![Page 1: Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB ... · Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB Amorphous Si films were deposited on SiO 2 (~200 nm)/Si substrate](https://reader034.vdocument.in/reader034/viewer/2022042612/5f4d392bf28208677a5d401c/html5/thumbnails/1.jpg)
Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB
Amorphous Si films were deposited on SiO2 (~200 nm)/Si substrate using Advanced Vacuum PECVD2 tool
wafer# Pressure
(mT) HF Power
(W)
Gas Flow-rate (sccm) Chuck Temperature (oC)
Film Deposition Rate (nm/min)
Stress (~200nm film thickness) SiH4 (2% in He) N2
1 600 30 1500 0 300 6.65 -945
2 600 100 1600 0 300 12.8 -1265
3* 800 30 1500 500 300 6.15 -465
4 600 30 1600 0 200 7.05 -1271
5 600 15 1600 0 300 5.6 -850
6 700 30 1800 0 300 5.49 -1245
*: The stress is lower because there is a SiNx component in the film (see the elliposmetry data, optical constants spectra, below).
![Page 2: Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB ... · Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB Amorphous Si films were deposited on SiO 2 (~200 nm)/Si substrate](https://reader034.vdocument.in/reader034/viewer/2022042612/5f4d392bf28208677a5d401c/html5/thumbnails/2.jpg)
Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB 1)a-Si#2: 600mT, 100W (HF), SiH4(2% in He) flow-rate=1600sccm, chuck temperature=300oC, and deposition time=20 minutes.
![Page 3: Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB ... · Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB Amorphous Si films were deposited on SiO 2 (~200 nm)/Si substrate](https://reader034.vdocument.in/reader034/viewer/2022042612/5f4d392bf28208677a5d401c/html5/thumbnails/3.jpg)
Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB
![Page 4: Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB ... · Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB Amorphous Si films were deposited on SiO 2 (~200 nm)/Si substrate](https://reader034.vdocument.in/reader034/viewer/2022042612/5f4d392bf28208677a5d401c/html5/thumbnails/4.jpg)
Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB 2) aSi#3: 800mT, 30W (HF), SiH4(2% in He)/N2 flow-rate=1500/500sccm, chuck temperature=300oC, and deposition time=20 minutes.
![Page 5: Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB ... · Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB Amorphous Si films were deposited on SiO 2 (~200 nm)/Si substrate](https://reader034.vdocument.in/reader034/viewer/2022042612/5f4d392bf28208677a5d401c/html5/thumbnails/5.jpg)
Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB
![Page 6: Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB ... · Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB Amorphous Si films were deposited on SiO 2 (~200 nm)/Si substrate](https://reader034.vdocument.in/reader034/viewer/2022042612/5f4d392bf28208677a5d401c/html5/thumbnails/6.jpg)
Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB 3)a-Si#4: 600mT, 30W (HF), SiH4(2% in He) flow-rate=1600 sccm, chuck temperature=200oC, and deposition time=20 minutes.
![Page 7: Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB ... · Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB Amorphous Si films were deposited on SiO 2 (~200 nm)/Si substrate](https://reader034.vdocument.in/reader034/viewer/2022042612/5f4d392bf28208677a5d401c/html5/thumbnails/7.jpg)
Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB
![Page 8: Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB ... · Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB Amorphous Si films were deposited on SiO 2 (~200 nm)/Si substrate](https://reader034.vdocument.in/reader034/viewer/2022042612/5f4d392bf28208677a5d401c/html5/thumbnails/8.jpg)
Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB 4)a-Si#5: 600mT, 15W (HF), SiH4(2% in He) flow-rate=1600 sccm, chuck temperature=300oC, and deposition time=20 minutes.
![Page 9: Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB ... · Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB Amorphous Si films were deposited on SiO 2 (~200 nm)/Si substrate](https://reader034.vdocument.in/reader034/viewer/2022042612/5f4d392bf28208677a5d401c/html5/thumbnails/9.jpg)
Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB
![Page 10: Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB ... · Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB Amorphous Si films were deposited on SiO 2 (~200 nm)/Si substrate](https://reader034.vdocument.in/reader034/viewer/2022042612/5f4d392bf28208677a5d401c/html5/thumbnails/10.jpg)
Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB 5)a-Si#2: 700mT, 30W (HF), SiH4(2% in He) flow-rate=1800sccm, chuck temperature=300oC, and deposition time=20 minutes.
![Page 11: Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB ... · Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB Amorphous Si films were deposited on SiO 2 (~200 nm)/Si substrate](https://reader034.vdocument.in/reader034/viewer/2022042612/5f4d392bf28208677a5d401c/html5/thumbnails/11.jpg)
Ning Cao, Staff Engineer, nano-fabrication Lab, UCSB