test data and percent improvement to competition_duplex 6-01-11
TRANSCRIPT
-
8/13/2019 Test Data and Percent Improvement to Competition_Duplex 6-01-11
1/2
COMPETITIVE TEST DATA COMPARISON
updated 11/22/2010 Test ItemTest Method(s) or Variation of
Test Method(s) EmployedUnits of Measure Duplex
Leading
Competitor
% Duplex is Better Performing Than the
Tested Competitive Product s
Solid Content (Tie Coat) ASTM-D5965 % by volume 74 63 17%
Solid Content (Surface Coat) ASTM-D5965 % by volume 80 74 8%
VOC (Tie Coat) ASTM-D2369 grams/liter 187 325 42%
VOC (Surface Coat) ASTM-D2369 grams/liter 149 248 40%
Flash Point (Tie Coat) ASTM-D3278 oC 30 28 7%
Flash Point (Surface Coat) ASTM-D3278o
C 34 32 6%
Contact Angle (Surface Coat)ASTM-D7334-08, ASTM-D5725
99 R03
Degrees, the larger angel indicates
better performance105 71 48%
Scratch Resistance (Tie Coat &
Surface Coat)ASTM-G171-03
grams, the larger value indicates
better performance499 493 1%
Abrasion Resistance ASTM-D4060-07 and
Condition: abrasion range = 25", weight load =
1350g, speed setting = 0.6in/secASTM-D2197-98 R04
Adhesion (Tie Coat to Epoxy using
Seaguard 6100)ASTM-D1002-05
joule per square meter, the high
value indicates better performance780 426 83%
Adhesion (Sur face Coat to Tie Coat) ASTM-D1002-05joule per square meter, the high
value indicates better performance164 155 6%
Pseudo-Barnacle Adhesion Strength ASTM-D5179-02psi, the smaller value indicates
better performance5.1 7.5 32%
Barnacle Adhesion Strength in Shear ASTM-D5618-94psi, the smaller value indicates
better performance5.8 10.2 43%
P
hysicalProperties
grams, the lower weight loss value
indicates better performance
FoulRelease
Performance
25%0.0106 0.0141Mechanical
Strengthof
theSystem
Adhesion
FujiFilm Smart Surfaces, LLC Fouling Solutions that Work with Nature
Test data and percent improvement to competition_Duplex 11_22_10 1 of 2
-
8/13/2019 Test Data and Percent Improvement to Competition_Duplex 6-01-11
2/2
COMPETITIVE TEST DATA COMPARISON
updated 11/22/2010 Test ItemTest Method(s) or Variation of
Test Method(s) EmployedUnits of Measure Duplex
Leading
Competitor
% Duplex is Better Performing Than the
Tested Competitive Product s
FujiFilm Smart Surfaces, LLC Fouling Solutions that Work with Nature
Modulus ASTM-D638
MPa, the lower (softer) value
indicates better foul release
performance
0.71 0.98 28%
Stress @ Break ASTM-D638MPa, the high value indicates
better mechanical strength1.12 0.57 96%
Elongation ASTM-D638%, the high value indicates better
mechanical strength139 89 56%
Energy to Br eak (Toughness) --N.mm, the high value indicates
better mechanical strength297 173 72%
MechanicalStrengthof
S
urfaceCoatItself
Test data and percent improvement to competition_Duplex 11_22_10 2 of 2