metallized chemical coated high barrier film...
TRANSCRIPT
KEY FEATURES - SPARSHPET-MH-CCHIB is Bi-axially Oriented Vacuum high barrier Metallized �lm. Metalize on chemical coated surface wound inside other side corona It has excellent barrier properties, enhanced high bond strength between metal to �lm, excellent machinability and high gloss. APPLICATIONS - Suitable for �exible packaging application like coffee, milk powder, ORS, cereals, juice, powder, snacks food, Tea etc.
Disclaimer: The data sheet information is to the best of our knowledge and experience. Some values may be customized wherever possible, as per the customer's requirement. Sparsh Industries Pvt Ltd makes no warranty, whatsoever, to the product fitness for any specific use. Data sheet is purely for reader's consideration and verification for sale or contract.
Metal surface
Plain surface
METALLIZED CHEMICAL COATED HIGH BARRIER FILM (MH-CCHIB)
TECHNICAL DATA SHEET
Proper�es Unit Test Method Typical Values
General
Thickness
Yield
Micron Sparsh Method
Sparsh Method 89.3
Op�cal
Op�cal Density (Tolerance +/ -5%) Internal
Mechanical
Tensile Strength(Min)
Elonga�on
MD
TD
MD
TD%
2000
1900
Surface
Surface Tension(Min) Dyne/cm
56 56 56
Thermal
%MD
TDShrinkage
@ 150⁰
C/30’
2.0±0.5 2.0±0.5 2.0±0.5
0.2±0.2 0.2±0.2 0.2±0.2
Barrier
MVTR (38 ⁰C/ 90% RH)
Oxygen Permeability (25 ⁰C/ 0 % RH)
Optical density can be customized from 2.6 to 3.0 as per requirement
<0.80
<0.60
90 ±10
100 ±10
2.5-2.8
59.5
12 ±0.3
<0.80
<0.60
90 ±10
100 ±10
71.4
2.5-2.8
10 ±0.2
<0.80
<0.60
90 ±10
100 ±10
2.5-2.8
8±0.2
ASTM D 3985 -95
ASTM F -1249
ASTM-D 1204
ASTM-D 2578
ASTM-D 882
ASTM-D 882
cc/m2/day
g/m2/day
Metallize side
Kg/cm2
M2/Kg
Sparsh Industries Private Limited
Factory:G-12 to G-20, UPSIDC, Jainpur Industrial Area,Kanpur Dehat, 209311, Uttar Pradesh, India
Registered OfficeSparsh House, 165, Patparganj Industrial Area, Delhi-110092, INDIA
Tel: Fax: Email: Web:
+91 11 42655646/4747+91 11 [email protected] URS is a member of Registrar of Standards (Holidings) Ltd.
2000 2000
1900 1900