content - nordroofsnordroofs.ie/data/product/33/nord-roofs-products-pdf.pdfmarket. russia belarus...

EuropEan history of thE Company Company profilE

BikroElast hppBipol hppBikroElast hmp BikroElast Epp BikroElast Epp 4.0 uniflEks Epp miDa stanDarD pV s4 yam 2000 Bipol stanDart hkp Bipol stanDart Ekp Bipol Xl EkpuniflEks Ekp uniflEks Ekp 5.0

ECoflEks V 2.0 ECoflEks pV 4.5 kg minEral ECoflEks V 4.5 kg minEral ECoflEks V 3.0 miDa tropik p40m prima plast nEW V 3.0 prima plast gV 4.0 miDa tropik C2000 prima plast pV 4.5 kg minEral

niCoBanD niCoBanD insiDE niCoBanD Duo

taBlE of tEChniCal spECifiCations

24

6 78 9

1011 1213141516 1718

20 21 2223 24 25262728

303132

34

ContEnt

roll-fED polymEr-BitumEn WatErproofing matErials

sBs moDifiED BitumEn roofing anD WatErproofing mEmBranE

app moDifiED BitumEn roofing anD WatErproofing mEmBranE

sElf-aDhEsiVE tapEs anD sEalants

2About CompAny

TechnoNICOL

1992

EuropEan historyof thE Company

tEChnoniCoL Company was foundEd.

2000TechnoNICOL continued its ex-pansion in Europe. The Company acquired its first foreign plant “Gargzdu MIDA”, located in Lithuania. At the same time, TechnoNICOL expanded its product range, and, therefore, MIDA fac-tory, which was producing bitumen shingles, began producing of roll-fed bitumen materials. This provided the Company opportunity to learn about a new and interesting seg-ment - products for pitched roofs. Products started to be actively deliv-ered to the Baltic countries (Latvia, Lithuania and Estonia).

2001-2008 The product range was actively expanded, and new plants were launched: • A production of stone wool

heat insulation under the TECHNO brand was launched as the production of TechnoNICOL XPS, heat-insu-lating slabs made of extruded polystyrene foam.

• Plant for producing flexible tiles SHINGLAS was opened in Ryazan.

• Production of mastics was or-ganized for making packaged deliveries of waterproofing and heat-insulating materials to European venues. Deliveries were made from Vyborg, Ryazan and Osipovichi plants.

At the same time, representative of-fices in Latvia, Poland and Turkey were opened during this period.

1993In 1993 in Moscow was opened the first office. In 1994 the Company launched its own first production plant for roll-fed roofing in Vyborg. In subsequent years, dozens of its own sales offices were opened throughout Russia.

1998The Vyborg plant started cooper-ating with Nordic countries, and it made its first deliveries of materials to Finland and Sweden. This estab-lished a new operational level for the Company, that set new challenges - acquiring knowledge of the foreign construction market, studying the regulatory and technological base became necessary.

1999The Company had 5 production sites and 35 retail branches in different regions of the Russian Federation. During this year the Company en-tered the Ukrainian market and opened its first retail branch in Kiev.Built in 1998 in Ryazan, the Technoflex plant became one of Europe’s most modern factories in the production of roofing and wa-terproofing materials. In 1999 began deliveries to Eastern European countries (Slovakia and the Czech Republic, Poland).

3aBout Company

technoniCol is the largest European manufacturer and supplier of roofi ng, water-proofi ng and heat-insulating materials.

the Corporation includes 37 factories, its own retail net-work and representative of-fi ces in 36 countries. the corporation’s turnover is more than 1350 million euros.

the goal of technoniCol is to create cost-effective ma-terials and solutions for the protection of the environ-ment and human health. more than 200 million peo-ple all over the world live and work in buildings constructed using technoniCol materials.

2008The “Dehtochema” Czech plant was acquired by the TechnoNICOL company, which is located in the city of Bělá pod Bezdězem. This plant had been manufacturing bitumen insulating materials for more than a hundred years. The plant was founded in 1868. The Company expanded its supply-chain to Central European countries.

This time was diffi cult for the Company, since TechnoNICOL, like all other major European producers, became affected by the global eco-nomic crisis. But the Company suc-cessfully overcame the crisis, while maintaining and even strengthen-ing its position in certain product markets.

2009-2013The Company has cooperated with more than 50 independent sales partners and retailers op-erating in Western and Eastern Europe, Nordic countries, and Baltic countries.

At the same time large-scale re-construction of the plant in the Belarusian town of Osipovichi was on its way. An increase in the product range and capacity of the plant was aimed at the pro-duction of roll-fed materials fo-cused exclusively on the European market.

Russia

Belarus

Ukraine

Romania

Hungary

Bulgaria

Turkey

Austria

Lithuania

Latvia

Poland

Germany

Denmark

Great Britain

Norway

Sweden

Czech Republic

Slovakia

Estonia

Finland

Serbia

Moldavia

Greece

Macedonia

Iceland

4aBout Company

TechnoNICOL

our production is designed to meet your requirements:Our production capacities and equipment give us ability to supply materials for large construction projects and to develop unique products based on your indi-vidual requirements.

Following the regional market demands, we extended geography of our plants. It made us more flexible and now we can supply our products more promptly without extra transportation costs.

We are proud of what we produce and create.We enjoy seeing how new high-quality materials are produced from plain raw components with our up-to-date equipment, our work and efforts. We are glad to know that our materials are used in the construction of such complex objects as: houses, plants, bridges, and social infrastructure facilities, which improve the level and quality of life.

Continuous progress and improvement: We are continuously improving ourselves and strive to do the same for the en-vironment. Our goal is to set a new quality level for cooperation of all players in the construction market.

We give consideration to both trivial and global issues: from usability of our products to upgrading the general qualification of specialists in the industry.

TechnoNICOL recipe for success and continuous progress is first and foremost improvement of services for its clients and partners. Competence of our person-nel, professional technical consultations, quality products and solutions, local bases and offices, entire scope of materials supply and installation services — all these enable us to approach every client individually. We want to be leaders not just in quality product manufacturing but also in meeting our clients expecta-tions.

The combination of advanced management, effective investments, and our structure aimed at company growth and development makes TechnoNICOL one of the leaders in production and distribution of insulation systems in Russia and European countries.Expanding our manufacturing capacities and our scope of services, imple-menting innovations, giving careful consideration to environment protection and energy efficiency, we are better than anybody else in meeting the social expectations and market demands.

social responsibility:We benefit society where we work and environment where we live. We enjoy being a part of what comes in 100 years.

• All plants of the Corporation are subjected to state environmental ap-praisal at their design stage. The inside and outside environment at our industrial sites is monitored daily. We invest in waste-free production, advanced equipment, and environmental protection technologies.

• All products developed and manufactured by TechnoNICOL meet sani-tary and environmental standards and are safe for human beings and the environment. We create energy-efficient technologies and materials to save the environment.

Company profilEown distribution network and representative offices in

is invested in environmentalprotection

36

1 miLLion Euros/yEar

countries of the world

about

sBs modified bitumen roofing and waterproofing membrane.

application areas:Designed for installation as the bottom layer of roof cladding on build-ings and constructions for waterproofing of engineering structures. Used for new roofing construction and for repair of old roof. Ideal for the installation as two-layer waterproofing for the foundations accord-ing to EN 13969. Can be used as underlayer for a bitumen shingles. Not recommended to use as one-layer roof cladding or one-layer water-proofing.

Description:Bikroelast EPP 4.0 is roll-fed, torchable, SBS-modified bitumen roofing and waterproofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of modified bitumen binder, consisting from bitumen, SBS (styrene-butadiene-styrene) polymer modifier and mineral filler (talc, dolomite etc.), on the polyester carrier. Polymer film is used on the top and bottom surfaces.

The material does not contain the substances which are dangerous for the people or animals.

application method:Torch-on application on the prepared surface. At use as underlayer for a bitumen shingles fastened mechanically.


TechnoNICOL

BikroElast Epp 4.0

multifunctional

universal waterproofing

Durability

product technical data

Properties Test method SBS modified bitumen

External fire performance EN 13501-5 ENV 1187:2002, test 2* ВROOF(t2)*

Length / width, m EN 1848-1 10×1

Weight, kg/m2 EN 1849-1 4.0-0.20

Reinforcement type and weight polyester, 180 g/m2

Maximum tensile force longitudinal / transverse, N/50 mm EN 12311-1 800/600±100

Resistance to tearing (nail shank), N EN 12310-1 180/180±50

Elongation, % EN 12311-1 50/50±25

Flow resistance at elevated temperature, °С EN 1110 ≥ 85

Flexibility at low temperature, °С / Ø mm EN 1109 ≤ -10/30

Watertightness, kPа EN 1928 200

Water vapour transmission properties EN 1931 µ=20 000

Protective covering type:

on the top polymer film

on the bottom polymer film

* This material is part of a two-layer roofing system and corresponds to the B-roof only in combination with a second layer of roofing system.

sBs modifiEd BitumEn roofing and watErproofing mEmBranEs

6




application areas:Designed for installation as the bottom layer of roof cladding on build-ings and constructions, for waterproofing of engineering structures and for vapour sealing. Used for new roofing construction and for repair of old roof on the rigid foundation. Not recommended to use as one-layer roof cladding or one-layer waterproofing.

Description:BIKROELAST HPP is roll-fed, torchable, SBS modified bitumen roofing and waterproofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of modified bitumen binder, consisting from bitumen, SBS (styrene-butadiene-styrene) polymer modifier and mineral filler (talc, dolomite etc.), on the glass-fiber mat carrier. Polymer film is used on the top and bottom surfaces. The material does not contain the substances which are dangerous for the people or animals.

application method:Torch-on application on the prepared surface.

BikroElast hpp

sBs modified

underlay membrane


Properties Test method BIKROELAST HPP


Length / width, m EN 1848-1 15/16х1

Weight, kg/m2 EN 1849-1 3.0-0.15

Reinforcement type and weight glass-fiber mat, 55 g/m2



Elongation, % EN 12311-1 2.2/2.2±0.22








7


TechnoNICOL




Description:BIPOL HPP is roll-fed, torchable, SBS modified bitumen roofing and wa-terproofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of polymer-bitumen binder, consisting from bitumen, SBS (styrene-butadiene-styrene) polymer modifier and mineral filler (talc, dolomite etc.), on the glass-fiber mat carrier. Polymer film is used on the top and bottom surfaces. The material does not contain the substances which are dangerous for the people or animals.


Bipol hpp

sBs modified

underlay membrane


Properties Test method BIPOL HPP



Weight, kg/m2 EN 1849-1 3.0-0.15




Elongation, % EN 12311-1 2.2/2.2±0.22








8





Description:BIKROELAST HMP is roll-fed, torchable, bitumen, SBS modified roofing waterproofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of modified bitumen binder, consisting from bitumen, SBS (styrene-butadiene-styrene) polymer modifier and mineral filler (talc, dolomite etc.), on the glass-fiber mat carrier. Polymer film is used on the bottom surface. The protective fine-grained sand layer is placed on the top surface. It provides possibility to install of the next (top) layer of roof cladding by standard torch-on ap-plication or by attaching it on hot- or cold-applied mastics. The material does not contain the substances which are dangerous for the people or animals.


BikroElast hmp

sBs modified

underlay membrane


Properties Test method BIKROELAST HMP


Length / width, m EN 1848-1 15/16×1

Weight, kg/m2 EN 1849-1 3.0-0.15




Elongation, % EN 12311-1 2.2/2.2±0.22






on the top fine-grained sand


9


TechnoNICOL



application areas:Designed for installation as the bottom layer of roof cladding on build-ings and constructions for waterproofing of engineering structures. Used for new roofing construction and for repair of old roof. Ideal for the installation as two-layer waterproofing for the foundations (accord-ing to EN 13969). Not recommended to use as one-layer roof cladding or one-layer waterproofing.

Description:Bikroelast EPP is roll-fed, torchable, SBS modified bitumen roofing and waterproofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of modified bitumen binder, consisting from bitumen, SBS (styrene-butadiene-styrene) polymer modifier and mineral filler (talc, dolomite etc.), on the polyester carrier. Polymer film is used on the top and bottom surfaces. The material does not contain the substances which are dangerous for the people or animals.


BikroElast Epp

sBs modified

underlay membrane


Properties Test method BIKROELAST EPP



Weight, kg/m2 EN 1849-1 3.0-0.15




Elongation, % EN 12311-1 50/50±25








10





Description:Bikroelast EPP 4.0 is roll-fed, torchable, SBS modified bitumen roofing and waterproofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of modified bitumen binder, consisting from bitumen, SBS (styrene-butadiene-styrene) polymer modifier and mineral filler (talc, dolomite etc.), on the polyester carrier. Polymer film is used on the top and bottom surfaces. The material does not contain the substances which are dangerous for the people or animals.


BikroElast Epp 4.0

sBs modified

underlay membrane


Properties Test method BIKROELAST EPP 4.0



Weight, kg/m2 EN 1849-1 4.0-0.2




Elongation, % EN 12311-1 50/50±25








11


TechnoNICOL




Description:UNIFLEKS EPP is roll-fed, torchable, bitumen, roofing and waterproof-ing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of polymer-bitumen binder, consisting from bitumen, SBS (styrene-butadiene-styrene) polymer modifier and mineral filler (talc, dolomite etc.), on the polyester carrier. Polymer film is used on the top and bottom surfaces.The material does not contain the substances which are dangerous for the people or animals.


uniflEks Epp

sBs modified

underlay membrane


Properties Test method UNIFLEKS EPP



Weight, kg/m2 EN 1849-1 3.7-0.185




Elongation, % EN 12311-1 50/50±25


Flexibility at low temperature, °С / Ø mm EN 1109 ≤ - 20/30






12




application areas:Designed for installation as the bottom layer of roof cladding on build-ings and constructions. Used for new roofing construction and for re-pair of old roof. Not recommended to use as one-layer roof cladding.

Description:MIDA Standard PV S4 is roll-fed, torchable, bitumen, roofing water-proofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of polymer-bitumen binder, consisting from bitumen, SBS (styrene-butadiene-styrene) polymer modifier and mineral filler (talc, dolomite etc.), on the polyester carrier. Fine-grained sand or polymer film is used as the top protective layer. Polymer film is used on the bottom surface. The material does not contain the substances which are dangerous for the people or animals.

application method:Torch-on application. Material can also be fastened mechanically, in this case membrane should be welded in the overlaps.

miDa stanDarD pV s4

sBs modified

underlay membrane


Properties Test method MIDA STANDARD PV S4



Thickness, mm EN 1849-1 4.0±0.2

Reinforcement type polyester



Elongation, % EN 12311-1 50/50±20


Flexibility at low temperature, °С / Ø mm EN 1109 ≤ -10

Watertightness, kPа EN 1928 watertight



on the top fine-grained sand or polymer film


13


TechnoNICOL



application areas:Designed for installation as the bottom layer of roof cladding, for water-proofing of engineering structures and for vapor sealing. Can be used as underlayer for bitumen shingles or other types of roofing materials for pitched roofs. Not recommended to use as one-layer roofing clad-ding or one-layer waterproofing.

Description:Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of polymer-bitumen binder, consisting from bitumen, SBS (styrene-butadiene-styrene) polymer modifier and mineral filler (talc, dolomite etc.), on the glass-fiber mat carrier. Fine-grained sand is used as the top and bottom protective sur-faces. The material does not contain the substances which are dangerous for the people or animals.

application method:Glued to the prepared surface on cold- and hot-applied bitumen mas-tics. Fastened mechanically at use as underlayer.

yam 2000

sBs modified

underlay membrane


Properties Test method YAM 2000


Length / width, m EN 1848-1 10/20х1Weight, kg/m2 EN 1849-1 2.0-0.1




Elongation, % EN 12311-1 2.2/2.2±0.22







on the bottom fine-grained sand

14




application areas:Designed for installation as the top layer of roof cladding on buildings and constructions, for waterproofing of engineering structures. Used for new roofing construction and for repair of old roof. Not recom-mended to use as one-layer roof cladding or one-layer waterproofing.

Description:BIPOL STANDART HKP is SBS modified bitumen roofing and water-proofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of modified bitumen binder, consisting from bitumen, SBS (styrene-butadiene-styrene) polymer modifier and mineral filler (talc, dolomite etc.), on the glass-fiber mat carrier. As top protective layer, the slate dressing compound is used for ultraviolet exposure protection of bitumen binder. Polymer film is used on the bottom surface. The material does not contain the substances which are dangerous for the people or animals.


Bipol stanDart hkp

sBs modified

Cap sheet membrane


Properties Test method BIPOL STANDART HKP


Length / width, m EN 1848-1 8/10/12х1

Weight, kg/m2 EN 1849-1 4.5-0.225




Elongation, % EN 12311-1 2.2/2.2±0.22






on the top coarse-grained slate


15


TechnoNICOL




Description:BIPOL STANDART EKP is SBS modified bitumen roofing and water-proofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of modified bitumen binder, consisting from bitumen, SBS (styrene-butadiene-styrene) polymer modifier and mineral filler (talc, dolomite etc.), on the polyester carrier. As top protective layer, the slate dressing compound is used for ultravio-let exposure protection of bitumen binder. Polymer film is used on the bottom surface. The material does not contain the substances which are dangerous for the people or animals.


Bipol stanDart Ekp

sBs modified

Cap sheet membrane


Properties Test method BIPOL STANDART EKP



Weight, kg/m2 EN 1849-1 4.5-0.225




Elongation, % EN 12311-1 50/50±25








16





Description:BIPOL XL EKP is SBS modified bitumen roofing and waterproofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of polymer-bitumen binder, consisting from bitumen, SBS (styrene-butadiene-styrene) polymer modifier and mineral filler (talc, dolomite etc.), on the polyester carrier. As top protective layer, the slate dressing compound is used for ultravio-let exposure protection of bitumen binder. Polymer film is used on the bottom surface. The material does not contain the substances which are dangerous for the people or animals.


Bipol Xl Ekp

sBs modified

Cap sheet membrane


Properties Test method BIPOL XL EKP



Weight, kg/m2 EN 1849-1 5.0-0.25




Elongation, % EN 12311-1 50/50±25








17


TechnoNICOL




Description:UNIFLEKS EKP is roll-fed, torchable, bitumen, roofing and waterproof-ing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of polymer-bitumen binder, consisting from bitumen, SBS (styrene-butadiene-styrene) polymer modifier and mineral filler (talc, dolomite etc.), on the polyester carrier. As top protective layer, the slate dressing compound is used for ultravio-let exposure protection of bitumen binder. Polymer film is used on the bottom surface. The material does not contain the substances which are dangerous for the people or animals.


uniflEks Ekp

sBs modified

Cap sheet membrane


Properties Test method UNIFLEKS EKP



Weight, kg/m2 EN 1849-1 4.7-0.235




Elongation, % EN 12311-1 50/50±25








18





Description:UNIFLEKS EKP 5.0 is roll-fed, torchable, bitumen, roofing and water-proofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of polymer-bitumen binder, consisting from bitumen, SBS (styrene-butadiene-styrene) polymer modifier and mineral filler (talc, dolomite etc.), on the polyester carrier. As top protective layer, the slate dressing compound is used for ultravio-let exposure protection of bitumen binder. Polymer film is used on the bottom surface.The material does not contain the substances which are dangerous for the people or animals.


uniflEks Ekp 5.0

sBs modified

Cap sheet membrane


Properties Test method UNIFLEKS EKP 5.0



Weight, kg/m2 EN 1849-1 5.0-0.25




Elongation, % EN 12311-1 50/50±25














TechnoNICOL

BikroElast Epp 4.0

multifunctional


Durability


Properties Test method APP modified bitumen



Weight, kg/m2 EN 1849-1 4.0-0.20




Elongation, % EN 12311-1 50/50±25









app modifiEd BitumEn roofing and watErproofing mEmBranEs

20


app modified bitumen roofing and waterproofing membrane.

application areas:Designed for installation as the bottom layer for various types of roofing systems. Can be used as vapor barrier and as a waterproofing cutoff. Material can also be used as underlayer for bitumen shingles or other types of roofing materials for pitched roofs. Not recommended to use as one-layer roof cladding or one-layer wa-terproofing.

Description:ECOFLEKS V 2.0 kg is APP modified bitumen roofing waterproofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of bitumen binder, consisting from bitumen, APP (atactic polypropylene) polymer modifier and min-eral filler (talc, dolomite etc.), on the glass-fiber mat carrier. Polymer film is used on the top and bottom surfaces. The material does not contain the substances which are dangerous for the people or animals.

application method:Fastened mechanically at use as the bottom layer of roof cladding and as underlayer for bitumen shingles. At use as a vapor barrier or water-proofing cutoff is placed freely, welded in the overlaps.

ECoflEks V 2.0 kg

app modified

underlay membrane


Properties Test method ECOFLEKS V 2.0 kg

Fire reaction ЕN 13501-1 class ЕLength / width, m EN 1848-1 15/16х1

Weight, kg/m2 EN 1849-1 2.0±0.2




Elongation, % EN 12311-1 4/4±2


Flexibility at low temperature, °С / Ø mm EN 1109 ≤ 0/30






21


TechnoNICOL


application areas:Designed for installation as the top layer of roof cladding on buildings and constructions, for waterproofing of engineering structures. Used for new roofing construction and for repair of old roof. Particularly suit-able for local repair. Not recommended to use as one-layer roof clad-ding or one-layer waterproofing.

Description:ECOFLEKS PV 4.5 kg Mineral is APP modified bitumen roofing water-proofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of polymer-bitumen binder, consisting from bitumen, APP (atactic polypropylene) polymer modi-fier and mineral filler (talc, dolomite etc.), on the polyester carrier. As top protective layer, the slate dressing compound is used for ultraviolet exposure protection of bitumen binder. Polymer film is used on the bot-tom surface. The material does not contain the substances which are dangerous for the people or animals.


ECoflEks pV 4.5 kg mineral

app modified

Cap sheet membrane


Properties Test method ECOFLEKS PV 4.5 kg Mineral

Fire reaction ЕN 13501-1 class ЕLength / width, m EN 1848-1 8/10/12х1

Weight, kg/m2 EN 1849-1 4.5±0.2




Elongation, % EN 12311-1 35/35±10








22



application areas:Designed for installation as the top layer of roof cladding on buildings and constructions, for waterproofing of engineering structures. Used for new roofing construction and for repair of old roof. Particularly suit-able for local repair. Not recommended to use as one-layer roof clad-ding or one-layer waterproofing.

Description:ECOFLEKS V 4.5 kg Mineral is APP modified bitumen roofing water-proofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of polymer-bitumen binder, consisting from bitumen, APP (atactic polypropylene) polymer modifier and mineral filler (talc, dolomite etc.), on the glass-fiber mat carrier. As top protective layer, the slate dressing compound is used for ultraviolet exposure protection of bitumen binder. Polymer film is used on the bot-tom surface. The material does not contain the substances which are dangerous for the people or animals.


ECoflEks V 4.5 kg mineral

app modified

Cap sheet membrane


Properties Test method ECOFLEKS V 4.5 kg Mineral

Fire reaction ЕN 13501-1 class ЕLength / width, m EN 1848-1 8/10/12х1

Weight, kg/m2 EN 1849-1 4.5±0.2












23


TechnoNICOL


application areas:Designed for installation as the bottom layer of roof cladding on build-ings and constructions. Used for new roofing construction and for re-pair of old roof. Not recommended to use as one-layer roof cladding or one-layer waterproofing.

Description:ECOFLEKS V 3.0 kg is APP modified bitumen roofing waterproofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of bitumen binder, consisting from bitumen, APP (atactic polypropylene) polymer modifier and min-eral filler (talc, dolomite etc.), on the glass-fiber mat carrier. Polymer film is used on the top and bottom surfaces.The material does not contain the substances which are dangerous for the people or animals.


ECoflEks V 3.0 kg

app modified

underlay membrane


Properties Test method ECOFLEKS V 3.0 kg


Weight, kg/m2 EN 1849-1 3.0±0.2












24



application areas:Designed for installation as the top layer of roof cladding on buildings and constructions. Used for new roofing construction and for repair of old roof. Not recommended to use as one-layer roof cladding.

Description:MIDA TROPIK P40M is roll-fed, torchable, bitumen, roofing and water-proofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of polymer-bitumen binder on polyester carrier. As top protective layer, the slate dressing com-pound is used for ultraviolet exposure protection of polymer-bitumen binder. Polymer film is used on the bottom surface. The material does not contain the substances which are dangerous for the people or animals.


miDa tropik p40m

app modified

Cap sheet membrane


Properties Test method MIDA TROPIK P40M

Fire reaction ЕN 13501-1 class ЕLength / width, m EN 1848-1 10×1




Elongation, % EN 12310-1 30/30±10

Flow resistance at elevated temperature, °С EN 12311-1 ≥ 110

Flexibility at low temperature, °С EN 1110 ≤ -5

Watertightness, kPа EN 1928 absolute





25


TechnoNICOL


application areas:Designed for installation as the bottom layer for various types of roofing systems. Can be used as vapor sealing and as a waterproofing cutoff. Not recommended to use as one-layer roof cladding or one-layer wa-terproofing. Do not use on the base of mineral wool.

Description:PRIMA PLAST NEW V 3.0 is APP modified bitumen roofing waterproof-ing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of bitumen binder, consisting from bitumen, APP (atactic polypropylene) polymer modifier and min-eral filler (talc, dolomite etc.), on the glass-fiber mat carrier. Polymer film is used on the top and bottom surfaces. The material does not contain the substances which are dangerous for the people or animals.

application method:Torch-on application on the prepared surface. As the vapor barrier is placed freely on the plane, welded in the overlaps.

prima plast nEW V 3.0

app modified

underlay membrane


Properties Test method PRIMA PLAST NEW V 3.0


Weight, kg/m2 EN 1849-1 3.0±5%

Reinforcement type glass-fiber mat

Maximum tensile force longitudinal / transverse, N/50 mm EN 12311-1 450/350



Flexibility at low temperature, °С EN 1110 ≤ -5






26



application areas:Designed for installation as the bottom layer for various types of roofing systems. Can be used as vapor sealing and as a waterproofing cutoff. Not recommended to use as one-layer roofing cladding or one-layer waterproofing.

Description:PRIMA PLAST GV 4.0 is APP modified bitumen roofing waterproofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of bitumen binder, consist-ing from bitumen, APP (atactic polypropylene) polymer modifier and mineral filler (talc, dolomite etc.), on the glass-fiber mat carrier. Fine-grained sand is used as the top protective layer. Polymer film is used on the bottom surface. The material does not contain the substances which are dangerous for the people or animals.

application method:Torch-on application on the prepared surface. As the vapor barrier is placed freely, welded in the overlaps.

prima plast gV 4.0

app modified

underlay membrane


Properties Test method PRIMA PLAST GV 4.0


Weight, kg/m2 EN 1849-1 4.0±5%






Flexibility at low temperature, °С / Ø mm EN 1109 ≤ 0






27


TechnoNICOL


application areas:Designed for installation as the bottom layer of roof cladding on build-ings and constructions. Can be used as vapor sealing and as a water-proofing cutoff. Used for new roofing construction and for repair of old roof. Not recommended to use as one-layer roofing cladding.

Description:MIDA TROPIK C 2000 is roll-fed, torchable, bitumen, roofing and wa-terproofing membrane. Manufactured according to EN 13707:2004+A2:2009. Material is produced by two-sided placing of polymer-bitumen binder on glass-fiber mat carrier. The top and bottom surfaces of the material are covered with the polymer film. The material does not contain the substances which are dangerous for the people or animals.

application method:Torch-on application on the prepared surface. As the vapor barrier is placed freely, welded in the overlaps.

miDa tropik C 2000

app modified

underlay membrane


Properties Test method MIDA TROPIK C 2000






Elongation, % EN 12311-1 ≥ 110

Flow resistance at elevated temperature, °С EN 1110 ≤ -5

Flexibility at low temperature, °С / Ø mm EN 1109 ≤ 0






28



application areas:Designed for installation as the top layer of roof cladding on buildings and constructions. Used for new roofing construction and for repair of old roof. Not recommended to use as one-layer roof cladding.

Description:PRIMA PLAST PV 4.5 kg Mineral is APP modified bitumen roofing wa-terproofing membrane. Manufactured according to ЕN 13707:2004 + А2:2009. Material is produced by two-sided placing of APP modified bitumen binder on the polyester carrier. As top protective layer, the slate dressing compound is used for ultraviolet exposure protection of bitumen binder. Polymer film is used on the bottom surface. The material does not contain the substances which are dangerous for the people or animals.


prima plast pV 4.5 kg mineral

app modified

Cap sheet membrane


Properties Test method PRIMA PLAST PV 4.5 kg Mineral


Weight, kg/m2 EN 1849-1 4.0-0.20



Elongation, % EN 12310-1 30/30±10


Flexibility at low temperature, °С EN 1110 ≤ 0

Adhesion of granules, % EN 1109 15±15












TechnoNICOL

BikroElast Epp 4.0

multifunctional


Durability


Properties Test method SELF-ADHESIVE TAPES



Weight, kg/m2 EN 1849-1 4.0-0.20




Elongation, % EN 12311-1 50/50±25









sELf-adhEsiVE tapEs and sEaLants

30


niCoBanD

Basic dimensionsWidth, cm 5 7.5 10 15 20 30

Length 3 m + + + + - -

Length 10 m - + + + + +

tape color

application areas:Sealing and waterproofing.

Description:NICOBAND is a universal self-adhesive sealing tape. It is produced by placing a color reinforced aluminum covering on a water-proof self-adhesive bitumen layer. The protective film on the adhesive bitumen layer is easy to remove.The material is easy and convenient to use, and it bonds ideally to concrete, gypsum, metal, bitumen, stone, wood and other surfaces. The sealing tape is designed for sealing seams and joints, repairing cracks, waterproofing, and corrosion protection.

application method:The surface must be clean, dry, and free from rust and dust. For a better and more durable bond a priming of the base is recom-mended. The surface and material temperature must be at least +5 °C. At lower temperatures it is necessary to heat the adhesive side of the material and the base. It is not recommended to apply a tape to hot vertical surfaces (with a temperature above +85 °C).

storage:Store in a place protected from atmospheric precipitation and direct sunlight.

Colored aluminum coating with protection from UV radiation

Self-adhesive sealing layer of bituminous

Easily removable protective film

31


TechnoNICOL


Length 3 m + + + + - -

Length 10 m - + + + + +

niCoBanD insiDE

application areas:The material is intended for indoor use. Suitable for:• Sealing joints in the ventilation system (ducts, floors exible ducts).

• Sealing of various pipes in cold areas.

• The product adjacencies to the walls, and other protruding parts for sealing the interior floors of the roll and mastic materials.

• The unit is waterproof floors in the rooms (bathrooms, kitchen) without the use of protective cement sand screed. Directly on the material can be glued ceramic tile.

Also used where the material will be closed from the effects of UV-rays:• The unit capillary cutoff for masonry and wood construction.

• Vapor barrier and waterproofing assembly seams at the organization of heat insulation of foamed polyethylene.

Description:NICOBAND INSIDE is a self-adhesive sealing and waterproofing polymer-bitumen tape. Produced by unilateral application of anti-adhesion to the polymer film self-adhesive bitumen-polymer binder consisting of bitumen, SIS (styrene-isoprene-styrene) polymer modifiers and special adhesive additives. Self-adhesive non-woven polypropylene (Spunbond) is used as a protective layer on the other side.

application method:Attached to the dry and cleaned surface. Fit, without any equipment. It is recommended to work at temperatures above +5 °C.


Bituminous self-adhesive sealing layer


Non-woven polypropylene (Spunbond)

32



Length 3 m + + + + - -

Length 10 m - + + + + +

niCoBanD Duo

application areas:Sealing seams, cracks and joints.

Description of material:NICOBAND DUO is a double-sided self-adhesive polymer-bitumen tape for sealing hidden seams and joints, for temporary fas-tening or for the simultaneous fixation and sealing of small elements. NICOBAND DUO consists of a polymer-bitumen layer of a special composition that provides good adhesion to virtually any surface. On both sides it is protected by polymer films, which are easily removed.The material is easy and convenient to apply. Has excellent adhesion to metal, concrete, plastic, asphalt, wood, glass, etc.

application method:The surface must be clean, dry, and free from rust and dust. For a better and more durable bond a priming of the base is recom-mended. The surface and material temperature must be at least +5 °C. At lower temperatures it is necessary to heat the adhesive side of the material and the base. It is not recommended to apply a tape to hot vertical surfaces (with a temperature above +85 °C).


Bituminous self-adhesive sealing layer









TechnoNICOL

BikroElast Epp 4.0

multifunctional


Durability


Properties Test method Table of technical specifications



Weight, kg/m2 EN 1849-1 4.0-0.20




Elongation, % EN 12311-1 50/50±25









taBLE of tEChniCaL spECifiCations

34


taBlE of tEChniCal spECifiCations

properties length / width

reinforcement type and weight Weight flexibility at low

temperatureflow resistance at

elevated temperature

maximum tensile force longitudinal

/ transverse

Elongationlongitudinal / transverse

resistance to tearing

longitudinal / transverse

application area top protective surface

Bottom protective surface

Units of measurement m kg/m2 °С °С N/50 mm % N

SBS modified bitumen roofing and waterproofing membrane.

BikroElast hpp 15/16x1 glass-fiber mat, 55 g/m2 3.0-0.15 ≤ -10 ≥ 85 400/250 ±100 2.2/2.2 ±0.22 50/50 ±10 underlay membrane polymer film polymer film

Bipol hpp 15/16х1 glass-fiber mat, 55 g/m2 3.0-0.15 ≤ -15 ≥ 85 400/250 ±100 2.2/2.2 ±0.22 50/50 ±10 underlay membrane polymer film polymer film

BikroElast hmp 15/16x1 glass-fiber mat, 55 g/m2 3.0-0.15 ≤ -10 ≥ 85 400/250 ±100 2.2/2.2 ±0.22 50/50 ±10 underlay membrane fine-grained sand polymer film

BikroElast Epp 15/16x1 polyester, 150 g/m2 3.0-0.15 ≤ -10 ≥ 85 600/500 ±100 50/50±25 180/180±50 underlay membrane polymer film polymer film

BikroElast Epp 4.0 8/10х1 polyester, 150 g/m2 4.0-0.2 ≤ -10 ≥ 85 600/500 ±100 50/50±25 180/180±50 underlay membrane polymer film polymer film

uniflEks Epp 8/10х1 polyester, 160 g/m2 3.7-0.185 ≤ -20 ≥ 95 700/500 ±100 50/50±25 180/180±30 underlay membrane polymer film polymer film

miDa stanDarD pV s4 8/10х1 polyester - ≤ -10 ≥ 85 600/500 ±100 50/50±20 200/200 ±100 underlay membrane fine-grained sand or polymer film polymer film

yam 2000 10/20х1 glass-fiber mat, 55 g/m2 2.0-0.1 ≤ -15 ≥ 85 300/300 ±50 2.2/2.2 ±0.22 30/30±10 underlay membrane fine-grained sand fine-grained sand

Bipol stanDart hkp 8/10/12х1 glass-fiber mat, 55 g/m2 4.5-0.225 ≤ -15 ≥ 85 400/250 ±100 2.2/2.2 ±0.22 50/50 ±10 сap sheet membrane coarse-grained slate polymer film

Bipol stanDart Ekp 8/10x1 polyester, 160 g/m2 4.5-0.225 ≤ -15 ≥ 85 600/500±100 50/50±25 180/180±50 сap sheet membrane coarse-grained slate polymer film

Bipol Xl Ekp 8/10х1 polyester, 160 g/m2 5.0-0.25 ≤ -15 ≥ 85 600/500±100 50/50±25 180/180±50 сap sheet membrane coarse-grained slate polymer film

uniflEks Ekp 8/10/12х1 polyester, 160 g/m2 4.7-0.235 ≤ -20 ≥ 95 700/500 ±100 50/50±25 180/180±30 сap sheet membrane coarse-grained slate polymer film

uniflEks Ekp 5.0 8/10/12х1 polyester, 180 g/m2 5.0-0.25 ≤ -20 ≥ 95 800/600±100 50/50±25 180/180±30 сap sheet membrane coarse-grained slate polymer film

APP modified bitumen roofing and waterproofing membrane.

ECoflEks V 2.0 15/16х1 glass-fiber mat, 55 g/m2 2.0±0.2 ≤ 0 ≥ 100 400/300 ±150 4/4 ±2 50/50 ±10 underlay membrane polymer film polymer film

ECoflEks pV 4.5 kg mineral 8/10/12х1 polyester, 140 g/m2 4.5±0.2 ≤ 0 ≥ 100 600/450 ±150 35/35 ±10 180/180 ±50 сap sheet membrane coarse-grained slate polymer film

ECoflEks V 4.5 kg mineral 8/10/12х1 glass-fiber mat, 55 g/m2 4.5±0.2 ≤ 0 ≥ 100 400/300 ±150 4/4 ±2 50/50 ±10 сap sheet membrane coarse-grained slate polymer film


miDa tropik p40m 10х1 polyester - ≤ -5 ≥ 110 600/400±100 30/30±10 - сap sheet membrane coarse-grained slate polymer film

prima plast nEW V 3.0 15/16х1 glass-fiber mat 3.0±5% ≤ -5 ≥ 120 450/350 ±150 5/5 ±2 - underlay membrane polymer film polymer film

prima plast gV 4.0 10x1 glass-fiber mat 4.0±5% ≤ 0 ≥ 130 400/300 ±150 6/6 ±4 50/50 ±10 underlay membrane fine-grained sand polymer film

miDa tropik C 2000 15х1 glass-fiber mat - ≤ -5 ≥ 110 300/200±100 6/6±4 - underlay membrane polymer film polymer film

prima plast pV 4.5 kg mineral 8/10х1 polyester 4.0-0.20 ≤ 0 ≥ 130 600/400 ±150 30/30±10 - сap sheet membrane coarse-grained slate polymer film

35


TechnoNICOL

properties length / width

reinforcement type and weight Weight flexibility at low

temperatureflow resistance at

elevated temperature

maximum tensile force longitudinal

/ transverse

Elongationlongitudinal / transverse

resistance to tearing

longitudinal / transverse

application area top protective surface

Bottom protective surface

Units of measurement m kg/m2 °С °С N/50 mm % N

SBS modified bitumen roofing and waterproofing membrane.

BikroElast hpp 15/16x1 glass-fiber mat, 55 g/m2 3.0-0.15 ≤ -10 ≥ 85 400/250 ±100 2.2/2.2 ±0.22 50/50 ±10 underlay membrane polymer film polymer film

Bipol hpp 15/16х1 glass-fiber mat, 55 g/m2 3.0-0.15 ≤ -15 ≥ 85 400/250 ±100 2.2/2.2 ±0.22 50/50 ±10 underlay membrane polymer film polymer film

BikroElast hmp 15/16x1 glass-fiber mat, 55 g/m2 3.0-0.15 ≤ -10 ≥ 85 400/250 ±100 2.2/2.2 ±0.22 50/50 ±10 underlay membrane fine-grained sand polymer film

BikroElast Epp 15/16x1 polyester, 150 g/m2 3.0-0.15 ≤ -10 ≥ 85 600/500 ±100 50/50±25 180/180±50 underlay membrane polymer film polymer film

BikroElast Epp 4.0 8/10х1 polyester, 150 g/m2 4.0-0.2 ≤ -10 ≥ 85 600/500 ±100 50/50±25 180/180±50 underlay membrane polymer film polymer film

uniflEks Epp 8/10х1 polyester, 160 g/m2 3.7-0.185 ≤ -20 ≥ 95 700/500 ±100 50/50±25 180/180±30 underlay membrane polymer film polymer film

miDa stanDarD pV s4 8/10х1 polyester - ≤ -10 ≥ 85 600/500 ±100 50/50±20 200/200 ±100 underlay membrane fine-grained sand or polymer film polymer film

yam 2000 10/20х1 glass-fiber mat, 55 g/m2 2.0-0.1 ≤ -15 ≥ 85 300/300 ±50 2.2/2.2 ±0.22 30/30±10 underlay membrane fine-grained sand fine-grained sand

Bipol stanDart hkp 8/10/12х1 glass-fiber mat, 55 g/m2 4.5-0.225 ≤ -15 ≥ 85 400/250 ±100 2.2/2.2 ±0.22 50/50 ±10 сap sheet membrane coarse-grained slate polymer film

Bipol stanDart Ekp 8/10x1 polyester, 160 g/m2 4.5-0.225 ≤ -15 ≥ 85 600/500±100 50/50±25 180/180±50 сap sheet membrane coarse-grained slate polymer film

Bipol Xl Ekp 8/10х1 polyester, 160 g/m2 5.0-0.25 ≤ -15 ≥ 85 600/500±100 50/50±25 180/180±50 сap sheet membrane coarse-grained slate polymer film

uniflEks Ekp 8/10/12х1 polyester, 160 g/m2 4.7-0.235 ≤ -20 ≥ 95 700/500 ±100 50/50±25 180/180±30 сap sheet membrane coarse-grained slate polymer film

uniflEks Ekp 5.0 8/10/12х1 polyester, 180 g/m2 5.0-0.25 ≤ -20 ≥ 95 800/600±100 50/50±25 180/180±30 сap sheet membrane coarse-grained slate polymer film

APP modified bitumen roofing and waterproofing membrane.


ECoflEks pV 4.5 kg mineral 8/10/12х1 polyester, 140 g/m2 4.5±0.2 ≤ 0 ≥ 100 600/450 ±150 35/35 ±10 180/180 ±50 сap sheet membrane coarse-grained slate polymer film

ECoflEks V 4.5 kg mineral 8/10/12х1 glass-fiber mat, 55 g/m2 4.5±0.2 ≤ 0 ≥ 100 400/300 ±150 4/4 ±2 50/50 ±10 сap sheet membrane coarse-grained slate polymer film


miDa tropik p40m 10х1 polyester - ≤ -5 ≥ 110 600/400±100 30/30±10 - сap sheet membrane coarse-grained slate polymer film

prima plast nEW V 3.0 15/16х1 glass-fiber mat 3.0±5% ≤ -5 ≥ 120 450/350 ±150 5/5 ±2 - underlay membrane polymer film polymer film

prima plast gV 4.0 10x1 glass-fiber mat 4.0±5% ≤ 0 ≥ 130 400/300 ±150 6/6 ±4 50/50 ±10 underlay membrane fine-grained sand polymer film

miDa tropik C 2000 15х1 glass-fiber mat - ≤ -5 ≥ 110 300/200±100 6/6±4 - underlay membrane polymer film polymer film

prima plast pV 4.5 kg mineral 8/10х1 polyester 4.0-0.20 ≤ 0 ≥ 130 600/400 ±150 30/30±10 - сap sheet membrane coarse-grained slate polymer film

content - nordroofsnordroofs.ie/data/product/33/nord-roofs-products-pdf.pdfmarket. russia belarus...

Documents