tests of vips in simulation, laboratory, and practice tests of vips in simulation, laboratory, and...
TRANSCRIPT
TESTS OF VIPS TESTS OF VIPS ININ SIMULATION, LABORATORY, AND PRACTICE SIMULATION, LABORATORY, AND PRACTICE
Georg-Wilhelm Mainka
Prof. em. Dr.-Ing.
University of Rostock, Germany
Heiko Winkler
Dipl.-Ing.
IAIB Wismar, Germany
9th International Vacuum Insulation Symposium
The Royal Institution of Great Britain London 2009-09-18
Revised Version 2009-09-30
THE KINDERGARTENTHE KINDERGARTENKITA „PLAPPERSNUT“ IN KITA „PLAPPERSNUT“ IN WISMARWISMAR
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
2
BEFORE RETROFITTING: 2004
AFTER RETROFITTING: 2009
EAST GABLE FACADE VIP 1
2005: Award of the Journal „Bauphysik“
PREFAB CONCRETE PANELS
WITH CERAMIC SKIN
INSIDEHALL
NORTH FACADE
WEST GABLE FFACADE VIP 2
CONSTRUCTION OF VIP1 AND CONSTRUCTION OF VIP1 AND VIP2VIP2
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
3
VIP1: GLASS-CERAMIC-SANDWICH
VIP2: ETICS WITH VIP-KERNEL
VIP1: VIP1: SANDWICH WITH 4 VIPS SANDWICH WITH 4 VIPS INSIDEINSIDE
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
4
NORTHERN HALF 2005SOUTHERN HALF 2005
ANCHOR PLATE
SANDWICH ELEMENT WITHUNSEALED JOINTS
SANDWICH ELEMENTCOATED ONTO THEANCHOR PLATE
THE GAP BETWEEN OLD FACADE AND SANDWICHWAS FILLED WITHMINERAL WOOL TO AVOID CONVECTION
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
5
VIP1: FACADE PLAN , NEARLY VIP1: FACADE PLAN , NEARLY READY FACADEREADY FACADE, , AND AND THERMOGRAPHYTHERMOGRAPHY
SOUTHERN HALF 2005
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
6
WB
1 =
WB
2W
B 3
WB1+2
[W/mK]
WB3
[W/mK]
U-value
[W/m²K]
equival. thickness EPS (λ=40mW/mK)
d [mm]
VIP (center)
- - 0,190 200
VIP (Sandw.)
0,091 0,0208 0,345 110
ESTERN FACADE CA. 140 m² (2 GABLE WALLS SOUTH-NORTH)
SANDWICH GLASS/CERAMIC WITH VIP-KERNEL (ADCO COMPANY)
VIP1: VIP1: INFLUENCE OF THERMAL BRIDGES INFLUENCE OF THERMAL BRIDGES (WB) (WB)
Φ‘= U*A + Σψ*l
d = λ/(Φ‘*A)
-43%
VIP1: VIP1: TEST IN THE CLIMATE TEST IN THE CLIMATE CHAMBERCHAMBER
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
7
INSTALLING THE FACADE INTO THE TESTFRAME
FACADE READY TO BE TESTEDUPPER RIGHT: GLASS SIDING ON TOP OF 4 VIPS
TO OBSERVE THEIR BEHAVIOUR
VIP 1: THERMAL BRIDGES VIP 1: THERMAL BRIDGES (WB)(WB)MEASUREMENT VS MEASUREMENT VS CALCULATIONCALCULATION
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
8
-4,5-4
-3,5-3
-2,5-2
-1,5-1
-0,50
-12 -9 -6 -3 0 3 6 9 12
Distance from the middle of joint [cm]
Su
rfa
ce te
mp
era
ture
[°C
]
surf. temp. (IR)
surf. temp. Heat3
WB2
WB1 WB3 WB3
IR-THERMOGRAPHY AT DIFFERENT THERMAL BRIDGES (WB)
DISTRIBUTION OF SURFACE-TEMPERATUREAT WB3
VIP1: LONG TERM VIP1: LONG TERM BEHAVIOURBEHAVIOUR
VENTILATION VENTILATION
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
9
SOUTHERN HALF NORTHERN HALF 2005UNDER
CONSTRUCTIONWITHOUT
MINERAL FIBERS
2009
VIP1: LONG TERM VIP1: LONG TERM BEHAVIOURBEHAVIOUR CRACKS CRACKS
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
10
Detail
SOUTHERN HALF 2009ADHESIVE FIGURES ADDED 2007 TO HIDE CRACKSNEW CRACKS OCCURED
CRACK
CRACK
CR
AC
K
CRACK
IMPACTHOLE
CRACK
CR
AC
KW
ith
salt
y R
ims
at
low
er
Ele
men
t B
ord
er
VIP2: ETICS WITH VIP-VIP2: ETICS WITH VIP-KERNEL KERNEL
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
11
NORTHERN HALF 2005under Construction
ELEMENTS
JOINTS AT SURFACE
COATING
FIXING JOINT BETWEEN ELEMENTS
VIP2: FACADE PLAN , READY VIP2: FACADE PLAN , READY FACADE, AND FACADE, AND THERMOGRAPHYTHERMOGRAPHY
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
12
SOUTHERN HALF 2005 READY
DETAILVENTILATED ELEMENT
VIP2: U-VALUEVIP2: U-VALUE
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
13
MEASURED U (k)-VALUE: U = 0.19 W/m²K
LONG TIME MONITORING: TEMPERATURES [°C] AND HEAT FLUX [W/m²]
VIP2: INFLUENCE OF THERMAL VIP2: INFLUENCE OF THERMAL BRIDGESBRIDGES
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
14
WESTERN FACADE CA. 140 m² (2 GABLE WALLS)
ETICS WITH VIP-KERNEL (STO COMPANY)
-value
[W/mK]
U-value
[W/m²K]
equival. thickness EPS (λ=40mW/mK)
d [mm]
VIP (center)
- 0,19 200
VIP (ThB) 0,00275 0,22 180
Φ‘= U*A + Σψ*l
d = λ/(Φ‘*A)
-10%
VIP2: LONG TERM VIP2: LONG TERM BEHAVIOURBEHAVIOUR
VENTILATION VENTILATION
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
15
2005
2009
NORTHERN HALF SOUTHERN HALF
CONCLUSION: VIP1CONCLUSION: VIP1
+ + Easy to handle structural glazing- High performance for adjustable fixing system- Avoid ventilation behind panels (mineral fibers)- Reasons for cracks in ceramic plates unknown,
probably to thin (3mm)- Surface to sensitive for impacts (Vandalism)- Ventilated VIPs: to many- Thermal bridges: extra energy loss 43%
not yet recommendednot yet recommendedto be further developed
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
16
CONCLUSION: VIP2CONCLUSION: VIP2
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
17
+ common ETICS-technique
+ VIP protected
+ Ventilated VIPs: very few: < 1%
+ Thermal bridges: extra energy loss 10%
recommendedrecommended
ENDEND
THANK YOU THANK YOU
VERY MUCH VERY MUCH
FOR YOUR ATTENTIONFOR YOUR ATTENTION
G.-W. MAINKA UNIVERSITY OF ROSTOCK H. WINKLER
IAIB WISMAR
TEST OF VIPS IN SIMULATION; LABORATORY, AND PRACTICE IVIS - THE ROYAL INSTITUTE OF GREAT BRITAIN - LONDON 2009-09-18
18
Georg-Wilhelm Mainka [email protected] Winkler [email protected]