Download - Lectures part 2 Methods for cure monitoring Manufacturing methods for composites MSK 20120213
Lectures part 2
Methods for cure monitoringManufacturing methods for
composites
MSK 20120213
2
Characterisation methods for the crosslinking in thermosets
1. Physical methods2. Thermal methods
3. Spectroscopic methods
MSK 20120213
3
Cure monitoring in composites
• The crosslinking of thermoset resins is a fundamental process in the manufacturing of composites
• This curing process must be done in a controlled manner in order to achieve good quality
• It is necessary to follow and check the the cross-linking reaction during and after the cure of the composite
• Important both in production and in R&D work
MSK 20120213
4
Methods to measure the degree of cure in composites
1. Techniques based on changes in physical properties: hardness, dielectric constant, viscosity
2. Techniques based on changes in chemical properties: reaction heat, chemical structure
MSK 20120213
5
Physical methods
1. Barcol hardness2. Gel time
3. Cure meters4. Rheology
MSK 20120213
6
Barcol hardness• Measurement of the surface
hardness by pressing a needle into the laminate surface
• Easy and fast method for quality control in production
• 10-20 measurements needed per laminate for statistically reproductive results
• Glas fibers near surface can disturb the measurement
MSK 20120213
7
Geltime measurement
• Mixing of curing resin in a beaker, time for gelling is detected by a stopwatch
• Most common method to characterise gel time by producers and end-users
• Simple and fast method, which can be used by any-one
• Subjective method• Must be done under standard
conditions
MSK 20120213
8
Thermal Scanning Rheometer
Gel-time detection by a oscillating probe
MSK 20120213
9
Rheological characterisation of the curing
• Most accurate characterisation of the curing process is obtained by studying the rheological properties
• Expensive instruments and skilled operators needed
Bohlin CVO rheometerMSK 20120213
10
Rheological methods1. Steady shearing flow properties
• only in liquid phase• data before the gel point can be detected• can give too long gel times due to shear thinning
near the gel point
2. Dynamic shearing flow properties• oscillatory shearing flow• both in liquid,rubbery and glassy states• data after the gel point can be detected• Storage modulus G’ and loss modulus G’’ are
measured• At the gel point is G’ = G’’ (tan = 1)
MSK 20120213
11
Harts 2
2
43
1 56
Steady shearing flowShear rate 1.17 s-1, 80 ºC, 2 wt-% BPO
Bohlin VOR, Cone & plate D = 30 mm, 5 º, 150 µm distance
Gel time 370 s, 6.2 min
Gel time 0/t -> 00 = viscosity at the start
t = viscosity at the time tMSK 20120213
12
Oscillatory shearing flow1 Hz, 80 ºC, 2 wt-% BPO
Harts 2
Gel time 350 s (5.8 min)
Bohlin VOR, Cone & plate D = 30 mm, 5 º, 150 µm distance
MSK 20120213
13
Thermal methods
Differential scanning calorimetry
MSK 20120213
14
DSC• The exothermal heat H which is liberated in the
crosslinking reaction is detected by DSC• Results depends on:
• Heating rate (10 ºC/min)• Sample preparation• Sampling (10 - 15 mg)• Atmosphere (nitrogen most common)• Thermal history
• Commonly used for quality control of laminates
MSK 20120213
MSK 2012021315
Differential scanning calorimetry (DSC)
Perkin-Elmer DSC 7
MSK 2012021316
DSC Principle
MSK 2012021317
The glass transition temperature can be detected from the DSC scan after a dynamic or isothermal scan
Glass transition temperature
Unsaturated polyesters have Tg’s at 50 - 70 ºC
18
Isothermal DSC scan
• A liquid thermoset is cured in the DSC, at the curing temperature
• Gives the total exothermal heat when assuming that all functional groups will react
MSK 20120213
19
Residual reactivity
• A cured thermoset sample is analysed in the DSC
• Any unreacted components will react during the scan, which can be detected as an exothermal heat
MSK 20120213
20
Degree of cureThe degree of cure t can be calculated from the isothermal scan and the residual reactivity scan:
(1) Htot = Hiso
(2) t = Ht / Htot
MSK 20120213
21
Spectroscopic methods
Raman spectroscopy
MSK 20120213
22
Benefits with Raman spectroscopy
• Well resolved spectra: simple calibration methods can be used
• No sample preparation: can be easily adapted to on-line measurements
• Weak water spectrum: works well with aqueous samples
• NIR and visible wavelengths: low-cost fibre optics can be used
MSK 20120213
23
Process Raman spectrometer
MSK 20120213
24
Spectral changes in a unsaturated polyester after crosslinking
ENDUR M 105 TB• Curing time 0.1 and 2 h• Sample thickness 0.5 cm• Measurement time 1 s• Laser effect 150 mW
1300140015001600170018001900-1000
0
1000
2000
3000
4000
5000
6000
7000
C=O
C=CArom. ring
CH(olef.)
CH(alif.)
RAMAN SHIFT (cm-1)
RA
MA
N I
NT
EN
SIT
Y
MSK 20120213
MSK 2007-11-30 25
The crosslinking reaction can be monitored
ENDUR M 105TB• 2 wt-% MEKP• Gel time 20 min, 23oC• Sample thickness 0.5 cm• Postcuring 50oC, 24h
10-1
100
101
102
103
104
-0.2
0
0.2
0.4
0.6
0.8
1
CURING TIME (h)
PE
AK
RA
TIO
(R
1620
/ R
1600
)
50oC, 24h
Gel time
100% cure
MSK 20120213
MSK 2007-11-30 26
Postcuring effects can be detected
ENDUR M 105TB• Curing time 30 h and 350 h• Postcuring 24h, 50oC• Measurement time10 s• Laser effect 150 mW
13001400150016001700180019000
0.5
1
1.5
2
2.5
3x 10
4
RAMAN SHIFT (cm-1)
RA
MA
N I
NTE
NS
ITY
C=OC=C
Arom. ring
CH(alif.)
MSK 20120213
27
Laminates can also be analysed
M 105 TB and glass fiber
• The glass gives its own background
• Longer measurement time
200400600800100012001400160018002000-0.5
0
0.5
1
1.5
2
2.5
3
3.5
4x 10
4
RAMAN SHIFT (cm-1)
RA
MA
N I
NT
EN
SIT
Y
HARTSI
HARTSI(50%) + LASIKUITU(50%)
MSK 20120213
28
Gel coats
MAXGUARD, clear gel coat• 0.5 mm thickness• Measurement time 1 s, 30
s
10-1
100
101
102
103
104
-0.2
0
0.2
0.4
0.6
0.8
1
CURING TIME (h)
PE
AK
RA
TIO
(R
1620
/ R
1600
)
+ 24h, 50oC
100% cure
MSK 20120213
The fibre-resin interaction
Surface treatmentFibre impregnation
MSK 20120213
Fibre – resin impregnation
• A efficient and fast impregnation of the reinforcement by the resin is essential in all composite processing
• Can be achieved mechanically by rolling or by the use of external pressure
• Heating helps the impregnation• The impregnation is highly depending on the
resin and the reinforcement characteristics
MSK 20120213
Effect of constituents on impregnation
Resin• Low viscosity enhances
resin flow• Fillers and additives can
enhance impregnation or make it more difficult
Reinforcement• Fibre surface treatment
enhances impregnation• A yarn with high twist is
more difficult to impregnate• Fabrics structure, a more
dense structure will make impregnation more difficult
• Flow layers will enhance impregnation
MSK 20120213
The reinforcement impregnation occurs during the processing of the composite
MSK 20120213
Manufacturing methods for composites
MSK 20120213
Different manufacturing methods
Open methods• Hand lay-up• Spraying• Filament
winding• Compression
moulding• Pultrusion
Closed methods• Resin transfer
moulding• Vacuum bag
infusion• Vacuum infusion
with flexible tooling
• Vacuum infusion with rigid tooling
• Autoclave processing
MSK 20120213
A mould is needed for the making of the composite product
MSK 20120213
Prepreg• Preimpregnated fabrics:
– A fabric is preimpregnated with the resin, and cuit into desired size
– The prepreg is then processed by compression moulding, pultrusion or filmanet winding
– Both thermoset prepregs and thermoplastic prepregs (GMT) are available
MSK 20120213
Processing methods
• Fiber impregnation by mechanical action– Hand lay up– Spray lay up– Filament winding
• Fiber impregnation by external pressure– RTM– Vacuum infusion– Autoclave, rubber bladder processing– Compression moulding (SMC and BMC)
MSK 20120213
Hand lay up
MSK 2007-11-30 38MSK 20120213
Mechanical impregnation of fibers
Hand lay up
MSK 20120213
Reinforcement placement in mold
• Pre-cutting to desired shape
• Preforming by heat and pressure
• Core material and inserts can be attached
MSK 20120213
Preformed glass fiber is oftem prepared in advantage with the desired shape
MSK 20120213
Spray up lamination
CHOPPED ROVING + RESIN
SPRAYED LAYER
RESIN
MSK 20120213
Equipment for spray up lamination
• Resin - peroxide mixing in spray
• Roving chopper• 108 bar output
pressure• Resin heating
possible• 200 l resin drums
MSK 20120213
44
Filament winding
• Winding of impregnated reinforcement yarns onto a rotating mold (mandrel)
• A precise, highly efficient and automated process
• Only for closed geometries which can rotate such as pipes, pressure vessels
• Fiber volume fractions can be varied in a laminate
MSK 20120213
45
Filament winding - process principle
4 degrees of freedom
Mandrel
MSK 20120213
46
Filament winding
Polar winding pattern
MSK 20120213
47
Filament winding
MSK 20120213
Resin impregnation - dip through
MSK 20120213
Resin impregnation – drum type
MSK 20120213
Resin impregnation – closed type
MSK 20120213
51
Mandrel removal after winding
Removable mandrel1. Treatment with release agent2. Release tape winding3. Water-soluble sand and salt mandrels4. Melting metal alloy mandrels5. Casted plaster mandrels
Integrated mandrel6. Termoplastic liner mandrel7. Metal liner mandrel
MSK 20120213
52
Filament winding - product examples
Liner for smoke chimney6 m diameter
25 min production time
Wind mill blade8 m x 38 m
Speeds up to 1 m/s100 kg/hMSK 20120213
MSK 20120213
Pressure vessels• Filament winding• Carbon fibers and
epoxy• Much lower weight
than metal• Not sensitive for
corrosive environments
• Better work safety and comfort
Fiber impregnation by external pressure
• Autoclave processing – fibre compaction under very high pressure in a chamber, commonly used for pre pregs
• Resin transfer moulding – fibre impregnation and compaction by a pressurised mould
• Vacuum infusion – fibre impregnation and compaction by external pressure (surrounding air)
MSK 20120213
Autoclave processingUsed for consolidisation of prepregs by
high pressure and curing by heating
MSK 2007-11-30 55MSK 20120213
MSK 20120213
Aircraft• Epoxy resins• Carbon, aramid
and glass fibers• Honey comb core
sandwich (Al)• Prepreg lay up
with autoclave cure
• Wings, control surfaces, hatches, covers, floors
JAS Gripen
SAAB 2000
Rubber bladder consolidation
MSK 2007-11-30 57MSK 20120213
RTM - Resin transfer molding
• Resin injection into a closed mold, containing the reinforcement, with the aid of pressure
• Rigid, metal molds are used• Mold can be heated if necessary• Large, complex and highly integrated
components can be produced• Low investment and mold costs• Good work environment• Medium length to long length series
MSK 20120213
RTM principle
Insertion of preformed
reinforcement
Resin injection by external pressure
Product demoulding
Curing under pressureHeating possible for resin curing
MSK 20120213
RTM automated process
MSK 20120213
MSK 20120213
Bicycle fram manufacture by bladder moulding process
MSK 2007-11-30 62MSK 20120213
Vacuum infusion molding• Resin injection into a closed mold,
containing the reinforcement, with the aid of vacuum
• Processing at room temperature• Higher external pressure seals the mold• As upper mold can either a vacuum bag
or a rigid shell be used• Lower investment cost• Only one high quality surface is obtained
MSK 20120213