synthesis and characterization of air-stable elemental fe...

7
Journal of Surface Engineered Materials and Advanced Technology, 2013, 3, 217-223 http://dx.doi.org/10.4236/jsemat.2013.33029 Published Online July 2013 (http://www.scirp.org/journal/jsemat) 217 Synthesis and Characterization of Air-Stable Elemental Fe Thin Films by Chemical Vapor Deposition of Fe 3 (CO) 12 On Mero, Nava Shpaisman, Judith Grinblat, Shlomo Margel * Institute of Nanotechnology and Advanced Materials, Department of Chemistry, Bar-Ilan University, Ramat-Gan, Israel. Email: * [email protected] Received May 7 th , 2013; revised June 7 th , 2013; accepted June 29 th , 2013 Copyright © 2013 On Mero et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. ABSTRACT New magnetic air-stable nanogranular Fe thin films of 10 ± 1.2 nm thickness were prepared onto silicon wafers at 150˚C under inert atmosphere by controlled Chemical Vapor Deposition (CVD) of triiron dodecacarbonyl (Fe 3 (CO) 12 ). These thin films, composed of sintered elemental Fe nanoparticles of 4.1 ± 0.7 nm diameter, are protected from air oxi- dation by a very thin carbon layer. The saturation magnetization of these thin Fe coatings was found to be close to that of bulk iron. The electrical resistivity behavior of the ferromagnetic thin films is similar to that of a semiconductor. In the present manuscript, these Fe thin coatings on Si wafers have been used as a catalyst for synthesizing crystalline carbon nanotubes (CNTs), by CVD using ethylene as a carbon precursor. Keywords: Magnetic Conductive Thin Coatings; Thin Fe Films; Nanogranular Magnetic Thin Films; Magnetic Coatings; Fe 3 (CO) 12 ; CNTs 1. Introduction Chemical Vapor Deposition (CVD) is a common techni- que for synthesizing thin coatings. This technique is based on the deposition of vapor of a desired material as thin films on a substrate surface. The process is usually performed in a controlled atmosphere (CVD) to avoid the interaction between the vapor and air [1,2]. In CVD, the material to be deposited is introduced as a precursor gas and then, still in the vapor phase, conformally coats the substrate surface [3,4]. Nanogranular magnetic films are composed of magne- tic nanoparticles embedded in a non-magnetic isolating matrix such as SiO 2 , Si 3 N 4 , Al 2 O 3 , BN, C, etc. [5,6]. These magnetic films exhibit improved properties such as oxidation resistance, corrosion resistance and wear resistance. Elemental iron is the most useful ferromag- netic element for electromagnetic interference and radio frequency interference magnetic shielding applications. It is significantly cheaper than other ferromagnetic materi- als, it has the highest magnetic moment at room tem- perature, a high Curie temperature and a fairly low coer- civity [7,8] In addition, iron is a commonly available element, and therefore significantly cheaper than other ferromagnetic materials. Fe thin films are easily oxidized by air and therefore significantly lose their high magnetic moment. To prevent these phenomena, previous publica- tions already illustrated that the elemental Fe should be protected by a passivation layer such as carbon [9], silica [10], and alumina [11]. Thin films of transition metals are often used for the synthesis of carbon nanotubes (CNTs) [12]. In addition to their very high aspect ratio, their potential for chemi- cal functionalization, and their characteristic electrical, mechanical, and thermal properties, CNTs have many applications including electronic devices (e.g., CNTs- based field effect transistors, interconnects for micro- processors, etc.), [13] electrodes for batteries [14,15] and supercapacitors [16], reinforced composites [17], etc. [18,19]. Typical catalysts widely employed in CNTs synthesis include transition metals, and more often fer- romagnetic metals such as Co, Fe and Ni [20,21]. In the present study, the synthesis and characterization of new nanogranular Fe/C magnetic conductive thin coa- tings on Si wafers, by CVD of Fe 3 (CO) 12 at low tempe- rature under inert atmosphere, are described. These films are composed of sintered elemental Fe nanoparticles pro- tected from air oxidation by a very thin layer of carbon. Since the carbon concentration in these coatings is rela- tively low (<3%), we will refer to these coatings as “Fe coatings”. The potential use of these Fe coatings as cata- * Corresponding author. Copyright © 2013 SciRes. JSEMAT

Upload: truongliem

Post on 26-Jun-2018

223 views

Category:

Documents


0 download

TRANSCRIPT

Journal of Surface Engineered Materials and Advanced Technology, 2013, 3, 217-223 http://dx.doi.org/10.4236/jsemat.2013.33029 Published Online July 2013 (http://www.scirp.org/journal/jsemat)

217

Synthesis and Characterization of Air-Stable Elemental Fe Thin Films by Chemical Vapor Deposition of Fe3(CO)12

On Mero, Nava Shpaisman, Judith Grinblat, Shlomo Margel*

Institute of Nanotechnology and Advanced Materials, Department of Chemistry, Bar-Ilan University, Ramat-Gan, Israel. Email: *[email protected] Received May 7th, 2013; revised June 7th, 2013; accepted June 29th, 2013 Copyright © 2013 On Mero et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

ABSTRACT

New magnetic air-stable nanogranular Fe thin films of 10 ± 1.2 nm thickness were prepared onto silicon wafers at 150˚C under inert atmosphere by controlled Chemical Vapor Deposition (CVD) of triiron dodecacarbonyl (Fe3(CO)12). These thin films, composed of sintered elemental Fe nanoparticles of 4.1 ± 0.7 nm diameter, are protected from air oxi- dation by a very thin carbon layer. The saturation magnetization of these thin Fe coatings was found to be close to that of bulk iron. The electrical resistivity behavior of the ferromagnetic thin films is similar to that of a semiconductor. In the present manuscript, these Fe thin coatings on Si wafers have been used as a catalyst for synthesizing crystalline carbon nanotubes (CNTs), by CVD using ethylene as a carbon precursor. Keywords: Magnetic Conductive Thin Coatings; Thin Fe Films; Nanogranular Magnetic Thin Films; Magnetic

Coatings; Fe3(CO)12; CNTs

1. Introduction

Chemical Vapor Deposition (CVD) is a common techni- que for synthesizing thin coatings. This technique is based on the deposition of vapor of a desired material as thin films on a substrate surface. The process is usually performed in a controlled atmosphere (CVD) to avoid the interaction between the vapor and air [1,2]. In CVD, the material to be deposited is introduced as a precursor gas and then, still in the vapor phase, conformally coats the substrate surface [3,4].

Nanogranular magnetic films are composed of magne- tic nanoparticles embedded in a non-magnetic isolating matrix such as SiO2, Si3N4, Al2O3, BN, C, etc. [5,6]. These magnetic films exhibit improved properties such as oxidation resistance, corrosion resistance and wear resistance. Elemental iron is the most useful ferromag- netic element for electromagnetic interference and radio frequency interference magnetic shielding applications. It is significantly cheaper than other ferromagnetic materi- als, it has the highest magnetic moment at room tem- perature, a high Curie temperature and a fairly low coer- civity [7,8] In addition, iron is a commonly available element, and therefore significantly cheaper than other ferromagnetic materials. Fe thin films are easily oxidized

by air and therefore significantly lose their high magnetic moment. To prevent these phenomena, previous publica- tions already illustrated that the elemental Fe should be protected by a passivation layer such as carbon [9], silica [10], and alumina [11].

Thin films of transition metals are often used for the synthesis of carbon nanotubes (CNTs) [12]. In addition to their very high aspect ratio, their potential for chemi- cal functionalization, and their characteristic electrical, mechanical, and thermal properties, CNTs have many applications including electronic devices (e.g., CNTs- based field effect transistors, interconnects for micro- processors, etc.), [13] electrodes for batteries [14,15] and supercapacitors [16], reinforced composites [17], etc. [18,19]. Typical catalysts widely employed in CNTs synthesis include transition metals, and more often fer- romagnetic metals such as Co, Fe and Ni [20,21].

In the present study, the synthesis and characterization of new nanogranular Fe/C magnetic conductive thin coa- tings on Si wafers, by CVD of Fe3(CO)12 at low tempe- rature under inert atmosphere, are described. These films are composed of sintered elemental Fe nanoparticles pro- tected from air oxidation by a very thin layer of carbon. Since the carbon concentration in these coatings is rela- tively low (<3%), we will refer to these coatings as “Fe coatings”. The potential use of these Fe coatings as cata- *Corresponding author.

Copyright © 2013 SciRes. JSEMAT

Synthesis and Characterization of Air-Stable Elemental Fe Thin Films by Chemical Vapor Deposition of Fe3(CO)12 218

lysts for synthesizing CNTs has also been demonstrated.

2. Experimental Section

2.1. Materials

The following substrates and analytical-grade chemicals were purchased from a commercial source and were used without further purification: cover glass slides, ethanol and Fe3(CO)12 protected by 1% - 10% methyl alcohol from Aldrich (Israel); P type, boron doped Si wafers with <100> orientation from Si-Mat, Israel; Ultra-high purity precursor gases (99.99999): ethylene, nitrogen, argon, hydrogen and a mixture of argon with 1% oxygen (Ar-O2) were purchased from Maxima Air Separation Center Ltd., Israel. Alumina (Al2O3)-coated Si wafers were prepared at the Hebrew University, Jerusalem, Israel, by e-beam evaporation of 10 nm interlayer of alumina on Si wafers. Water was purified by passing deionized water through an Elga stat Spectrum reverse osmosis system (Elga Ltd., High Wycombe, UK).

2.2. Fabrication of the Nanogranular Fe Thin Films

Si wafers where cut into 7 × 7 mm2 samples, cleaned by sequential soaking in baths of ethanol, distilled water and again ethanol, and then dried with an N2 gas flow. The thin film fabrication system is composed of a 90 cm long quartz tube furnace with an inside diameter of 35 mm and a 10 cm heating zone sealed by two glass connectors (one in each side of the quartz tube) which allow a gas flow of the inert gas from the gas canister. A brass cruci- ble with three 7 mm3 wells was positioned under the heating zone in the middle of the quartz tube. Prior to the thin film fabrication, 0.00317 mmol of Fe3(CO)12 pre- cursor was added to the bottom of each of the three 7 mm3 wells in the crucible, and three 7 mm2 Si wafers or carbon coated copper grids (TEM grids) were placed horizontally at the top of the wells. The crucible was then pushed into the middle of the quartz tube and kept under Ar atmosphere in the tube furnace. The temperature of the quartz tube was then raised to 150˚C at a rate of 10˚C /min and then maintained at 150˚C for 1 min. The pre- cursor vapors were deposited on the heated (150˚C) sub- strates and decomposed to produce the Fe thin films of 10 ± 1.2 nm thickness on the substrates.

Synthesis of the Fe thin films for the XRD measure- ments were performed similarly, substituting the Si wafers for glass wafers, Synthesis of the Fe thin films for the elec- trical resistance measurements and for the CNTs growth were performed similarly, substituting the Si wafers for alumina-coated Si wafers [22].

2.3. Fabrication of the CNTs

CNTs were grown on the Fe films by a CVD process

with ethylene as a precursor gas, according to the litera- ture [23]. Briefly, the CVD system used was composed of two one-zone tube furnaces (Lindberg Blue) with a quartz tube with external diameter of 25 mm and MKS mass flow controllers. The Fe-alumina coated Si wafers were placed in a crucible in the heating zone at the bot- tom of the quartz tube. The preheating temperature in the first furnace was set at 770˚C and the growth temperature in the second furnace was set at 750˚C. The process con- sisted of a 15-min annealing step with flows of Ar (100 [sccm]) and H2 (400 [sccm]) followed by 15-minute growth step with the additional flows of Ar-O2 (100 [sccm]) and C2H4 (200 [sccm]) [23]. At the end of the growth step, the Ar-O2 and C2H4 flows were stopped, a min. later the H2 flow was stopped, and after another min. the quartz tube was pushed out from the furnace and the sample was cooled down to room temperature under Ar flow.

2.4. Characterization

The structure of the Fe thin films and the CNTs growth were investigated by High Resolution Transmission Electron Microscope, HRTEM, (JEOL JEM-2100 (LaB6) at 200 kV). The HRTEM is integrated with a digital Scanning device (STEM) comprising of annular Dark- Field (DF) and Bright-Field (BF) detectors and a Thermo Scientific energy-dispersive X-ray spectrometer (EDS) system for elemental analysis. TEM observations were made by taking BF images, HRTEM images and selected area electron diffraction (SAED) patterns. Fourier Trans- form Analysis (FFT) of high resolution images technique was used for structural analysis of the Fe thin films. Scanning and mapping were performed in STEM mode and the elemental analysis was performed using the EDS system equipped with the Noran System Six software.

Specimens for observation in the HRTEM were pre- pared in three ways: 1) TEM lamella samples of the Fe thin films on Si wafers were fabricated through the Fo- cused Ion Beam (FIB) FEI Helios 600 system. In this process, the region of interest is first covered with Pt to protect the Fe thin coatings from damage caused by the FIB milling process. Then, several adjacent holes of the film were milled by a gallium ion beam. Subsequently the lamella was lifted-up by a micromanipulator and glued on the TEM grid where the final thinning takes place; 2) Direct deposition of the Fe films on a standard carbon TEM support; 3) Scraping CNTs from the alu- mina-coated Si wafers into isopropanol and then putting one drop on the carbon TEM grids for characterization.

Surface elemental analysis was obtained by X-ray Photoelectron Spectroscopy (XPS; model AXIS-HS, Kratos Analytical, England) using Al Kα lines, at 10- 9Torr, with a take-off angle of 90˚. Powder X-Ray Dif- fraction (XRD) patterns were recorded using an X-ray

Copyright © 2013 SciRes. JSEMAT

Synthesis and Characterization of Air-Stable Elemental Fe Thin Films by Chemical Vapor Deposition of Fe3(CO)12 219

diffractometer (model D8 Advance, Bruker AXS) with Cu Ka radiation source filtered with a graphite mono- chromator (λ = 1.5406 A). Measurements were per- formed at a temperature of 298 K, the X-ray beam was generated at 40 kV and 40 mA power and a 0.050˚ step- width with a 36 s counting time for each step where ap- plied. Isothermal magnetization measurements at room temperature were performed in a commercial (Quantum Design) Superconducting Quantum Interference Device (SQUID) magnetometer. Mössbauer Spectroscopy (MS) studies were performed using a conventional constant acceleration drive and a 50 m Ci 57 Co:Rh source. The velocity calibration was performed at room temperature- Fe absorber, and the isomer shifts (I.S.). I.S values re- ported are relative to that of iron. The observed spectra were least-square fitted by theoretical spectra, assuming a distribution of hyperfine interaction parameters, corre- sponding to non-equivalent iron locations differing in lo- cal environment. Electrical resistance characterization as function of temperature was performed in quantum de- sign PPMS (Physical Property Measurement System). Four silver-paint contacts were used in all the electrical resistance measurements. The electrical resistance ex- periments were done by applying 5 μA current through the magnetic films; the temperature was raised at a rate of 6 K/min from 4 to 373 K. The samples were placed near to a standard Pt thermometer which monitored the temperature increase and measured voltage from a volt- meter was translated to the samples’ electrical resistance.

3. Results and Discussion

HRTEM cross section image prepared by the FIB tech- nique as described in the experimental part was used for characterization of the Fe thin films deposited on Si wa- fers. Figure 1A shows a typical Fe film image of 10 ± 1.2 nm thickness deposited on a Si wafer.

The Pt on top of the film is due to the FIB lamella preparation process as described in the experimental part. Figure 1B is the high-resolution image of the Fe nanopar- ticles that make up the Fe film (taken from an area of Figure 1A). It is clearly seen that this film is composed of a few layers of sintered Fe nanoparticles of 4.1 ± 0.7 nm

Figure 1. Cross-sectional TEM micrograph of a typical Fe thin film of 10 ± 1.2 nm thickness on a Si wafer (A). Image B is a HRTEM micrograph of image A and image C is a STEM image of the cross-section showing the iron’s line scan in the blue curve.

diameter. Figure 1C illustrates STEM image of the line scan profile for the elemental Fe (blue). It is clearly shown that the peak in the blue curve is located at the same region as marked for Fe in images A and B.

A typical XRD pattern of these films, as shown in Figure 2 exhibits peaks at 2 and 2 = 65.6 (200) corre- sponding to the cubic bcc crystalline metallic Fe struc- ture (MW = 55.85 g/mol, S.G: Im-3m, Z = 2, a = 2.86 Å). The Fe composition and crystallinity of the Fe films were ferther investigated by Mössbauer Spectroscopy (MS). Figure 3 presents the MS of a typical Fe thin film of 10 ± 1.2 nm thickness on a Si wafer. This figure shows typi- cal sextets with hyperfine parameters.

The hyperfine parameters deduced for the major sub- spectrum (67%) are I.S = 0 mm/s and Heff = 330 kOe. The distance between the two extreme peaks of the sextet is 10.5 mm/s, indicating pure metallic Fe. The thin film MS spectrum is composed of magnetically ordered and unordered nanoparticles; at room temperature, the sextet is associated with magnetically ordered (crystalline) par- ticles (67%) while the main broad peak is associated with magnetically unordered (non-crystalline) particles (33%). Similar MS spectra were also observed for the other Fe coatings, regardless of their thickness.

Figure 2. A typical XRD pattern of the Fe thin film.

Figure 3. Mössbauer spectrum at room temperature of a ty- pical Fe thin film on a Si wafer.

Copyright © 2013 SciRes. JSEMAT

Synthesis and Characterization of Air-Stable Elemental Fe Thin Films by Chemical Vapor Deposition of Fe3(CO)12 220

Table 1 lists the surface elemental composition of these Fe films as measured by XPS. These XPS meas- urements show that the films’ surface is mostly com- posed of carbon (63.9% C, 6.5% Fe and 29.6% O), in contrast to their weight percent in the Fe3(CO)12 precur- sor: 28.4% C, 37.8% O and 33.8% Fe. Overall, the XPS reflected electron beam decays as the x-ray beam pene- trates deeper into the matter, hence the high surface con- centration of C and low surface concentration of Fe to- gether with the XRD results indicate that most of the carbon of the Fe films is concentrated in the outer layer of the magnetic film, thereby preventing the Fe content of the coatings from oxidizing in air. The surface content of O (29.6%) as shown in Table 1 is probably related to oxidized Fe and C. High resolution XPS measurements, as shown in Table 2, indeed indicate that the carbon frac- tion of the most outer surface is composed of 76% C-C bonds and 24% of ether, carbonyl and carboxyl groups.

The magnetic properties of these Fe films coated on Si wafers were measured by the SQUID magnetometer at room temperature. Figure 4 represents the field depend- ence of the magnetization measured at 300 K of a typical Fe coating of 10 ± 1.2 nm thickness on a Si wafer. This

Table 1. Surface elemental composition of a typical Fe thin film as measured by XPS.

Weight %

[O] [C] [Fe] Composition

29.6 63.9 6.5 Surface

Table 2. Surface carbon functional groups analysis of a typical Fe thin film as measured by high resolution XPS.

Weight %

COO C = O C-O C-C Carbon bond type

76.0 Surface composition 10.4 9.1 4.5

Figure 4. A magnetization curve of a typical Fe thin film.

figure shows a ferromagnetic-type curve as indicated by the existence of the hysteresis loop. The saturation mag- netization (MS) and coerecivity values obtained at 300 K were 1657 emu/cm3 and 375 Oe. The MS bulk value of zero-valent Fe is 1734 emu/cm3 while that of bulk mag- netite is 480 emu/cm3 [24,25]. The Ms value of this film is slightly lower than that of bulk elemental Fe probably due to the carbon and oxidized Fe existing on the surface of these films, as illustrated in Table 1 by XPS meas- urements.

The nanostructure and composition of the Fe thin films were investigated by HRTEM microscopy. Figure 5 pre- sents a typical HRTEM photomicrograph of 2 μm2 area of a typical Fe thin film deposited on a carbon grid. The figure displays the well-resolved lattice-fringe contrast of the crystalline nanoparticles and their identification was based on the analysis of this high resolution image. Insert A (Figure 5) is the computed FFT of the portion of the image outlined by the white square. In this figure it is possible to identify unambiguously elemental Fe crystal- line nanoparticles. This insert presents sets of reflections that can be assigned to the d 110 family of planes of the above mentioned Fe BCC structure. Insert B (Figure 5) demonstrates the filtered and magnified portion of the image outlined by the white square and shows the lattice fringes d110 = 0.2 nm of the cubic Fe BCC structure (a = 2.86 Å). Some clear and individual Fe nanoparticles dis- playing only the lattices of the d 110 plane can be dis- cerned, as emphasized in the image, the existence of a non-crystalline matrix between nanoparticles defines them in Figure 5. HRTEM investigation of this film also revealed a very small and undefined portion of Fe3O4 phase, the distances measured between lattice fringes were 0.25 nm (d 222) and 0.26 nm (d 113) of the cubic

Figure 5. HRTEM of a 2 μm2 area of a typical Fe thin film deposited on a carbon grid. Insert A is the Fourier trans- form taken from the area marked by the white square showing sets of reflections matching the structure of ele- mental Fe. Inset B is the filtered and magnified image of the area marked by the white square, displaying the lattice fringes for elemental Fe.

Copyright © 2013 SciRes. JSEMAT

Synthesis and Characterization of Air-Stable Elemental Fe Thin Films by Chemical Vapor Deposition of Fe3(CO)12 221

Fe3O4 FCC structure (a = 8.35 Å), Utilization of these ad- vanced nano-techniques, together with the XRD results provided unambiguous evidence that the thin films de- scribed in this study are composed of nanoparticles of elemental Fe (BCC structure unit cell parameter a = 2.86 Å). As the XRD measurements show only the presence of Fe, it can be concluded safely that the nano-regions of Fe3O4 found in these electron microscopy studies, are the result of bare Fe oxidation found on the most outer sur-face layer of the thin film when exposed to air.

Results showing that the films are composed mainly of elemental Fe have led us to the assumption that these films can be used as electric conductors. Figure 6 de- monstrates the electrical resistivity behavior of a typical Fe thin film as function of temperature (I = 5 µA) at a rate of 6 K/min from 4 to 373 K.

The measured electrical resistivity of the alumina- coated Si wafers before the Fe coating process was sev- eral K'Ώs at all the measured temperatures. This result confirms that all resistivity results were not obtained from a substrate conduction leakage. Figure 6 exhibits that the resistance of the Fe film decreased as the tem- perature increased, e.g., 1289 Ω at 38 K and 30 Ω at room temperature. This behavior resembles that of a se- miconductor and can be correlated with the mixed crys-talline and non-crystalline structure of the Fe films, which acts as an obstacle to electron flow at low tem-peratures [26]. Another interesting feature is observed at low temperatures wherein these 10 ± 1.2 nm thin films do not conduct in the region of T ≤ 37 K (R = ∞ Ω). This phenomenon is probably related to the 2D structure of the 10 ± 1.2 nm film as shown in Figure 1 [27,28]. This can be explained by the temperature-dependent evolution of the band gap and density of electron states in systems containing a low number of atoms such as two dimen-sional structures similarly to our thin film [29]. In 2-di- mensional systems where nanocrystalline particles have distinct shapes and edges, the electron density of states is

Figure 6. Electric resistance of a typical Fe thin film as a function of temperature.

localized below a critical energy (EC) also known as the “mobility edge”, separateing localized and delocalized states. EC, in the 10 ± 1.2 nm Fe thin film, occurs at T = 37 K, hence, below this temperature R = ∞ Ω, while above this temperature the electrons can overcome the non-crystalline, non-conducting matrix/nanoparticles and undergo tunneling between crystalline nanoparticles [26], This result is also consistent with the Mössbauer result which showed 33% of non crystalline iron. This electric resistivity result in addition to the magnetization, XRD and Mössbauer measurements where repeated on the same films during 12 months and shown no significant change in the magnetic and electrical films properties. Typical catalysts widely employed in CNTs synthesis include transition metals, and often ferromagnetic metals such as Co, Fe and Ni [20,21]. Preliminary study indeed indicated that our Fe thin films can be used as precursors for synthesizing multi-wall CNTs (MWCNTs), as shown in Figure 7. The CNTs’ length was impossible to meas-ure as they were not vertically aligned. The diameter, walls and length of the CNTs depend extensively on the film characteristics, the unique properties of the pre-sented film and especially the condensed nanoparticle structure of the films.

4. Conclusion

This work demonstrates a simple CVD process for the fabrication of 10 ± 1.2 nm conductive magnetic Fe thin coatings on Si wafers. The films produced in this method show the metallic properties of the precursor’s metal and are composed of Fe nanoparticles condensed together and protected from oxidation by a very thin carbon layer. The preliminary potential use of these films as a catalyst for CNT growth has been illustrated. Further improve- ments of the Fe thin coating process, e.g., films of con- trolled thicknesses, and the formation of improved CNTs are planned for future investigation.

Figure 7. Typical HRTEM images of MWCNTs grown on the Fe thin coating on alumina-coated Si wafers. For the HRTEM pictures, the Fe coating containing the CNTs was scraped from the alumina-coated Si wafer and deposited onto the TEM carbon grid.

Copyright © 2013 SciRes. JSEMAT

Synthesis and Characterization of Air-Stable Elemental Fe Thin Films by Chemical Vapor Deposition of Fe3(CO)12 222

5. Acknowledgements

This study was partially supported by a Minerva grant (microscale and nanoscale articles and thin films for medical applications). We thank to Dr. Tomer Zimerin for helping in the preparation of the CNTs.

REFERENCES [1] I. Corrales-Mendoza, A. Conde-Gallardo and V. M. San-

chez-Resendiz, “Nd(1-x)Fe(x)OF Thin Films Deposited by Chemical Vapor Deposition and Their Arsenic Diffu- sion,” IEEE Transactions on Applied Superconductivity, Vol. 21, No. 3, 2011, pp. 2849-2852. doi:10.1109/TASC.2010.2084983

[2] M. L. Hitchman and K. F. Jensen, “Chemical Vapor De- position, in: Principles and Applications,” Academic Press, London, San Diego, 1993, p. 677.

[3] Y. H. Low, M. F. Bain, D. C. S. Bien, J. H. Montgomery, B. M. Armstrong and H. S. Gamble, “Selective Deposi- tion of CVD Iron on Silicon Dioxide and Tungsten,” Mi- croelectronic Engineering, Vol. 83, No. 11-12, 2006, pp. 2229-2233. doi:10.1016/j.mee.2006.10.008

[4] Q. P. Wei, Z. M. Yu, M. N. R. Ashfold, Z. Chen, L. Wang and L. Ma, “Effects of Thickness and Cycle Pa- rameters on Fretting Wear Behavior of CVD Diamond Coatings on Steel Substrates,” Surface & Coatings Tech-nology, Vol. 205, No. 1, 2010, pp. 158-167. doi:10.1016/j.surfcoat.2010.06.026

[5] Z. W. Liu and C. K. Ong, “Microstructure and Thickness Dependent Magnetic Properties of Nanogranular Co-Zn- O Thin Films FOr Microwave Applications,” Journal of Alloys and Compounds, Vol. 509, No. 41, 2011, pp. 10075- 10079. doi:10.1016/j.jallcom.2011.08.039

[6] S. F. Zhang and P. M. Levy, “Conductivity and Magne- toresistance in Magnetic Granular Films,” Journal of Ap- plied Physics, Vol. 73, No. 10, 1993, pp. 5315-5319. doi:10.1063/1.353766

[7] F. S. Hung, F. Y. Hung and C. M. Chiang, “Crystalliza- tion and Annealing Effects of Sputtered tin Alloy Films on Electromagnetic Interference Shielding,” Applied Sur- face Science, Vol. 257, No. 8, 2011, pp. 3733-3738. doi:10.1016/j.apsusc.2010.11.126

[8] S. S. Azim, A. Satheesh, K. K. Ramu, S. Ramu and G. Venkatachari, “Studies on Graphite Based Conductive Paint Coatings,” Progress in Organic Coatings, Vol. 55, No. 1, 2006, pp. 1-4. doi:10.1016/j.porgcoat.2005.09.001

[9] E. Sutter, p. Albrecht, F. E. Camino and P. Sutter, “Mono- layer Graphene as Ultimate Chemical Passivation Layer for Arbitrarily Shaped Metal Surfaces,” Carbone, Vol. 48, No. 15, 2010, pp. 4414-4420. doi:10.1016/j.carbon.2010.07.058

[10] Y. Wang, H. Gao, R. Yeredla, H. Xu and M. Abrecht, “Preparation of Iron Particles Coated with Silica,” Jour- nal of Colloid and Interface Science, Vol. 217, No. 1, 1999, pp. 203-207.

[11] F. Jay, V. Gauthier and S. Dubois, “Iron Particles Coated with Alumina: Synthesis by a Mechanofusion Process and

Study of the High-Temperature Oxidation Resistance,” Journal of the American Ceramic Society, Vol. 89, No. 11, 2006, pp. 3522-3528.

[12] M. Gaillard, C. Boulmer-leborgne, N. Semmar and E. Millon, A. Petit, “Carbon Nanotube Growth from Metal- lic Nanoparticles Deposited by Pulsed-Laser Deposition on Different Substrates,” Applied Surface Science, Vol. 258, No. 23, 2012, p. 9237. doi:10.1016/j.apsusc.2011.12.115

[13] P. Avouris, J. Appenzeller, R. Martel and S. J. Wind, “Carbon Nanotube Electronics,” Proceedings of the IEEE, Vol. 91, No. 11, 2003, pp. 1772-1784. doi:10.1109/JPROC.2003.818338

[14] B. J. Landi, M. J. Ganter, C. D. Cress, R. A. DiLeo and R. P. Raffaelle, “Carbon Nanotubes for Lithium Ion Batteries,” Energy & Environmental Science, Vol. 2, No. 6, 2009, pp. 638-654. doi:10.1039/b904116h

[15] B. L. Ellis, K. T. Lee and L. F. Nazar, “Positive Electrode Materials for Li-Ion and Li-Batteries,” Chemistry of Ma- terials, Vol. 22, No. 3, 2010, pp. 691-714. doi:10.1021/cm902696j

[16] M. Inagaki, H. Konno and O. Tanaike, “Carbon Materials for Electrochemical Capacitors,” Journal of Power Sources, Vol. 195, No. 24, 2010, pp. 7880-7903. doi:10.1016/j.jpowsour.2010.06.036

[17] J. N. Coleman, U. Khan, W. J. Blau and Y. K. Gun’ko, “Small But Strong: A Review of the Mechanical Pro- perties of Carbon Nanotube-Polymer Composites,” Car- bon, Vol. 44, No. 9, 2006, pp. 1624-1652. doi:10.1016/j.carbon.2006.02.038

[18] V. N. Popov, “Carbon Nanotubes: Properties and Appli- cation,” Materials Science & Engineering R-Reports, Vol. 43, No. 3, 2004, pp. 61-102. doi:10.1016/j.mser.2003.10.001

[19] M. Paradise and T. Goswami, “Carbon Nanotubes—Pro- duction and Industrial Applications,” Materials & Design, Vol. 28, No. 5, 2007, pp. 1477-1489. doi:10.1016/j.matdes.2006.03.008

[20] A. M. Cassell, J. A. Raymakers, J. Kong, H. J. Dai, “Large Scale CVD Synthesis of Single-Walled Carbon Nanotubes,” Journal of Physical Chemistry B, Vol. 103, No. 31, 1999, pp. 6484-6492. doi:10.1021/jp990957s

[21] P. Chen, H. B. Zhang, G. D. Lin, Q. Hong and K. R. Tsai, “Growth of Carbon Nanotubes by Catalytic Decomposi- tion of CH4 or CO on a Ni-MgO Catalyst,” Carbon, Vol. 35, No. 10-11, 1997, pp. 1495-1501. doi:10.1016/S0008-6223(97)00100-0

[22] T. de los Arcos, F. Vonau, M. G. Garnier, V. Thommen, H. G. Boyen, P. Oelhafen, M. Duggelin, D. Mathis and R. Guggenheim, “Influence of Iron-Silicon Interaction on the Growth of Carbon Nanotubes Produced by Chemical Vapor Deposition,” Applied Physics Letters, Vol. 80, No. 13, 2002, pp. 2383-2385. doi:10.1063/1.1465529

[23] G. D. Nessim, A. Al-Obeidi, H. Grisaru, E. S. Polsen, C. R. Oliver, T. Zimrin, A. J. Hart, D. Aurbach and C. V. Thompson, “Synthesis of Tall Carpets of Vertically Aligned Carbon Nanotubes by In-Situ Generation Of Wa- ter Vapor through Preheating of Added Oxygen,” Carbon,

Copyright © 2013 SciRes. JSEMAT

Synthesis and Characterization of Air-Stable Elemental Fe Thin Films by Chemical Vapor Deposition of Fe3(CO)12

Copyright © 2013 SciRes. JSEMAT

223

Vol. 50, No. 11, 2012, pp. 4002-4009. doi:10.1016/j.carbon.2012.04.043

[24] R. M. Bozorth, “Ferromagnetism (Chapter XII),” D. Van Nostrand Company, New York, 1951.

[25] Q. W. Chen, Y. T. Qian, Z. Y. Chen, Y. Xie, G. E. Zhou and Y. H. Zhang, “Hydrothermal Deposition of Magnetite (Fe3O4) Thin-Films,” Materials Letters, Vol. 24, No. 1-3, 1995, pp. 85-87. doi:10.1016/0167-577X(95)00081-X

[26] Y. Qi, K. Sakai and H. Murakami, “Thickness Effect on Sheet Resistance in BSCCO Mixed Crystal Thin Film,” Journal of Low Temperature Physics, Vol. 117, No. 3-4, 1999, pp. 669-673.

[27] A. Kanda, S. Katsumoto and S. Kobayashi, “Charge- Soliton Transport-Properties in 2-Dimensional Array of

Small Josephson-Junctions,” Journal of the Physical So- ciety of Japan, Vol. 63, No. 12, 1994, pp. 4306-4309. doi:10.1143/JPSJ.63.4306

[28] J. Siegel, O. Lyutakov, V. Rybka, Z. Kolska and V. Svor- cik, “Properties of Gold Nanostructures Sputtered on Glass,” Nanoscale Research Letters, Vol. 6, 2011, p. 96. doi:10.1186/1556-276X-6-96

[29] G. D. Nessim, “Carbon Nanotube Synthesis with Special Focus on Thermal Chemical Vapor Deposition,” Nano- scale, Vol. 2, No. 8, 2010, pp. 1306-1323. doi:10.1039/b9nr00427k