stp183 eb/jan. 1956 - astm international · gohn , guerard and freynik on phosphor bronze reduction...

96
INDEX TO ILLUSTRATIONS FIGS. 1 to 22—Mechanical Properties of Various Phosphor Bronze Alloy Strips FIGS. 23 to 44—S-N Diagram of Various Phosphor Bronze Alloy Strips FIGS. 45 to 54—Summary of S-N Diagrams, Minimum Curves FIGS. 55 to 70—Effect of Variation in Tin Content on Various Mechanical Prop- erties FIGS. 71 to 82—Effect of Variation in Tin Content on Mechanical Properties of Various Tempers of Phosphor Bronze Strips FIGS. 83 to 85—-Effect of Variation in Phosphorus Content on Mechanical Prop- erties of 3, 4, and 5 per cent Tin Phosphor Bronze Strips FIGS. 86 to 95—Effect of Variation in Grain Size on Mechanical Properties of Phosphor Bronze Strips STP183-EB/Jan. 1956 Copyright © 1956 by ASTM International www.astm.org

Upload: vancong

Post on 09-Jan-2019

215 views

Category:

Documents


0 download

TRANSCRIPT

Page 1: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

INDEX TO ILLUSTRATIONS

FIGS. 1 to 22—Mechanical Properties of Various Phosphor Bronze Alloy StripsFIGS. 23 to 44—S-N Diagram of Various Phosphor Bronze Alloy StripsFIGS. 45 to 54—Summary of S-N Diagrams, Minimum CurvesFIGS. 55 to 70—Effect of Variation in Tin Content on Various Mechanical Prop-

ertiesFIGS. 71 to 82—Effect of Variation in Tin Content on Mechanical Properties of

Various Tempers of Phosphor Bronze StripsFIGS. 83 to 85—-Effect of Variation in Phosphorus Content on Mechanical Prop-

erties of 3, 4, and 5 per cent Tin Phosphor Bronze StripsFIGS. 86 to 95—Effect of Variation in Grain Size on Mechanical Properties of

Phosphor Bronze Strips

STP183-EB/Jan. 1956

Copyright© 1956 by ASTM International www.astm.org

Page 2: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

20

FIG. 1.—Mechanical Properties of Electrolytic Tough Pitch Copper Strip.Nominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Reduction by Cold-Rolling, Per Cent

Page 3: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

21

FIG. 2.—Mechanical Properties of Electrolytic Tough Pitch Copper Strip.Nominal ready-to-finish grain size—0.015 mm

Nominal thickness—0.040 in.

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per Cent

Page 4: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

22 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

FIG. 3.—Mechanical Properties of 0.5 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent

Nominal ready-to-finish grain size—0.035 mmNominal thickness—0.040 in.

Reduction by Cold-Rolling, Per Cent

Page 5: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

FIG. 4.—Mechanical Properties of 0.5 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm

Nominal thickness—0.040 in.

23

Reduction by Cold-Rolling, Per Cent

Page 6: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

24 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

FIG. 5.—Mechanical Properties of 1 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Reduction by Cold-Rolling, Per Cent

Page 7: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 25

Reduction by Cold-Rolling, Per Cent

FIG. 6.—Mechanical Properties of 1 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm

Nominal thickness—0.040 in.

Page 8: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

26 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per Cent

FIG. 7.—Mechanical Properties of 2 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Page 9: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 27

Reduction by Cold-Rolling, Per Cent

FIG. 8.—Mechanical Properties of 2 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm

Nominal thickness—0.040 in.

Page 10: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

28 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per Cent

FIG. 9.—Mechanical Properties of 3 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Page 11: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRON 29

Reduction by Cold-Rolling, Per Cent

FIG. 10.—Mechanical Properties of 3 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm

Nominal thickness—0.040 in.

Page 12: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

30 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

10,4

Reduction by Cold-Rolling, Per CentFIG. 11.—Mechanical Properties of 4 per cent Tin Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish gram size—0.035 mm

Nominal thickness—0.040 in.

Page 13: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 31

Reduction by Cold-Rolling, Per CentFIG. 12.—Mechanical Properties of 4 per cent Tin Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm

Nominal thickness—0.040 in.

Page 14: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

32

Reduction by Cold-Rolling, Per CentFIG, 13.—Mechanical Properties of 5 per cent Tin Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish gram size—0.035 mm

Nominal thickness—0.040 in.

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Page 15: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GTJERARD, AND FREYNIK ON PHOSPHOR BRONZE 33

Reduction by Cold-Rolling, Per Cent

FIG. 14.—Mechanical Properties of 5 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm

Nominal thickness—0.040 in.

Page 16: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per Cent

FIG. 15.—Mechanical Properties of 8 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

34

Page 17: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 35

Reduction by Cold-Rolling, Per Cent

FIG. 16.—Mechanical Properties of 8 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish gram size—0.015 mm

Nominal thickness—0.040 in.

Page 18: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

36 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per Cent

FIG. 17.—Mechanical Properties of 10 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Page 19: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Reduction by Cold-Rolling, Per CentFIG. 18.—Mechanical Properties of 10 per cent Tin Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm

Nominal thickness—0.040 in.

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 37

Page 20: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

38 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per Cent

FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.40 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Page 21: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 39

Reduction by Cold-Rolling, Per CentFIG. 20.—Mechanical Properties of 4 per cent Tin Phosphor Bronze Strip.

Nominal phosphorus content—0.40 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Page 22: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

40 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per Cent

FIG. 21.—Mechanical Properties of 4 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.40 per centNominal ready-to-finish grain size—0.075 mm

Nominal thickness—0.040 in.

Page 23: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Reduction by Cold-Rolling, Per Cent

FIG. 22.—Mechanical Properties of 5 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.40 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 41

Page 24: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-Failure

FIG. 23.—Fatigue Characteristics of Electrolytic Tough Pitch Copper Strip.Nominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Page 25: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-FoilureFIG. 24.—Fatigue Characteristics of Electrolytic Tough Pitch Copper Strip.

Nominal ready-to-finish grain size—0.035 mmNominal thickness—0.040 in.

Page 26: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-FailureFIG. 25.—Fatigue Characteristics of 0.5 per cent Tin Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-fmish gram gize—0.035 mm

Nominal thickness—0.040 in.

Page 27: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-Failure

FIG. 26.—Fatigue Characteristics of 0.5 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent

Nominal ready-to-finish grain size—0.015 mmNominal thickness—0.040 in.

Page 28: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-Failure

FIG. 27.—Fatigue Characteristics of 1 per cent Tin Phosphor Bronze Strip.Nominal Phosphorus content—0.05 per cent

Nominal ready-to-finish grain size—0.035 mmNominal thickness—0.040 in.

Page 29: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-Failure

FIG. 28.—Fatigue Characteristics of 1 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent

Nominal ready-to-finish grain size—0.015 mmNominal thickness—0.040 in.

Page 30: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-Failure

FIG. 29.—Fatigue Characteristics of 2 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent

Nominal ready-to-finish gram size—0.035 mmNominal thickness—0.040 in.

Page 31: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-FoilureFIG. 30.—Fatigue Characteristics of 2 per cent Tin Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm

Nominal thickness—0.040 in.

Page 32: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-FoilureFIG. 31.—Fatigue Characteristics of 3 per cent Tin Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Page 33: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-Failure

FIG. 32.—Fatigue Characteristics of 3 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm

Nominal thickness—0.040 in.

Page 34: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-Failure

FIG. 33.—Fatigue Characteristics of 4 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Page 35: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-FallureFIG. 34.—Fatigue Characteristics of 4 per cent Tin Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm

Nominal thickness—0.040 in.

Page 36: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-Foilure

FIG. 35.—Fatigue Characteristics of 5 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish gram size—0.035 mm

Nominal thickness—0.040 in.

Page 37: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cyc les—to —Failure

FIG. 36.—Fatigue Characteristics of 5 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish gram size—0.015 mm

Nominal thickness—0.040 in.

Page 38: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-FailureFIG. 37.—Fatigue Characteristics of 8 per cent Tin Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Page 39: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-FailureFIG. 38.—Fatigue Characteristics of 8 per cent Tin Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm

Nominal thickness—0.040 in.

Page 40: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-Failure

FIG. 39.—Fatigue Characteristic of 10 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Page 41: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to—FailureFIG. 40.—Fatigue Characteristics of 10 per cent Tin Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm

Nominal thickness—0.040 in.

Page 42: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-FoilureFIG. 41.—Fatigue Characteristics of 3 per cent Tin Phosphor Bronze Strip.

Nominal phosphorus content—0.40 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Page 43: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-FailureFIG. 42.—Fatigue Characteristics of 4 per cent Tin Phosphor Bronze Strip.

Nominal phosphorus content—0.40 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Page 44: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-Fai lure

FIG. 43.—Fatigue Characteristics of 4 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.40 per centNominal ready-to-finish grain size—0.075 mm

Nominal thickness—0'040 in.

Page 45: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-Failure

FIG. 44.—Fatigue Characteristics of 5 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.40 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Page 46: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

64 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Number of Cycles-ro-Foilure(a)

FIG. 45.—Comparison of Fatigue Characteristics of Electrolytic Tough Pitch Copper Strip.Nominal thickness—0.040 in.

(a) Nominal ready-to-finish grain size—0.035 mm.(6) Nominal ready-to-finish gram size—0.015 mm.

Number of Cycles-to-Failure(b)

Page 47: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 65

Number of Cycles-to—Failure(a)

FIG. 46.—Comparison of Fatigue Characteristics of 0.5 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per centNominal thickness—0.040 in.

(a) Nominal ready-to-finish gram size—0.035 mm.(6) Nominal ready-to-finish grain size—0.015 mm.

Number of Cycles-to-Foilure

(b)

Page 48: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-Failure

(a)

FIG. 47.—Comparison of Fatigue Characteristics of 1 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent

Nominal thickness—0.040 in.(a) Nominal ready-to-finish grain size—0.035 mm.(6) Nominal ready-to-finish gram size—0.015 mm.

GOHN, GUERARD, AND pREYNIK ON PHOSPHOR BRONZE66

Number of Cycles-to-Failure(b)

Page 49: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Number of Cycles-to-Foilure

(a)

FIG. 48.—Comparison of Fatigue Characteristics of 2 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent

Nominal thickness—0.040 in.(a) Nominal ready-to-finish grain size—0-035 mm.(6) Nominal ready-to-finish grain size—0.015 mm.

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 67

Number of Cycles-to-Foilure

(b)

Page 50: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Number of Cycles-to-Failure(b)

FIG. 49.—Comparison of Fatigue Characteristics of 3 per cent Tin Phosphor Bronze Strip.Nominal thickness—0.040 in.

(a) Nominal ready-to-finish gram size—0.035 mm, Nominal phosphorus content—0.05 per cent.(5) Nominal ready-to-finish gram size—0.015 mm, Nominal phosphorus content—0.05 per cent,(c) Nominal ready-to-finish grain size—0.035 mm, Nominal phosphorus content—0.40 per cent.

68

Number of Cycles -•to- Failure(a)

Number of Cycles-to-Failure(C)

Page 51: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 69

Number of Cycles-to-Foilure(a)

FIG. 50.—Comparison of Fatigue Characteristics of 4 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent.

Nominal thickness—0.040 in.(a) Nominal ready-to-finish grain size—0.035 mm.(6) Nominal ready-to-finish grain size—0.015 mm.

Number of Cycles-to-Failure

(b)

Page 52: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

70 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

FIG. 51.—Comparison of Fatigue Characteristics of 4 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.40 per cent.

Nominal thickness—0.040 in.(a) Nominal ready-to-finish gram size—0.035 mm.(6) Nominal ready-to-finish gram size—0.075 mm.

Number of Cycles-to-Foilure

(a)

Number of Cycles-to-Failure

(b)

Page 53: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GtJERARD, AND FREYNIK ON PHOSPHOR BRONZE 71

Number of Cycles-to-Failure(a) .

Number of Cycles-to-Failure(b)

Number of Cycles-to-Failure(C)

FIG. 52.—Comparison of Fatigue Characteristics of 5 per cent Tin Phosphor Bronze Strip.Nominal thickness—0.040 in.

(a) Nominal ready-to-finish grain size—0.035 mm, Nominal phosphorus content—0.05 per cent.(b) Nominal ready-to-finish grain size—0.015 mm, Nominal phosphorus content—0.05 per cent.(c) Nominal ready-to-finish grain size—0.035 mm, Nominal phosphorus content—0.40 per cent.

Page 54: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

72 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Number of Cycles-to-Failure(a)

Number of Cycles-to-Failure

(b)FIG. 53.—Comparison of Fatigue Characteristics of 8 per cent Tin Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per cent.Nominal thickness—0.040 in.

(a) Nominal ready-to-finish gram size—0.035 mm.(6) Nominal ready-to-finish grain size—0.015 mm.

Page 55: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Number of Cycles-to-Failure(a)

Number of Cycles-to-Foilure(b)

FIG. 54.—Comparison of Fatigue Characteristics of 10 per cent Tin Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent.

Nominal thickness—0.040 in.(a) Nominal ready-to-fiinsh grain size—0.035 mm.(6) Nominal ready-to-fiinsh gram szie—0.015 mm.

73

Page 56: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

74 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per Cent

FIG. 55.—Effect of Variation in Tin Content on the Tensile Strength of Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent.Nominal ready-to-finish grain size—0.035 mm.

Nominal thickness—0.040 in.

Page 57: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 75

Reduction by Cold-Rolling, Per Cent

FIG. 56.—Effect of Variation in Tin Content on the Tensile Strength of Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent.Nominal ready-to-finish grain size—0.015 mm.

Nominal thickness—0.040 in.

Page 58: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

76 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per CentFIG. 57.—Effect of Variation in Tin Content on the Proportional Limit of Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per cent.Nominal ready-to-finish grain size—0.035 mm.

Nominal thickness—0.040 in.

Page 59: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 77

Reduction by Cold-Rolling, Per Cent

FIG. 58.—Effect of Variation in Tin Content on the Proportional Limit of Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent.Nominal ready-to-finish grain size—0.015 mm.

Nominal thickness—0.040 in.

Page 60: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

78 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per Cent

FIG. 59.—Effect of Variation in Tin Content on the Yield Strength at 0.01 per cent Offset ofPhosphor Bronze Strip.

Nominal phosphorus content—0.05 per cent.Nominal ready-to-finish grain size—0.035 mm.

Nominal thickness—0.040 in.

Page 61: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 79

Reduction by Cold-Rolling, Per Cent

FIG. 60.—Effect of Variation in Tin Content on the Yield Strength at 0.01 per cent Offset ofPhosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm.

Nominal thickness—0.040 in.

Page 62: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

80 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per Cent

FIG. 61.—Effect of Variation in Tin Content on the Yield Strength at 0.2 per cent Offset ofPhosphor Bronze Strip.

Nominal phosphorus content—-0.05 per centNominal ready-to-finish grain size—0.035 mm.

Nominal thickness 0.040 in.

Page 63: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 81

Reduction bv Cold-Rolling, Per Cent

FIG. 62.—Effect of Variation in Tin Content on the Yield Strength at 0.2 per cent Offset ofPhosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm.

Nominal thickness—0.040 in.

Page 64: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

82 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling,Per CentFIG. 63.—Effect of Variation in Tin Content on the Ductility of Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.035 mm.

Nominal thickness—0.040 in.

Page 65: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 83

Reduction by Cold-Rolling, Per Cent

FIG. 64.—Effect of Variation in Tin Content on the Ductility of Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent

Nominal ready-to-finish grain size—0.015 mm.Nominal thickness—0.040 in.

Page 66: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

84 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per Cent

FIG. 65.—Effect of Variation in Tin Content on the Rockwell "B" Hardness of Phosphor BronzeStrip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.035 mm

Nominal thickness—0.040 in.

Page 67: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 85

Reduction by Cold-Rolling, Per Cent

FIG. 66.—Effect of Variation in Tin Content on the Rockwell "B" Hardness of Phosphor BronzeStrip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish gram size—0.015 mm.

Nominal thickness—0.040 in.

Page 68: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

86 GOHN, GUERAKD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per Cent

FiG. 67.—Effect of Variation in Tin Content on the Rockwell "30T" Hardness of PhosphorBronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.035 mm.

Nominal thickness—0.040 in.

Page 69: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 87

Reduction by Cold-Rolling,Per Cent

FIG. 68.—Effect of Variation in Tin Content on the Rockwell "30T" Hardness of PhosphorBronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish gram size—0.015 mm.

Nominal thickness—0.040 in.

Page 70: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE88

Reduction by Cold-Rolling, Per Cent

(b)FIG. 69.—Effect of Variation in Tin Content on the Modulus of Elasticity of Phosphor Bronze

Strip.Nominal phosphorus content—0.05 per cent

Nominal thickness—0.040 in.(a) Nominal ready-to-finish gram size—0.035 mm.(b) Nominal ready-to-finish grain size—0.015 mm.

Page 71: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 89

Reduction by Cold-Rolling,Per Cent

(b)FIG. 70.—Effect of Variation in Tin Content on the Bending Fatigue Properties of Phosphor

Bronze Strip at 10s Cycles of Reversed Stress.Nominal phosphorus content—0.05 per cent

Nominal thickness—0.040 in.(a) Nominal ready-to-finish grain size—0.035 mm.(6) Nominal ready-to-finish grain size—0.015 mm.

Page 72: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

90

Tin, Per Cent

FIG. 71.—Mechanical Properties of Annealed Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent

Nominal ready-to-finish grain size—0.035 mm.Nominal thickness—0.040 in.

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Page 73: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 91

Tin, Per CentFIG. 72.—Mechanical Properties of Annealed Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm.

Nominal thickness—0.040 in.

Page 74: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

92 GOHN, GTJERARD, AND FREYNIK ON PHOSPHOR BRONZE

Tin,Per CentFIG. 73.—Mechanical Properties of Half-Hard Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.035 mm.

Nominal thickness—0.040 in.

Page 75: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 93

Tin, Per CentFIG. 74.—Mechanical Properties of Half-Hard Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm.

Nominal thickness—0.040 in.

Page 76: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

94 GOHN, GTTERARD, AND FREYNIK ON PHOSPHOR BRONZE

Tin, Per Cent

FIG. 75.—Mechanical Properties of Hard Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent

Nominal ready-to-finish gram size—0.035 mm.Nominal thickness—0.040 in.

Page 77: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 95

Tin, Per Cent

FIG. 76.—Mechanical Properties of Hard Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent

Nominal ready-to-finish grain size—0.015 mm.Nominal thickness—0.040 in.

Page 78: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

96 GOHN, GTJERARD, AND FREYNIK ON PHOSPHOR BRONZE

Tin, Per Cent

FIG. 77.—Mechanical Properties of Extra-Hard Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent

Nominal ready-to-finish grain size—0.035 mm.Nominal thickness—0.040 in.

Page 79: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

97

Tin, Per CentFIG. 78.—Mechanical Properties of Extra-Hard Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish gram size—0.015 mm.

Nominal thickness—0.040 in'.

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Page 80: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

98 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Tin, Per CentFIG. 79.—Mechanical Properties of Spring Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.035 mm.

Nominal thickness—0.040 in.

Page 81: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Tin. Per CentFIG. 80.—Mechanical Properties of Spring Phosphor Bronze Strip.

Nominal phosphorus content—0.05 per centNominal ready-to-finish grain size—0.015 mm.

Nominal thickness—0.040 in.

99

Page 82: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

100 GOHN. GUERARD. AND FREYNIK ON PHOSPHOR BRONZE

Tin, Per Cent

FIG. 81.—Mechanical Properties of Extra-Spring Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent

Nominal ready-to-finish grain size—0.035 mm.Nominal thickness—0.040 in.

Page 83: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GTJERARD, AND FBEYNIK ON PHOSPHOR BRONZE

Tin, Per Ctrrt

FIG. 82.—Mechanical Properties of Extra-Spring Phosphor Bronze Strip.Nominal phosphorus content—0.05 per cent

Nominal ready-to-finish grain size—0.015 mm.Nominal thickness—0.040 in.

101

Page 84: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Reduction by Cold-Rolling,Per Cent

FIG. 83.—Effect of Phosphorus Content on the Mechanical Properties of 3 per cent Tin PhosphorBronze Strip.

GOHN, GUERARD, AND PREYNIK ON PHOSPHOR BRONZE102

Nominal ready-to-finish grain size—0.035 mm.Nominal thickness—0.040 in.

Nominal phosphorus content [0.05 per cent,[0.40 per cent,

Page 85: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 103

Reduction by Cold-Rolling, Per Cent

FIG. 84.—Effect of Phosphorus Content on the Mechanical Properties of 4 per cent Tin PhosphorBronze Strip.

Nominal ready-to-finish grain size—0.035 mm.Nominal thickness—0.040 in.

Nominal phosphorus content 0.40 per cent.00.06 per cent

Page 86: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

104 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per Cent

FIG. 85.—Effect of Phosphorus Content on the Mechanical Properties of 5 per cent Tin PhosphorBronze Strip.

Nominal ready-to-finish grain size—0.035 mm.Nominal thickness—0.040 in.

Nominal phosphorus content (0.05 per cent,0.40 per cent,

Page 87: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 105

Reduction by Cold-Rolling, Per Cent

FIG. 86.—Effect of Grain Size on the Mechanical Properties of Electrolytic Tough Pitch CopperStrip.

Nominal ready-to-finish grain size—0.030 mm.Nominal thickness—0.040 in.

0.015 mm,

Page 88: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Reduction by Cold-Rolling, Per Cent

FIG. 87.—Effect of Grain Size on the Mechanical Properties of 0.5 per cent Tin Phosphor BronzeStrip.

106 GOHN. GTJERARD. AND FREYNIK ON PHOSPHOR BRONZE

Nominal phosphorus content—0.05 per centNominal thickness—0.040 in.

Nominal ready-to-finish grain size 0.035 mm,0.015 mm,

Page 89: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 107

Reduction by Cold-Rolling, Per CentFIG. 88.—Effect of Grain Size on the Mechanical Properties of 1 per cent Tin Phosphor Bronze

Strip.Nominal phosphorous content—0.05 per cent.

Nominal thickness—0.040 in.

Nominal ready-to-finish grain size 0.035 mm,0.015 mm,

Page 90: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

Reduction by Cold-Rolling, Per CentFIG. 89.—Effect of Grain Size on the Mechanical Properties of 2 per cent Tin Phosphor Bronze

Strip.

108 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Nominal phosphorous content—0.05 per cent.Nominal thickness—0.040 in.

Nominal ready-to-finish grain size 10.035 mm,[0.015 mm,

Page 91: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZ

Reduction by Cold-Rolling,Per Cent

FIG. 90.—Effect of Grain Size on the Mechanical Properties of 3 per cent Tin Phosphor BronzeStrip.

Nominal phosphorous content—0.05 per cent.Nominal thickness—0.040 in.

Nominal ready-to-finish grain size 10.035 mm,L0.015 mm,

109

Page 92: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

110 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per Cent

FIG. 91.—Effect of Grain Size on the Mechanical Properties of 4 per cent Tin Phosphor BronzeStrip.

Nominal phosphorous content—0.05 per cent.Nominal thickness—0.040 in.

Nominal ready-to-finish grain size 0.035 mm,0.015 mm,

Page 93: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNJK ON PHOSPHOR BRONZE 111

Reduction by Cold-Rolling, Per Cent

FIG. 92.—Effect of Grain Size on the Mechanical Properties of 5 per cent Tin Phosphor BronzeStrip.

Nominal phosphorous content—0.05 per cent.Nominal thickness—0.040 in.

Nominal ready-to-finish grain size 0.036 mm,0.015 mm,

Page 94: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

112 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling, Per CentFIG. 93.—Effect of Grain Size on the Mechanical Properties of 8 per cent Tin Phosphor Bronze

Strip.Nominal phosphorous content—0.05 per cent.

Nominal thickness—0.040 in.Nominal ready-to-finish grain size 10.035 mm,

10.015 mm,

Page 95: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE 113

Reduction by Cold-Rolling, Per CentFIG. 94.—Effect of Grain Size on the Mechanical Properties of 10 per cent Tin Phosphor Bronze

Strip.Nominal phosphorus content—0.05 per cent.

Nominal thickness—0.040 in.

Nominal ready-to-finish grain size 10.035 mm,10.010 mm,

Page 96: STP183 EB/Jan. 1956 - ASTM International · GOHN , GUERARD AND FREYNIK ON PHOSPHOR BRONZE Reduction by Cold-Rolling, Per Cent FIG. 19.—Mechanical Properties of 3 per cent Tin Phosphor

114 GOHN, GUERARD, AND FREYNIK ON PHOSPHOR BRONZE

Reduction by Cold-Rolling,Per CentFIG. 95.—Effect of Grain Size on the Mechanical Properties of 4 per cent Tin Phosphor Bronze

Strip.Nominal phosphorus content—0.40 per cent.

Nominal thickness, 0.040 in.Nominal ready-to-finish grain size 0.035 mm,

0.075 mm,