Study of MgB 2 Thin Films on Nb by Pulse Laser Deposition. S.Mitsunobu, S.Inagaki, H.Nakanishi, M.Wake and M.Fukutomi* KEK,NIMR*. Scope of talk Introduction Forming method Mgb2 thin film PLD equipment Precursor annealing RF Measurement of the MgB2 thin film and Nb - PowerPoint PPT PresentationTRANSCRIPT
Study of MgB2 Thin Films on Nb by Pulse Laser Deposition
S.Mitsunobu, S.Inagaki, H.Nakanishi, M.Wake and M.Fukutomi*
KEK,NIMR*
Scope of talkScope of talk
IntroductionIntroduction
Forming method Mgb2 thin filmForming method Mgb2 thin film PLD equipment PLD equipment Precursor annealing Precursor annealing
RF Measurement of the MgB2 thin film and NbRF Measurement of the MgB2 thin film and Nb
Measurement of photo electron from the MgB2 thin Measurement of photo electron from the MgB2 thin film and Nbfilm and Nb
SummarySummary
INTRODUCTION
The large efforts have been concentrated on Nb cavities for International Linear Collider (ILC). The maximum accelerating field gradient of Nb cavities is limited about 50 MV/m due to Hcsh. MgB2 have higher Tc than Nb and expected to have higher Hcsh. Thin films of MgB2 on Nb is useful to increase future ILC energy upgrading.
At KEK, the preliminary test of thin films on Nb by Pulse Laser Deposition(PLD) method have been started and initially the direct deposition
of MgB2 film on Nb was studied.
Conceptual Drawing of Pulse Laser Deposition
Laser system of PLD
Vacuum Chamber of PLD
MgB2 Target
Substrate
PLD Processing
Heating 620oC in 1atom Ar
MgB2 film directly formed on Nb of 2.5mm thick
Heating 620oC
Q measurement system
Cu Cold test cavity
Q measurement system
QLs of MgB2 film on Nb & Nb
0
10000
20000
30000
40000
50000
60000
70000
80000
0 50 100 150 200 250 300 350
Temp ( K)
QL QL(MgB2-Nb)
QL(Nb)
QL for Nb & MgB2 film
0
10000
20000
30000
40000
50000
60000
70000
80000
0 10 20 30 40 50 60 70
Temp ( K)
QL QL(MgB2-Nb)
QL(Nb)
Photo electron measurement by PLD system
Nb MgB2 film on Nb
Relative Intensity of Photo electron
by 284nm laser wave length
Summery
• MgB2 precursor films formed on Nb by PLD.• The precursor film annealed at 620oC. • Cold RF measurement have been done.• The film partially superconducting.• Preliminary, photo electrons were measured for
Nb and MgB2. Some damaging of MgB2 surface was induced by defocused laser beam.
• More study will be continued.