Stainless steel 1.4501Grade 1.4501 is austenitic­ferritic also referred to as super duplex stainless steel, combine many of the beneficial propertiesof ferritic and austenitic steels. It offers enhanced pitting and crevice corrosion resistance in environments, where standardstainless and duplex steels are unsuitable. The duplex microstructure contributes higher strength and resistance to stresscorrosion cracking, combined with good weldability features.

Applications:• Components in offshore

• Waste water

• Sea water desalination

• Chemical  plants  with  aggressive  chloride­containing media:  heat  exchangers,  separator  parts,  compressor  and  pumpcomponents, turbine blades

 

The information on our web site is accurate to the best of our knowledge and understanding. Although every effort has been made to ensureaccuracy, the company cannot accept any responsibility for any direct or indirect damages resulting from possible errors or incorrect

application of the information of this publication. We reserve the right to make changes.

Copyright © 2014 Rautaruukki Corporation. All rights reserved.

Document printed on 24.06.2014 www.ruukki.com

Dimensions

Hot­rolled EN 1.4501 (S32760)

Dimensions mm Theor. weightThickness Width Length kg/m2 kg/pc

6 1500 3000 49,50 223,0

8 1500 3000 66,00 297,0

10 1500 3000 82,50 371,0

12 1500 3000 99,00 446,0

15 1500 3000 124,00 557,0

20 1500 3000 165,00 743,0

25 1500 3000 206,25 928,0

 

Properties

General properties

• Hot forming temperature range is 1150­1000°C, air cooling

• Solution annealing temperature range is 1040­1120°C, air or water cooling

• Recommended application temperature range 10­300°C, becomes brittle in higher temperatures

• Pitting and crevice corrosion resistance superior to EN 1.4404

• The yield strength is about twice that of austenitic steels, which enables savings in material weight

• Cold working requires substantially higher forces than for austenitic steels

• Due to the higher strength, spring back effect is also higher than for autenitic grades

• With a high speed steel tooling machining is able at the same feeds and speeds as with 1.4404

• 1.4501 can be welded by TIG,MIG, SMAW,SAW, FCW and PAW. Also applicable for laser, resistance and high frequencewelding.

Thermal conductivity at 20°C W/(mK): 13

Specific thermal capacity at 20°C J/(kgK): 475

Electrical resistivity at 20°C (Ωmm2)/m: 0.8

Magnetizable: Yes

Chemical properties (% by mass)

C Si Mn Pmax

S N Cr Cu Mo Nb Ni Others

acc. to EN 10088­2 ≤0.030

≤1.00

≤1.00

0.035 ≤0.015

0.20­0.30 24.0­26.0 0.50­1.00 3.0­4.0 ­ 6.0­8.0 W0.50­1.00

acc. to ASTM A240/A 240M

≤0.030

≤1.00

≤1.00

0.030 ≤0.010

0.20­0.30 24.0­26.0 0.50­1.00 3.0­4.0 6.0­8.0 W0.50­1.00

Mechanical properties

Product Thicknessmax/mm

Rp0.2Mpa

RmMpa

A80< 3mm Tr

A≥ 3mm Tr

Impact energyISO­V (Long.)

Impact energyISO­V (Tr.)

acc. to EN 10088­2 Plate 75 530 730­930 25 25 100 60

acc. to ASTM A240/A 240M 530 750 25

Stainless steel 1.4501

2

Resistant to intergranular corrosion in delivery condition: Yes

Resistant to intergranular corrosion in sensitized condition: Yes

Minimum 0.2%­proof strength, MPa at temperatures °C

100°C 150°C 200°C 250°C

450 420 400 380

Minimum Rm, MPa at a temperature (in °C) of

50°C 100°C 150°C 200°C 250°C

acc. to EN 10028­7 771 680 660 640 630

Physical properties

According to EN 10088­1

Density kg/dm3 Modulus of elasticity at (GPA)

20°C 100°C 200°C 300°C 400°C 500°C

7.8 200 194 186 180 ­ ­

Mean coefficient of thermal expansion

20°C­100°C 100°C­200°C 200°C­300°C 300°C­400°C 400°C­500°C 500°C­600°C

13.0 13.5 14.0 ­ ­ ­

 

The content of this document has been created from web page last updated 25 Apr 2014Our sales and technical support are happy to give you more information. Visit www.ruukki.com/contact­us.