twi radio graphic interpretation.(weld defects & repair)
TRANSCRIPT
![Page 1: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/1.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Weld Defects & Repairs
Radiographic InterpretationRadiographic Interpretation
![Page 2: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/2.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Faults in Fusion WeldsFaults in Fusion Welds
![Page 3: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/3.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Defects which may be detected by visual inspection can be grouped under the following headings
Cracks
Solid inclusions
Surface and profiles
Misalignment (set-up
irregularities)
Gas pores and porosity
Lack of fusion
Mechanical damage
Parent material damage
Miscellaneous
Faults in Fusion WeldsFaults in Fusion Welds
![Page 4: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/4.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
CracksCracks
![Page 5: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/5.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Classified by Shape
Longitudinal
Transverse
Branched
Chevron
Classified by Position
HAZ
Centreline
Crater
Fusion zone
Parent metal
Cracks that may occur in welded materials are caused generally by many factors and may be classified by shape and position, cracks are classed as planar.
CracksCracks
![Page 6: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/6.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Hydrogen induced cold cracking (HICC)
Solidification cracking (Hot Tearing)
Lamellar tearing
Re heat cracking
Process CracksProcess Cracks
![Page 7: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/7.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Longitudinal parent metal crack
Longitudinal weld metal crack Lamellar tearing
Transverse weld metal crack
CracksCracks
![Page 8: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/8.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Transverse crack Longitudinal crack
![Page 9: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/9.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
InclusionsInclusions
![Page 10: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/10.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Root piping
Cluster porosityGas pore
Blow hole
Herringbone porosity
Loss of gas shield
Damp electrodes
Contamination
Arc length too large
Damaged electrode flux
Moisture on parent material
Welding current too low
Gas pore <1.5mm Blow hole.>1.6mm
Gas CavitiesGas Cavities
![Page 11: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/11.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Root piping
Porosity
Gas CavitiesGas Cavities
![Page 12: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/12.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Cluster porosity Herringbone porosity
![Page 13: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/13.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Slag originates from welding flux
MAG and TIG welding process produce silica inclusions
Slag is caused by inadequate cleaning
Other inclusions include tungsten and copper inclusions from the TIG and MAG welding process
Slag inclusions are defined as a non-metallic inclusion caused by some welding process
Slag inclusions
Parallel slag lines Lack of interun fusion + slag
Lack of sidewall fusion with
associated slag
Solid InclusionsSolid Inclusions
![Page 14: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/14.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Elongated slag linesInterpass slag inclusions
![Page 15: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/15.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Lack of FusionLack of Fusion
![Page 16: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/16.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Incomplete filled groove + Lack of sidewall fusion
12
1. Lack of sidewall fusion2. Lack of inter-run fusion
Poor welder skill
Incorrect electrode
manipulation
Arc blow
Incorrect welding
current/voltage
Incorrect travel speed
Incorrect inter-run cleaning
Lack of FusionLack of Fusion
![Page 17: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/17.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
An imperfection at the toe or root of a weld caused by metal flowing on to the surface of the parent metal
without fusing to it
Contamination
Slow travel speed
Incorrect welding technique
Current too low
OverlapOverlap
![Page 18: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/18.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Toe OverlapToe OverlapFillet weldFillet weld
Toe OverlapToe OverlapButt weldButt weld
OverlapOverlap
![Page 19: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/19.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Incomplete root fusion
Incomplete root penetration
Low Amps/volts
Large Root face
Small Root Gap
Fast Travel Speed
Incorrect Electrode Angle
Contamination
Arc blow
Weld Root DefectsWeld Root Defects
![Page 20: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/20.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Lack of root fusion Lack of root Penetration
Weld Root DefectsWeld Root Defects
![Page 21: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/21.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Lack of root penetration Lack of root fusion
![Page 22: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/22.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Surface & ProfileSurface & Profile
![Page 23: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/23.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Incomplete filled groove Poor cap profile
Excessive cap height
Poor cap profiles and excessive cap reinforcements may lead to stress concentration points at the weld toes and will also contribute to overall poor toe blend
Weld Profile DefectsWeld Profile Defects
![Page 24: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/24.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Incomplete filled grooveExcess cap reinforcement
![Page 25: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/25.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Poor stop/starts
Weld Profile DefectsWeld Profile Defects
![Page 26: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/26.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Miscellaneous DefectsMiscellaneous Defects
![Page 27: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/27.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Spatter Excessive current
Damp electrodes
Contamination
Incorrect wire feed speed
when welding with the MAG
welding process
Arc blow
Miscellaneous DefectsMiscellaneous Defects
![Page 28: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/28.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Accidental striking of the arc
onto the parent material
Faulty electrode holder
Poor cable insulation
Poor return lead clamping
Arc strike
Miscellaneous DefectsMiscellaneous Defects
![Page 29: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/29.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
An irregular groove at the toe of a weld run in the parent metal
Excessive amps/volts
Excessive travel speed
Incorrect electrode angle
Excessive weaving
Incorrect welding technique
Electrode too large
Cap & Root UndercutCap & Root Undercut
![Page 30: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/30.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Intermittent Cap Undercut
Cap UndercutCap Undercut
![Page 31: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/31.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd M.S.RogersCopyright © 2003 TWI Ltd
Cap undercutRoot undercut
![Page 32: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/32.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Shrinkage groove
Insufficient weld metal deposited in the root pass
Too fast a cooling rate during the application of the root bead pass
Poor welding technique
A shallow groove caused by contraction in the weld metal along each side of the penetration bead
Weld Root DefectWeld Root Defect
![Page 33: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/33.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Concave root
Root faces too large
Root gap too large
Excessive back purge pressure during TIG welding
Excessive root bead grinding before the application of the second pass
A shallow groove, which may occur in the root of a butt weld
Weld Root DefectWeld Root Defect
![Page 34: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/34.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Concave Root
Weld Root DefectWeld Root Defect
![Page 35: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/35.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Excessive root penetration
Root faces too small
Root gap too large
Excessive amps/volts
Slow travel speed
Root penetration bead in excess in accordance with the
relevant specification being used
Weld Root DefectWeld Root Defect
![Page 36: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/36.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Weld Root DefectWeld Root Defect
Excessive root penetration
![Page 37: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/37.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd M.S.RogersCopyright © 2003 TWI Ltd
Concave root Excess root penetration
![Page 38: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/38.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
High Amps/volts
Small Root face
Large Root Gap
Slow Travel SpeedBurn through
A localized collapse of the weld pool due to excessive penetration resulting in a hole in the root run
Weld Root DefectWeld Root Defect
![Page 39: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/39.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Weld Root DefectWeld Root Defect
Burn Through
![Page 40: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/40.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Loss or insufficient back
purging gas
Most commonly occurs
when welding stainless
steels
Purging gases include
argon, helium and
occasionally nitrogen
Oxidized Root (Root Coking)Oxidized Root (Root Coking)
![Page 41: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/41.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Crater pipeCrater pipe
Weld craterWeld crater
Crater PipeCrater Pipe
![Page 42: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/42.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Crater pipe is a shrinkage defect and not a gas defect, it has the appearance of a gas pore in the weld crater
Too fast a cooling rate
Deoxidization
reactions and liquid to
solid volume change
Contamination
Crater cracksCrater cracks(Star cracks)(Star cracks)
Crater pipeCrater pipe
Crater PipeCrater Pipe
![Page 43: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/43.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Mechanical DamageMechanical Damage
![Page 44: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/44.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Mechanical damage can be defined as any surface material damage cause during the manufacturing process.This can included damage caused by:
Grinding
Hammering
Chiselling
Chipping
Breaking off welded attachments (torn surfaces)
Using needle guns to compress weld capping runs
Mechanical DamageMechanical Damage
![Page 45: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/45.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Mechanical DamageMechanical Damage
Mechanical Damage/Grinding Mark
Chipping Marks
![Page 46: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/46.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Set-up IrregularitiesSet-up Irregularities
![Page 47: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/47.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
A variation of leg lengths on a fillet weld
Note: Unequal leg lengths on a fillet weld may be specified as part of the design, in which case it will not be considered as a defect.
Unequal Leg LengthsUnequal Leg Lengths
![Page 48: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/48.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Plate/pipe Linear Misalignment (Hi-Lo)
Angular Misalignment
Linear misalignment is measured from the lowest plate to the highest point.
Angular misalignment is measured in degrees
Set-up IrregularitiesSet-up Irregularities
![Page 49: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/49.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Linear Misalignment
Set-up IrregularitiesSet-up Irregularities
![Page 50: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/50.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Linear Misalignment
Set-up IrregularitiesSet-up Irregularities
![Page 51: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/51.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Any QuestionsAny Questions
??
![Page 52: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/52.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
QU 1. Give two main causes for the occurrence of a burn through
QU 2. Give two main causes for the occurrence of excessive root penetration on a single-V butt weld
QU 3. Give five defects, which may occur when welding carbon steel using the MMA welding process with the current setting to low
QU 4. Give three possible causes for the occurrence of lack of side wall fusion
QU 5. Sketch the following defects
a. Lack of root wall fusion b. Lack of root penetration
c. Incomplete filled groove d. Concave root
QuestionsQuestionsWeld Defects
![Page 53: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/53.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Material InspectionMaterial Inspection
Course notes section references 6
![Page 54: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/54.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
All materials arriving on site should be inspected for:
Size / dimensions
Condition
Type / specification
In addition other elements may need to be considered depending on the materials form or shape
Material InspectionMaterial Inspection
![Page 55: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/55.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Parent material defects include:
Lamination
Mechanical damage Lap
Segregation line
Laminations are caused in the parent plate by the steel making process, originating from ingot casting defects.Segregation bands occur in the centre of the plate and are low melting point impurities such as sulphur and phosphorous.Laps are caused during rolling when overlapping metal does not fuse to the base material.
Material InspectionMaterial Inspection
![Page 56: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/56.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Material InspectionMaterial Inspection
Plate Lamination
![Page 57: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/57.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd M.S.RogersCopyright © 2004 TWI Ltd
Weld RepairsWeld Repairs
Course notes section references 16
![Page 58: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/58.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Authorization for repair
Removal and preparation for repair
Testing of repair - visual and NDT
In the event of repair
Weld RepairsWeld Repairs
![Page 59: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/59.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
A weld repair may be used to improve weld profiles or
extensive metal removal
Repairs to fabrication defects are generally easier than
repairs to service failures because the repair procedure
may be followed
The main problem with repairing a weld is the
maintenance of mechanical properties
During the inspection of the removed area prior to welding
the inspector must ensure that the defects have been
totally removed and the original joint profile has been
maintained as close as possible
Weld RepairsWeld Repairs
![Page 60: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/60.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
The specification or procedure will govern how the defective areas are to be removed. The method of removal may be
Grinding
Chipping
Machining
Filing
Oxy-Gas gouging
Arc air gouging
Weld RepairsWeld Repairs
![Page 61: TWI Radio Graphic Interpretation.(Weld Defects & Repair)](https://reader036.vdocument.in/reader036/viewer/2022081415/55157b8c4979590c1e8b4cfe/html5/thumbnails/61.jpg)
T E
C H
N O
L O
G Y
M.S.RogersCopyright © 2004 TWI Ltd
Any QuestionsAny Questions
??