PRODUCT BULLETIN
Maxxam™ HST Polypropylene FormulationsEnhanced Polypropylene Materials For Automotive Lightweighting
The Maxxam™ HST line of filled polypropylene
(PP) materials provide 15–25 percent
greater strength at equivalent glass loading
of traditional glass-filled (GF) PP using
proprietary chemical coupling technology.
These materials offer exceptional levels of
stiffness and heat deflection performance
compared to GF PP. Maxxam materials are
designed for injection molded structural parts
with demanding mechanical and thermal
property requirements, and can serve as an
integral lightweighting solution.
Maxxam HST material enables multiple
lightweighting approaches:
• Replace heavier engineered GF resins,
such as nylon
• Redesign traditional GF PP parts
with thinner walls
KEY CHARACTERISTICS
• Chemically coupled
• Exceptional dimensional stability
• High flow grades
MARKETS AND APPLICATIONS
These high-performance PP formulations are
lighter weight solutions for automotive parts
typically manufactured with long glass fiber
PP. Highlights of Maxxam HST include:
• Provides lightweight solution in structural
applications
• Solves distortion and warpage issues
in instrumental panel carriers
• Resists deformation up to approximately
150°C in under-the-hood applications
• Allows for higher regrind usage while
maintaining property integrity
0
2000
4000
6000
8000
6500 6500 65006300
MP
a
Flexural Modulus (MPa)
MaxxamHST 5430
30% GFNylon 6/6*
*Conditioned at 50% relative humidity
30% LGF PP
30% GF PC/ABS
Stiffness comparison of Maxxam HST to 30% GF engineering polymers
www.polyone.com
Copyright © 2019, PolyOne Corporation. PolyOne makes no representations, guarantees, or warranties of any kind with respect to the information contained in this document about its
accuracy, suitability for particular applications, or the results obtained or obtainable using the information. Some of the information arises from laboratory work with small-scale equipment
which may not provide a reliable indication of performance or properties obtained or obtainable on larger-scale equipment. Values reported as “typical” or stated without a range do not
state minimum or maximum properties; consult your sales representative for property ranges and min/max specifications. Processing conditions can cause material properties to shift
from the values stated in the information. PolyOne makes no warranties or guarantees respecting suitability of either PolyOne’s products or the information for your process or end-use
application. You have the responsibility to conduct full-scale end-product performance testing to determine suitability in your application, and you assume all risk and liability arising from
your use of the information and/or use or handling of any product. POLYONE MAKES NO WARRANTIES, EXPRESS OR IMPLIED, INCLUDING, BUT NOT LIMITED TO, IMPLIED WARRANTIES
OF MERCHANTABILITY AND FITNESS FOR A PARTICULAR PURPOSE, either with respect to the information or products reflected by the information. This literature shall NOT operate as
permission, recommendation, or inducement to practice any patented invention without permission of the patent owner.
PROPERTY CONDITION UNITS TEST METHOD 5430 5435 5440 5450
Reinforcement % - % - 30 35 40 50
Specific Gravity 73°F (23°C) - ISO 1183 1.13 1.18 1.23 1.35
Tensile Strength Yield MPa ISO 527 102 105 113 130
Flexural Modulus 73°F (23°C) MPa ISO 178 6,500 8,000 9,400 11,500
Notched Charpy 73°F (23°C) kJ/m2 ISO 179 9.4 9.3 11.0 12.0
Heat Deflection 264 psi °C ISO 75 152 152 153 154