integrated-circuit technologyj.guntzel/ine5442/csi_aulas05-08.pdf · 1 integrated-circuit...

1

INTEGRATED-CIRCUIT TECHNOLOGY

1. Processing Steps

1.1. Photolitography

1.2. Oxidation

1.3. Layer Deposition

1.4. Etching

1.5. Diffusion

1.6 Backend: assembly, test

2. Bipolar Technology

3. CMOS Technology

0. Silicon crystal growth and wafer preparation

2

CRYSTAL GROWTH

• Czochralski Process is a

Technique in Making

Single-Crystal Silicon

• A Solid Seed Crystal is

Rotated and Slowly

Extracted from a Pool of

Molten Si

• Requires Careful Control

to Give Crystals Desired

Purity and Dimensions

3

Wafer Slicing & Polishing

The silicon ingot is grown and individual wafers are sliced.

The silicon ingot is sliced into

individual wafers, polished, and

cleaned.

silicon wafer

p+ silicon substrate

4

Photoresist Coating Processes

p- epi

p+ substrate

field oxide

photoresist

PhotoresistsNegative Photoresist *

Positive Photoresist *

Other Ancillary Materials (Liquids)Edge Bead Removers *

Anti-Reflective Coatings *

Adhesion Promoters/Primers (HMDS) *

Rinsers/Thinners/Corrosion Inhibitors *

Contrast Enhancement Materials *

DevelopersTMAH *

Specialty Developers *

Inert GasesAr

N2

5

Exposure Processes

p- epi

p+ substrate

field oxide

photoresist

ExposeKr + F2 (gas) *

Inert GasesN2

6

1. Photolitography – Basic Concept

Photolitography – Basic Concept

7

Photolitography using positive photoresist

8

The simplest method of producing an oxide layer

consists of heating a silicon wafer in an oxidizing

atmosphere.

9

Oxidation of the silicon surface

10

6min20min1.7hWet O2

15min40min1.7h6h30hDry O2

1200°C1100°C1000°C900°C800°CAmbient

Times required to grow 0.1µµµµm of oxide on (III) silicon

Silicon Melting Point, 1410°C

11

Selective SiO2 growth, using local oxidation

12

Vapor deposition. PVD (a) and CVD(b).

13

Chemical Vapor Deposition (CVD) Dielectric

* High proportion of the total product use

CVD DielectricO2

O3

TEOS *

TMP *

TEOSSource

LPCVDChamber

TransferChamber

Gas Inlet

Exhaust

RF Power

Wafer

MeteringPump

Inert MixingGas

Process Gas

Vaporizer

DirectLiquid

Injection

n-w ell

p-channel transistor

p-w ell

n-channel transistorp+ substrate

Metal 1insulator layer 2

Chemical Reactions

Si(OC2H5)4 + 9 O3 → SiO2 + 5 CO + 3 CO2 + 10 H2O

Process Conditions (ILD)

Flow Rate: 100 to 300 sccm

Pressure: 50 Torr to Atmospheric

14

Epitaxy and mechanisms of

defect formation in the epitaxial layer

15

Epitaxial Silicon DepositionGasInput Lamp

Module

QuartzLamps

Wafers

Susceptor

Exhaust

* High proportion of the total product use

Chemical Reactions

Silicon Deposition: HSiCl3 + H2 → Si + 3 HCl

Process Conditions

Flow Rates: 5 to 50 liters/min

Temperature: 900 to 1,100 degrees C.

Pressure: 100 Torr to Atmospheric

silicon wafer

p- silicon epi layer

p+ silicon substrate

Dopants

AsH3

B2H6

PH3

Etchant

HCl

Carriers

Ar

H2 *

N2

Silicon Sources

SiH4

H2SiCl2HSiCl3 *

SiCl4 *

16

Wet etching.

17

Dry etching.

18

Conductor Etch

* High proportion of the total product use

EtchChambers

Cluster ToolConfiguration

TransferChamber

Loadlock

Wafers

RIE Chamber

TransferChamber

Gas Inlet

Exhaust

RF Power

Wafer

p+ substrate

p-w ell

n-channel transistor

n-w ell

p-channel transistor

source-drain areas

gate linew idth

gate oxide

Polysilicon EtchesHBr *

C2F6

SF6 *

NF3 *

O2

Aluminum EtchesBCl3 *

Cl2

DiluentsAr

He

N2

Chemical Reactions

Silicon Etch: Si + 4 HBr → SiBr4 + 2 H2

Aluminum Etch: Al + 2 Cl2 → AlCl4Process Conditions

Flow Rates: 100 to 300 sccm

Pressure: 10 to 500 mTorr

RF Power: 50 to 100 Watts

19

Dielectric Etch

* High proportion of the total product use

EtchChambers

Cluster ToolConfiguration

TransferChamber

Loadlock

Wafers

RIE Chamber

TransferChamber

Gas Inlet

Exhaust

RF Power

Wafer

Contact locations

n-w ell

p-channel transistor

p-w ell

n-channel transistorp+ substrate

Chemical Reactions

Oxide Etch: SiO2 + C2F6 → SiF4 + CO2 + CF4 + 2 CO

Process Conditions

Flow Rates: 10 to 300 sccm

Pressure: 5 to 10 mTorr

RF Power: 100 to 200 Watts

Plasma Dielectric EtchesCHF3 *

CF4

C2F6

C3F8

CO *

DiluentsAr

He

N2

CO2

O2

SF6

SiF4

20

Diffusion mechanism

21

2.00.7Arsenic

2.10.8Antimony

4.61.60.5Phosphorus

7.33.61.50.9Boron

1200°C1100°C1000°C950°CDopant

Representative junction depths, in microns

(1020 atoms/cm3 source, 1016 atoms/cm3 background,

15min predeposition, 1h drive-in)

22

Diffusion of dopants through a window in the SiO2 layer.

23

Ion Implantation

180 kV

ResolvingAperture

Ion Source

Equipment Ground

Acceleration Tube

90°Analyzing Magnet

Terminal Ground

20 kV

Focus Neutral beam and beam path gated

Beam trap andgate plate

Wafer in waferprocess chamber

X - axisscanner

Y - axisscanner

Neutral beam trap and beam gate

GasesAr

AsH3

B11F3 *

He

N2

PH3

SiH4

SiF4

GeH4

SolidsGa

In

Sb

LiquidsAl(CH3)3

* High proportion of the total product use

junction depth

p- epi

p+ substrate

field oxide

photoresist mask

n-w ell

p-channel transistor

phosphorus

(-) ions

Process Conditions

Flow Rate: 5 sccm

Pressure: 10-5 Torr

Accelerating Voltage: 5 to 200 keV

24

Chemical Mechanical Planarization (CMP)

* High proportion of the total product use.

Platen

PolishingHead

PadConditioner

Carousel

HeadSweep Slide

Load/UnloadStation

Wafer HandlingRobot & I/O

Polishing Pad

SlurryDelivery

Platen

WaferCarrier

Wafer

n-w ell

p-channel transistor

p-w ell

n-channel transistorp+ substrate

Backing (Carrier) FilmPolyurethane

PadPolyurethane

Pad ConditionerAbrasive

CMP (Oxide)Silica Slurry

KOH *

NH4OH

H2O

CMP (Metal)Alumina *

FeNO3

Process Conditions (Oxide)

Flow: 250 to 1000 ml/min

Particle Size: 100 to 250 nm

Concentration: 10 to 15%, 10.5 to 11.3 pH

Process Conditions (Metal)

Flow: 50 to 100 ml/min

Particle Size: 180 to 280 nm

Concentration: 3 to 7%, 4.1 - 4.4 pH

*

25

Electrical Test Probe

Defective IC

Individual integrated circuits are tested to distinguish good

die from bad ones.

n-well

p-channel transistor

p-well

n-channel transistorp+ substrate

bonding padnitride

Metal 2

26

Die Cut and AssemblyGood chips are attached to a lead frame package.

27

Die Attach and Wire Bonding

lead frame gold wire

bonding pad

connecting pin

28

Final Test

Chips are electrically tested under varying environmental conditions.

29

2. Bipolar Technology

Diffusion of the buried layer. Segment of

the mask (a) and cross-section of

the npn transistor (b) after the diffusion.

30

Island formation. Segment of the mask (a) and

cross-section of the npn transistor (b) after diffusion of

the p-type isolation.

31

Transistor base p-type diffusion. Segment of the mask (a) and

cross-section of the npn transistor (b) after

base diffusion

32

Emitter diffusion. Segment of the mask (a) and

cross-section of the npn transistor (b) after

emitter diffusion.

33

Layout (a) and cross-section of the complete

npn transistor (b).

34

Active regions in the n-well CMOS inverter.

Edges of active regions in the mask (a) and cross-section

of the inverter (b).

3. CMOS Technology

35

Polysilicon region in the n-well CMOS inverter.

Window in the mask (a) and cross-section of the

inverter (b).

36

Implantation of n-channel transistor drain and source.

Window in the n-select mask (a) and cross-section of the

inverter (b).

37

CMOS inverter. Composite layout (a),

cross-section (b), and electrical diagram (c).

38

References

1. W. Maly, Atlas of IC Technologies, Benjamin/Cummings Publications,

1987

2. Conrad T. Sorenson, “Semiconductor Manufacturing Technology:

Semiconductor Manufacturing Processes,”

http://www.erc.arizona.edu/Education/MME%20Course%20Materials/

MME%20Modules/Manufacturing%20Module/Manufac%20Overview.p

pt

3. Young Soon Song. et. al., “EE 4345 - Semiconductor Electronics

Design Project. Silicon Manufacturing,”

www.uta.edu/ronc/4345sp02/lectures/L09a_4345_Sp02.ppt