the photo-electrochemical disinfection of water using a novel bubble column reactor
DESCRIPTION
The photo-electrochemical disinfection of water using a novel bubble column reactor P. A. Christensen. Deuteronomy Chapter 12 Verse 12 and 13. “ You will have a blade upon your weapon; when you “ease yourself” outside, you will dig with the blade, and cover what comes from you”. - PowerPoint PPT PresentationTRANSCRIPT
![Page 1: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/1.jpg)
The photo-electrochemical disinfection of water using a novel bubble column
reactor
P. A. Christensen
![Page 2: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/2.jpg)
Acknowledgements
The people who really did the work PDRAs: Dr. J. C. Harper and Dr. Sze Tai Lau Students: Ms. S. Kosa, Mr. J. Tinlin, Ms. P. Meynet Staff: Dr. J. Gunlazuardi, (University of Indonesia); Dr. T. P. Curtis, (Department of Civil Engineering); Dr. T. A. Egerton, (Department of Chemistry); Professor K. Scott, Department of Chemical and Process Engineering Funding and support: EPSRC, Ineos Chlor, Huntsman PU
![Page 3: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/3.jpg)
“You will have a blade upon your weapon; when you “ease yourself” outside, you will dig with the blade, and cover what comes from you”
Deuteronomy Chapter 12 Verse 12 and 13
![Page 4: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/4.jpg)
Housesteads Roman Fort, Hadrain’s Wall, Northumberland, GOC
Netties
N
(Latrines)
![Page 5: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/5.jpg)
The latrine at Housesteads Roman fort
![Page 6: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/6.jpg)
![Page 7: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/7.jpg)
Structure of Presentation
•Aim•Introduction-Photocatalysis by TiO2
•Reactor design•Reactor characterisation•Light sources•Electrodes•Disinfection data: E. coli•Disinfection data: Cryptosporidium•Disinfection data: E. coli -the effect of Fe•A warning for the academic•Conclusions•Further work
![Page 8: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/8.jpg)
Aim
To develop a photoelectrochemical detoxification system to facilitate the
recycling of wastewater from industrial processes.
To explore the potential of such a system for disinfection.
(Does EFE take place?)
![Page 9: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/9.jpg)
Introduction: Photocatalysis by TiO2
an example of an AOP
Advanced
Oxidation
Process
![Page 10: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/10.jpg)
OxidantRedox
potential/V vs NHE
Cl2 1.36O3 2.07
.OH 2.80F2 3.03
![Page 11: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/11.jpg)
Solar Detoxification
'Solar'bacteria
PlantsAdvanced Oxidation Processes
Photo-Fenton Reaction Semiconductor Photocatalysis
Slurry
Titanium Dioxide
Immobilised Film
'Promoted' Non-promoted
'Promoted' Non-promoted
Non-electrochemical Electrochemical
One sun Concentrated sunlight
Solar Furnace Technology
Combustion Hydrogenation
Scheme 1: Summary of the processes currently employed in Solar Detoxification
Homogeneous Heterogeneous
'Free' iron Coordinatediron
Gas phaseAqueous phase
PhotocatalyticOxidation
From P. A.Christensen andG. M. Walker,"Opportunites forthe UK in SolarDetoxification",ETSUS/P4/00249/REP,HMSO, London,1996.
![Page 12: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/12.jpg)
The generation of hydroxyl radicals at irradiated TiO2 ( < 410 nm)
h
-OHads
-OHadsh+
e-.OHads
e-h+
e-
TiO2 particle
![Page 13: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/13.jpg)
Semiconductor Photocatalysis
Slurry
• Minority carrier length 0.1 m
• Small particle size
- Long settlement times
- Membrane filtration
• Low throughput
Immobilised film
• Severe MT limitations
• AND - EFE • BUT - reactor design
![Page 14: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/14.jpg)
V
e-O2
H2O
e- h+ h
e-
e-
‘Fatal Attraction’The Electric Field Enhancement Effect
(How?)TiO2 photoanode Counter electrode
![Page 15: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/15.jpg)
Reactor Design
(Not designed specifically for disinfection)
![Page 16: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/16.jpg)
Reactor Design Criteria
The reactor should exploit the EFE effect.
(The reactor should be capable of treatingwater containing strongly absorbing pollutantssince this is characteristic of a number oftypical effluent streams arising from industrialactivity).
The mass transport characteristics of thereactor should be as efficient as possible.
![Page 17: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/17.jpg)
The supply of oxidant, (O2), to the counterelectrode should be sufficient to ensure thatthis process is not rate limiting as has beenobserved elsewhere.
The relative geometry of the lamp andphotoanode should maximise absorption oflight by the latter.
The reactor should be economically feasibleand require low maintenance.
![Page 18: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/18.jpg)
These criteria led to the design of a concentric tube reactor which offered maximum exposure of the photoanode to the UV light whilst minimising the light path and achieving good mass transport conditions.
![Page 19: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/19.jpg)
To reservoir
AirSparge
From reservoir
SIDE VIEW
UV
LAMP
NiCounterelectrode
TiO2 Working electrode
PLAN VIEW
UV lamp
Glass walls
Gauze 125 mmx 115 mm
The Bubble Column Reactor
Electrode cassettes
![Page 20: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/20.jpg)
PUMP
N2 INLET
LAMP HOUSINGALUMINIUM CAGE
ANNULUS
RESERVOIR
![Page 21: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/21.jpg)
The Bubble Column Reactor
(Single electrode cassette)
![Page 22: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/22.jpg)
Reactor Characterisation
![Page 23: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/23.jpg)
2.00x10-5 2.20x10-5 2.40x10-5 2.60x10-5 2.80x10-5
5.8x10-6
6.0x10-6
6.2x10-6
6.4x10-6
6.6x10-6
6.8x10-6
Qv / m3 s-1
kL / m s-1
22
24
26
28
30
32
Re
Calculated mass transfer coefficient (kL, ) and Reynolds ()number through electrode annulus as a function of volumetricflow rate. The reactor was characterised via the reduction of
1mM Fe(CN)63- in aqueous 0.5M K2CO3. Ni mesh WE, Pt/Steel
mesh CE.
Mesh electrodes arenot promoting
(sufficient)turbulence bythemselves.
![Page 24: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/24.jpg)
0.00 0.05 0.10 0.15 0.20 0.25 0.300
2
4
6
8
10
k L / 1
0-5 m
s-1
Gas-Liquid Fraction ( )
Mass transfer coefficient as a function of gas-liquidfraction (). Volumetric flow rate = 2 x 10-5 m3 s-1.
As soon as bubble flow initiated, marked increase in kL.
![Page 25: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/25.jpg)
0.0 0.1 0.2 0.3 0.4 0.5 0.60
500
1000
1500
2000
2500R
e
uG / m s-1
Dependence of Reynolds number on bubble rise velocity.Volumetric flow rate = 2 x 10-5 m3 s-1
Reynolds numbersufficiently highto maintainturbuluent flow
![Page 26: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/26.jpg)
Applying the correlations obtained by Akita andYoshida [K. Akita and F. Yoshida, Ind. Eng. Chem.Proc. Des. Dev., 13 (1974) 84], the estimated thebubble size distribution (Sauter mean diameter) was inthe range of approximately 3-8 mm, consistent withexperimental observations.
The gas-liquid mass transfer coefficients, kg, were thencalculated as a function of bubble rise velocity (ug) andwere found to be c. three times greater than thecorresponding solution-to-electrode mass transfercoefficients, kL.
![Page 27: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/27.jpg)
Hence, for the photoelectrochemical oxidation ofdilute solutions:
-the dissolution of oxygen into the liquid phase isunlikely to be the rate limiting process-
(provided the gas velocities are not so high as toinduce slug flow)
![Page 28: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/28.jpg)
The light source(s)
![Page 29: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/29.jpg)
300 350 400 450
0.0
0.2
0.4
0.6
0.8
1.0
2 x 8W
2 x 32W
400W /100
Inte
nsity
/a.u
.
Wavelength /nm
Emission profiles from the 8W, 32W and 400W lamps used in our experiments. Actinometry shows that the emission of the
400W lamp is 100 x that of the 2 x 32W lamps at 435 nm
Anatase Rutile
![Page 30: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/30.jpg)
Photonic Efficiencies
Defining the ‘charge carrier’ photonicefficiency as:
PE(%) = 100 x (no of electrons in the external circuit)no of incident photons
PEThermal = 1.7% and PESol-gel = 0.6%;for Io 8 x 10-10 Ein cm-2 s-1.
![Page 31: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/31.jpg)
The Electrodes (Photoanodes)
(As coatings on a mixture of substrates: 1 cm2 and 25 cm2 Ti plates, and
11.5 cm x 12.5 cm Ti mesh rolled into a cylinder)
![Page 32: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/32.jpg)
Thermal TiO2 films were prepared by first cleaning the Ti metal substrates (ie. mesh) with ethanol and then placing them in a furnacepreheated at the required temperature for 10 min.in air, after which time they were allowed to cool slowly.
The TiO2 sol-gel electrodes were prepared from the product of the acidcatalysed reduction of titanium di-isopropyl acetoacetonate with water[L. Kavan and M. Gratzel, Electrochim. Acta, 40 (1995) 643 - 652].Dip-coated films were applied by immersing the titanium substrate intothe gel product and withdrawing slowly to ensure good coverage of thecatalyst. The resulting amorphous layer was heated at the required temperature for 10 mins. The procedure was repeated five times.
Electrode Preparation
Geometric surface area
High surface area.
![Page 33: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/33.jpg)
450 500 550 600 650 7000.100.150.200.250.300.350.400.450.500.550.600.650.700.750.800.850.90
I h m
A/c
m2 @
1.2V
vs A
g/A
gCl
Heating temperature °C
The effect of heating temperature on the photocurrent densityof the sol-gel TiO2 films formed on 5 cm x 5 cm Ti plates.
2 x 32W ‘sunbed’ lamps.
Tapwater
+ Methanol
![Page 34: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/34.jpg)
We generally find that the photocurrents observed usingthermal TiO2 films do not show any significant change onaddition of, eg. methanol, in contrast to those observed atthe ‘sol-gel’ films, where significant increases areobserved, as well as lower onset potentials.
This suggests that methanol cannot compete effectivelyfor holes at the surface of thermal films.
‘Kill’ mechanism?
![Page 35: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/35.jpg)
450 500 550 600 650 700 750 800 10000.00
0.05
0.10
0.15
0.20
0.25
0.30
0.35
0.40I hv
@ 1
.2V
/mA
cm
-2
Preparation temperature /°C
No change onaddition ofmethanol
Note - max c. 750 C
The effect of heating temperature on the photocurrent density of the resultant thermal TiO2 film. 5 cm x 5 cm Ti plates, 2 x 32W
‘sunbed’ lamps.
![Page 36: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/36.jpg)
Cyclic voltammogramms, (forward sweeps only, for clarity), recorded using the 500 cm3 BCR, single sol-gel electrode cassette, Ni counter electrode mesh, 1.4 mM
Na2SO4, 2 x 8W UVA lamps.
![Page 37: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/37.jpg)
Disinfection data
(Data for batch operation, reactor volume 500 cm3, unlessotherwise stated)
![Page 38: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/38.jpg)
The effect of film fabrication temperature on the activity of thermal TiO2 mesh electrodes towards the killing of E. coli.
107 cm-3 (500 cm3), single electrode cassette, Ni counter electrode mesh, 1.4 mM Na2SO4, 2 x 8W UVA lamps, V = 1.3V.
Batch mode.
![Page 39: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/39.jpg)
‘100% kill’ = 5 log inactivation; 107 – c. 102 cm-3
Dependence of kill on fabrication temperatureconsistent with dependence of Ihv, and hence with kill
via .OH.
![Page 40: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/40.jpg)
3.0 3.5 4.0 4.5 5.01.5
2.0
2.5
3.0
3.5
Sol-gel Film
Thermal Film
Log(
r i /ce
lls m
l-1 m
in-1)
Log(Ci /cells ml-1)Kinetic studies on disinfection in 250 cm3 batch reactor Log(Initial Rate) vs Log(Cell conc). 2 x 8W UVA lamps
(Philips Lighting UK Ltd. Model TL/02/8, = 300 nm - 475 nm, max = 360 nm) positioned 6 cm above the reactor vessel.
The light intensity, (Optronic Laboratories Inc. 730A radiometer/chemical actinometry), was c. 8 x 10-10 Ein cm-2
s-1. 1V vs AgCl.
Electrodecharacteristics
critical
5 x 5 cm2 plate photo-anode in 250 cm3 cell
![Page 41: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/41.jpg)
Comparison of the BCR data obtained with the thermal and sol-gel TiO2 films with those obtained using P25 slurry. 107 cm-3, 2 x 8W UVA lamps/sparge/ 1.4 mM Na2SO4. Photo-electrochemical experiments: single
electrode cassette, Ni counter electrode mesh.
Electrodecharacteristics
critical
![Page 42: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/42.jpg)
0
10
20
30
40
50
60 Initial stock viability
ThermalBlank
ThermalRun
Sol-gelRun
Sol-gelBlank
% V
iabl
e oo
cyst
s
The inactivation of Cryptosporidium oocsysts in tap water in a 135 cm3 batch reactor, 2 x 8W UVA lamps, 25 cm2 sol-gel
TiO2 electrode, 1.2V vs Ag/AgCl applied potential. The error bars represent multiple comparisons at the 95% level
Electrodecharacteristics
critical
![Page 43: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/43.jpg)
Flow system, sol-gel electrode mesh, 107 E. coli cm-3 (500 cm3 BCR + 2 dm3 reservoir, flow rate = 100 cm3 min-1), single
electrode cassette, Ni counter electrode mesh, 1.4 mM Na2SO4, 2 x 8W UVA lamps, V = 3.0V.
3 x longer for 5 x more!!
But- catalytic activity too low
![Page 44: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/44.jpg)
The catalyst activities need improving…….a little thing(!?), but...
“…well, that certainly screws up our chance of conquering the universe!”
![Page 45: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/45.jpg)
However-
- Iron
![Page 46: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/46.jpg)
0.00 0.25 0.50 0.75 1.00 1.25 1.50 1.75 2.000.0
0.1
0.2
0.3
0.4
0.5
0.6
0.7
0.8
I h /m
Acm
-2 @
1.2
V v
s Ag/
AgC
l
Atm.% Fe
1 cm2 Sol gel TiO2/Ti photoanode, fabricated at 500 C. Photocurrents measured in tap water with and without added methanol as a function of the atom % of added Fe. 2 x 32W
sunbed lamps.
Steady decline in photocurrent as Fe content increases-reflected in ‘activity’?
Added methanol
No methanol
![Page 47: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/47.jpg)
2 3 4 5 6 7 8 90
102030405060708090
100 Thermal ElectrodeFe Doped Electrode
Sol-gel ElectrodeICI Electrode
% k
ill o
f E.C
oli.
Photocurrent /mA
% Kill of E. Coli (107 cm-3) in the BCR at 1.3V after 15 minutes,using various TiO2 photoanodes
Kill mechanism?
![Page 48: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/48.jpg)
But….
![Page 49: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/49.jpg)
The potential limitations of Advanced Oxidation Processes involving the use of O3 and/or H2O2 were highlighted by the Cryptosporidiosis outbreak in Kitchener-Waterloo, Ontario where the post-outbreak review of operations found no relevant treatment breaks, indicating intrinsic problems associated with H2O2 and O3 -based treatment.
The final conclusion of the report* on theCryptosporidiosis outbreak in Kitchener-Waterloo,Ontario: “We are entering into a new era when we canmeet or exceed regulatory requirements and are stillconfronted by episodes of this nature” highlights theseconcerns.
*B. Pett et. al., Proc. AWWA WQTC, 1993, Miami,Florida, 1739
![Page 50: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/50.jpg)
Effect of bicarbonate ion concentration on the kill of 107 E. coli cm-3 (500 cm3) in the BCR; 1.4 mM Na2SO4, 2 x 8W UVA lamps, single electrode cassette, Ni counter electrode mesh. Thermal film mesh, V =
1.3V; sol-gel film mesh V = 3.0V.
![Page 51: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/51.jpg)
Effect of phosphate ion concentration on the kill of 107 E. coli cm-3 (500 cm3) in the BCR; 1.4 mM Na2SO4, 2 x 8W UVA lamps,
single electrode cassette, Ni counter electrode mesh. Thermal TiO2 mesh, V = 1.3V; sol-gel mesh V = 3.0V.
![Page 52: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/52.jpg)
Conclusions•Although not designed for disinfection, the BCR showed good mass transport and light utilisation characteristics, with supply of oxidant to the counter electrode, and reduction thereat, not being rate limiting.
•The photoelectrochemical disinfection of water inoculated with a range of pathogens including Cp, E. coli and Clostridium Prefringens spores has been observed using simple TiO2 photoanodes and relatively low intensity UVA lamps and low applied voltages (< 3V). The kill rate is increased substantially over that observed at zero applied potential.
![Page 53: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/53.jpg)
•The mechanism of disinfection remains unclear. However, it is clear that disinfection activity depends very much upon the nature of the TiO2 photoanode employed, and may not simply involve OH radicals as the active agent.
•In our hands, the photoelectrochemical disinfection of water proved more effective than photochemical disinfection using a TiO2 slurry.
•The catalytic activity of the photoanodes remains too low.
![Page 54: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/54.jpg)
The most recent reactor design: the Tower reactor
![Page 55: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/55.jpg)
Ti Rod
Ti-meshNi-mesh
PTFE wheel
60 mm
40 mm
40 mm
40 mm
40 mm
60 mm
Stainless Steel supporting rod
UV lamp housing
Sintered glass gas distributor
Ni Rod
![Page 56: The photo-electrochemical disinfection of water using a novel bubble column reactor](https://reader036.vdocument.in/reader036/viewer/2022062521/568131c8550346895d982f58/html5/thumbnails/56.jpg)
Preliminary disinfection data from the tower reactor. 4.3 x 106 CFU ml-1, 4.6 dm3 aqueous 1.4mM Na2SO4, 5 x thermal TiO2/Ti mesh + Ni mesh cassettes. 2 x 25W UVA lamps, 50% intensity.
Reactor volume 7 dm3.
Electrochem(1.6V)
Photocatalytic
Photoelectrocat(1.6V)