In comparison of glass cloth, carbon fabric carries absolutely high strength, high elasticity, and high thermo-stable
characteristics in the current composite market. It also broadly used in industrial field by using its functional property.
Specific use : Carbon fabric also can be produced prepreg type and even if it is definitely stronger than steel, it is lighter than general F.R.P. Currently, it is widely applied in the aerospace business field and also it is used for industrial, constructional
and sports leisure business field.
Product IDWidth(mm)
Density(count/inch2)
Thickness
(mm)
Weight(g/m2)
Woven type
Warp Fill
YC-3K 200gsm 1,000 12.5 13.5 0.25 200PLAINTWILL
YC-3K 240gsm 1,000 15 15 0.26 240PLAINTWILL
YC-3K PVC 240gsm
1,000 15 15 0.30 380PVC
Black
CB131Carbon & Basalt
hybrid1,000 12.5 13.5 0.25 303 PLAIN
YC-3K 380gsm 1,000 25 25 0.34 3808H
SATIN
YC-12K 400gsm 1,000 6 6 0.43 400PLAINTWILL
Width=> 1,000~1,500mmWeight=> 200gsm~400gsm
General prepreg type=> Epoxy & Phenol
Carbon fabric and Prepreg
YOU CHANG
Sample
Carbon fiber Vinyl
Face FilmSolvent
AdhesiveRelease Liner Size
0.09mm 30μ 140g 127cm X 50m
YOU CHANG
UD Prepreg Carbon Fabric
General Modulus Prepreg(24Ton) without Scrim-Standard Resin Content-
High Modulus Prepreg(46Ton) with Scrim-Low Resin content-
Product ID
CFWt
(g/m²)
ResinWt
(g/m²)
ResinContent(%)
TotalWt(g/m²)
Thickness(mm)
CP 050NS 50 37 40 92 0.061
CP 075NS 75 46 38 121 0.080
CP 100NS 100 54 35 154 0.101
CP 125NS 125 62 33 187 0.121
CP 150NS 150 74 33 224 0.145
CP 175NS 175 86 33 261 0.169
CP 200NS 200 99 33 299 0.194
CP 250NS 250 123 33 373 0.241
Product ID
CFWt
(g/m²)
ResinWt
(g/m²)
ResinContent
(%)
ScrimWt
(g/m²)Total
Wt(g/m²)Thickness
(mm)
46H 0503 55 37 40 35 127 0.091
46H 0693 69 36 34 35 140 0.098
46H 0923 92 39 30 35 166 0.114
46H 1163 116 50 30 35 201 0.136
46H 1393 139 60 30 35 234 0.157
46H 1603 160 69 30 35 264 0.176
46H 1843 184 79 30 35 298 0.198
YOU CHANG
APPLICATION
After the heating process for surface treatment of glass fabric, we manufacture semi-hardened materials called "prepreg" with proper
resin such as, epoxy, phenolic, and unsaturated polyester.
The application is going to be for fishing rods, arrowheads, and it is also applicable for industrial use.
Product ID
Width(mm)
Density(count/inch2) Thickness
(mm) Weight(g/m2)
Woven type
Remarks
Warp Fill
YC-103 1,030 60 52 0.03 25 PLAIN
YC-210 1,020 64 25 0.10 1084H
SATIN
YC-218 1,020 64 26 0.18 2084H
SATIN
YC-224 1,020 50 26 0.24 3024H
SATIN
YC-7781 1,020 57 54 0.23 3008H
SATIN
YC-1522 AN2
24”,25”27”,30”
24 22 0.15 122 (4oz) PLAINSurfingboard
YC-2110 N2
24”,25”27”,30”
18 17 0.21 187 (6oz) PLAINSurfingboard
Glass fiber fabric & Prepreg
YOU CHANG
YOU CHANG
After the heating process for surface treatment of glass fabric, we manufacture semi-hardened materials called "prepreg" with proper
resin such as, epoxy, phenolic, and unsaturated polyester.
Glass Coated fabric
fabrics Finishing styleglass
fabrics Temp
glass fabrics Features glass fabrics Applications
Aluminum coated with fiberglass fabric
550℃heat reflection, abrasion
proofheat protection cushions, motor vehicle industry, protection for piping outside
Dying and coloring fiberglass fabric
550℃ heat protectionheat protection, welding defender and
differentiate work area
Graphite coated with fiberglass fabric
750℃increase resistance to
abrasion and flame, high temperature absorb mote
welding defender, general purpose insulation
Heat cleaning fiberglass fabric
550℃decrease pulverous mote,
good osmosis.welding defender, general purpose
insulation
PTFE coated with fiberglass fabric
550℃anti-adhesive surface, soil
repellent, acid resistantconveyor belt, acid resistant seclusion
Silicone rubber coating coated with fiberglass
fabric550℃
mechanical load, chemical, oil and corrosive of resistant
welding defender, compensators, insulation mats, heat production quilt
Polyurethane coated with fiberglass fabric
550℃good resistance to abrasion
and cuts, waterproof, allergen resistant
welding protection
Vermiculite coating 750℃increase resistance to
abrasion, flame, high heat
heavy duty insulation and seal, Widely used in exhausting, taking a breath,
ventilation, smoke and dust, waste gas of the steel, electricity, metallurgy, chemical industry the systematic
pipeline compensation of dealing with etc..
Steel wire reinforcing fiberglass fabric
550℃ increase tensile strength heavy duty insulation and seal
PVC coated fiberglass fabric
550℃good resistance to abrasion,
oil, and cuts, waterproofwelding protection, covering fabric
Acrylic coated fiberglass fabric
550℃good resistance to abrasion and cuts. allergen resistant and anti‐adhesive surface
welding protection
Neoprene coated fiberglass fabric
550℃good resistance to
abrasion,allergen resistantwelding protection
Level off veins fiberglass fabric
550℃good resistance to abrasion
and cutswelding protection, heat preservation
Latex coated fiberglass fabric
550℃
waterproof, gas defender and increase resistance to abrasion, high temperature
absorb
welding protection, waterproof material, fireproof material
Fluoroelastomer coated fiberglass
fabric550℃
increase resistance to abrasion, oil, acid and high
temperature
Non-metal expanse joints, heat preservation material
Ethylene propylene-diene monomer coated
fiberglass fabric550℃
increase resistance to abrasion and high
temperature
Non-metal expanse joints, heat preservation material
Acrylonitrile-butadiene rubber coated
fiberglass fabric550℃
increase resistance to abrasion and high
temperature
Non-metal expanse joints, heat preservation material
Glass cloth for industrial & constructional use
Product IDWidth(mm)
Density(count/inch2)
Thickness
(mm)
Weight(g/m2)
Woven type
Warp Fill
YC-108 1,070 4242
(52)0.08 77(84) PLAIN
YC-113 1.020 35 25 0.13 127 PLAIN
YC-1181,020~1,250
35 30 0.18 176 PLAIN
YC-3181,020~1,150
18 18 0.18 193 PLAIN
YC-318 black PVC coating
1,020 18 18 0.48 580 PLAIN
YC-533 silver & black
coating1,020 20 22 0.32 330 TWILL
YC-533 silver PVC coating
1,020 20 22 0.56 624 TWILL
YC-558 1,020 35 26 0.58 510 TWILL
YC-7500 1,020 15 13 0.25 300 PLAIN
YC-7500 Black coating
1,020 15 13 0.25 309 PLAIN
YC-7628 1,020 44 34 0.18 210 PLAIN
Glass cloth laminated with aluminum foil is required for thermo-stable materials for finishing work, vertical curtains for fireproof
materials for electromagnetic proof, and shipbuilding business field.
Using the application of its characteristics, such as, high-tensile strength, measure stability, and electrical insulation, various
adhesive tapes and Drybit for crack prevention are produced with the material.
For replacement of asbestos fabric, glass fabric coated with fireproof resin is manufactured for canvas.
For various purposes, fireproof and fire-resistant materials are produced with proper resin, for example, polyurethane, P.V.C,
silicone, rubber, and Teflon resin.
YOU CHANG
ALKALI-RESISTANT FIBERGLASS MESH
YOU CHANG
Alkali-resistant fiberglass mesh fabric is basis of any heat insulation system. Cracks are prevented because of good chemical corrosion resistance and high warp and weft strength~Distortions insulation system from high impact are
minimized because the directions.
Application(1) ALKALI-RESISTANT FIBERGLASS MESH is widely used in wall
reinforcement,out –side wall heat insulation,roof waterproof,wall corner. (2) It can also reinforce cement,plastic,bitumen,plaster,marble,mosaic etc (3) It is an ideal engineering material in construction
Mesh size
2.5mm×2.5mm, 4mm×4mm,5mm×5mm, 6mm×6mm, 7mm×7mm, 8mm×8mm,
10mm×10mm,12mm×12mm
The unit grams 60g/m2to 580g/m2
Width 10cm to 3m
Length 50m/roll to 1500m/roll
ColorWhite,yellow,blue,green,win
e red,orange.etc
Raw Materialc-glass yarn or e-glass
yarn
Packing:Plastic bag+carton+pallet
Technical Specification:
Spec. widthResin mark
Resin content
(%)
Alkali Resistant Properties
(%)
Tensile Strength
(N)
Range Of Weight
Warp--Weft Yarn
4x4mm,75g/m2
100cm
BASF +factory
glue
18 ≥50 ≧740 75g±5g 60×2--120
4x4mm,90g/m2
100cm 18 ≥50 ≧910 90g±5g 72×2--140
4x4mm,110g/m2
100cm 18 ≥50 ≧1100 110g±5g 88×2--176
4x4mm,145g/m2
11cm-300cm
18 ≥50 ≧1500 145g±5g 116×2--232
4x4mm,160g/m2
11cm-300cm
18 ≥50 ≧1585 160g±5g 128×2--256
Reinforcement material
Product Name
Fiber Type
Fiber Strengt
h(Mpa)
Fiber Stiffne
ss(Gpa)
Areal Weight(g/m2)
Fabric Thick-ness
(mm)*
Style
YC-N200
high strength carbon
4,900 230 200 0.111Woven
UD
YC-N300
high strength carbon
4,900 230 300 0.166Woven
UD
YC-H300
Intermediate modulus carbon
4,600 340 300 0.166Woven
UD
CARBON WRAP SYSTEM
ARAMID WRAP SYSTEM
Product Name
Fiber Type Fiber
Strength(Mpa)
Fiber Stiff-ness
(Gpa)
Areal Weight(g/m2)
Fabric Thick-ness
(mm)*
Style
YC-A280
Kevlar 2,880 100
280 0.194Woven
UD
YC-A415
415 0.288Woven
UD
YOU CHANG
• APPLICATION
Multi-axial Fabric
YOU CHANG
PRODUCT FEATURES:1.No binder used;2.Fast wet-out;3.High strength in a specific direction;4.Increase the properties of laminated FRP in terms of ultimate
tensile strength, delaminating resistance under stress and flexural strength;
5.Reduce the weight of FRP;6.Make FRP surface smoother;7.Simplify the operation of Hand Lay-up and improve productivity.
Chopped Strand Mat
TYPE OF GLASS E GLASS
Filament diameter 11-12Micron
Sizing of roving Silcane
Blinder type Emulsion or powder
Wet out speed 3-4Min
Chopped strand length 50mm
Weight(g/m2) 100,250,300,450,600,900
Width(mm) 30,60,1250,1050,1020,3200
YOU CHANG
• APPLICATION
Chopped CF & Chopped strand
YOU CHANG
Chopped CF
Compatible with cement for constructing bridge and road.
TYPE USED YARNCHOPPING
LENGTH
ThermosettingTOHO
YARN
3mm,6mm,
8mm,12mmThermoplastic
Chopped Strand
1. E-Glass Chopped Strands for BMC are widely used in transportation, construction, electronics,chemical industry.
2. E-Glass Chopped Strands for Thermoplastics are mainly used in injection and compression molding processes
Waste carbon fiber
for making carbon chopped or recycle to make carbon material.
Ballistic Fabric
YOU CHANG
A. Kevlar/Twaron Ballistic Fabric
Kevlar / Twaron Ballistic Fabric for making bulletproof jackets, helmets, plates, etc.:Specification: 1.20 by 2.42M; 1.60 by 3.20M; or length 100M+Area Density: 225g/m2Ballistic Layers for NIJ IIIA: 24Mini order: 100 sq.m; sample is available and charged.Capacity: 10 kilo sq.m monthlyKevlar / aramid ballistic fabric is softer and more comfortable than UHMW-PE, but it is weaker on UV resistant, low moisture sensibility and not waterproof.Guarantee Period: the material are in 5 years warranty.Note: the material can be preserved under temperature 300 centigrade
B. UHMW-PE Ballistic Fabric
We supply UHMW-PE UD (unidirectional) fabric sheet which is for making bulletproof applications. It is a roll product consisting of two/four plies of unidirectional polyethylene fiber crossplied at 0/90 degree, sandwiched with a thermoplastic film. It features lightweight, soft, comfort, outstanding UV resistant, low moisture sensibility and waterproof, also is powerful protection capability and high specific energy absorption. Our supplying specifications'''' range is from 140g/m2, 150g/m2, 160g/m2 and 170g/m2; continuous roll of fabric sheet is available
C. Ballistic HPPE Plate
Our ballistic HPPE plates substitute the traditional hard steel, Kevlar or Aramid plates for inserts of bulletproof vests and vehicle armoring.We have ballistic HPPE plates on levels NIJ IIIA III and III+, and ceramic & PE composite plates Level NIJ IV, their sizes may be made under your requirement.The main material is UHMW-PE (Ultra High Molecular Weight Polyethylene) fiber which is the best ballistic raw material nowadays.
High Silica Products - 1200℃ :
YOUCHANG Silica cloth is a high performance textile fabric that has 96%
SiO2, flexible fabric designed for use where severe temperature conditions
exist.
It used for thermal insulating and heat protection. It will not burn, rot or
deteriorate and resist most acids. It will keep good state when it works at
1100℃ for a long time. It works at 1400℃ more than 15 minutes and works
at 1700℃ more than 15 seconds.
Applications:
• Used for heat preservation and thermal insulating.
• Welding/cutting, molten metal splash protection.
• Heat and flame shielding, stress relief.
• Hose and cable protection and emergency fire blankets
Main Specifications:
YOU CHANG
Silica fabric
Model Weave
Warp FillTensile Strength
minWeight Thickness Width
Per cm Per cm Fill Warp g/m2 mm m
0300P01 Plain 18 13 1200 1000 300 0.28 0.8-0.82
0300S028H
Stain18 13 1500 1200 600 0.6 0.914
0300S048H
Stain18 13 4400 3400 1200 1.4 0.914
SiO2 content ≤96%
Endurance of temperature 1200℃/1800℉
Instantaneous temperature 1700℃/3000℉
Surfacing Tissue mainly used in the surface layers of FRP products. It features even Fiber distribution, soft feel, level and smooth fiber surface, less glue
content, quick resin soak and good pattern fitness. It can improve the product surface property on corrosion resistance, compressive strength,
seepage resistance, and longer service life. It is also suitable for spraying; pattern pressing and other FRP pattern technology.
Applications:
• Imparts a reinforced resin - rich surface for general FRP products
• Suitable for hand lay-up or press moulding where intricate contours are present and also for pipe and tank winding application
• Multicompatibility binder results in softer and more flexible tissue and improved surface - laminate bonding
• Resin - rich surface prevents crack formation and improves visual appearance of final product
Main Specifications:
Fiberglass Surfacing Tissue
ApplicationDensity(g/m)
Moisture Content(%)
Binder Content(%)
Wetting Time(%)
Tensile Strength(N/5cm)
Filament Winding
20
<0.2
7 <8 ≥20
30 6 <10 ≥25
50 6 <16 ≥40
Hand lay
30 7 <10 ≥20
40 6 <15 ≥25
50 6 <20 ≥30
YOU CHANG
Product Features :
ㆍ Rapid and complete wet out, Good processing characteristics
ㆍ Low resin demand during processing
ㆍ High composite mechanical properties
Storage :This Product should be stored in dry, cool, clean and rain-proof area. Recommended temperature range of storage is between 15℃-35℃ and relative humidity between 35%-65%.
Main Specifications:
Direct Roving
YOU CHANG
Linear Density(Tex)
Size Content(%)
Moisture Content(%)
Stiffness(mm)
Net Weight(kgs)
Application
ISO1887 ISO3344 ISO3341
240,300,600,1200,2400,4400,4800
0.15±0.15 ≤0.10 ≥0.4015.6,17, 22
Weaving
Filament Winding
Pultrusion
Direct Roving for Filament Winding, Pultrusion, Weaving :Direct Roving is an E-glass roving produced by directly winding a certain
number of individual fibers from the bushing without twist. It is coated with a silane-based size and is designed for reinforcing unsaturated polyester,
epoxy, vinylester and phenolic resins.
It is specially used to produce GRP FRP pipes, pressure vessels, gratings and profiles and, when converted into woven rovings, boats and chemical storage
tanks with filament winding, pultrusion and weaving process.
Fiberglass Plain Weaving Fabric mainly means the fabric woven by fiberglass
yarn in plain weaving.
Applications:
It is mainly used in vessel, building, electricity insulation(designated as E-
grade Fabric) and the production of various composite materials and
reinforced materials. It is widely used for manufacturing FRP sheets, pipe,
rods, car body, boat hull, fan blade and Varieties of profiles etc.
Product Features :
• Plain veave, even thickness and low fuzz;
• High strength in both warp and weft direction;
• Incombustibility, corrosion resistance and heat
resistance;
Main Specifications:
YOU CHANG
C glass fabric
ModelType of
Glass
Density(ends/cm)Area Weight
(GSM)Width (cm) WeaveWarp
Denisty
Weft
Denisty
CW100H C 10 9 90 90 Plain
CW105 C 8 8 105 124 Plain
CW140 C 7 6.8 131 90 Plain
CW180A C 8 7 145 90 Plain
CW180D C 6 5 145 90 Plain
CW260 C 12 8 260 100 Plain
EW100B E 20 20 100 100 Plain
EW140B E 16 12 140 100 Plain
EW200 E 8 7 200 100 Plain
HS2 and HS4 - are high strength glass fibers made from magnesium alumina
silicate system which meets the needs of military and other applications
where high strength and high performance is required.
S-Glass is generally used for polymer matrix composites that require
improved mechanical properties compared to E-glass based composites. This
is often the case when the material is operated under more extreme
conditions.
S-Glass will has the same working qualities as a standard E-glass, however
you will gain an approximate 25-30% increase in breaking strength. Used in
applications where the most possible strength is required while keeping
weight to a minimum.
Applications:
Aerospace, marine and arms industries due to its high tensile strength and higher modulus of elasticity when compared to e-glass.
Advantageous :
• 30 to 40% better tensile strength
• 16 to 20% higher modulus of elasticity
• 100 to 150 degrees celsius better temperature endurance
• 10 fold higher fatigue resistance
• Excellent impact resistance because of the high elongation to breakage
• High ageing and corrosion resistance
• Quick resin wet-out properties
• Weight saving at the same performance
YOU CHANG
S glass fabric
Main Specifications for S Glass Woven Roving :
Main Specifications for High Strength S Glass Fiber Fabric :
Style No. Warp TexFill Te
xCount
(ends/cm)
Breaking Strength >
(N/25mm)
Weight (G/m2)
SWR260 240 240 W. 6.1 F. 4.7 1800 1400 260
SWR480 480 480 W. 5.0 F. 5.0 2799 2700 480
SWR600 1290 1290 W. 2.7 F. 1.9 4350 3050 610
SWR800 2033 2033 W. 2.0 F. 2.0 4570 4570 810
Style No.Warp Tex
Count (ends/cm)
Breaking Strength
(N/25mm)
Weight(G/m2
)
Weave Pattern
Warp Fill Warp Fill
SW80B-90b SC8-12 x 1 x 2 16 16 500 500 80 2/2 Twill
SW100A-90a SC8-12 x 1 x 2 20 20 550 550 100 Plain
SW110C-90a SC8-12 x 1 x 2 22 22 600 600 110 4HS
SW140B-90a SC8-12 x 2 x 2 14 14 900 900 140 2/2 Twill
SW140C-90a SC8-12 x 2 x 2 14 14 900 900 140 4HS
SW180D-90a SC8-12 x 2 x 2 18 18 1200 1200 180 5HS
SW210B-92a SC8-12 x 2 x 3 16 12 1600 1350 210 2/2 Twill
SW210A1-92a SC8-24 x 1 x 3 16 12 1600 1350 210 Plain
SW220B-90a SC8-12 x 2 x 3 18 14 1900 1600 240 2/2 Twill
SW220C-90a SC8-12 x 2 x 3 18 14 2000 1600 240 4HS
SW220D-90a SC8-12 x 2 x 3 18 14 2000 1600 240 5HS
SW220B-90b SC8-12 x 2 x 3 18 14 1900 1600 240 2/2 Twill
SW220C-90b SC8-12 x 2 x 3 18 14 1900 1600 240 4HS
SW240F-92a SC8-12 x 2 x 3 20 14 2700 1500 260 8HS
SW280F1-90a SC8-24 x 1 x 3 20 18 2000 1700 280 8HS
S glass Woven Roving & fabric