Wet Etching
ESS4810 LectureFall 2010
Introduction
• Selective removal of specific materials• Chemical process• Isotropic etching• Anisotropic etching• Advantages
– Simple, inexpensive• Disadvantage
– Poor process control
![Page 2: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/2.jpg)
Wet Etching
1. Reactant transport to surface2. Selective and controlled reaction of
etchant with the film to be etched3. Transport of by-products away from
the surface
1
2
3
Etching of Silicon
![Page 3: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/3.jpg)
Isotropic Etching of Silicon• HNA system
– HNO3
– HF– CH3COOH or H2O (as a diluent)
222623 6 HOHHNOSiFHHFHNOSi +++→++
OHSiFHSiOHF 2622 26 +→+
224 4 HSiOOHSi +→+ −+
+− ++→++ HOHHNOHNOOHHNO 222 2223
Etching Profiles
Without agitation
With agitation
![Page 4: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/4.jpg)
Iso-Etch Curves
Masking Materials
![Page 5: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/5.jpg)
Anisotropic Etching
Anisotropic Etching of Silicon
• Alkali Hydroxide (KOH, NaOH, etc.)
• Ethylenediamine Pyrocatechol (EDP)
• Tetramethyl Ammonium Hydroxide (TMAH)
![Page 6: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/6.jpg)
![Page 7: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/7.jpg)
Anisotropic Etching
![Page 8: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/8.jpg)
Silicon Crystallography
Miller Indices
• [i, j, k]– a specific direction of a unit vector
• < i, j, k>– a family of equivalent directions
• (i, j, k)– a specific crystal plane
• {i, j, k}– a family of equivalent planes
![Page 9: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/9.jpg)
Miller Indices
• Angles between planes– ∠ between [abc] and [xyz] given by– ax+by+cz = |(a,b,c)|*|(x,y,z)|*cos(Θ)
• {100} and {110}: 45°• {100} and {111}: 54.74°• {110} and {111}: 35.26°, 90°, and 144.74°
![Page 10: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/10.jpg)
Silicon Crystallography
Lateral Underetch
![Page 11: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/11.jpg)
EDP <100> EDP <110>
KOH <100> KOH <110>
Anisotropic Etching
![Page 12: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/12.jpg)
![Page 13: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/13.jpg)
EDP Etching
![Page 14: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/14.jpg)
![Page 15: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/15.jpg)
Wet Etching of Thin Films
• Silicon dioxide– HF– Buffered HF (BHF)-10:1 HF/NH3F “BOE”
• Silicon Nitride– Phosphoric acid– Selectivity [Si3N4/SiO2] = 40/1
• Polysilicon– KOH, EDP, and TMAH
Wet Etching of Quartz
• Anisotropic etching by HF– with 10.9mol/l, Rate ~ 9.6 µm/hr
• Ammonium fluoride (NH4F)• Saturated ammonium bifluoride (NH4HF2)• Require metal mask or oxide mask• Amorphous Si or Poly Si can be used as
mask for deep etching
![Page 16: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/16.jpg)
References
• K.E. Petersen, “Silicon as a Mechanical Material,” Proc. IEEE, vol. 70, pp. 420-457, May 1982
• G.T.A. Kovacs, N.I. Maluf, and K.E. Petersen, “Bulk Micromachining of Silicon,” Proc. IEEE, vol. 86, pp. 1536-1551, August 1998
Etching Bias
• Bias = df - dm
• Complete isotropic etching B=2hf
• Complete anisotropic etching B=0
mask
![Page 17: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/17.jpg)
Degree of Anisotropy
• Af = 0 : isotropic
• Af = 1 : anisotropic 0=B
fhB 2=
Etching of Steps with a Slope
final
![Page 18: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/18.jpg)
Worst-Case Design Considerations for Etching
Step height variation
Variation of film thickness across wafer
Etching mask can be eroded
during film etching
Design Considerations for Etching
• Film thickness variation
• Film etching rate variation
• Over-etching around step
• With mask erosion
)1((max) δ+⋅= ff hh
)1((min) fff vv φ−⋅=
)1()1(
)1(
2
1
h
h
v
ht
ff
fT +⋅
−⋅
+=
φδ
![Page 19: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/19.jpg)
Bulk Micromachining of Silicon
ESS4810 LectureFall 2010
Introduction
• Purpose of bulk micromachining– Selectively remove significant
amounts of silicon from a substrate• Three categories
– In terms of the state of the etchant– Wet, vapor, and plasma
• The majority of currently shipping silicon sensors are made using bulk etching
![Page 20: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/20.jpg)
Purposes
• To undercut structures that are required to physically move
• To form membranes on one side of a wafer
• To make a variety of trenches, holes, or other structures
Possible Machined Structures
![Page 21: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/21.jpg)
Possible Machined Structures
Possible Machined StructuresWafer Surface<100> Plane
Cavity
Nozzle
Membrane
Cantilevers
Bridge
Wafer Surface<100> Plane
Cavity
Nozzle
Membrane
Cantilevers
Bridge
![Page 22: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/22.jpg)
Comparison of Silicon Etchants
Etching Profile
[100]-oriented wafers [110]-oriented wafer
![Page 23: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/23.jpg)
Corner Compensation
Corner Compensation
KOH(110) > (100) > (111)
EDP(100) > (110) > (111)
![Page 24: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/24.jpg)
Etch-Rate Modulation• Highly p-doped silicon regions greatly
attenuate the etch rate• Selective doping can be used to define
specific regions of the silicon that remain, while the bulk is etched away
![Page 25: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/25.jpg)
Vapor-Phase Etching
• Xenon difluoride etching
• Non-plasma, isotropic, and dry• Very high selectivity for aluminum,
silicon dioxide, silicon nitride, and photoresist
Vapor-Phase Etching
• Interhalogen etch chemistries– Avoid the extremely rough silicon
surfaces that are formed using XeF2etching
– Thermal silicon dioxide mask and various interhalogen gases (BrF3 and ClF3) with a xenon diluent
• Laser-driven vapor-phase etching
![Page 26: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/26.jpg)
Deep Reactive Ion Etching
![Page 27: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/27.jpg)
Deep Reactive Ion Etching• Alternating between etching and
protective polymer deposition
CMOS Integration
![Page 28: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/28.jpg)
![Page 29: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/29.jpg)
Lab 1 and 2
Si
Lab 1:1. Wafer cleaning2. Thermal oxidation
Wet Oxide
Lab 2-1: 1. Lithography (PR AZ 5214, mask #1for bulk etching window)
Si
PR AZ 5214 (positive)
Si
Lab 2-2: 1.Break wafer into A and B2.B: BOE wet etching
A: RIE dry etching3.PR strip, wafer cleaning
Part A Part Bdry etching wet etching
![Page 30: Wet Etching - National Tsing Hua Universitymx.nthu.edu.tw/~yucsu/4810/Lec04.pdf · 2010-10-17 · Wet Etching ESS4810 Lecture Fall 2010 Introduction • Selective removal of specific](https://reader030.vdocument.in/reader030/viewer/2022040116/5ea67c08f629a5370c22bca3/html5/thumbnails/30.jpg)