8/7/2019 THYROPLAST PHX_Supra
1/1
USA 800.323.1233 CANADA 800.268.4977 HEAT TREATMENT 800.265.0862www.schmolz-bickenbach.us www.schmolz-bickenbach.ca
Chemistry
Description
Typical C Cr Ni Cu Nb
Analysis 0.05 15.0 4.5 3.5 +
THYROPLAST PH X SUPRA is a corrosion-resistant,
martensitic precipitation hardened stainless steel.
THYROPLAST PH X SUPRA is supplied in pre-hardened
condition with a hardness of 38-42 HRC.
Excellent resistance to corrosion
Excellent polishability
Excellent dimensional stability
Good strength
Good toughness
Applications
Physical Properties (38-42 HRC)
Coefficient of
Thermal
Expansion
700F 2000F
5.9 X 10-6
/0
F
700F 4000F
6.0 X 10-6
/0
F
700F 7500F
9.2 X 10-6
/0
F
Thermal
Conductivity
700F115 Btu/in/ft2/hr/0F
3000F125 Btu/in/ft2/hr/0F
9400F155 Btu/in/ft2/
hr/0F
Heat Treatment
THYROPLAST PH X SUPRA
Technical Data Sheet
MechanicalProperties
Characteristics
Density: 0.285 lbs./in3 (room temperature)
Toughness (Charpy-V notch): 25 ft-lbs. at 38 HRC
Hardness
HRC
Y.S
(0.2%)
Ksi
T.S.
Ksi
EL
(%)
3840
42
160170
175
162172
180
12.812.2
12.2
Polishing
Tool should be polished using the guidelines for polishing
stainless steel. When properly polished, an A-1 surface finish is
achievable. .
WeldingRecommendations THYROPLAST PH X SUPRA is recommended for tools/
molds for the processing of corrosive plastics.
Refer to aging diagram below for aging temperatures.
Aging is performed by uniformly heating to aging tempera-
ture, equalizing temperature from surface to center, holding
for 4 hours at specified temperature, and air cooling.
3032
34
36
38
40
42
44
46750
800
850
900
950
1000
1050
1100
1150
1200
1250
Temperature in F
HardnessHR
THYROPLAST PH X SUPRA can be welded using shielded
metal arc welding process. Oxyacetylene welding is notrecommended.
THYROPLAST PH X SUPRA usually does not require
preheating to prevent cracking
AWS E/ER 630 filler material should be used to produce propertie
comparable to the parent material. If welded in the solution-treated condition, the welds can be aged
to the desired strength level after welding.
If welded in the over aged condition, the part must be solution
treated and then aged. It may be advantageous to preheat to ap-proximately 2000F and weld in the over aged (H 11500F) conditionfor repair welds more than 1 deep or where high welding stressesare anticipated.
For less critical applications, where high weld strength, hardness,
final polish or texture quality is not paramount a standard austenitistainless steel filler, E/ER308L, should be considered. This type o
filler will not produce the precipitation hardening response.
Corrosion Properties
All statements regarding the properties or utilization of the materials or products
mentioned are for the purposes of description only. Guarantees regarding the
existence of certain properties or a certain utilization are only valid if agreed
upon in writing.
General Notes