polychem products gshs 1625polychemproducts.co.in/product catalogue.pdfgshs 1625 flexible,...
TRANSCRIPT
GSHS 1625
FLEXIBLE, FLAME-RETARDANTPOLYOLEFIN
600V, 125OC, 2:1
Polychem Products
GSHS-1625 is a flexible, flame-retardant heat –shrinkable polyolefin tube. It is designed for
a vide range of application including insulation for electric & electronic devices, wire strain
relief and protective covering for parts such as resistors and capacitors.
Applications
Shrink Ratio : 50% or more in the radial direction
7% in the axial direction
Continuous operation temperature :-55oC to 125
oC
Flammability : UL VW-1, CSA OFT, -F-MARK
Excellent electrical properties.
High resistance to chemicals and oils.
Features
SPECIFICATION VALUES
STANDARDS
UL 224 (File No.:E84393) CSA C22.2 (File No.: LR55659)
PassVW-1Flammability
No sign of degradation158oC/168 hrsCopper Stability
No corrosion158oC/168 hrsCopper corrosion
Chemical
Min. 10 14
Q – cm -Volume resistivity
Min.2.5kV/1 Minute-Dielectric strength
Electrical
Physical
Max. 17.64kgf/mm2-Secant modulus
No cracks158oC/168 hrsFlexibility
No crack-30oC/1 hrCold bend
No crack136oC/1 hrHeat shock
Max. 50%125oC/1 hrDeformation
Unaged
AgedMin. 70% of the Value
of unaged specimens
Min. 100%
158oC/168 hrs
Tensile Strength
Elongation
Min. 1.06kgf/mm2
Min 200%
ASTM D 638Tensile strength
Elongation
VALUE TEST METHODPROPERTY
GSHS-1625
FLEXIBLE, FLAME-RETARDANT
POLYOLEFIN600V, 125
OC, 2:1
Product Dimensions
Due to contiuous development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than specified if recovery
is restricted during shrinkage.Other lengths and sizes are available subject to special order.
D d
T
Ordering Information
Standard colors : Black, White, Yellow, Red, Blue, Green, Gray, orange,Brown & Violet , Clear (Non flame-
retardant).
Size selection : Always order the largest size that will shrink snugly over the component to be covered.
Standard package : On spools.
Ordering description : Specify product name, size, and color [for example, GSHS-1625-0.25Tx6mm-BK]
200
200
200
200
200
200
100
100
100
100
100
100
100
100
50
50
50
50
50
50
50
50
50
50
50
50
50
31
0.356
0.432
0.432
0.4.32
0.432
0.432
0.559
0.559
0.559
0.559
0.599
0.559
0.559
0.559
0.686
0.686
0.686
0.686
0.762
0.762
0.762
0.762
0.864
0.864
0.864
0.864
0.864
0.864
0.75
1.00
1.25
1.50
1.75
2.00
2.50
3.00
3.50
4.00
4.5
5.00
5.50
6.00
6.50
7.00
7.50
8.00
9.00
10.00
11.00
12.00
12.50
13.00
14.00
15.00
16.00
19.00
1.9
2.3
2.8
3.3
3.8
4.3
5.3
6.3
7.6
8.6
9.6
10.6
11.6
12.6
13.6
14.6
15.6
16.9
18.9
20.9
22.9
24.9
26.2
27.2
29.2
31.2
33.2
39.0
(METRIC SIZE)
0.20 T X 1.5
0.25 T X 2.0
0.25 T X 2.5
0.25 T X 3.0
0.25 T X 3.5
0.25 T X 4.0
0.25 T X 5.0
0.25 T X 6.0
0.25 T X 7.0
0.25 T X 8.0
0.25 T X 9.0
0.25 T X 10.0
0.25 T X 11.0
0.25 T X 12.0
0.30 T X 13.0
0.30 T X 14.0
0.30 T X 15.0
0.30 T X 16.0
0.35 T X 18.0
0.35 T X 20.0
0.40 T X 22.0
0.40 T X 24.0
0.40 T X 25.0
0.40 T X 26.0
0.40 T X 28.0
0.40 T X 30.0
0.40 T X 32.0
0.43 T X 38.0
STANDARD
LENGTH
(M)
T(Min.) Wall thickness
of Recovered after
heating (mm)
d(Max.) Inside
Diameter of Recovered
after heating (mm)
D(Nom.) Inside
Diameter of expanded
as supplied (mm)
SIZE
Polychem Products
Expanded as suppliedFully recovered after heating
Min.shrink temperature : 100 oC
GSHS 1635 F
FLEXIBLE, FLAME-RETARDANT
POLYOLEFIN
600V, 135OC, 2:1
GSHS-1635F is a flexible, flame-retardant heat –shrinkable polyolefin tube. It is designed for a vide range of applications requiring highly heat – resistance, including insulation for
electric & electronic devices, wire strain relief and protective covering for parts such as resistors and capacitors.
Applications
Shrink Ratio : 50% or more in the radial direction
7% in the axial direction
Continuous operation temperature :-55oC to 135
oC
Flammability : UL VW-1, CSA OFT, -F-MARK
Excellent electrical properties.
High resistance to chemicals and oils.
Features
SPECIFICATION VALUES
STANDARD
UL 224 (File No.:E84393) CSA C22.2 (File No.: LR55659) MIL -I-23053/5 Class 1 Type
PassVW-1Flammability
No sign of degradation158oC/168 hrsCopper Stability
No corrosion158oC/168 hrsCopper corrosion
Chemical
Min. 10 14
Q – cm -Volume resistivity
Min.2.5kV/1 Minute-Dielectric strength
Electrical
Physical
Max. 17.64kgf/mm2
-Secant modulus
No cracks158oC/168 hrsFlexibility
No crack-55oC/4 hrsCold bend
No crack250oC/4 hrsHeat shock
Max. 50%158oC/1 hrDeformation
Unaged
Aged Min. 75% of the Value of
unaged specimens
Min. 100%
158oC/168 hrs
Tensile Strength
Elongation
Min. 1.06kgf/mm2
Min 200%
ASTM D 638Tensile strength
Elongation
VALUE TEST METHODPROPERTY
Polychem Products
GSHS-1635F
FLEXIBLE, FLAME-
RETARDANT POLYOLEFIN600V, 135
OC, 2:1
Product Dimensions
Due to contiuous development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than specified if recovery
is restricted during shrinkage.Other lengths and sizes are available subject to special order.
D d
t
Ordering Information
Standard colors : Black[BK],white[WT],yellow[YL],red[RD],blue[BL],green[GN],gray[GY],brown[BN].
Size selection : Always order the largest size that will shrink snugly over the component to be covered.
Standard package : On spools.
Ordering description : Specify product name, size, and color [for example, GSHS 1635F – 0.20 T X 1.5mm BK]
200
200
200
200
200
200
100
100
100
100
100
100
100
100
50
50
50
50
50
50
50
50
50
50
50
50
50
31
0. 356
0. 432
0. 432
0. 4.32
0. 432
0. 432
0. 559
0. 559
0. 559
0. 559
0. 599
0. 559
0. 559
0. 559
0. 686
0. 686
0. 686
0. 686
0. 762
0. 762
0. 762
0. 762
0. 864
0. 864
0. 864
0. 864
0. 864
0. 864
0. 75
1. 00
1. 25
1. 50
1. 75
2. 00
2. 50
3. 00
3. 50
4. 00
4. 50
5. 00
5. 50
6. 00
6. 50
7. 00
7. 50
8. 00
9. 00
10.00
11.00
12.00
12.50
13.00
14.00
15.00
16.00
19.00
1. 9
2. 3
2. 8
3. 3
3. 8
4. 3
5. 3
6. 3
7. 6
8. 6
9. 6
10. 6
11. 6
12. 6
13. 6
14. 6
15. 6
16. 9
18. 9
20. 9
22. 9
24. 9
26. 2
27. 2
29. 2
31. 2
33. 2
39.0
(METRIC SIZE)
0. 20 T X 1.5
0. 25 T X 2.0
0. 25 T X 2.5
0. 25 T X 3.0
0. 25 T X 3.5
0. 25 T X 4.0
0. 25 T X 5.0
0. 25 T X 6.0
0. 25 T X 7.0
0. 25 T X 8.0
0. 25 T X 9.0
0. 25 T X 10.0
0. 25 T X 11.0
0. 25 T X 12.0
0. 30 T X 13.0
0. 30 T X 14.0
0. 30 T X 15.0
0. 35 T X 16.0
0. 35 T X 18.0
0. 35 T X 20.0
0. 40 T X 22.0
0. 40 T X 24.0
0. 40 T X 25.0
0. 40 T X 26.0
0. 40 T X 28.0
0. 40 T X 30.0
0. 40 T X 32.0
0. 43 T X 38.0
STANDARD
LENGTH
(M)
t(Min.) Wall thickness
of Recovered after
heating (mm)
d(Max.) Inside
Diameter of Recovered
after heating (mm)
D(Nom.) Inside
Diameter of expanded
as supplied (mm)
SIZE
Polychem Products
Expanded as suppliedFully recovered after heating
Min.shrink temperature : 120 oC
GSHS 1675
HIGH TEMPERATURE CHEMICAL-RESISTANT PVF2
600V, 175OC, 2:1
GSHS-1675 is a rigid, flame-retardant heat –shrinkable PVF2 for applications requiring outstanding abrasion and cut-through resistance. It reliably protects wires,
solder joints, terminals, connections and components from most industrial fuels, solvents and chemicals.
Applications
Shrink Ratio : 50% or more in the radial direction
7% in the axial direction
Continuous operation temperature :-55oC to 175
oC
Flammability : UL VW-1, CSA OFT
Excellent electrical properties.
High resistance to chemicals and oils.
Features
SPECIFICATION VALUES
STANDARDS
UL 224 (File No.:E84393) MIL -I-23053/8
PassVW-1Flammability
No sign of degradation180oC/168 hrsCopper Stability
No corrosion180oC/168 hrsCopper corrosion
Chemical
Min. 10 13
Q – cm -Volume resistivity
Min.2.5kV/1 Minute-Dielectric strength
Electrical
Physical
Min. 84.4kgf/mm2-Secant modulus
No cracks180oC/168 hrsFlexibility
No crack-55oC/4 hrsCold bend
No crack300oC/1 hrHeat shock
Max. 50%150oC/1 hrDeformation
Unaged
Aged Min. 70% of the Value
of unaged specimens180oC/168 hrs
Tensile Strength
Elongation
Min. 3.52kgf/mm2
Min. 150%
ASTM D 638Tensile strength
Elongation
VALUE TEST METHODPROPERTY
Polychem Products
GSHS-1675
HIGH TEMPERATURE CHEMICAL-RESISTANT
PVF2 600V, 175OC, 2:1
Product Dimensions
Due to contiuous development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than specified if recovery
is restricted during shrinkage.Other lengths and sizes are available subject to special order.
D d
t
Ordering Information
Standard colors : CLEAR
Size selection : Always order the largest size that will shrink snugly over the component to be covered.
Standard package : On spools & IN 1.2 MTR CUT LENGTH
Ordering description : Specify product name, size, and color [for example, GSHS 1675 – 0.10 T X 3/64’’]
0.10
0.10
0.12
0.12
0.12
0.14
0.14
0.14
0.18
0.20
As supplied
(nom)
t(mm)
Wall Thickness
0.203
0.203
0.229
0.229
0.229
0.279
0.279
0.279
0.356
0.406
After recovery
(min.)
STANDARD
LENGTH
(m)
Inside Diameter
SIZE
(Diameter)
200
100
100
100
1.2
1.2
1.2
1.2
1.2
1.2
0.58
0.79
1.17
1.57
2.36
3.18
4.75
6.35
9.53
12.7
1.4
1.8
2.6
3.4
5.0
6.6
10.1
13.3
20.1
26.6
(INCH SIZE)
3/64’’
1/16’’
3/32’’
1/8’’
3/16’’
¼’’
3/8’’
½’’
¾’’
1’’
After recovery
d(max.)
as supplied
D(nom)mm
Polychem Products
Expanded as suppliedFully recovered after heating
Min.shrink temperature : 150oC
GSHS 3635
FLEXIBLE, FLAME-RETARDANTPOLYOLEFIN HIGH SHRINK RATIO
600V, 135OC, 3:1
GSHS-3635 is a flexible, High shrink ratio flame-retardant, heat-resistant, heat-shrinkable polyolefin tube. It is needed to cover large size difference like harness with installed
connectors. Also ideal for light-duty harnessing, jacketing and identification of wires, cables and electrical and electronic components.
Applications
Shrink Ratio : 67% or more in the radial direction
10% in the axial direction
Continuous operation temperature :-55oC to 135
oC
Flammability : UL VW-1, CSA OFT, -F-MARK
Excellent electrical properties.
High resistance to chemicals and oils.
Features
SPECIFICATION VALUES
PassVW-1Flammability
No sign of degradation158oC/168 hrsCopper Stability
No corrosion1580C/168 hrsCopper corrosion
Chemical
Min. 10 14
Q – cm -Volume resistivity
Min.2.5kV/1 Minute-Dielectric strength
Electrical
Physical
Max. 17.64kgf/mm2-Secant modulus
No cracks158oC/168 hrsFlexibility
No crack-55oC/4 hrsCold bend
No crack250oC/4 hrsHeat shock
Max. 50%158oC/1 hrDeformation
Unaged
AgedMin. 75% of the Value
of unaged specimens
Min. 100%
158oC/168 hrs
Tensile Strength
Elongation
Min. 1.06kgf/mm2
Min 200%
ASTM D 638Tensile strength
Elongation
VALUE TEST METHODPROPERTY
Polychem Products
GSHS-3635
FLEXIBLE, FLAME-RETARDANTPOLYOLEFIN HIGH SHRINK
RATIO 600V, 135OC, 3:1
Product Dimensions
Due to contiuous development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than specified if recovery
is restricted during shrinkage.Other lengths and sizes are available subject to special order.
D d
W
Ordering Information
Standard colors : Black (other colors are available on request).
Size selection : Always order the largest size that will shrink snugly over the component to be covered.
Standard package : On spools
Ordering description : Specify product name, size, and color [for example, GSHS 3635 –1.5mm blk]
0.23
0.26
0.27
0.28
0.28
0.41
0.45
0.50
As supplied
(nom)
Wall Thickness-W(mm)
0.40
0.50
0.59
0.68
0.68
0.77
0.90
1.04
After recovery
(min.)
STANDARD
LENGTH
(m)
Inside Diameter
SIZE
(Diameter)
200
200
100
50
50
50
50
31
0.50
1.0
2.00
3.00
4.00
6.00
8.00
13.00
1.8
3.2
6.2
9.3
12.3
18.5
25
39
(METRIC SIZE)
1.5
3
6
9
12
18
24
38
After recovery
d(max.)
as supplied
D(mm)
Polychem Products
Expanded as suppliedFully recovered after heating
Min. Shrink temperature : 120 oC
GSHS 3635W
DUAL-WALL,FLAME-RETARDANTPOLYOLEFIN HIGH SHRINK RATIO
600V, 135OC, 3:1
GSHS-3635W is designed for all general purpose applications such as the insulations and strain relief of electrical connections and termination , light duty harnessing ,
jacketing, bundling and color coding of wires. Few sizes cover a vide range of diameters, allowing reduce inventory and this tubing easily accommodate awkward,
irregular shapes.
Applications
Shrink Ratio : 67% or more in the radial direction
10% in the axial direction
Continuous operation temperature :-55oC to 135
oC
Flammability : UL VW-1, CSA OFT (Jacket Only)
Excellent electrical properties.
High resistance to chemicals and oils.
Minimum Shrink Temparature: 900 C
Features
SPECIFICATION VALUES
PassVW-1Flammability
No sign of degradation158oC/168 hrsCopper Stability
No corrosion158oC/168 hrsCopper corrosion
Chemical
Min. 10 14
Q – cm -Volume resistivity
Min.2.5kV/1 Minute-Dielectric strength
Electrical
Physical
Max. 17.64kgf/mm2
-Secant modulus
No cracks158oC/168 hrsFlexibility
No crack-55oC/4 hrsCold bend
No crack250oC/4 hrsHeat shock
Max. 50%158oC/1 hrDeformation
Unaged
AgedMin. 75% of the Value of
unaged specimens
Min. 100%
158oC/168 hrs
Tensile Strength
Elongation
Min. 1.06kgf/mm2
Min 200%
ASTM D 638Tensile strength
Elongation
VALUE TEST METHODPROPERTY
Polychem Products
GSHS-3635W
DUAL-WALL,FLAME-RETARDANTPOLYOLEFIN HIGH SHRINK
RATIO 600V, 135OC, 3:1
Product Dimensions
Due to contiuous product development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than specified if
recovery is restricted during shrinkage.Other lengths and sizes are available subject to special order.
D d
W
Ordering Information
Standard colors : Black (other colors are available on request).
Size selection : Always order the largest size that will shrink snugly over the component to be covered.
Standard package : 1.2 Mtrs in cut length
Ordering description : Specify product name, size, and color [for example, GSHS 3635W – 3.0 mm blk]
0.53
0.45
0.50
0.55
0.77
0.78
0.76
0.85
0.90
0.95
As supplied
(nom)
W(mm)
Wall Thickness
1.0
1.20
1.30
1.50
2.00
2.20
2.30
2.50
2.50
2.50
After recovery
(min.)
STANDARD
LENGTH
(m)
Inside DiameterSIZE
(Diameter)
1.2
1.2
1.2
1.2
1.2
1.2
1.2
1.2
1.2
1.2
1.00
2.00
3.00
4.00
6.00
8.00
13.0
17.0
25.0
34.0
3.2
6.2
9.6
12.6
20.0
25.0
39.0
50.0
75.0
100.0
(METRIC SIZE)
3.0
6.0
9.0
12.0
19.0
24.0
38.0
50.0
75.0
100.0
After recovery
(max.)(d)
as supplied (D)
(mm)
Polychem Products
Expanded as suppliedFully recovered after heating
Min. shrink temperature : 120oC
BUS BAR TUBING
Avoid short circuit fault caused by small animals such as mice, snakes and so on.
Prevent bus bar from chemical corrosion effected by strong acid, alkali, salt etc.
Avoid accidental injure, for instance, that overhaul person enters electric ferous clearance
by mistakes.
Be suit to the trend of smaller switch cabinets.
Be applied in bus duct for insulation among buses.
Applications
PROPERTY
Bus Bar insulation tubings can be used for both copper and aluminum bus bars
of rectangular and circular cross section
Typical Features
PASSFlame Retardance Test
> 75KV PeakPeak Voltage
42KV, 1 MinWithstand Voltage
> 2KV/mmDielectric Strength
4.3 X 10 14 Q.CMVolume Resistivity
VALUEITEM
Polychem Products
DIMENSIONS BUS BAR TUBING
1. 5 + 0.2690. 8 + 0.2150180150
1. 5 + 0.2560. 8 + 0.2120150120
1. 5 + 0.2430. 8 + 0.2100100/ 120100
1. 5 + 0.2430. 8 + 0.29010090
1. 5 + 0.2430. 8 + 0.28080/ 10080
1. 5 + 0.2320. 8 + 0.2708070
1. 3 + 0.2320. 8 + 0.2606060
1. 3 + 0.2270. 8 + 0.2505050
1. 2 + 0.2210. 8 + 0.2404040
1. 2 + 0.2150. 8 + 0.2353535
W . T W. TI. DI. D
After Recovered (mm)As Supplied ( mm)
Width of
Bus Bar
(mm)
Part No.
APPLICATION FOR 1KV
3. 5 + 0. 2801. 2 + 0. 2200Max.200
3. 5 + 0. 2611. 2 + 0. 2180Max.180
3. 5 + 0. 2611. 2 + 0. 2150200150
3. 0 + 0. 2481. 2 + 0. 2120150120
3. 0 + 0. 2401. 2 + 0. 2100120100
3. 0 + 0. 2321. 2 + 0. 28080/10080
3. 0 + 0. 2241. 2 + 0. 2608065
2. 5 + 0. 2201. 2 + 0. 2505050
2. 2 + 0. 2 151. 2 + 0. 2404040
2. 2 + 0. 2131. 0 + 0. 2303030
2. 2 + 0. 291. 0 + 0. 2202020
W . T W. TI. DI. D
After Recovered (mm)As Supplied ( mm)
Width of Bus
Bar
(mm)
Part No.
APPLICATION FOR 10 KV
Polychem Products
BUS BAR TUBING
DIMENSIONS
APPLICATION FOR 35 KV
5. 5 + 0. 3802. 8 + 0. 3200Max.200
5. 5 + 0. 3612. 8 + 0. 3180Max.180
5. 0 + 0. 3612. 5 + 0. 3150200150
5. 0 + 0. 3482. 5 + 0. 312015012
4. 5 + 0. 3402. 5 + 0. 3100120100
4. 5 + 0. 3322. 2 + 0. 38080/10080
4. 5 + 0. 3242. 2 + 0. 3608065
4. 5 + 0. 3202. 2 + 0. 3505050
4. 0 + 0. 3152. 0 + 0. 3404040
4. 0 + 0. 3132. 0 + 0. 3303030
W . T W. TI. DI. D
After Recovered (m
m)
As Supplied ( mm)
Width of
Bus Bar
(mm)
Part No.
Due to continuous productdevelopment specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than specified if recovery is restricted during shrinkage. Other lengths and sizes are available
subject to special order.
Ordering Information
Standard colors : yellow[YL], red[RD], green[GN].
Size selection : Always order the largest size that will shrink snugly over the component to be covered.
Standard package : 1 mtr in cut length
Ordering description : Specify product name, size, and color.
Polychem Products
BUS BAR TAPEPolychem Products
5 MTRSRED50 mm
5 MTRSRED25 mm
PACKING in rollCOLORSIZE
GSHS 1625LTVERY FLEXIBLE, FLAME-RETARDANT
POLYOLEFIN600V, 125
OC, 2:1
GSHS-1625LT is a very flexible, flame-retardant low temperature heat –shrinkable polyolefin tube. It is designed for a vide range of applications specially required rapid shrinking, including insulation for electric & electronic devices, wire strain
relief and protective covering for parts such as resistors and capacitors.
Applications
Shrink Ratio : 50% or more in the radial direction
7% in the axial direction
Continuous operation temperature :-55oC to 125
oC
Flammability : UL VW-1, CSA OFT, -F-MARK
Low temperature shrinking.
High resistance to chemicals and oils.
Features
SPECIFICATION VALUES
STANDARD
UL 224 (File No.:E84393) CSA C22.2 (File No.: LR55659)
PassVW-1Flammability
No sign of degradation158oC/168 hrsCopper Stability
No corrosion1580C/168 hrsCopper corrosion
Chemical
Min. 10 14
Q – cm -Volume resistivity
Min.2.5kV/1 Minute-Dielectric strength
Electrical
Physical
Max. 17.64kgf/mm2
-Secant modulus
No cracks158oC/168 hrsFlexibility
No crack-30oC/1 hrCold bend
No crack136oC/1 hrHeat shock
Max. 50%125oC/1 hrDeformation
Unaged
AgedMin. 70% of the Value
of unaged specimens
Min. 100%
158oC/168 hrs
Tensile Strength
Elongation
Min. 1.06kgf/mm2
Min 200%
ASTM D 638Tensile strength
Elongation
VALUE TEST METHODPROPERTY
Polychem Products
GSHS-1625LT
VERY FLEXIBLE, FLAME-RETARDANT
POLYOLEFIN600V, 125
OC, 2:1
Product Dimensions
Due to continuous development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than specified if recovery
is restricted during shrinkage.Other lengths and sizes are available subject to special order.
D d
T
Ordering Information
Standard colors : Black, White, Yellow, Red, Blue, Green, Gray, Brown & Violet Clear (Non-flame retardant).
Size selection : Always order the largest size that will shrink snugly over the component to be covered.
Standard package : On spools.
Ordering description : Specify product name, size, and color [for example, GSHS-1625-0.25Tx6mm-Black]
200
200
200
200
200
200
100
100
100
100
100
100
100
100
50
50
50
50
50
50
50
50
50
50
50
50
50
31
0.356
0.432
0.432
0.4.32
0.432
0.432
0.559
0.559
0.559
0.559
0.599
0.559
0.559
0.559
0.686
0.686
0.686
0.686
0.762
0.762
0.762
0.762
0.864
0.864
0.864
0.864
0.864
0.864
0.75
1.00
1.25
1.50
1.75
2.00
2.50
3.00
3.50
4.00
4.5
5.00
5.50
6.00
6.50
7.00
7.50
8.00
9.00
10.00
11.00
12.00
12.50
13.00
14.00
15.00
16.00
19.00
1.9
2.3
2.8
3.3
3.8
4.3
5.3
6.3
7.6
8.6
9.6
10.6
11.6
12.6
13.6
14.6
15.6
16.9
18.9
20.9
22.9
24.9
26.2
27.2
29.2
31.2
33.2
39.0
0(METRIC SIZE)
0.20 T X 1.5
0.25 T X 2.0
0.25 T X 2.5
0.25 T X 3.0
0.25 T X 3.5
0.25 T X 4.0
0.25 T X 5.0
0.25 T X 6.0
0.25 T X 7.0
0.25 T X 8.0
0.25 T X 9.0
0.25 T X 10.0
0.25 T X 11.0
0.25 T X 12.0
0.30 T X 13.0
0.30 T X 14.0
0.30 T X 15.0
0.30 T X 16.0
0.35 T X 18.0
0.35 T X 20.0
0.40 T X 22.0
0.40 T X 24.0
0.40 T X 25.0
0.40 T X 26.0
0.40 T X 28.0
0.40 T X 30.0
0.40 T X 32.0
0.43 T X 38.0
STANDARD
LENGTH
(M)
T(Min.) Wall thickness
of Recovered after
heating (mm)
d(Max.) Inside
Diameter of Recovered
after heating (mm)
D(Nom.) Inside
Diameter of expanded
as supplied (mm)
SIZE
Polychem Products
Expanded as suppliedFully recovered after heating
GSHS 1625THIGHLY FLEXIBLE, FLAME-RETARDANT
THIN-WALL POLYOLEFIN150V, 125
OC, 2:1
GSHS-1625T is a very flexible, flame-retardant, thin-wall heat –shrinkable polyolefin tube.
It is designed for rapid shrinking and greater packaging density including insulation for
electric & electronic devices, wire strain relief and protective covering for parts such as
resistors and capacitors.
Applications
Shrink Ratio : 50% or more in the radial direction
7% in the axial direction
Continuous operation temperature :-55oC to 125
oC
Flammability : UL VW-1, CSA OFT, -F-MARK
Excellent electrical properties.
High resistance to chemicals and oils.
Features
SPECIFICATION VALUES
STANDARD
UL 224 (File No.:E84393) CSA C22.2 (File No.: LR55659)
PassVW-1Flammability
No sign of degradation158oC/168 hrsCopper Stability
No corrosion1580C/168 hrsCopper corrosion
Chemical
Min. 10 14
Q – cm -Volume resistivity
Min.2.5kV/1 Minute-Dielectric strength
Electrical
Physical
Max. 17.64kgf/mm2
-Secant modulus
No cracks158oC/168 hrsFlexibility
No crack-30oC/1 hrCold bend
No crack136oC/1 hrHeat shock
Max. 50%125oC/1 hrDeformation
Unaged
AgedMin. 70% of the Value
of unaged specimens
Min. 100%
158oC/168 hrs
Tensile Strength
Elongation
Min. 1.06kgf/mm2
Min 200%
ASTM D 638Tensile strength
Elongation
VALUE TEST METHODPROPERTY
Polychem Products
GSHS-1625T
HIGHLY FLEXIBLE, FLAME-RETARDANT
THIN-WALL POLYOLEFIN150V, 125
OC, 2:1
Product Dimensions
Due to continuous development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than specified if recovery
is restricted during shrinkage.Other lengths and sizes are available subject to special order.
D d
W
Ordering Information
Standard colors : Black
Size selection : Always order the largest size that will shrink snugly over the component to be covered.
Standard package : On spools.
Ordering description : Specify product name, size, and color [for example, GSHS-1625T-0.10Tx1.5mm-
Black]
200
200
200
200
100
100
100
100
100
0. 180
0. 180
0. 180
0. 250
0. 250
0. 250
0. 250
0. 250
0. 250
0. 50
0. 75
1. 00
1. 25
1. 50
1. 75
2. 00
2. 50
3. 00
1. 3
1. 8
2. 3
2. 8
3. 2
3. 8
4. 5
5. 5
6. 5
(METRIC SIZE)
0.10 T X 1. 0
0.10 T X 1. 5
0.10 T X 2. 0
0.15 T X 2. 5
0.15 T X 3. 0
0.15 T X 3. 5
0.15 T X 4. 0
0.15 T X 5. 0
0.15 T X 6. 0
STANDARD
LENGTH
(M)
W(Min.) Wall thickness
Of Recovered after
heating (mm)
d(Max.) Inside
Diameter of Recovered
after heating (mm)
D(Nom.) Inside
Diameter of expanded
as supplied (mm)
SIZE
Polychem Products
Expanded as suppliedFully recovered after heating
GSHS 1625G
FLEXIBLE,NON-TOXIC,FLAME- RETARDANT POLYOLEFIN
600V, 125OC, 2:1
GSHS-1625G is a flexible, non-toxic, flame-retardant low temperature heat –shrinkable polyolefin tube. It is designed for the environment protection tube which does not contain any brominated flame-retardant chemicals and it is used for a wide range of applications
such as insulation and protective covering
Applications
Shrink Ratio : 50% or more in the radial direction
7% in the axial direction
Continuous operation temperature :-55oC to 125
oC
Flammability : UL VW-1, CSA OFT, -F-MARK
Environment protection tube
Excellent electrical properties
High resistance to chemicals and oils.
Features
SPECIFICATION VALUES
STANDARD
UL 224 (File No.:E84393) CSA C22.2 (File No.: LR55659)
PassVW-1Flammability
No sign of degradation158oC/168 hrsCopper Stability
No corrosion158oC/168 hrsCopper corrosion
Chemical
Min. 10 14
Q – cm -Volume resistivity
Min.2.5kV/1 Minute-Dielectric strength
Electrical
Physical
Max. 17.64kgf/mm2
-Secant modulus
No cracks158oC/168 hrsFlexibility
No crack-30oC/1 hrCold bend
No crack136oC/1 hrHeat shock
Max. 50%125oC/1 hrDeformation
Unaged
AgedMin. 70% of the Value
of unaged specimens
Min. 100%
158oC/168 hrs
Tensile Strength
Elongation
Min. 1.06kgf/mm2
Min 200%
ASTM D 638Tensile strength
Elongation
VALUE TEST METHODPROPERTY
Polychem Products
GSHS 1625GFLEXIBLE,NON-TOXIC,
FLAME- RETARDANT POLYOLEFIN600V, 125
OC, 2:1
Product Dimensions
Due to continuous development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than
specified if recovery is restricted during shrinkage.Other lengths and sizes are available subject to special order.
D d
W
Ordering Information
Standard colors : Black
Size selection : Always order the largest size that will shrink snugly over the component to be covered.
Standard package : On spools.
Ordering description : Specify product name, size, and color [for example, GSHS-1625G-0.25Tx6mm-Black]
200
200
200
200
200
200
100
100
100
100
100
100
100
100
50
50
50
50
50
50
50
50
50
50
50
50
50
31
0.356
0.432
0.432
0.4.32
0.432
0.432
0.559
0.559
0.559
0.559
0.599
0.559
0.559
0.559
0.686
0.686
0.686
0.686
0.762
0.762
0.762
0.762
0.864
0.864
0.864
0.864
0.864
0.864
0.75
1.00
1.25
1.50
1.75
2.00
2.50
3.00
3.50
4.00
4.5
5.00
5.50
6.00
6.50
7.00
7.50
8.00
9.00
10.00
11.00
12.00
12.50
13.00
14.00
15.00
16.00
19.00
1.9
2.3
2.8
3.3
3.8
4.3
5.3
6.3
7.6
8.6
9.6
10.6
11.6
12.6
13.6
14.6
15.6
16.9
18.9
20.9
22.9
24.9
26.2
27.2
29.2
31.2
33.2
39.0
0(METRIC SIZE)
0.20 T X 1.5
0.25 T X 2.0
0.25 T X 2.5
0.25 T X 3.0
0.25 T X 3.5
0.25 T X 4.0
0.25 T X 5.0
0.25 T X 6.0
0.25 T X 7.0
0.25 T X 8.0
0.25 T X 9.0
0.25 T X 10.0
0.25 T X 11.0
0.25 T X 12.0
0.30 T X 13.0
0.30 T X 14.0
0.30 T X 15.0
0.30 T X 16.0
0.35 T X 18.0
0.35 T X 20.0
0.40 T X 22.0
0.40 T X 24.0
0.40 T X 25.0
0.40 T X 26.0
0.40 T X 28.0
0.40 T X 30.0
0.40 T X 32.0
0.43 T X 38.0
STANDARD L
ENGTH
(M)
W(Min.) Wall thickness
Of Recovered after
heating (mm)
d(Max.) Inside
Diameter of Recovered
after heating (mm)
D(Nom.) Inside
Diameter of expanded
as supplied (mm)
SIZE
Polychem Products
Expanded as suppliedFully recovered after heating
Min.shrink temperature : 110 oC
GSHS 1625W
DUAL-WALL,FLEXIBLE POLYOLEFIN TUBING
600V, 125OC, 2:1
ApplicationsGSHS-1625W is designed for all general purpose applications such as the insulations and
strain relief of electrical connections and termination , light duty harnessing , jacketing,
bundling
Continuous temperature range:-55oC to 125
oC
Flammability : UL VW-1 Level (Outside layer Only)
Minimum Shrink Temperature: 90oC
Shrink Ratio : 50% or more in the radial direction
Features
SPECIFICATION VALUES
PassUl 224Flammability (VW-1)
No sign of degradation
Min. 100%
Ul 224
158oC/168 hrs
Copper Stability
Elongation
No corrosionML-I-23053
175oC/168 hrs
Copper corrosion
Chemical
Min. 1 X 10 14 Q– cm Ul 224Volume resistivity
Min. 2500V UL 224Dielectric strength
Electrical
Physical
Max. 173 MPaUL 224Secant modulus
No crack @ -550C MIL_I_23053Low Temperature Flexibility
Pass @ 2500CX4hrsMIL-I-23053Heat shock
Density
Unaged
AgedMin. 75% of the Value of
unaged specimens
Min. 100%
ASTM D 638
UL 224
175oC/168 hrs
Tensile Strength
Elongation
Max. 1.40g/ cm2 @230C
Min. 1.06kgf/mm2
Min 200%
ASTM D-792
ASTM D 638
UL 224
Tensile strength
Elongation
VALUES TEST METHODSPROPERTY
Polychem Products
GSHS-1625W
DUAL-WALL,FLEXIBLEPOLYOLEFIN TUBING
600V, 125OC, 2:1
Product Dimensions
Due to contiuous development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than specified if recovery
is restricted during shrinkage.Other lengths and sizes are available subject to special order.
D d
W
Ordering Information
Standard colors : Black
Size selection : Always order the largest size that will shrink snugly over the component to be covered.
Standard package : 1.2 Mtrs in cut length
Ordering description : Specify product name, size, and color [for example, GSHS 1625w – 3.0 mm
blk]
0. 25
0. 50
0. 25
0. 25
0. 25
0. 35
0. 40
0. 43
As supplied
(nom)
W(mm)
Wall Thickness
0. 43
0. 76
0. 56
0. 56
0. 56
0. 76
0. 86
0. 86
After recovery
(min.)
STANDARD
LENGTH
(m)
(Nom.)
Inside DiameterSIZE
(Diameter)
1. 2
1. 2
1. 2
1. 2
1. 2
1. 2
1. 2
1. 2
1. 5
2. 5
3. 5
4. 5
6. 0
9. 0
12. 5
19. 0
3. 0
5. 0
7. 0
9. 0
12.0
18.0
25.0
38.0
(METRIC SIZE)
3.0
5.0
7.0
9.0
12.0
18.0
25.0
38.0
After recovery
(d) (max.)
as supplied
(D) (mm)
Polychem Products
Expanded as suppliedFully recovered after heating
GSHS 1635Y/G
YELLOW GREEN STRIPED,FLEXIBLE POLYOLEFIN TUBING
600V, 135OC, 2:1
ApplicationsGSHS-1635Y/G is designed for all general purpose application such as the insulation and
strain relief of electrical connection and termination, light-duty harnessing, jacketing and
bundling of wires where the international electrical ground designation is intended.
Continuous temperature range:-55oC to 135
oC
Flammability : UL VW-1, -F- mark
Minimum Shrink Temperature: 900C
Shrink Ratio : 50% or more in the radial direction
Features
SPECIFICATION VALUES
PassUl 224Flammability (VW-1)
No sign of degradation
Min. 100%
Ul 224
158oC/168 hrs
Copper Stability
Elongation
No corrosionML-I-23053
175oC/168 hrs
Copper corrosion
Chemical
Min. 1 X 10 14
Q – cm Ul 224Volume resistivity
Min. 2500V UL 224Dielectric strength
Electrical
Physical
Max. 173 MPaUL 224Secant modulus
No crack @ -55oC MIL-I-23053Low Temperature Flexibility
Pass @ 250oCX4hrsMIL-I-23053Heat shock
Density
Unaged
AgedMin. 0.8 kgf/mm2
Min. 100%
ASTM D 638
UL 224
175oC/168 hrs
Tensile Strength
Elongation
Max. 1.40g/ cm2 @23oC
Min. 1.06kgf/mm2
Min 200%
ASTM D-792
ASTM D 638
UL 224
Tensile strength
Elongation
VALUES TEST METHODSPROPERTY
Polychem Products
GSHS-1635Y/G
YELLOW GREEN STRIPED FLEXIBLE POLYOLEFIN TUBING
600V, 135OC, 2:1
Product Dimensions
Due to contiuous development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than specified if recovery
is restricted during shrinkage.Other lengths and sizes are available subject to special order.
D d
T
Ordering Information
Standard colors : Yellow / Green
Size selection : Always order the largest size that will shrink snugly over the component to be covered.
Standard package : On spools.
Ordering description : Specify product name, size, and color [for example, GSHS 1635Y/G – 0.25 T X 3.5mm
200
200
200
200
100
100
100
100
100
100
100
100
100
100
50
50
50
50
50
50
50
50
50
50
50
50
0. 432
0. 4.32
0. 432
0. 432
0. 559
0. 559
0. 559
0. 559
0. 599
0. 559
0. 559
0. 559
0. 686
0. 686
0. 686
0. 686
0. 762
0. 762
0. 762
0. 762
0. 864
0. 864
0. 864
0. 864
0. 864
0. 864
1. 25
1. 50
1. 75
2. 00
2. 50
3. 00
3. 50
4. 00
4. 50
5. 00
5. 50
6. 00
6. 50
7. 00
7. 50
8. 00
9. 00
10.00
11.00
12.00
12.50
13.00
14.00
15.00
16.00
19.00
2. 8
3. 3
3. 8
4. 3
5. 3
6. 3
7. 6
8. 6
9. 6
10. 6
11. 6
12. 6
13. 6
14. 6
15. 6
16. 9
18. 9
20. 9
22. 9
24. 9
26. 2
27. 2
29. 2
31. 2
33. 2
39.0
(METRIC SIZE)
0. 25 T X 2.5
0. 25 T X 3.0
0. 25 T X 3.5
0. 25 T X 4.0
0. 25 T X 5.0
0. 25 T X 6.0
0. 25 T X 7.0
0. 25 T X 8.0
0. 25 T X 9.0
0. 25 T X 10.0
0. 25 T X 11.0
0. 25 T X 12.0
0. 30 T X 13.0
0. 30 T X 14.0
0. 30 T X 15.0
0. 35 T X 16.0
0. 35 T X 18.0
0. 35 T X 20.0
0. 40 T X 22.0
0. 40 T X 24.0
0. 40 T X 25.0
0. 40 T X 26.0
0. 40 T X 28.0
0. 40 T X 30.0
0. 40 T X 32.0
0. 43 T X 38.0
STANDARD
LENGTH
(M)
T(Min.) Wall thickness
Of Recovered after
heating (mm)
d(Max.) Inside
Diameter of Recovered
after heating (mm)
d(Nom.) Inside
Diameter of expanded
as supplied (mm)
SIZE
Polychem Products
PHWT
ADHESIVE-LINED HEAVY WALLPOLYOLEFIN TUBING
ApplicationsPHWT is designed for insulating and sealing cable splices, electrical connections, jacket
repairs and terminations. Ideally suited for submersible, direct-buried installations, or
wherever mechanical protection is required in an electrical insulation system.
Operating temperature range:-55oC to 125
oC
Minimum Shrink Temperature: 1200C
Shrink Ratio : 67% or more in the radial direction
Features
SPECIFICATION VALUES
7 days in transformer oil
Min. 300%
ISO 1817
ISO 37
Fluid resistance
Elongation
Pass rating 1
Min. 300%
ASTM G 21
ISO 37
Resistance to Fungi
Elongation
Max 0.1% @23oC X14
days
ISO 62Water absorption
Chemical
Min. 1 X 10 13
Q – cm IEC 93Volume resistivity
Min. 20 kV/mm IEC 243Dielectric strength
Electrical
Physical
120oCIEC 216Thermal endurance
No crack@ 225oC4hrsASTM D 2671Heat shock
No crack @ -55oCX4 hrsASTM D 2671Low Temperature Flexibility
Density
Unaged
Aged Min. 1.2 kgf/mm2
Min. 300%
ASTM D 638
ISO 37
150oC/168 hrs
Tensile Strength
Elongation
Max. 1.10g/ cm2 @23oC
Min. 1.4 kgf/mm2
Min. 350%
ASTM D-792
ASTM D 638
ISO 37
Tensile strength
Elongation
VALUES TEST METHODSPROPERTY
Polychem Products
PHWT
ADHESIVE LINED HEAVY WALL POLYOLEFIN TUBING
Product Dimensions
Due to contiuous development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than specified if recovery
is restricted during shrinkage.Other lengths and sizes are available subject to special order.
D d
W
Ordering Information
Standard colors : Black
Size selection : Always order the largest size that will shrink snugly over the component to be covered.
Standard package : 1.2 Mtrs in cut length
Ordering description : Specify product name, size, and color [for example,: PHWT 0.80Tx13mm Black
0.70
0.80
0.80
1.00
1.30
1.30
1.30
1.30
1.30
1.30
1.40
1.40
As supplied
(nom)
W(mm)
Wall Thickness
1.80
2.40
2.40
3.00
4.10
4.10
4.10
4.10
4.10
4.20
4.50
4.50
After recovery
(min.)
STANDAR
D
LENGTH
(m)
Inside Diameter
SIZE
(Diameter)
1. 2
1. 2
1. 2
1. 2
1. 2
1. 2
1. 2
1. 2
1.2
1.2
1.2
1.2
3.0
4.0
6.0
8.0
12.0
16.0
21.0
25.0
30.0
36.0
50.0
50.0
9.0
13.0
20.0
33.0
43.0
51.0
70.0
85.0
90.0
130.0
160.0
180.0
(METRIC SIZE)
9.0
13.0
20.0
33.0
43.0
51.0
70.0
85.0
90.0
130.0
160.0
180.0
After recovery
d(max.)
as supplied
D(mm)
Polychem Products
PMWT
ADHESIVE-LINED MEDIUM WALLPOLYOLEFIN TUBING
PMWT is designed for insulating and sealing cable splices, electrical connections, jacket
repairs and terminations. Ideally suited for submersible, direct-buried installations, or
wherever mechanical protection is required in an electrical insulation system.
Applications
Operating temperature range:-55oC to 125
oC
Minimum Shrink Temperature: 1200C
Shrink Ratio : 67% or more in the radial direction
Features
SPECIFICATION VALUES
7 days in transformer oil
Min. 300%
ISO 1817
ISO 37
Fluid resistance
Elongation
Pass rating 1
Min. 300%
ASTM G 21
ISO 37
Resistance to Fungi
Elongation
Max 0.1% @230C X14 da
ys
ISO 62Water absorption
Chemical
Min. 1 X 10 13
Q – cm IEC 93Volume resistivity
Min. 20 kV/mm IEC 243Dielectric strength
Electrical
Physical
1200CIEC 216Thermal endurance
No crack@ 2250C4hrsASTM D 2671Heat shock
No crack @ -550CX4 hrsASTM D 2671Low Temperature Flexibility
Density
Unaged
Aged Min. 1.2 kgf/mm2
Min. 300%
ASTM D 638
ISO 37
150oC/168 hrs
Tensile Strength
Elongation
Max. 1.10g/ cm2 @230C
Min. 1.4 kgf/mm2
Min. 350%
ASTM D-792
ASTM D 638
ISO 37
Tensile strength
Elongation
VALUES TEST METHODSPROPERTY
Polychem Products
PMWT
ADHESIVE LINED MEDIUMWALL POLYOLEFIN TUBING
Product Dimensions
Due to contiuous development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than specified if recovery
is restricted during shrinkage.Other lengths and sizes are available subject to special order.
D d
W
Ordering Information
Standard colors : Black
Size selection : Always order the largest size that will shrink snugly over the component to be covered.
Standard package : 1.2 Mtrs in cut length
Ordering description : Specify product name, size, and color [for example,: PMWT 0.50Tx16mm Black
0.40
0.50
0.70
0.70
0.70
0.80
0.90
0.90
1.00
1.00
1.00
1.00
1.00
As supplied
(nom)
W(mm)
Wall Thickness
1.00
1.50
2.00
2.00
2.00
2.50
3.00
3.00
3.30
3.30
3.50
3.50
3.50
After recovery
(min.)
STANDARD
LENGTH
(m)
Inside Diameter
SIZE
(Diameter)
1. 2
1. 2
1. 2
1. 2
1. 2
1. 2
1. 2
1. 2
1.2
1.2
1.2
1.2
1.2
3.0
5.0
8.0
12.0
16.0
19.0
22.0
25.0
29.0
34.0
42.0
50.0
60.0
10.0
16.0
25.0
35.0
50.0
63.0
75.0
85.0
95.0
115.0
140.0
160.0
180.0
(METRIC SIZE)
10.0
16.0
25.0
35.0
50.0
63.0
75.0
85.0
95.0
115.0
140.0
160.0
180.0
After recovery
d(max.)
as supplied
D(mm)
Polychem Products
DRET
DIESEL-RESISTANT, FLEXIBLE,ELASTOMERIC POLYOLEFIN TUBING
DRET is used for insulation, strain relief and abrasion protection on cable harnesses and wire
bundles in military industries. Especially, provides fluids and solvent resistance including
lubricating oil ground-vehicle fuels and hydraulic fluids.
Applications
Operating temperature range:- -75oC to 120
oC
Flammability : Mil-I-23053/16 Rated
Minimum Shrink Temperature: 1350C
Shrink Ratio : 50% or more in the radial direction
Typical Features
SPECIFICATION VALUES
Max. 1.10g/ cm2 @230CASTM D-792Density
PassMIL-I-23053Flammability
Min. 1.1kgf/mm2
Min. 200%
Min. 200V/mil
MIL-I-23053
23OC/24 hrs
Fluid resistance
Tensile strength
Elongation
Dielectric Strength
No corrosionMIL-I-23053
150OC/16 hrs
Copper corrosion
Chemical
Min. 1 X 10 11
Q – cm ASTM D 876Volume resistivity
Min. 300 V/mil ASTM D 876Dielectric strength
Electrical
Physical
Pass @ 200oC x 4 hrsMIL-I-23053Heat shock
No crack @ -750CMIL-I-23053Low Temperature Flexibility
Unaged
Aged Min. 0.8 kgf/mm2
Min. 200%
ASTM D 638
150oC/168 hrs
Tensile Strength
Elongation
Min. 1.1 kgf/mm2
Min. 250%
ASTM D 638Tensile strength
Elongation
VALUES TEST METHODSPROPERTY
Standards
MIL-I-23053/16
Polychem Products
DRET
DIESEL-RESISTANT,FLEXIBLE,ELASTOMERIC
POLYOLEFIN TUBING
Product Dimensions
Due to contiuous development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than specified if recovery
is restricted during shrinkage.Other lengths and sizes are available subject to special order.
D d
W
Ordering Information
Standard colors : Black
Size selection : Always order the largest size that will shrink snugly over the component to be covered.
Standard package : 1.2 Mtrs in cut length
Ordering description : Specify product name, size, and color [for example,: DRET0.45Tx1/8” Black
0.45
0.45
0.45
0.50
0.60
0.70
0.85
1.00
1.10
1.30
1.50
As supplied
(nom)
W(mm)
Wall Thickness
070
0.75
0.80
0.90
1.05
1.45
1.70
2.20
2.45
2.85
3.20
After recovery
(min.)
STANDARD
LENGTH
(m)
Inside Diameter
SIZE
(Diameter)
200
100
100
50
50
50
50
31
31
31
31
1.57
2.36
3.18
4.75
6.35
9.53
12.70
15.90
19.10
25.40
38.10
3.2
4.8
6.4
9.6
12.7
19.1
25.4
31.8
38.1
50.8
76.2
INCH SIZE
1/8
3/16
¼
3/8
½
¾
1
1-1/4
1-1/2
2
3
After recovery
d(max.)
as supplied
D(mm)
Polychem Products
HFSPHeat Shrinkable Fiber Optic Splice Protector
Features :
Consist of crosslinked polyolefin, hot fusion tubing and stainless reinforcing steel rod
Keep optic transmission properties of optical fiber
Provide strength and protection to optical fiber splices
Easily use and avoid any damages to the optical fiber during installation
Clear sleeve make it easy to detect splice before shrinkage
Sealing structure make the splice free from effect of temperature and humidity from environment
Operating Temperature
-55 - 60 oC
Shrinking temperature range
90 – 110 oC
Technical Data
+ 5ASTM D 2671Longitudinal Change (%)
2.5IEC 243Dielectric Constant
20IEC 243Dielectric Strength (KV/mm)
0.94ISO R 1183DDensity (g/cm2)
700ASTM D 2671Ultimate Elongation (%)
18ASTM D 2671Tensile Strength (MPa)
Typical DataTest methodProperties
1.9--2.00.51.2 + 0.140HFSP-40M
</= 1.350.50.5 + 0.123HFSP-23M
</= 2.601.21.2 + 0.145HFSP-45T
</= 3.001.51.3 + 0.123HFSP-23
</= 3.001.5 1.3 + 0.145HFSP-45
</= 3.001.51.3 + 0.161HFSP-61
(mm)(mm)(mm)(mm)
O.D of splice protecto
r after recovered
Steel Rod D
d
I.D of fusion tube
D
Length
L
Order Ref.No.
Packing
100 Pieces/Bag
Polychem Products
FUSION TUBE
Features
one of the components from HSFP is called FUSION TUBE
Also called as EVA TUBE (Ethylene Vinyl Acetate)
200 mtrs1.5 mm1.7 mm
200 mtrs1.9 mm2.9 mm
200 mtrs1.3 mm2.3 mm
200 mtrs0.5 mm0.9 mm
Packing (roll)Inside DiameterOutside Diameter
Product Dimensions
Polychem Products
Due to contiuous development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than specified if recovery is restricted during shrinkage.
Other lengths and sizes are available subject to special order.
END CAPS
Features
Specifications
After recoveredAs supplied
120
80
70
40
30
25
70
45
38
25
15
9
Inside Diameter
(mm)
3.5 mm170RSF – 6
3.5 mm150RSF – 5
2.7 mm130RSF – 4
3.4 mm120RSF – 3
2.6 mm100RSF – 2
2.3 mm90RSF – 1
Wall thickness
after shrinking
Length
(mm)
Order Ref.
No.
Polychem Products
Due to contiuous development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness of the tubing will be less than specified if recovery is restricted during shrinkage.
Other lengths and sizes are available subject to special order.
Heat Shrinkable Silicone Rubber Tube
Product Dimensions
3.0 + 0.35 + 0.2130.0 + 2.0260.0 + 2.0160~240.0250
3.0 + 0.31.5 + 0.2120.0 + 2.0210.0 + 2.0130~190.0200
3.0 + 0.31.5 + 0.2100.0 + 2.0185.0 + 2.0110~150.0180
3.0 + 0.31.5 + 0.280.0 + 2.0155.0 + 2.090.0~130.0150
3.0 + 0.31.5 + 0.258.0 + 2.0110.0 + 2.070.0~90.0110
3.0 + 0.31.5 + 0.247.0 + 1.090.0 + 2.060.0~80.090
3.0 + 0.31.5 + 0.242.0 + 1.080.0 + 2.050.0~65.080
3.0 + 0.31.5 + 0.135.0 + 1.066.0 + 2.040.0~60.065
3.0 + 0.31.5 + 0.129.0 + 1.055.0 + 2.040.0~60.055
3.0 + 0.31.0 + 0.123.0 + 1.045.0 + 1.033.0~50.045
2.0 + 0.31.0 + 0.116.0 + 0.531.0 + 1.025.0~42.030.0
2.0 + 0.31.0 + 0.114.0 + 0.425.0 + 1.018.0~28.025.0
2.0 + 0.31.0 + 0.112.0 + 0.423.0 + 1.015.0~23.020.0
1.5 + 0.20.75 + 0.19.0 + 0.217.0 + 1.09.0~15.017.0
1.5 + 0.20.75 + 0.16.0 + 0.212.0 + 1.06.0~10.012.0
1.0 + 0.20.5 + 0.14.3 + 0.28.6 + 0.44.5~7.08.0
1.0 + 0.20.5 + 0.13.3 + 0.26.6 + 0.33.2~6.06.0
1.0 + 0.20.5 + 0.12.9 + 0.25.6 + 0.32.8~5.05.0
1.0 + 0.20.5 + 0.12.2 + 0.14.5 + 0.32.3~4.04.0
1.0 + 0.20.5 + 0.11.6 + 0.13.2 + 0.21.8~2.53.0
1.0 + 0.20.5 + 0.10.8 + 0.12.2 + 0.21.2~2.02.0
1.0 + 0.20.5 + 0.10.8 + 0.11.7 + 0.21.1~1.41.5
Range of
Application
After recoveryAs suppliedAfter recoveryAs supplied
Wall ThicknessInside DiaSIZE
Polychem Products
Due to contiuous product development specification are subject to change. Users are requested to evaluate the products independently. The wall thickness
of the tubing will be less than specified if recovery is restricted during shrinkage.
Other lengths and sizes are available subject to special order.
CATVADHESIVE-LINED
HEAVY WALL POLYOLEFIN TUBINGS
Applications
CATV is designed for fast and simple installation allowing clean and easy connector re-en
try. Especially, high performance adhesive provides an absolutely waterproof seal and me
chanical protection for the CATV industry.
Operating Temperature : -55 0C to 125 0C
Mimimum Shrink Temperature : 120 OC
Shrink ration : 67% or more in the radial direction
Typical Features
Elongation
Min. 200%
Min. 300%
ElongationAged
Max. 1.20g/ cm2 @230CASTM D-792Density
No penetration50 oC x 14 daysWater penetration
Max. 0.1%ASTM D 570
23OC/24 hrs
Water absorption
Min 1x1014 () -cmASTM D 257Volume resistivityChemical
Min. 13.8kV/mmASTM D 149Dielectric Strength
No crack @ -55 oC X 4hrs ASTM D 2671Low temperature flexibility
Physical
Electrical
110N / 25mm
80 N / 25 mm
ASTM D 1000
ASTM D 1000
Adhesive peel strength to
Polyethylene
Aluminum
No crack @2250C x 4 hrsASTM D 2671Heat Shock
Unaged
Min. 0.8 kgf/mm2UL 224
150oC/168 hrs
Tensile Strength
Min. 1.1 kgf/mm2
ASTM D 638
Tensile strength
VALUES TEST METHODSPROPERTY
Specification Values
CATV
ADHESIVE-LINED
HEAVY WALL POLYOLEFIN TUBINGS
Product Dimensions
1.50
1.50
2.70
2.70
3.00
3.00
3.00
3.90
After recovery
(min)
1.2
1.2
1.2
1.2
1.2
1.2
1.2
1.2
Standard
Length
(m)
0.70
0.60
1.10
1.00
1.20
1.10
1.20
1.60
As supplied
(nom)
W(mm)
Wall Thickness
3.0
6.0
9.0
9.0
13.0
13.0
18.0
25.0
10.0
19.0
27.0
33.0
38.0
43.0
51.0
70.0
10.0
19.0
27.0
33.0
38.0
43.0
51.0
70.0
M
E
T
R
I
C
S
I
Z
E
After recovery
(Max)
As supplied
(min)
D(mm)
Inside Diameter
SIZE
(Diameter)
Ordering Information
Standard Color : Black
Ordering Description : Specify Product name, size and Color.
[Ex.LG-CATV 1.10T x 27 mm Black]
VIT-300, VIT-600
NOT HEAT-SHRINKABLE PVC TUBING
300,600V, 105OC
Polychem Products
VIT-300/600 is a flexible, flame-retardant not heat-shrinkable polyvinyl chloride tube. They
are widely used for protective covering for wires.
Applications
Continuous operation temperature :-10oC to 105
oC
Flammability : UL VW-1, CSA OFT
Excellent electrical properties.
High resistance to chemicals
Features
SPECIFICATION VALUES
STANDARDS
UL 224 (File No.:E84393) CSA C22.2 (File No.: LR55659)
PassVW-1Flammability
No sign of degradation136oC/168 hrsCopper Stability
No corrosion136oC/168 hrsCopper corrosion
Chemical
Min. 10 10
Q – cm -Volume resistivity
Min.2.5kV/1 Minute-Dielectric strength
Electrical
Physical
No cracks136oC/168 hrsFlexibility
No crack-10oC/1 hrCold bend
No crack121oC/1 hrHeat shock
Max. 50%121oC/1 hrDeformation
Unaged
Aged Min. 70% of the Value
of unaged specimens136oC/168 hrs
Tensile Strength
Elongation
Min. 1.06kgf/mm2
Min 100%
ASTM D 638Tensile strength
Elongation
VALUE TEST METHODPROPERTY
VIT-300, VIT-600
NOT HEAT-SHRINKABLE PVC TUBING
300/600V, 105OC
Product Dimensions
Due to continuous product development specifications are subject to change. Users are requested to evaluate the products independently.
Ordering InformationStandard colors : Black & Clear
Ordering description : Specify product name, size, and color [for example, VIT – 600 22 AWG Clear
VIT - 600VIT - 300
0.53
0.53
0.53
0.68
0.68
0.68
0.68
0.68
0.68
0.68
0.68
0.68
0.68
0.68
0.68
0.68
0.68
0.68
0.68
T(Nom.)
Thickness (mm)
VIT - 600
0.69
0.86
1.07
1.34
1.68
1.93
2.16
2.14
2.69
3.00
3.38
3.76
4.22
4.72
5.28
5.94
6.68
7.40
8.38
D(Nom.) Inside
Diameter (mm)
0.30
0.40
0.40
0.40
0.40
0.40
0.40
0.40
0.40
0.53
0.53
0.53
0.53
0.53
0.53
0.53
0.53
0.53
0.53
T(Nom.)
Thickness (mm)
VIT- 300
305
1.75
1.90
2.15
3.45
3.85
4.10
4.30
4.55
4.85
5.40
5.80
6.15
6.60
7.10
7.70
8.35
9.10
9.75
10.8
1.30
1.65
1.90
2.10
2.50
2.75
2.95
3.20
3.50
4.05
4.45
4.80
5.25
5.75
6.85
7.00
7.75
8.40
9.45
((AWG
SIZE)
22
20
18
16
14
13
12
11
10
9
8
7
6
5
4
3
2
1
0
STANDARD LE
NGTH
(M)D(Nom.) Outer
Diameter (mm
)
VIT - 600
D(Nom.) Outer
Diameter (mm)
VIT - 300
SIZE
Polychem Products
Polychem products# 28, 3rd Cross, Church Road, New Thippasandra, Bangalore – 560 075.
Tel : 080-2529 7126, 98456 34834 & 98440 45286,
Fax : 080-2529 7126, email : [email protected]
Additional Products available on special request
1) Flexible 3:2 Shrink ratio polyolefin with meltable
adhesive for brake/fuel pipe of automobiles.
Also available without adhesive.
2) Adhesive coated tubes / Non Adhesive coated
tubes in
a) 4:1
b) 5:1
c) 6:1 shrink ratio
3) Non Shrinkable tubes:
a) Polyolefin
b) Kynar
4) Non Halogen thin Wall polyolefin
5) Semi rigid polyolefin tubing (butt spice) for tough
and high abrasion resistance.
6) PVC Heat shrinkable tubes with UL Approvals.
7) Anti tracking tubing
8) Teflon sleeves
9) Heat Shrinkable oil resistant tube
10) 3:1 shrink ratio Kynar (PVF2) sleeves
11) Heat shrinkable sheath
12) Heat shrinkable semi conductor tubes.
13) Heat Shrinkable Cable breakouts and sheds
14) Cold Shrinkable tubes
15) Expandable sleeves
16) Cable end caps
17) Heat Shrink Angles and Boots
18) Kapton Film,Normex,Formex,Ceramic,Mylar Film,
Teflon Tape,and silicon sleeve
19) Marker sleeves in Ladder form.
20) Protective sleeve upto 1500 degress C