 0

0C

IS-12235:2004

Tensile Strength Mpa IS-12235:2004

Vicat softening temperature IS-12235:2004

Effect on water IS-12235:2004

113. U PVC Rain Water Pipe (as per IS 13592)

Complete 1 mtr. x 3 Pcs.

10-12


2. Visual appearance IS-12235:2004

3. Reversion Test, % IS-12235:2004

4. Stress Relief Test, IS-12235:2004

5. Vicat Softening Temp.°C IS-12235:2004

6. Resistance to Sulphuric Acid, g IS-12235:2004

7. Impact Strength at 0°C IS-12235:2004

8. Tensile Strength, MPa IS-12235:2004

9. Water Tightness of joint IS-13592:2013

of 30

S. NO.



114. Veneer Ply Wood (as per IS 1328)

Complete Full width x 1 mtr. length

25 -28

1.Visual appearance Visually


4. Finish Visually


6. Resistance to water IS-1328:1996

7. Mycological test IS-1734:1983

8. Static Bending Strength IS-1734:1983

115. Vitrified Tile (IS-15622:2006) (Group B-I, a)

Complete 20 nos 7-10 Water Absorption IS 13630 (P-2): 2006 Modulus of rupture IS 13630 (P-6): 2006 Scratch hardness of Surface IS 13630 (P-13): 2006 Thermal Stock resistant IS 13630 (P-5): 2006 Dimension (a) Length (b) Width

IS 13630 (P-1): 2006

Surface Quality IS 13630 (P-1): 2006

Straightness of sides IS 13630 (P-1): 2006 Rectangularity IS 13630 (P-1): 2006 (B) Chemical Properties 1. Resistance to staining

IS 13630 (P-8): 2006

2. Chemical Resistance IS 13630 (P-8): 2006

116 Washer Rockwell Hardness IS-1586:2000 1 Pc.

5-7

Brinell Hardness

Chemical Composition 1. Carbon, % 2. Manganese, % 3. Silicon, % 4. Sulphur, % 5. Phosphorous, %

IS 228(P-I):1987 IS 228(P-2):1987 IS 228(P-3):1989 IS 228(P-9):1989 IS 228(P-3):1987

Mass of zinc coating IS-6745:1972

117. Water Proofing Compound (IS 2645:2003)

Complete 2 kg/ ltr 7-8

Chloride Content IS-6925:1973

Setting Time IS-4031(Pt-5):1988

Compressive Strength IS-4031(Pt-6):1988

Permeability to water % of Neat IS-2645:2003

Mortar --

118 Water (for construction purpose)

Complete 2.5 lit. 7 to 10

Acidity IS-456:2000

Alkalinity IS-456:2000

Solid Content IS-3025(Pt-18)

Organic & Inorganic IS-3025(Pt-18)

Sulphate (as SO3) IS-3025(Pt-24)

Chloride (as Cl) IS-3025(Pt-32)

pH IS-3025(Pt-11)

Suspended Solids IS-3025(Pt-17)

of 30

S. NO.



119. Water (for Drinking purpose)

Complete 2.5 ltr. 8-10

Colour IS-3025(Pt-4)

Odour IS-3025(Pt-5)

Taste IS-3025(Pt-7)

Turbidity IS-3025(Pt-10)

pH IS-3025(Pt-11)

T.Hardness IS-3025(Pt-21)

Iron IS-3025(Pt-53)

Chloride IS-3025(Pt-32)

T.Dissolved Solids IS-3025(Pt-16)

Fluoride IS-3025(Pt-60)

Coliform organisms IS-1622:1981

E. Coli IS-1622:1981

120. WMM (MORTH Spec.)

Complete 15 kg 8-10 Gradation IS 2386(Pt-1):1963 Impact Value IS 2386(P-4):1963 Maximum Dry Density (MDD) IS 2720(P-8):1983 Optimum Moisture Content (OMC) IS 2720(P-8):1983 Los Angles Absorption Value IS 2720(P-4):1983 Water Absorption IS 2386(P-3):1963 Atterberg Limit a) Liquid Limit b) Plastic Limit c) Plasticity Index

IS 2720(Pt-5):1985

Deleterious Constituents MORTH Spec. Combined Flakiness & Elongation IS 2386(P-1):1963

of 30

s.pioneertestinglaboratory.com/certificate_file/facilties available... · is-4985:2000 page 6 of 30...

Documents