welcome to the mobile paint manufacturing co., inc. painting

The Best Paint Under the Sun!

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

Welcome to theMOBILE PAINT MANUFACTURING CO., INC.

PAINTING SYSTEMS GUIDEPLEASE NOTE

This document may take several minutes to load depending on the speed of your connection.Do not try to navigate through the document until the status bar at the bottom of your screen

indicates "Done". Best viewed with Acrobat Reader version 5.0 available free from Adobe.

Go to Painting Systems GuideGo to Painting Systems Guide Introduction

Go to Painting Systems Guide Index


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

MOBILE PAINT MANUFACTURING CO., INC.PAINTING SYSTEMS GUIDE

Go to Painting Systems Guide Introduction



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

INDEX TO PAINTING SYSTEMS GUIDEINTRODUCTIONIntroduction to Mobile Paints and the Painting Systems Guide

GUIDE TO GOVERNMENT SPECIFICATIONSA cross reference of Federal / Military Paint Specifications and our equivalent commercial products

SSPC SPECIFICATIONS FOR SURFACE PREPARATIONA summary of surface preparation specifications by the Society for Protective Coatings (SSPC)

FERROUS METALSCoating systems for steel surfaces for non-immersion service at ambient temperatures FERROUS METAL PRIMER GUIDEOverview of Anticorrosive Metal Primers

GALVANIZED METALS & ALUMINUMCoating systems for galvanized metal and aluminum for non-immersion service at ambient temperatures

HIGH TEMPERATURE SURFACESCoating systems for steel surfaces in service at temperatures up to 1,000OF

EXTERIOR MASONRYCoating systems for masonry, including cement block, concrete, brick, plaster, stucco, and gypsum board

INTERIOR MASONRYCoating systems for interior cement block, plaster, concrete, and gypsum board surfaces

WOOD FINISHESInterior and exterior finishes for wood

FLOOR FINISHESInterior and exterior finishes for wood and concrete floors and decks

WATER STORAGE TANKSInterior and exterior painting systems for water storage tanks - Potable water, fire protection water, plantprocess water, and de-mineralized water.

WASTE WATER TREATMENT PLANTSPainting systems for industrial waste water treatment plants and sewage treatment plants.

MARINE FINISHESMarine painting systems for commercial, military and recreational vessels

INDEX OF PRODUCT DATA SHEETS


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

MOBILE PAINT MANUFACTURING CO., INC.

Introduction to Painting Systems Guide

Mobile Paints, founded in 1921, has over 80 years experience in formulating top-quality architectural, indus-trial and marine coatings for tropical and subtropical climates. We were pioneers in developing effective andenvironmentally safe mildew inhibitors as well as lead-free paints for residential and industrial service. Basi-cally conservative, we put quality first and are proud of our logo:

“The Best Paint Under the Sun!”

This guide is a series of paint systems specifications for industrial, institutional, commercial and residentialapplications, covering both specific materials, such as ferrous metals, and specific services, such as floors.Product data sheets are available online at our Web Site (www.blpmobilepaint.com) and an index can befound in this publication. Material Safety Data Sheets are also available on request.

Individual sections of this guide cover Water Storage Tanks and Waste Water Treatment Plants.

Alternate systems are offered wherever practical in order to give additional flexibility in matching finish andservice required. Maintenance upgrade systems are included where applicable.

Systems include surface preparation and application details. The scope has been expanded to include main-tenance painting for upgrading deteriorated systems to high performance coatings.

Except as noted, all products listed are lead-free, chromate-free, mercury-free, and compliant with currentVOC regulations. As regulations may change, consult your Mobile Paint representative for products meetingspecific requirements in your area.

Mobile Paints offers a complete line of marine finishes for commercial, military and recreational vessels.Marine systems are also covered in this guide. We invite your inquiry and will be happy to work with you onyour specific requirements.

It is impossible to cover each specific situation in a guide such as this. For particular situations, consult yourBLP Mobile Paint representative for recommendations.

We appreciate your confidence in our products and look forward to being of service.


1

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

FED / MIL SPEC BLP MOBILE PAINTNUMBER DESCRIPTION ALTERNATE PRODUCT

SS-W-110 ** Water Repellent, Colorless Silicone Base Dub-L-Tite Silicone ExteriorWaterproofing, Clear 74-12

TT-C-535 Coating, Epoxy, Two Component, for Interior MoPoxYTM HS Epoxyon Metal, Wood, Concrete and Masonry Coating 613-series

TT-C-542 Coating, Polyurethane, Oil Free, MothaneTM MC-63 63-AF-1Moisture Curing (Type II Class A)

TT-C-550 Coating System, Glaze, Interior, MoPoxYTM HS Epoxyfor Masonry Surfaces Coating 613-series

TT-C-555 ** Masonry Coating System, Textured WEATHER-TITETM ELASTOMERICWall Coating 43-20

GUIDE TO GOVERNMENT SPECIFICATION COATINGS

This guide contains information concerning products manufactured by Mobile Paint Mfg. Co., Inc. and those products’application as performance equivalents to certain Federal and Military Specification coatings. These BLP Mobile Paintproducts are manufactured from quality raw materials to rigid quality standards and are recommended as performanceequivalents to the listed government specifications under their intended conditions of use.

Under some conditions of use, government specification coatings, while giving satisfactory performance, may not bethe coating or coating system most ideally suited to the job. Technical assistance is available through the Mobile PaintLaboratory in developing a coating system which is ideally suited to your requirements.

Unless so designated, the BLP Mobile Paint products cannot be certified as specification material. These products areoffered as substitutes only and should not be represented otherwise. If you have special requirements or if thespecification in question is not contained in the list, contact our Customer Service Department for assistance.

This information is offered in good faith and believed to be accurate at the time of publication. This information is subjectto change without prior notice

PLEASE NOTE: Government Specification Numbers in the following list are annotated with one or two asterisks(*) to note the following:

* Denotes that a Special Order Product is available which meets the specification requirements** Denotes that the Mobile Paint Product listed meets the specification requirements

2

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


TT-E-485 * Enamel, Semigloss, Rust Inhibiting Special RUS-KIL® Semi-gloss52-Series (Special Order Only)or RUS-KIL® Hi-Hide 655 series

TT-E-487 Enamel, Floor & Deck SpeeDeck® Polyurethane Floor& Deck Enamel 50-series

TT-E-489G * Gloss Synthetic Enamel Class A - NAM-A-LAC® Alkyd All PurposeAir Drying Enamel 30-series

TT-E-489H * Enamel, Alkyd, Gloss, Low VOC Special order only

TT-E-490 * Enamel, Silicone Semi-gloss Exterior Silicone Alkyd Enamel 13-Series& 432-series (High gloss only)

TT-E-491 Gloss Synthetic Enamel Class A - NAM-A-LAC® Alkyd All PurposeAir Drying Enamel 30-series

TT-E-505 Enamel, Odorless Alkyd, Interior High Gloss, NAM-A-LAC® Alkyd All PurposeWhite & Light Tints Enamel 30-series

TT-E-506 Enamel, White, Gloss, Interior NAM-A-LAC® Alkyd All PurposeEnamel 30-series

TT-E-508 * Interior Semi-gloss Enamel (Alkyd) COVENTRY® Lustarite AlkydTints & White Satin Enamel 135-series

TT-E-509 Enamel, Odorless, Alkyd Interior, COVENTRY® Lustarite AlkydSemi-gloss, Whites & Tints Satin Enamel 135-series

TT-E-529 Semi-gloss Synthetic Enamel Type I - Air Dry Special Order Only

TT-E-543 * Interior Enamel Undercoat (Alkyd) COVENTRY® Wood Sealer 19-8Tints & White

TT-E-545 Enamel, Odorless, Alkyd Interior, COVENTRY® Wood Sealer 19-8Undercoat, Flat Tints & White

TT-E-1593 Enamel, Silicone Alkyd, Gloss Jack Tar® Silicone Yacht Finish432-series

3

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


TT-E-1793 Enamel, Semi-gloss, Metal & Wood COVENTRY® Lustarite Alkyd SatinClass A - Air Dry Enamel 135-series

TT-F-1098 Filler, Block, Solvent Thinned for Bloc-FilTM 60-7 (Water Thinned)Porous Surfaces (NOTE: Substitute Product)

TT-P-19 Exterior Acrylic Emulsion WEATHER-TITETM MOPACOTE100% Acrylic Latex Flat HousePaint 40-series

TT-P-25 * Primer, Paint, Exterior Ready-Mixed WEATHER-TITETM Southern White®

for Wood Primer with Busan 5-6

TT-P-28 * Paint, Aluminum Heat Resistant (1200°F) BLP Silicone Heat ResistantAluminum 11-61

TT-P-29 * Paint, Latex Base, Interior Flat, White & Tints COVENTRY® Latex Flat WallPaint 35-series

TT-P-31 Red & Brown Iron Oxide Paint (Roof SPEED PRIMETM Red Oxide 9-78& Barn Paint)

TT-P-32 Blackboard Coating, Type I - Black, Chalkboard Slating, Black 17-11Type II - Green & Green 17-44

TT-P-37 Paint, Oil (Alkyd), Exterior Trim WEATHER-TITETM PermanentTrim & Accent 25-series

TT-P-52 Paint, Oil (Alkyd) Wood Shakes and Rough Weather Protector® Exterior WoodSiding Stain & Preservative 1411-40

TT-P-55 Paint, Polyvinyl Acetate Emulsion (Exterior) Smooth-Cote® Exterior VinylAcrylic House Paint Flat 291-series

TT-P-59 Paint, Ready-Mixed, International Orange Jack Tar® Yacht Deck EnamelSafety Orange - 450-61

TT-P-61 Ready-Mixed Black Paint RUS-KIL® Rust InhibitingEnamel Black 10-11

4

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


TT-P-71 Exterior Ready-Mixed Green Paint RUS-KIL® Rust InhibitingEnamel 10-series

TT-P-81 Paint, Ready-Mixed, Exterior Medium Shades WEATHER-TITETM 5-seriesSOUTHERNIZED® MildewResistant House Paint

TT-P-85 Paint, Traffic and Airfield Marking, BLP Street Marking Oil Base PaintSolvent Based 58-16 White, 58-51 Yellow

TT-P-96 * Paint, Latex Base, for Exterior Wood WEATHER-TITETM 40-seriesand Metal Surfaces. White & Tints 100% Acrylic Flat House Paint

TT-P-102 * Paint, Oil Alkyd (Modified) Exterior, Chalk and WEATHER-TITETM 5-seriesFume Resist., Lead-Free, Ready-Mixed, White SOUTHERNIZED® Oil House Paint

TT-P-115 Exterior Traffic Paint White & Yellow Type I BLP Street Marking Oil BasePaint 58-series

TT-P-620 Exterior Masonry Conditioner Chalk-Koter, White 29-16

TT-P-636 * Primer Coating, Alkyd, Wood and RUS-KIL® Rust Inhibiting Primer,Ferrous Metal Red 10-10

TT-P-641 Primer Coating, Zinc Dust-Zinc Oxide Special Order Only(For Galvanized Surfaces)

TT-P-645A * Primer, Paint, Zinc Chromate Prymall 35 Yellow ZincChromate Primer 9-55

TT-P-645B * Primer, Paint, Zinc Molybdate Zinc Moly Primer Yellow 80242(May be stocked in some locations)

TT-P-650 Interior White Primer, Latex, Type I, COVENTRY® Prymall 2 AcrylicReady-Mixed Primer and Sealer 19-7

TT-P-664C * Primer Coating, Rust Inhibiting, Lacquer Mo-BarTM Universal PrimerResisting Red 28-DR-105

5

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


TT-P-664D * Primer Coating, Rust Inhibiting, Lacquer Mo-BarTM PM III Universal PrimerResisting Red 28-DR-160

TT-P-1510 Paint, Latex, Exterior for Wood Surfaces WEATHER-TITETM 40-series100% Acrylic Latex Flat HousePaint

TT-P-1511 * Paint, Latex Base, Type I Semi-gloss COVENTRY® Latex Semi-glossEnamel 1335-series

TT-P-1728 Paint, Latex, Interior COVENTRY® Latex Flat WallPaint 35-series

TT-P-1975 Primer Coating, Latex Base, Exterior ACR-A-LACTM Acrylic Latex(For Metal) Primer Red 330-7 or

H20 RUS-KIL® Primer 310-9

TT-P-1984 Primer Coating, Latex Base, Exterior WEATHER-TITETM 100% Acrylic(Undercoat for Wood) Latex Universal Primer 6-6

TT-R-248 Remover-Solvent Type, Water Rinsable Super XL Water Wash PaintRemover 74-24

TT-S-176 Sealer, Surface, Varnish Type, Floor, NUWOOD® Poly-Var FloorWood or Cork Varnish, Gloss 70-12

TT-S-1992 Stain, Latex, Exterior for Wood Surfaces Weather Protector® Int./Ext.Acrylic Latex Stain 44-series

TT-T-266 Thinner, Dope and Lacquer Lacquer Thinner #15 75-21,Lacquer Thinner #60 75-22,Lacquer Thinner #1000 75-23

TT-T-291 * Thinner, Paint, Mineral Spirits, MoPaxOl® Low Odor Paint &Type I Regular Varnish Thinner 75-1

TT-T-306 Thinner, Synthetic Resin Enamel TEC Thinner 75-11

TT-V-51 * Varnish, Asphalt Asphaltum #1 61-11

6

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


TT-V-71 Interior Varnish NUWOOD® Special Floor &Trim Varnish 70-13

TT-V-81 * Varnish, Mixing for Aluminum Special Order OnlyType I and Type II

TT-V-85 Varnish, Oil, Low sheen, Brush or Spray NUWOOD® MoPaCo-VarTM FlatWater White Varnish 70-21

TT-V-109 Varnish, Spar, Alkyd-Resin NUWOOD® MoPaCo-VarTMGlossWater White Varnish 70-23

TT-V-119 Varnish, Spar, Phenolic Resin Jack Tar® 100% PhenolicMarine Spar Varnish 470-31

TT-V-121 Water Resisting Spar Varnish Jack Tar® 100% PhenolicMarine Spar Varnish 470-31

DOD-E-698 * Enamel, Alkyd, Deck, Black SpeeDeck® Polyurethane Floor& Deck Enamel 50-series(Not Semi-gloss)

DOD-E-699 * Enamel, Deck Gray SpeeDeck® Polyurethane Floor& Deck Enamel 50-series(Not Semi-gloss)

DOD-E-700 * Enamel, Deck, Interior, Gray SpeeDeck® Polyurethane Floor& Deck Enamel 50-series(Not Semi-gloss)

DOD-E-1115 * Enamel, Interior and Exterior, Special Order OnlyWhite (Formula 30)

DOD-E-1265 Enamel, Ship, Exterior, Ocean Gray NAM-A-LAC® Alkyd All PurposeEnamel 30-series

MIL-C-4556d * Steel Tank Coating System MoPoxYTM HB Primer 40-DR-5 &MoPoxYTM HB White 40-AW-13

7

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


MIL-E-15090 * Enamel, Equipment, Light Gray Special Order Only(Formula 111) Type I & Type III

DOD-P-15146 * Exterior Enamel, Dull Black Formula 104 RUS-KIL® Rust InhibitingEnamel Flat Black 10-12

DOD-P-15328 ** Primer (Wash) Pretreatment Vinyl Wash Primer 9-42

MIL-P-15931 ** Paint, Anti-fouling, Vinyl Formula 121 Jack Tar® Vinyl Anti-foulingRed 473-73

MIL-P-19451 ** Paint, Antifouling, Cold Plastic, Formula 105 Jack Tar® VIP Cold PlasticAnti-fouling Red 473-71

DOD-P-21035 ** Paint, High Zinc Dust Galv. Repair Coating Gray 80166(May be stocked in some locations)

MIL-C-22750 Coating, Epoxy/Polyamide MoPoxYTM HS Epoxy Coating613-series

DOD-P-23236A Paint Coating Systems, Steel Ship Tank, Class 1 - 40-AW-13Fuel and Salt Water Ballast, Type I Class 2 - 40-AX-7

Class 3 - 28-DH-50Class 4 - Not Available

MIL-P-23377 ** Primer Coating, Epoxy-Polyamide MoPoxYTM Catalyzed EpoxyPrimer 40-DN-4

MIL-P-24441 * Paint, Epoxy-Polyamide Special Order OnlyType I, Type III or Type IV (May be stocked in some locations)

DOD-P-24596 * Coating Compounds, Non-Flaming, Special Order OnlyFire Protective

DOD-P-24607 * Enamel, Interior, Non-Flaming (Dry), Special Order OnlyChlorinated Alkyd Resin, Semigloss

DOD-E-24635 * Enamel, Silicone Alkyd Copolymer Special Order Only(May be stocked in some locations)

8

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


MIL-P-28577 Primer, Water Reducible WEATHER-TITETM 100% AcrylicLatex Universal Primer 6-6

MIL-P-28578 Paint, Water Reducible, Semi-Gloss WEATHER-TITETM 100% AcrylicLatex Gloss House Paint140-series

MIL-P-28582 Primer Coating, Exterior WEATHER-TITETM Southern White®

Primer with Busan 5-6

MIL-P-38336 Primer Coating, Inorganic Zinc MoZincTM 3 Inorganic ZincCoating 28-DH-50

MIL-C-81309 Corrosion Preventative Compound BLP Lube 60TM 10-60Type II, Class 2

MIL-C-83286 * Coating, Urethane, Aliphatic Isocyanate Special Order Only

MIL-C-85285 * Coating, Polyurethane, High Solids, Type II Special Order Only

1

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

SURFACE PREPARATION SPECIFICATIONS

SOCIETY FOR PROTECTIVE COATINGS

PROPER SURFACE PREPARATION is the key to maximum service from any paint system. The following is a briefsummary of the standards published by the Society for Protective Coatings, formerly the Steel Structures Painting Council,40 24th Street, 6th Floor, Pittsburgh, Pennsylvania 15222-4643. Please refer to the full specification for further informa-tion.

SSPC-SP 1: SOLVENT CLEANING

Solvent Cleaning covers many methods of cleaning, some of which go beyond solvent action and utilize chemicalcleaning to remove oil, grease, dirt, soil, drawing compounds and other similar matter. It includes the removal of oldpaints by the use of paint removers or alkaline paint strippers. Corrosive salts, such as chlorides and sulfates are notremoved with hydrocarbons and must be removed with water prior to cleaning the surface with hydrocarbon solvents.This method of cleaning will not remove rust, rust scale, or mill scale. When rags are used for solvent cleaning, theyshould be changed frequently as they absorb grease and act as a transfer medium for contaminants. Any alkalinecompounds should be removed carefully as they may form soap, which will inhibit good adhesion of future coatingsystems. As a final step for extra protection, the surface should be wiped clean with a weak phosphoric acid solution.Caution should always be taken when using solvent cleaning because of the danger of combustion.

SSPC-SP 2: HAND TOOL CLEANING

Hand Tool Cleaning is primarily a method for preparing metal surfaces for coating by removing loose mill scale, looserust and loose paint by hand brushing, sanding, scraping or chipping. Other hand-impact tools or a combination of thesemethods can be used. This type of cleaning is normally used in preparing surfaces where corrosion is only a minorproblem. Care should always be taken on weld seams or spots to remove flux as it promotes premature system failure.Hand cleaning is not recommended for the faster drying finishing systems, such as vinyls.

SSPC-SP 3: POWER TOOL CLEANING

Power Tool Cleaning is a method of preparing metal surfaces for coating by removing the loose mill scale, loose rust, andloose old paint with power wire brushes, impact tools, grinders, sanders or a combination of the tools. In employing thismethod, care should be taken that burnished mill scale is not mistaken for bright, clean metal. Primer coatings will notadhere to burnished areas of this type and premature failure results. This system does not intend that tight mill scale, tightrust, and tight paint be removed by this process. Loose mill scale, loose rust, and loose paint, and other detrimentalforeign matter present, however, shall be removed.

2

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

SSPC-SP 5: WHITE METAL BLAST CLEANING

White Metal Blast Cleaning is a method of preparing surfaces for coating by removing all mill scale, rust scale, paint, orother foreign matter by the use of abrasive propelled either through nozzles by compressed air or by centrifugal wheels.“White Metal” is defined as a surface with a gray-white uniform metallic color, slightly roughened to form a suitableanchor pattern for coatings. The surface shall be free of visible mill scale, rust, corrosion, oxide, paint or other foreignmatter. The cost of this method is comparatively high and is generally used only when required for top performance ofsophisticated coating systems.

SSPC-SP 6: COMMERCIAL BLAST CLEANING

Commercial Blast Cleaning is a method of preparing surfaces for coating by removing all mill scale, rust scale, paint, orother foreign matter by the use of abrasive propelled either through nozzles by compressed air or by centrifugal wheels. Itrequires the removal of all visible scale, rust, and other surface contaminants. Evenly dispersed very light shadows,streaks, and discoloration caused by stains of rust, stains of mill scales, and stains of previously applied paint may remainon no more than 33% of the surface. Slight residues of rust and paint may also be left in the craters or pits if the originalsurface is pitted.

SSPC-SP 7: BRUSH-OFF BLAST CLEANING

Brush-Off Blast Cleaning is a method of preparing surfaces for coating by removing loose mill scale, loose rust scale,loose paint, or other foreign matter by the use of abrasive propelled either through nozzles by compressed air or bycentrifugal wheels. It is not intended that the surface be free of all scale, rust, and paint. The remaining scale, rust, andpaint should be tight and the surface should be sufficiently abraded to provide good adhesion and bonding of paint. Thelow cost of this method may result in economical protection in mild environments. A blast-cleaned surface should betreated or primed before any rusting occurs or the benefit of blast cleaning is lost. The exposed bare metal will rust quicklyunder conditions of high humidity, when wet, or when in a corrosive atmosphere. It is best practice to prime or chemicallytreat within eight hours of blasting.

SSPC-SP 10: NEAR-WHITE BLAST CLEANING

Near-White Blast Cleaning is a method of preparing surfaces for coating by removing nearly all mill scale, rust scale,paint, or other foreign matter by the use of abrasive propelled either through nozzles by compressed air or by centrifugalwheels. A “Near-White” blast cleaned finish is defined as one from which all oil, grease, dirt, mill scale, rust, corrosionproducts, oxides, paint or other foreign matter have been completely removed from the surface except for very lightshadows, very slight streaks, or slight discoloration caused by rust stain, mill scales oxides, or slight residue of paint orcoating that may remain. At least 95% of each square inch of surface shall be free of all visible residues and the remaindershall be limited to the slight discoloration mentioned above.

3

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

SSPC-SP 11: POWER TOOL CLEANING TO BARE METAL

Power Tool Cleaning to Bare Metal is a method of preparing metal surfaces for painting by removing all mill scale, rustscale, paint, or other foreign matter by the use of power tools to produce a bare metal surface and to retain or produce asurface profile. The surface shall be free of visible mill scale, rust, corrosion, oxide, paint or other foreign matter. Slightresidues of rust and paint may be left in the lower portions of pits if the original surface is pitted.


Ferrous Metals Systems1

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

RECOMMENDED PAINTING SPECIFICATIONSFOR FERROUS METALS

For Non-Immersion Service at Ambient Temperatures

This section covers ferrous metals, including structural steel, non-galvanized roof decking, exteriors of storage tanks andsilos, tubing, pipe racks, platforms, ladders, siding, doors and door frames, both interior and exterior, for non-immersionservice at ambient temperatures.

Originally written for new industrial construction, the scope has been expanded to include coating systems for commercial,institutional, and residential construction and for maintenance painting, both for recoating original systems and for upgradingdeteriorated industrial coating systems where removal of existing coatings is not feasible or practical but high performanceis required.

Proper surface preparation is essential to the life of any coating system. Abrasive blasting is the preferred method ofremoving rust and mill scale on new steel and old paint, rust and similar surface contaminants on previously painted steelprior to coating. In addition to cleaning the surface, abrasive blasting cuts the steel to provide an anchor pattern whichassures good adhesion of the primer to the substrate.

Solvent clean to remove grease, oil and similar contaminants which cannot be removed successfully with abrasive blasting.

The Society for Protective Coatings, formerly the Steel Structures Painting Council, is the recognized authority on surfacepreparation and painting procedures for steel and reference is made to their standards as follows:

Solvent Cleaning SSPC-SP 1Hand Cleaning SSPC-SP 2Power Tool Cleaning SSPC-SP 3White Metal Blast SSPC-SP 5Commercial Blast SSPC-SP 6Brush-off Blast SSPC-SP 7Near White Blast SSPC-SP 10Power Tool Cleaning to Bare Metal SSPC-SP 11

Details will be found in Section 3 of this book, SSPC Standards.

Wet blasting is becoming more common to control dust from abrasive blasting and comply with stringent EPA requirements,requiring new techniques and the use of additives to the blasting water to prevent immediate rust bloom. Consult yourBLP Mobile Paint representative for equipment and additive recommendations.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

Choice of the coating system will ultimately depend on the surface to be coated, condition of this substrate or of theexisting coating and the degree of surface preparation possible, the skill of the applicator and the time available, desiredservice life of the paint system, and the economic and regulatory factors involved.

When specifying coatings, one should always think of the substrate or surface to be painted, surface preparation,pretreatment, shop coat, primer, and intermediate and finish coats as the entire coating system.

Please see the FERROUS METALS PRIMER GUIDE for additional primers and shop coats.

In new construction, industry practice is to clean and prime structural steel prior to erection. The shop coat or primerselected depends on the finish paint chosen, which is again a function of the service required from the coating system.

After erection, all nuts, bolts, scratches and abraded areas should be cleaned and spot-primed before additional coats ofprimer or finish are applied. Welds should be ground smooth to remove weld splatter before priming.

Maintenance painting is the same as for new construction except for surface preparation and spot priming when completeremoval of the existing coating system is not contemplated. Maintenance upgrading to high performance coatings iscovered at the end of this section.

The following sections are listed in order of increasing protection and are intended for non-immersion service atambient temperatures.

SECTION 01. ALKYD SYSTEMS - good protection against normal weathering. Least expensive, easiest surface preparationand application, but shortest service life. May be applied by brush, roller or spray.

SECTION 02. ACRYLIC LATEX SYSTEMS - water thinned, may be applied over a variety of primers including alkyd,acrylic, galvanized steel and inorganic zinc. Offers superior resistance to weathering and ultraviolet, good resistance tomild chemical fumes and salt spray. May be applied by brush, roller or spray.

SECTION 03. SILICONE ALKYD SYSTEMS - combine ease of surface preparation and application with excellent resistanceto weathering and ultraviolet, good resistance to mild chemical fumes and salt spray. Has outstanding gloss and colorretention. May be applied by brush, roller or spray over alkyd, silicone alkyd and acrylic primers.

SECTION 04. CATALYZED EPOXY AND POLYURETHANES - superior resistance to chemicals, especially alkalis, moisture,and abrasion. Good resistance to most solvents, marine environments, acid splashes. Most epoxies will chalk on exposureto ultraviolet. Topcoat with acrylic epoxy or catalyzed polyurethane to prevent chalking in exterior service.Suitable for immersion service in fresh and salt water. Immersion service is covered separately in sections on WaterStorage Tanks and Waste Water Treatment Plants.

Recommended for use in industrial and marine service for factories, refineries, tank farms, pipelines, chemical andpharmaceutical plants, waste water treatment plants, and other institutional and commercial applications such as machineshops, schools, hospitals, laundries, kitchens and food processing areas, where a durable, easily-cleaned and attractivefinish is desired. Available in high gloss and semi-gloss in a wide range of colors. Waterborne formulations are available.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

SECTION 05 - INORGANIC ZINC-RICH PRIMER SYSTEMS - Excellent galvanic protection in moderate to severe industrialand marine service. See SECTION 04 for high performance topcoats.

SECTION 06 - ZINC-RICH EPOXY PRIMER SYSTEMS - Combine the wetting properties, chemical and abrasion resistanceof a catalyzed epoxy with the galvanic protections afforded by inorganic zinc. See SECTION 04 for high performancetopcoats.

SECTION 07 - MAINTENANCE UPGRADE SYSTEMS - For upgrading deteriorated systems..Mobile Paints offers a wide range of industrial finishes for specialized applications. Please consult your BLP Mobile Paintrepresentative for specific recommendations.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

RECOMMENDED PAINTING SPECIFICATIONSFOR FERROUS METALS


This section covers ferrous metals, including structural steel, non-galvanized roof decking, tubing,pipe racks, exteriors ofstorage tanks and silos, platforms, ladders, siding, doors and door frames, both interior and exterior, for non-immersionservice at ambient temperatures.Recommended systems include surface preparation, recommended shop coat, and field-applied primers, intermediateand finish coats.

Systems have been expanded to include residential, commercial, institutional, light industrial, heavy industrial and marineservice as indicated.Additional systems are included for maintenance and upgrading existing deteriorated coatings.

Specific applications such as Potable Water Storage Tanks, OEM, Waste Water Treatment Plants, Tank Farms, FoodProcessing Areas, and Pharmaceutical Plants will be found in their individual sections.

Please see the FERROUS METALS PRIMER GUIDE for additional primers and shop coats.

In addition to the products listed, Mobile Paints formulates an extensive line of specialty coatings, product finishes, andFederal Specification Paints. Please call your BLP Mobile Paint representative for assistance in meeting your requirements.1-800-621-6952.

SECTION 01 - ALKYD SYSTEMS:01 ALKYD SYSTEMS offer good protection against normal weathering, mild chemical fumes and normal abrasion.Least expensive, easiest surface preparation and application, shortest service life. Available in a wide range of colors. Notsuitable for immersion service. All systems are VOC compliant. Suitable for Interior and Exterior service except as noted.

Please see the FERROUS METAL PRIMER GUIDE for additional primers and shop coats.

Surface Preparation: Commercial Blast, SSPC-SP 6, recommendedPower Tool Clean, SSPC-SP 2, recommended minimumHand Tool Clean, SSPC-SP 3, minimum acceptableSolvent Clean, SSPC-SP 1, to remove oil or grease

Application: Brush, Roller, Airless or Conventional Spray



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

01.A Alkyd System, High Gloss, Residential, Commercial & Light Industrial Service

Coat Product High Gloss Enamel Finish VOC Sq Ft Mils

Shop 9-78 SPEED PRIME Red Oxide Primer 3.76 447 1.5Prime 10-10 RUS-KIL Metal Primer, Red 3.35 395 2Intermediate 10-Series RUS-KIL Gloss Enamel 3.35 385 2Finish 10-Series RUS-KIL Gloss Enamel 3.35 385 2

Total Dry Mils 7.5

01.B Alkyd System, High Gloss, Residential, Commercial & Light Industrial Service


Shop 9-78 SPEED PRIME Red Oxide Primer 3.76 447 1.5Prime 10-10 RUS-KIL Metal Primer, Red 3.35 395 2Intermediate 30-Series NAM-A-LAC Non-Toxic Enamel 3.18 409 1.5Finish 30-Series NAM-A-LAC Non-Toxic Enamel 3.18 409 1.5

Total Dry Mils 6.5

01.C Alkyd System, Semi-Gloss, Interior, Residential, Commercial & Light Industrial Service

Coat Product Semi-Gloss Enamel Finish VOC Sq Ft Mils

Shop 9-78 SPEED PRIME Red Oxide Primer 3.76 447 1.5Prime 10-10 RUS-KIL Metal Primer, Red 3.35 395 2Intermediate 135-Series COVENTRY Lustarite Satin-Gloss 3.04 427 2Finish 135-Series COVENTRY Lustarite Satin-Gloss 3.04 427 2

Total Dry Mils 7.5

01.D Alkyd System, High Gloss, Industrial Service


Shop 28-DR-154 MO-BAR Universal LCF Primer 4.50 379 1.5Prime 28-DR-160 MO-BAR PM-III LCF Universal Primer 3.49 387 2Intermediate 10-Series RUS-KIL Gloss Enamel 3.35 385 2Finish 10-Series RUS-KIL Gloss Enamel 3.35 385 2

Total Dry Mils 7.5



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

01.E Alkyd System, Spray Fog Dry Semi-Gloss, Interior, Commercial & Industrial Service

Coat Product Semi-Gloss Enamel Finish VOC Sq Ft Mils

Shop 9-78 SPEED PRIME Red Oxide Primer 3.76 447 1.5Prime 10-9 RUS-KIL Metal Primer, Gray 3.35 395 2Intermediate* 61-BW-2 SPRAY FOG DRY Semi-Gloss Coating 3.25 382 2Finish* 61-BW-2 SPRAY FOG DRY Semi-Gloss Coating 3.25 382 2* Apply by airless spray

Total Dry Mils 7.5

01.F Alkyd System, Spray Fog Dry Flat, Interior, Commercial & Industrial Service

Coat Product Flat Enamel Finish VOC Sq Ft Mils

Shop 9-78 SPEED PRIME Red Oxide Primer 3.76 447 1.5Prime 10-9 RUS-KIL Metal Primer, Gray 3.35 395 2Intermediate* 6-DW-58 SPRAY FOG DRY Flat Coating 3.17 407 2Finish* 6-DW-58 SPRAY FOG DRY Flat Coating 3.17 407 2* Apply by airless spray

Total Dry Mils 7.5

SECTION 02 - ACRYLIC LATEX ENAMEL SYSTEMS:

02 ACRYLIC LATEX ENAMELS are the latest development in a general purpose finish for interior and exteriorservice. Lead, chromate and mercury free. Very low VOC. Easy to apply over a variety of primers and substrates includingzinc and galvanized metals. Good resistance to normal weathering and mild chemical fumes. Waterborne, low odor, easycleanup.Not for immersion service.Please see the FERROUS METAL PRIMER GUIDE for additional primers and shop coats.

Surface Preparation: Commercial Blast, SSPC-SP 6, preferredPower Tool Clean, SSPC-SP 2, recommended minimumHand Tool Clean, SSPC-SP 3, minimum acceptableSolvent Clean, SSPC-SP 1, to remove oil or grease




251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

02.A Acrylic Latex DTM System, High Gloss, Residential to Light Industrial Service

Coat Product Acrylic Gloss DTM Enamel Finish VOC Sq Ft Mils

Shop 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Prime 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Intermediate 310-Series H2O RUS-KIL Acrylic DTM Enamel 1.09 295 2Finish 310-Series H2O RUS-KIL Acrylic DTM Enamel 1.09 295 2

Total Dry Mils 8.0

02.B Acrylic Latex System, High Gloss, Residential to Light Industrial Service

Coat Product Acrylic Gloss Enamel Finish VOC Sq Ft Mils

Shop 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Prime 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Intermediate 330-Series ACR-A-LAC Acrylic Gloss Enamel 2.11 293 2Finish 330-Series ACR-A-LAC Acrylic Gloss Enamel 2.11 293 2

Total Dry Mils 8.0

02.C Acrylic Latex System, Medium Gloss, Residential to Light Industrial Service

Coat Product Acrylic Gloss Enamel Finish Sq Ft Mils

Shop 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Prime 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Intermediate 140-Series WEATHER-TITE 100% Acrylic Gloss 1.99 296 2Finish 140-Series WEATHER-TITE 100% Acrylic Gloss 1.99 296 2

Total Dry Mils 8.0

02.D Acrylic Latex System, Satin Gloss, Residential to Light Industrial Service

Coat Product Acrylic Satin Gloss Enamel Finish VOC Sq Ft Mils

Shop 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Prime 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Intermediate 240-Series WEATHER-TITE 100% Acrylic Satin 2.19 271 2Finish 240-Series WEATHER-TITE 100% Acrylic Satin 2.19 271 2

Total Dry Mils 8.0



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

02.E Acrylic Latex System, Flat, Residential to Light Industrial Service

Coat Product Acrylic Flat Finish VOC Sq Ft Mils

Shop 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Prime 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Intermediate 40-Series WEATHER-TITE 100% Acrylic Flat 1.03 291 2Finish 40-Series WEATHER-TITE 100% Acrylic Flat 1.03 291 2

Total Dry Mils 8.0

02.F Vinyl Latex System, Interior, Flat, Residential to Light Industrial Service

Coat Product Latex Flat Finish VOC Sq Ft Mils

Shop 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Prime 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Intermediate 35-Series COVENTRY Interior Latex Flat 0.83 375 1.5Finish 35-Series COVENTRY Interior Latex Flat 0.83 375 1.5

Total Dry Mils 7.0

02.G Acrylic Latex System, Interior, Semi-Gloss, Residential to Light Industrial Service

Coat Product Acrylic Semi-Gloss Enamel Finish VOC Sq Ft Mils

Shop 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Prime 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Intermediate 1335-Series COVENTRY Acrylic Latex Semi-Gloss 2.00 345 1.5Finish 1335-Series COVENTRY Acrylic Latex Semi-Gloss 2.00 345 1.5

Total Dry Mils 7.0

02.H Acrylic Latex System, Interior, Eggshell, Residential to Light Industrial Service

Coat Product Acrylic Eggshell Enamel Finish VOC Sq Ft Mils

Shop 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Prime 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Intermediate 2335-Series COVENTRY Acrylic Eggshell Enamel 0.86 375 1.5Finish 2335-Series COVENTRY Acrylic Eggshell Enamel 0.86 375 1.5

Total Dry Mils 7.0



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

02.I Acrylic Latex System, Interior, High Gloss, Residential to Light Industrial Service

Coat Product Acrylic High Gloss Enamel Finish VOC Sq Ft Mils

Shop 310-09 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Prime 310-09 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Intermediate 335-Series COVENTRY Acrylic High Gloss Enamel 1.09 408 1.5Finish 335-Series COVENTRY Acrylic High Gloss Enamel 1.09 408 1.5

Total Dry Mils 7.0

02.J Acrylic Latex System, Interior, Fog Dry, Flat, Commercial to Light Industrial Service

Coat Product Acrylic Flat Enamel Finish VOC Sq Ft Mils

Shop 310-9 H2O RUS-KIL Acrylic Metal Primer 3.35 345 2Prime 310-9 H2O RUS-KIL Acrylic Metal Primer 3.35 345 2Intermediate* 55-DW-3 SPRAY Fog Dry Acrylic Flat White 0.80 322 2Finish* 55-DW-3 SPRAY Fog Dry Acrylic Flat White 0.80 322 2*Apply by airless spray

Total Dry Mils 8.0

02.K Acrylic Latex System, Interior, Fog Dry, Gloss, Commercial to Light Industrial Service

Coat Product Acrylic Gloss Enamel Finish VOC Sq Ft Mils

Shop 310-9 H2O RUS-KIL Acrylic Metal Primer 3.35 345 2Prime 310-9 H2O RUS-KIL Acrylic Metal Primer 3.35 345 2Intermediate* 55-AW-9 SPRAY Fog Dry Acrylic Gloss White 0.75 289 2Finish* 55-AW-9 SPRAY Fog Dry Acrylic Gloss White 0.75 289 2*Apply by airless spray

Total Dry Mils 8.0



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

SECTION 03 - SILICONE ALKYD SYSTEMS:

03 SILICONE ALKYDS offer excellent resistance to marine and industrial environments, weathering and ultravioletexposure. Good resistance to mild chemical fumes, outstanding gloss and color retention. Easy to apply. Not for immersionservice.Lead, chromate and mercury free.


Surface Preparation: Commercial Blast, SSPC-SP 6, recommendedPower Tool Clean, SSPC-SP 2, recommended minimumHand Tool Clean, SSPC-SP 3, minimum acceptableSolvent Clean, SSPC-SP 1, to remove oil or grease


03.A Silicone Alkyd System, High Gloss, Residential, Commercial & Industrial Service

Coat Product High Gloss Silicone Alkyd Enamel VOC Sq Ft Mils

Shop 9-78 SPEED PRIME Red Oxide Primer 3.76 447 1.5Prime 10-10 RUS-KIL Metal Primer, Red 3.35 395 2Intermediate 432-Series JACK TAR Silicone Yacht Finish 3.57 484 1.5Finish 432-Series JACK TAR Silicone Yacht Finish 3.57 484 1.5

Total Dry Mils 6.5

03.B Silicone Alkyd System, High Gloss, Heavy Industrial & Marine Service

Coat Product High Gloss Silicone Alkyd Enamel VOC Sq Ft Mils

Shop 28-DR-160 MO-BAR PR-III Universal Primer 3.49 387 2Prime 28-DR-160 MO-BAR PR-III Universal Primer 3.49 387 2Intermediate 432-Series JACK TAR Silicone Yacht Finish 3.57 484 1.5Finish 432-Series JACK TAR Silicone Yacht Finish 3.57 484 1.5

Total Dry Mils 7.0



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

SECTION 04 - CATALYZED EPOXY AND POLYURETHANE SYSTEMS:

04 CATALYZED EPOXY AND POLYURETHANE SYSTEMS offer superior resistance to many chemicals, especiallyalkalis, abrasion and moisture, together with good resistance to most solvents, acid splashes and chemical fumes.Recommended for Commercial, Light Industrial, heavy Industrial, and Marine Service at ambient temperatures.Excellent for interior use in chemical and pharmaceutical plants, schools, hospitals, kitchens and food processing areas,laundries, and other institutional, industrial and commercial installations where maximum protection and durability arerequired. Available in a wide range of colors for an easily cleaned and attractive finish.While most epoxies have excellent resistance to fresh and salt water, immersion service is covered in separate sectionsunder Water Storage Tanks and Sewage Treatment Plants. Waterborne epoxies are offered but should not be used inimmersion service.Epoxy mastics are generally surface tolerant and suitable both as primers for sandblasted steel and for application overferrous metal surfaces where optimum surface preparation may not be feasible. Also recommended as a sealer / barriercoat over existing deterioratedcoatings to allow upgrading to high performance systems such as epoxies and polyurethanes.

The following epoxy primers and epoxy-mastics are available and may be interchanged within the suggested systemrecommendations. Topcoat with catalyzed polyurethane or acrylic epoxy to prevent chalking in exterior service.

Code Description VOC Sq Ft DFT/Gal

40-DR-5 MOPOXY HB Epoxy Primer, Red 3.49 131 6.0513-10 MOPOXY Epoxy Primer, Red 4.24 322 2.0613-10 MOPOXY HS Epoxy Primer, Red 2.00 382 341-Series MOPOXY IR (Indefinate Recoat) DTM Mastic 2.29 136 840-AY-2 MOPOXY MASTIC Aluminum 0.51 248 640-AW-32 MOPOXY MASTIC White 1.30 217 640-AH-51 MOPOXY MASTIC Gray 1.30 217 641-Series MOPOXY PLUS High Solids Mastic 2.36 131 841-AF-2 MOPOXY PRE-PREP Penetrating Sealer 0.00 1604 140-DR-12 MOPOXY PCP Preconstruction Primer 5.25 388 1

The following Coal Tar epoxies are generally used in immersion or underground service and are not topcoated.

40-AX-7 MO-TAR C-200 Polyamide Coal Tar 1.56 157 840-BX-6 MO-TAR HB-90 High Build Coal Tar 1.13 67 20

Please review our FERROUS METAL PRIMER GUIDE for additional detail.

CATALYZED POLYURETHANES offer good outstanding color and gloss retention. Recommended for marine environments,tank farms, chemical plants, and heavy equipment. Not recommended for immersion service.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

The following catalyzed polyurethane formulations are available and may be used interchangeably within the suggestedsystem recommendations. Other formulations are available for special service.

Code Description VOC Sq Ft DFT/Gal

72-Series MOTHANE Polyurethane Enamel 4.11 339 2Apply by Airless or Conventional Spray only

72-Series MOTHANE HD (Heavy Duty) Polyurethane 4.11 268 2.5Apply by Airless or Conventional Spray, Brush or Roll

72-Series MOTHANE HS-1000 (High Solids) Polyurethane 2.45 513 2Apply by Airless or Conventional Spray, Brush or Roll

72-Series MOTHANE HS-900 (High Solids) Polyurethane 2.47 417 2.5Apply by Airless or Conventional Spray only

Mobile Paints offers a wide range of epoxies and polyurethanes for special applications. Ask your BLP Mobile Paintrepresentative for detailed recommendations.


Surface Preparation: Commercial Blast, SSPC-SP 6, preferred minimumPower Tool Clean, SSPC-SP 2, minimum acceptableSolvent Clean, SSPC-SP 1, to remove oil or grease

Application: Brush, Roller, Airless or Conventional Spray unless otherwise indicated

04.A Catalyzed Water-Borne Acrylic Epoxy, Commercial & Light Industrial Service

Coat Product High Gloss W/B Catalyzed Acrylic VOC Sq Ft Mils

Shop 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Prime 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2Intermediate 69-AW-5 MOPOXY H2O-100 W/B Acrylic Epoxy 1.71 313 2Finish 69-AW-5 MOPOXY H2O-100 W/B Acrylic Epoxy 1.71 313 2

Total Dry Mils 8.0



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

04.B Catalyzed Water-Borne Epoxy System, Commercial & Industrial Service

Coat Product Semi-Gloss W/B Amide Epoxy Finish VOC Sq Ft Mils

Shop 69-DR-1* MOPOXY H2O Polyamide Metal Primer 0.89 257 3Prime 69-DR-1* MOPOXY H2O Polyamide Metal Primer 0.89 257 3Intermediate 69-AW-6 MOPOXY H2O-200 W/B Amide Epoxy 1.00 225 3Finish 69-AW-6 MOPOXY H2O-200 W/B Amide Epoxy 1.00 225 3

* May also use 310-9 H2O RUS-KIL PrimerTotal Dry Mils 12.0

04.C Catalyzed Epoxy System, Commercial & Industrial Service

Coat Product High Gloss Epoxy Finish VOC Sq Ft Mils

Shop 40-DR-12 MOPOXY PCP Preconstruction 5.25 348 1Prime 513-10 MOPOXY Metal Primer 4.24 322 2Intermediate 513-Line MOPOXY High* Gloss Epoxy Coating 4.30 314 2Finish 513-Line MOPOXY High* Gloss Epoxy Coating 4.30 314 2

* use catalyst 77-17 for semi-glossTotal Dry Mils 7.0

04.D Catalyzed Epoxy System, Commercial & Industrial Service

Coat Product High Solids Semi-Gloss Epoxy Finish VOC Sq Ft Mils

Shop 40-DR-12 MOPOXY PCP Preconstruction 5.25 348 1Prime 613-10 MOPOXY HS High Solids Metal Primer 2.00 382 3Intermediate 613-line MOPOXY HS High Solids S/G Epoxy 2.00 374 3Finish 613-line MOPOXY HS High Solids S/G Epoxy 2.00 374 3

Total Dry Mils 10.0

04.E Catalyzed Epoxy System, Commercial & Industrial Service

Coat Product Acrylic Epoxy High Gloss Finish VOC Sq Ft Mils

Shop 40-DR-12 MOPOXY PCP Preconstruction 5.25 348 1Prime 613-10 MOPOXY HS High Solids Metal Primer 2.00 382 3Intermediate 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 8.0



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

04.F Catalyzed Epoxy / Epoxy Mastic / Polyurethane System, Heavy Industrial & Marine Service

Coat Product High Gloss Polyurethane Finish VOC Sq Ft Mils

Prime 613-10 MOPOXY HS High Solids Metal Primer 2.00 382 3Intermediate 40-AW-32 MOPOXY Mastic, White 1.30 217 6Finish 72-Series MOTHANE HD Polyurethane 4.11 268 2.5Finish 72-Series MOTHANE HD Polyurethane 4.11 268 2.5

Total Dry Mils 14.0

04.G Catalyzed Epoxy / Epoxy Mastic / Polyurethane System, Heavy Industrial & Marine Service


Prime 613-10 MOPOXY HS High Solids Metal Primer 2.00 382 3Intermediate 40-AW-32 MOPOXY Mastic, White 1.30 217 6Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 13.0

All of the below are high-solids, low VOC and may be used interchangeably as Primer and Intermediate coats in thefollowing systems.All may be topcoated with either catalyzed epoxy or polyurethane for maximum protection in heavy industrial and marineenvironments.

MOPOXY MASTIC is a high solids, high build, surface tolerant amine epoxy formulated for application over sound rust and/or deteriorated paint systems as a base coat for upgrading to high performance coatings such as acrylic epoxies andpolyurethanes. Superior performance over abrasive blasted steel in heavy industrial and marine environments. Excellentresistance to fresh and salt water, most organic solvents, chemical splashes and fumes, and abrasion.

MOPOXY PLUS is a high-performance, high solids DTM polyamide epoxy with excellent adhesion to tight rust, goodadhesion to damp surfaces, and cures at low temperatures. Excellent resistance to fresh and salt water, detergents andcorrosive chemicals. Very good resistance to fumes and spills of most organic solvents, acids, and alkalis. Superiorperformance over blast cleaned steel.

MOPOXY IR - Indefinite Recoatability Epoxy - is a high-solids, high-build, surface tolerant, DMTpolyamide coating whichmay be applied to damp, rusty surfaces, allowed to dry for prolonged periods, then topcoated with other epoxies orpolyurethanes without loss of intercoat adhesion.Good anticorrosive properties. Solvent sensitive. Superior anticorrosive properties over blast-cleaned steel.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

04.H Catalyzed Epoxy Mastic /Epoxy System, Heavy Industrial & Marine Service

Coat Product High Gloss Epoxy Finish VOC Sq Ft Mils

Prime 40-AH-51 MOPOXY Mastic, Dawn Gray 1.30 217 6Intermediate 40-AW-32 MOPOXY Mastic, White 1.30 217 6Finish 513-Line MOPOXY High* Gloss Epoxy Coating 4.30 314 2Finish 513-Line MOPOXY High* Gloss Epoxy Coating 4.30 314 2

* use catalyst 77-17 for semi-glossTotal Dry Mils 16.0

04.I Catalyzed Epoxy Mastic /Epoxy System, Heavy Industrial & Marine Service


Prime 40-AH-51 MOPOXY Mastic, Dawn Gray 1.30 217 6Intermediate 40-AW-32 MOPOXY Mastic, White 1.30 217 6Finish 613-line MOPOXY HS High Solids Epoxy 2.00 374 3Finish 613-line MOPOXY HS High Solids Epoxy 2.00 374 3

Total Dry Mils 18.0

04.J Catalyzed Epoxy Mastic /Acrylic Epoxy System, Heavy Industrial & Marine Service

Coat Product High Gloss Acrylic Epoxy Finish VOC Sq Ft Mils

Prime 40-AH-51 MOPOXY Mastic, Dawn Gray 1.30 217 6Intermediate 40-AW-32 MOPOXY Mastic, White 1.30 217 6Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 16.0



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

04.K Catalyzed Epoxy Mastic /Polyurethane System, Very Heavy Industrial & Marine Service


Prime 40-AH-51 MOPOXY Mastic, Dawn Gray 1.30 217 6Intermediate 40-AW-32 MOPOXY Mastic, White 1.30 217 6Finish 72-Series MOTHANE HD Polyurethane 4.11 268 2.5Finish 72-Series MOTHANE HD Polyurethane 4.11 268 2.5

Total Dry Mils 17.0

04.L Catalyzed Epoxy Mastic /Polyurethane System, Very Heavy Industrial & Marine Service

Coat Product High Solids Polyurethane Finish VOC Sq Ft Mils

Prime 40-AY-2 MOPOXY Mastic, Aluminum 0.51 248 6Intermediate 40-AW-32 MOPOXY Mastic, White 1.30 217 6Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 16.0

04.M Catalyzed Epoxy Mastic /Acrylic Epoxy System, Heavy Industrial & Marine Service

Coat Product Acrylic Epoxy Gloss Finish VOC Sq Ft Mils

Prime 41-CW-1 MOPOXY-PLUS DTM Epoxy 2.36 131 8Intermediate 41-CW-1 MOPOXY-PLUS DTM Epoxy 2.36 131 8Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 20.0



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

04.N Catalyzed DTM Epoxy Mastic /Polyurethane System, Heavy Industrial & Marine Service


Prime 41-CW-1 MOPOXY-PLUS DTM Epoxy 2.36 131 8Intermediate 41-CW-1 MOPOXY-PLUS DTM Epoxy 2.36 131 8Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 20.0

04.O Indefinitely Recoatable Epoxy/Polyurethane System, Heavy Industrial & Marine Service


Prime 41-BK-14 MOPOXY IR High Solids Epoxy Buff 2.29 136 8Intermediate 41-BK-14 MOPOXY IR High Solids Epoxy Buff 2.29 136 8Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 20.0

04.P Recoatable Epoxy/Polyurethane System, Heavy Industrial & Marine Service


Prime 41-BK-14 MOPOXY IR High Solids Epoxy Buff 2.29 136 8Intermediate 41-BK-14 MOPOXY IR High Solids Epoxy Buff 2.29 136 8Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 20.0



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

SECTION 05 - INORGANIC ZINC-RICH PRIMER SYSTEMS:

05 INORGANIC ZINC-RICH PRIMERS offer excellent galvanic protection in moderate to severe industrial andmarine environments. Excellent resistance to fresh and salt water, detergents, and most chemicals, moisture and abrasion.High performance topcoats are recommended for severe chemical exposures. Heat resistant to 750 degrees Fahrenheit.

Recommended for tank farms, pipe racks, in heavy industrial or marine service.Inorganic zinc requires a clean surface and good anchor pattern for good adhesion.

Surface Preparation: White Metal Sandblast, SSPC-SP-5, preferredCommercial Sandblast, SSPC-SP 6, minimum acceptable

Application: Airless or Conventional Spray with constant mechanical agitation

Inorganic Zinc is much more porous than hot-dip galvanizing and may be top-coated without application of vinyl washprimer. See Galvanized Metals & Aluminum for details.

Top-coat Application: Apply mist coat to wet zinc thoroughly to dispel air and avoid bubbles.Follow by full body coat while still tacky,

05.A Inorganic Zinc/Epoxy Mastic/Polyurethane System, Very Heavy Industrial & Marine ServiceRecommended for tank farms, pipe racks, in heavy industrial or marine service.


Prime 28-DH-50 MO-ZINC #3 Inorganic Zinc Primer 3.88 342 3Intermediate 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 13.0

05.B Inorganic Zinc/Epoxy Mastic/Epoxy System, Heavy Industrial & Marine Service

Coat Product High solids Semi-Gloss Epoxy Finish VOC Sq Ft Mils

Prime 28-DH-50 MO-ZINC #3 Inorganic Zinc Primer 3.88 342 3Intermediate 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 613-Series MOPOXY HS High Solids Epoxy 2.00 374 3Finish 613-Series MOPOXY HS High Solids Epoxy 2.00 374 3

Total Dry Mils 15.0



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

05.C Inorganic Zinc/Epoxy Mastic/Epoxy System, Heavy Industrial & Marine Service

Coat Product Acrylic Epoxy Gloss Finish VOC Sq Ft Mils

Prime 28-DH-50 MO-ZINC #3 Inorganic Zinc Primer 3.88 342 3Intermediate 40-AW-32 MOPOXY Mastic, White 1.30 217 6Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 13.0

SECTION 06 - ZINC-RICH EPOXY PRIMER SYSTEMS:

06 ZINC-RICH EPOXY PRIMER combines the wetting properties, chemical and abrasion resistance of a catalyzedepoxy with the galvanic protection afforded by inorganic zinc.

Excellent resistance to fresh and salt water, detergents and most chemicals, abrasion and moisture. Excellent for touch-upof inorganic zinc primers. VOC Compliant.Recommended for tank farms, pipe rack, severe industrial and marine environments.Topcoat recommended for severe exposures.

Surface Preparation: Near-White Metal Blast, SSPC-SP10, recommendedCommercial Sandblast, SSPC-SP 6, recommended minimumPower Tool Clean, SSPC-SP 2, minimum acceptable

Application: Airless or Conventional Spray with continual mechanical agitation.

The following zinc-rich epoxy primers are available and may be used interchangeably:

Code Description VOC Sq Ft Mils

40-CM-2 MOPOXY ZR Zinc Rich Primer 3.45 321 2.540-CM-4 MOPOXY ZR Zinc Rich Primer, Green 3.89 257 3.540-DH-6 MIL-DTL-24441 F 159 ZR Primer 2.50 336 3.0

In the interest of simplicity, we have written the following recommendations based on the application of 40-CM-2 becauseof its low VOC and very high zinc content in the dry film.

Please see the FERROUS METAL PRIMER GUIDE for additional primers and shop coats.Ask your BLP Mobile Paint representative for detailed recommendations.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

06.A Zinc-Rich Epoxy/Epoxy/Polyurethane System, Very Heavy Industrial & Marine Service

Recommended for tank farms, pipe rack, severe industrial and marine environments.


Prime 40-CM-2 MOPOXY ZR Zinc Rich Epoxy Primer 3.45 321 2.5Intermediate 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 12.5

06.B Zinc-Rich Epoxy/Epoxy Mastic/Epoxy System, Heavy Industrial & Marine Service


Prime 40-CM-2 MOPOXY ZR Zinc Rich Epoxy Primer 3.45 321 2.5Intermediate 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 613-Series MOPOXY HS High Solids Epoxy 2.00 374 3Finish 613-Series MOPOXY HS High Solids Epoxy 2.00 374 3

Total Dry Mils 14.5

06.C Zinc-Rich Epoxy/Epoxy Mastic/Acrylic Epoxy, Heavy Industrial & Marine Service


Prime 40-CM-2 MOPOXY ZR Zinc Rich Epoxy Primer 3.45 321 2.5Intermediate 40-AW-32 MOPOXY Mastic, White 1.30 217 6Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 12.5



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

SECTION 07 - MAINTENANCE UPGRADE SYSTEMS:

07 FOR UPGRADING deteriorated alkyd, silicone alkyd and acrylic finishes and repairing catalyzed epoxy andpolyurethane systems where removal of existing coatings is not possible.

See Section 04, Catalyzed Epoxy and Polyurethane Systems, for additional coatings.

MOPOXY MASTIC Aluminum is a very high solids, low VOC, surface tolerant high performance epoxy coating offeringexcellent protection in moderate to severe industrial and marine environments. DTM or use as base coating over rust anddeteriorated paint for upgrading to high performance topcoats.

MOPOXY MASTIC is a high-solids, high-build, surface tolerant amine epoxy formulated for application over sound rustand/or deteriorated paint systems as a base coat for upgrading to high performance coatings such as acrylic epoxies andpolyurethanes.

MOPOXY IR , Indefinite Recoatablility Epoxy, is a high-solids, surface-tolerant, high-build polyamide coating which maybe applied to damp, rusty surfaces, allowed to dry for prolonged periods, then topcoated with other epoxies or polyurethaneswithout loss of intercoat adhesion. Good anticorrosive properties.

MOPOXY PLUS is a high-performance high-solids DTM polyamide epoxy with excellent adhesion to tight rust, goodadhesion to damp surfaces, and cures at low temperatures. Excellent resistance to fresh and salt water, detergents andcorrosive chemicals. Very good resistance to fumes and spills of most organic solvents, acids and alkalis.

MOPOXY PRE-PREP is a 100% solids epoxy with very low viscosity and excellent substrate wetting properties. Excellentfor badly rusted areas where sandblasting and removal of existing coatings is not possible and only minimal cleaning ispossible. Penetrates and bonds rust and deteriorated coatings into a solid film which seals out moisture and oxygen.

Allow to cure for 24 hours, then apply recommended intermediate coat while still slightly soft. Will accept a wide varietyof coatings.

MO-BAR Universal Primer is a high-quality, quick-drying modified alkyd anticorrosive primer or shop coat. Use as a barriercoat to prevent lifting of solvent-sensitive coatings by high performance top coats. Excellent protection against corrosionin mild industrial and marine environments.All systems recommended are suitable for heavy industrial and marine service.

Surface Preparation: Pressure Wash (3,000 psi or better) to remove contaminationSolvent Clean, SSPC-SP 1, to remove oil and greasePower Tool Clean, SSPC-SP 2, preferredHand Tool Clean, SSPC-SP 3, minimum recommended

Application: Brush, roller or airless or conventional spray.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

07.A Epoxy Mastic / High Solids Polyurethane System


Spot Prime 40-AY-2 MOPOXY MASTIC, Aluminum 0.51 248 6Prime 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 16.0

07.B Epoxy Mastic / Acrylic Epoxy System


Spot Prime 40-AY-2 MOPOXY MASTIC, Aluminum 0.51 248 6Prime 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 16.0

07.C IR Epoxy / High Solids Polyurethane System


Spot Prime 41-BK-14 MOPOXY IR High Solids Epoxy Buff 2.29 136 8Prime 41-BK-14 MOPOXY IR High Solids Epoxy Buff 2.29 136 8Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 20.0

07.D IR Epoxy / Acrylic Epoxy System


Spot Prime 41-BK-14 MOPOXY IR High Solids Epoxy Buff 2.29 136 8Prime 41-BK-14 MOPOXY IR High Solids Epoxy Buff 2.29 136 8Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 20.0



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

07-E Low Viscosity Epoxy / Epoxy Mastic / High Solids Polyurethane System


Prime 41-AF-2 MOPOXY PrePrep Clear 0.00 1069 1.5Intermediate 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 11.5

07-F Low Viscosity Epoxy / Epoxy Mastic / Acrylic Epoxy System


Prime 41-AF-2 MOPOXY PrePrep Clear 0.00 1069 1.5Intermediate 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 11.5

07-G Universal Primer / Epoxy Mastic / High Solids Polyurethane System


Prime 28-DR-160 MO-BAR PM-III Universal Primer 3.49 393 1.5Intermediate 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 11.5

07-H Universal Primer / Epoxy Mastic / Acrylic Epoxy System


Prime 28-DR-160 MO-BAR PM-III Universal Primer 3.49 393 1.5Intermediate 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 11.5

1


Ferrous Metals Systems - Primer Guide

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

FERROUS METAL PRIMER GUIDE INDEX

Overview of Anticorrosive Metal Primers

Section 1 - Alkyd Primers for Ferrous Metals1.a MO-BAR Universal Primers1.b QD QUICK DRY Metal Primers1.c FD FAST DRY Metal Primers1.d Miscellaneous Specialty Items

Section 2 - Waterborne Metal Primers2.a Waterborne Acrylic Metal Primers2.b Waterborne Alkyd Metal Primers2.c Waterborne Epoxy Metal Primers

Section 3 - Zinc Rich Metal Primers3.a Inorganic Zinc-Rich Primers3.b Organic Zinc-Rich Epoxy Primers

Section 4 - Epoxy Primers for Ferrous Metals4.a MoPoxY Catalyzed Epoxy Metal Primers4.b MoPoxY DTM Primers & Intermediate Coats

Section 5 - Coal Tar Epoxies5.a MO-TAR Coal Tar Epoxy

2



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

FERROUS METAL PRIMER GUIDE

This Guide is intended to show a representative selection of the Ferrous Metal Primers and Shop Coats formulated byMobile Paints. In addition, we offer an extensive selection of products for OEM, Federal Specification and Navy Formulas,product finishes, and private labels. Please contact our home office for your specific requirements.

Section 1 ALKYD PRIMERS FOR FERROUS METALS

1.a MOBAR UNIVERSAL PRIMER

MO-BAR Universal Primer: A high-quality, quick-drying phenolic-modified alkyd universal anticorrosive primer or shopcoat. Use as barrier coat to prevent lifting of existing solvent-sensitive coatings by high performance top coats. Excellentprotection against corrosion in mild industrial and marine environments. Recoat time between 1 and 4 hours except underhigh performance top coats when longer cure may be required.

Product Item Description VOC DFT Sq Ft Dry Time:Code Mils Gallon ToTouch To Handle To Recoat

28-DR-164 MO-BAR 3.5 VOC Universal Primer, LCF, Red 3.40 1.5 535 15 min 1 hr 3 hrs

28-DH-93 MO-BAR PM-III Univeral Primer, LCF, Gray 3.49 2 387 10 min 20 min 4 hrs28-DR-160 MO-BAR PM-III Universal Primer, LCF, Red 3.49 2 387 10 min 20 min 4 hrs

28-DH-95 MO-BAR PM-II Universal Primer, Gray 4.30 1.5 393 15 min 1 hr 3 hrs28-DR-145 MO-BAR PM-II Universal Primer, Red 4.30 1.5 393 15 min 1 hr 3 hrs28-DW-13 MO-BAR PM-II Universal Primer, White 4.30 1.5 393 15 min 1 hr 3 hrs

28-DH-37 MO-BAR Universal Primer, Gray 4.50 1.5 382 5 min 15 min 1 hr28-DR-105 MO-BAR Universal Primer, Red 4.50 1.5 382 5min 15 min 1 hr28-DW-12 MO-BAR Universal Primer, White 4.50 1.5 382 5 min 15 min 1 hr

28-DH-83 MO-BAR Universal Primer, LCF, Gray 4.50 1.5 379 5 min 15 min 1 hr28-DR-154 MO-BAR Universal Primer, LCF, Red 4.50 1.5 379 5 min 15 min 1 hr

3



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

1.b QD QUICK DRY METAL PRIMERS

QD QUICK-DRY: Modified alkyd anticorrosive primers for service as primer or shopcoat. Excellent protection againstcorrosion in mild industrial and marine environments. Very fast dry time allows short recoat period between 1 to 4hours.Product Item Description VOC DFT Sq Ft Dry Time:Code Mils Gallon ToTouch To Handle ToRecoat

28-DH-97 HS Hi-Solids Primer, LCF, Gray 2.95 2 375 15 min 1 hr 3 hrs

28-DH-117 HS High Solids Primer, LCF, Gray 3.10 1 372 10 min 1 hr 4 hrs

28-DH-84 SPEED PRIME 10 QD Primer, LCF, Gray 3.50 1 522 15 min 30 min 1 hr

28-DH-75 QD-58 Quick Dry LCF Primer, Gray 4.15 2 320 10 min 30 min 1 hr28-DR-134 QD-58 Quick Dry LCF Primer, Red 4.15 2 320 10 min 30 min 1 hr

28-DH-64 QD-Lead Free Primer, LCF, Blue Gray 4.20 2 319 10 min 30 min 1 hr

28-DR-126 Fast Dry Primer, LCF, Red 4.25 1.5 400 30 min 1 hr 2 hrs

28-DH-73 SPEED PRIME II Zinc Chromate, Gray 4.29 1.5 349 15 min 30 min 4 hrs28-DR-127 SPEED PRIME II Zinc Chromate, Red 4.29 1.5 349 15 min 30 min 4 hrs

1.c FD FAST DRY METAL PRIMERS

FD FAST-DRY: Modified alkyd anticorrosive primers or shopcoats. Offer excellent protection against corrosion in mildindustrial and marine environments. Average recoat time of 8 to 24 hours.


28-DH-74 SPEED PRIME HS High Solids ZC, Gray 2.56 2 482 30 min 2 hrs 12 hrs28-DR-136 SPEED PRIME HS High Solids ZC, Red 2.56 2 482 30 min 2 hrs 12 hrs

28-DR-166 SPEED PRIME HS LCF Red Primer 2.70 2 461 30 min 2 hrs 12 hrs

28-DH-97 High Solids LCF Primer, Gray 2.95 2 375 30 min 2 hrs 12 hrs

28-DR-147 High Solids LCF Red Oxide 3.25 2 417 30 min 1 hr 8 hrs

10-5 RUS-KIL Rust Inhibiting Primer, LCF, White 3.35 2 395 2 hrs 4 hrs 24 hrs10-9 RUS-KIL Rust Inhibiting Primer, LCF, Gray 3.35 2 395 2 hrs 4 hrs 24 hrs10-10 RUS-KIL Rust Inhibiting Primer, LCF, Red 3.35 2 395 2 hrs 4 hrs 24 hrs

521-5 QD-521 Quick Dry Primer, White 3.50 1.5 556 1 hr 4 hrs 12 hrs521-8 QD-521 Quick Dry Primer, Gray 3.50 1.5 556 1 hr 4 hrs 12 hrs521-10 QD-521 Quick Dry Primer, Red 3.50 1.5 556 1 hr 4 hrs 12 hrs

9-78 SPEED PRIME Red Oxide Primer, LCF 3.76 1.5 447 45 min 2 hrs 8 hrs

520-8 QD-520 Quick Dry Primer, Gray (OEM) 3.91 1.5 450 1 hr 2 hr 8 hrs520-10 QD-520 Quick Dry Primer, Red (OEM) 3.91 1.5 450 1 hr 2 hr 8 hrs520-5 QD-520 Quick Dry Primer, White (OEM) 4.31 1.5 389 1 hr 2 hr 8 hrs

4



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

1.d MISCELLANEOUS SPECIALTY ITEMS


80439 DOD-P-21035B Galvanizing Repair 2.46 2 532 30 min 8 hrs max 8 hrs

409-68 Jack Tar Phenolic A/C ZC Primer, Brown 2.81 6 310 20 min 3 hrs 16 hrs

10-7 RUS-KIL Brite Galvanizing Coating 4.17 1 666 15 min 45 min 3 hrs10-8 RUS-KIL Cold Galvanizing Coating 4.13 1 666 15 min 45 min 3 hrs

80242 TT-P-645B Zinc Molybdate Yellow (LCF) 2.83 1.5 595 4 - 6 hrs 6 - 8 hrs

9-42 VINYL Wash Primer 6.04 0.5 252 5 min 15 min 30 min

Section 2 WATERBORNE METAL PRIMERS

2.a WATERBORNE ACRYLIC METAL PRIMERS

High performance, water-reducible acrylic latex corrosion-inhibiting primers for ferrous metal, galvanized metal, andaluminum. Excellent adhesion, flexibility, blister resistance and mild chemical resistance. Excellent protection in mildindustrial and marine exposures. Use as primer or shop coat. Lead-free, chromate-free, mercury-free, low VOC.


310-6 H2O RUS-KIL Primer, LCF, White 1.14 2 345 1 hr 4 hrs 4 hrs310-8 H2O RUS-KIL Primer, LCF, Gray 1.14 2 345 1 hr 4 hrs 4 hrs310-9 H2O RUS-KIL Primer, LCF, Red 1.14 2 345 1 hr 4 hrs 4 hrs

55-DH-2 W/R ACRYLIC Metal Primer, LCF, Light Gray 1.39 2 341 30 min 1 hr 2 hrs

55-DR-9 W/R ACRYLIC Metal Primer, LCF, Red 1.61 1 602 30 min 1 hr 2 hrs

2.b WATERBORNE ALKYD METAL PRIMERS

Manufactured to special order. Please contact your BLP Mobile Paints Sales Representative for particulars

5



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

2.c WATERBORNE EPOXY METAL PRIMERS


69-DR-1 MOPOXY H2O Epoxy Primer, LCF, Red 0.89 3 257 2 hrs 6 hrs 24 hrs

Section 3 ZINC RICH PRIMERS

3.a INORGANIC ZINC RICH PRIMERS

INORGANIC ZINC RICH PRIMERS offer excellent galvanic protection from corrosion in moderate to severe industrialand marine environments. Excellent resistance to fresh and salt water, detergents and most chemicals.Very good resistanceto most organic solvents. May require topcoating with epoxy or polyurethane for maximum chemical resistance. Heatresistant to 750 degrees Fahrenheit.


28-DH-50 MO-ZINC #3 Inorganic Zinc 3.88 3 342 1 hr 2 hrs 24 hrs

28-DH-86 MO-ZINC HS-15 Inorganic Zinc 3.40 3 380 1 hr 2 hrs 24 hrs

3.b ORGANIC ZINC RICH EPOXY PRIMERS

ORGANIC ZINC RICH EPOXY PRIMERS offer excellent galvanic protection from corrosion in moderate to severe industrialand marine environments. Excellent resistance to fresh and salt water, detergents and most chemicals. Very good resistanceto most organic solvents. Superior primer for use with high performance epoxy or polyurethane topcoats.


40-CM-2 MOPOXY ZR Epoxy Zinc Rich Primer 3.45 2.5 321 1 hr 4 hrs 18 hrs

40-CM-4 MOPOXY ZR Epoxy Zinc Rich Primer 3.89 3.5 257 30 min 1 hr 2 hrs

40-DH-6 MIL-DTL-24441 F 159 Zinc Rich Primer 2.50 3 336 2 hrs 8 hrs 12 hrs

6



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

Section 4 EPOXY PRIMERS FOR FERROUS METALS

4.a MoPoxY CATALYZED EPOXY PRIMERS

MOPOXY Catalyzed Epoxy Primers offer excellent protection in moderate to severe industrial and marine environments.Excellent resistance to fresh and salt water, detergents and most chemicals. Very good resistance to fumes and spillageof most organic solvents, acids and alkalis. Specialized formulations available for specific services. Recommended primersunder epoxy and polyurethane top coats.


613-10 MOPOXY HS High Solids Primer, LCF, Red 2.10 3 374 3 hrs 8 hrs 24 hrs

40-DR-5 MOPOXY HB High Build Metal Primer, Red 3.49 6 131 2 hrs 8 hrs 24 hrs

513-10 MOPOXY Epoxy Metal Primer, Red 4.24 2 322 2 hrs 8 hrs 24 hrs

40-DN-4 MOPOXY Primer, Yellow, MIL-P-23377 4.96 2 224 30 min 1 hr 2 hrs

40-DR-12 MOPOXY PCP Preconstruction Primer (LCF) 5.25 1 602 2 min 5 min 1 hr

4.b MOPOXY DTM PRIMERS & INTERMEDIATE COATS

MOPOXY DTM Direct to Metal Primers offer excellent corrosion protection for steel surfaces where abrasive blasting is notfeasible and for upgrading existing coating systems to high performance epoxy / polyurethane topcoats. Specialized formulationsoffer excellent recoatability, adhesion to damp surfaces, and other special advantages.41-AF-2, MOPOXY Pre-Prep Sealer, isa 100% solids water-thin penetrating sealer formulated for areas where zero surface preparation is possible. Penetrates chalkingand scaling paint, rust, and other contaminants to form a solid film which can be finished with a high performance epoxy-masticpolyurethane system.


41-AF-2 MOPOXY PRE-PREP Sealer, Clear 0.00 1 1604 48 hrs hard 24 hrs

40-AH-51 MOPOXY MASTIC, LCF, Gray 1.30 6 217 3 hrs 8 hrs 24 hrs40-AR-19 MOPOXY MASTIC, LCF, Red 1.30 6 217 3 hrs 8 hrs 24 hrs40-AW-32 MOPOXY MASTIC, LCF, White 1.30 6 217 3 hrs 8 hrs 24 hrs

40-AY-2 MOPOXY MASTIC, Aluminum 1.50 6 248 3 hrs 8 hrs 24 hrs

41-BK-14 MOPOXY IR Indefinate Recoat, LCF, Buff 2.29 8 136 1 hr 5 hrs 12 hrs

41-BH-3 MOPOXY ST HS LCF, Gray 2.36 8 131 16 hrs hard 5 hrs41-BK-1 MOPOXY ST HS LCF, Buff 2.36 8 131 16 hrs hard 5 hrs

41-CH-1 MOPOXY PLUS, LCF, Gray 2.36 8 131 9 hrs hard 4 hrs41-CW-1 MOPOXY PLUS, LCF, White 2.36 8 131 9 hrs hard 4 hrs

7



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

Section 5 COAL TAR EPOXIES

5.a MO-TAR COAL TAR EPOXY

MO-TAR is a heavy-duty, chemical and corrosion resistant with excellent chemical and abrasion resistance in severe industrial &marine service. For steel and masonry surfaces. Excellent resistance to fresh and salt water, solvents, petroleum products, acidsand alkalis. Excellent for underground and immersion service. All formulations are Lead-free and Chromate-Free.


40-BX-6 MO-TAR HB-90 High Build Epoxy, Black 1.13 20 67 8 hrs 16 hrs 16 hrs

40-AR-16 MO-TAR C-200 Polyamide Epoxy, Red 1.56 8 157 4 hrs 6 hrs 6 hrs40-AX-7 MO-TAR C-200 Polyamide Epoxy, Black 1.56 8 157 4 hrs 6 hrs 6 hrs

1

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Galvanized Metals & Aluminum Systems

RECOMMENDED PAINTING SPECIFICATIONSFOR GALVANIZED METALS & ALUMINUM


This section covers hot dip galvanized structural steel and steel plate, roof decking and piping, and aluminum surfaces, ininterior and exterior service at ambient temperatures. Not intended for immersion service.

Many paints are not compatible with zinc and require the application of vinyl wash primer as a pretreatment or of an acrylicprimer to guarantee adhesion of coating systems to the zinc, as indicated in each system.

Aluminum is included in this section because it also requires the use of vinyl wash primer or of an acrylic primer to promoteadhesion.Inorganic zinc is not included in this section because it normally does not require application of vinyl wash primer fortopcoat adhesion. See FERROUS METALS for application details.Vinyl wash primer contains zinc chromate. All other products are lead, chromate and mercury-free.

SURFACE PREPARATION

Galvanized steel sheet and pipe are customarily coated with oil to prevent galvanic action while stacked. This oil must beremoved prior to painting. Solvent Cleaning, SSPC-SP 1, is the preferred method of removing oil and grease.

Aluminum may be cleaned and etched with a Phosphoric acid based cleaner to promote coating adhesion.

Surface preparation will be the same for all systems.

Alternate Primers: Code Description VOC Sq. Ft. Mils

6-6 WEATHER-TITE 100% Acrylic Primer 1.17 393 2.009-5 GALVA-TEC Acrylic Primer 0.90 317 1.509-42 Vinyl Wash Primer 5.72 314 0.5080439A&B MIL-P-21035 Cold Galvanize Repair 2.46 532 2.0010-7 RUS-KIL Brite Galvanizing Coating 4.17 666 1.0010-8 RUS-KIL Cold Galvanizing Coating 4.13 666 1.00310-9 H2O RUS-KIL Acrylic DTM Primer 1.14 345 2.0040-DN-4 MOPOXY Primer Yellow MIL-P-23377d 4.96 224 2.00

2

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



SECTION 01 ALKYD SYSTEMS FOR GALVANIZED & ALUMINUM

01 ALKYD SYSTEMS offer good protection against normal weathering, mild chemical fumes and normal abrasion.Least expensive, easiest surface preparation and application, shortest service life. Available in a wide range of colors.Not suitable for immersion service. Vinyl wash primer or acrylic metal primer required for adhesion. See above for AlternatePrimers.

All systems are VOC compliant. All are for interior and exterior service except as noted.

Surface Preparation: Solvent Clean, SSPC-SP1 to remove grease or oil.

Application: Brush, Roller, Airless or Conventional Spray.

01.A Alkyd System, High Gloss, Residential, Commercial & Industrial Service

Coat Product High Gloss Enamel Finish VOC Sq. Ft. Mils

Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 10-Series RUS-KIL Gloss Enamel 3.35 385 2.00Finish 10-Series RUS-KIL Gloss Enamel 3.35 385 2.00

Total Dry Mils 4.50

01.B Alkyd System, High Gloss, Residential, Commercial, & Industrial Service

Coat Product Alkyd Semi-Gloss Enamel Finish VOC Sq. Ft. Mils

Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 30-Series NAM-A-LAC Non-Toxic Enamel 3.18 314 1.50Finish 30-Series NAM-A-LAC Non-Toxic Enamel 3.18 314 1.50

Total Dry Mils 3.50

01.C Alkyd System, Semigloss, Residential, Commercial, & Light Industrial Service

Coat Product High Gloss Enamel Finish VOC Sq. Ft. Mils

Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 135-Series COVENTRY Lustarite Satin-Gloss 3.04 427 2.00Finish 135-Series COVENTRY Lustarite Satin-Gloss 3.04 427 2.00

Total Dry Mils 4.50

3

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



01.D Alkyd System, Spray Fog-Dry, Flat, Interior, Commercial & Industrial Service

Coat Product Sweep-Dry Flat Enamel Finish VOC Sq Ft Mils

Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 6-DW-58* SPRAY FOG-DRY Flat White 3.17 407 2.00Finish 6-DW-58* SPRAY FOG-DRY Flat White 3.17 407 2.00* Apply by airless spray

Total Dry Mils 4.50

01.E Alkyd System, Spray Fog Dry, Semi-Gloss, Interior, Commercial & Industrial Service

Coat Product Sweep-Dry Semi-Gloss Enamel Finish VOC Sq Ft Mils

Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 61-BW-2* SPRAY FOG-DRY Semi-Gloss White 3.25 382 2.00Finish 61-BW-2* SPRAY FOG-DRY Semi-Gloss White 3.25 382 2.00* Apply by airless spray

Total Dry Mils 4.50

SECTION 02 ACRYLIC LATEX SYSTEMS FOR GALVANIZED & ALUMINUM

02 WATERBORNE ACRYLIC LATEX ENAMELS are the latest development in general-purpose finishes for interiorand exterior service. Easy to apply over a variety of primers and substrates including zinc and galvanized metals. Goodresistance to normal weathering and mild chemical fumes.Not for immersion service. Lead, chromate and mercury free. Low VOC.

Apply directly to zinc or aluminum. No pretreatment required. Acrylic latex primer optional.

Surface Preparation: Solvent Clean, SSPC-SP 1, to remove oil or grease.Application: Brush, Roller, Airless or Conventional Spray

02.A Acrylic Latex System, High-Gloss, Residential to Light Industrial Service

Coat Product High Gloss Acrylic Finish VOC Sq. Ft. Mils

Prime* 310-9 H2O RUS-KIL Acrylic Metal Primer 1.14 345 2.00Intermediate 310-Series H2O RUS-KIL Acrylic DTM Finish 1.09 295 2.00Finish 310-Series H2O RUS-KIL Acrylic DTM Finish 1.09 295 2.00*Corrosion-resistant primer optional

Total Dry Mils 6.00

4

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



02.B Acrylic Latex DTM System, High-Gloss, Residential to Light Industrial Service

Coat Product High Gloss DTM Acrylic Finish VOC Sq. Ft. Mils

Prime* 310-9 H2O RUS-KIL Acrylic DTM Metal Primer 1.14 345 2.00Intermediate 330-Series ACR-A-LAC 100% Acrylic Gloss 2.11 293 2.00Finish 330-Series ACR-A-LAC 100% Acrylic Gloss 2.11 293 2.00*Corrosion-resistant primer optional

Total Dry Mils 6.00

02.C Acrylic Latex System, Exterior, Gloss, Residential to Light Industrial Service

Coat Product Gloss Acrylic Finish VOC Sq. Ft. Mils

Prime 6-6 WEATHER-TITE Universal Primer 1.17 393 1.50Intermediate 140-Series WEATHER-TITE 100% Acrylic Gloss 1.99 296 2.00Finish 140-Series WEATHER-TITE 100% Acrylic Gloss 1.99 296 2.00

Total Dry Mils 5.50

02.D Acrylic Latex System, Exterior, Satin Gloss, Residential to Light Industrial Service

Coat Product Satin-Gloss Acrylic Finish VOC Sq. Ft. Mils

Prime 6-6 WEATHER-TITE Universal Primer 1.17 393 1.50Intermediate 240-Series WEATHER-TITE 100% Acrylic Satin 2.19 271 2.00Finish 240-Series WEATHER-TITE 100% Acrylic Satin 2.19 271 2.00

Total Dry Mils 5.50

02.E Acrylic Latex System, Exterior, Flat, Residential to Light Industrial Service

Coat Product Flat Acrylic Finish VOC Sq. Ft. Mils

Prime 6-6 WEATHER-TITE Universal Primer 1.17 393 1.50Intermediate 40-Series WEATHER-TITE 100% Acrylic Flat 1.03 291 2.00Finish 40-Series WEATHER-TITE 100% Acrylic Flat 1.03 291 2.00

Total Dry Mils 5.50

5

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



02.F Vinyl Latex System, Interior, Flat, Residential to Light Industrial Service

Coat Product Flat Latex Finish VOC Sq. Ft. Mils

Prime* 310-9 H2O RUS-KIL Acrylic DTM Metal Primer 1.14 345 2.00Intermediate 35-Series COVENTRY Interior Latex Flat 0.83 375 1.50Finish 35-Series COVENTRY Interior Latex Flat 0.83 375 1.50*Corrosion-resistant primer optional

Total Dry Mils 5.00

02.G Acrylic Latex System, Interior, Semi-Gloss, Residential to Light Industrial Service

Coat Product Semi-Gloss Acrylic Finish VOC Sq. Ft. Mils

Prime* 310-9 H2O RUS-KIL Acrylic DTM Metal Primer 1.14 345 2.00Intermediate 1335-Series COVENTRY Latex Semi-Gloss 2.00 345 1.50Finish 1335-Series COVENTRY Latex Semi-Gloss 2.00 345 1.50*Corrosion-resistant primer optional

Total Dry Mils 5.00

02.H Acrylic Latex System, Interior, Eggshell, Residential to Light Industrial Service

Coat Product Eggshell Acrylic Finish VOC Sq. Ft. Mils

Prime* 310-9 H2O RUS-KIL Acrylic DTM Metal Primer 1.14 345 2.00Intermediate 2335-Series COVENTRY Acrylic Eggshell 0.86 375 1.50Finish 2335-Series COVENTRY Acrylic Eggshell 0.86 375 1.50*Corrosion-resistant primer optional

Total Dry Mils 5.00

02.I Acrylic Latex System, Interior, High Gloss, Residential to Light Industrial Service

Coat Product High Gloss Acrylic Enamel Finish VOC Sq. Ft. Mils

Prime* 310-9 H2O RUS-KIL Acrylic DTM Metal Primer 1.14 345 2.00Intermediate 335-Series COVENTRY Acrylic High Gloss Enamel 1.09 408 1.50Finish 335-Series COVENTRY Acrylic High Gloss Enamel 1.09 408 1.50*Corrosion-resistant primer optional

Total Dry Mils 5.00

6

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



02.J Acrylic Latex System, Interior, Fog-Dry Flat, Commercial & Industrial Service

Coat Product Flat Sweep-Dry Acrylic Finish VOC Sq. Ft. Mils

Prime 310-9 H2O RUS-KIL Acrylic DTM Metal Primer 1.14 345 2.00Intermediate 55-DW-3* SPRAY Fog-Dry Acrylic Flat White 0.80 322 2.00Finish 55-DW-3* SPRAY Fog-Dry Acrylic Flat White 0.80 322 2.00

*Use airless spray

Total Dry Mils 6.00

02.K Acrylic Latex System, Interior, Fog-Dry Gloss, Commercial & Industrial Service

Coat Product Gloss Sweep-Dry Acrylic Finish VOC Sq. Ft. Mils

Prime 310-9 H2O RUS-KIL Acrylic DTM Metal Primer 1.14 345 2.00Intermediate 55-AW-9* SPRAY Fog-Dry Acrylic Gloss White 0.75 289 2.00Finish 55-AW-9* SPRAY Fog-Dry Acrylic Gloss White 0.75 289 2.00

*Use airless spray

Total Dry Mils 6.00

SECTION 03 SILICONE ALKYD SYSTEMS FOR GALVANIZED & ALUMINUM

03 SILICONE ALKYDS offer outstanding gloss and color retention, excellent resistance to industrial and marineenvironments, weathering and ultraviolet exposure, and good resistance to mild chemical fumes. Not for immersionservice. Easy to apply. Lead, chromate and mercury free. VOC compliant.

Vinyl wash primer or acrylic latex metal primer required for adhesion.All systems are VOC Compliant

Surface Preparation: Solvent Clean, SSPC-SP1 to remove grease or oil.

Application: Brush, Roller, Airless or Conventional Spray.

03.A Silicone Alkyd System, High Gloss, Residential, Commercial, Marine & Industrial Service

Coat Product High Gloss Silicone Alkyd Finish VOC Sq. Ft. Mils

Pretreat 9-42 Vinyl Wash Primer 314 0.50Intermediate 432-Series JACK TAR Silicone Yacht Finish 484 1.50Finish 432-Series JACK TAR Silicone Yacht Finish 484 1.50

Total Dry Mils 3.50

7

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



SECTION 04 EPOXY & POLYURETHANE SYSTEMS FOR GALVANIZED & ALUMINUM

04 CATALYZED EPOXY AND POLYURETHANE SYSTEMS offer superior resistance to many chemicals, especiallyalkalis, abrasion, and moisture, together with good resistance to most organic solvents, acid splashes and chemicalfumes.For Commercial, Heavy Industrial and Marine Service at ambient temperatures. We do not recommend galvanized metalfor immersion service because of possible galvanic action.

CATALYZED EPOXIES are excellent for interior use in schools, hospitals, institutions, laundries, kitchens and foodprocessing areas, chemical and pharmaceutical plants, and other industrial and commercial installations where maximumprotection and durability are required. Available in high gloss and semigloss in a wide range of colors for an easily cleanand attractive finish.Waterborne formulations are available.

The following primers are recommended for adhesion:

Code Description VOC Sq. Ft. Mils9-42 Vinyl Wash Primer 5.72 314 0.5040-DN-4 MOPOXY Primer Yellow MIL-P-23377 4.96 224 2.00310-9 H2O RUS-KIL Acrylic DTM Primer 1.14 345 2.00

CATALYZED POLYURETHANES offer good chemical and solvent resistance with outstanding color and gloss retention.Recommended for marine environments, tank farms, pipe racks, chemical plants, and heavy equipment. Not for immersionservice.The following catalyzed polyurethane formulations are available and may be used interchangeably within the suggestedsystem recommendations. Other formulations are available for special service.

Code Description VOC Sq Ft DFT /Gal

72-Series MOTHANE Polyurethane Enamel 4.11 339 2Apply by Airless or Conventional Spray only

72-Series MOTHANE HD (Heavy Duty) Polyurethane 4.11 268 2.5Apply by Airless or Conventional Spray, Brush or Roll

72-Series MOTHANE HS-1000 (High Solids) Polyurethane 2.45 513 2Apply by Airless or Conventional Spray, Brush or Roll

72-Series MOTHANE HS-900 (High Solids) Polyurethane 2.47 417 2.5Apply by Airless or Conventional Spray only

Mobile Paints offers a wide range of epoxies and polyurethanes for special applications. Ask your BLP Mobile Paintrepresentative for detailed recommendations.

Surface Preparation: Solvent Clean, SSPC-SP1, to remove oil and grease

Application: Brush, Roller, Airless or Conventional Spray unlessotherwise indicated.

8

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



04.A Catalyzed Waterborne Acrylic Epoxy System, Commercial & Industrial Service

Coat Product High Gloss W/B Catalyzed Acrylic VOC Sq. Ft. Mils

Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 69-AW-5 MOPOXY H2O-100 W/B Acrylic Epoxy 1.71 313 2.00Finish 69-AW-5 MOPOXY H2O-100 W/B Acrylic Epoxy 1.71 313 2.00

Total Dry Mils 4.50

04.B Catalyzed Waterborne Amide Epoxy System, Commercial & Industrial Service

Coat Product Semi-Gloss W/B Amide Epoxy Finish VOC Sq. Ft. Mils

Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 69-AW-6 MOPOXY H2O-200 W/B Amide Epoxy 1.00 225 2.00Finish 69-AW-6 MOPOXY H2O-200 W/B Amide Epoxy 1.00 225 2.00

Total Dry Mils 4.50

04.C Catalyzed Epoxy System, Commercial & Industrial Service

Coat Product High Gloss Epoxy Finish VOC Sq. Ft. Mils

Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 513-Series MOPOXY High Gloss Epoxy 4.30 314 2.00Finish 513-Series MOPOXY High Gloss Epoxy 4.30 314 2.00

Total Dry Mils 4.50

04.D Catalyzed Epoxy System, Commercial & Industrial Service

Coat Product High Solids Semi-Gloss Epoxy Finish VOC Sq. Ft. Mils

Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 613-Series MOPOXY HS High Solids S/G Epoxy 2.00 374 3.00Finish 613-Series MOPOXY HS High Solids S/G Epoxy 2.00 374 3.00

Total Dry Mils 6.50

9

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



04.E Catalyzed Epoxy Mastic /Epoxy System, Heavy Industrial & Marine Service

Coat Product High Solids Semi-Gloss Epoxy Finish VOC Sq. Ft. Mils

Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 40-AW-32 MOPOXY MASTIC White 1.30 217 6.00Finish 613-Series MOPOXY HS High Solids Epoxy 2.00 374 3.00Finish 613-Series MOPOXY HS High Solids Epoxy 2.00 374 3.00

Total Dry Mils 12.50

04.F Catalyzed Epoxy Mastic /Acrylic Epoxy System, Heavy Industrial & Marine Service

Coat Product High Gloss Acrylic Epoxy Finish VOC Sq. Ft. Mils

Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 40-AW-32 MOPOXY Mastic, White 1.30 217 6.00Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2.00Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2.00


04.G Catalyzed Epoxy Mastic /Polyurethane System, Heavy Industrial & Marine Service

Coat Product High Solids Gloss Polyurethane Finish VOC Sq. Ft. Mils

Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 40-AW-32 MOPOXY Mastic, White 1.30 217 6.00Finish 72-Series MOTHANE HD Polyurethane 4.11 268 2.50Finish 72-Series MOTHANE HD Polyurethane 4.11 268 2.50


04.H Catalyzed DTM Epoxy /Polyurethane System, Heavy Industrial & Marine Service

Coat Product High Gloss Polyurethane Finish VOC Sq. Ft. Mils

Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 41-CW-1 MOPOXY-PLUS DTM Epoxy 2.36 131 6.00Finish 72-AW-26 MOTHANE HS-1000 Polyurethane 2.45 268 2.00Finish 72-AW-6 MOTHANE HS-1000 Polyurethane 2.45 268 2.00


10

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



04.I Catalyzed DTM Epoxy /Acrylic Epoxy System, Heavy Industrial & Marine Service


Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 41-CW-1 MOPOXY-PLUS DTM Epoxy 2.36 131 6.00Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2.00Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2.00


04.J Recoatable Epoxy / Polyurethane System, Heavy Industrial & Marine Service


Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 41-BK-14 MOPOXY IR High Solids Epoxy Buff 2.29 136 8.00Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2.00Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2.00


04.K Recoatable Epoxy / Acrylic Epoxy System, Heavy Industrial & Marine Service


Pretreat 9-42 Vinyl Wash Primer 5.72 314 0.50Intermediate 41-BK-14 MOPOXY IR High Solids Epoxy Buff 2.29 136 8.00Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2.00Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2.00


11

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



SECTION 05 - MAINTENANCE UPGRADE SYSTEMS:

05 FOR UPGRADING deteriorated alkyd, silicone alkyd and acrylic finishes and repairing catalyzed epoxy andpolyurethane systems where removal of existing coatings is not possible.

MOPOXY MASTIC Aluminum is a very high solids, low VOC, surface tolerant high performance epoxy coating offeringexcellent protection in moderate to severe industrial and marine environments. DTM or use as base coating over soundrust and /or previous paint for upgrading to high performance topcoats.

MOPOXY MASTIC is a high-solids, high-build, surface tolerant amine epoxy formulated for application over sound rustand/or previous paint systems as a base coat for upgrading to high performance coatings such as acrylic epoxies andpolyurethanes.

MOPOXY IR , Indefinite Recoatability Epoxy, is a high-solids, surface-tolerant, high-build polyamide coating which maybe applied to damp, rusty surfaces, allowed to dry for prolonged periods, then topcoated with other epoxies or polyurethaneswithout loss of intercoat adhesion. Good anticorrosive properties.

MOPOXY PLUS is a high-performance high-solids DTM polyamide epoxy with excellent adhesion to tight rust, good adhesionto damp surfaces, and cures at low temperatures. Excellent resistance to fresh and salt water, detergents and corrosivechemicals. Very good resistance to fumes and spills of most organic solvents, acids and alkalis.

MOPOXY PRE-PREP is a 100% solids epoxy with very low viscosity and excellent substrate wetting properties. Excellentfor badly rusted areas where sandblasting and removal of existing coatings is not possible and only minimal cleaning ispossible. Penetrates and bonds rust and deteriorated coatings into a solid film which seals out moisture and oxygen.

Allow to cure for 24 hours, then apply recommended intermediate coat while still slightly soft. Will accept a wide variety ofcoatings.

MO-BAR Universal Primer is a high-quality, quick-drying modified alkyd anticorrosive primer or shop coat. Use as a barriercoat to prevent lifting of solvent-sensitive coatings by high performance top coats. Excellent protection against corrosion inmild industrial and marine environments.

All systems recommended are suitable for heavy industrial and marine service.

Surface Preparation: Pressure Wash (3,000 psi or better) to remove contaminationSolvent Clean, SSPC-SP 1, to remove oil and greasePower Tool Clean, SSPC-SP 2, preferredHand Tool Clean, SSPC-SP 3, minimum recommended

Application: Brush, roller or airless or conventional spray.

12

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



05.A Epoxy Mastic / High Solids Polyurethane System


Spot Prime 40-AY-2 MOPOXY MASTIC, Aluminum 0.51 248 6Prime 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 72-Series MOTHANE HD Polyurethane 4.11 2.68 2.5Finish 72-Series MOTHANE HD Polyurethane 4.11 2.68 2.5

Total Dry Mils 17.0

05.B Epoxy Mastic / Acrylic Epoxy System


Spot Prime 40-AY-2 MOPOXY MASTIC, Aluminum 0.51 248 6Prime 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 16.0

05.C IR Epoxy / High Solids Polyurethane System


Spot Prime 41-BK-14 MOPOXY IR High Solids Epoxy Buff 2.29 136 8Prime 41-BK-14 MOPOXY IR High Solids Epoxy Buff 2.29 136 8Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 20.0

05.D IR Epoxy / Acrylic Epoxy System


Spot Prime 41-BK-14 MOPOXY IR High Solids Epoxy Buff 2.29 136 8Prime 41-BK-14 MOPOXY IR High Solids Epoxy Buff 2.29 136 8Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 20.0

13

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



05-E Low Viscosity Epoxy / Epoxy Mastic / High Solids Polyurethane System


Prime 41-AF-2 MOPOXY PrePrep Clear 0.00 1069 1.5Intermediate 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 11.5

05-F Low Viscosity Epoxy / Epoxy Mastic / Acrylic Epoxy System


Prime 41-AF-2 MOPOXY PrePrep Clear 0.00 1069 1.5Intermediate 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 11.5

05-G Universal Primer / Epoxy Mastic / High Solids Polyurethane System


Prime 28-DR-160 MO-BAR PM-III Universal Primer 3.49 393 1.5Intermediate 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 11.5

05-H Universal Primer / Epoxy Mastic / Acrylic Epoxy System


Prime 28-DR-160 MO-BAR PM-III Universal Primer 3.49 393 1.5Intermediate 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 11.5

High Temperature Paint Systems for Ferrous Metals1

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

RECOMMENDED PAINTING SPECIFICATIONS FOR FERROUS METALS AT HIGH TEMPERATURES

For Non-Immersion Service Only

PART IINTRODUCTION

Surface Preparation and Temperature Ranges for Paints

Part IIINDEX OF COATING SYSTEMS

Detailed Index of Coating Systems

Part IIICOATING SYSTEMS

Recommended Primers, Intermediate Coats

Finish Coats, Dry Film Thickness and Coverage

SUMMARY INDEX01 - Steel Surfaces - up to 200O F, Constant02 - Steel Surfaces - up to 300O F, Constant03 - Steel Surfaces - up to 500O F, Constant04 - Steel Surfaces - up to 500O F Constant, 800O F Intermittent05 - Steel Surfaces - up to 800O F Constant, 1000O F Intermittent



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


PART IINTRODUCTION

This section covers ferrous metals, including structural steel, chimneys, exteriors of storage tanks and silos, tubing and pipes,boilers, compressors, reactors, generators, heat exchangers and similar equipment for non-immersion service at elevated tempera-tures.

Proper surface preparation is essential to the life of any coating system. Sandblasting is the preferred method of removing rust andmill scale on new steel and old paint, rust, and similar contaminants on previously painted steel prior to coating. In addition tocleaning the surface, sandblasting cuts the steel to provide an anchor pattern which assures good adhesion of the primer to thesubstrate.

Solvent clean to remove grease, oil and similar contaminants which cannot be removed successfully with abrasive blast cleaning.

The Society for Protective Coatings, formerly the Steel Structures Painting Council is the recognized authority on surface prepara-tion and painting procedures for steel and reference is made to their standards as follows:


See Section 3, SSPC, for detailed descriptions of the above standards.

Commercial Blast cleaning should be considered the minimum acceptable surface preparation when specifying paint systems forservice at elevated temperatures.

Wet sandblasting is becoming more common because of stringent EPA requirements, requiring new techniques and the use ofadditives to the blasting water to prevent immediate rust bloom. Consult your BLP Mobile Paint representative for equipment andadditive recommendations.


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


PART IINTRODUCTION (continued)

MAXIMUM OPERATING TEMPERATURES FOR PAINTS

Zinc melts at 780 degrees Fahrenheit. Aluminum melts at 1,220 degrees. Steel turns red at 1,000 degrees and melts at 1,535degrees.

Paints oxidize at accelerated rates as the temperature increases. Because of the importance of determining the exact temperaturerange required, it is recommended that surface temperatures be verified with an accurate thermometer. Please call your nearestBLP Mobile Paint representative for assistance.

The following guide is conservative and for non-immersion service only. Temperatures are shown in degrees Fahrenheit.

ProductProduct Description Code Constant Intermittent

Vinyl, Solvent Thinned 160 180

Chlorinated Rubber 160 180

Phenolic, Non-Catalyzed 190 180

Alkyd Enamels 275 300

Acrylic Latex Gloss Enamels 200 250

Epoxies, Catalyzed 200 250

Epoxy-Phenolic, Catalyzed 200 250

Polyurethane, Catalyzed 200 250

Silicone Alkyd Primer 28-DR-79 375 400

Silicone Alkyd Enamel 432-Line 300 400

Silicone Alkyd Aluminum 11-61 500 600

Inorganic Zinc 28-DH-50 600 750

HR Silicone Acrylic Aluminum 62-AY-5 800 1,000

Silicone Hi-Heat Aluminum 62-AY-1 1,000 1,200


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

01 - Steel Surfaces - up to 200O F, Constant

01.A Inorganic Zinc/Epoxy/Polyurethane System for Heavy Industrial Service01.B Zinc Rich Epoxy/Epoxy/Polyurethane System for Heavy Industrial Service01.C Inorganic Zinc/Modified Acrylic Latex System for Light Industrial Service01.D Alkyd/Silicone Alkyd System for Residential, Marine and Light Industrial Service01.E Acrylic Latex DTM System for Residential to Light Industrial Service


02.A Silicone Alkyd System for Heavy Industrial Service


03.A Silicone Alkyd Aluminum for Heavy Industrial Service

04 - Steel Surfaces - up to 500O F Constant, 800O F Intermittent

04.A Heat Resitant - Silcone Acrylic Aluminum for Heavy Industrial Service

05 - Steel Surfaces - up to 800O F Constant, 1000O F Intermittent

05.A Silicone Acrylic Aluminum for Heavy Industrial Service




251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

01 STEEL SURFACES, AMBIENT TEMPERATURE UP TO 200 F CONSTANT

01.A Inorganic Zinc/Epoxy/Polyurethane System for maximum protection

Coat Product VOC Sq Ft Mils

Shop Prime 28-DH-50 MO-ZINC #3 Inorganic Zinc 3.88 342 3Intermediate 40-AW-32 MOPOXY MASTIC, White 1.3 217 6Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 13.0

01.B Zinc Rich Epoxy/Epoxy/Polyurethane System for maximum protection


Prime 40-CM-2 MOPOXY ZR Zinc Rich Primer 3.45 321 2.5Intermediate 40-AW-32 MOPOXY MASTIC, White 1.3 217 6Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 12.5

01.C Inorganic Zinc/Modified Acrylic Latex DTM System for superior protection


Shop Prime 28-DH-50 MO-ZINC #3 Inorganic Zinc 3.88 342 3Finish 310-Series H2O RUS-KIL® DTM Acrylic Enamel 1.09 295 2Finish 310-Series H2O RUS-KIL® DTM Acrylic Enamel 1.09 295 2

Total Dry Mils 7.0


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

01.D Alkyd/Silicone Alkyd System for superior gloss and color retention

Coat Product High Gloss VOC Sq Ft Mils

Shop 28-DR-160 MO-BAR PM-III Universal Primer 3.49 387 2Prime 28-DR-160 MO-BAR PM-III Universal Primer 3.49 387 2Intermediate 432-Series JACK TAR® Silicone Yacht Finish 3.57 484 1.5Finish 432-Series JACK TAR® Silicone Yacht Finish 3.57 484 1.5

Total Dry Mils 7.0

01.E Acrylic Latex DTM System, High Gloss, for light industrial service


Shop 310-9 H2O RUS-KIL® Acrylic Metal Primer 1.14 345 2Prime 310-9 H2O RUS-KIL® Acrylic Metal Primer 1.14 345 2Intermediate 310-Series H2O RUS-KIL® Acrylic DTM Enamel 1.09 295 2Finish 310-Series H2O RUS-KIL® Acrylic DTM Enamel 1.09 295 2

Total Dry Mils 8.0

02 STEEL SURFACES UP TO 300o F CONSTANT

02.A Silicone Alkyd System for good corrosion resistance, excellent gloss retention


Shop 28-DR-79 Silicone Alkyd Primer 3.76 449 1.5Prime 28-DR-79 Silicone Alkyd Primer 3.76 449 1.5Intermediate 432-Series JACK TAR® Silicone Yacht Finish 3.57 484 1.5Finish 432-Series JACK TAR® Silicone Yacht Finish 3.57 484 1.5

Total Dry Mils 6.0


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

03 STEEL SURFACES UP TO 500o F CONSTANT

03.A Silicone Alkyd Aluminum for good corrosion resistance, excellent gloss retention

Coat Product VOC Sq Ft MilsPrime 11-61 HR Silicone Alkyd Aluminum 4.61 450 1Finish 11-61 HR Silicone Alkyd Aluminum 4.61 450 1

Total Dry Mils 2.0

04 STEEL SURFACES UP TO 500o F CONSTANT, 800o F INTERMITTENT

04.A Silicone Acrylic Aluminum for good corrosion resistance, gloss retention


Prime 62-AY-5 HR Silicone Acrylic Aluminum 4.34 427 1.5Finish 62-AY-5 HR Silicone Acrylic Aluminum 4.34 427 1.5

Total Dry Mils 3.0

05 STEEL SURFACES UP TO 800o F CONSTANT, 1,000o F INTERMITTENT

05.A Silicone Aluminum for good corrosion resistance, excellent gloss retention


Prime 62-AY-1 HR Silicone Aluminum 4.38 409 1.5Finish 62-AY-1 HR Silicone Aluminum 4.38 409 1.5

Total Dry Mils 3.0

1

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Exterior Masonry Systems

Index of Recommended Coating Systems for Exterior Masonry Page 1Each system includes prime or fill coat, first and second coats of compatible products.First, look for the substrate to be coated, then the type of finish desired

Introduction - Recommended Painting Specifications Page 2A basic introduction to our products

Recommended Products Page 2All products listed are recognized for their history of quality and service.Product data sheets and color cards are in the last section of this book

Application Details for Painting Exterior Masonry Page 5

SUGGESTED SYSTEMS

Section 01 Exterior Exposed Block or Concrete Masonry Units Page 7

Section 02 Exterior Cement Plaster, Stucco, Concrete, Brick or Drywall Page 10

Section 03 Exterior Exposed Plaster, Concrete or Brick Clear Sealant Page 14

Section 04 Concrete Secondary Contention Dike Systems Page 15

Section 05 Traffic Zone Marking on Concrete and Asphalt Page 16

RECOMMENDED PAINTING SPECIFICATIONS FOR EXTERIOR MASONRY SURFACES

INDEX

2

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)




Mobile Paints was founded in Mobile, Alabama in 1921 and was a pioneer in formulating top-quality architectural, industrialand marine coatings and finishes for tropical and subtropical climates. From this beginning, Mobile has expanded through-out the Southeastern and South Central United States, Puerto Rico and the Virgin Islands. Mobile Paints is recognized forits dedication to quality and service.

This section includes recommendations for finishing new exterior concrete, cement block, brick, plaster or stucco surfacesexposed to normal conditions experienced in typical residential, commercial, industrial and marine environments, forprotecting masonry surfaces which are to be left unpainted, and for refinishing previously painted masonry surfaces.For severe exposures and specific coating problems, please consult your BLP Mobile Paint representative.

RECOMMENDED COATINGS AND PRIMERS

WEATHER-TITETM is the modern industry standard for exterior masonry coatings. Formulated with 100% acrylic resins, it“breathes”, allowing moisture in the wall to transpire and evaporate without damaging the paint film.

WEATHER-TITETM has exceptional color stability and is available in a wide range of designer colors. It has outstandingresistance to blistering, lime burn and ultraviolet degradation.

WEATHER-TITETM contains an effective mildewcide, is lead-free, chromate-free, mercury- free, and low VOC.

WEATHER-TITETM 100% Acrylic Latex House Paint is formulated in Flat, Gloss and Satin finishes.

WEATHER-TITETM 100% Acrylic Universal Primer and WEATHER-TITETM Premium 100 Caulk are part of the completeline of WEATHER-TITETM exterior paints and coatings.

WEATHER-TITETM ELASTOMERIC Wall Coating has extraordinary properties of elongation, stretching and contractingwith the substrate while bridging small cracks and waterproofing against wind-driven rain. Especially recommended forolder buildings with moisture problems.

SMOOTH-COTE® and Architectural are the brand names for our contractor professional coatings which are available in acomplete line of interior and exterior finishes and primers. All exterior products contain an effective mildewcide. All are lead-free, mercury-free, chromate-free, and low VOC.

3

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)




RECOMMENDED COATINGS AND PRIMERS(continued)

In addition to the above architectural latex acrylic coatings for residential, commercial, and light industrial service, thefollowing products are recommended for areas subject to more severe service, such as schools, service stations, laundries,car washes, and hospitals, up to and including heavy industrial installations. All are available in an excellent selection ofstandard colors as shown on their respective color cards and in a wide range of custom colors

NAM-A-LAC® is the brand name for our first line high gloss alkyd enamels. Nontoxic, self-leveling, fast drying, they areavailable in a wide range of stock colors as well as an extensive palette of custom colors. Recommended for interior andexterior service over properly prepared wood, metal or masonry surfaces. Very good color retention, good abrasion andsolvent resistance, good resistance to marine and mild industrial environments.

ACR-A-LACTM is the brand name for our line of waterborne high gloss acrylic enamels, which share the same color cardwith our NAM-A-LAC line. 100% acrylic, they have superior gloss and color retention and are excellent for residential,institutional, commercial and light industrial service. Low odor, low VOC, fast drying, they are suitable for interior andexterior service over properly prepared wood, metal or masonry surfaces.

RUS-KIL® is the brand name for our line of rust inhibiting alkyd enamels for residential, institutional, commercial andindustrial service. Available in OSHA Safety Colors and a wide range of industrial and custom colors. Suitable for interiorand exterior service over properly prepared wood, metal or masonry surfaces.

H2O RUS-KIL® is the brand name for our line of direct-to-metal (DTM) waterborne high gloss acrylic enamels which sharethe RUS-KIL color card. 100% acrylic, they have excellent gloss and color retention. Low odor, low VOC, and fast dryingH2O RUS-KIL® gives excellent interior and exterior service over properly prepared wood, metal or masonry surfaces.

MoPoxYTM is Mobile Paints’ brand name for our family of catalyzed epoxies which offer superior resistance to fresh and saltwater, solvents, many chemicals and abrasion for institutional, commercial, industrial and marine service where maximumprotection and durability are required. Special formulations are stocked for use in food processing plants, kitchens,pharmaceutical plants and other areas requiring direct food contact or FDA certification.

MoPoxYTM is recommended for use in schools, hospitals, laundries, shopping centers, chemical and pharmaceutical plants,waste water treatment plants, potable water storage tanks, and other industrial and commercial installations. Please consultyour BLP Mobile Paint Representative for specific recommendations for problem areas.

4

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)




RECOMMENDED COATINGS AND PRIMERS(continued)

MoPoxYTM is available in solvent-thinned, waterborne and 100% solids formulations.

While most epoxies will chalk under ultraviolet exposure, ultraviolet-resistant formulations are available.

MoPoxYTM is available in standard industrial colors, OSHA safety colors, and many custom colors on special order.

MOTHANETM is Mobile Paint’s brand name for our family of catalyzed polyurethanes which combine good chemical andabrasion resistance with outstanding color and gloss retention and ease of application. Usually specified as top coat inepoxy-polyurethane systems for heavy industrial and marine service, MOTHANE has been proven effective as a masonryfinish in areas such as in service stations where an easily maintained exterior finish is required. Available in severalformulations and a wide range of stock and custom colors.

H2O LOX CHALK Clear sealer is a highly penetrating, clear waterborne acrylic sealer which penetrates and bonds residualchalk left on exterior masonry surfaces after cleaning. Seals the surface and provides excellent adhesion for finish coats.Low odor, excellent resistance to moisture and alkali. Lead-free, mercury-free, chromate-free and low VOC.

Please consult your BLP Mobile Paint Representative for specific recommendations.

5

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



APPLICATION DETAILS FOR PAINTINGEXTERIOR MASONRY SURFACES

Proper surface preparation is essential for the maximum life of any painting or coating system.

New masonry should be allowed to cure for at least 30 days before painting. Surfaces should be clean, dry, and freeof dust, laitance, and form-release oil. All window frames, door jambs, joints and hairline cracks should be caulkedwith WEATHER-TITETM Premium 100 Siliconized Acrylic Caulking. Larger cracks should be filled and bridgedwith WEATHER-TITETM Elastomeric Patch.

Fill exposed block or Concrete Masonry Units (CMU) with one coat of BLOC-FILTM Latex Block Filler, 60-7, beforefinishing.

Prime new masonry with WEATHER-TITETM 100% Acrylic Universal Primer, 6-6, to seal the surface and provide betteradhesion and coverage to the finish coats. Proper priming will add considerably to the life of the painting system and willalso make maintenance repainting easier in the future.

Old or previously painted masonry surfaces should be pressure washed to remove dirt and chalking or peeling paint. Killmildew with a solution of JOMAX and Clorox as directed on the JOMAX label. Apply with a low pressure sprayer, allow topenetrate and kill the roots of the mildew, then wash with high pressure water. Remove grease or oil with detergents.Rinse. Surface must be clean and dry and chalk free prior to painting. Prime either with WEATHER-TITETM

Universal Primer 6-6, H20 LOX CHALK Clear Acrylic Sealer 74-45 or Smooth-Cote® Exterior Primer 206-10.

Caulk all window frames, door jams, joints and cracks with WEATHER-TITETM Premium 100 Caulk. Larger cracks shouldbe filled and bridged with WEATHER-TITETM Elastomeric Patch.

When applying WEATHER-TITETM Elastomeric Wall Coating, special attention should be given to surface preparation inorder to assure proper adhesion to the substrate and complete sealing of all cracks, joints, window frames, door jams, andother areas where water can penetrate the fabric of the building. It is also important to apply the full recommended dry filmthickness for maximum protection. The recommended form of application is by airless spray in order to achieve 7.5 milsdry per coat. If applied by roller, this will normally require two coats because of the weight or viscosity of the product.

Please consult your BLP Mobile Paint Representative for specific recommendations for problem areas.

6

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



APPLICATION DETAILS FOR SEALINGEXPOSED EXTERIOR MASONRY SURFACES

Unpainted exterior concrete, brick, cement plaster, stucco, or exposed aggregate should be waterproofed to protect thefabric of the structure from moisture, to control the growth of mildew on the surface and to reduce dirt pickup, staining andefflorescence.

Mobile Paints offers four systems in this field. Two are solvent based; two are waterborne. All products are invisible whendry and do not affect the color or appearance of the masonry. None forms a measurable film. All repel water, causing tobead on the surface and run off while allowing moisture in the wall to evaporate. All reduce dirt pickup, staining andefflorescence. All are lead, chromate and mercury free.

PRODUCTS

DUB-L-TITETM Silicone Waterproofing, Clear, 74-12 is a clear, 5% silicone solution for use on masonry only. Containsno wax and will not stain the surface. May be painted over with solvent-thinned masonry paints after curing. Meets therequirements of Federal Specification SS-W-110C.

WEATHER-TITETM Waterproofing Sealer, Clear, 74-7, is transparent and paintable. Contains no silicones, may be paintedwith oil or latex paints once dry. For use on masonry, brick, wood, canvas and fabrics.

WEATHER-TITETM H2O Dub-L-Tite Clear Waterproofing, 74-13, is a transparent, wax-free, waterborne silicone/silatewaterproofing sealer for masonry surfaces. Can be painted with solvent thinned masonry paints after curing.

WEATHER-TITETM H2O Clear Waterproofing, 74-17, is a silicone-free, transparent, paintable waterproofing sealer formasonry, wood canvas and fabric. Can be painted with oil or latex paints after drying.

APPLICATION DETAILS

See Application Details for Painting Exterior Masonry Surfaces for Surface Preparation instructions.

Application: Saturate surface thoroughly. Best applied with a low pressure sprayer but may be brushed or rolled. Surfaceshould be saturated and running wet.

7

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



01 EXTERIOR EXPOSED BLOCK OR CONCRETE MASONRY UNITS (CMU)

01.A Exterior Block, Unplastered, 100% Acrylic Latex Flat System

Coat Product Premium Quality, Flat Finish VOC Sq Ft Mils

Fill 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 40-Line WEATHER-TITETM 100% Acrylic Flat 1.03 291 2Finish 40-Line WEATHER-TITETM 100% Acrylic Flat 1.03 291 2

Total Dry Mils 5

01.B Exterior Block, Unplastered, 100% Acrylic Latex Gloss System

Coat Product Premium Quality, Gloss Finish VOC Sq Ft Mils

Fill 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 140-Line WEATHER-TITETM 100% Acrylic Gloss 1.99 296 2Finish 140-Line WEATHER-TITETM 100% Acrylic Gloss 1.99 296 2

Total Dry Mils 5

01.C Exterior Block, Unplastered, 100% Acrylic Latex Satin System

Coat Product Premium Quality, Satin Finish VOC Sq Ft Mils

Fill 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 240-Line WEATHER-TITETM 100% Acrylic Satin 2.19 271 2Finish 240-Line WEATHER-TITETM 100% Acrylic Satin 2.19 271 2

Total Dry Mils 5

01.D Exterior Block, Unplastered, 100% Acrylic Latex High Gloss System


Fill 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 330-Line ACR-A-LACTM 100% Acrylic Gloss Enamel 2.11 293 2Finish 330-Line ACR-A-LACTM 100% Acrylic Gloss Enamel 2.11 293 2

Total Dry Mils 5

8

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



01.E Exterior Block, Unplastered, Elastomeric 100% Acrylic System

Coat Product Premium Quality, Eggshell Finish VOC Sq Ft Mils

Fill 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 43-20 WEATHER-TITETM Elastomeric Wall Coat 0.80 100 7.5Finish 43-20 WEATHER-TITETM Elastomeric Wall Coat 0.80 100 7.5

Total Dry Mils 16

01.F Exterior Block, Unplastered, Alkyd Gloss Enamel System


Fill 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 30-Line NAM-A-LAC® Gloss Enamel 3.18 409 1.5Finish 30-Line NAM-A-LAC® Gloss Enamel 3.18 409 1.5

Total Dry Mils 4

01.G Exterior Block, Unplastered, Alkyd Gloss Enamel System


Fill 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 10-Line RUS-KIL® Rust Inhibitive Enamel 3.35 385 2Finish 10-Line RUS-KIL® Rust Inhibitive Enamel 3.35 385 2

Total Dry Mils 5

01.H Exterior Block, Unplastered, High-Solids Semi-gloss Epoxy System

Coat Product Premium Quality, Satin Finish VOC Sq Ft Mils

Fill 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 613-Line MoPoxYTM HS High Solids Epoxy 2.00 374 3Finish 613-Line MoPoxYTM HS High Solids Epoxy 2.00 374 3

Total Dry Mils 7

9

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



01.I Exterior Block, Unplastered, Catalyzed Polyurethane System


Fill 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 72-AW-21 MOTHANE HD Polyurethane Enamel (White) 4.11 268 2.5Finish 72-AW-21 MOTHANE HD Polyurethane Enamel (White) 4.11 268 2.5

Total Dry Mils 6

01.J Exterior Block, Unplastered, Acrylic Latex Flat System

Coat Product Professional Quality, Flat Finish VOC Sq Ft Mils

Fill 260-45 ARCHITECTURAL Latex Block Filler 0.88 100 1First 296-Line SMOOTH-COTE® 100% Acrylic Flat 1.25 283 1.5Finish 296-Line SMOOTH-COTE® 100% Acrylic Flat 1.25 283 1.5

Total Dry Mils 4

01.K Exterior Block, Unplastered, Acrylic Latex Semi-Gloss System

Coat Product Professional Quality, Semi-Gloss Finish VOC Sq Ft Mils

Fill 260-45 ARCHITECTURAL Latex Block Filler 0.88 100 1First 295-Line SMOOTH-COTE® 100% Acrylic Semi-Gloss 2.54 335 1.5Finish 295-Line SMOOTH-COTE® 100% Acrylic Semi-Gloss 2.54 335 1.5

Total Dry Mils 4

01.L Exterior Block, Unplastered, 100% Acrylic Latex Gloss System

Coat Product Professional Quality, Gloss Finish VOC Sq Ft Mils

Fill 260-45 ARCHITECTURAL Latex Block Filler 0.88 100 1First 294-Line SMOOTH-COTE® 100% Acrylic Gloss 1.48 377 1.5Finish 294-Line SMOOTH-COTE® 100% Acrylic Gloss 1.48 377 1.5

Total Dry Mils 4

10

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



01.M Exterior Block, Unplastered, Vinyl Acrylic Latex Flat System


Fill 260-45 ARCHITECTURAL Latex Block Filler 0.88 100 1First 291-Line SMOOTH-COTE® Vinyl Acrylic Flat 1.30 290 1.5Finish 291-Line SMOOTH-COTE® Vinyl Acrylic Flat 1.30 290 1.5

Total Dry Mils 4

02 EXTERIOR CEMENT PLASTER, STUCCO, CONCRETE, BRICK OR DRYWALL

02.A Exterior Masonry, Plaster and Drywall, Acrylic Latex Flat System

Coat Product Premium Quality, Flat Finish VOC Feet Mils

Prime 6-6 WEATHER-TITETM Universal Primer 1.17 393 1.5First 40-Line WEATHER-TITETM 100% Acrylic Flat 1.03 291 2Finish 40-Line WEATHER-TITETM 100% Acrylic Flat 1.03 291 2

Total Dry Mils 5.5

02.B Exterior Masonry, Plaster and Drywall, Acrylic Latex Gloss System

Coat Product Premium Quality, Gloss Finish VOC Feet Mils

Prime 6-6 WEATHER-TITETM Universal Primer 1.17 393 1.5First 140-Line WEATHER-TITETM 100% Acrylic Gloss 1.99 296 2Finish 140-Line WEATHER-TITETM 100% Acrylic Gloss 1.99 296 2

Total Dry Mils 5.5

02.C Exterior Masonry, Plaster and Drywall, Acrylic Latex Satin System

Coat Product Premium Quality, Satin Finish VOC Feet Mils

Prime 6-6 WEATHER-TITETM Universal Primer 1.17 393 1.5First 240-Line WEATHER-TITETM 100% Acrylic Satin 2.19 271 2Finish 240-Line WEATHER-TITETM 100% Acrylic Satin 2.19 271 2

Total Dry Mils 5.5

11

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



02.D Exterior Masonry, Plaster and Drywall, Acrylic Latex Gloss System


Prime 6-6 WEATHER-TITETM Universal Primer 1.17 393 1.5First 330-Line ACR-A-LACTM 100% Acrylic Gloss Enamel 2.11 293 2Finish 330-Line ACR-A-LACTM 100% Acrylic Gloss Enamel 2.11 293 2

Total Dry Mils 5.5

02.E Exterior Masonry, Plaster and Drywall, Elastomeric 100% Acrylic System

Coat Product Premium Quality, Eggshell Finish VOC Sq Ft Mils

Prime 6-6 WEATHER-TITETM Universal Primer 1.17 393 1.5First 43-20 WEATHER-TITETM Elastomeric Wall Coat 0.80 100 7.5Finish 43-20 WEATHER-TITETM Elastomeric Wall Coat 0.80 100 7.5

Total Dry Mils 16.5

02.F Exterior Masonry, Plaster and Drywall, Alkyd Gloss Enamel System


Prime 6-6 WEATHER-TITETM Universal Primer 1.17 393 1.5First 30-Line NAM-A-LAC® Gloss Enamel 3.18 409 1.5Finish 30-Line NAM-A-LAC® Gloss Enamel 3.18 409 1.5

Total Dry Mils 4.5

02.G Exterior Masonry, Plaster and Drywall, Alkyd Gloss Enamel System


Prime 6-6 WEATHER-TITETM Universal Primer 1.17 393 1.5First 10-Line RUS-KIL® Rust Inhibitive Enamel 3.35 385 2Finish 10-Line RUS-KIL® Rust Inhibitive Enamel 3.35 385 2

Total Dry Mils 5.5

12

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



02.H Exterior Masonry, Plaster and Drywall, High-Solids Semi-gloss Epoxy System

Coat Product Premium Quality, Semigloss Finish VOC Sq Ft Mils

Prime 6-6 WEATHER-TITETM Universal Primer 1.17 393 1.5First 613-Line MoPoxY HS High Solids Epoxy 2.00 374 3Finish 613-Line MoPoxY HS High Solids Epoxy 2.00 374 3

Total Dry Mils 7.5

02.I Exterior Masonry, Plaster and Drywall, High-Solids Epoxy/High Gloss Acrylic Epoxy System

Coat Product Premium Quality, Gloss Finish* VOC Sq Ft Mils

Prime 6-6 WEATHER-TITETM Universal Primer 1.17 393 1.5First 613-Line MoPoxY HS High Solids Epoxy 2.00 374 3Finish 41-AW-2 MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

*Excellent Gloss Retention in Sunlight

Total Dry Mils 6.5

02.J Exterior Masonry, Plaster and Drywall, Catalyzed Polyurethane System


Prime 6-6 WEATHER-TITETM Universal Primer 1.17 393 1.5First 72-AW-21 MOTHANE HD Polyurethane Enamel (White) 4.11 268 2.5Finish 72-AW-21 MOTHANE HD Polyurethane Enamel (White) 4.11 268 2.5

Total Dry Mils 6.5

02.K Exterior Masonry, Plaster and Drywall, Acrylic Latex Flat System


Prime 206-10 SMOOTH-COTE® Acrylic Primer 1.48 387 1.5First 296-Line SMOOTH-COTE® 100% Acrylic Flat 1.25 283 1.5Finish 296-Line SMOOTH-COTE® 100% Acrylic Flat 1.25 283 1.5

Total Dry Mils 4.5

13

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



02.L Exterior Masonry, Plaster and Drywall, Acrylic Latex Semi-Gloss System

Coat Product Professional Quality, Semi-Gloss Finish VOC Sq Ft Mils

Prime 206-10 SMOOTH-COTE® Acrylic Primer 1.48 387 1.5First 295-Line SMOOTH-COTE® 100% Acrylic Semi-Gloss 2.54 335 1.5Finish 295-Line SMOOTH-COTE® 100% Acrylic Semi-Gloss 2.54 335 1.5

Total Dry Mils 4.5

02.M Exterior Masonry, Plaster and Drywall, 100% Acrylic Latex Gloss System

Coat Product Professional Quality, Gloss Finish VOC Sq Ft Mils

Prime 206-10 SMOOTH-COTE® Acrylic Primer 1.48 387 1.5First 294-Line SMOOTH-COTE® 100% Acrylic Gloss 1.48 377 1.5Finish 294-Line SMOOTH-COTE® 100% Acrylic Gloss 1.48 377 1.5

Total Dry Mils 4.5

02.N Exterior Masonry, Plaster and Drywall, Vinyl Acrylic Latex Flat System


Prime 206-10 SMOOTH-COTE® Acrylic Primer 1.48 387 1.5First 291-Line SMOOTH-COTE® Vinyl Acrylic Flat 1.30 290 1.5Finish 291-Line SMOOTH-COTE® Vinyl Acrylic Flat 1.30 290 1.5

Total Dry Mils 4.5

14

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



03 EXTERIOR EXPOSED PLASTER, CONCRETE OR BRICK, CLEAR SEALANT

03.A Exterior Exposed Concrete, Aggregate or Brick, Solvent-thinned Silicone Sealant System

Coat Product Premium Quality - Clear, Non-Paintable VOC Sq Ft Mils

Prime 74-12 WEATHER-TITETM Dub-L-Tite Silicone Waterproofing 6.19 100 N/AFinish 74-12 WEATHER-TITETM Dub-L-Tite Silicone Waterproofing 6.19 100 N/A

Total Dry Mils N/A

03.B Exterior Exposed Concrete, Aggregate or Brick, Solvent-thinned Non-Silicone Sealant System

Coat Product Premium Quality - Clear, Paintable VOC Sq Ft Mils

Prime 74-7 WEATHER-TITETM Waterproofing Sealer 5.30 100 N/AFinish 74-7 WEATHER-TITETM Waterproofing Sealer 5.30 100 N/A

Total Dry Mils N/A

03.C Exterior Exposed Concrete, Aggregate or Brick, Waterborne Silicone/Silane Sealant System

Coat Product Premium Quality - Clear, Paintable w/ SolventThinned Paint after curing. VOC Sq Ft Mils

Prime 74-13 WEATHER-TITETM H2O Dub-L-Tite, Clear 0.00 100 N/AFinish 74-13 WEATHER-TITETM H2O Dub-L-Tite, Clear 0.00 100 N/A

Total Dry Mils N/A

03.D Exterior Exposed Concrete, Aggregate or Brick, Waterborne Non-Silicone Sealant SystemAlso for wood canvas and fabric

Coat Product Premium Quality - Clear, Paintable VOC Sq Ft Mils

Prime 74-17 WEATHER-TITETM H2O Waterproofing, Clear 0.68 100 N/AFinish 74-17 WEATHER-TITETM H2O Waterproofing, Clear 0.68 100 N/A

Total Dry Mils N/A

15

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



SECTION 04 CONCRETE SECONDARY CONTENTION DIKE SYSTEMS

The below systems have been used successfully in a variety of exposures. Please ask your BLP Mobile PaintRepresentative for recommendations for your specific requirements.

04.A Exterior Masonry, Catalyzed Epoxy System

Coat Product Premium Quality - Semi-gloss Epoxy System VOC Sq Ft Mils

Prime* 613-Line MoPoxYTM HS High Solids Epoxy 2.00 374 3First 613-Line MoPoxYTM HS High Solids Epoxy 2.00 374 3Finish 613-Line MoPoxYTM HS High Solids Epoxy 2.00 374 3* Thin 10% with MoPoxYTM Brushing Thinner 75-35

Total Dry Mils 9

04.B Exterior Masonry, Catalyzed Epoxy/Acrylic Epoxy System**

Coat Product Premium Quality-High Gloss Acrylic Epoxy Sys. VOC Sq Ft Mils

Prime* 613-Line MoPoxYTM HS High Solids Epoxy 2.00 374 3First 613-Line MoPoxYTM HS High Solids Epoxy 2.00 374 3Finish 41-AW-2 MOPOX-ACRYL Acrylic Epoxy 3.50 409 2* Thin 10% with MoPoxYTM Brushing Thinner 75-35**Excellent gloss retention under ultraviolet solar exposure

Total Dry Mils 8

04.C Exterior Masonry, Catalyzed Epoxy Mastic / Polyurethane System

Coat Product Premium Quality - High Gloss Finish VOC Sq Ft Mils

Prime 41-AF-2 MoPoxYTM PRE-PREP Sealer, Clear 0.00 1604 1First 40-AW-32 MoPoxYTM Mastic White 1.30 217 6Finish 72-AW-26 MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 9

16

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



04.D Exterior Masonry, Catalyzed Epoxy, Epoxy Mastic System

Coat Product Premium Quality - Gloss Finish VOC Sq Ft Mils

Prime 41-AF-2 MoPoxYTM PRE-PREP Sealer, Clear 0.00 1604 1First 40-AW-32 MoPoxYTM Mastic White 1.30 217 6Finish 40-AW-32 MoPoxYTM Mastic White 1.30 217 6

Total Dry Mils 13

04.E Exterior Masonry, Catalyzed Epoxy, Epoxy Mastic, Acrylic Epoxy System*

Coat Product Premium Quality - Gloss Finish VOC Sq Ft Mils

Prime 41-AF-2 MoPoxYTM PRE-PREP Sealer, Clear 0.00 1604 1First 40-AW-32 MoPoxYTM Mastic White 1.30 217 6Finish 41-AW-2 MOPOX-ACRYL Acrylic Epoxy 3.50 409 2*Excellent gloss retention under ultraviolet solar exposure

Total Dry Mils 9

SECTION 05 TRAFFIC ZONE MARKING ON CONCRETE AND ASPHALT PAVING AREAS

05.A Traffic Zone Marking on Concrete or Asphalt Paving Areas

Coat Product Premium Quality - Matte Finish VOC Sq Ft Mils

Finish 258-Line BLP LATEX Street Marking Paint 0.56 200 3

Application:

Brush or roll: 3.8 mils DFT or 6 mils wet film thickness will yield a 4" stripe 600 feet longSpray: 9.3 mils DFT or 15 mils wet film thickness will yield a 4" stripe 300 feet long. Thisthickness is required when using as a binder for drop-on reflective glass beads.

1

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Interior Masonry Systems

RECOMMENDED PAINTING SPECIFICATIONS FOR INTERIOR MASONRY SURFACES INDEX

Index of Recommended Coating Systems for Interior Masonry Page 1-3Each system includes prime or fill coat, first and second coats of compatible products.First, look for the substrate to be coated, then the type of finish desired

Recommended Products Page 4-5All products listed are recognized for their history of quality and service.Product data sheets and color cards are in the last section of this book

Introduction - Recommended Painting Specifications Page 6-7Surface Preparation

SUGGESTED SYSTEMS

Section 01 Interior Masonry, Plaster or Drywall Page 8-12

Section 02 Interior Block (Concrete Masonry Units) Unplastered Page 13-17

2

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



RECOMMENDED COATING SYSTEMS FOR INTERIOR MASONRY INDEX

Section 01 Interior Masonry, Plaster or DrywallPremium Quality - Residential, Commercial, Institutional & Industrial Service

01.A COVENTRY ® One coat Flat Wall Finish01.B COVENTRY® Semi-gloss Acrylic Enamel Finish01.C COVENTRY® Premium Eggshell Enamel Ffinish01.D COVENTRY® Acrylic High Gloss Enamel Finish01.E ACR-A-LACTM High Gloss Acrylic Enamel Finish01.F H2O RUS-KIL® DTM Acrylic Enamel Finish01.G COVENTRY® Lustarite Alkyd Satin-Gloss Finish01.H NAM-A-LAC® Alkyd Gloss Enamel Finish01.I RUS-KIL® Alkyd Rust Inhibitive Enamel Finish01.J MoPoxYTM H2O-100 Waterborne Acrylic Epoxy High Gloss Finish01.K MoPoxYTM H2O-200 Waterborne Amide Epoxy Semi-gloss Finish01.L MoPoxYTM 513-Series High Gloss Amide Epoxy Finish01.M MoPoxYTM Mastic / 513-Series High Gloss Amide Epoxy Finish01.N MoPoxYTM 613-Series High Solids Semi-gloss Amide Epoxy Finish01.O MoPoxYTM Mastic / 613-Series High Solids Semi-gloss Amide Epoxy Finish

Professional Quality, Residential, Commerical, Instifutional & Light Industrial Service

01.P SMOOTH-COTE® Interior Latex Flat Finish01.Q SMOOTH-COTE® Interior Latex Semi-gloss Finish01.R SMOOTH-COTE® Interior Acrylic Latex Eggshell Finish01.S SMOOTH-COTE® Interior Alkyd Semi-gloss Finish

3

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



Section 02Interior Block (Concrete Masonry Units) UnplasteredPremium Quality - Residential, Commercial, Institutional & Industrial Service

02.A COVENTRY® One coat Flat Wall Finish02.B COVENTRY® Semi-gloss Acrylic Enamel Finish02.C COVENTRY® Premium Eggshell Enamel Ffinish02.D COVENTRY® Acrylic High Gloss Enamel Finish02.E ACR-A-LACTM High Gloss Acrylic Enamel Finish02.F H2O RUS-KIL® DTM Acrylic Enamel Finish02.G COVENTRY® Lustarite Alkyd Satin-Gloss Finish02.H NAM-A-LAC® Alkyd Gloss Enamel Finish02.I RUS-KIL® Alkyd Rust Inhibitive Enamel Finish02.J MoPoxYTM H2O-100 Waterborne Acrylic Epoxy High Gloss Finish02.K MoPoxYTM H2O-200 Waterborne Amide Epoxy Semi-gloss Finish02.L MoPoxYTM 513-Series High Gloss Amide Epoxy Finish02.M MoPoxYTM Mastic / 513-Series High Gloss Amide Epoxy Finish02.N MoPoxYTM 613-Series High Solids Semi-gloss Amide Epoxy Finish02.O MoPoxYTM Mastic / 613-Series High Solids Semi-gloss Amide Epoxy Finish

Professional Quality - Residential, Commerical, Instifutional & Light Industrial Service

02.P SMOOTH-COTE® Interior Latex Flat Finish02.Q SMOOTH-COTE® Interior Latex Semi-gloss Finish02.R SMOOTH-COTE® Interior Acrylic Latex Eggshell Finish02.S SMOOTH-COTE® Interior Alkyd Semi-gloss Finish

4

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



RECOMMENDED PRODUCTS FOR INTERIOR MASONRY SURFACES

The below listing is representative of available products which may be used interchangeably within the designatedsystems depending upon conditions and desired service.

Additional detail of product characteristics and application methods will be found in the referenced Product Data Sheetsat the rear of this book.For specific recommendations, please consult your BLP Mobile Paint Representative.

Number Description VOC Covers DFT

Primers

6-6 WEATHER-TITETM 100% Acrylic Universal Primer 1.17 393 1.5019-7 COVENTRY® PRYMALL 2 QD Acrylic Primer 0.96 302 1.50219-19 SMOOTH-COTE® Interior Latex Primer 1.13 283 1.50206-10 SMOOTH-COTE® Acrylic Primer 1.48 387 1.5060-7 BLOC-FIL Latex Block Filler 0.55 100 1.00260-45 Architectural Latex Block Filler 0.88 85-100 1.00260-55 Architectural Latex Block Filler Brite White 0.70 85-100 1.00

Acrylic & Vinyl Waterborne Finishes

35-Series COVENTRY® One Coat Flat Latex Wall Finish 0.83 375 1.501335-Series COVENTRY® Semi-gloss Acrylic Enamel 2.00 345 1.502335-Series COVENTRY® Premium Eggshell Enamel 0.86 375 1.50335-Series COVENTRY® Acrylic Latex High Gloss Enamel 1.09 408 1.50330-Series ACR-A-LACTM 100% Acrylic Gloss Enamel 2.11 293 2.00310-Series H2O RUS-KIL® DTM Acrylic Enamel 1.09 295 1.50289-Series SMOOTH-COTE® Interior Latex Flat Finish 0.89 346 1.50290-Series SMOOTH-COTE® Latex Semi-Gloss Enamel 1.60 252 1.50292-Series SMOOTH-COTE® Acrylic Latex Eggshell Enamel 0.85 395 0.50

5

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



RECOMMENDED PRODUCTSFOR INTERIOR MASONRY SURFACES

Alkyd Finishes

135-Series COVENTRY® Lustarite Alkyd Satin Gloss Enamel 3.04 427 2.0030-Series NAM-A-LAC® Gloss Enamel 3.18 409 1.5010-Series RUS-KIL® Rust Inhibitive Gloss Enamel 3.35 385 2.0050-Series SpeeDeck ® Polyurethane Enamel 3.35 388 2.00520-Series QD-520 Quick Dry Enamel (OEM) 4.07 417 1.50521-Series QD-521 Quick Dry Enamel 3.72 467 1.50293-Series SMOOTH-COTE® Alkyd Semi-gloss Enamel 2.85 449 2.00

Catalyzed Epoxies & Epoxy Mastic

613-Line MoPoxYTM HS High Solids Semi-gloss Epoxy 2.00 374 3.00513-Line MoPoxYTM High Gloss Epoxy 4.30 314 2.0069-AW-5 MoPoxYTM H2O-100 Waterborne Acrylic Epoxy, Gloss 1.71 313 2.0069-AW-6 MoPoxYTM H2O-200 Waterborne Epoxy, Semi-gloss 1.00 225 3.0040-AW-32 MoPoxYTM MASTIC , White 1.30 217 6.0041-AF-2 MoPoxYTM Pre-Prep Sealer, Clear 0.00 1604 1.0041-AW-2 MOPOX-ACRYL Acrylic Epoxy, High Gloss 3.50 409 2.00

6

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



RECOMMENDED PAINTING SPECIFICATIONSFOR INTERIOR MASONRY SURFACES

Mobile Paints was founded in Mobile, Alabama, in 1921 and was originally dedicated to formulating top-quality architectural,industrial and marine coatings for the Gulf Coast’s tropical and subtropical climates. Subsequently, we have expanded ourgeographical horizon to include more northern regions and are recognized for the high quality and durability of our productsthroughout our market area.

This section includes recommended coating systems for interior masonry surfaces including brick, plaster, and gypsumboard walls and ceilings as well as unplastered cement block or concrete masonry units (CMU), in residential, commercial,institutional and industrial service.

Each coating system details the primer, intermediate, and finish coats and is suitable for residential, commercial, institutionaland industrial service as indicated. In addition to the usual latex, acrylic and alkyd finishes, we include a variety of catalyzedepoxy systems for clean rooms in pharmaceutical plants, food processing plants, and areas subject to frequent wetting,such as car washes and showers.

All products are lead-free, chromate-free, mercury-free, and VOC compliant.

SURFACE PREPARATION

Proper surface preparation is essential to the life of any coating system. All masonry surfaces should be allowed to cure forat least 30 days before painting. Surfaces should be clean, dry, and free from dust, laitance, and mold release oil. Gypsumboard should be dusted thoroughly to remove sanding dust. Seal openings around door jams and windows with WEATHER-TITETM Premium 100 Siliconized Acrylic Caulk.

Bare or unplastered block (CMU) should be filled with either BLOC-FIL Latex Block Filler, 60-7, for normal service orBLOC-SEALTM Acrylic, 19-10, for service in areas subject to frequent washing or wetting.

Previously painted surfaces must be clean and dry. Scrape and sand peeling or flaking paint to provide a soundsurface. Sand high gloss finishes to insure good intercoat adhesion. Prime bare areas with one coat ofCOVENTRY® PRYMALL 2 Q D Acrylic Primer, 19-7, 1.5 mils dry. Consult your BLP Mobile Paint Representativefor recommendations for specific requirements.

7

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



RECOMMENDED PAINTING SPECIFICATIONSFOR INTERIOR COATING SYSTEMS

All systems are based on our top-quality products and are generally organized in order of increasing chemical and abrasionresistance. All products are lead-free, chromate-free, mercury-free, and VOC compliant. All products may be applied bybrush, roller, or airless or conventional spray.

COVENTRY® is the brand name for our first line interior primers and finishes which are available in flat, eggshell, semi-gloss and high gloss latex acrylic coatings and enamels; alkyd satin-gloss enamel, and acrylic primers for wood andmasonry. In addition to our famous “Southern White Collection” of whites, these are available in an almost unlimited rangeof custom colors though our Color Studio system.

NAM-A-LAC® is the brand name of our first line high gloss alkyd enamels. Non-toxic, self-leveling, fast-dry, they areavailable in a wide range of stock colors as well as an extensive palette of custom colors and are formulated for interior andexterior service.

ACR-A-LACTM is the brand name for our line of waterborne high gloss acrylic enamels, which share the same color cardwith our NAM-A-LAC® line. 100% acrylic, they have superior gloss and color retention and are excellent for residential,institutional, commercial and light industrial service. Low odor, low VOC, fast drying, they are suitable for interior andexterior service.

RUS-KIL® is the brand name for our line of rust-inhibiting alkyd enamels for residential, institutional, commercial andindustrial service. These are stocked in White, Black, OSHA Safety Colors, and Industrial colors as shown on the RUS-KIL®

color card, and are also available in a wide range of custom colors. Suitable for interior and exterior service.

H2O RUS-KIL® is the brand name for our DTM waterborne high gloss acrylic enamels which share the standardRUS-KIL® color card. 100% acrylic, they have superior gloss and color retention. Low odor, low VOC, fast drying, they areexcellent for interior or exterior service.

MoPoxYTM is the brand name for our extensive line of catalyzed epoxies, offering formulations for institutional, commercial,and industrial coating systems where maximum protection and durability are required. Both standard and waterborneformulations are available. In addition to an extensive color card, a wide range of custom colors are shaded to order.

MoPoxYTM offers superior resistance to chemicals, especially alkalis, moisture, and abrasion, and good resistance to mostsolvents and acid splashes. Special formulations are stocked for use in food processing plants, kitchens, pharmaceuticalplants and other areas where direct food contact certification is required.

Recommended for use in schools, hospitals, laundries, shopping centers, kitchens and food processing areas, chemicaland pharmaceutical plants, waste water treatment plants, potable water storage tanks, and other industrial and commercialinstallations. Formulations are available for specific chemical or food product resistance requirements. Please ask yourBLP Mobile paint representative for assistance in meeting your coating needs.

SMOOTH-COTE® is our brand name for our Professional Line of interior and exterior primers and finishes.

8

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



SECTION 01 INTERIOR MASONRY, PLASTER AND DRYWALL

01.A Latex Flat Finish, Residential, Commercial & Light Industrial Service

Coat Product Premium Quality VOC Sq. Ft. Mils

Prime 19-7 PRYMALL 2 Q D Acrylic Primer 0.96 302 1.5First 35-Series COVENTRY® One Coat Flat Wall Finish 0.83 375 1.5Finish 35-Series COVENTRY® One Coat Flat Wall Finish 0.83 375 1.5

Total Dry Mils 4.5

01.B Acrylic Semi-gloss Finish, Residential, Commercial & Light Industrial Service

Coat Product Premium Quality, 100% Acrylic Latex VOC Sq. Ft. Mils

Prime 19-7 PRYMALL 2 Q D Acrylic Primer 0.96 302 1.5First 1335-Series COVENTRY® Semi-gloss Acrylic Enamel 2.00 345 1.5Finish 1335-Series COVENTRY® Semi-gloss Acrylic Enamel 2.00 345 1.5

Total Dry Mils 4.5

01.C Acrylic Eggshell Finish, Residential, Commercial & Light Industrial Service


Prime 19-7 PRYMALL 2 Q D Acrylic Primer 0.96 302 1.5First 2335-Series COVENTRY® Premium Eggshell Enamel 0.86 375 1.5Finish 2335-Series COVENTRY® Premium Eggshell Enamel 0.86 375 1.5

Total Dry Mils 4.5

01.D Acrylic High Gloss Finish, Residential, Commercial & Light Industrial Service


Prime 19-7 PRYMALL 2 Q D Acrylic Primer 0.96 302 1.5First 335-Series COVENTRY® Latex High Gloss Enamel 1.09 408 1.5Finish 335-Series COVENTRY® Latex High Gloss Enamel 1.09 408 1.5

Total Dry Mils 4.5

9

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



01.E Acrylic High-Gloss Enamel, Residential, Commercial & Light Industrial Service


Prime 19-7 PRYMALL 2 Q D Acrylic Primer 0.96 302 1.5First 330-Series ACR-A-LACTM 100% Acrylic Gloss Enamel 2.11 293 2Finish 330-Series ACR-A-LACTM 100% Acrylic Gloss Enamel 2.11 293 2

Total Dry Mils 5.5

01.F Acrylic High-Gloss Enamel Finish, Residential, Commercial & Light Industrial Service


Prime 19-7 PRYMALL 2 Q D Acrylic Primer 0.96 302 1.5First 310-Series H2O RUS-KIL® DTM Acrylic Enamel 1.09 295 2Finish 310-Series H2O RUS-KIL® DTM Acrylic Enamel 1.09 295 2

Total Dry Mils 5.5

01.G Alkyd Semi-Gloss Enamel System Residential, Commercial & Light Industrial Service


Prime 19-7 PRYMALL 2 Q D Acrylic Primer 0.96 302 1.5First 135-Series COVENTRY® Lustarite Satin-Gloss Enamel 3.04 427 2Finish 135-Series COVENTRY® Lustarite Satin-Gloss Enamel 3.04 427 2

Total Dry Mils 5.5

01.H Alkyd Gloss Enamel System, Residential, Commercial & Light Industrial Service


Prime 19-7 PRYMALL 2 Q D Acrylic Primer 0.96 302 1.5First 30-Series NAM-A-LAC® Gloss Enamel 3.18 409 1.5Finish 30-Series NAM-A-LAC® Gloss Enamel 3.18 409 1.5

Total Dry Mils 4.5

10

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



01.I Alkyd Gloss Enamel System, Residential, Commercial & Industrial Service


Prime 19-7 PRYMALL 2 Q D Acrylic Primer 0.96 302 1.5First 10-Series RUS-KIL® Rust Inhibitive Enamel 3.35 385 2Finish 10-Series RUS-KIL® Rust Inhibitive Enamel 3.35 385 2

Total Dry Mils 5.5

01.J Waterborne Acrylic Gloss Epoxy Finish, Commercial & Light Industrial Service


Prime 19-7 PRYMALL 2 Q D Acrylic Primer 0.96 302 1.5First 69-AW-5 MoPoxYTM H20-100 Acrylic Epoxy 1.71 313 2Finish 69-AW-5 MoPoxYTM H20-100 Acrylic Epoxy 1.71 313 2

Total Dry Mils 5.5

01.K Waterborne Amide Epoxy System, Commercial & Industrial Service


Prime 19-7 PRYMALL 2 Q D Acrylic Primer 0.96 302 1.5First 69-AW-6 MoPoxYTM H20-200 WB Amide Epoxy 1.00 225 3Finish 69-AW-6 MoPoxYTM H20-200 WB Amide Epoxy 1.00 225 3

Total Dry Mils 7.5

01.L Amide Gloss Epoxy System, Commercial & Industrial Service


Prime 19-7 PRYMALL 2 Q D Acrylic Primer 0.96 302 1.5First 513-Series MoPoxYTM High Gloss Epoxy 4.24 322 2Finish 513-Series MoPoxYTM High Gloss Epoxy 4.24 322 2

Total Dry Mils 5.5

11

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



01.M Epoxy Mastic/Amide Gloss Epoxy System, Commercial & Industrial Service


Prime 19-7 PRYMALL 2 Q D Acrylic Primer 0.96 302 1.5First 40-AW-32 MoPoxYTM Mastic White 1.30 217 6Second 513-Series MoPoxYTM High Gloss Epoxy 4.24 322 2Finish 513-Series MoPoxYTM High Gloss Epoxy 4.24 322 2

Total Dry Mils 11.5

01.N High-solids Amide Semi-Gloss Epoxy System, Commercial & Industrial Service


Prime 19-7 PRYMALL 2 Q D Acrylic Primer 0.96 302 1.5First 613-Series MoPoxYTM HS High Solids Epoxy 2.00 374 3Finish 613-Series MoPoxYTM HS High Solids Epoxy 2.00 374 3

Total Dry Mils 7.5

01.O Epoxy Mastic/Semi-Gloss Epoxy System, Heavy Industrial Service


Prime 19-7 PRYMALL 2 Q D Acrylic Primer 0.96 302 1.5First 40-AW-32 MoPoxYTM Mastic White 1.30 217 6Second 613-Series MoPoxYTM HS High Solids Epoxy 2.00 374 3Finish 613-Series MoPoxYTM HS High Solids Epoxy 2.00 374 3

Total Dry Mils 13.5

01.P Latex Flat Finish, Residential, Commercial & Light Industrial Service

Coat Product Professional Quality VOC Sq.Ft. Mils

Prime 219-19 SMOOTH-COTE® Interior Latex Primer 1.13 283 1.5First 289-Series SMOOTH-COTE® Interior Latex Flat 0.89 346 1.5Finish 289-Series SMOOTH-COTE® Interior Latex Flat 0.89 346 1.5

Total Dry Mils 4.5

12

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



01.Q Latex Semi-Gloss Finish, Residential, Commercial & Light Industrial Service


Prime 219-19 SMOOTH-COTE® Interior Latex Primer 1.13 283 1.5First 290-Series SMOOTH-COTE® Latex Semi-Gloss 1.60 252 1.5Finish 290-Series SMOOTH-COTE® Latex Semi-Gloss 1.60 252 1.5

Total Dry Mils 4.5

01.R Latex Acrylic Eggshell Finish, Residential, Commercial & Light Industrial Service


Prime 219-19 SMOOTH-COTE® Interior Latex Primer 1.13 283 1.5First 292-Series SMOOTH-COTE® Acrylic Latex Eggshell 0.85 395 1.5Finish 292-Series SMOOTH-COTE® Acrylic Latex Eggshell 0.85 395 1.5

Total Dry Mils 4.5

01.S Alkyd Semi-gloss Finish, Residential, Commercial & Light Industrial Service


Prime 219-19 SMOOTH-COTE® Interior Latex Primer 1.13 283 1.5First 293-Series SMOOTH-COTE® Alkyd Semi-Gloss 2.85 449 2Finish 293-Series SMOOTH-COTE® Alkyd Semi-Gloss 2.85 449 2

Total Dry Mils 5.5

13

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



SECTION 02 INTERIOR BLOCK (CONCRETE MASONRY UNITS) UNPLASTERED

02.A Latex Flat Finish, Residential & Commercial Service

Coat Product Premium Quality VOC Sq.Ft. Mils

Prime 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 35-Series COVENTRY® One Coat Flat Wall Finish 0.83 375 1.5Finish 35-Series COVENTRY® One Coat Flat Wall Finish 0.83 375 1.5

Total Dry Mils 4.0

02.B Acrylic Semi-Gloss Finish, Residential, Commercial, Institutional & Light Industrial Service


Prime 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 1335-Series COVENTRY® Semi-gloss Acrylic Enamel 2.00 345 1.5Finish 1335-Series COVENTRY® Semi-gloss Acrylic Enamel 2.00 345 1.5

Total Dry Mils 4.0

02.C Acrylic Eggshell Finish, Residential, Commercial, Institutional & Light Industrial Service


Prime 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 2335-Series COVENTRY® Premium Eggshell Enamel 0.86 375 1.5Finish 2335-Series COVENTRY® Premium Eggshell Enamel 0.86 375 1.5

Total Dry Mils 4.0

02.D Acrylic Gloss Enamel System, Residential, Commercial & Light Industrial Service


Prime 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 335-Series COVENTRY® Latex Acrylic High Gloss Enamel 1.09 408 1.5Finish 335-Series COVENTRY® Latex Acrylic High Gloss Enamel 1.09 408 1.5

Total Dry Mils 4.0

14

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



02.E Acrylic Gloss Enamel System, Residential, Commercial & Light Industrial Service


Prime 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 330-Series ACR-A-LACTM 100% Acrylic Gloss Enamel 2.11 293 2Finish 330-Series ACR-A-LACTM 100% Acrylic Gloss Enamel 2.11 293 2

Total Dry Mils 5.0

02.F Acrylic Gloss Enamel System, Residential, Commercial & Light Industrial Service


Prime 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 310-Series H2O RUS-KIL® Acrylic DTM Enamel 1.09 295 2Finish 310-Series H2O RUS-KIL® Acrylic DTM Enamel 1.09 295 2

Total Dry Mils 5.0

02.G Alkyd Semi-Gloss Enamel System, Residential, Commercial & Light Industrial Service


Prime 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 135-Series COVENTRY® Lustarite Satin-Gloss Enamel 3.04 427 2Finish 135-Series COVENTRY® Lustarite Satin-Gloss Enamel 3.04 427 2

Total Dry Mils 5.0

02.H Alkyd Gloss Enamel System, Residential, Commercial & Light Industrial Service


Prime 60-07 BLOC-FIL Latex Block Filler 0.55 100 1First 30-Series NAM-A-LAC® Gloss Enamel 3.18 409 1.5Finish 30-Series NAM-A-LAC® Gloss Enamel 3.18 409 1.5

Total Dry Mils 4.0

15

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



02.I Alkyd Gloss Enamel System, Commercial & Industrial Service

Coat Product Premium Industrial Quality VOC Sq. Ft. Mils

Prime 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 10-Series RUS-KIL® Gloss Enamel 3.35 385 2Finish 10-Series RUS-KIL® Gloss Enamel 3.35 385 2

Total Dry Mils 5.0

02.J Waterborne Acrylic Gloss Epoxy Finish, Commercial & Light Industrial Service


Prime 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 69-AW-5 MoPoxYTM H20-100 WB Acrylic Epoxy 1.71 313 2Finish 69-AW-5 MoPoxYTM H20-100 WB Acrylic Epoxy 1.71 313 2

Total Dry Mils 5.0

02.K Waterborne Amide Epoxy System, Commercial & Industrial Service


Prime 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 69-AW-6 MoPoxYTM H20-200 WB Amide Epoxy 1.00 225 3Finish 69-AW-6 MoPoxYTM H20-200 WB Amide Epoxy 1.00 225 3

Total Dry Mils 7.0

02.L Amide Gloss Epoxy System, Commercial & Industrial Service


Prime 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 513-Series MoPoxYTM High GlossEpoxy 4.30 314 2Finish 513-Series MoPoxYTM High GlossEpoxy 4.30 314 2

Total Dry Mils 5.0

16

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



02.M Epoxy Mastic/High Gloss Epoxy System, Heavy Industrial Service


Prime 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 40-AW-32 MoPoxYTM MASTIC White 1.30 217 6Second 513-Series MoPoxYTM High GlossEpoxy 4.30 314 2Finish 513-Series MoPoxYTM High GlossEpoxy 4.30 314 2

Total Dry Mils 11.0

02.N High-solids Amide Semi-Gloss Epoxy System, Commercial & Industrial Service


Prime 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 613-Series MoPoxYTM HS High Solids Epoxy 2.00 374 3Finish 613-Series MoPoxYTM HS High Solids Epoxy 2.00 374 3

Total Dry Mils 7.0

02.O Epoxy Mastic/Semi-Gloss Epoxy System, Heavy Industrial Service


Prime 60-7 BLOC-FIL Latex Block Filler 0.55 100 1First 40-AW-32 MoPoxYTM MASTIC White 1.30 217 6Second 613-Series MoPoxYTM HS High Solids Epoxy 2.00 374 3Finish 613-Series MoPoxYTM HS High Solids Epoxy 2.00 374 3

Total Dry Mils 13.0

02.P Latex Flat Finish, Residential & Commercial Service

Coat Product Professional Quality VOC Feet Mils

Prime 260-45 ARCHITECTURAL Block Filler 0.88 85 1First 289-Series SMOOTH-COTE® Interior Latex Flat 0.89 346 1.5Finish 289-Series SMOOTH-COTE® Interior Latex Flat 0.89 346 1.5

Total Dry Mils 4.0

17

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



02.Q Latex Semi-Gloss Finish, Residential, Commercial & Light Industrial Service


Prime 260-45 ARCHITECTURAL Block Filler 0.88 85 1First 290-Series SMOOTH-COTE® Latex Semi-Gloss 1.60 252 1.5Finish 290-Series SMOOTH-COTE® Latex Semi-Gloss 1.60 252 1.5

Total Dry Mils 4.0

02.R Latex Acrylic Eggshell Finish, Residential, Commercial & Light Industrial Service


Prime 260-45 ARCHITECTURAL Block Filler 0.88 85 1First 292-Series SMOOTH-COTE® Acrylic Latex Eggshell 0.85 395 1.5Finish 292-Series SMOOTH-COTE® Acrylic Latex Eggshell 0.85 395 1.5

Total Dry Mils 4.0

02.S Alkyd Semi-gloss Finish, Residential, Commercial & Light Industrial Service


Prime 260-45 ARCHITECTURAL Block Filler 0.88 85 1First 293-Series SMOOTH-COTE® Alkyd Semi-Gloss 2.85 449 2Finish 293-Series SMOOTH-COTE® Alkyd Semi-Gloss 2.85 449 2

Total Dry Mils 5.0


Wood Finishing Specifications1

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

RECOMMENDED PAINTING SPECIFICATIONS

FOR WOOD SURFACES

Please see section on FLOORS for Floor Finishing Systems

INDEX OF COATING SYSTEMS


INTRODUCTION

Page 3

Discussion of surface preparation and product advantages

COATING SYSTEMS

Page 7

Recommended Primers, Intermediate Coats,Finish Coats, Dry Film Thickness and Coverage

01 - Interior, Natural Grain

02 - Interior, Painted Finishes

03 - Exterior, Natural Grain

04 - Exterior, Painted Finishes

PRODUCT DATA SHEETS & COLOR CARDSWill be found in the last section of this book



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

RECOMMENDED SPECIFICATIONS FOR WOOD FINISHING

Well-finished wood is the hallmark of elegance.

Interior wood may be oiled, stained, varnished, or lacquered for a natural finish to display its grain and beauty, or paintedto match or contrast with adjoining wall surfaces. Fire retardant systems are included for Class A fire protection.

Exterior wood should always be protected from the weather. Even cedar, cypress and redwood benefit from a clearwaterproofing to repel water and protect against rot. Clear oil sealers, oil and acrylic stains, and marine varnishes combinethe beauty of a natural finish with protection. New waterborne sealants are now available and included in this specification.

Traditional coating systems include oil based house paints and enamels and a full line of waterborne acrylic latex paintsand enamels which offer exceptional gloss and color retention.

Marine varnishes and silicone alkyd enamels offer extra protection and durability in marine and industrial environments.

Catalyzed epoxies, both solvent-thinned and waterborne, offer excellent abrasion and chemical resistance.

Mobile Paints manufactures a wide variety of finishes for wood, both for interior and exterior, for residential, commercial,institutional, industrial and marine service. In the interests of simplification, we have limited our recommendations to themost widely used systems which have a long record of user satisfaction, and detail these below.

All recommended finishes are lead-free, chromate-free, mercury-free and VOC compliant. All are available in a widepalette of colors.

Floor finishes are covered in a separate section under FLOORS.

Please ask your BLP Mobile Paint representative for specific recommendations.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

INTERIOR SURFACE PREPARATION

Surface preparation is the same for all woods, independent of the finish to be applied.

Fill any nail holes with matching color putty. Sand lightly to remove any irregularities. Dust with tack cloth to remove all dust.Surface must be clean, dry and dust-free.

RECOMMENDED INTERIOR WOOD FINISHES

All products recommended are lead-free, mercury-free, chromate-free and VOC compliant.

NUWOOD® Penetrating Wood Finish, 71-Series - A premium quality polyurethane wood stain and finish for interior woodand wood products. Excellent as a stain and sealer where a natural wood grain finish is desired. Available in a wide varietyof standard and custom colors. May be finished with NUWOOD® Polyurethane Varnish, 72-Series, or NUWOOD® Tung OilFinish, 72-45.

NUWOOD® Polyurethane Varnish - A clear, pale varnish with excellent resistance to abrasion, water, mild acids and alkalis,grease, alcohol and soil. Available in gloss, 72-35, and satin-gloss, 72-36, finishes. May be applied directly to wood orover polyurethane stain. Suitable for use on all interior woodwork including floors

NUWOOD® Tung Oil Finish 72-45 - A clear, hand-rubbed finish with excellent resistance to water spotting, alcohol, greaseand abrasion. Excellent for paneling, doors, cabinets and furniture. Not recommended for floors.

CLEARCOAT II, 9835-241, is a Class A, interior, fire protective varnish. May be applied over existing varnishes or primersand topcoated with NUWOOD Polyurethane Varnish for additional protection.

BLP Spraying Lacquer , 9835 Series - Quick dry, water-white, non-yellowing, with a complimentary line of lacquer stains fornatural wood finishes. Also available in tint bases for an almost unlimited range of colors. Excellent for kitchen cabinets,furniture, paneling, doors and door frames and trim. Apply by spray only. Not recommended for floors.

COVENTRY® is the brand name for our premium line of interior wall finishes and primers. Finishes are available inOne-Coat Flat Wall Finish, 35-Series; Semi-gloss Acrylic Enamel, 1335-Series; Eggshell Acrylic Enamel, 2335-Series;and High Gloss Acrylic Enamel, 335-Series. Excellent coverage, easy to apply, quick-drying, odorless, with a wide range ofcolors. Washable, easily maintained.

COVENTRY® Lustarite, 135-Series - a complimentary alkyd satin-gloss enamel . Excellent coverage, easy to apply, quickdrying, low odor, with a wide range of colors. . Washable, easily maintained. Recommended for areas subject to moderatesoiling, abrasion or light chemical exposure.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

ACR-A-LACTM 100% Acrylic Gloss Enamel, 330-Series - high gloss, low odor, 100% acrylic, with excellent coverage, easyto apply, quick drying. Shares color card with NAM-A-LAC® Alkyd Gloss enamel and is also available in with a wide rangeof custom colors. Washable, easily maintained. Recommended for areas subject to moderate soiling, abrasion or chemicalexposure. Suitable for interior and exterior service.

NAM-A-LAC® Alkyd Gloss Enamel, 30-Series - excellent coverage, easy to apply, quick drying, low odor. Shares color cardwith ACR-A-LACTM and is also available in a wide range of custom colors. Washable, easily maintained. Recommended forareas subject to moderate soiling, abrasion or chemical exposure. Suitable for interior and exterior service.

RUS-KIL® Rust Inhibiting Alkyd Gloss Enamel, 10-Series - an industrial grade general purpose enamel suitable for interiorand exterior service on a variety of surfaces. Available in OSHA Safety Colors and other standard colors as shown on theRUS-KIL® color card and a wide variety of custom colors.

H2O RUS-KIL® DTM 100% Acrylic Gloss Enamel, 310-Series - high gloss, low odor, 100% acrylic, with excellent coverage,easy to apply, quick drying. Available in OSHA Safety Colors and other standard colors as shown on the RUS-KIL colorcard as well as a wide range of custom colors. Washable, easily maintained. Recommended for areas subject to light tomoderate soiling, abrasion or chemical exposure. Suitable for interior and exterior service.

FIRECOAT 320, 9835-239 - A Class A, Underwrites Laboratories Classified, interior latex fire protective coating. May beapplied to wood, drywall or fiberglass over a suitable primer or other commercial latex based product. White. Custompastels are available. May be topcoated with any of the above finish products.

MOPOXYTM Catalyzed Epoxy - superior resistance to chemicals, especially alkalis, and abrasion. Good resistance to mostsolvents, acid splashes. Available in a wide range of formulations for specific services, including direct food contact.Extensive palette of colors. Recommended for use in schools, hospitals, kitchens and food processing areas, chemicaland pharmaceutical plants, and other commercial, institutional and industrial installations. where a durable and easilymaintained finish is required.

Waterborne formulations available.

Please see your BLP Mobile Paint representative for specific recommendations.

SMOOTH-COTE® is Mobile’s brand name for our line of Professional primers and coatings and is available in Flat, Semi-gloss, and Satin Latex and Semi-gloss Alkyd finishes for interior service.

.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

EXTERIOR SURFACE PREPARATION

Fill any nail holes with matching color putty. Sand lightly to remove any irregularities. Dust with tack cloth to remove all dust.Caulk all joints and openings with WEATHER-TITETM Premium 100 Siliconized Acrylic Caulking in desired color.

Mildew and stains should be removed by washing with a solution of Jomax, Clorox and Trisodium Phosphate as directedon the Jomax label. Clean with high pressure water if necessary to remove chalking paint and other contamination. Surfacemust be clean, dry and dust free.

RECOMMENDED EXTERIOR WOOD FINISHES

WEATHER PROTECTOR® Exterior Clear Sealer & Preservative, 7-10 - A transparent penetrating sealer with mildewcideand ultraviolet screening agents to help new lumber retain its natural look. May be tinted.

WEATHER-TITE® Waterproofing Sealer, Clear, 74-7 - A transparent, paintable, waterproofing sealer for masonry, concrete,brick, stucco, wood, and canvas. Contains no silicones. Prevents water penetration while allowing surface to breathe. Maybe painted when dry.

WEATHER-TITE® H20 Waterproofing Sealer, Clear. 74-17 - A transparent, paintable waterproofing sealer. Waterborne.Contains no silicones. Suitable for use on most porous surfaces such as masonry, wood, canvas and fabric. Preventswater penetration while allowing the treated surface to breathe.

WEATHER PROTECTOR® Interior/Exterior Acrylic Wood Stain, 44 Line - A 100% acrylic latex waterborne solid hide stainsuitable for interior and exterior use. Available in stock colors, custom colors, and a semitransparent formulation. May bevarnished for interior service. Contains an effective mildewcide.

JACK TAR® 100% Phenolic Marine Spar Varnish, 470-31 - A clear, high gloss marine varnish for industrial, commercial andresidential use on exterior exposed wood or metal surfaces

JACK TAR® Marine Spar Varnish with Ultraviolet Filter, 470-34 - A 100% phenolic high gloss clear finish containing aneffective ultraviolet filter. For exterior weather-exposed wood surfaces such as doors, wood trim, hatches, transoms, decks,paneling and spars.

WEATHER-TITETM Southernized Mildew Treated House Paint, 5 Line - An oil based exterior house paint formulated towithstand extreme temperatures and excessive humidity as well as mild chemical fumes and salt air. Contains an effectivemildewcide. Wide range of colors, excellent color retention.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

WEATHER-TITETM 100% Alkyd Universal Primer, 6-6 - A high quality 100% acrylic latex primer for interior or exterior useon wood, masonry, galvanized metal and aluminum. Contains effective mildewcides. Prevents bleeding of many stains.Fast drying, low odor, easy to apply.

ACR-A-LACTM 100% Acrylic Gloss Enamel, 330-Series - high gloss, low odor, 100% acrylic, with excellent coverage, easyto apply, quick drying. Shares color card with NAM-A-LAC® Alkyd Gloss enamel and is also available in with a wide rangeof custom colors. Washable, easily maintained. Recommended for areas subject to moderate soiling, abrasion or chemicalexposure. Suitable for interior and exterior service.

NAM-A-LAC® Alkyd Gloss Enamel, 30-Series - excellent coverage, easy to apply, quick drying, low odor. Shares color cardwith ACR-A-LACTM and is also available in a wide range of custom colors. Washable, easily maintained. Recommended forareas subject to moderate soiling, abrasion or chemical exposure. Suitable for interior and exterior service.

RUS-KIL® Rust Inhibiting Alkyd Gloss Enamel, 10-Series - an industrial grade general purpose enamel suitable for interiorand exterior service on a variety of surfaces. Available in OSHA Safety Colors and other standard colors as shown on theRUS-KIL® color card and a wide variety of custom colors.

H2O RUS-KIL® DTM 100% Acrylic Gloss Enamel, 310-Series - high gloss, low odor, 100% acrylic, with excellent coverage,easy to apply, quick drying. Available in OSHA Safety Colors and other standard colors as shown on the RUS-KIL® colorcard as well as a wide range of custom colors. Washable, easily maintained. Recommended for areas subject to light tomoderate soiling, abrasion or chemical exposure. Suitable for interior and exterior service.

JACK TAR® Silicone Yacht Finish, 432-Series - a high gloss silicone alkyd enamel with excellent gloss and color retentionin marine and industrial environments.

SMOOTH-COTE® is our brand name for a complete line of professional quality alkyd and latex architectural primers andcoatings for interior and exterior service



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

01 INTERIOR WOOD FINISHES, NATURAL GRAIN

01.A Interior Wood, Natural, Gloss Polyurethane Varnish System


Prime 71-Line NUWOOD® Penetrating Wood Stain 4.61 750 1.00First 72-35 NUWOOD® Polyurethane Gloss Finish 3.77 673 1.00Finish 72-35 NUWOOD® Polyurethane Gloss Finish 3.77 673 1.00

Total Dry Mils 3.00

01.B Interior Wood, Natural, Satin-Gloss Polyurethane Varnish System


Prime 71-Line NUWOOD® Penetrating Wood Stain 4.61 750 1.00First 72-36 NUWOOD® Polyurethane Satin Finish 3.77 558 1.00Finish 72-36 NUWOOD® Polyurethane Satin Finish 3.77 558 1.00

Total Dry Mils 3.00

01.C Interior Wood, Natural, Rubbed Tung Oil Finish


Prime 72-45 NUWOOD® Tung Oil Finish 4.51 502 1.00First 72-45 NUWOOD® Tung Oil Finish 4.51 502 1.00Finish 72-45 NUWOOD® Tung Oil Finish 4.51 502 1.00

Total Dry Mils 3.00

01.D FIRE RETARDANT Varnish System


Prime 9835-241 CLEARCOAT II Fire Retardant Varnish 4.19 135 5.00First 9835-241 CLEARCOAT II Fire Retardant Varnish 4.19 135 5.00Finish with any of the above finish coatsPlease ask your BLP Mobile Paint service representative for details




251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

01.E Interior Wood, Natural, Gloss Lacquer System


Prime 9835-165 Lacquer Sanding Sealer Water-White 152 1.00First 9835-098 Clear Lacquer, Water-White, Gloss 205 0.80Second 9835-098 Clear Lacquer, Water-White, Gloss 205 0.80Finish 9835-098 Clear Lacquer, Water-White, Gloss 205 0.80

Total Dry Mils 3.40

01.F Interior Wood, Natural, Satin-Gloss Lacquer System


Prime 9835-165 Lacquer Sanding Sealer Water-White 152 1.00First 9835-100 Clear Lacquer, Water-White, Satin 205 0.80Second 9835-100 Clear Lacquer, Water-White, Satin 205 0.80Finish 9835-100 Clear Lacquer, Water-White, Satin 205 0.80

Total Dry Mils 3.40

02 INTERIOR WOOD, PAINTED FINISHES

02.A Interior Wood, Vinyl Latex Flat Finish. Residential, Commercial & Light Industrial ServiceCoat Product Premium Quality VOC Sq.Ft. Mils

Prime 319-8 COVENTRY®Acrylic Enamel Undercoat 0.76 351 1.50First 35-Series COVENTRY® Flat Wall Finish 0.83 375 1.50Finish 35-Series COVENTRY® Flat Wall Finish 0.83 375 1.50

Total Dry Mils 4.50

02.B Interior Wood, Acrylic Latex Eggshell Enamel System, Residential, Commercial & Light Industrial Service


Prime 319-8 COVENTRY® Acrylic Enamel Undercoat 0.76 351 1.50First 2335-Series COVENTRY® Premium Eggshell Enamel 0.86 375 1.50Finish 2335-Series COVENTRY® Premium Eggshell Enamel 0.86 375 1.50

Total Dry Mils 4.50



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

02.C Interior Wood, Acrylic Latex Semi-Gloss Enamel System Residential, Commercial & Light Industrial Service


Prime 319-8 COVENTRY® Acrylic Enamel Undercoat 0.76 351 1.50First 1335-Line COVENTRY® Semi-gloss Acrylic Enamel 2.00 345 1.50Finish 1335-Line COVENTRY® Semi-gloss Acrylic Enamel 2.00 345 1.50

Total Dry Mils 4.50

02.D Interior Wood, Acrylic High Gloss Enamel System Residential, Commercial & Light Industrial Service


Prime 319-8 COVENTRY® Acrylic Enamel Undercoat 0.76 351 1.50First 335-Series COVENTRY® Acrylic High Gloss Enamel 1.09 408 1.50Finish 335-Series COVENTRY® Acrylic High Gloss Enamel 1.09 408 1.50

Total Dry Mils 4.50

02.E Interior Wood, 100% Acrylic Gloss Enamel System, Residential, Commercial & Light Industrial Service


Prime 319-8 COVENTRY® Acrylic Enamel Undercoat 0.76 351 1.50First 330-Series ACR-A-LACTM 100% Acrylic Gloss Enamel 2.11 293 2.00Finish 330-Series ACR-A-LACTM 100% Acrylic Gloss Enamel 2.11 293 2.00

Total Dry Mils 5.50

02.F Interior Wood, 100% Acrylic Gloss DTM Enamel System, Residential, Commercial & Light Industrial Service


Prime 319-8 COVENTRY® Acrylic Enamel Undercoat 0.76 351 1.50First 310-Series H2O RUS-KIL® DTM Acrylic Enamel 1.09 295 2.00Finish 310-Series H2O RUS-KIL® DTM Acrylic Enamel 1.09 295 2.00

Total Dry Mils 5.50



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

02.G Interior Wood, Fire Retardant Finishing System, Residential, Commercial & Light Industrial Service


Prime 319-8 COVENTRY® Acrylic Enamel Undercoat 0.76 351 1.50First 9835-239 FIRECOAT 320 0.80 145 4.00Second 9835-239 FIRECOAT 320 0.80 145 4.00Finish with any of the above-listed topcoatsConsult your BLP Mobile Paints service representative for details.

Total Dry Mils 9.50

02.H Interior Wood, Latex Flat System, Residential, Commercial & Light Industrial Service


Prime 219-8 SMOOTH-COTE® Enamel Undercoat 0.79 347 1.50First 289-line SMOOTH-COTE® Interior Latex Flat 0.89 346 1.50Finish 289-line SMOOTH-COTE® Interior Latex Flat 0.89 346 1.50

Total Dry Mils 4.50

02.I Interior Wood, Latex Semi-gloss System, Residential, Commercial & Light Industrial Service


Prime 219-8 SMOOTH-COTE® Enamel Undercoat 0.79 347 1.50First 290-line SMOOTH-COTE® Int. Latex Semi-gloss 1.60 252 1.50Finish 290-line SMOOTH-COTE® Int. Latex Semi-gloss 1.60 252 1.50

Total Dry Mils 4.50

02.J Interior Wood, Latex Eggshell System, Residential, Commercial & Light Industrial Service


Prime 219-8 SMOOTH-COTE® Enamel Undercoat 0.79 347 1.50First 292-line SMOOTH-COTE® Int. Latex Eggshell 0.85 395 1.50Finish 292-line SMOOTH-COTE® Int. Latex Eggshell 0.85 395 1.50

Total Dry Mils 4.50



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

02.K Interior Wood, Alkyd Semi-Gloss Enamel System, Residential, Commercial & Light Industrial Service


Prime 19-8 COVENTRY® Alkyd Enamel Undercoat 3.35 387 2.00First 135-Series COVENTRY® Lustarite Satin-Gloss 3.04 427 2.00Finish 135-Series COVENTRY® Lustarite Satin-Gloss 3.04 427 2.00

Total Dry Mils 6.00

02.L Interior Wood, Alkyd Gloss Enamel System, Residential, Commercial & Light Industrial Service


Prime 19-8 COVENTRY®Alkyd Enamel Undercoat 3.35 3.87 2.00First 30-Series NAM-A-LAC® Gloss Enamel 3.18 409 1.50Finish 30-Series NAM-A-LAC® Gloss Enamel 3.18 409 1.50

Total Dry Mils 5.00

02.M Interior Wood, Alkyd Gloss Enamel System, Residential, Commercial & Light Industrial Service

Coat Product Premium Industrial Quality VOC Sq.Ft. Mils

Prime 19-8 COVENTRY® Alkyd Enamel Undercoat 3.35 387 2.00First 10-Series RUS-KIL® Alkyd Gloss Enamel 3.35 385 2.00Finish 10-Series RUS-KIL® Alkyd Gloss Enamel 3.35 385 2.00

Total Dry Mils 6.00

02.N Interior Wood, Amide High Solids Epoxy Semi-gloss System,Residential, Com. & Light Industrial Service


Prime* 613-Series MOPOXYTM HS Semi-gloss Epoxy 2.00 374 3.00First 613-Series MOPOXYTM HS Semi-gloss Epoxy 2.00 374 3.00Finish 613-Series MOPOXYTM HS Semi-gloss Epoxy 2.00 374 3.00*Thin first coat 20% with MOPOXYTM Brushing Thinner 75-35

Total Dry Mils 9.00



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

02.O Interior Wood, Amide High Solids Epoxy High-Gloss System, Residential, Com. & Light Industrial Service


Prime* 513-Series MOPOXYTM High Gloss Epoxy 4.30 314 2.00First 513-Series MOPOXYTM High Gloss Epoxy 4.30 314 2.00Finish 513-Series MOPOXYTM High Gloss Epoxy 4.30 314 2.00*Thin first coat 20% with MOPOXY Brushing Thinner 75-35

Total Dry Mils 6.00

02.P Interior Wood, Waterborne Acrylic Epoxy High Gloss System


Prime* 69-AW-5 MOPOXYTM H2O-100 White 1.71 313 2.00First 69-AW-5 MOPOXYTM H2O-100 White 1.71 313 2.00Finish 69-AW-5 MOPOXYTM H2O-100 White 1.71 313 2.00*Thin first coat 20% with Water

Total Dry Mils 6.00

02.Q Interior Wood, Waterborne Amide Epoxy Semi-Gloss System


Prime* 69-AW-6 MOPOXYTM H2O-200 White 1.00 225 2.00First 69-AW-6 MOPOXYTM H2O-200 White 1.00 225 2.00Finish 69-AW-6 MOPOXYTM H2O-200 White 1.00 225 2.00*Thin first coat 20% with Water

Total Dry Mils 6.00

02.R Interior Wood, White or Tinted Gloss Lacquer System


Prime 9835-172 Lacquer Sanding Sealer Hi-Build WhiteFirst 9835-line Lacquer Tint Base 345 1.00Second 9835-line Lacquer Tint Base 345 1.00Third 9835-line Lacquer Tint Base 345 1.00

Total Dry Mils 3.00



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

02.S Interior Wood, Alkyd Semi-gloss System, Residential, Commercial & Light Industrial Service


Prime 219-8 SMOOTH-COTE® Enamel Undercoat 0.79 347 1.50First 293-line SMOOTH-COTE® Int Alkyd Semi-gloss 2.85 449 2.00Finish 293-line SMOOTH-COTE® Int Alkyd Semi-gloss 2.85 449 2.00

Total Dry Mils 5.50

03 EXTERIOR WOOD FINISHES, NATURAL GRAIN

03.A Exterior Wood, Natural Finish, Oil-based Sealer & Preservative, Residential & Commercial Service


Prime 7-10 WEATHER-PROTECTOR® Sealer 4.61 150 0.50Finish 7-10 WEATHER-PROTECTOR® Sealer 4.61 150 0.50

Penetrating finish, film thickness cannot be accurately measured

Total Dry Mils 1.00

03.B Exterior Wood, Natural Finish, Clear Waterproofer (Paintable), Residential & Commercial Service


Prime 74-7 WEATHER-TITE® Clear Waterproofing 5.30 150 0.50Finish 74-7 WEATHER-TITE® Clear Waterproofing 5.30 150 0.50


Total Dry Mils 1.00



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

03.C Exterior Wood, Natural Finish, Waterborne Clear Waterproofer (Paintable), Residential & Commercial Service


Prime 74-17 H2O WEATHER-TITE® Clear 0.68 150 0.50Finish 74-17 H2O WEATHER-TITE® Clear 0.68 150 0.50


Total Dry Mils 1.00

03.D Exterior Wood, Natural Finish, Acrylic Wood Stain,Residential & Commercial Service


Prime 44-Line WEATHER PROTECTOR® Acrylic Stain 1.77 275 1.50Finish 44-Line WEATHER PROTECTOR® Acrylic Stain 1.77 275 1.50

Total Dry Mils 3.00

03.E Exterior Wood, 100% Phenolic Marine Spar Varnish


Prime 470-31 JACK TAR® 100% Phenolic Spar Varnish 3.79 657 1.00First 470-31 JACK TAR® 100% Phenolic Spar Varnish 3.79 657 1.00Finish 470-31 JACK TAR® 100% Phenolic Spar Varnish 3.79 657 1.00

Total Dry Mils 3.00

03.F Exterior Wood, Marine Spar Varnish with Ultraviolet Filter


Prime 470-34 JACK TAR® Spar Varnish, UV Filter 3.82 657 1.00First 470-34 JACK TAR® Spar Varnish, UV Filter 3.82 657 1.00Finish 470-34 JACK TAR® Spar Varnish, UV Filter 3.82 657 1.00

Total Dry Mils 3.00



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

04 EXTERIOR WOOD, PAINTED FINISH

04.A Exterior Wood, Southernized Oil-Based Gloss House Paint


Prime 5-6 WEATHER-TITE® Oil Base Primer 2.93 440 2.00First 5-Series WEATHER-TITE® Oil Base House Paint 1.28 645 2.00Finish 5-Series WEATHER-TITE® Oil Base House Paint 1.28 645 2.00

Total Dry Mils 6.00

04.B Exterior Wood, 100% Acrylic Flat Finish House Paint


Prime 6-6 WEATHER-TITE® 100% Acrylic Primer 1.17 393 2.00First 40-Series WEATHER-TITE® 100% Acrylic Flat 1.03 291 2.00Finish 40-Series WEATHER-TITE® 100% Acrylic Flat 1.03 291 2.00

Total Dry Mils 6.00

04.C Exterior Wood, 100% Acrylic Gloss Finish House Paint


Prime 6-6 WEATHER-TITE® 100% Acrylic Primer 1.17 393 2.00First 140-Series WEATHER-TITE® 100% Acrylic Gloss 1.99 296 2.00Finish 140-Series WEATHER-TITE® 100% Acrylic Gloss 1.99 296 2.00

Total Dry Mils 6.00

04.D Exterior Wood, 100% Acrylic Satin Finish House Paint


Prime 6-6 WEATHER-TITE® 100% Acrylic Primer 1.17 393 2.00First 240-Series WEATHER-TITE® 100% Acrylic Satin 2.19 271 2.00Finish 240-Series WEATHER-TITE® 100% Acrylic Satin 2.19 271 2.00

Total Dry Mils 6.00



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

04.E Exterior Wood, Silicone Alkyd Yacht Finish, High Gloss

Coat Product Premium Marine Quality VOC Sq.Ft. Mils

Prime* 432-Series JACK TAR® Silicone Yacht Finish 3.57 484 1.50First 432-Series JACK TAR® Silicone Yacht Finish 3.57 484 1.50Finish 432-Series JACK TAR® Silicone Yacht Finish 3.57 484 1.50* Thin 10% with MOPAXOL Thinner 75-1

Total Dry Mils 4.50

04.F Exterior Wood, Acrylic Flat Finish, Residential, Commercial & Light Industrial Service


Prime 206-10 SMOOTH-COTE® 100% Acrylic Primer 1.48 387 1.50First 291-line SMOOTH-COTE® Vinyl Acrylic Flat 1.30 290 1.50Finish 291-line SMOOTH-COTE® Vinyl Acrylic Flat 1.30 290 1.50

Total Dry Mils 4.50

04.G Exterior Wood, Acrylic Gloss Finish, Residential, Commercial & Light Industrial Service


Prime 206-10 SMOOTH-COTE® 100% Acrylic Primer 1.48 387 1.50First 294-line SMOOTH-COTE® 100% Acrylic Gloss 1.48 377 1.50Finish 294-line SMOOTH-COTE® 100% Acrylic Gloss 1.48 377 1.50

Total Dry Mils 4.50

04.H Exterior Wood, Acrylic Semi-gloss Finish, Residential, Commercial & Light Industrial Service


Prime 206-10 SMOOTH-COTE® 100% Acrylic Primer 1.48 387 1.50First 295-line SMOOTH-COTE® 100% Acrylic Semi-gloss 1.54 335 1.50Finish 295-line SMOOTH-COTE® 100% Acrylic Semi-gloss 1.54 335 1.50

Total Dry Mils 4.50



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

04.I Exterior Wood, Acrylic Flat Finish, Residential, Commercial & Light Industrial Service


Prime 206-10 SMOOTH-COTE® 100% Acrylic Primer 1.48 387 1.50First 296-line SMOOTH-COTE® 100% Acrylic Flat 1.25 283 1.50Finish 296-line SMOOTH-COTE® 100% Acrylic Flat 1.25 283 1.50

Total Dry Mils 4.50


Floor & Deck Finishing Specifications1

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

RECOMMENDED FINISHING SPECIFICATIONS

FOR FLOORS AND DECKS

Beautiful floors are the focal point of any room or area.

A gleaming floor is the joy of any homemaker and the hallmark of an efficient and well run commercial or industrialestablishment.

Decks, terraces, walks and piers enhance the exterior beauty of homes, hotels, marinas and other areas.

This section includes a full range of floor finishing systems for residential, commercial, light industrial and heavyindustrial applications, both interior and exterior, and is divided as follows:

SURFACE PREPARATION

RECOMMENDED PRODUCTS

01 INTERIOR WOODEN FLOORS

02 INTERIOR CONCRETE FLOORS

03 INTERIOR STEEL DECKING

04 EXTERIOR WOOD DECKS

05 EXTERIOR CONCRETE DECKS

06 EXTERIOR STEEL DECKS

A comprehensive index will be found on the next page

Please consult your BLP Mobile Paints representative for specific recommendations.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

SURFACE PREPARATION

INTERIOR WOODEN FLOORS

New wooden floors should be inspected carefully prior to finishing. Nail holes should be filled and the floor sandedwith fine sandpaper to a smooth finish. All dust must be removed. Good ventilation is essential. Never paint orvarnish on days of high humidity or rain. Follow instructions exactly for a finish of which to be proud.

GOOD VENTILATION IS ESSENTIAL TO ASSURE PROPER EVAPORATION OF SOLVENTS AND PREVENTDANGEROUS ACCUMULATIONS OF FUMES.

CONCRETE FLOORS

Moisture damage is the major cause of paint failure as well as the lifting of other types of flooring laid over concretefloors at or below grade level. A moisture barrier installed prior to construction will prevent the percolation ofmoisture through the slab. Omission of this moisture barrier is almost impossible to correct and seriously limits theselection and durability of the finish.

Bare concrete should always be etched with muriatic acid and rinsed with clear water to remove the laitance whichis a natural result of trowelling and to leave the surface porous and receptive to paint. The surface must be clean,dry and dust free.

Previously sealed concrete presents a series of problems beginning with the correct identification of the sealerused and whether it can be removed to allow the adhesion of paint. Please check with your BLP Mobile Paintrepresentative for specific recommendations.

STEEL DECKING

Surface preparation is covered in Ferrous Metals in this book. Solvent clean steel iaw SSPC-SP 1 to removegrease and oil. “Near-White Blast Cleaning” iaw SSPC-SP 10 is recommended; “Commercial Blast” iaw SSPC-SP 6 should be considered minimum acceptable preparation for marine environments.

If abrasive cleaning is not possible because of mechanical or environmental considerations, “Power Tool Clean”iaw SSPC-SP 3 and treat as in the section on Maintenance Upgrade Systems under Ferrous Metals.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

RECOMMENDED PRODUCTS

All products are lead-free, chromate-free, mercury-free and VOC-compliant.

NUWOOD® Penetrating Wood Finish, 71-Series, is a polyurethane stain or wood finish.

NUWOOD® Polyurethane Varnish - Very pale, durable, with excellent resistance to abrasion, hot and cold water,acid, alkali, grease, alcohol and soil. Recommended for homes, public buildings, institutions, schools andgymnasiums. Available in Gloss, 72-35, and Satin, 72-36.

FLO-TEC® Phenolic HD Gym Floor Finish - Low viscosity wood finish which penetrates into the pores of thewood, sealing the surface and hardening the wood fibers to a considerable depth. Leaves no varnish film on thesurface. Highly recommended for gymnasium floors as well as other residential and institutional uses.

WEATHER-TITE® Waterproofing Sealer, Clear, 74-7 -clear waterproofing which penetrates and repels water,protecting against rot and mildew. Does not change color or appearance of wood. Easy to apply. Contains nosilicones, may be painted after 24 hours.

WEATHER-TITE® H2O Waterproofing Clear, 74-17 - a clear, waterborne, paintable waterproofing sealer for masonry,wood, canvas and fabric. Contains no silicones. Low odor.

DUB-L-TITETM Silicone Waterproofing, Clear, 74-12 - a clear silicone waterproofing for masonry surfaces.Penetrates and repels water while allowing the surface to breathe. Forms no film and does not change color. Easyto apply. .

WEATHER-TITE H2O Dub-L-Tite Clear Waterproofing, 74-13 - a clear waterborne silicone/silane sealer for exteriormasonry surfaces. Forms no film and will not change the appearance of the surface.

H2O Concrete Stain, 308-Series - a waterborne polyurethane acrylic stain with good color and gloss retention andexcellent abrasion resistance..SPEEDECK® Polyurethane Floor & Deck Enamel - a polyurethane modified alkyd enamel - Excellent protectionagainst abrasion and weather in mild industrial and marine environments. Good color and gloss retention. Availablein stock colors as seen on the color card and in a wide range of custom colors.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

H2O Acrylic Floor & Patio Satin Finish, 350-Series - Waterborne polyurethane modified acrylic enamel for interiorand exterior service. Good color and gloss retention, excellent abrasion resistance. Available in stock colors asseen on the color card and in a wide range of custom colors.

JACK TAR® Silicone Yacht Finish, 432 Line - Silicone Alkyd Enamel - All of the advantages and color range ofalkyd enamels plus outstanding gloss and color retention under ultraviolet. Unsurpassed for residential, commercial,institutional, industrial and marine use.

MOPOXYTM- our brand name for our complete line of catalyzed epoxies. Extremely durable, excellent chemicaland abrasion resistance. Recommended for residential, institutional, commercial and industrial service.

MOTHANE - our brand name for our line of catalyzed polyurethane. Extremely durable, excellent chemical andabrasion resistance. Outstanding gloss and color retention. Recommended for residential, institutional, commercialand industrial service.

MOPOXYTM H2O-200 Waterborne Amide Epoxy - very good abrasion, moisture and chemical resistance. Lowodor. Semi-gloss finish. Very low VOC

MOPOXYTM HS High Solids Epoxy - a high-solids amide cured epoxy with excellent chemical, moisture andabrasion resistance.

MOPOXY-PLUSTM is a high solids, high build, surface tolerant epoxy with excellent abrasion, moisture and chemicalresistance.

MOPOXYTM PRE-PREP Sealer, Clear, 41-AF-2, is a two component, 0 VOC, 100% solids epoxy which is almostwater-thin with exceptional penetration properties. MOPOXY PRE-PREP requires 48 hours at 75 F for full cure.Allow to dry overnight and apply finish coat while the prime coat is still slightly tacky. If a clear sealer is desired,apply a second coat of MOPOXY PRE-PREP as a finish coat.

MOPOXYTM AR-100 Deck Armor, 41-BW-1, is a 100% solids, 0 VOC, high performance deck coating with excellentresistance to moisture, abrasion and mechanical damage and good resistance to most solvents and chemicals.Apply by airless spray at the rate of 26 square feet per gallon to produce a dry film thickness of 60 mils.

MOPOXYTM NS-200 Non-Skid Deck Armor, 41-BW-12, is a 94.9% solids, very low VOC, high performance deckcoating with excellent resistance to moisture, abrasion and mechanical damage and good resistance to mostsolvents and chemicals. Apply by brush, roller of trowel at the rate of 24 square feet per gallon to produce a dryfilm thickness of 60 mils.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

INTERIOR FLOOR FINISHING SYSTEMS

01 WOOD FLOORS, INTERIOR, RESIDENTIAL & COMMERCIAL SERVICE

01.A Interior Wood Floors, Natural, Gloss Polyurethane Varnish System

Coat Product Residential & Commercial Service VOC Sq.Ft. Mils

Prime 71-Series NUWOOD® Penetrating Wood Stain 4.61 750 N/AFirst 72-35 NUWOOD® Polyurethane Gloss Finish 3.77 673 1Finish 72-35 NUWOOD® Polyurethane Gloss Finish 3.77 673 1

Total Dry Mils 2.0

01.B Interior Wood Floors, Natural, Satin-Gloss Polyurethane Varnish System

Coat Product Residential & Commercial Service VOC Sq.Ft. Mils

Prime 71-Series NUWOOD® Penetrating Wood Stain 4.61 750 N/AFirst 72-36 NUWOOD® Polyurethane Satin Finish 3.77 673 1Finish 72-36 NUWOOD® Polyurethane Satin Finish 3.77 673 1

Total Dry Mils 2.0

01.C Interior Wood Floors, Natural, Phenolic Gym Floor Finish

Coat Product Commercial & Institutional Service VOC Sq.Ft. Mils

Prime 70-41 FLO-TEC Phenolic HD Gym Floor Finish 4.45 500 1First 70-41 FLO-TEC Phenolic HD Gym Floor Finish 4.45 500 1Finish 70-41 FLO-TEC Phenolic HD Gym Floor Finish 4.45 500 1

Total Dry Mils 3.0

01.D Interior Wood Floors, Waterborne Polyurethane Acrylic Satin Enamel Finish

Coat Product Residential & Light Commercial Service VOC Sq.Ft. Mils

Prime 6-06 WEATHER-TITE Acrylic Universal Primer 1.17 393 1.5First 350-Series H2O Acrylic Floor & Patio Finish 2.00 305 2Finish 350-Series H2O Acrylic Floor & Patio Finish 2.00 305 2

Total Dry Mils 5.5



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

01.E Interior Wood Floors, Polyurethane Gloss Enamel Finish


Prime* 50-Series SPEEDECK® Polyurethane Enamel 3.35 388 2Finish 50-Series SPEEDECK® Polyurethane Enamel 3.35 388 2

*Thin 10% with MoPaxOl® Thinner 75-1 on new wood

Total Dry Mils 4.0

01.F Interior Wood Floors, Waterborne Amide Epoxy Semi-gloss Finish

Coat Product Commercial & Light Industrial Service VOC Sq.Ft. Mils

Prime* 69-AW-6 MOPOXYTM H2O-200 Epoxy Coating. 1.00 225 3Finish 69-AW-6 MOPOXYTM H2O-200 Epoxy Coating. 1.00 225 3

*Thin 20% with MOPOXYTM H2O Thinner 43-EF-89 on new wood

Total Dry Mils 6.0

01.G Interior Wood Floors, Catalyzed Polyamide Epoxy Semi-gloss Finish


Prime* 613-Series MOPOXYTM HS High Solids Epoxy Coating. 2.10 374 3Finish 613-Series MOPOXYTM HS High Solids Epoxy Coating. 2.10 374 3

*Thin 10% with MOPOXYTM Brushing Thinner 75-35 on new wood

Total Dry Mils 6.0

01.H Interior Wood Floors, Catalyzed Polyamide Epoxy High-gloss Finish


Prime* 513-Series MOPOXYTM High Gloss Epoxy Coating. 5.14 314 2Finish 513-Series MOPOXYTM High Gloss Epoxy Coating. 5.14 314 2

*Thin 10% with MOPOXYTM Brushing Thinner 75-35 on new wood

Total Dry Mils 4.0



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

02 C0NCRETE FLOORS, INTERIOR, RESIDENTIAL, COMMERCIAL & INDUSTRIAL

02.A Interior Concrete Floors, Waterborne Polyurethane Acrylic Satin Finish


Prime 308-Series H2O Concrete Stain, Satin Gloss 2.00 374 1.5Finish 308-Series H2O Concrete Stain, Satin Gloss 2.00 374 1.5

Total Dry Mils 3.0

02.B Interior Concrete Floors, Waterborne Polyurethane Acrylic Enamel Satin Finish


Prime 350-Series H2O Acrylic Floor & Patio Satin Finish 2.00 305 2Finish 350-Series H2O Acrylic Floor & Patio Satin Finish 2.00 305 2

Total Dry Mils 4.0

02.C Interior Concrete Floors, Polyurethane Enamel Gloss Finish


Prime* 50-Series SPEEDECK® Polyurethane Enamel 3.35 388 2Finish 50-Series SPEEDECK® Polyurethane Enamel 3.35 388 2

*Thin 10% with MoPaxOl® Thinner 75-1 on new concrete

Total Dry Mils 4.0

02.D Interior Concrete Floors, Waterborne Catalyzed Epoxy System, Semi-Gloss Finish

Coat Product Commercial & Industrial Service VOC Sq.Ft. Mils

Prime* 69-AW-6 MOPOXY H2O-200 Amide Epoxy 1.00 225 3First 69-AW-6 MOPOXY H2O-200 Amide Epoxy 1.00 225 3Second 69-AW-6 MOPOXY H2O-200 Amide Epoxy 1.00 225 3

*May be thinned slightly with water to improve penetration on new concrete

Total Dry Mils 9.0



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

02.E Interior Concrete Floors, High-Solids Catalyzed Epoxy System, Semi-Gloss Finish


Prime* 613-Series MOPOXY HS High Solids Epoxy 2.10 374 3First 613-Series MOPOXY HS High Solids Epoxy 2.10 374 3Finish 613-Series MOPOXY HS High Solids Epoxy 2.10 374 3

* Thin 20% with MOPOXY Brushing Thinner, 75-35 on new concrete

Total Dry Mils 9.0

02.F Interior Concrete Floors, Catalyzed Epoxy System, High-Gloss Finish


Prime* 513-Series MOPOXY High Gloss Epoxy Coating. 5.14 314 2First 513-Series MOPOXY High Gloss Epoxy Coating. 5.14 314 2Finish 513-Series MOPOXY High Gloss Epoxy Coating. 5.14 314 2

* Thin 20% with MOPOXY Brushing Thinner, 75-35 on new concrete

Total Dry Mils 6.0

02.G Interior Concrete Floors, High Build Epoxy System, Semi-Gloss Finish

Coat Product Heavy Industrial Service VOC Sq.Ft. Mils

Prime 41-AF-2 MOPOXY-PREP Epoxy Sealer 0.00 1069 1.5First 41-CW-1 MOPOXY-PLUS HB HS Epoxy 2.36 131 8Second 613-Series MOPOXY HS High Solids Epoxy 2.10 374 3Finish* 613-Series MOPOXY HS High Solids Epoxy 2.10 374 3

*Add JACK TAR Non-Skid, 492-03, for anti-skid properties

Total Dry Mils 15.5

02.H Interior Concrete Floors, 100% Solids Epoxy Finish


Prime 41-AF-2 MOPOXY-PREP Epoxy Sealer 0.00 1069 1.5Finish 41-BW-1* MOPOXY AR-100 Deck Armor 0.00 26 60

*Apply by airless spray or trowel

Total Dry Mils 61.5



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

02.I Interior Concrete Floors, High Solids Non-Skid Epoxy Finish


Prime** 41-AF-2 MOPOXY-PREP Epoxy Sealer 0.00 1069 1.5Finish 41-BW-12* MOPOXY NS-200 Non-Skid Deck Armor 0.75 24 60

*Apply by brush, roller or trowel** Alternate Primer: MOPOXY HS Epoxy 613-line

Total Dry Mils 61.5

03 STEEL DECKING, INTERIOR, RESIDENTIAL, COMMERCIAL & INDUSTRIAL SERVICE

03.A Interior Steel Decking, Polyurethane Gloss Enamel Finish


Prime 10-10 RUS-KIL® Metal Primer, Red 3.35 395 2First 50-Series SPEEDECK® Polyurethane Enamel 3.35 388 1.5Finish 50-Series SPEEDECK® Polyurethane Enamel 3.35 388 1.5

Total Dry Mils 5.0

03.B Interior Steel Decking, Waterborne Catalyzed Epoxy System, Semi-Gloss Finish


Prime 69-DR-1 MOPOXY H2O-200 Metal Primer 0.89 257 3First 69-AW-6 MOPOXY H2O-200 Amide Epoxy 1.00 225 3Finish* 69-AW-6 MOPOXY H2O-200 Amide Epoxy 1.00 225 3

* Add JACK TAR Non-Skid 492-3 to finish coat for anti-skid properties

Total Dry Mils 9.0

03.C Interior Steel Decking, High-Solids Catalyzed Epoxy System, Semi-Gloss Finish


Prime 613-10 MOPOXY HS High Solids Epoxy Primer 2.00 382 3First 613-Series MOPOXY HS High Solids Epoxy 2.10 374 3Finish* 613-Series MOPOXY HS High Solids Epoxy 2.10 374 3


Total Dry Mils 9.0



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

03.D Interior Steel Decking, Catalyzed Epoxy System, High-Gloss Finish


Prime 513-10 MOPOXY Epoxy Primer 4.24 322 2First 513-Series MOPOXY High Gloss Epoxy Coating. 5.14 314 2Finish* 513-Series MOPOXY High Gloss Epoxy Coating. 5.14 314 2


Total Dry Mils 6.0

03.E Interior Steel Decks, High Build Epoxy System, Semi-Gloss Finish

Coat Product Commercial, Industrial & Marine Service VOC Sq.Ft. Mils

Prime 613-10 MOPOXY HS High Solids Epoxy Primer 2.00 382 3First 41-CW-1 MOPOXY-PLUS HB HS Epoxy 2.36 131 8Second 613-Series MOPOXY HS High Solids Epoxy 2.10 374 3Finish* 613-Series MOPOXY HS High Solids Epoxy 2.10 374 3


Total Dry Mils 17.0

03.F Interior Steel Decking, 100% Solids Epoxy Finish

Coat Product Heavy Industrial & Marine Service VOC Sq.Ft. Mils

Prime 613-10 MOPOXY HS High Solids Epoxy Primer 2.00 382 3Finish 41-BW-1* MOPOXY AR-100 Deck Armor 0.00 26 60


Total Dry Mils 63.0

03.G Interior Steel Decking, High Solids Non-Skid Epoxy Finish


Prime 613-10 MOPOXY HS High Solids Epoxy Primer 2.00 382 3Finish 41-BW-12* MOPOXY NS-200 Non-Skid Deck Armor 0.75 24 60

*Apply by brush, roller or trowel

Total Dry Mils 63.0

Mobile Paints has a wide selection of specialized epoxies. We invite your inquiry.



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

EXTERIOR FLOOR & DECK FINISHING SYSTEMS

04 WOOD DECKS, EXTERIOR - RESIDENTIAL, COMMERCIAL, MARINE SERVICE

04.A Exterior Wooden Decks, Clear Waterborne Waterproofing, Natural Finish


Prime 74-17 H2O WEATHER-TITE® Clear Waterproofing 0.68 100 N/AFinish 74-17 H2O WEATHER-TITE® Clear Waterproofing 0.68 100 N/A

Total Dry Mils 0.0

04.B Exterior Wooden Decks, Clear Waterproofing, Natural Finish


Prime 74-7 WEATHER-TITE® Clear Waterproofing 6.14 100 N/AFinish 74-7 WEATHER-TITE® Clear Waterproofing 6.14 100 N/A

Total Dry Mils 0.0

04.C Exterior Wood Decks, Waterborne Polyurethane Enamel, Satin Gloss Finish


Prime 6-6 WEATHER-TITE Acrylic Universal Primer 1.17 393 1.5Finish 350-Series H2O Acrylic Floor & Patio Satin Finish 2.00 305 2Second 350-Series H2O Acrylic Floor & Patio Satin Finish 2.00 305 2

Total Dry Mils 5.5

04.D Exterior Wood Decks, Polyurethane Enamel, Gloss Finish


Prime* 50-Series SPEEDECK® Polyurethane Enamel 3.35 388 1.5First 50-Series SPEEDECK® Polyurethane Enamel 3.35 388 1.5Finish 50-Series SPEEDECK® Polyurethane Enamel 3.35 388 1.5


Total Dry Mils 4.5



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

04.E Exterior Wood Decks, Silicone Alkyd Enamel, Gloss Finish

Coat Product Residential, COMMERCIAL & Marine Service VOC Sq.Ft. Mils

Prime* 432-Line JACK TAR® Silicone Yacht Finish 3.57 484 1.5Second 432-Line JACK TAR® Silicone Yacht Finish 3.57 484 1.5Finish 432-Line JACK TAR® Silicone Yacht Finish 3.57 484 1.5


Total Dry Mils 4.5

05 CONCRETE FLOORS & DECKS, EXTERIOR FINISHING SYSTEMS

05.A Exterior Concrete Decks, Clear Waterborne Silicone Waterproofing, Natural Finish

Coat Product Residential, Commercial & Marine Service VOC Sq.Ft. Mils

Prime 74-13 WEATHER-TITE ® H2O Dub-L-Tite Clear 0.00 100 N/AFinish 74-13 WEATHER-TITE® H2O Dub-L-Tite Clear 0.00 100 N/A

Total Dry Mils 0.0

05.B Exterior Concrete Decks, Clear Silicone Waterproofing, Natural Finish


Prime 74-12 DUB-L-TITE Clear Waterproofing 6.19 100 N/AFinish 74-12 DUB-L-TITE Clear Waterproofing 6.19 100 N/A

Total Dry Mils 0.0

05.C Exterior Concrete Decks, Waterborne Polyurethane Acrylic Stain, Satin Finish


Prime 308-Series H2O Concrete Stain 2.00 374 1.5First 308-Series H2O Concrete Stain 2.00 374 1.5Finish 308-Series H2O Concrete Stain 2.00 374 1.5

Total Dry Mils 4.5



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

05.D Exterior Concrete Decks, Waterborne Polyurethane Acrylic Enamel, Satin Gloss Finish


Prime 350-Series H2O Acrylic Floor & Patio Satin Finish 2.00 305 2First 350-Series H2O Acrylic Floor & Patio Satin Finish 2.00 305 2Finish 350-Series H2O Acrylic Floor & Patio Satin Finish 2.00 305 2

Total Dry Mils 6.0

05.E Exterior Concrete Decks, Polyurethane Enamel, Gloss Finish, Residential, Commercial & Marine Service


Prime* 50-Series SPEEDECK® Polyurethane Enamel 3.35 388 1.5First 50-Series SPEEDECK® Polyurethane Enamel 3.35 388 1.5Finish 50-Series SPEEDECK® Polyurethane Enamel 3.35 388 1.5


Total Dry Mils 4.5

05.F Exterior Concrete Decks, Silicone Alkyd Enamel, Gloss Finish


Prime* 432-Line JACK TAR® Silicone Yacht Finish 3.57 484 1.5Second 432-Line JACK TAR® Silicone Yacht Finish 3.57 484 1.5Finish 432-Line JACK TAR® Silicone Yacht Finish 3.57 484 1.5


Total Dry Mils 4.5



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

06 STEEL DECKING, EXTERIOR, RESIDENTIAL, COMMERCIAL & INDUSTRIAL SERVICE

06.A Exterior Steel Decking, Polyurethane Gloss Enamel Finish


Prime 10-10 RUS-KIL® Metal Primer, Red 3.35 395 2First 50-Series SPEEDECK® Polyurethane Enamel 3.35 388 1.5Finish* 50-Series SPEEDECK® Polyurethane Enamel 3.35 388 1.5

* Add JACK TAR® Non-Skid 492-3 to finish coat for anti-skid properties

Total Dry Mils 5.0

06.B Exterior Steel Decks, Silicone Alkyd Enamel, Gloss Finish


Prime 10-10 RUS-KIL® Metal Primer, Red 3.35 395 2First 432-Line JACK TAR® Silicone Yacht Finish 3.57 484 1.5Finish* 432-Line JACK TAR® Silicone Yacht Finish 3.57 484 1.5


Total Dry Mils 5.0

06.C Exterior Steel Decking, High-Solids Epoxy/Polyurethane System, High Gloss Finish

Coat Product Industrial & Marine Service VOC Sq.Ft. Mils

Prime 613-10 MOPOXY HS High Solids Epoxy Primer 2.00 382 3First 613-Series MOPOXY HS High Solids Epoxy 2.10 374 3Second 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish* 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2


Total Dry Mils 10.0



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

06.D Exterior Steel Decks, High Build Epoxy/Polyurethane System, High Gloss Finish


Prime 613-10 MOPOXY HS High Solids Epoxy Primer 2.00 282 3First 41-CW-1 MOPOXY-PLUS HB HS Epoxy 2.36 131 8Second 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish* 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2


Total Dry Mils 15.0

06.E Exterior Steel Decking, 100% Solids Epoxy Finish


Prime 613-10 MOPOXY HS High Solids Epoxy Primer 2.00 282 3Finish 41-BW-1* MOPOXY AR-100 Deck Armor 0.00 26 60


Total Dry Mils 63.0

06.G Exterior Steel Decking, High Solids Non-Skid Epoxy Finish


Prime 613-10 MOPOXY HS High Solids Epoxy Primer 2.00 382 3Finish 41-BW-12* MOPOXY NS-200 Non-Skid Deck Armor 0.75 24 60

*Apply by brush, roller or trowel

Total Dry Mils 63.0

Mobile Paints has a wide selection of specialized epoxies. We invite your inquiry.

1

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Water Storage Tanks Systems

RECOMMENDED PAINTING SPECIFICATIONS FOR WATER STORAGE TANKS

This section covers interior finishes for water storage tanks for potable water, for fire protection water, raw process waterand for de-mineralized or distilled water at ambient temperatures.

Representative exterior coating systems are included but a more extensive listing will be found under Ferrous Metals inthis same book. Originally written for new construction, the scope of Ferrous Metals has been expanded to includemaintenance painting, both for recoating original systems and for upgrading coating systems

The NSF is the recognized authority for potable water storage tanks. Recommended coatings approved by this organizationalso meet AWWA requirements for potable water and are suitable for direct food contact in food processing andpharmaceutical plants.

The Society for Protective Coatings, formerly the Steel Structures Painting Council, is the recognized authority on surfacepreparation and painting procedures for steel. Reference is made to their standards as follows:

Solvent Cleaning SSPC-SP 1Hand Cleaning SSPC-SP 2Power Tool Cleaning SSPC-SP 3White Metal Blast SSPC-SP 5Commercial Blast SSPC-SP 6Brush-off Blast SSPC-SP 7Near White Blast SSPC-SP 10Power Tool Clean to Bare Metal SSPC-SP 11

Commercial sandblast iaw SSPC-SP 6 should be considered the minimum acceptable surface preparation for non-immersionservice.

White Metal Blast iaw SSPC-SP 5 is the minimum acceptable surface preparation for immersion service.

Wet sandblasting is becoming more common to control dust and to comply with EPA requirements, requiring new techniquesand the use of additives to the blasting water to prevent immediate rust bloom. Consult your BLP Mobile Paint representativefor equipment and additive recommendations.

Shop coats and primers for piping, pumps and non-critical areas should be selected to be compatible with the exteriorfinish system specified. After erection, all nuts, bolts, abraded areas and scratches should be cleaned and spot primedbefore additional coats of primer or finish are applied. Welds should be ground to remove weld splatter before priming.Positive ventilation is essential as a safety measure to prevent any accumulation of solvent vapors during both applicationand during the curing period. We recommend the use of an extractor 24 hours a day until cure is complete.

2

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



In temperate climates, we recommend a 7 to 14 day curing period. As catalyzed epoxies cure more rapidly in tropicalclimates, we have found that a 5 to 7 day curing period is acceptable if continuous forced ventilation is maintained.

After curing is complete, rinse thoroughly with fresh water to remove any dust or residual solvent contamination, then sealand fill with water for service.

POTABLE WATER TANKS

All products recommended are approved by the NSF for lining potable water tanks and meet USDA and AWWA regulations.

MoPoxY HS-50 Epoxy Coating is a high-build, high-solids, polyamide epoxy certified to ANSI/NSF Standard 61 for potablewater tank lining. Best applied by airless spray, may be rolled or brushed. VOC compliant, lead, chromate and mercuryfree. Acceptable for use on direct food contact surfaces.

Surface preparation: White Metal Blast iaw SSPC-SP 5 is minimum acceptable for immersion service.

FIRE PROTECTION STORAGE TANKS & RAW PRODUCTION WATER TANKS


The following products are recommended for immersion service for non-potable water storage tanks. All offer excellentresistance to fresh and salt water immersion.

MoPoxYTM PRIME Preconstruction Primer is a modified polyamide epoxy designed for use as a shop coat to protectcleaned steel against corrosion during fabrication and assembly. Also an excellent tie coat or zinc seal over inorganic zinc.Weldable, compatible with all below listed systems.

MoPoxYTM HB High Build Epoxy Primer is a marine epoxy designed for ship-bottom service. High solids, VOC - compliant.Lead and mercury free. Best applied by airless spray, may be rolled or brushed.

MoPoxYTM MASTIC is an amine adduct direct to metal (DTM) coating with excellent resistance to abrasion, salt and freshwater immersion. High-build, very high-solids, very low-VOC. Lead, mercury and chromate free. Best applied by airlessspray, may be rolled or brushed.

MoPoxYTM -PLUS is a modified polyamine direct to metal (DTM) epoxy with excellent resistance to fresh and salt waterimmersion and abrasion. High build, high solids, low VOC. Lead, mercury and chromate free. Best applied by airless spray,may be rolled or brushed.

MIL-P-24441/29, Formula 150, Type IV, is a green polyamide epoxy primer formulated for Naval use on bilges, underwaterhulls and other surfaces subject to salt water immersion. Low VOC and lead free.

MIL-P-24441, Formula 152, Type IV, White, is a hard, durable, chemical resistant, non porous polyamide epoxy suitablefor use over Formula 150. Suitable for fresh and salt water immersion. Other color formulations are available.

MoPoxYTM PHENOLIC Epoxy is a high performance heavy duty formulation with excellent chemical and abrasion resistance,suitable for fresh and salt water immersion. Also certifiable under 40 CFR 175.300 for direct food contact.

3

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



DE-MINERALIZED WATER TANKS

De-mineralized water, distilled water, and de-ionized water are all highly reactive and require special coatings for containment.The below-listed products are recommended for ambient to slightly elevated temperatures; for high temperatures, consultyour BLP Mobile Paint representative.


MoPoxYTM GF Glass Flake Phenolic Epoxy is a high performance heavy duty tank lining, reinforced with glass flakepigment, for maximum resistance to permeation by water and chemicals. This product has excellent abrasion, water andchemical resistance at elevated temperatures. High build, high solids, low VOC. Lead, mercury, and chromate free. Applyby airless spray only.

MoPoxYTM MASTIC is an amine adduct direct to metal (DTM) coating with excellent resistance to abrasion, salt and freshwater immersion. High-build, very high-solids, very low-VOC, lead, mercury and chromate free. Best applied by airlessspray, may be rolled or brushed.

MoPoxYTM -PLUS is a modified polyamine direct to metal (DTM) epoxy with excellent resistance to fresh and salt waterimmersion and abrasion. High build, high solids, low VOC. Lead, mercury and chromate free. Best applied by airless spray,may be rolled or brushed.

4

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



WATER STORAGE TANKS - INTERIOR COATING SYSTEMS

01 POTABLE WATER TANKS

All products recommended are certified by the NSF for lining potable water tanks and meet ANSI/NSF Standard 61.

01.A Polyamide Epoxy System, 3.4 VOC

Coat Product Premium Quality Epoxy VOC Sq Ft Mils

Prime 40-BH-11 MoPoxYTM HS-50 NSF, Gray 3.40 134 6Finish 40-BW-5 MoPoxYTM HS-50 NSF, White 3.40 134 6

Total Dry Mils 12.0

02 FIRE PROTECTION STORAGE TANKS & RAW PRODUCTION WATER TANKS

02.A Preconstruction Primer: for use as shop coat during fabrication and erection.


Shop 40-DR-12 MoPoxYTM PRIME, Red 5.25 348 1Coat Compatible with all below systems

Total Dry Mils 1.0

02.B Epoxy Primer/Epoxy Mastic Finish


Prime 40-DR-5 MoPoxYTM HB Hi-Build Primer, Red 3.49 131 6Finish 40-AW-32 MoPoxYTM MASTIC, White 1.30 217 6

Total Dry Mils 12.0

02.C Epoxy Mastic Primer & Finish


Prime 40-AH-51 MoPoxYTM MASTIC, Dawn Gray 1.30 217 6Finish 40-AW-32 MoPoxYTM MASTIC, White 1.30 217 6

Total Dry Mils 12.0

5

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



02.D Epoxy High-Build, High-Solids Primer & Finish


Prime 41-CH-1 MoPoxYTM -PLUS, Haze Gray 2.36 131 8Finish 41-CW-1 MoPoxYTM -PLUS, White 2.36 131 8

Total Dry Mils 16.0

02.E Navy Formulation MIL-P-24441Type IV Epoxy Primer and Finish


Prime 40-CM-7 MIL-P-24441/T IV /F 150 Primer Green 2.80 346 3Finish 40-AW-42 MIL-P-24441/T IV /F 152 White 1.30 319 3

Total Dry Mils 6.0

02.F Phenolic Epoxy Primer and Finish, Maximum Protection


Prime 41-AH-1 MoPoxYTM PH Phenolic Epoxy, Gray 2.81 156 6Intermediate 41-AH-1 MoPoxYTM PH Phenolic Epoxy, Gray 2.81 156 6Finish 41-AH-1 MoPoxYTM PH Phenolic Epoxy, Gray 2.81 156 6Apply by airless spray only

Total Dry Mils 18.0

03 DE-MINERALIZED WATER TANKS

03.A Glass Flake Phenolic Epoxy Primer & Finish, Maximum Protection


Prime 41-AH-2 MoPoxYTM GF Glass Flake Phenolic, Gray 2.65 122 8Intermediate 41-AH-2 MoPoxYTM GF Glass Flake Phenolic, Gray 2.65 122 8Finish 41-AH-2 MoPoxYTM GF Glass Flake Phenolic, Gray 2.65 122 8Apply by airless spray only

Total Dry Mils 24.0

6

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



03.B Epoxy Mastic Primer & Finish


Prime 40-AH-51 MoPoxYTM MASTIC, Dawn Gray 1.30 217 6Finish 40-AW-32 MoPoxYTM MASTIC, White 1.30 217 6

Total Dry Mils 12.0

03.C Epoxy High-Build, High-Solids Primer & Finish


Prime 41-CH-1 MoPoxYTM -PLUS, Haze Gray 2.36 131 8Finish 41-CW-1 MoPoxYTM -PLUS, White 2.36 131 8

Total Dry Mils 16.0

7

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



WATER STORAGE TANKS - EXTERIOR COATING SYSTEMS

04 WATER TANKS - EXTERIOR COATING SYSTEMS

The below systems are representative of the exterior coating systems suitable for this service. For additional systems,please see sections on Ferrous Metal Systems.

04.A Alkyd System, High Gloss, Residential, Commercial & Light Industrial Service


Shop 9-78 SPEED PRIME Red Oxide Primer 3.76 447 1.5 Prime 10-10 RUS-KIL® Metal Primer, Red 3.35 395 2 Intermediate 10-Series RUS-KIL® Gloss Enamel 3.35 385 2 Finish 10-Series RUS-KIL® Gloss Enamel 3.35 385 2

Total Dry Mils 7.5

04.B Acrylic Latex DTM System, High Gloss, Residential to Light Industrial Service

Coat Product High Gloss Acrylic Enamel Finish VOC Sq Ft Mils

Shop 310-9 H2O RUS-KIL® Acrylic Metal Primer, Red 1.14 345 2Prime 310-9 H2O RUS-KIL® Acrylic Metal Primer, Red 1.14 345 2Intermediate 310-Series H2O RUS-KIL® Acrylic DTM Enamel 1.09 295 2Finish 310-Series H2O RUS-KIL® Acrylic DTM Enamel 1.09 295 2

Total Dry Mils 8.0

04.C Silicone Alkyd System, High Gloss, Residential, Commercial & Industrial Service

Coat Product High Gloss Silicone Alkyd Enamel Finish VOC Sq Ft Mils

Shop 9-78 SPEED PRIME Red Oxide Primer 3.76 447 1.5Prime 10-10 RUS-KIL® Metal Primer, Red 3.35 395 2Intermediate 432-Series JACK TAR® Silicone Yacht Enamel 3.57 484 1.5Finish 432-Series JACK TAR ®Silicone Yacht Enamel 3.57 484 1.5

Total Dry Mils 6.5

04.D Catalyzed Epoxy / Epoxy Mastic / Polyurethane System, Heavy Industrial & Marine Service


Shop 613-10 MoPoxYTM HS High Solids Metal Primer 2.00 382 3Prime 40-AW-32 MoPoxYTM MASTIC, White 1.30 217 6Intermediate 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 13.0

1

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Waste Water Treatment Plants

RECOMMENDED PAINTING SPECIFICATIONSFOR INDUSTRIAL WASTE WATER AND

SEWAGE TREATMENT PLANTS

INDEX

INTRODUCTION

SURFACE PREPARATION STANDARDS

Part I: FERROUS METALS

01 - Ferrous Metal, Non-Immersion Service02 - Ferrous Metal, Immersion Service03 - Galvanized Steel, Non-Immersion Service04 - Zinc-Rich Primer on Steel, Non-Immersion Service

Part II - MASONRY SURFACES

05 - Interior Unplastered Cement Masonry Units06 - Interior Cement Plaster or Gypsum Board07 - Exterior Unplastered Cement Masonry Units08 - Exterior Exposed Concrete or Brick09 - Exterior Cement Plaster, Stucco or Concrete10 - Masonry Surfaces, Immersion Service

Part III - OTHER

11 - Fiberglass Reinforced Pipe (FRP)12 - Maintenance Upgrade Systems

Product Data Sheets and Color Cards will be found at the back of this book.

2

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)





INTRODUCTION

Because of the aggressive atmosphere of sewage and waste water treatment plants and the difficulty of maintenance afterthese plants have been placed in operation, we have limited our recommendations to those high-performance systemsand products which have been proven to offer the longest service life.

In general, we recommend catalyzed epoxy and polyurethane coatings throughout for their exceptional resistance tochemicals, fumes, abrasion and moisture. Applied as specified over a properly prepared substrate, they will give years ofservice under adverse conditions with a minimum of maintenance while retaining their color and gloss to provide anattractive and easily cleaned plant. In addition to a large selection of standard colors, custom colors are available inkeeping with the modern tradition of making our work places and necessary plants as attractive as possible.

Originally written for new construction only, the scope of this specification has been expanded to include upgradingdeteriorated paint systems where sandblasting is not feasible or practical but high performance is required.

All products recommended are lead-free, chromate-free, and mercury-free, with the exception of Vinyl Wash Primer, whichis required for adhesion of topcoats on galvanized metal, and which contains zinc chromate. All systems are VOC-Compliant.

Surface preparation is indicated for critical areas, such as surfaces subjected to immersion service.

All products are formulated for application by airless spray but may be applied by brush or roller unless otherwise indicated.If applied by roller, high-build formulations will normally require two coats for each 3 mils specified as it is difficult to applymore than 3 mils per coat by roller.

For detailed recommendations covering specific problems, please consult your BLP Mobile Paint representative.

3

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)





SURFACE PREPARATION

The Society for Protective Coatings, formerly the Steel Structures Painting Council, is the recognized authority on surfacepreparation and reference is made to their standards as follows:


Commercial Sandblast iaw SSPC-SP 6 should be considered as the minimum acceptable surface preparation for non-immersion service.

White Metal Blast iaw SSPC-SP 5 is the minimum acceptable surface preparation for steel in immersion service.

Brush-off Blast iaw SSPC-SP 7 is recommended for concrete surfaces in immersion service.

Wet sandblasting is becoming more common because of stringent EPA regulations, requiring new techniques and the useof additives in the blasting water to prevent immediate rust bloom. Consult your BLP Mobile Paint representative forequipment and additive recommendations.

Shop coats and primers for piping, pumps and non-critical areas must be compatible with the finish system specified. Aftererection, all nuts, bolts, abraded areas and scratches should be Hand Cleaned (SSPC-SP 2) or Power Tool Cleaned(SSPC-SP ) and spot primed before additional coats of primer or finish are applied. Welds should be ground to removeweld splatter before priming.

4

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



01 FERROUS METAL SYSTEMS, NON-IMMERSION SERVICE

This section covers ferrous metals, including structural steel, non-galvanized roof deckings, tanks and silos, tubing, pipe racks,platforms, ladders, siding, doors and door frames and equipment, both interior and exterior, subject to weathering, splashingand mild fumes, at ambient temperatures in sewage and waste water treatment plants. Not for immersion service.

All systems are lead-free, chromate-free, mercury-free, and VOC compliant.

Surface Preparation: Commercial Blast, SSPC-SP 6, preferred minimumPower Tool Clean, SSPC-SP 2, minimum for non-critical areasSolvent Clean, SSPC-SP 1, to remove oil or grease

Application: Airless spray preferred, conventional spray, brush or roller

01.A Catalyzed Epoxy/Polyurethane System, Severe Service, Exterior

Coat Product High Gloss Catalyzed Polyurethane Finish VOC Sq.Ft. Mils

Prime 613-10 MoPoxY HS High Solids Metal Primer 2.00 382 3Intermediate 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 72-AW-26 MOTHANE HS-1000 Polyurethane, White 2.45 513 2Finish 72-AW-26 MOTHANE HS-1000 Polyurethane, White 2.45 513 2

Total Dry Mils 13.0

01.B Catalyzed Epoxy/Acrylic Epoxy, Severe Service, Exterior

Coat Product High Gloss Acrylic Epoxy Finish VOC Sq.Ft. Mils

Prime 613-10 MoPoxY HS High Solids Metal Primer 2.00 382 3Intermediate 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 41-AW-2 MOPOX-ACRYL White 3.50 409 2Finish 41-AW-2 MOPOX-ACRYL White 3.50 409 2

Total Dry Mils 13.0

01.C Catalyzed Epoxy Mastic/High-Solids Polyurethane System, Severe Service, Exterior


Prime 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Intermediate 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 72-AW-26 MOTHANE HS-1000 Polyurethane, White 2.45 513 2Finish 72-AW-26 MOTHANE HS-1000 Polyurethane, White 2.45 513 2

Total Dry Mils 16.0

5

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



01.D Catalyzed Epoxy System, Semi-Gloss, Severe Service, Interior

Coat Product Semi-Gloss Catalyzed Epoxy Finish VOC Sq.Ft. Mils

Prime 613-10 MoPoxY HS High Solids Metal Primer 2.00 382 3Intermediate 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 613-17 MoPoxY HS High Solids Epoxy, White 2.10 374 3Finish 613-17 MoPoxY HS High Solids Epoxy, White 2.10 374 3

Total Dry Mils 15.0

01.E Epoxy Mastic/Catalyzed Epoxy System, Semi-Gloss, Severe Service, Interior


Prime 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Intermediate 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 613-17 MoPoxY HS High Solids Epoxy, White 2.10 374 3Finish 613-17 MoPoxY HS High Solids Epoxy, White 2.10 374 3

Total Dry Mils 18.0

01.F Catalyzed Waterborne Epoxy System, Semi-Gloss, Moderate Service, Interior

Coat Product Semi-Gloss Waterborne Amide Epoxy VOC Sq.Ft. Mils

Prime 69-DR-1 MoPoxY H2O-200 Metal Primer 0.89 257 3Intermediate 69-DR-1 MoPoxY H2O-200 Metal Primer 0.89 257 3Finish 69-AW-6 MoPoxY H2O-200 Amide Epoxy 1.00 225 3Finish 69-AW-6 MoPoxY H2O-200 Amide Epoxy 1.00 225 3

Total Dry Mils 12.0

6

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



02 FERROUS METALS, IMMERSION SERVICE

This section covers ferrous metal, including holding and settling tanks and aeration equipment,structural steel, ladders and platforms subject to immersion service at ambient temperatures.

Surface Preparation: White Metal Blast, SSPC-SP 5, minimum acceptableApplication: Airless Spray preferred. May be brushed or rolled unless otherwise noted.

02.A Glass Flake Phenolic Epoxy System

Coat Product Severe service, Maximum protection VOC Sq.Ft. Mils

Prime 41-AH-2 MoPoxY GF Light Gray 2.65 122 8Intermediate 41-AH-2 MoPoxY GF Light Gray 2.65 122 8Finish 41-AH-2 MoPoxY GF Light Gray 2.65 122 8Apply by airless spray only

Total Dry Mils 24.0

02.B Epoxy Mastic Coating System

Coat Product Severe service, Low-VOC VOC Sq.Ft. Mils

Prime 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 40-AH-51 MoPoxY MASTIC, Gray 1.30 217 6Finish 40-AW-32 MoPoxY MASTIC, White 1.30 217 6

Total Dry Mils 18.0

02.C Coal Tar Epoxy Coating System

Coat Product Severe service, Low-VOC VOC Sq.Ft. Mils

Prime 40-AX-7 MO-TAR C-200 Coal Tar Epoxy Coating 1.56 157 8Finish 40-AX-7 MO-TAR C-200 Coal Tar Epoxy Coating 1.56 157 8Finish 40-AX-7 MO-TAR C-200 Coal Tar Epoxy Coating 1.56 157 8

Total Dry Mils 24.0

02.D High-Build Coal Tar Epoxy Coating System

Coat Product Polyamide Coal Tar Epoxy VOC Sq.Ft. Mils

Prime & 40-BX-6 MO-TAR HB-90 Coal Tar Epoxy Coating 1.13 67 20Finish

Total Dry Mils 20.0

7

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



03 GALVANIZED STEEL, NON-IMMERSION SERVICE

Galvanized steel decking, piping, and similar items are customarily factory coated with oil to prevent galvanic actionwhile stacked. This must be removed prior to painting either by Solvent Cleaning iaw SSPC-SP 1, or by washing with adetergent solution and rinsing with clear water.Galvanized steel requires a pretreatment to insure adhesion of subsequent coats.

Surface Preparation: Solvent Clean, SSPC-SP1, to remove oil or greasePretreatment: Vinyl Wash Primer to promote adhesion

03.A Galvanized Steel, Catalyzed Epoxy/High-Solids Polyurethane System, Exterior Service


Pre-Treat 9-42 VINYL WASH Primer 5.72 252 0.5Prime 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 72-AW-26 MOTHANE HS-1000 Polyurethane, White 2.45 513 2Finish 72-AW-26 MOTHANE HS-1000 Polyurethane, White 2.45 513 2

Total Dry Mils 10.5

03.B Galvanized Steel, Catalyzed Epoxy System, Semi-Gloss, Interior Service


Pre-Treat 9-42 VINYL WASH Primer 5.72 252 0.5Prime 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 613-17 MoPoxY HS High Solids Epoxy, White 2.10 374 3Finish 613-17 MoPoxY HS High Solids Epoxy, White 2.10 374 3

Total Dry Mils 12.5

03.C Catalyzed Waterborne Epoxy System, Semi-Gloss, Interior Service

Coat Product Semi-Gloss WB Amide Cured Epoxy Finish VOC Sq.Ft. Mils

Pre-Treat 9-42 VINYL WASH Primer 5.72 252 0.5Prime 69-DR-1 MoPoxY H2O-200 Metal Primer 0.89 257 3Finish 69-AW-6 MoPoxY H2O-200 Amide Epoxy 1.00 225 3Finish 69-AW-6 MoPoxY H2O-200 Amide Epoxy 1.00 225 3

Total Dry Mils 9.5

8

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



04 ZINC-RICH PRIMER ON STEEL, NON-IMMERSION SERVICE

Inorganic zinc requires a clean surface and good anchor pattern, best achieved by sandblasting. White Metal Blast,SSPC-SP 5, is preferred. Commercial Sandblast, SSPC-SP 6 is minimum acceptable. Apply by airless or conventionalspray with constant mechanical agitation.

MoPoxY MASTIC may be applied directly over inorganic zinc by airless spray if a mist coat is applied first to penetratethe pores of the zinc, followed by a full coat. If applied by brush or roller, vinyl wash primer is required.

Surface Preparation: White Metal Blast, SSPC-SP 5, PreferredCommercial Sandblast, SSPC-SP 6, Minimum acceptable

Application, Zinc: Airless or Conventional Spray with constant mechanical agitation.

Application, Epoxy: Airless spray: Apply mist coat of epoxy to zinc, follow with full body coat.Brush or roller: Pretreat with Vinyl Wash Primer

04.A Inorganic Zinc/Epoxy Mastic/High-Solids Polyurethane System, Exterior Service

Coat Product High Gloss Polyurethane Finish VOC Sq.Ft. Mils

Prime 28-DH-50 MO-ZINC Inorganic Zinc Primer 3.88 342 3Intermediate 40-AW-32 MoPoxY MASTIC, White 1.20 217 6Finish 72-AW-26 MOTHANE HS-1000 Polyurethane, White 2.45 513 2Finish 72-AW-26 MOTHANE HS-1000 Polyurethane, White 2.45 513 2

Total Dry Mils 13.0

04.B Inorganic Zinc/Epoxy Mastic/Acrylic Epoxy System, Exterior Service


Prime 28-DH-50 MO-ZINC Inorganic Zinc Primer 3.88 342 3Intermediate 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 41-AW-2 MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-AW-2 MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 13.0

04.C Inorganic Zinc/Epoxy Mastic/Semi-Gloss Epoxy System, Interior Service

Coat Product Semi-Gloss Epoxy Finish VOC Sq.Ft. Mils

Prime 28-DH-50 MO-ZINC Inorganic Zinc Primer 3.88 342 3Intermediate 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 613-17 MoPoxY HS High Solids Epoxy, White 2.10 374 3Finish 613-17 MoPoxY HS High Solids Epoxy, White 2.10 374 3

Total Dry Mils 15.0

9

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



04.D Inorganic Zinc/Waterborne Epoxy System, Interior Service

Coat Product Semi-Gloss WB Amide Epoxy Finish VOC Sq.Ft. Mils

Prime 28-DH-50 MO-ZINC Inorganic Zinc Primer 3.88 342 3Intermediate 9-42 VINYL WASH Primer 5.72 252 0.5Finish 69-AW-6 MoPoxY H2O-200 Amide Epoxy 1.00 225 3Finish 69-AW-6 MoPoxY H2O-200 Amide Epoxy 1.00 225 3

Total Dry Mils 9.5

Zinc-rich epoxy primers combine the improved wetting properties and chemical and abrasion resistance of a catalyzedepoxy with the sacrificial protection afforded by inorganic zinc.

Excellent resistance to fresh and salt water, detergents and most chemicals, abrasion and moisture. Excellent for touch-up of inorganic zinc primers. VOC Compliant

Surface Preparation: Commercial Sandblast, SSPC-SP 6, recommended minimumPower Tool Clean, SSPC-SP 2, minimum acceptable

Application: Airless or conventional spray with continuous mechanical agitation

04.E Zinc-Rich Epoxy/Epoxy Mastic/High-solids Polyurethane System, Exterior Service


Prime 40-CM-4 MoPoxY ZR Zinc Rich Epoxy Primer 3.89 257 3.5Intermediate 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 72-AW-26 MOTHANE HS-1000 Polyurethane, White 2.45 513 2Finish 72-AW-26 MOTHANE HS-1000 Polyurethane, White 2.45 513 2

Total Dry Mils 13.5

Total Dry Mils ERR

04.F Zinc-Rich Epoxy/Epoxy Mastic/Semi-Gloss Epoxy, Interior Service


Prime 40-CM-4 MoPoxY ZR Zinc Rich Epoxy Primer 3.89 257 3.5Intermediate 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 613-17 MoPoxY HS High Solids Epoxy, White 2.00 374 3Finish 613-17 MoPoxY HS High Solids Epoxy, White 2.00 374 3

Total Dry Mils 15.5

10

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



05 INTERIOR EXPOSED MASONRY UNITS, NON-IMMERSION SERVICE

05.A Catalyzed Semi-Gloss Epoxy System, Interior Service


Fill 19-10 BLOC-SEAL 0.44 100 1Prime 19-7 PRYMALL 2 QD Primer & Sealer 1.13 302 1.5Finish 613-17 MoPoxY HS High Solids Epoxy, White 2.00 374 3Finish 613-17 MoPoxY HS High Solids Epoxy, White 2.00 374 3

Total Dry Mils 8.5

05.B Waterborne Catalyzed Epoxy System, Interior Service

Coat Product Semi-Gloss Waterborne Amide Epoxy Finish VOC Sq.Ft. Mils

Fill 19-10 BLOC-SEAL 0.44 100 1Prime 19-7 PRYMALL 2 QD Primer & Sealer 1.13 302 1.5Finish 69-AW-6 MoPoxY H20-200 WB Amide-Epoxy 1.00 225 3Finish 69-AW-6 MoPoxY H20-200 WB Amide-Epoxy 1.00 225 3

Total Dry Mils 8.5

06 INTERIOR CEMENT PLASTER OR GYPSUM BOARD

06.A Catalyzed Semi-Gloss Epoxy System, Interior Service


Prime 19-7 PRYMALL 2 QD Primer & Sealer 1.13 302 1.5Finish 613-17 MoPoxY HS High Solids Epoxy, White 2.00 374 3Finish 613-17 MoPoxY HS High Solids Epoxy, White 2.00 374 3

Total Dry Mils 7.5

06.B Waterborne Catalyzed Epoxy System, Interior Service

Coat Product Semi-Gloss Waterborne Amide Epoxy Finish VOC Sq.Ft. Mils

Prime 19-7 PRYMALL 2 QD Primer & Sealer 1.13 302 1.5Finish 69-AW-6 MoPoxY H20-200 WB Amide-Epoxy 1.00 225 3Finish 69-AW-6 MoPoxY H20-200 WB Amide-Epoxy 1.00 225 3

Total Dry Mils 7.5

11

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



07 EXTERIOR UNPLASTERED CEMENT MASONRY UNITS

WEATHER-TITETM Acrylic House Paint is the industry standard for exterior masonry finishes. 100% acrylic, it transpires,allowing moisture in the masonry to evaporate without damaging the paint film. Highly resistant to alkali. Contains aneffective mildewcide. Excellent color retention.

07.A Acrylic Latex System, Flat Finish

Coat Product Acrylic Latex Flat Finish VOC Sq.Ft. Mils

Fill 60-7 BLOC-FIL Latex Block Filler 0.55 100 1Prime 6-6 WEATHER-TITETM 100% Acrylic Universal Primer 1.17 393 2Finish 40-Series WEATHER-TITETM 100% Acrylic House Paint 1.03 291 2Finish 40-Series WEATHER-TITETM 100% Acrylic House Paint 1.03 291 2

Total Dry Mils 7.0

07.B Acrylic Latex System, Gloss Finish

Coat Product Acrylic Latex, High Semi-Gloss Finish VOC Sq.Ft. Mils


Total Dry Mils 7.0

07.C Acrylic Latex System, Satin Finish

Coat Product Acrylic Latex, Satin Gloss Finish VOC Sq.Ft. Mils


Total Dry Mils 7.0

12

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



07.D Elastomeric Acrylic System

WEATHER-TITETM Elastomeric Wall Coat is 100% acrylic and offers exceptional resistance to alkali, moisture, sun, andmildew. Bridges small cracks, protects against wind driven rain.Excellent for maintenance upgrade service where existing paints have failed.

Coat Product Acrylic Latex Elastomeric Finish VOC Sq.Ft. Mils

Fill 60-7 BLOC-FIL Latex Block Filler 0.55 100 1Prime 6-6 WEATHER-TITETM 100% Acrylic Universal Primer 1.17 393 2Finish 43-25 WEATHER-TITETM ELASTOMERIC Wall Coat 0.80 100 7.5Finish 43-25 WEATHER-TITETM ELASTOMERIC Wall Coat 0.80 100 7.5

Total Dry Mils 18.0

08 EXTERIOR EXPOSED CONCRETE OR BRICK

WEATHER-TITETM DUB-L-TITE is a clear silicone sealer which penetrates into the pores of the surface and forms aninvisible barrier to repel water. Does not change the appearance of the substrate. Recommended for exposed concrete,exposed aggregate, brick and similar surfaces.

H2O DUB-L-TITE is a waterborne silicone/silane formulation offering low VOC and low odor.

08.A Clear Silicone Sealer & Water Repellant

Coat Product VOC Sq.Ft. Mils

Prime 74-12 DUB-L-TITE TMSilicone Sealer, Clear 6.19 100 1Finish 74-12 DUB-L-TITETM Silicone Sealer, Clear 6.19 100 1

Total Dry Mils 2.0

08.B Clear Waterborne Silicone/Silane Sealer & Water Repellant

Coat Product VOC Sq.Ft. Mils

Prime 74-13 H2O DUB-L-TITE Silicone Sealer, Clear 0.00 100 1Finish 74-13 H2O DUB-L-TITE Silicone Sealer, Clear 0.00 100 1

Total Dry Mils 2.0

13

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



09 EXTERIOR CEMENT PLASTER, STUCCO OR CONCRETE

09.A Acrylic Latex System, Flat Finish

Coat Product Acrylic Latex Flat Finish VOC Sq.Ft. Mils

Prime 6-6 WEATHER-TITETM 100% Acrylic Universal Primer 1.17 393 2Finish 40-Series WEATHER-TITETM 100% Acrylic House Paint 1.03 291 2Finish 40-Series WEATHER-TITETM 100% Acrylic House Paint 1.03 291 2

Total Dry Mils 6.0

09.B Acrylic Latex System, Gloss Finish

Coat Product Acrylic Latex, High Semi-Gloss Finish VOC Sq.Ft. Mils


Total Dry Mils 6.0

09.C Acrylic Latex System, Satin Finish

Coat Product Acrylic Latex, Satin Gloss Finish VOC Sq.Ft. Mils


Total Dry Mils 6.0

09.D Elastomeric Acrylic Latex System

Coat Product Acrylic Latex, Elastomeric Finish VOC Sq.Ft. Mils

Prime 6-6 WEATHER-TITETM 100% Acrylic Universal Primer 1.17 393 2Finish 43-25 WEATHER-TITETM ELASTOMERIC Wall Coat 0.80 100 7.5Finish 43-25 WEATHER-TITETM ELASTOMERIC Wall Coat 0.80 100 7.5

Total Dry Mils 17.0

14

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



10 MASONRY SURFACES, IMMERSION SERVICE

Masonry surfaces subject to immersion service require either Brush Blasting, SSPC-SP 7, or acid etching with muriaticacid to remove laitance and provide the porosity required for good adhesion.

10.A Glass Flake Phenolic Epoxy System

Coat Product Maximum abrasion & chemical resistance VOC Sq.Ft. Mils

Prime 41-AH-2 MoPoxY GF Light Gray 2.65 122 8Second 41-AH-2 MoPoxY GF Light Gray 2.65 122 8Finish 41-AH-2 MoPoxY GF Light Gray 2.65 122 8Apply by airless spray, only.

Total Dry Mils 24.0

10.B Epoxy Mastic Coating

Coat Product Severe service VOC Sq.Ft. Mils

Prime 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 40-AH-51 MoPoxY MASTIC, Gray 1.30 217 6Finish 40-AH-51 MoPoxY MASTIC, Gray 1.30 217 6

Total Dry Mils 18.0

10.C Coal Tar Epoxy Coating System


Prime 40-AX-7 MO-TAR C-200 Coal Tar Epoxy Coating 1.56 157 8Finish 40-AX-7 MO-TAR C-200 Coal Tar Epoxy Coating 1.56 157 8Finish 40-AX-7 MO-TAR C-200 Coal Tar Epoxy Coating 1.56 157 8

Total Dry Mils 24.0

10.D High-Build Coal Tar Epoxy Coating System


Prime* 40-BX-6 MO-TAR HB-90 Coal Tar Epoxy Coating 1.13 67 20Finish 40-BX-6 MO-TAR HB-90 Coal Tar Epoxy Coating 1.13 67 20* Thin up to 20% with MoPoxY Spraying Thinner 75-37

Total Dry Mils 40.0

15

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



11 FIBERGLASS REINFORCED PIPE (FRP)

11.A Epoxy/High-Solids Polyurethane System, Exterior Service


Surface Preparation: Wet Sand with 50:50 water/Al-Co-Sol solutionPrime 613-17 MoPoxY HS High Solids White 2.00 374 3Finish 72-AW-26 MOTHANE HS-1000 Polyurethane, White 2.45 513 2Finish 72-AW-26 MOTHANE HS-1000 Polyurethane, White 2.45 513 2

Total Dry Mils 7.0

11.B Epoxy System, High-Solids, Semi-Gloss, Interior Service


Surface Preparation: Wet Sand with 50:50 water/Al-Co-Sol solutionPrime 613-17 MoPoxY HS High Solids White 2.00 374 3Finish 613-17 MoPoxY HS High Solids White 2.00 374 3

Total Dry Mils 6.0

16

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



12 MAINTENANCE UPGRADE SYSTEMS

For upgrading deteriorated alkyd or silicone alkyd finishes and repairing catalyzed epoxy and polyurethane systemswhere sandblasting is not possible to remove existing coatings.

MoPoxY MASTIC is a high-solids, high-build, surface-tolerant amine epoxy formulated for application over sound rustand/or deteriorated paint systems as a base coat for upgrading to high performance coatings such as acrylic epoxies orpolyurethanes.

MoPoxY IR, Indefinite Recoatablity Epoxy, is a high-solids, surface-tolerant, high-build coating which may be applied todamp, rusty surfaces, allowed to dry for prolonged periods, then topcoated with other epoxies or polyurethanes withoutloss of intercoat adhesion.

MoPoxY PRE-PREP is a 100% solids epoxy with very low viscosity and excellent substrate wetting properties.Excellent for badly rusted areas where sandblasting and removal of existing coatings is not feasible and only minimalcleaning is possible. Penetrates and bonds rust and deteriorated coatings into a solid film which seals out moisture andoxygen.

Allow to cure for 24 hours, then apply recommended intermediate coat while still slightly soft. Will accept a wide varietyof coatings.

All systems are lead-free, chromate-free, mercury-free and VOC compliant.

Surface Preparation: Pressure Wash (3,000 psi or better) to remove contaminationSolvent Clean, SSPC-SP 1, to remove oil and greasePower Tool Clean, SSPC-SP 2, preferredHand Tool Clean, SSPC-CP 3, minimum recommended

Application: Brush, roller, or airless or conventional spray

12.A Catalyzed Epoxy Mastic/Polyurethane System


Spot Prime 40-AY-2 MoPoxY MASTIC, Aluminum 0.51 248 6Prime 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 72-AW-26 MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-AW-26 MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 16.0

17

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



12.B Catalyzed Epoxy Mastic/Acrylic Epoxy System


Spot Prime 40-AY-2 MoPoxY MASTIC, Aluminum 0.51 248 6Prime 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 16.0

12.C Recoatable Epoxy/Polyurethane System


Spot Prime 41-BK-14 MoPoxY IR High Solids Epoxy Buff 2.29 136 8Prime 41-BK-14 MoPoxY IR High Solids Epoxy Buff 2.29 136 8Finish 72-AW-26 MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-AW-26 MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 20.0

12.D Recoatable Epoxy/Acrylic Epoxy System


Spot Prime 41-BK-14 MoPoxY IR High Solids Epoxy Buff 2.29 136 8Prime 41-BK-14 MoPoxY IR High Solids Epoxy Buff 2.29 136 8Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 20.0

12.E Low-Viscosity Epoxy/Epoxy Mastic/Polyurethane System


Prime 41-AF-2 MoPoxY PRE-PREP Clear 0.00 1069 1.5Intermediate 40-AW-32 MoPoxY MASTIC, White 1.30 217 6Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2Finish 72-Series MOTHANE HS-1000 Polyurethane 2.45 513 2

Total Dry Mils 11.5

18

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



12-F Low-Viscosity Epoxy/Epoxy Mastic/Acrylic Epoxy System


Prime 41-AF-2 MOPOXY PRE-PREP Clear 0.00 1069 1.5Intermediate 40-AW-32 MOPOXY MASTIC, White 1.30 217 6Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2Finish 41-Series MOPOX-ACRYL Acrylic Epoxy 3.50 409 2

Total Dry Mils 11.5

Marine Coating Systems1

251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

RECOMMENDED PAINTING SPECIFICATIONS FORMARINE COATING SYSTEMS

Painting Recommendations For Ships and BoatsSteel, Fiberglass and Wood

Part IINTRODUCTION

Introduction to Coating Systems and Surface Preparation



Part IIICOATING SYSTEMS

Recommended Surface Preparation, Primers, Intermediate CoatsFinish Coats, Dry Film Thickness and Coverage

SUMMARY INDEX01 - Steel Vessels - Exterior - Above Water Line02 - Steel Vessels - Exterior - Below Water Line03 - Steel Vessels - Exterior - Decks & Ladders04 - Steel Vessels - Interior - Bulkhead & Overhead05 - Steel Vessels - Interior - Ladders, Decks & Passageways06 - Fiberglass Vessels - Exterior - Above Water Line07 - Fiberglass Vessels - Exterior - Below Water Line08 - Fiberglass Vessels - Exterior - Decks & Ladders09 - Fiberglass Vessels - Interior - Bulkhead & Overhead10 - Fiberglass Vessels - Interior - Ladders, Decks & Passageways11 - Wooden Vessels - Exterior - Above Water Line12 - Wooden Vessels - Exterior - Below Water Line13 - Wooden Vessels - Exterior - Decks & Ladders14 - Wooden Vessels - Interior - Bulkhead & Overhead15 - Wooden Vessels - Interior - Ladders, Decks & Passageways16 - Engine Room17 - Potable Water Tanks18 - Fuel Tanks19 - Bilges & Voids



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Part IIntroduction

Marine coatings are a unique group, in that they must resist the harshest of environments. They mustprotect from constant salt water spray, high humidity, impact, abrasion, high temperatures, immersion andfouling, as well as, intense assault from sunlight andultraviolet rays.

In order to simplify the selection, we will present several recommended systems for each area to becoated. Surface preparation, primers, intermediate and topcoats are listed for both interior and exteriorsurfaces. Systems are listed in inverse order of service life.

Surface preparation is the key to the life expectancy of any coating system. It is even more critical in thecase of marine coatings. Each system will contain a recommended surface preparation for steel, fiberglassand wood.

While most products listed may be rolled or brushed, they are best applied by spray.

Mobile Paint Manufacturing Co., Inc. has over 80 years experience in formulating and manufacturing topquality industrial, marine and architectural coatings for tropical and subtropical climates. We manufacture anextensive line of items for specialized services including tank linings for chemicals, potable water tanks,fuel and oil tanks, high heat coatings and numerous Military Specification coatings. Please contact yourMobile Paint Manufacturing Co., representative for specific recommendations for particular needs.


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Part IIIndex of Coating Systems

01 Steel Vessels - Exterior - Above Water Line

01.A MoPoxYTM ZR / MoPoxYTM Plus / MOTHANETM Polyurethane System01.B JackTar® Phenolic / JackTar®Silicone Alkyd System01.C Alkyd / JackTar® Silicone Alkyd EnamelSystem01.D Alkyd / JackTar®Alkyd Enamel System

02 Steel Vessels - Exterior - Below Water Line

02.A MoPoxYTM Plus / JackTar® Vinyl Antifouling System02.B JackTar® Phenolic / JackTar® Cold Plastic Antifouling System02.C JackTar® Phenolic / JackTar® Dub-L-Cop Antifouling System

03 Steel Vessels - Exterior - Decks & Ladders

03.A MoPoxYTM ZR / MoPoxYTM HS / MoPoxYTM AR-200 Deck Armor High Build System03.B MoPoxYTM ZR / MoPoxYTM HS / MoPoxYTM NS-200 Deck Armor High Build Non-Skid System03.C MoPoxYTM ZR / MoPoxYTM HS Epoxy System

04 Steel Vessels - Interior - Bulkhead & Overhead

04.A MoPoxYTM HS Epoxy System04.B Rus-Kil® Rust Inhibitive Enamel System

05 Steel Vessels - Interior - Ladders, Decks & Passageways

05.A MoPoxYTM HS Epoxy System05.B Rus-Kil® / JackTar®Alkyd Enamel System

06 Fiberglass Vessels - Exterior - Above Water Line06.A MoPoxYTM Plus / MOTHANETM Polyurethane System06.B JackTar® Silicone Alkyd Enamel System06.C JackTar®Alkyd Enamel System


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



(continued)

07 Fiberglass Vessels - Exterior - Below Water Line


08 Fiberglass Vessels - Exterior - Decks & Ladders

08.A MoPoxYTM HS / MoPoxYTM AR-200 Deck Armor High Build System08.B MoPoxYTM HS / MoPoxYTM NS-200 Deck Armor High Build Non-Skid System08.C MoPoxYTM HS Epoxy System

09 Fiberglass Vessels - Interior - Bulkhead & Overhead


10 Fiberglass Vessels - Interior - Ladders, Decks & Passageways

10.A MoPoxYTM HS Epoxy System10.B Rus-Kil® Primer / JackTar®Alkyd Enamel System

11 Wooden Vessels - Exterior - Above Water Line11.A MoPoxYTM Plus / MOTHANETM Polyurethane System11.B JackTar® Silicone Alkyd Enamel System11.C JackTar®Alkyd Enamel System

12 Wooden Vessels - Exterior - Below Water Line



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)



(continued)

13 Wooden Vessels - Exterior - Decks & Ladders

13.A MoPoxYTM HS / MoPoxYTM AR-200 Deck Armor High Build System13.B MoPoxYTM HS / MoPoxYTM NS-200 Deck Armor High Build Non-Skid System13.C MoPoxYTM HS Epoxy System

14 Wooden Vessels - Interior - Bulkhead & Overhead


15 Wooden Vessels - Interior - Ladders, Decks & Passageways


16 Engine Room


17 Potable Water Tanks

17.A MoPoxYTM HS-50 NSF Epoxy System

18 Fuel Tanks

18.A MoPoxYTM Mastic Epoxy System

19 Bilges & Voids

19.A MoPoxYTM Plus Epoxy System


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

Part IIICoating Systems for Ships and Boats

Section 01 STEEL VESSELS - EXTERIOR - ABOVE WATER LINE

Surface Preparation: Near White Metal Sandblast (SSPC-SP10) is preferred and Commercial Sandblast (SSPC-SP6) isminimum acceptable.

01.A MoPoxYTM ZR / MoPoxYTM Plus / MOTHANETM Polyurethane SystemCombines excellent chemical, solvent and abrasion resistance with superior gloss and color retention for maximum service.

Coat Product Description Sq.Ft Mils

Prime 40-CM-4 MoPoxY ZR Zinc Rich Epoxy Primer 257 3.5Intermediate 41-CW-1 MoPoxYTM Plus Epoxy Coating 131 8Finish * 72-series MOTHANETM Polyurethane Coating 339 2Finish * 72-series MOTHANETM Polyurethane Coating 339 2

* Alternate Finish 72-series MOTHANETM HD Polyurethane Coating 268 2.5* Alternate Finish 72-series MOTHANETM HS-1000 Polyurethane Coating 513 2* Alternate Finish 72-series MOTHANETM HS-900 Polyurethane Coating 428 2.5

Total Dry Mils 15.5 – 16.5

01.B JackTar® Phenolic / JackTar®Silicone Alkyd SystemCombines easier application with good resistance properties and excellent color and gloss retention.


Prime 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Intermediate 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Finish 432-line JACK TAR® Silicone Yacht Finish 484 1.5Finish 432-line JACK TAR® Silicone Yacht Finish 484 1.5

Total Dry Mils 9.0


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 01 STEEL VESSELS - EXTERIOR - ABOVE WATER LINE (continued):

01.C Alkyd / JackTar® Silicone Alkyd EnamelSystemProvides greater economy, ease of application and excellent color and gloss retention.


Prime 10-10 RUS-KIL® Metal Primer 337 2Intermediate 10-10 RUS-KIL® Metal Primer 337 2Finish 432-line JACK TAR® Silicone Yacht Finish 484 1.5Finish 432-line JACK TAR® Silicone Yacht Finish 484 1.5

Total Dry Mils 7.0

01.D Alkyd / JackTar®Alkyd Enamel SystemEconomic protection in mild marine service. Good color and gloss retention.


Prime 10-10 RUS-KIL® Metal Primer 337 2Finish 450-line JACK TAR® Yacht Deck Enamel 420 1.5Finish 450-line JACK TAR® Yacht Deck Enamel 420 1.5

Total Dry Mils 5.0


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 02 STEEL VESSELS - EXTERIOR - BELOW WATER LINE

Surface Preparation: Near White Metal Sandblast (SSPC-SP10) is preferred and Commercial Sandblast (SSPC-SP6)is minimum acceptable.

02.A MoPoxYTM Plus / JackTar® Vinyl Antifouling SystemOffers maximum durability for steel vessels. This system consists of two coats of high solids, high build epoxy primer and two coats ofcuprous oxide, vinyl copolymer, anti-fouling paint.


Prime 41-CW-1 MoPoxYTM Plus Epoxy Coating 131 8Intermediate 41-CW-1 MoPoxYTM Plus Epoxy Coating 131 8Finish 473-73 JACK TAR® Vinyl Anti-fouling Paint 485 2Finish 473-73 JACK TAR® Vinyl Anti-fouling Paint 485 2

Total Dry Mils 20Note: Adding a third coat of anti-fouling paint to the break of the bow and to the rudder/prop wash area will extend the service lifeof an anti-fouling system.

02.B JackTar® Phenolic / JackTar® Cold Plastic Antifouling SystemOffers excellent protection and durability for sailboats and slower moving vessels. This system consists of a phenolic anti-corrosiveprimer and a cuprous oxide anti-fouling paint.


Prime 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Intermediate 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Intermediate 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Finish 473-71 JACK TAR® Cold Plastic Anti-fouling Paint 537 2Finish 473-71 JACK TAR® Cold Plastic Anti-fouling Paint 537 2



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 02 STEEL VESSELS - EXTERIOR - BELOW WATER LINE (continued):

02.C JackTar® Phenolic / JackTar® Dub-L-Cop Antifouling SystemOffers good, economical protection for shrimp boats and other slow moving steel hull vessels. This system consists of a phenolic anti-corrosive primer and a modified rosin based cuprous oxide anti-fouling paint.


Prime 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Intermediate 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Intermediate 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Finish 473-74 JACK TAR® Dub-L-Cop Bottom Paint 568 2Finish 473-74 JACK TAR® Dub-L-Cop Bottom Paint 568 2



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 03 STEEL VESSELS - EXTERIOR - DECKS & LADDERS

Surface Preparation: Near White Metal Sandblast (SSPC-SP10) is preferred and Commercial Sandblast (SSPC-SP6)is minimum acceptable.

03.A MoPoxYTM ZR / MoPoxYTM HS / MoPoxYTM AR-200 Deck Armor High Build SystemFor maximum service life, superior impact and abrasion resistance. Designed specifically for cargo and work deckson shrimp boats,supply boats, crew boats, drydocks, etc… or any steel deck requiring exceptional long term protection.


Prime * 40-CM-4 MoPoxYTM ZR Zinc Rich Epoxy 257 3.5Finish 41-BW-1 MoPoxYTM Deck Armor AR-100 26 60

Total Dry Mils 63.0 – 63.5* Alternate Primer 613-10 MoPoxYTM HS High Solids Epoxy Primer 382 3

03.B MoPoxYTM ZR / MoPoxYTM HS / MoPoxYTM NS-200 Deck Armor High Build Non-Skid SystemFor maximum service life, superior impact and abrasion resistance. Same protection and properties as the abovesystem, except in a non-skid formulation.


Prime * 40-CM-4 MoPoxYTM ZR Zinc Rich Epoxy 257 3.5Finish 41-BH-12 MoPoxYTM Deck Armor NS-200 24 60

Total Dry Mils 63.0 – 63.5* Alternate Primer 613-10 MoPoxYTM HS High Solids Epoxy Primer 382 3

03.C MoPoxYTM ZR / MoPoxYTM HS Epoxy SystemA high performance deck coating system providing long term protection in marine environments.


Prime * 40-CM-4 MoPoxYTM ZR Zinc Rich Epoxy 257 3.5Finish 613-series MoPoxYTM HS High Solids Epoxy Finish 374 3Finish 613-series MoPoxYTM HS High Solids Epoxy Finish (NOTE) 374 3

Total Dry Mils 9 – 9.5* Alternate Primer 613-10 MoPoxYTM HS High Solids Epoxy Primer 382 3

NOTE: Add JACK TAR® Non-Skid Deck Compound, 492-3 to the final finish coat for use in critical work and traffic areas.


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 04 STEEL VESSELS - INTERIOR - BULKHEAD & OVERHEAD

Surface Preparation: Commercial Sandblast (SSPC-SP6) is preferred. Power Tool Clean (SSPC-SP3) or Hand ToolClean (SSPC-SP2) are minimum acceptable.

04.A MoPoxYTM HS Epoxy SystemCombines excellent protection, maximum resistance to soiling and ease of cleaning.


Prime 613-10 MoPoxYTM HS Primer 382 3Finish 613-line MoPoxYTM HS Epoxy 374 3Finish 613-line MoPoxYTM HS Epoxy 374 3

Total Dry Mils 9

04.B Rus-Kil® Rust Inhibitive Enamel SystemGood resistance to soiling and easy maintenance


Prime 10-10 RUS-KIL® Metal Primer 337 2Finish 10-line RUS-KIL® Enamel 417 1.5Finish 10-line RUS-KIL® Enamel 417 1.5

Total Dry Mils 5


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 05 STEEL VESSELS - INTERIOR - DECKS, LADDERS & PASSAGEWAYS

Surface Preparation: Commercial Sandblast (SSPC-SP6) is preferred. Power Tool Clean (SSPC-SP3) or Hand ToolClean (SSPC-SP2) are minimum acceptable.




Total Dry Mils 9

05.B Rus-Kil® / JackTar®Alkyd Enamel SystemGood resistance to soiling and easy maintenance


Prime 10-10 RUS-KIL® Metal Primer 337 2Finish 450-line JACK TAR® Yacht Deck Enamel 420 1.5Finish 450-line JACK TAR® Yacht Deck Enamel (NOTE) 420 1.5

Total Dry Mils 5NOTE: Add JACK TAR® Non-Skid Deck Compound, 492-3 to the final finish coat for use in critical work and traffic areas.


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 06 FIBERGLASS VESSELS - EXTERIOR - ABOVE WATER LINE

Surface Preparation: Wet sand with a 50:50 solution of Al-Co-Sol, 75-41 and water to remove all traces of wax, mold releasecompounds, etc.. Wipe clean with clean rags saturated with same solution. Immediately (within 1 hour) before applying coating directlyto fiberglass, wipe down fiberglass with MoPoxYTM Thinner, 75-35, or MOTHANETM Thinner, 43-EF-70, or BLP Vinyl Thinner, 475-31.Use only clean cotton rags for cleaning and fiberglass preparation.

06.A MoPoxYTM Plus / MOTHANETM Polyurethane SystemCombines excellent chemical, solvent and abrasion resistance with superior gloss and color retention for maximum service.


Prime 41-CW-1 MoPoxYTM Plus Epoxy Coating 131 8Finish * 72-series MOTHANETM Polyurethane Coating 339 2Finish * 72-series MOTHANETM Polyurethane Coating 339 2


Total Dry Mils 12 - 13

06.B JackTar®Silicone Alkyd SystemCombines easier application with good resistance properties and excellent color and gloss retention.


Prime 432-line JACK TAR® Silicone Yacht Finish 484 1.5Finish 432-line JACK TAR® Silicone Yacht Finish 484 1.5

Total Dry Mils 3.0

06.C JackTar®Alkyd Enamel SystemEconomic protection in mild marine service. Good color and gloss retention.


Prime 450-line JACK TAR® Yacht Deck Enamel 420 1.5Finish 450-line JACK TAR® Yacht Deck Enamel 420 1.5

Total Dry Mils 3.0


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 07 FIBERGLASS VESSELS - EXTERIOR - BELOW WATER LINE

Surface Preparation: Wet sand with a 50:50 solution of Al-Co-Sol, 75-41 and water to remove all traces of wax, mold releasecompounds, etc.. Wipe clean with clean rags saturated with same solution. Immediately (within 1 hour) before applying coating directlyto fiberglass, wipe down fiberglass with MoPoxYTM Thinner, 75-35, or MOTHANETM Thinner, 43-EF-70, or BLP Vinyl Thinner, 475-31.Use only clean cotton rags for cleaning and fiberglass preparation.

07.A MoPoxYTM Plus / JackTar® Vinyl Antifouling SystemOffers maximum durability for fiberglass vessels. This system consists of one coat of high solids, high build epoxy primer and twocoats of cuprous oxide, vinyl copolymer, anti-fouling paint.


Prime 41-CW-1 MoPoxYTM Plus Epoxy Coating 131 8Finish 473-73 JACK TAR® Vinyl Anti-fouling Paint 485 2Finish 473-73 JACK TAR® Vinyl Anti-fouling Paint 485 2




Prime 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Intermediate 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Finish 473-71 JACK TAR® Cold Plastic Anti-fouling Paint 537 2Finish 473-71 JACK TAR® Cold Plastic Anti-fouling Paint 537 2



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 07 FIBERGLASS VESSELS - EXTERIOR - BELOW WATER LINE (continued):

07.C JackTar® Phenolic / JackTar® Dub-L-Cop Antifouling SystemOffers good, economical protection for shrimp boats and other slow moving fiberglass hull vessels. This system consists of a phenolicanti-corrosive primer and a modified rosin based cuprous oxide anti-fouling paint.


Prime 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Intermediate 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Finish 473-74 JACK TAR® Dub-L-Cop Bottom Paint 568 2Finish 473-74 JACK TAR® Dub-L-Cop Bottom Paint 568 2



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 08 FIBERGLASS VESSELS - EXTERIOR - DECKS & LADDERS

Surface Preparation: Wet sand with a 50:50 solution of Al-Co-Sol, 75-41 and water to remove all traces of wax, moldrelease compounds, etc.. Wipe clean with clean rags saturated with same solution. Immediately (within 1 hour) before applying coatingdirectly to fiberglass, wipe down fiberglass with MoPoxYTM Thinner, 75-35, or MOTHANETM Thinner, 43-EF-70, or BLP Vinyl Thinner,475-31. Use only clean cotton rags for cleaning and fiberglass preparation.

08.A MoPoxYTM HS / MoPoxYTM AR-200 Deck Armor High Build SystemFor maximum service life, superior impact and abrasion resistance. Designed specifically for any fiberglass deck requiring excep-tional long term protection.


Prime 613-10 MoPoxYTM HS High Solids Epoxy Primer 382 3Finish 41-BW-1 MoPoxYTM Deck Armor AR-100 26 60

Total Dry Mils 63

08.B MoPoxYTM HS / MoPoxYTM NS-200 Deck Armor High Build Non-Skid SystemFor maximum service life, superior impact and abrasion resistance. Same protection and properties as the above system, except ina non-skid formulation.


Prime 613-10 MoPoxYTM HS High Solids Epoxy Primer 382 3Finish 41-BH-12 MoPoxYTM Deck Armor NS-200 24 60

Total Dry Mils 63

08.C MoPoxYTM HS Epoxy SystemA high performance deck coating system providing long term protection in marine environments.


Prime 613-10 MoPoxYTM HS High Solids Epoxy Primer 382 3Finish 613-series MoPoxYTM HS High Solids Epoxy Finish 374 3Finish 613-series MoPoxYTM HS High Solids Epoxy Finish (NOTE) 374 3

Total Dry Mils 9



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 09 FIBERGLASS VESSELS - INTERIOR - BULKHEAD & OVERHEAD





Total Dry Mils 9




Total Dry Mils 5


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 10 FIBERGLASS VESSELS - INTERIOR - DECKS, LADDERS & PASSAGEWAYS





Total Dry Mils 9



Prime 10-10 RUS-KIL® Metal Primer 337 2Finish 450-line JACK TAR® Yacht Deck Enamel 420 1.5Finish 450-line JACK TAR® Yacht Deck Enamel (NOTE) 420 1.5



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 11 WOODEN VESSELS - EXTERIOR -ABOVE WATER LINE

Surface Preparation: New wood should be sanded with fine garnet paper. Previously painted wood should be thoroughly cleanedand washed, then sanded with medium-fine garnet paper to remove all gloss. Feather-edge old paint around bare areas and spot primeas below. If old paint is in poor condition, remove completely and treat as new wood.

11.A MoPoxYTM Plus / MOTHANETM Polyurethane SystemCombines excellent chemical, solvent and abrasion resistance with superior gloss and color retention for maximum service.


Prime 41-CW-1 MoPoxYTM Plus Epoxy Coating 131 8Finish * 72-series MOTHANETM Polyurethane Coating 339 2Finish * 72-series MOTHANETM Polyurethane Coating 339 2


Total Dry Mils 12 - 13

11.B JackTar®Silicone Alkyd SystemCombines easier application with good resistance properties and excellent color and gloss retention.


Prime 432-line JACK TAR® Silicone Yacht Finish (thinned 10%) 484 1.5Finish 432-line JACK TAR® Silicone Yacht Finish 484 1.5Finish 432-line JACK TAR® Silicone Yacht Finish 484 1.5

Total Dry Mils 4.5

11.C JackTar®Alkyd Enamel SystemEconomic protection in mild marine service. Good color and gloss retention.


Prime 450-line JACK TAR® Yacht Deck Enamel (thinned 10%) 420 1.5Finish 450-line JACK TAR® Yacht Deck Enamel 420 1.5Finish 450-line JACK TAR® Yacht Deck Enamel 420 1.5

Total Dry Mils 4.5


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 12 WOODEN VESSELS - EXTERIOR - BELOW WATER LINE

Surface Preparation: Pressure wash with clean water to remove any surface contaminants. Allow to dry completely and sand toremove all coatings. Surface to be painted must be bare wood which is sound, clean and thoroughly dry prior to painting.

12.A MoPoxYTM Plus / JackTar® Vinyl Antifouling SystemOffers maximum durability for wooden vessels. This system consists of one coat of high solids, high build epoxy primer and twocoats of cuprous oxide, vinyl copolymer, anti-fouling paint.


Prime 41-CW-1 MoPoxYTM Plus Epoxy Coating 131 8Finish 473-73 JACK TAR® Vinyl Anti-fouling Paint 485 2Finish 473-73 JACK TAR® Vinyl Anti-fouling Paint 485 2




Prime 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Intermediate 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Intermediate 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Finish 473-71 JACK TAR® Cold Plastic Anti-fouling Paint 537 2Finish 473-71 JACK TAR® Cold Plastic Anti-fouling Paint 537 2



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 12 WOODEN VESSELS - EXTERIOR - BELOW WATER LINE

12.C JackTar® Phenolic / JackTar® Dub-L-Cop Antifouling SystemOffers good, economical protection for shrimp boats and other slow moving wooden hull vessels. This system consists of a phenolicanti-corrosive primer and a modified rosin based cuprous oxide anti-fouling paint.


Prime 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Intermediate 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Intermediate 409-68 JACK TAR® Phenolic Anti-corrosive Primer 310 3Finish 473-74 JACK TAR® Dub-L-Cop Bottom Paint 568 2Finish 473-74 JACK TAR® Dub-L-Cop Bottom Paint 568 2



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 13 WOODEN VESSELS - EXTERIOR - DECKS & LADDERS

Surface Preparation:. New wood should be sanded with fine garnet paper. Previously painted wood should be thoroughly cleanedand washed, then sanded with medium-fine garnet paper to remove all gloss. Feather-edge old paint around bare areas and spot primeas below. If old paint is in poor condition, remove completely and treat as new wood.

* NOTE: Primer should be thinned 15 - 20% on bare wood surfaces.

13.A MoPoxYTM HS / MoPoxYTM AR-200 Deck Armor High Build SystemFor maximum service life, superior impact and abrasion resistance. Designed specifically for any deck requiring exceptional longterm protection.


Prime * 613-10 MoPoxYTM HS High Solids Epoxy Primer 382 3Finish 41-BW-1 MoPoxYTM Deck Armor AR-100 26 60

Total Dry Mils 63

13.B MoPoxYTM HS / MoPoxYTM NS-200 Deck Armor High Build Non-Skid SystemFor maximum service life, superior impact and abrasion resistance. Same protection and properties as the above system, except ina non-skid formulation.


Prime * 613-10 MoPoxYTM HS High Solids Epoxy Primer 382 3Finish 41-BH-12 MoPoxYTM Deck Armor NS-200 24 60

Total Dry Mils 63

13.C MoPoxYTM HS Epoxy SystemA high performance deck coating system providing long term protection in marine environments.


Prime * 613-10 MoPoxYTM HS High Solids Epoxy Primer 382 3Finish 613-series MoPoxYTM HS High Solids Epoxy Finish 374 3Finish 613-series MoPoxYTM HS High Solids Epoxy Finish (NOTE) 374 3

Total Dry Mils 9



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 14 WOODEN VESSELS - INTERIOR - BULKHEAD & OVERHEAD






Total Dry Mils 9




Total Dry Mils 5


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 15 WOODEN VESSELS - INTERIOR - DECKS, LADDERS & PASSAGEWAYS





Prime * 613-10 MoPoxYTM HS Primer 382 3Finish 613-line MoPoxYTM HS Epoxy 374 3Finish 613-line MoPoxYTM HS Epoxy (NOTE) 374 3




Prime * 10-10 RUS-KIL® Metal Primer 337 2Finish 450-line JACK TAR® Yacht Deck Enamel 420 1.5Finish 450-line JACK TAR® Yacht Deck Enamel (NOTE) 420 1.5



251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 16 ENGINE ROOM - BULKHEAD, OVERHEAD & DECKS

Surface Preparation:Steel - Commercial Sandblast (SSPC-SP6) is preferred. Power Tool Clean (SSPC-SP3) or Hand Tool Clean (SSPC-SP2)are minimum acceptable.

Fiberglass - Wet sand with a 50:50 solution of Al-Co-Sol, 75-41 and water to remove all traces of wax, mold release compounds, etc..Wipe clean with clean rags saturated with same solution. Immediately (within 1 hour) before applying coating directly to fiberglass, wipedown fiberglass with MoPoxYTM Thinner, 75-35, or MOTHANETM Thinner, 43-EF-70, or BLP Vinyl Thinner, 475-31. Use only cleancotton rags for cleaning and fiberglass preparation.

Wood - New wood should be sanded with fine garnet paper. Previously painted wood should be thoroughly cleaned andwashed, then sanded with medium-fine garnet paper to remove all gloss. Feather-edge old paint around bare areas and spot prime asbelow. If old paint is in poor condition, remove completely and treat as new wood.




Prime 613-10 MoPoxYTM HS Primer 382 3Finish 613-line MoPoxYTM HS Epoxy 374 3Finish 613-line MoPoxYTM HS Epoxy (NOTE) 374 3

Total Dry Mils 9NOTE: Add JACK TAR® Non-Skid Deck Compound, 492-3 to the final finish coat for use on decks in work and traffic areas.



Prime 10-10 RUS-KIL® Metal Primer 337 2Finish 10-line RUS-KIL® Enamel 417 1.5Finish 10-line RUS-KIL® Enamel (NOTE) 417 1.5

Total Dry Mils 5NOTE: Add JACK TAR® Non-Skid Deck Compound, 492-3 to the final finish coat for use on decks in work and traffic areas.


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 17 POTABLE WATER TANKS

Surface Preparation:Steel - White Metal Sandblast (SSPC-SP5) is required.


17.A MoPoxYTM HS-50 NSF Epoxy SystemApproved by National Sanitation Foundation (NSF), Standard 61, for contact with potable water


Prime 40-BH-11 MoPoxYTM HS-50 NSF Epoxy 134 6Finish 40-BW-5 MoPoxYTM HS-50 NSF Epoxy 134 6

Total Dry Mils 12

Provide adequate ventilation during application, continuing ventilation during entire cure cycle. Allow the system to cure a minimum of7 days (at 75°F minimum) after application of the finish coat. Perform a “fresh water” rinse after cure cycle and prior to placing intoservice.

Section 18 FUEL TANKS (INCLUDING COMPENSTATED FUEL TANKS)

Surface Preparation:Steel - White Metal Sandblast (SSPC-SP5) is required.

18.A MoPoxYTM Mastic Epoxy System


Prime 40-AH-51 MoPoxYTM Mastic Epoxy 217 6Finish 40-AW-32 MoPoxYTM Mastic Epoxy 217 6

Total Dry Mils 12

Provide adequate ventilation during application, continuing ventilation during entire cure cycle. Allow the system to cure a minimum of7 days (at 75°F minimum) after application of the finish coat.


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)


Section 19 BILGES & VOIDS

Surface Preparation:Steel - Commercial Sandblast (SSPC-SP6) is preferred. Power Tool Clean (SSPC-SP3) or Hand Tool Clean (SSPC-SP2)are minimum acceptable.


Wood - New wood should be sanded with fine garnet paper. Previously painted wood should be thoroughly cleaned andwashed, then sanded with medium-fine garnet paper to remove all gloss. Feather-edge old paint around bare areas and spot prime asbelow. If old paint is in poor condition, remove completely and treat as new wood. Primer should be thinned 15 - 20% on bare woodsurfaces.

19.A MoPoxYTM Plus Epoxy SystemCombines maximum protection with minimum maintenance.


Prime 41-CW-1 MoPoxYTM Plus 131 8Finish 41-CW-1 MoPoxYTM Plus 131 8

Total Dry Mils 16

Provide adequate ventilation during application, continuing ventilation during entire cure cycle. Allow the system to cure a minimum of7 days (at 75°F minimum) after application of the finish coat.


PAINTING SYSTEMS GUIDE


251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

1

330 Line ACR-A-LACTM 100% Acrylic Gloss Enamel330-7 ACR-A-LACTM 100% Acrylic Metal Primer Red260-45 ARCHITECTURALTM Latex Block Filler

60-7 BLOC-FILTM Latex Block Filler19-10 BLOC-SEALTM Block Fill Base

1335 Line COVENTRY® 100% Acrylic Latex Semi-Gloss Enamel2335 Line COVENTRY® Acrylic Eggshell Enamel19-8 COVENTRY® Wood Sealer, White319-8 COVENTRY® Latex Enamel Undercoat335 Line COVENTRY® Latex High Gloss Enamel35 Line COVENTRY® Latex Flat Wall Paint135 Line COVENTRY® LUSTARITE® Alkyd Satin Enamel19-7 COVENTRY® Prymall 2 Q.D. Primer & Sealer

74-12 DUB-L-TITETM Silicone Waterproofing, Clear

43-25 ELASTOMERIC ROOF COATING Reflective White43-20 ELASTOMERIC WALL COAT, White19-8 ENAMEL UNDERCOAT and Wood Sealer: see also COVENTRY®

70-41 FLO-TECTM Phenolic Heavy Duty Gym Floor Finish55-DW-3 FOG DRY ACRYILIC COATING, Flat White55-AW9 FOG DRY ACRYILIC COATING, Gloss White6-DW-58 FOG DRY ALKYD FLAT COATING, White61-BW-2 FOG DRY ALKYD GLOSS COATING, White61-AW-6 FOG DRY ALKYD SEMI-GLOSS COATING, White

9-5 GALVA-TECTM 100% Acrylic Galvanized Primer80166 GALVANIZING REPAIR COATING DOD-P-21035A




251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

2

308-Line H2O Concrete Stain 100% Acrylic310-Line H2O RUS-KIL® Acrylic DTM Rust Resistant Coating310-Line H2O RUS-KIL® Acrylic DTM Rust Resistant Primers350-Line H2O Floor & Patio Satin Finish !00% Acrylic Polyurethane62-AY-5 HEAT RESISTANT ALUMINUM, Silicone Acrylic11-61 HEAT RESISTANT ALUMINUM, Silicone Alkyd62-AY-1 HIGH HEAT RESISTANT ALUMINUM, Silicone28-DR-147 HIGH SOLIDS PRIMER, Red Oxide

470-31 JACK TAR® 100% Phenolic Marine Spar Varinsh470-34 JACK TAR® Marine Spar Varnish w/ Ultraviolet Filter492-3 JACK TAR® Non-Skid Deck Compound432 Line JACK TAR® Silicone Yacht Finish

9835-165 LACQUER Sanding Sealer9835-172 LACQUER SS Hi Build White9835-Line LACQUER Tint Bases9835-098 LACQUER, Clear, WW Gloss9835-100 LACQUER, Clear, WW Satin

LUSTARITE®: See COVENTRY® LUSTARITE®

MARE ISLAND EPOXIES: See MIL-P-2444140-CM-1 MIL-P-24441 F 150 Type IV Green Primer40-AW-42 MIL-P-24441 F 152 Type IV White28-DR-160 MO-BARTM PM-III Universal Primer, Red (Gray 29DH093)40-AX-7 MO-TARTM C-200 Epoxy Coating, Black40-BX-6 MO-TARTM HB 90 Epoxy Coating28-DH-50 MO-ZINCTM 3 Inorganic Zinc Rich Primer

MOPACOTE®: See WEATHER-TITETM

41-Series MOPOX-ACRYLTM Acrylic Epoxy Coating40-AF-10 MoPoxYTM Clear Base - see 513 line for data41-BW-1 MoPoxYTM DECK ARMOR AR-10041-BH-12 MoPoxYTM DECK ARMOR NS-200, Non-skid41-AH-2 MoPoxYTM GF Glass Flake Phenolic Epoxy Coating, Gray




251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

3

69-AW-5 MoPoxYTM H2O-100 Waterborne Epoxy Acrylic, White69-DR-1 MoPoxYTM H2O-200 Waterborne Epoxy Metal Primer69-AW-6 MoPoxYTM H2O-200 Waterborne Polyadide Epoxy Coating, White40-DR-5 MoPoxYTM HB High Build Metal Primer40-BW-5 MoPoxYTM HS-50 NSF Epoxy Coating (For Potable Water)41-CW-2 MoPoxYTM HS-60 NSF Epoxy Coating (For Potable Water)613 Line MoPoxYTM HS High Solids Epoxy Coating613-10 MoPoxYTM HS High Solids Epoxy Metal Primer40-CM-11 MoPoxYTM HZR Zinc Rich Epoxy Primer, Green41-BK-14 MoPoxYTM IR High Solids Epoxy40-AY-2 MoPoxYTM MASTIC Aluminum40-AH-51 MoPoxYTM MASTIC Epoxy Coating, Gray40-AW-32 MoPoxYTM MASTIC Epoxy Coating, White41-AH-1 MoPoxYTM PH Phenolic Epoxy Coating, Gray41-CH-1 MoPoxYTM PLUS High-Build Epoxy Coating41-AF-2 MoPoxYTM PRE-PREP Rust Penetrating Sealer41-DM-3 MoPoxYTM PRIME Zinc Preconstruction Primer, HAPS Free41-DM-1 MoPoxYTM PRIME Zinc Preconstruction Primer\40-DR-12 MoPoxYTM PRIME Preconstruction Primer41-DM-2 MoPoxYTM ZR HS Zinc Rich HAPS Free Primer40-CM-4 MoPoxYTM ZR Zinc Rich Epoxy Primer, Green72 Line MOTHANETM HS-1000 Aliphatic Acrylic Polyurethane Enamel

30 Line NAM-A-LAC® All Purpose Enamel71 Line NUWOOD® Penerating Wood Finish72-35 NUWOOD® Polyurethane Gloss Finish72-36 NUWOOD® Polyurethane Satin Finish72-45 NUWOOD® Tung Oil Clear Stain

19-7 PRYMALL 2 Q.D. Primer and Sealer: See also COVENTRY®

310 Line RUS-KIL® H20 Acrylic see H2O RUS-KIL®

650 Line RUS-KIL® HI-HIDE 650 Gloss Enamel655 Line RUS-KIL® HI-HIDE 655 Semi-Gloss Enamel




251-443-6110251-408-0410(FAX)

800-621-6952800-672-6707(AL)

4

10 Line RUS-KIL® Rust Inhibiting Coating10 Line RUS-KIL® Rust Inhibiting Primer (Red, Gray, White)

28-DR-79 SILICONE ALKYD High Heat Primer206-10 SMOOTH-COTE® Exterior 100% Acrylic House Paint Primer296 Line SMOOTH-COTE® Exterior Acrylic Flat House Paint295 Line SMOOTH-COTE® Exterior Acrylic Semi-Gloss House Paint205-20 SMOOTH-COTE® Exterior & Interior Primer (Oil)

205-22 SMOOTH-COTE® Exterior Alkyd Oil Base House Paint205-10 SMOOTH-COTE® Exterior Oil Base House Paint Primer (Alkyd)291 Line SMOOTH-COTE® Exterior Vinyl Acrylic Flat House Paint293-Line SMOOTH-COTE® Interior Alkyd Semi-Gloss Enamel292-Line SMOOTH-COTE® Interior Latex Eggshell289-Line SMOOTH-COTE® Interior Latex Flat219-19 SMOOTH-COTE® Interior Latex Primer/Sealer290-Line SMOOTH-COTE® Interior Latex Semi-Gloss Enamel9-78 SPEED PRIME Red Oxide Primer28-DR-166 SPEED PRIMER HS High Solids Primer, Red50-Line SPEEDECK® Floor & Deck Enamel

SPRAY FOG DRY: see FOG DRY

9-42 VINYL WASH PRIMER

40 Line WEATHER-TITETM 100% Acrylic Latex House Paint - Flat140 Line WEATHER-TITETM 100% Acrylic Latex House Paint - Gloss240 Line WEATHER-TITETM 100% Acrylic Latex House Paint - Satin60-Series WEATHER-TITETM 100 Premium Siliconized Acrylic Caulk74-7 WEATHER-TITETM Clear Waterproofing Sealer5-20 WEATHER-TITETM Southern White Gloss House Paint5-6 WEATHER-TITETM Southern White House Paint Primer6-6 WEATHER-TITETM Universal 100% Acrylic Latex Primer7-10 WEATHER PROTECTOR® Exterior Clear Sealer & Preservative44 Line WEATHER PROTECTOR® Interior/Exterior Acrylic Latex Stain